Surface-modified effect pigment and nail varnish composition

Abstract
The invention relates to a surface-modified effect pigment comprising particular additives and to the production thereof. The present invention further provides a nail varnish composition comprising a) at least one effect pigment that has been surface-modified with a starting material (additive), where the effect pigment comprises a substrate in platelet form and optionally at least one coating applied to the substrate, b) at least one hydrocarbon resin as binder, and c) at least one solvent or solvent mixture, where the starting material (additive) for surface modification of the effect pigment is at least one compound taken from the group consisting of phosphoric ester-containing, phosphonic ester-containing, phosphonic acid-containing, fatty acid-containing and/or silane-containing compounds or mixtures thereof.
Description

The present invention relates to a surface-modified effect pigment and to a process for production thereof and to nail varnish compositions comprising said surface-modified effect pigment.


EP 1 812 518 A2 discloses pearlescent pigments provided with at least one phosphorus compound on the surface. The pearlescent pigments are especially suitable for use in powder coatings.


EP 2 227 508 A1 describes metal effect pigments coated with at least one metal oxide layer, wherein the surface of the metal oxide layer includes at least one fluoroalkyl- and/or fluoroaryl-containing surface modifier or covalently bonded polysiloxane. The metal effect pigments are especially employed in powder coatings.


EP 2 318 463 A1 discloses metal effect pigments coated with at least one metal oxide layer, wherein the surface of the metal oxide layer includes covalently bonded polysiloxane. The metal effect pigments are especially suitable for use in powder coatings.


EP 2 576 702 A1 relates to the use of surface-modified effect pigments especially in powder coatings. The effect pigment surface here has been surface-modified with at least one compound containing epoxy groups.


EP 1 462 085 A1 discloses a nail varnish composition with a mirror effect which comprises particles having metallic luster in a proportion of ≥2% by weight, based on the total weight of the nail varnish composition. EP 1 462 085 A1 does not disclose any surface-modified effect pigments.


EP 1 299 066 A2 describes a nail varnish comprising aluminum platelets and having a mirror-like appearance. According to EP 1 299 066 A2, the nail varnish has to comprise nitrocellulose having a molecular weight of >56 000 as film former for a mirror-like effect to be achievable on a fingernail. Nevertheless, the mirror effects achievable thereby are limited and in need of improvement.


EP 1 746 913 A2 discloses a flexible article comprising at least one bonding layer for fixing of the article on a fingernail, at least one organic film and at least one component responsible for an optical effect, for example. The latter may serve, for example, to impart a mirror effect to the flexible article.


EP 1 792 598 A1 describes a nail varnish having specular gloss, which comprises colloidal precious metal particles having an average particle size of 10 to 100 nm in a proportion of 5% to 50% by weight, based on the total weight of the nail varnish.


EP 1 796 794 A1 discloses a cosmetic composition comprising a PVD aluminum pigment at a pigmentation level of 0.05% to 5.0% by weight, based on the total weight of the cosmetic composition, and at least one leafing additive. Leafing additives used are long-chain phosphoric esters or a mixture of multiple long-chain phosphoric esters. However, the leafing effect is not fully manifested in most nail varnishes.


EP 1 082 952 A1 discloses a cosmetic composition, for example a nail varnish, comprising metal-coated glass particles.


JP 2012081236 A discloses the securing of a mirror on a fingernail.


EP 2 248 514 A2 describes nitrocellulose-free nail varnish compositions comprising at least one styrene/maleic anhydride copolymer as high-gloss film former, at least one epoxy resin as co-film former, at least one reactive component and at least one solvent.


The nitrocellulose-free nail varnish composition is said to have comparable or better adhesion properties than nitrocellulose-containing nail varnish compositions. In EP 2 248 514 A2, no surface-modified effect pigments are used as colorants.


It is an object of the present invention to provide an effect pigment for use in a nail varnish composition which is crucial in determining the visual appearance of the nail varnish composition after application and drying. In the case of high-quality metal effect pigments, specular gloss and preferably exceptional specular gloss is to be enabled.


More particularly, it is a further object of the present invention to provide a nail varnish composition that enables a good leafing effect of surface-modified effect pigments.


The object underlying the invention is achieved by the provision of a surface-modified effect pigment comprising a metallic substrate in platelet form that has optionally been coated with at least one metal oxide, metal hydroxide and/or metal oxide hydrate or a nonmetallic substrate in platelet form that has optionally been coated with at least one metal oxide, metal hydroxide and/or metal oxide hydrate, wherein

    • a) the metallic substrate in platelet form is produced by wet grinding and has an h50 from a range from 20 nm to less than 100 nm and the starting material (additive) used for surface modification is
      • i) phosphoric acid cetyl ester or cetylphosphoric acid from a range from 2% by weight to less than 40% by weight or
      • ii) phosphoric acid stearyl ester or stearyl phosphate from a range from 5% by weight to less than 20% by weight or
      • iii) phosphonic acids of the formula R—P(O)(OH)2 with R=linear alkyl moiety having a carbon chain from a range from C8 to C14, in a total amount preferably from a range from 4% by weight to 45% by weight, based in each case on the total weight of the optionally coated metallic substrate in platelet form, or
    • b) the metallic substrate in platelet form is produced by PVD methods and has an average thickness h50 from a range from 13 nm to 60 nm and the starting material (additive) used for surface modification is
      • i) phosphoric acid cetyl ester or cetylphosphoric acid from a range from 10% by weight to 50% by weight or
      • ii) phosphoric acid stearyl ester or stearyl phosphate from a range from 13% by weight to 50% by weight or
      • iii) phosphonic acids of the formula R—P(O)(OH)2 with R=linear alkyl moiety having a carbon chain from a range from C8 to C14, in a total amount from a range from 5% by weight to 50% by weight, based in each case on the total weight of the optionally coated metallic substrate in platelet form, or
    • c) the nonmetallic substrate in platelet form has a D50 from a range from 2 μm to 360 μm and the starting material (additive) used for surface modification is
      • i) phosphoric acid cetyl ester or cetylphosphoric acid from a range from 5% by weight to 30% by weight or
      • ii) phosphoric acid stearyl ester or stearyl phosphate from a range from 2% by weight to 25% by weight,
      • based in each case on the total weight of the optionally coated nonmetallic substrate in platelet form, or
    • d) the nonmetallic substrate is a glass platelet that has been coated with metallic silver and has a D50 from a range from 2 μm to 360 μm and an average thickness h50,glass of the glass platelet within a range from 70 nm to 530 nm and an average thickness of the metallic silver coating within a range from 9 nm to 27 nm and the starting material (additive) used for surface modification is
      • i) phosphoric acid cetyl ester or cetylphosphoric acid from a range from 3% by weight to less than 40% by weight or
      • ii) phosphoric acid stearyl ester or stearyl phosphate from a range from 5% by weight to less than 30% by weight or
      • iii) phosphonic acids R—P(O)(OH)2 with R=linear alkyl moiety having a carbon chain from a range from C8 to C14, in a proportion from a range from 15% by weight to 43% by weight, based in each case on the total weight of the silver-coated glass platelet.


The object of the invention is additionally achieved by a process for producing the surface-modified effect pigment, wherein the process comprises the following steps:

    • i. suspending the metallic substrate in platelet form that has optionally been coated with at least one metal oxide, metal hydroxide and/or metal oxide hydrate or the nonmetallic substrate in platelet form that has optionally been coated with at least one metal oxide, metal hydroxide and/or metal oxide hydrate in at least one solvent,
    • ii. adding the phosphoric acid cetyl ester or the phosphoric acid stearyl ester or the phosphonic acid at optionally elevated temperature to the suspension from step i. and stirring the suspension then obtained,
    • iii. filtering, optionally drying, the surface-modified effect pigment obtained in step ii.


The object of the underlying invention is also achieved by the provision of a nail varnish composition comprising


a) at least one effect pigment surface-modified with a starting material (additive), where the effect pigment comprises a substrate in platelet form and optionally comprises at least one coating applied to the substrate,


b) at least one hydrocarbon resin and


c) at least one solvent or solvent mixture,


wherein the starting material (additive) used for surface modification of the effect pigment is at least one compound from the group consisting of phosphoric ester-containing, phosphonic ester-containing, phosphonic acid-containing, fatty acid-containing and/or silane-containing compounds or mixtures thereof.


