Patent Grant
10736717
This application is a national stage application under 35 U.S.C. 371 of PCT Application No. PCT/EP2007/005681 having an international filing date of 27 Jun. 2007, which designated the United States, which PCT application claimed the benefit of German Application No. 102006034866.4 filed 25 Jul. 2006, the entire disclosure of each of which are hereby incorporated herein by reference.
The invention relates to a dental implant with a post element that can be inserted into a jawbone and with a mounting element associated with same, to which mounting element a dental prosthesis element can be attached, with the post element being embodied as an yttrium- and/or aluminum oxide-stabilized zirconium oxide-based ceramic body.
Dental implants are known in a wide variety of forms. They are usually used through screwing into the jawbone at the site of a tooth which has been extracted or has fallen out in order to hold a prosthetic mounting element or a crown as a dental prosthesis after a healing phase of three to four months. To this end, such a dental implant is usually embodied as an appropriately-shaped metal or ceramic body and shaped in the manner of a pin and has at its apical end a mostly self-cutting screw thread with which the pin is inserted into the appropriately-prepared implant bed.
As a rule, dental implants are manufactured from titanium, zirconium, niobium or tantalum or of histocompatible alloys which contain one of these elements as the main component. Moreover, dental implants are also manufactured from ceramics. The ceramics used are usually zirconium oxide-based ceramics in which the tetragonal phase is stabilized preferably through the admixture of yttrium oxide (TZP, TZP-A with aluminum oxide components) or which are reinforced through the (usually additional) admixture of aluminum oxide, aluminum oxide [sic] (ATZ ceramics). However, other aluminum oxide-based dental implants are also known.
The goal of all of these implants is that the osseous tissue be given the opportunity to quickly and permanently bond with the implant surface. There is also talk of so-called osseointegration here. In this context, it has already been known for some time that the microscopic structure of the implant surfaces has a special importance for the promotion of osseointegration. In particular, porous surfaces with a pore size in the micrometer range have proven advantageous up to now. As a result of the enlarged contact surface between implant and bone, bone growth is promoted and the rate of bone accretion after the post-operative trauma is therefore increased.
For example, ceramic-based dental implants of the above-named type are described in EP 1 450 722 B1, in which a roughening in the post element with a roughness depth of 4 μm to 20 μm is provided in order to promote osseointegration. There, surface structures are first produced through radiation treatment.
Moreover, metallic dental implants with a homogenous nanostructured surface are known from DE 20 2005 002 450 U1. As a result of an especially favorable wetting behavior, such nanostructured surfaces appear to promote the growing-in of the implants and the integration into the osseous tissue.
The methods known up to now for the surface structuring of ceramic bodies, particularly for use as dental implants, particularly comprise sandblasting, etching and laser treatment. The ceramic dental implants currently available on the market are usually sandblasted and generally have a roughness depth of 0.5 μm to ca. 4 μm.
Although the above-named approaches have already been able to achieve improvements in the ingrowth behavior of the dental implants, there continues to be a desire for even more extensive improvements in this regard.
It is therefore the object of the invention to propose a dental implant of the aforementioned type which has a further-improved ingrowth or integration behavior during the healing into the bone.
This object is achieved according to the invention in that the surface of the dental implant is provided at least in a partial area with a structure that has nanoscopic pores or an otherwise executed nanoscopic structure, and in that it has a depletion zone with a reduced yttrium and/or aluminum oxide element compared with the internal volume.
The invention takes the idea as a starting point that an especially extensive promotion of the osseointegration can be achieved by designing, in particular, the surface structure in the relevant area of the post element in an uncompromising manner such that it supports osseointegration. For this purpose, a surface structure on a nanoscopic scale, i.e. particularly with nanoscopic pores, which is conducive to this objective should be made available. As it surprisingly turned out during the use of yttrium-stabilized zirconium oxide for the ceramic body, the formation of such nanoscopic structures or pores near the surface can be encouraged greatly by performing a targeted reshaping of the tetragonal crystal structure (present in the internal volume of the ceramic body) of the yttrium-stabilized zirconium oxide into the monocline crystal structure. To achieve this in an especially simple manner, the targeted removal of the yttrium portion from the material is provided for near the surface, which brings about the transformation and formation of the monocline phase.
The production of the depletion zone in the surface area provided for in this manner by the invention which ends up bringing about the desired structure and the desired characteristics upon connection with the body tissue can be achieved, in particular, through the selective extraction of individual components such as, for example, chemical elements and/or oxides from the surface, preferably through an appropriately-selected etching process. Such favorable structures can be produced, in particular, by extracting from the surface individual elements and/or individual metal oxides located in the ceramic (zirconium oxide, aluminum oxide, yttrium oxide, hafnium oxide, etc.), particularly yttrium oxide and hafnium oxide. A depletion zone of these metal oxides is thus produced on and/or in the area of the surface near the boundary.
