Patent Application
20090277995
The present invention relates to a supporting strut for supporting an intermediate deck that is arranged in an aircraft fuselage, with said supporting strut comprising a hollow cylindrical rod body that comprises a fibre reinforced material, wherein the two ends of said rod body are designed as attachment sections for detachable attachment to the aircraft fuselage or to the intermediate deck. Apart from this, the invention also comprises a method for producing such a rod body. Furthermore, an aircraft comprising a fuselage in which such supporting struts are installed forms part of the invention.
Aircraft of the type of interest in the present document comprise at least one intermediate deck that extends across an aircraft fuselage in order to create a multi-level design. In a commercial aircraft such an intermediate deck is, for example, provided in order to install passenger seats thereon, which passenger seats occupy the upper region of the aircraft fuselage. In contrast to this, the lower region of the aircraft fuselage, i.e. the region below the intermediate deck, is normally used as a cargo hold. In particular in case of large-volume aircraft fuselages, the corresponding large-area intermediate decks need to be additionally supported relative to the aircraft fuselage in order to provide adequate static stability. For this purpose the supporting struts of interest in this document, which are detachably attached between the at least one intermediate deck and the aircraft fuselage, are used.
From the general state of the art it is known to produce supporting struts by wrapping carbon fibre threads around a mandrel, which carbon fibre threads are then embedded in epoxy resin. Such winding usually takes place at an angle of approximately 45° relative to the longitudinal axis of the mandrel, and subsequently, in order to improve stability, at an angle of approximately 70° relative to the longitudinal axis of the mandrel. After the material has been wound onto the mandrel and after the epoxy resin has cured or hardened, the mandrel can be removed, and a hollow-cylindrical rod body results, which on both ends is fitted out with rod ends in order to make possible attachment to the intermediate deck and the aircraft fuselage respectively.
Such rod bodies are associated with a disadvantage as a result of the deviation of the fibre alignment from the optimal alignment, which deviation is due to the production process, thus resulting in thicker wall thicknesses in the dimensioning that is required to achieve adequate buckling resistance. Associated with this, the rod body has a comparatively heavier weight, which is basically undesirable in aircraft construction. Rod bodies produced in this way are associated with a further disadvantage in that shock loading can have a significant negative effect on the stability of the supporting strut. Known supporting struts are thus comparatively susceptible to damage. Furthermore, due to the material used, meeting the required fire-resistance characteristics is problematic or often achievable only with the use of additional measures, for example special coatings.
It is the object of the present invention to create a supporting strut whose rod body features a lightweight construction while at the same time providing good buckling resistance and resistance to damage, as well as providing improved fire-resistance characteristics.
This object is met, based on a supporting strut according to the precharacterising part of claim 1 in conjunction with its characteristic features. From the point of view of process technology, the object is met by claim 6. The respective related dependent claims disclose advantageous improvements of the invention.
The invention includes the technical teaching according to which the rod body comprises at least one first reinforcement layer made from a carbon fibre fabric with an identical number of warp- and weft threads in 45° alignment or 90° alignment as well as at least one second reinforcement layer made from a carbon fibre fabric comprising a higher number of warp threads than weft threads in 0° alignment, which together with artificial resin, preferably epoxy resin, form a compact fibre reinforced material.
The carbon fibre fabric that is used to form the reinforcement layers can either be made entirely from carbon fibre threads, or can at least predominantly comprise carbon fibre threads. The 45° alignment or 90° alignment stated refers to the direction of the warp threads relative to the longitudinal axis of the rod body. Analogously the same also applies in relation to the stated 0° alignment. In this case the warp threads extend parallel to the longitudinal axis of the rod body.
The prepreg interlaid scrim that arises by stack formation with the at least one first reinforcement layer together with the at least one second reinforcement layer can be designed such that a first reinforcement layer is arranged immediately adjacent to a second reinforcement layer, or such that several first reinforcement layers are combined with several second reinforcement layers and any others. The prepreg interlaid scrim used according to the invention features a fine count structure and in its final state is comparatively more resistant to impact loads. With the use of a special production method, which is explained below, good strength can be achieved with relatively thin walls. This method is based on repeated thermal compacting that reduces the settling distance of the material, reduces the risk of folds developing when the material is wound onto the mandrel, reduces the incidence of cavity formation and also stabilises the selected fibre orientation.
According to a measure that improves the invention, it is proposed that at least one outer reinforcement layer, instead of comprising a carbon fibre fabric, comprises a glass fibre fabric. When compared to carbon fibre fabric, glass fibre fabric has a special characteristic in that it renders impact damage cracks or delamination visually better detectable, which can be used to advantage as a visual damage indicator. Thus damage to the rod body can be detected in a simple manner without additional active sensors or expensive non-destructive testing (NDT) measures such as ultrasonic testing. Furthermore, the outer layer of the woven glass-fibre fabric provides protection from galvanic corrosion.
