1. Field of the Invention
The present invention relates to a surface acoustic wave device used for a resonator, a band pass filter, or other suitable devices.
2. Description of the Related Art
Heretofore, a surface acoustic wave device that utilizes a surface acoustic wave has been widely used as, for example, a resonator or a filter device. For example, in Japanese Unexamined Patent Application Publication No. 2001-44787, as one example of such a surface acoustic wave device, a surface acoustic wave device is disclosed which includes a SiO2 film formed on a piezoelectric substrate so as to cover an IDT electrode and a SiN film formed on the SiO2 film.
As a result of the SiO2 film being formed so as to cover the IDT electrode, the surface acoustic wave device disclosed in Japanese Unexamined Patent Application Publication No. 2001-44787 has excellent frequency temperature characteristics. In addition, in the surface acoustic wave device disclosed in Japanese Unexamined Patent Application Publication No. 2001-44787, when the thickness of the SiN film formed on the SiO2 film is adjusted, the frequency characteristics of the surface acoustic wave device can be adjusted. Thus, the frequency accuracy can be improved.
However, in the surface acoustic wave device disclosed in Japanese Unexamined Patent Application Publication No. 2001-44787, for example, spurious response may be disadvantageously generated between a resonant frequency and an anti-resonant frequency or in a passband due to an unnecessary wave.
Preferred embodiments of the present invention provide a surface acoustic wave device that prevents or decreases degradation in frequency characteristics caused by an unnecessary wave.
A surface acoustic wave device according to a preferred embodiment of the present invention includes a piezoelectric substrate, an IDT electrode, a first dielectric layer, and a second dielectric layer. The IDT electrode is provided on the piezoelectric substrate. The first dielectric layer is provided on the piezoelectric substrate. The first dielectric layer is preferably made of silicon oxide. The second dielectric layer is provided on the first dielectric layer. The second dielectric layer has an acoustic velocity greater than that of the first dielectric layer. The surface acoustic wave device according to this preferred embodiment of the present invention may preferably further include a third dielectric layer. The third dielectric layer is disposed between the first dielectric layer and the piezoelectric substrate. The third dielectric layer covers a surface of the piezoelectric substrate and an upper surface and side surfaces of the IDT electrode.
In a preferred embodiment of the surface acoustic wave device according to the present invention, the thickness of the third dielectric layer is preferably at least about 1.5% of the wavelength determined by the pitch between electrode fingers of the IDT electrode, for example. With this structure, the degradation in frequency characteristics caused by an unnecessary wave is more effectively prevented or decreased.
In another preferred embodiment of the surface acoustic wave device according to the present invention, the thickness of the third dielectric layer is preferably equal to or less than that of the first dielectric layer, for example.
In another preferred embodiment of the surface acoustic wave device according to the present invention, the third dielectric layer is preferably made of silicon nitride, silicon oxynitride, diamond, alumina, or aluminum nitride, for example.
In another preferred embodiment of the surface acoustic wave device according to the present invention, the second dielectric layer is preferably made of silicon nitride, silicon oxynitride, diamond, alumina, or aluminum nitride, for example.
In another preferred embodiment of the surface acoustic wave device according to the present invention, the piezoelectric substrate is preferably made of LiNbO3 or LiTaO3, for example.
In another preferred embodiment of the surface acoustic wave device of the present invention, the piezoelectric substrate is preferably a 120° to 130° rotated Y-cut X-propagation LiNbO3 substrate. In this structure, when the Rayleigh wave is used as a main mode, and the SH wave is set as an unnecessary wave, the degradation in frequency characteristics caused by the SH wave, which is an unnecessary wave, can be more effectively reduced or prevented.
In another preferred embodiment of the surface acoustic wave device according to the present invention, the piezoelectric substrate is preferably a −10° to 10° rotated Y-cut X-propagation LiNbO3 substrate, for example. In this structure, when the SH wave is used as a main mode, and the Rayleigh wave is set as an unnecessary wave, the degradation in frequency characteristics caused by the Rayleigh wave, which is an unnecessary wave, is more effectively prevented or decreased.