To wit, through the treatment of the ceramic base body in the manner of etching and, particularly, of intercrystalline etching, a specific nanostructure is formed on the surface. A multitude of comparatively small pores or recesses with an average extension in the sub-micrometer range, preferably smaller than 500 nm and particularly smaller than 250 nm, can be found here. Such structures can be detected, for example, by means of electron microscope imaging. The surface is characterized particularly in that the depth of the nanostructure, which is to say the depth of the pores that can be produced here, is greater than the structural width, i.e. the characteristic lateral extension of the produced structures.
The ratio in the nanostructure between the structural depth and the structural width is expediently greater than 1:1, preferably greater than 1.5:1 and particularly greater than 2:1.
The depletion zone is advantageously arranged in a portion of the post element which can be inserted into a jawbone.
Through the production of the depletion zone, the occurrence of a nanoscopic structure with the described characteristics is aided and/or made possible. Moreover, it is suspected that the oxides of the ceramics used, particularly hafnium isotopes, have radioactive characteristics. If these are detached from the surface and are not in direct contact with the bone and/or tissue cells, this can have a positive influence on bone growth and bone preservation.
Some investigations with respect to wetting characteristics have shown that there are two particular factors for the wetting characteristics of surfaces. The first factor for the wetting characteristics is the degree of hydrocarbon contamination on the surface. Wetting experiments with water and samples of titanium have shown that, immediately after etching, a hydrophilic behavior with wetting angles of less than 15° is present. After several hours of storage of the samples under exposure to air, this behavior diminishes and can end up becoming hydrophobic.
The second factor can be described as follows. Depending on the structures smaller than 100 μm, especially smaller than 10 μm and particularly smaller than 0.5 μm, it is observed that the wetting behavior can be influenced toward hydrophilia or hydrophobia. It turned out that in structures with this structure size and with pointed and sharp-edged elevations, the wetting characteristics change toward hydrophobic behavior. Elevations with such a structure size and rounded-off or harmonic elevations change the wetting behavior toward hydrophilia. Structures with the described dimensions in which the elevations have average radii that are greater than 5 nm, preferably greater than 10 nm and particularly greater than 50 nm but smaller than 500 nm, have proven to be especially favorable. Further investigations have shown that this behavior is applicable to ceramic surfaces as well.
Particularly in zirconium oxide-based ceramics, especially favorable wetting characteristics were detected when the structures are smaller than 1 μm, preferably smaller than 0.5 μm and particularly smaller than 0.2 μm, and the elevations have average radii that are greater than 5 nm, preferably greater than 10 nm and particularly greater than 50 nm but smaller than 500 nm. Depending on the structure in the structural size range between 50 nm and 50 μm, a capillary effect occurs prior to the contamination with hydrocarbons and/or through the superimposition of the described nanostructure. Said nanostructure is characterized in that water rises upward against the force of gravity on the surface, particularly on a dental implant. This characteristic proves to be especially favorable since, in this manner, proteins, particularly the BPM proteins, can be stored in and/or on the surface and/or accumulated in large quantities. This occurs either as a result of the surface being wetted with blood or the implants being pretreated with a protein-enriched liquid.
In a ceramic surface with hydrophilic characteristics (wetting angle less than 15°) and in a nanostructure in which the ratio between the structural depth and the structural width is greater than 1:1, advantageously greater than 1.5:1 and particularly greater than 2:1, there is the possibility that the proteins will get caught in the structures and be available to promote bone growth.
The microscopic surface enlargement available for the dental implant by way of the depletion zone is characterized in that mostly round craters are formed which resemble a lunar landscape. Th[ese] craters are characterized in that the ratio between structural depth and structural width is less than 1:1, preferably less than 1:2 and particularly less than 1:5. The craters have a diameter of greater than 0.5 μm, particularly greater than 1 μm and less than 60 μm and particularly less than 40 μm. The depth of the craters is typically less than 4 μm, advantageously less than 3 μm and particularly less than 2 μm.
The good wetting characteristics of the ceramic body that can be achieved with the invention are also especially well-suited to especially advantageous use in dental or other bone implants and other applications as well. For example, these characteristics also prove to be especially important in the attachment of ceramic bodies by means of an adhesive, lacquer, cement, etc., and are therefore especially advantageous when used in conjunction with adhesive compounds of any kind. As a result, ceramic prosthetic elements (crowns, bridges, inlays, onlays) were able to be joined with a better bond to the attaching adhesive/cement than previously.