Preferred developments of the nail varnish composition are specified.


The object is also achieved by provision of a process for producing the nail varnish composition of the invention.


The object of the underlying invention is also achieved by the use of a surface-modified effect pigment in nail varnishes.


The effect pigments surface-modified in accordance with the invention may comprise a metallic substrate in platelet form that is optionally coated with at least one metal oxide, metal hydroxide and/or metal oxide hydrate or a nonmetallic substrate in platelet form that is optionally coated with at least one metal oxide, metal hydroxide and/or metal oxide hydrate.


The metallic substrates in platelet form may be produced via conventional wet or dry grinding or via PVD methods.


The metallic substrates in platelet form may be selected from the group consisting of aluminum platelets, copper platelets, zinc platelets, iron platelets, titanium platelets, stainless steel platelets, silver platelets, alloys and mixtures of the aforementioned metals.


Preferably, the metallic substrates in platelet form are selected from the group consisting of aluminum platelets, copper platelets, zinc platelets, iron platelets, stainless steel platelets, alloys and mixtures of the above-listed metals. The aforementioned metallic substrates in platelet form may also have one or more layers of or comprising at least one metal oxide, metal hydroxide and/or metal oxide hydrate of high and/or low refractive index and may optionally have been dried and/or optionally calcined. For instance, the metallic substrates in platelet form used may thus also be commercially available coated metal effect pigments. In a preferred embodiment, the metallic substrates in platelet form to be used in accordance with the invention have not been coated.


More preferably, the metallic substrates in platelet form are selected from the group consisting of aluminum platelets, copper platelets, zinc platelets, iron platelets, alloys and mixtures of the above-listed metals. Most preferably, the metallic substrates in platelet form are selected from the group consisting of aluminum platelets, copper platelets, zinc platelets, alloys and mixtures of the above-listed metals. Particularly preferably, the metallic substrates in platelet form used are aluminum platelets.


Additionally preferred are aluminum platelets that are produced by PVD methods.


In a preferred embodiment, the metallic substrates in platelet form are PVD pigments, particularly aluminum PVD pigments.


These preferably have an average thickness h50 in a range from 13 nm to 80 nm, further preferably from a range from 13 nm to 60 nm and more preferably in a range from 20 nm to 40 nm.


Below 13 nm, the metallic PVD pigments, especially aluminum pigments, become too dark and too transparent.


Above 80 nm, there is a considerable decline in the optical properties and the hiding power, and a specular gloss is achievable only with difficulty.


If metal effect pigments are used in cosmetic formulations, they have to meet certain purity demands, for example the EU Cosmetic Regulation 1223/2009 or FDA 21CFR part 73.


If, for example, aluminum platelets are used as metallic substrate in platelet form, these preferably have an aluminum content of ≥97% by weight, further preferably of ≥98% by weight, more preferably of ≥99% by weight and most preferably of ≥99.7% by weight, based in each case on the total weight of the aluminum platelet. In a preferred embodiment, the aluminum platelets also have a mercury content of preferably ≤1 ppm, an arsenic content of preferably ≤2 ppm, a lead content of preferably ≤10 ppm, a cadmium content of preferably ≤1 ppm, a barium content of preferably ≤10 ppm, a chromium content of preferably ≤20 ppm, a nickel content of preferably ≤20 ppm, a copper content of preferably ≤20 ppm, a cobalt content of preferably ≤20 ppm, an antimony content of preferably ≤2 ppm, a selenium content of preferably ≤10 ppm and a zinc content of preferably ≤20 ppm.


If copper platelets are used as metallic substrate in platelet form, these preferably have a copper content of ≥95% by weight, further preferably of ≥96% by weight, more preferably of ≥97% by weight and most preferably of ≥98% by weight, based in each case on the total weight of the copper platelet. In a preferred embodiment, the copper platelets also have a mercury content preferably of ≤1 ppm, an arsenic content preferably of ≤3 ppm, a lead content preferably of ≤20 ppm, a cadmium content preferably of ≤15 ppm, a barium content preferably of ≤10 ppm, a chromium content preferably of ≤20 ppm, a nickel content preferably of ≤20 ppm, a cobalt content preferably of ≤20 ppm, an antimony content preferably of ≤2 ppm and a selenium content preferably of ≤10 ppm.


If gold bronze platelets are used as metallic substrate in platelet form, these preferably have a copper content from a range from 70% by weight to 95% by weight, a zinc content from a range from <5% by weight to <30% by weight, an aluminum content from a range from 0.01% by weight to ≤1.5% by weight, a tin content from a range from 0.001% by weight to ≤0.5% by weight, based in each case on the total weight of the gold bronze platelets. In a preferred embodiment, the gold bronze platelets also have a mercury content preferably of ≤1 ppm, an arsenic content preferably of ≤3 ppm, a lead content preferably of ≤20 ppm, a cadmium content preferably of ≤15 ppm, a barium content preferably of ≤10 ppm, a chromium content preferably of ≤20 ppm, a nickel content preferably of ≤20 ppm, a cobalt content preferably of ≤20 ppm, an antimony content preferably of ≤2 ppm and a selenium content preferably of ≤10 ppm.


If iron platelets are used as metallic substrate in platelet form, these are preferably produced from reductively treated carbonyl iron powder according to the main claim of EP 1 251 152 A1.


In a further embodiment, the aluminum or aluminum alloy platelets usable as metallic substrate in platelet form are wet-chemically oxidized according to the main claim of WO 96/38505 A1 and optionally have a metal chalcogenide layer of high refractive index according to the main claim of WO 2005/049739 A2.


In a further embodiment, the surface-modified effect pigments to be used in the nail varnish composition of the invention comprise commercially available leafing aluminum effect pigments, for example Etemabrite Premier 251, Eternabrite Premier 255 or Etemabrite Premier 351, each from Silberline.


In a preferred embodiment, the surface-modified effect pigments for use in the nail varnish composition of the invention comprise, as metallic substrate in platelet form, aluminum platelets produced by PVD methods or metal effect pigments according to the main claim of WO 2010/086165 A1, for example METALURE A41010 AE, METALURE A41506 EN, METALURE A 41510 EN, METALURE A31017 AE, METALURE A31010 BG, METALURE A31010 AE, METALURE A21010 AE, METALURE L55350AE, METALURE L63418, METALURE L 55700, METALURE A 61010 BG, METALURE A61010 AE, METALURE A61006 AE, METALURE A61006 BG, METALURE A41010 BG or METALURE L71011AE, all from ECKART GmbH.


The average thickness h50 of the metallic substrates in platelet form that are optionally to be coated is preferably within a range from 10 nm to 2000 nm, further preferably within a range from 13 nm to 1500 nm, more preferably within a range from 15 nm to 900 nm and most preferably within a range from 18 nm to 600 nm. The average thickness h50 is understood in accordance with the invention to mean the average value of the cumulative distribution curve of the thickness distribution unless stated otherwise.


The determination of h50 was preferably effected by the method described in WO 2004/087816 A2 (pages 24 and 25) by means of SEM.


The h50 of the cumulative frequency distribution of the thickness distribution function as preferably obtained by counting in the SEM states that 50% of the surface-modified effect pigments measured have a thickness less than or equal to the particular value reported.


In further preferred embodiments, metallic substrates in platelet form used are wet-ground aluminum platelets having a span of the thickness distribution Δh=(h90−h10)/h50 from a range from 30% to 140% and preferably from a range from 30% to 70% and most preferably from a range from 30% to 50%. The production of metal effect pigments of this kind is described in WO 2004/087816 A2 or WO 2008/077612 A2, which are hereby incorporated by reference.


In a further embodiment, metallic substrates in platelet form used are copper platelets or gold bronze platelets having a thickness distribution characterized by an h50 of 10 to 50 nm, and an h90 of 20 to 70 nm. The production of metallic effect pigments of this kind can be found in WO 2009/152941 A2.


In a further embodiment, the relative standard deviation of the thickness distribution of the metallic substrates in platelet form is 11% to 98%, preferably 22% to 78%, more preferably 28% to 68% and most preferably 34% to 64%. The relative standard deviation in [%] is the quotient of calculated standard deviation of the thickness distribution and average thickness h50.