With the surface acoustic wave devices according to various preferred embodiments of the present invention, the third dielectric layer is provided between the first dielectric layer and the piezoelectric substrate so as to cover the surface of the piezoelectric substrate and the upper surface and the side surfaces of the IDT electrode. Thus, the degradation in frequency characteristics caused by an unnecessary wave is prevented or decreased.
The above and other elements, features, steps, characteristics and advantages of the present invention will become more apparent from the following detailed description of the preferred embodiments with reference to the attached drawings.
Hereinafter, as a preferred embodiment of the present invention, a ladder type surface acoustic wave filter device 1 shown in
As shown in
The series arm resonators S1 to S4 and the parallel arm resonators P1 to P3 each include at least one surface acoustic wave resonator. A schematic plan view of such a surface acoustic wave resonator 20 is shown in
The surface acoustic wave resonator 20 includes a piezoelectric substrate 21. The piezoelectric substrate 21 may preferably be made of, for example, LiNbO3 or LiTaO3. The piezoelectric substrate 21 may preferably be, for example, a 120° to 130° rotated Y-cut X-propagation LiNbO3 substrate or a −10° to 10° rotated Y-cut X-propagation LiNbO3 substrate.
On a primary surface 21a of the piezoelectric substrate 21, an IDT electrode 22 is provided. The IDT electrode 22 includes a pair of comb-shaped electrodes which are alternately arranged side by side. The IDT electrode 22 may be made of any appropriate electrically conductive material. The IDT electrode 22 may preferably be made of, for example, a metal selected from the group consisting of Al, Pt, Au, Ag, Cu, Ni, Ti, Cr, and Pd or an alloy including at least one metal selected from the group consisting of Al, Pt, Au, Ag, Cu, Ni, Ti, Cr, and Pd. In addition, the IDT electrode 22 may also preferably be defined by a laminate of electrical conductive layers made of the above-mentioned metals and/or alloys.
On the primary surface 21a, a first dielectric layer 23 is provided. The first dielectric layer 23 is preferably made of silicon oxide, for example. Thus, the first dielectric layer 23 has a temperature coefficient of frequency (TCF) with a positive or negative slope opposite to that of the piezoelectric substrate 21. Accordingly, since the first dielectric layer 23 is provided, the frequency temperature characteristics of the surface acoustic wave resonator 20 are improved. As a result, the frequency temperature characteristics of the surface acoustic wave filter device 1 are improved.
The thickness of the first dielectric layer 23 is not particularly limited as long as an elastic wave excited at the IDT electrode 22 is allowed to become a surface acoustic wave. The thickness of the first dielectric layer 23 may preferably be set, for example, in a range from approximately the electrode thickness to about 0.5λ (λ is the wavelength determined by the pitch between electrode fingers of the IDT electrode).
On the first dielectric layer 23, a second dielectric layer 24 is provided. The first dielectric layer 23 is covered with this second dielectric layer 24. The second dielectric layer 24 has an acoustic velocity greater than that of the first dielectric layer 23. The second dielectric layer 24 may preferably be made of, for example, silicon nitride, silicon oxynitride, diamond, alumina, or aluminum nitride. By adjusting the thickness of this second dielectric layer 24, the frequency characteristics of the surface acoustic wave resonator 20 can be adjusted. As a result, the frequency characteristics of the surface acoustic wave filter device 1 can be adjusted. Thus, when the second dielectric layer 24 is provided, the surface acoustic wave filter device 1 can be manufactured with excellent frequency accuracy. In addition, after manufacturing, the frequency characteristics, such as filter characteristics, can be easily adjusted.
In addition, the thickness of the second dielectric layer 24 is not particularly limited as long as an elastic wave excited at the IDT electrode 22 is allowed to become a surface acoustic wave. The thickness of the second dielectric layer 24 may preferably be set, for example, in a range of about 0.002λ to about 0.05λ (λ is the wavelength determined by the pitch between the electrode fingers of the IDT electrode).
Furthermore, in this preferred embodiment, between the first dielectric layer 23 and the piezoelectric substrate 21, a third dielectric layer 25 is preferably provided. A primary surface 21a of the piezoelectric substrate 21 and an upper surface 22a and side surfaces 22b and 22c of the IDT electrode 22 are directly covered by the third dielectric layer 25. The third dielectric layer 25 is in direct physical contact with the primary surface 21a of the piezoelectric substrate 21 and the upper surface 22a and the side surfaces 22b and 22c of the IDT electrode 22.