If an adhesive or other liquid fastening material wets the entire surface as a result of good wetting characteristics, a liquid transition occurs between the ceramic workpiece and the fastening material (preferably an adhesive). In this manner, optimized retention characteristics occur and an optimized bond is created between workpiece and fastening material. These characteristics can be preferably used in all areas in which zirconium oxide- or aluminum oxide-based ceramic workpieces are used.
By virtue of the favorable wetting characteristics of the surface, the flow characteristics in liquids and gases of ceramic workpieces with such a surface are also influenced.
Moreover, with regard to the phase characteristics, analysis has shown that the ratio between the tetragonal and the monocline phase changed as a result of one of the above-described treatments on the surface. After the sintering process and prior to insertion into the patient's mouth, the proportion of the monocline phase in the surface was able to be increased or reduced by means of such a process to or by at least 0.1%, preferably to or by more than 0.5% and particularly to or by more than 1.5%. Since the surface is placed under pressure through the lower density of the monocline phase, the initial formation of cracks is inhibited in this manner and an increase in the initial strength can be expected.
Particularly, the production of the provided depletion zone in the surface of the ceramic body can occur by means of an etching process in an appropriately-selected acid bath. The provided reaction partners for the ceramic of the base body, which is to say the ions with components from the VIIth main group of the periodic system of elements, are able to act here particularly as halogens for the respective metals. In particular, the acid bath can comprise ions which consist of the elements fluorine (F) or chlorine (Cl) or include these as components. During treatment in the acid bath, the possibility is brought about for the ions of the acid to chemically change the surface and remain on the surface as contaminants.
Some of the abovementioned ions are also required for cell growth. Consequently, these contaminants can be produced intentionally and be detectable on the surface in the range of greater than 0.1%, preferably greater than 1% and particularly greater than 3%, and have a positive influence on bone growth.
The very nanostructures occurring in this process appear to generally promote the wetting behavior of the ceramic body or, when used as a dental implant, to promote the protein accretion and collagen and cell bonding. Chemical characteristics of the surface in the micrometer range and in the nanometer range also play a substantial role here (e.g. hydrophilic or hydrophobic, doped or pure, etc.). In the present case, an advantage of the ceramic or implant surfaces produced or prepared using the method according to the invention which is especially important for oral implantology appears to consist particularly in the fact that they have a markedly hydrophilic nature which is not lost even after long-term contact of the implant body with the Earth's atmosphere, for example.
The contact angle which a drop of liquid wetting the surface forms with the surface can be used as a measure of hydrophilic character. As has been shown, the ceramic surfaces treated according to the novel method lead to a decidedly good wettability with contact angles of less than 10°, particularly with water. This means that drops of liquid on the surface have the shape of a very flat spherical cap. In addition, the thus-expressed hydrophilic nature of the produced metal bodies remains durably intact even over a time period of more than a few days.
The dental implant, and its ceramic body in particular, is preferably manufactured using a specifically selected method. For this purpose, an implant base body is preferably used as the ceramic base body which is provided with a microstructured, preferably sandblasted, laser-treated and/or etched surface. The implant surface of the dental implant manufactured in this manner has a multitude of irregularly arranged but statistically approximately homogeneously distributed pores with a roughness depth of ca. 0.5 μm to 20 μm on the one hand, but craters with a diameter of 0.5 μm to ca. 60 μm are produced on the other hand which have a roughness depth of less than 4 μm and particularly less than 2 μm and additionally have the described nanoscopic structure. Dental implants designed in this manner strongly support and accelerate the healing process occurring after the implantation through stimulation of the activity of the bone-forming cells, the osteoblasts. Even so, the manufacturing process for the implant is comparatively simple and cost-effective to carry out and control, even on an industrial scale. The process parameters are preferably selected such that a nanostructure of the above-described type forms on the surface of the implant base body superimposed on the microstructure.
The ceramic body is preferably embodied as a bone implant, especially preferably as a dental implant, preferably of a zirconium oxide-based ceramic, a zirconium oxide-containing ceramic or an aluminum oxide-containing ceramic, advantageously with a microstructured surface, with a nanostructure being superimposed on the microstructure and with nitrogen atoms and/or oxygen compounds being preferably accumulated in the area of the surface.
The advantages attained with the invention consist particularly in the fact that, by means of a chemical process that is simple and cost-effective to carry out, a ceramic body, particularly for use as a dental implant, with a nanostructure and a nano-roughness can be manufactured which has an advantageous effect on the healing process after anchoring of the implant in the jawbone and, particularly, also affects the attainable strength of the bond between bone and implant. Through the doping of foreign atoms, particularly nitrogen atoms, into the implant surface, the effect can be amplified even more. What is more, by virtue of the nano-scale surface structure of the ceramic body with regard to the hydrophilic characteristics and/or capillary effects associated therewith, liquids can be introduced especially simply and effectively into the surface. This could be used, for example, to place medications or other agents or reagents on the surface. However, other advantageous applications are also conceivable due to the good wettability, with the application of lacquers, adhesives or other surface coatings onto the ceramic body being facilitated considerably, for example.