The surface-modified effect pigments of the invention, based on metallic, uncoated substrates in platelet form, to be used with preference in a nail varnish composition may optionally have at least one layer composed of or comprising at least one metal oxide, metal hydroxide and/or metal oxide hydrate, where the metal ion is selected from the group of the metals consisting of Al, Si, Sn, Zn, Ti and Fe, preferably selected from the group of the metals consisting of Al and Si. Above-listed metal oxides, metal hydroxides and/or metal oxide hydrates may take the form of (i) separate layers, (ii) mixed metal oxide, mixed metal hydroxide and/or mixed metal oxide hydrate or (iii) be in separate layers on the metallic substrate in platelet form.


The surface-modified effect pigments of the invention, based on metallic substrates in platelet form, to be used preferably in a nail varnish composition, may have any average particle size D50. The D50 values of the surface-modified effect pigments of the invention, based on metallic substrates in platelet form, to be used preferably in a nail varnish composition, are preferably within a range from 2 μm to 150 μm, further preferably within a range from 2.5 μm to 170 μm, further preferably within a range from 3 μm to 140 μm, more preferably within a range from 3.5 μm to 90 μm and most preferably within a range from 3.8 μm to 56 μm. Exceptionally preferably, the surface-modified effect pigments of the invention, based on metallic substrates in platelet form, to be used with preference in a nail varnish composition have a D50 from a range from 2.5 μm to 14 μm or from a range from 15 μm to 35 μm. Below 2 μm there is a distinct decrease in gloss values, and above 150 μm no uniformly continuous metallic surface is obtained.


Preferably, the metallic substrates in platelet form that have been produced by wet grinding and have an average thickness h50 below 100 nm have a D50 from a range from 8 μm to 25 μm.


The D10 values of the surface-modified effect pigments of the invention, based on metallic substrates in platelet form, to be used with preference in a nail varnish composition are preferably within a range from 1 μm to 60 μm, further preferably within a range from 2 μm to 40 μm, more preferably within a range from 4 μm to 31 μm and most preferably within a range from 5 μm to 19 μm. Below 1 μm there is a distinct decrease in gloss values, and above 60 μm no uniformly continuous metallic surface is obtained.


The D90 values of the surface-modified effect pigments of the invention, based on metallic substrates in platelet form, to be used with preference in a nail varnish composition are preferably within a range from 10 μm to 600 μm, further preferably within a range from 30 μm to 200 μm, more preferably within a range from 40 μm to 150 μm and most preferably within a range from 45 μm to 120 μm. Below 10 μm there is a distinct decrease in gloss values, and above 600 μm no uniformly continuous metallic surface is obtained.


In one embodiment, the surface-modified effect pigments of the invention, based on metallic substrates in platelet form, to be used preferably in a nail varnish composition, have a span ΔD, defined as








Δ

D

=



D
90

-

D
10



D
50



,





from a range from 0.7 to 2.5, preferably from a range from 0.8 to 2.2, further preferably from a range from 0.9 to 1.9, more preferably from a range from 0.9 to 1.8 and most preferably from a range from 1 to 1.7.


In a further embodiment, the surface-modified effect pigments of the invention, based on metallic substrates in platelet form, to be used with preference in a nail varnish composition have an aspect ratio, defined as the quotient of D50 and average thickness, preferably from a range from 10 to 2000, further preferably from a range from 30 to 1200, more preferably from a range from 100 to 1100 and most preferably from a range from 200 to 1000. Below the lower limits the optical properties of the metallic effect pigments are still insufficient for achievement of specular gloss, and above 2000 the metallic effect pigments are producible only with great difficulty.


In a further embodiment, the surface-modified effect pigments of the invention, based on metallic substrates in platelet form, to be used preferably in a nail varnish composition, preferably have an average total thickness h50 from a range from 20 nm to 4000 nm, further preferably from a range from 30 nm to 3000 nm, more preferably from a range from 70 nm to 2000 nm and most preferably from a range from 230 nm to 1300 nm.


Average total thickness is understood to mean the complete average thickness of the surface-modified effect pigment, i.e. metallic substrate in platelet form plus optional coating plus surface modification.


In a preferred embodiment, the surface-modified effect pigments of the invention that are to be used preferably in a nail varnish composition, comprise as metallic substrate in platelet form, metal platelets produced by a PVD method having a D50 from a range from 2.5 μm to 90 μm, further preferably from a range from 8 μm to 25 μm, and an average thickness from a range from 13 nm to 60 nm. In this embodiment, the aluminum platelets are preferably not coated. The oxide layer naturally present on aluminum platelets is not regarded here as an applied coating.


Surprisingly, it is also possible to achieve specular gloss effects with very small PVD pigments. These pigments can be produced, for example, by further grinding standard PVD pigments or comminuting them by the action of ultrasound.


More preferably, these metal platelets are aluminum platelets.


More preferably, these aluminum PVD pigments have a D50 within in a range from 6 μm to 18 μm and an average thickness within a range from 14 nm to 40 nm. Most preferred are aluminum PVD pigments having a D50 within a range from 7 μm to 16 μm and an average thickness within a range from 15 nm to 35 nm.


In further embodiments, wet-ground metal platelets and especially aluminum platelets having a similar average thickness to PVD pigments are used.


Thus, preference is given to wet-ground metal platelets and especially aluminum platelets having an average thickness h50 from a range from 20 to less than 100 nm and most preferably an average thickness h50 from a range from 25 to 60 nm.


Metal effect pigments of this kind can also be used to achieve specular gloss effects, although metal pigments produced by PVD methods generally give even better results.


The nonmetallic substrates in platelet form may be selected from the group consisting of natural mica platelets, synthetic mica platelets, glass platelets, SiO2 platelets, Al2O3 platelets, kaolin platelets, talc platelets and bismuth oxychloride platelets.


The surface-modified effect pigments of the invention that are to be used with preference in a nail varnish composition or the surface-modified effect pigments may also be based on mixtures of the above-specified nonmetallic substrates in platelet form.


The aforementioned nonmetallic substrates in platelet form may also have one or more layers composed of or comprising at least one metal oxide, metal hydroxide and/or metal oxide hydrate of high and/or low refractive index and may have been calcined. For instance, substrates used may thus also be pearlescent pigments or interference pigments.


Preferably, the nonmetallic substrates in platelet form are selected from the group consisting of natural mica platelets, synthetic mica platelets, glass platelets, SiO2 platelets, Al2O3 platelets and mixtures thereof. More preferably, the nonmetallic substrates in platelet form are selected from the group consisting of natural mica platelets, synthetic mica platelets, glass platelets and mixtures thereof. Most preferred nonmetallic substrates in platelet form are synthetic mica platelets and/or glass platelets. Glass platelets in particular are preferred as nonmetallic substrate in platelet form.


The glass platelets usable as nonmetallic substrate in platelet form may, with regard to their composition, consist of silicate glass, such as soda-lime glass, lead crystal glass, E glass, A glass, C glass, ECR glass, Duran glass, window glass, laboratory glass, aluminosilicate glass or borosilicate glass. The glass platelets preferably have a composition corresponding to the teaching, especially corresponding to the main claim, of EP 1 980 594 B1, more preferably corresponding to the teaching, especially corresponding to the respective main claims, of EP 1 829 833 B1 or of EP 2 042 474 B1. The glass platelets usable as nonmetallic substrate in platelet form are preferably produced by the process described in EP 289 240 B1.


In one embodiment, the glass platelets can be specifically colored through the addition of at least one inorganic colorant in the production thereof. Suitable colorants are those that do not break down at the respective melting temperature of the glass composition. The total proportion of colorant here is preferably within a range from 0.1% by weight to 20% by weight, more preferably within a range from 0.2% by weight to 15% by weight and most preferably within a range from 0.5% by weight to 10% by weight, based in each case on the total weight of the glass composition. Suitable colorants are especially elemental precious metals, such as Au, Pd or Pt, the cations or complex anions of the elements Cu, Cr, Mn, Fe, Ti and/or Co, and mixtures of the above-listed colorants.


In a further embodiment, the refractive index of the glass platelets usable as nonmetallic substrate in platelet form is within a range from 1.45 to 1.80, preferably within a range from 1.50 to 1.70.