The third dielectric layer 25 is preferably made of a dielectric material different from that of the first dielectric layer 23. The third dielectric layer 25 may preferably be made of, for example, silicon nitride, silicon oxynitride, diamond, alumina, or aluminum nitride. In addition, the third dielectric layer 25 may have an acoustic velocity greater or less than that of the first dielectric layer 23.
The thickness of the third dielectric layer 25 is equal or substantially equal to or less than that of the first dielectric layer 23 and is preferably, for example, at least about 1.5% of the wavelength determined by the pitch between the electrode fingers of the IDT electrode 22.
In addition, methods for forming the first to the third dielectric layers 23 to 25 are not particularly limited. The first to the third dielectric layers 23 to 25 may be formed, for example, by a sputtering method or a CVD method.
As described above, in this preferred embodiment, between the first dielectric layer 23 and the piezoelectric substrate 21, the third dielectric layer 25 is preferably arranged so as to cover the primary surface 21a of the piezoelectric substrate 21 and the upper surface 22a and the side surfaces 22b and 22c of the IDT electrode 22. Thus, by changing the thickness of the third dielectric layer 25, the acoustic velocity relationship between a plurality of types of surface acoustic waves excited by the IDT electrode 22 may be shifted. Accordingly, the frequency of spurious response caused by an unnecessary surface acoustic wave may be set far from the resonant frequency and the anti-resonant frequency of the main mode which is used to obtain the performance of the device.
For example, when the piezoelectric substrate 21 is a 120° to 130° rotated Y-cut X-propagation LiNbO3 substrate, the Rayleigh wave is used as a main mode, and the SH wave is set as an unnecessary wave, a frequency position of spurious response caused by the SH wave may be located at an outer side portion of the frequency band between the resonant frequency and the anti-resonant frequency of the Rayleigh wave or outside the passband set by the Rayleigh wave. As a result, excellent frequency characteristics are effectively achieved.
In addition, for example, when the piezoelectric substrate 21 is a −10° to 10° rotated Y-cut X-propagation LiNbO3 substrate, the SH wave is used as a main mode, and the Rayleigh wave is set as an unnecessary wave, a frequency position of spurious response caused by the Rayleigh wave may be located at an outer side portion of the frequency band between the resonant frequency and the anti-resonant frequency of the SH wave or outside the passband set by the SH wave. As a result, excellent frequency characteristics are effectively achieved.
Hereinafter, this effect will be described in detail with reference to particular non-limiting examples.
First, in accordance with the following design parameters, surface acoustic wave resonators each having substantially the same structure as that of the surface acoustic wave resonator 20 described above were formed by variously changing the thickness of the third dielectric layer, and the resonant frequency and the anti-resonant frequency of the Rayleigh wave which was a main mode and a frequency position of spurious response caused by the SH wave which was an unnecessary wave were measured. In addition, the ratio (F(SH)/Fa) of the frequency of spurious response caused by the SH wave to the anti-resonant frequency of the Rayleigh wave was calculated. The results are shown in
Design Parameters of Surface Acoustic Wave Resonator
Piezoelectric substrate: 129° rotated Y-cut X-propagation LiNbO3 substrate
Structure of IDT electrode: Ti film (thickness: about 10 nm)/AlCu film (thickness: about 130 nm, Cu content: about 10 percent by mass)/Ti film (thickness: about 10 nm)/Pt film (thickness: about 80 nm)/NiCr film (thickness: about 10 nm)/piezoelectric substrate
Wavelength of IDT electrode (λ): about 4.0 μm
Duty of IDT electrode: about 0.48
First dielectric layer: SiO2 film with a thickness of about 1,100 nm
Second dielectric layer: Si3N4 film with a thickness of about 40 nm
Third dielectric layer: Si3N4 film with a thickness of about 0 nm, about 50 nm, about 100 nm, or about 150 nm
From the results shown in
In addition, as described above, since the change mode in frequency characteristics of the Rayleigh wave and that of the SH wave with respect to the wavelength normalized thickness of the third dielectric layer are different from each other, when the SH wave is used as a main mode, and the Rayleigh wave is set as an unnecessary wave, with the third dielectric layer provided as described above, the degradation in frequency characteristics resulting from the spurious response caused by an unnecessary wave are also effectively prevented or decreased.