Preferably, each reinforcement layer should be made with at least two radial windings, so that adequate overall stability is provided. Two to three windings are particularly preferred. Winding can be facilitated by means of a rotary drive of the mandrel. Likewise it is imaginable to implement an axially spiralling layer structure of the various reinforcement layers so as to achieve improved stability. In this context it is important that the fibre orientation of 45°, 90° or 0° is largely maintained, and that the normal tolerance ranges of plus/minus 10% are adhered to. To this extent the information relating to the angular alignment according to the subject of the invention is to be interpreted as having to be within the tolerance range.
According to the invention, the rod body, which forms the subject of the invention, of the supporting strut is made by carrying out the following steps at least once:
a) first pre-compacting of a prepreg interlaid scrim, either at room temperature or at a higher temperature, comprising at least one first reinforcement layer made of a carbon fibre fabric with an identical number of warp- and weft threads in 45° alignment or 90° alignment, as well as at least one second reinforcement layer made of a carbon fibre fabric with a greater number of warp threads than weft threads in 0° alignment of the warp threads, which are connected with artificial resin under the force of pressure;
b) wrapping the prepreg interlaid scrim, which comprises the reinforcement layers, at least twice around a preferably pre-heated mandrel in order to produce a hollow cylinder;
c) wrapping a pre-tensioned thermoplastic woven textile tape for intermediate compacting around the mandrel onto which the prepreg interlaid scrim has been laid.
Preferably, in this way two to four prepreg interlaid scrims are formed by repeatedly carrying out the steps set out above so as to ensure adequate wall thickness while at the same time maintaining light weight. Each time, the woven textile tape that is used for second intermediate compacting is preferably removed, by unwinding, prior to the mandrel next being wrapped with a further prepreg interlaid scrim so that the thinnest-possible wall thicknesses can be achieved. The woven textile tape does not contribute to the stability of the rod body but instead is only used in a corset-like manner during production in order to generate an external counterforce when the material on the mandrel on the inside expands as a result of an increase in the temperature, thus causing the desired compacting effect. At the same time, as a result of this, air is evacuated from the fibre reinforced material, and excess artificial resin is removed. It is important to understand that compacting does not result in complete solidification of the artificial resin. Instead, complete curing of the artificial resin is achieved during a final processing step that will be described below. After all the reinforcement layers have been applied, and after intermediate compacting of them has been completed, a glass fibre prepreg is applied as a final single layer.
The temperature increase which causes a volume increase of the mandrel material, combined with a concurrent outer enclosing by means of the woven textile tape, in turn causes the fibre reinforced material to be de-aerated and compressed, with excess material being removed.
Final curing of the mandrel onto which the reinforcement layers have been placed in the manner described above preferably takes place according to the following steps:
g) a peel ply layer and/or a perforated release-film layer is wound onto the last, i.e. outermost, reinforcement layer for the purpose of removing excess artificial resin in order to improve the surface;
h) this is followed by a pre-tensioned thermoplastic woven textile tape as a last wrapping being wound on; after which
i) curing of the artificial resin at an increase in the temperature, while at the same time final compacting is carried out.
This ensures that excess artificial resin is reliably removed to maximise stability, and that overall an outer surface of corresponding quality results. This is a prerequisite for any damage that the rod body may sustain becoming more easily visible.
In this arrangement final curing can be carried out in a computer-controlled curing oven with or without a rotary device.
Preferably, after the curing process, the woven textile tape as well as the peel ply layer and, if present, also the perforated release-film layer are removed by being unwound from the last or outermost reinforcement layer in order to obtain the rod body of the supporting strut so that it is ready for assembly.
After its removal from the mandrel, the rod body is cut to the desired dimension and the surfaces are activated for rod-end bonding.
Thereafter on each open end of the hollow-cylindrical rod body rod ends made from a light metal can be inserted, which rod ends in the installed state are preferably integrally fixed by means of a suitable adhesive material. Via the rod ends, detachable attachment to the aircraft fuselage and/or to the at least one intermediate deck of the aircraft fuselage takes place with the use of suitable screw-, pin- or bolt means.
Further measures that improve the invention are shown below in more detail with reference to the figures together with the description of a preferred exemplary embodiment of the invention. The following are shown:
According to
According to
Prior to the final hardening of the artificial resin, which hardening is illustrated in the diagram, as a result of an increase in the temperature to produce the rod body 3, the prepreg interlaid scrim 6 is generated according to the following layer design.
According to
According to
According to
After intermediate compacting the woven textile tape 11 is removed in that it is unwound from the prepreg interlaid scrim 6.
The production sequence described above is subsequently repeated three more times.
According to
According to
When the rod body 3 is cured, the woven textile tape 11 as well as the peel ply layer 7 and the perforated release-film layer 8 are removed by being unwound from the exterior reinforcement layer 10d so that the installation-ready rod body 3 of the supporting strut is formed. After its removal from the mandrel, the rod body is cut to the desired dimension and the surfaces are activated for rod-end bonding. Once the rod ends have been bonded into place the supporting strut is basically ready for use.