In a further embodiment, the nonmetallic substrates in platelet form, especially glass platelets, may have been coated with a layer comprising or consisting of silicon oxide, silicon hydroxide, silicon oxide hydrate. For example, the aforementioned coating, in the case of use of glass platelets, can protect the glass surface from chemical alteration, such as swelling, leaching of glass constituents or dissolution in aggressive acidic coating solutions.


The synthetic mica platelets usable as nonmetallic substrate in platelet form may have a composition according to the main claim of CN 102718229 A or according to the main claim of US 2014/0251184 A1. They may additionally be produced according to the details in EP 0 723 997 A1, page 3 to page 4.


The synthetic mica platelets usable as nonmetallic substrate in platelet form are preferably fluorphlogopite platelets of the formula KMg3AlSi3O10F2, KMg2½(Si4O10)F2 or NaMg2½(Si4O10)F2, especially fluorphlogopite platelets of the formula KMg3AlSi3O10F2, which, according to x-ray fluorescence analysis (XRF), preferably have the constituents specified in table 1 in the form of the respective metal oxide within the ranges listed therein.









TABLE 1





Preferred compositions of synthetic mica


platelets according to XRF analysis


Composition of synthetic mica platelets, figures


in % by weight, based in each case on the total


weight of the synthetic mica platelets


















SiO2
38 to 46



Al2O3
10 to 14



K2O
 9 to 13



Fe2O3
0.01 to 0.25



MgO
26 to 34



MnO
  0 to 0.05



Na2O
 0 to 13










The average thickness h50 of the nonmetallic substrates in platelet form that are optionally to be coated is preferably within a range from 50 nm to 5000 nm, more preferably within a range from 60 nm to 3000 nm and most preferably within a range from 70 nm to 2000 nm.


In one embodiment, the average thickness h50,glass for glass platelets as nonmetallic substrate in platelet form which is optionally to be coated is within a range from 750 nm to 1500 nm, preferably within a range from 850 nm to 1400 nm and more preferably within a range from 900 nm to 1300 nm.


Thinner nonmetallic substrates in platelet form lead to a lower total thickness of the surface-modified effect pigments of the invention that are to be used with preference in a nail varnish composition and optionally to be coated, or of the surface-modified effect pigments.


Thus, likewise preferred as nonmetallic substrate in platelet form are glass platelets having an average thickness h50,glass within a range from 50 nm to 700 nm, further preferably within a range from 101 nm to 600 nm, more preferably within a range from 160 nm to 500 nm and most preferably within a range of 200 nm to 400 nm.


In a further embodiment, the average thickness h50,glass of the natural or synthetic mica platelets as nonmetallic substrate in platelet form which is optionally to be coated is preferably within a range from 80 nm to 1300 nm, further preferably within a range from 90 nm to 1000 nm, more preferably within a range from 99 nm to 800 nm and most preferably within a range from 200 nm to 600 nm.


If nonmetallic substrates in platelet form below an average thickness h50 of 50 nm are coated with metal oxides of high refractive index, for example, extremely fracture-sensitive effect pigments are obtained that can break up even on incorporation into the respective application medium, which in turn causes significant lowering of the gloss.


Above an average thickness of the nonmetallic substrate in platelet form of 5000 nm, the effect pigments overall can become too thick. This is associated with poorer specific hiding capacity, meaning that the area covered per unit weight of effect pigment is lower. Moreover, such thick effect pigments have a lower degree of plane-parallel orientation to the substrate in the application medium. Poorer orientation in turn results in reduced gloss. With regard to tactile properties too, excessively thick effect pigments can be disadvantageous overall in any application.


In one embodiment, the relative standard deviation of the thickness distribution of the nonmetallic substrates in platelet form is 15% to 100%, preferably 17% to 70%, more preferably 19% to 61% and most preferably 21% to 41%. The relative standard deviation in [%] is the quotient of calculated standard deviation and average thickness h50.


The nonmetallic substrates in platelet form may optionally be coated with at least one metal oxide, metal hydroxide and/or metal oxide hydrate. This optional coating may have at least one layer of high refractive index and/or at least one layer of low refractive index. A layer of high refractive index is understood to mean a layer having a refractive index of n≥1.8, preferably of n≥2.0 and more preferably of n≥2.2. A layer of low refractive index is understood to mean a layer having a refractive index of n<1.8 and preferably of n<1.6. For classification into layers of high and low refractive index, refractive indices known from literature are employed.


The optionally present coating may comprise at least one layer of high refractive index composed of or comprising at least one metal oxide, metal hydroxide and/or metal oxide hydrate, where the metal ion is selected from the group of metals consisting of Ti, Fe, Sn, Mn, Zr, Ca, Sr, Ba, Ni, Ag, Zn, Cu, Ce, Cr and Co, preferably selected from the group of metals consisting of Ti, Fe, Sn, Zr, Ag, Zn, Cu, Ce and Cr, and more preferably selected from the group of metals consisting of Ti, Fe and Sn. Above-listed metal oxides, metal hydroxides and/or metal oxide hydrates may take the form of (i) a mixed layer or (ii) a mixed metal oxide, mixed metal hydroxide and/or mixed metal oxide hydrate, preferably of an iron titanate, such as ilmenite, pseudobrookite or pseudorutile, or (iii) be present in separate layers on the nonmetallic substrate in platelet form.


Alternatively or additionally to the aforementioned at least one layer of high refractive index, the coating optionally present may comprise at least one layer of low refractive index composed of or comprising at least one metal oxide, metal hydroxide and/or metal oxide hydrate, where the metal ion is selected from the group of metals consisting of Si, Al and B. If layers of high and low refractive index are present in the coating optionally present, these are preferably present alternately.


In one embodiment, the at least one layer of high refractive index and/or the at least one layer of low refractive index may have been doped, where the doping may comprise metal oxides, metal hydroxides and/or metal oxide hydrates wherein the metal ion is selected from the group of metals consisting of Al, Ce, Zr and Sn, preferably consisting of Al, Zr and Sn. The total proportion of doping is preferably ≤1% by weight, more preferably ≤0.5% by weight and most preferably ≤0.2% by weight, based in each case on the total weight of the surface-modified effect pigments.


In a further embodiment, the coating optionally present may, alternatively or additionally to the layer comprising at least one metal oxide, metal hydroxide and/or metal oxide hydrate, comprise at least one semitransparent metal layer. The metals of the semitransparent metal layer may be selected from the group consisting of Ag, Al, Cr, Ni, Au, Pt, Pd, Cu, Zn and Ti, preferably selected from the group consisting of Ag, Au and Cu. The semitransparent metal layer may of course also comprise alloys or mixtures of the above-listed metals. The average thickness of the semitransparent metal layer is preferably within a range from 1 nm to 30 nm, more preferably within a range from 4 nm to 26 nm and more preferably within a range from 7 nm to 21 nm.


In a preferred embodiment, the nonmetallic substrates in platelet form include at least one of the above-described layers, more preferably at least one layer composed of or comprising metal oxides, metal hydroxides and/or metal oxide hydrates of high refractive index.


In a further embodiment, the surface-modified effect pigments of the invention that are to be used with preference in a nail varnish composition or the surface-modified effect pigments, based in each case on nonmetallic substrates in platelet form, have a span ΔD, defined as








Δ

D

=



D
90

-

D
10



D
50



,





from a range from 0.7 to 2.0, preferably from a range from 0.7 to 1.5, further preferably from a range from 0.8 to 1.3, more preferably from a range from 0.8 to 1.2 and most preferably from a range from 0.85 to 1.1.


The advantages of a narrow size classification in relation to color purity and/or gloss of the resulting effect pigments are described, for example, in EP 2 217 664 A1, EP 2 346 950 A1, EP 2 356 181 A1. EP 2 346 949 A1, EP 2 367 889 A1.


The surface-modified effect pigments of the invention, based on nonmetallic substrates in platelet form, to be used preferably in a nail varnish composition, have an average particle size D50 from a range from 2 μm to 360 μm. The D50 values of the surface-modified effect pigments of the invention, based on nonmetallic substrates in platelet form, to be used with preference in a nail varnish composition are preferably within a range from 3 μm to 350 μm, further preferably within a range from 4 μm to 211 μm, further preferably within a range from 6 μm to 147 μm, more preferably within a range from 7 μm to 99 μm and most preferably within a range from 8 μm to 56 μm. Exceptionally preferably, the surface-modified effect pigments of the invention, based on nonmetallic substrates in platelet form, to be used with preference in a nail varnish composition have a D50 value from a range from 3 to 15 μm or from a range from 10 to 35 μm or from a range from 25 to 45 μm or from a range from 30 to 65 μm or from a range from 40 to 140 μm or from a range from 135 to 250 μm.