Next, as an example, a surface acoustic wave filter device having the structure similar to that of the above-described surface acoustic wave filter device 1 was produced with the following design parameters, and the insertion loss was measured. The result is shown in
In addition, as a comparative example, a surface acoustic wave filter device having the structure similar to that of the surface acoustic wave filter device described above was produced except that the third dielectric layer was not provided, and the insertion loss was measured. The result is shown in
Design Parameters of Example
Piezoelectric substrate: 129° rotated Y-cut X-propagation LiNbO3 substrate
Structure of IDT electrode: Ti film (thickness: about 10 nm)/AlCu film (thickness: about 130 nm, Cu content: about 10 percent by mass)/Ti film (thickness: 10 nm)/Pt film (thickness: 80 nm)/NiCr film (thickness: about 10 nm)/piezoelectric substrate
First dielectric layer: SiO2 film with a thickness of about 1,000 nm
Second dielectric layer: Si3N4 film with a thickness of about 40 nm
Third dielectric layer: Si3N4 film with a thickness of about 100 nm
As shown in
In addition, when the third dielectric layer is provided between the first dielectric layer and the piezoelectric substrate so as to cover the surface of the piezoelectric substrate and the upper surface and the side surfaces of the IDT electrode, the second dielectric layer may not be provided. Even in this case, since the frequency characteristics of a main mode and that of spurious response which is an unnecessary wave are confirmed to behave differently from each other with respect to the thickness of the third dielectric layer, it is understood that the effects of preferred embodiments of the present application are still obtained.
While preferred embodiments of the present invention have been described above, it is to be understood that variations and modifications will be apparent to those skilled in the art without departing from the scope and spirit of the present invention. The scope of the present invention, therefore, is to be determined solely by the following claims.
Number | Date | Country | Kind |
---|---|---|---|
2010-294555 | Dec 2010 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
7573178 | Inoue et al. | Aug 2009 | B2 |
7939989 | Solal et al. | May 2011 | B2 |
20040164644 | Nishiyama et al. | Aug 2004 | A1 |
20050281210 | Makino | Dec 2005 | A1 |
20070214622 | Nishiyama et al. | Sep 2007 | A1 |
20080067891 | Matsuda et al. | Mar 2008 | A1 |
20080303379 | Nakai et al. | Dec 2008 | A1 |
20090058225 | Kadota | Mar 2009 | A1 |
20090128260 | Block et al. | May 2009 | A1 |
20100060102 | Goto et al. | Mar 2010 | A1 |
20120161577 | Abbott et al. | Jun 2012 | A1 |
Number | Date | Country |
---|---|---|
10 2006 022 580 | Nov 2007 | DE |
11 2007 001 259 | Jun 2009 | DE |
2 093 881 | Aug 2009 | EP |
06-164293 | Jun 1994 | JP |
11-088102 | Mar 1999 | JP |
2001-044787 | Feb 2001 | JP |
2002-084156 | Mar 2002 | JP |
2004-112748 | Apr 2004 | JP |
2004-297369 | Oct 2004 | JP |
2006-121233 | May 2006 | JP |
2007-235711 | Sep 2007 | JP |
2005083881 | Sep 2005 | WO |
2007097186 | Aug 2007 | WO |
Entry |
---|
Official Communication issued in International Patent Application No. PCT/JP2011/078778, mailed on Feb. 14, 2012. |
Official Communication issued in corresponding German Patent Application No. 11 2011 104 653.7, mailed on Feb. 26, 2014. |
Official Communication issued in corresponding German Patent Application No. 11 2012 002 502.4, mailed on Jul. 8, 2014. |
Number | Date | Country | |
---|---|---|---|
20130285504 A1 | Oct 2013 | US |
Number | Date | Country | |
---|---|---|---|
Parent | PCT/JP2011/078778 | Dec 2011 | US |
Child | 13930238 | US |