The especially favorable hydrophilic behavior of the treated surface obtained through the obtained nanostructure or nano-roughness can be recognized, for example, through the thereby-obtained characteristic wetting angle, which is particularly less than 15°. In addition, as a result of the nanopores, nanostructures, the doping or accretion of nitrogen atoms/compounds on and/or at the surface, the thus-obtained hydrophilic behavior lasts comparatively longer than in a ceramic surface that has been chemically activated.
Sample embodiments of the invention are explained in further detail on the basis of a drawing.
The post element 2 and the mounting element 4 can also be embodied as a single-piece variant.
The post element 2 is anchored in an appropriately-prepared implant bed of the jawbone. The thread construction ensures a high level of primary stability and a uniform transfer into the jawbone of the forces occurring during masticatory stress. Moreover, the bone is intended to grow as directly as possible against the implant during the healing phase following the implantation and connect closely therewith. This process, known as osseointegration, is improved considerably through a targeted roughening of the implant surface.
To produce this roughening, an appropriately-selected treatment is provided. Through an appropriate etching process, for example in an appropriately-selected acid bath, the depletion zone in the surface of the ceramic body is produced which is characterized by a lower proportion of selected materials in comparison to the internal volume of the ceramic body, particularly of yttrium used for the stabilization of the zirconium oxide, and consequently also by a lower proportion of the crystallographic monocline phase. This results in the very favorable surface roughnesses on a nanoscopic and microscopic scale shown in
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2007/005681 | 6/27/2007 | WO | 00 | 3/27/2009 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2008/011948 | 1/31/2008 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4330891 | Branemark et al. | May 1982 | A |
| 4876148 | Virkar | Oct 1989 | A |
| 4950294 | Hakamatsuka | Aug 1990 | A |
| 5222983 | Schmitz et al. | Jun 1993 | A |
| 5250352 | Tyszblat | Oct 1993 | A |
| 5603338 | Beaty | Feb 1997 | A |
| 6380113 | Kim et al. | Apr 2002 | B1 |
| 6974625 | Hunter et al. | Dec 2005 | B2 |
| 7858192 | Zhang et al. | Dec 2010 | B2 |
| 20020072807 | Nawa et al. | Jun 2002 | A1 |
| 20030029910 | Goretta et al. | Feb 2003 | A1 |
| 20040152034 | Cummings et al. | Aug 2004 | A1 |
| 20050106534 | Gahlert | May 2005 | A1 |
| 20050119758 | Alexander | Jun 2005 | A1 |
| 20050187638 | Wilfried et al. | Aug 2005 | A1 |
| 20050266270 | Lasater | Dec 2005 | A1 |
| 20060147880 | Krumsiek et al. | Jul 2006 | A1 |
| 20080213726 | Schlottig et al. | Sep 2008 | A1 |
| 20090220561 | Jin et al. | Sep 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| 202005002450 | Jul 2005 | DE |
| 1450722 | Sep 2004 | EP |
| 1777206 | Apr 2007 | EP |
| WO 2004 096075 | Nov 2004 | WO |
| WO 2005027771 | Mar 2005 | WO |
| WO 2005070322 | Aug 2005 | WO |
| Entry |
|---|
| Kohal et al., “Loaded custom-made zirconia and titanium implants show similar osseointegration: an animal experiment,” Journal of periodontology, Sep. 2004, vol. 75, No. 9, pp. 1262-1268. |
| Bone tissue response to surface-modified zirconia implants: a histomorphometric and removal torque study in the rabbit, Clinical implant dentistry and related research, 2005, vol. 7 supplement 1, pp. S12-S20. |
| Oh et al. “Significantly accelerated osteoblast cell growth on aligned TiO2 nanotubes”, Apr. 6, 2006, Journal of Biomedical Materials Research, vol. 78A, issue 1, pp. 97-103. |
| Ilavsky et al, “Phase composition and its changes during annealing of plasma-sprayed YSZ”, 2000, Surface and Coatings Technology 127 (2000) 120-129. |
| International Search Report prepared by the European Patent Office dated Nov. 5, 2007, for International Application No. PCT/EP2007/005681. |
| International Preliminary Report on Patentability prepared by the European Patent Office dated Nov. 5, 2007, for International Application No. PCT/EP2007/005681. |
| Written Opinion for International (PCT) Application No. PCT/EP2007/005681, dated Nov. 5, 2007. |
| Number | Date | Country | |
|---|---|---|---|
| 20090258327 A1 | Oct 2009 | US |