The D10 values of the surface-modified effect pigments of the invention, based on nonmetallic substrates in platelet form, to be used with preference in a nail varnish composition are preferably within a range from 1 to 120 μm. More preferably, the D10 values of the surface-modified effect pigments of the invention, based on nonmetallic substrates in platelet form, to be used preferably in a nail varnish composition are within a range from 1 μm to 5 μm or within a range from 5 μm to 25 μm or within a range from 10 μm to 30 μm or within a range from 20 μm to 45 μm or within a range from 25 μm to 65 μm or within a range from 75 to 110 μm.


The D90 values of the surface-modified effect pigments of the invention, based on nonmetallic substrates in platelet form, to be used with preference in a nail varnish composition are preferably within a range from 6 to 500 μm. More preferably, the Do values of the surface-modified effect pigments of the invention, based on nonmetallic substrates in platelet form, to be used preferably in a nail varnish composition are within a range from 8 μm to 250 μm or within a range from 10 μm to 150 μm or within a range from 40 μm to 70 μm or within a range from 68 μm to 110 μm or within a range from 120 μm to 180 μm or within a range from 400 μm to 490 μm.


In a particularly preferred embodiment, the surface-modified effect pigments for use in a nail varnish composition comprise, as nonmetallic substrate in platelet form, glass platelets having a D50 from a range from 9 μm to 390 μm, an average thickness from a range from 90 nm to 590 nm, preferably from a range from 110 nm to 340 nm, a glass composition according to the main claim of WO 2007/148758 A1 or of WO 2010/024283 A1 and a semitransparent layer composed of or comprising metallic silver.


The average thickness of the metallic or nonmetallic substrate in platelet form that has been coated with a metal oxide, metal hydroxide and/or metal oxide hydrate and the average total thickness of the surface-modified effect pigment is determined using a cured paint film in which the surface-modified effect pigments of the invention that are to be used preferably in a nail varnish composition are aligned essentially plane-parallel to the substrate. For this purpose, a cross section of the cured paint film is examined under a scanning electron microscope (SEM) to determine the thickness of the metallic or nonmetallic substrate in platelet form or the total thickness of the surface-modified effect pigment for at least 100 surface-modified effect pigments and find the statistical average. According to the invention, the term “average” always means the h50, unless stated otherwise.


In the case of surface-modified effect pigments of the invention that are to be used with preference in a nail varnish composition and have not been coated with a metal oxide, metal hydroxide and/or a metal oxide hydrate, the average thickness h50 is preferably determined by the method described in WO 2004/087816 A2 (pages 24 and 25) by means of SEM.


The D10, D50 and D90 values of the cumulative frequency distribution of the volume-averaged size distribution function as obtained by laser diffraction methods mean that, respectively, 10%, 50% and 90% of the surface-modified effect pigments analyzed have a volume-averaged diameter of less than or equal to the value specified in each case.


In this context, the size distribution curve of the surface-modified effect pigments of the invention that are to be used with preference in a nail varnish composition and of the surface-modified effect pigments, based in each case on nonmetallic substrates in platelet form, are determined with the Malvern Mastersizer 2000 instrument according to the manufacturer's instructions. The scattered light signals are evaluated by the Fraunhofer theory, which also includes refraction and absorption characteristics of the particles. The size distribution curve of the surface-modified effect pigments of the invention that are to be used with preference in a nail varnish composition and of the surface-modified effect pigments, based in each case on metallic substrates in platelet form, are ascertained with the Quantachrome Cilas 1064 instrument or the Horiba LA-930 instrument.


The scattered light signals are evaluated by the Fraunhofer theory, which also includes refraction and absorption characteristics of the particles.


It has been found that the effect pigments surface-modified in accordance with the invention do not show good results in all nail varnish systems as disclosed, for example, in EP 1796794 B2. Frequently, the leafing effect is lost on application or thereafter, with the associated effect that the optical properties of the effect pigments are not fully manifested.


Therefore, an essential constituent of the present invention is the provision of a nail varnish in which the leafing properties of the surface-modified effect pigments are very well manifested.


The invention is therefore also directed to a nail varnish composition comprising


a) at least one effect pigment surface-modified with a starting material (additive), where the effect pigment is a substrate in platelet form and optionally comprises at least one coating applied to the substrate,


b) at least one hydrocarbon resin and


c) at least one solvent or solvent mixture,


wherein the starting material (additive) used for surface modification of the effect pigment is at least one compound from the group consisting of phosphoric ester-containing, phosphonic ester-containing, phosphonic acid-containing, fatty acid-containing and/or silane-containing compounds or mixtures thereof.


The phosphoric esters and/or phosphoric acids and/or phosphonic esters and/or phosphonic acids usable for surface modification may be phosphoric esters of the general formula (R—O)n—P(O)(OR′)(OR″)m or phosphonic esters of the general formula R—P(O)(OR)(OR″) where the R, R′ and R″ moieties are preferably defined as follows: R=linear and/or branched alkyl moiety having a carbon chain from a range from C10 to C20 and R′═R″═H, linear and/or branched alkyl moiety having a carbon chain from a range from C1 to C6, preferably C1 to C3, where R′ and R″ may be identical or different and where n=1 or 2 and m=n−1 and n+m=2.


In this context, with regard to the number n, it is possible for either pure forms of the monoesters (n=1) or diesters (n=2) or mixtures thereof to be present.


In a particularly preferred embodiment, surface modification of the effect pigments for use in a nail varnish composition of the invention is accomplished using primary phosphoric acids or phosphonic acids with R=linear unsubstituted alkyl moiety having a carbon chain from a range from C12 to CIS, preferably from a range from C14 to C18 and R′═R″═H. Further preferably in this context, n=1 (monoester).


A preferred phosphonic acid is laurylphosphonic acid and preferred phosphoric acids are cetyl phosphate or stearyl phosphate.


Surface modification can be accomplished using, for example, 2-ethylhexylphosphoric ester (CAS: 12645-31-7), laurylphosphoric ester (CAS: 12751-23-4), cetylphosphoric ester (CAS: 3539-43-3), stearylphosphoric ester (CAS: 39471-52-8) and/or monoethylmono-(9Z)-9-octadecenylphosphoric ester (CAS: 10483-96-2).


Particular preference is given to cetylphosphoric ester, stearylphosphoric ester or laurylphosphoric ester and particular preference is given to cetylphosphoric ester or stearylphosphoric ester and very particular preference is given to cetylphosphoric ester.


The fatty acids usable for surface modification may be fatty acids of the general formula R—COOH where the R moiety is preferably defined as follows:

  • i. R=linear and/or branched alkyl moiety having a carbon chain from a range from C12 to C26, preferably from a range from C14 to C24, further preferably from a range from C16 to C22 and more preferably from a range from C18 to C20; or
  • ii. R=linear and/or branched alkenyl moiety having a carbon chain from a range from C12 to C26, preferably from a range from C14 to C24, further preferably from a range from C16 to C22 and more preferably from a range from C18 to C20; or
  • iii. R=linear and/or branched alkynyl moiety having a carbon chain from a range from C12 to C26, preferably from a range from C14 to C24, further preferably from a range from C16 to C22 and more preferably from a range from C18 to C20.


In a preferred embodiment, surface modification of the effect pigments usable in a nail vanish composition of the invention is accomplished using fatty acids with R=linear unsubstituted alkyl moiety having a carbon chain from a range from C12 to C20, preferably from a range from C14 to C18.


The silanes usable for surface modification may be silanes of the general formula R—Si(OR′)3 where the R and R′ moieties are preferably defined as follows:


R=linear and/or branched alkyl moiety having a carbon chain from a range from C6 to C23, preferably from a range from C7 to C20, more preferably from a range from C8 to C18 and R′=linear and/or branched alkyl moiety having a carbon chain from a range from C1 to C4, preferably from a range from C1 to C and more preferably from a range from C1 to C2, where the alkyl moiety R in further embodiments may comprise at least one substituent selected from the group consisting of —OH, —OCH3, —OC2H5, —NH2, linear and/or branched alkyl moiety having a carbon chain from a range from C1 to C6.


For production of the surface-modified effect pigments of the invention for use with preference in a nail varnish composition, the starting material (additive) for surface modification is preferably used in an amount from a range from 1.5% by weight to 50% by weight, more preferably from a range from 3.2% by weight to 40% by weight and most preferably from a range from 4.8% by weight to 23% by weight, based in each case on the total weight of the effect pigment used.


Since the amounts of the additive specified here are based on the starting material, the actual amount of additive in the ready-coated effect pigment may be smaller since, for example, in the case of an amount of 50% by weight, not all the additive can be absorbed onto the pigment surface. Accordingly, it is also possible for smaller amounts of the leafing additives to be found in the applications comprising the pigments, especially in nail varnishes.


The effect of the quite high amounts of additive in the starting material is very high and dense coating of the effect pigment surface with the additive.


In a particularly preferred embodiment, the starting material (additive) used for surface modification of effect pigments based on metallic substrates in platelet form that have been produced by wet grinding and have an average substrate thickness h50 from a range from 20 nm to 100 nm is at least one phosphonic acid of the formula R—P(O)(OH)2 with R=linear alkyl moiety having a carbon chain from a range from C8 to C14, in a total amount preferably from a range from 4% by weight to 45% by weight, further preferably from a range from 5% by weight to 43% by weight, more preferably from a range from 6% by weight to 42% by weight and most preferably from a range from 9% by weight to 41% by weight, based in each case on the total weight of the effect pigment used.


In a further particularly preferred embodiment of the invention, the starting material (additive) used for surface modification of effect pigments based on metallic substrates in platelet form that have been produced by PVD methods and have an average substrate thickness h50 from a range from 13 nm to 60 nm is at least one phosphonic acid of the formula R—P(O)(OH)2 with R=linear alkyl moiety having a carbon chain from a range from C8 to C14, in a total amount from a range from 5% by weight to 50% by weight, further preferably from a range from 6% by weight to 48% by weight, more preferably from a range from 7% by weight to 45% by weight and most preferably from a range of 10% by weight to 42% by weight, based in each case on the total weight of the effect pigment used.


Insufficient leafing of the effect pigments takes place below the specified amounts of phosphonic ester. Above the specified amounts of phosphonic ester, it is possible for excessively large amounts of the phosphonic acids to be introduced into the finished nail varnish composition.


In this context, it is particularly preferable that the effect pigments are coated with the phosphonic ester in a separate step before they are introduced into the nail varnish system.


In a further preferred embodiment, the starting material (additive) used for surface modification of effect pigments based on metallic substrates in platelet form that may have been produced by wet grinding or via PVD methods, having an average substrate thickness from a range from 20 nm to 90 nm, is at least one fatty acid in a total amount from a range from preferably 4% by weight to 28% by weight, further preferably from a range from 4% by weight to 25% by weight, more preferably from a range from 6% by weight to 20% by weight and most preferably from a range from 8% by weight to 17% by weight, based in each case on the total weight of the effect pigment used.


In a further preferred embodiment, the starting material (additive) used for surface modification of effect pigments based on metallic substrates in platelet form that may have been produced by wet grinding or via PVD methods, having an average substrate thickness from a range from 20 nm to 90 nm, is at least one silane in a total amount preferably from a range from 5% by weight to 39% by weight, further preferably from a range from 10% by weight to 35% by weight, more preferably from a range from 15% by weight to 32% by weight and most preferably from a range from 18% by weight to 30% by weight, based in each case on the total weight of the effect pigment used.


In very particularly preferred embodiments, at least one phosphoric ester and/or at least one phosphoric acid of the formula (R—O)n—P(O)(OR′)(OR″)m where each R=linear alkyl moiety having a carbon chain from a range from C14 to C18, and where R′ and R″ are each independently H, CH3, C2H5 or C3H8 and where n=1 or 2 and m=n−1 and n+m=2, in a total amount from a range from 14% by weight to 40% by weight, based on the total weight of the effect pigment used, are used as starting material (additive) for surface modification of effect pigments based on metallic substrates in platelet form that have been produced by PVD methods, having an average substrate thickness h50 from a range from 15 nm to 40 nm, preferably 20 to 40 nm. Further preferably, in this context, R′═R″═H. In addition, it is particularly preferable that n=1.


In very particularly preferred embodiments, at least one phosphoric ester and/or a phosphoric acid of the formula (R—O)n—P(O)(OR′)(OR″)m where each R=linear alkyl moiety having a carbon chain from a range from C14 to C18, and where R′ and R″ are independently H, CH3, C2H5 or C3H8, and where n=1 or 2 and m=n−1 and n+m=2, in a total amount from a range from 14% by weight to 31% by weight, based on the total weight of the effect pigment used, are used as starting material (additive) for surface modification of effect pigments based on metallic substrates in platelet form that have been produced by wet grinding, having an average substrate thickness from a range from more than 40 nm to 90 nm, preferably from 45 nm to 80 nm. Further preferably, in this context, R′═R″═H. In addition, it is particularly preferable that n=1.


In further-preferred embodiments, at least one fatty acid R—COOH with R=linear alkyl moiety having a carbon chain from a range from C15 to C19 in a total amount from a range from 11% by weight to 15% by weight, based on the total weight of the effect pigment used, is used as starting material (additive) for surface modification of effect pigments based on metallic substrates in platelet form having an average substrate thickness from a range from 20 nm to 90 nm, and/or


at least one silane R—Si(OR′)3 with R=linear alkyl moiety having a carbon chain from a range from C14 to C20 in a total amount from a range from 21% by weight to 29% by weight, based on the total weight of the effect pigment used, is used for surface modification of effect pigments based on metallic substrates in platelet form having an average substrate thickness from a range from 20 nm to 90 nm.


According to the invention, “total amount” is understood to mean the complete amount of starting material (additive), irrespective of whether the starting material is exclusively at least one phosphoric ester or exclusively at least one phosphonic ester or a mixture of at least one phosphoric ester and at least one phosphonic ester or a mixture of different phosphonic acids or a mixture of different fatty acids or a mixture of different silanes.


The surface-modified effect pigments of the invention may find use in cosmetic formulations, especially in nail varnish compositions. A particular feature of the surface-modified effect pigments in nail varnish compositions is their excellent leafing characteristics.


Nail Varnish Composition of the Invention:


The invention is further directed to a nail vanish composition that enables and maintains the leafing effect of the effect pigments in an excellent manner.


This nail vanish composition of the invention comprises:

  • a) at least one effect pigment surface-modified with a starting material (additive), where the effect pigment comprises a substrate in platelet form and optionally comprises at least one coating applied to the substrate,
  • b) at least one hydrocarbon resin as binder and
  • c) at least one solvent or solvent mixture,


wherein the starting material (additive) used for surface modification of the effect pigment is at least one compound from the group consisting of phosphoric ester-containing, phosphonic ester-containing, phosphonic acid-containing, fatty acid-containing and/or silane-containing compounds or mixtures thereof.


The nail varnish composition of the invention comprising at least one surface-modified effect pigment, by contrast with most commercially available nail varnish compositions, preferably does not include any nitrocellulose. The visual appearance of the nail varnish composition of the invention, after application and drying, is determined to a crucial degree by the at least one surface-modified effect pigment.


The nail varnish composition of the invention comprises the at least one surface-modified effect pigment preferably in a proportion from a range from 0.3% by weight to 8.5% by weight, further preferably from a range from 0.5% by weight to 5.0% by weight, more preferably from a range from 0.6% by weight to 3.0% by weight and most preferably from a range from 0.8% by weight to 1.9% by weight, based in each case on the total weight of the nail varnish composition.


In a particularly preferred embodiment, the nail varnish composition of the invention comprises at least one surface-modified, optionally coated aluminum pigment, where the surface-modified aluminum pigment has a D50 from a range from 5 μm to 100 μm, preferably from a range from 2 μm to 60 μm, and the average thickness of the aluminum platelet is within a range from 10 nm to 100 nm, preferably within a range from 20 nm to nm. In this embodiment, the starting material (additive) used for surface modification of the optionally coated aluminum pigment is preferably at least one phosphoric ester R—O—P(O)(OR′)(OR″) with R=linear alkyl moiety having a carbon chain from a range from C14 to C18, R′═R″═H in a proportion from a range from 10% by weight to 50% by weight, based on the total weight of the effect pigment used. The nail varnish composition of the invention here comprises the above-described surface-modified, optionally coated aluminum pigment preferably in a proportion from a range from 0.6% by weight to 3.0% by weight, more preferably from a range from 0.8% by weight to 1.9% by weight, based in each case on the total weight of the nail varnish composition.


Below the amounts of the specific substances to be used as starting material (additive) for surface modification that are specified for the effect pigments surface-modified in accordance with the invention or the various above-described effect pigment/additive combinations for the respective different types of effect pigment, insufficient leafing of the effect pigments takes place.


Above the amounts of the additives specified in each case, excessively large amounts of the additives may possibly be introduced into the finished nail varnish composition.


It is particularly preferable here that the effect pigments are coated with the additive in a separate step before they are introduced into the nail varnish system.


A preferred process for producing the surface-modified effect pigments of the invention therefore comprises the following steps:

    • i. suspending the metallic substrate in platelet form that has optionally been coated with at least one metal oxide, metal hydroxide and/or metal oxide hydrate or the nonmetallic substrate in platelet form that has optionally been coated with at least one metal oxide, metal hydroxide and/or metal oxide hydrate in at least one solvent,
    • ii. adding the phosphoric acid cetyl ester or the phosphoric acid stearyl ester at optionally elevated temperature to the suspension from step i. and stirring the suspension then obtained,
    • iii. filtering, optionally drying, the surface-modified effect pigment obtained in step ii.


The solvent used is preferably a solvent compatible with the nail varnish of the invention. Particular preference is given to using butyl acetate.


In the case of PVD metal pigments or in the case of particularly thin metal pigments produced by wet grinding, the drying step iii. will be dispensed with and these pigments will instead be left in a dispersion.


A portion of the additives used will not adhere to the surface of the effect pigment as the surface is already saturated. For high and uniform coverage, however, it is important to provide sufficient amounts of additive since only then can a strong leafing effect be expected.


In the nail varnish compositions of the invention, the surface-modified effect pigments preferably adopt an ordered arrangement at the surface of the clearcoat, i.e. of the nail varnish composition of the invention without surface-modified effect pigments. According to the invention, “adopt an ordered arrangement at the surface” means that the surface-modified effect pigments, on the nail varnish base and/or proceeding from the nail varnish composition/air or nail varnish composition/overcoat interface, are in the third of the nail varnish composition that adjoins this interface in the direction of the varnished substrate. Preferably, the surface-modified effect pigments float in the clearcoat and become aligned at the clearcoat surface. The surface-modified effect pigments therefore show marked leafing characteristics in the nail varnish composition of the invention.


Due to these marked leafing characteristics of the surface-modified effect pigments, it is possible in accordance with the invention to produce nail varnish compositions that owe their visual appearance mainly to the at least one surface-modified effect pigment added to the nail varnish base. Depending on the at least one surface-modified effect pigment, nail varnish compositions which, after application and drying, are notable for their metallic character, their mother-of-pearl-like shimmer, their interference color, a color change at different viewing angles, intense sparkle effects and/or silky appearance, to name just a few effects achievable by way of example, are thus obtainable in a simple manner. It is of course possible, according to the visual effect to be achieved, to also add various surface-modified effect pigments to the nail varnish composition, it being possible here for both the surface modification and the effect pigments to be different from one another. “Effect pigments different from one another” are also understood to mean effect pigments that are identical by nature, for example aluminum pigments, but differ from one another in terms of their particle size, for example.


A peculiarity that should also be mentioned in the case of use of surface-modified effect pigments based on aluminum platelets or based on metallic silver-coated nonmetallic substrates in platelet form is that it is possible thereby to obtain, after application and drying, nail varnish compositions having specular gloss. In the ideal case, the nail varnish compositions of the invention in that case have, after application and drying, such high image sharpness that a viewer is virtually able to view a mirror image therein.


According to the invention, “specular gloss” is understood to mean that the nail varnish composition, after application to glass plates by means of a bar applicator (Erichsen System Wasag Model 288 film applicator, from Erichsen) in a wet film thickness of 110 μm and after subsequent drying at room temperature, has at least 120 gloss units, measured in the 20° geometry (Byk-Gardner, digital catalog “Qualitätskontrolle für Lacke und Kunststoffe” [Quality Control for Paints and Plastics], page 16) and at least 1100 haze units (H log). According to the invention, excellent specular gloss is understood to mean achievement of at least 150 gloss units, measured in the 20° geometry (Byk-Gardner, digital catalog “Qualitätskontrolle für Lacke und Kunststoffe”, page 16) and at least 1100 haze units (H log). The gloss and haze units (H log) are preferably determined here with the haze-gloss instrument, from Byk-Gardner. If the nail varnish applications of the invention have microscopically small structures, light is scattered thereon close to the reflection angle, which reduces the image sharpness of the nail varnish applications. Gloss (20° geometry) and haze are preferably not considered independently of one another in the assessment of specular gloss. The higher the numerical value of the gloss units in the 20° geometry, the lower the numerical value of the haze units (H log) can be or vice versa; the higher the numerical value of the haze units (H log), the lower the numerical value of the gloss units in the 20° geometry can be in order still to be perceived as specular gloss by the human eye. The higher the numerical value of the gloss units in the 20° geometry and the higher the numerical value of the haze units (H log), the higher the visually perceptible image sharpness of the nail varnish application.


In a very preferred embodiment, the nail varnish compositions of the invention, after application to glass plates by means of a bar applicator (Erichsen System Wasag Model 288 film applicator, from Erichsen) in a wet film thickness of 110 μm and after subsequent drying at room temperature, have at least 200 gloss units, preferably at least 300 gloss units, more preferably at least 400 gloss units, most preferably at least 450 to 1500 gloss units, in each case measured in the 20° geometry, and at least 1200 haze units (H log), preferably at least 1300 haze units (H log), more preferably at least 1400 haze units (H log) and most preferably at least 1410 to 2000 haze units (H log). In this embodiment too, in the case of a relatively low numerical value of the gloss units, measured in the 20° geometry, preference is given to a relatively high numerical value of the haze units (H log).


In a preferred embodiment, the nail varnish compositions of the invention which, after application and drying, feature excellent specular gloss contain 0.4% by weight to 2.7% by weight, preferably 0.5% by weight to 1.8% by weight, based in each case on the total weight of the nail varnish composition, of surface-modified effect pigments based on aluminum platelets, where the aluminum platelets have a D50 from a range from 2 μm to 500 μm, preferably from a range from 2.5 μm to 90 μm, and an average thickness from a range from 15 nm to 1000 nm, preferably from a range from 18 nm to 60 nm.


In a particularly preferred embodiment, the nail varnish compositions of the invention which, after application, feature excellent specular gloss contain 0.6% by weight to 4.9% by weight, preferably 0.3% by weight to 3.8% by weight, based in each case on the total weight of the nail varnish composition, of surface-modified effect pigments based on aluminum platelets, where the aluminum platelets have a D50 from a range from 5 μm to 150 μm, preferably from a range from 10 μm to 60 μm, and an average thickness from a range from 10 nm to 600 nm, preferably from a range from 20 nm to 100 nm.


In a preferred embodiment, the nail varnish compositions of the invention after application to a glass plate by means of a bar applicator (Erichsen System Wasag Model 288 film applicator, from Erichsen) in a wet film thickness of 100 μm and subsequent drying at room temperature, have at least 200 gloss units, measured in the 20° geometry, and at least 1200 haze units (H log).


In a preferred embodiment, the nail varnish composition of the invention comprises at least one surface-modified effect pigment in a proportion from a range from 0.1% by weight to 8.4% by weight, preferably in a proportion from a range from 0.15% by weight to 6.9% by weight, more preferably in a proportion from a range from 0.2% by weight to 4.3% by weight, based in each case on the total weight of the nail varnish composition, of at least one hydrocarbon resin and at least one solvent.


In a further preferred embodiment, the nail varnish composition of the invention comprises at least one surface-modified effect pigment based on a metallic substrate in platelet form, where the effect pigment has an average particle size D50 from a range from 2 μm to 60 μm and an average total thickness from a range from 10 nm to 150 nm.


Binder:


The nail varnish compositions of the invention comprise at least one hydrocarbon resin as binder, where the binder preferably has a binder solids content from a range from 25% by weight to 64% by weight, further preferably from a range from 25% by weight to 60% by weight, further preferably from a range from 28% by weight to 55% by weight, more preferably from a range from 29% by weight to 50% by weight and most preferably from a range from 35% by weight to 43% by weight, based in each case on the total weight of the nail varnish composition.


Below a binder content of 25% by weight, no good optical effects resulting from the effect pigments were any longer apparent in the nail varnish applied.


Above 60% by weight, the optical quality of the effect pigments likewise declines and the viscosity of the nail varnish compositions of the invention increasingly becomes too high.


The nail varnish compositions of the invention preferably comprise, as binder, hydrocarbon resins having an average molecular weight (Mw) from a range from 800 to 6000, preferably from a range of 900 to 5000, or from a range from 8000 to 10000, preferably from a range from 8500 to 9300. Average molecular weight MW was determined by means of gel permeation chromatography (GPC) with a polystyrene standard.


Hydrocarbon resins are understood to mean synthetic resins that form through reaction of hydrocarbons (excluding olefins) with themselves in the presence of aluminum chloride or sulfuric acid as catalyst. Hydrocarbon resins are subdivided in accordance with their structure into petroleum resins, terpene resins and coumarone-indene resins. Also counted among the hydrocarbon resins are the reaction products of xylene and formaldehyde, the xylene-formaldehyde resins.


Hydrocarbon resins are produced in a known manner by heating high-boiling fractions from gasoline pyrolysis (pyrolysis oil) or the isoprene-free C5 fraction from gasoline pyrolysis in the presence of aluminum chloride. The hydrocarbon resins are soluble in most organic solvents, for example esters, ethers, hydrochlorocarbons and aromatics.


Without being bound to a theory, the inventors suspect that, in the case of use of polar binders, the effect pigments coated with suitable additives are still partly wetted by the binder and therefore do not have the desired leafing effect. By contrast, the resins in the nail varnish composition of the invention are very nonpolar and accordingly do not wet the effect pigments. As a result, the effect pigments can better develop the leafing effect.


In preferred embodiments, nail varnish compositions comprising aromatic hydrocarbon resins are used.


The nail varnish compositions of the invention may comprise, as binder, hydrocarbon resins such as, for example, Kristalex F100 Hydrocarbon Resin, Kristalex 5140 Hydrocarbon Resin, Kristalex 3070 Hydrocarbon Resin, Kristalex 3085 Hydrocarbon Resin, Kristalex F115 Hydrocarbon Resin, each from Eastman.


Preferably, the nail varnish compositions of the invention comprise, as binder, hydrocarbon resins Kristalex F100 Hydrocarbon Resin and Kristalex 5140 Hydrocarbon Resin.


In particularly preferred embodiments, the nail varnish composition of the invention contains hydrocarbon resin in an amount that makes up 80% to 100% by weight, further preferably 90% to 99% by weight, of the overall organic binder.


The use of hydrocarbon resins in nail varnishes as a main constituent of the binder is unusual to the inventors' knowledge. Hydrocarbon resins are usually very rare constituents of nail varnishes and, if they are used, they are used in comparatively small proportions with other binders.


In a particularly preferred embodiment, the nail varnish compositions of the invention comprise at least two different hydrocarbon resins having a first average molecular weight MW of 1200 to 1600 g/mol and a second average molecular weight MW of 4500 to 5500 g/mol in a weight ratio of 1:1 to 1:10, preferably 1:1 to 1:8, more preferably 1:1 to 1:4 and most preferably 1:1 to 1:2 of the two different hydrocarbon resins.


In further embodiments, the nail varnish composition contains virtually no additional binders, if any, from the group of nitrocellulose, polyester resins, polyvinyl resins, alkyd resin, epoxy resins or cellulose acetate butyrate. These binders are preferably present in proportions of below 10% by weight, further preferably below 5% by weight and more preferably of below 1% by weight and most preferably below 0.1% by weight, based in each case on the total weight of hydrocarbon resins and additional binders. These binders have been found to be a hindrance if anything to the achievement of a truly strong mirror effect.


Without being bound to a theory, the inventors suspect that, in nail varnish compositions that contain the abovementioned binders, these at least partly wet the effect pigments owing to their stronger polarity and as a result they have poorer leafing properties.


Solvent:


The nail varnish compositions of the invention preferably contain particular solvents. Solvents added to the nail varnish compositions of the invention may be ethyl acetate, butyl acetate, isopropanol.


Preferably, the nail varnish composition of the invention contains a mixture of isopropanol, ethyl acetate and butyl acetate as solvent.


More preferably, the nail varnish composition of the invention contains the solvent mixture of isopropanol, ethyl acetate and butyl acetate in an amount which makes up 70% to 100% by weight, further preferably 75% to 98% by weight, based on the total solvent in the nail varnish composition.


It is unimportant here whether these preferred solvents are introduced by the binders or the effect pigment dispersion.


In further preferred embodiments, in this solvent mixture, the ratio of butyl acetate to the solvent mixture is 50% to 99% by weight and more preferably 55% to 98.5% by weight.


In a further particularly preferred embodiment, the proportion of isopropanol is below 20% by weight, preferably below 15% by weight, and further preferably below 10% by weight, based in each case on the total solvent.


Excessively high proportions of isopropanol in the nail varnish composition of the invention lead to a poor visual appearance of the effect pigments. This is probably attributable to excessively rapid drying of the nail varnishes after application thereof.


In a further particularly preferred embodiment, the nail varnish composition of the invention comprises at least one surface-modified effect pigment based on a metallic substrate in platelet form, at least two different hydrocarbon resins, and the solvents ethyl acetate, butyl acetate, isopropanol.


The nail varnish compositions of the invention are applicable in an extremely simple manner to a human or synthetic fingernail and/or toenail. During application, they are notable for good leveling and, after subsequent drying, form a homogeneous film on a human or synthetic fingernail and/or toenail.


In preferred embodiments, the nail varnish of the invention contains 50% by weight to 70% by weight, preferably 55% by weight to 68% and more preferably 57% to 65% by weight of solvent, based in each case on the weight of the overall nail varnish.


Below 55% by weight, there is an excessively significant rise in the viscosity of the nail varnish and the effect pigments are unable to adopt an optimal orientation, which leads to a reduction in up to loss of specular gloss.


Above 70% by weight, there is a reduction in the viscosity of the nail varnish, which leads to poorly controllable application of the nail varnish to the fingernail.


Further Constituents:


The nail varnish compositions of the invention may additionally contain one or more further constituents. Particular mention should be made here of plasticizers and antioxidants.


Plasticizers used may, for example, be glycols and derivatives thereof, for example diethylene glycol ethyl ether, diethylene glycol methyl ether, diethylene glycol butyl ether or additionally diethylene glycol hexyl ether, ethylene glycol ethyl ether, ethylene glycol methyl ether, ethylene glycol butyl ether, ethylene glycol hexyl ether, glycol esters, derivatives of propylene glycol and especially propylene glycol phenyl ether, propylene glycol diacetate, dipropylene glycol butyl ether, tripropylene glycol butyl ether, propylene glycol methyl ether, dipropylene glycol ethyl ether, tripropylene glycol methyl ether and diethylene glycol methyl ether, propylene glycol butyl ether, or mixtures thereof.


In addition, plasticizers used may especially be esters of carboxylic acids, for example of citrates, especially trimethyl citrate, tributyl citrate, trimethylacetyl citrate, tributylacetyl citrate, tri-2-ethylhexyl acetyl citrates or of phthalates, especially dimethoxyethyl phthalate; or of phosphates, especially tricresyl phosphate, tributyl phosphate, triphenyl phosphate, tributoxyethyl phosphates or of tartrates, especially dibutyl tartrate; adipates, carbonates, sebacates; benzyl benzoate, butyl acetyl ricinoleate, glyceryl acetyl ricinoleate, butyl glycolate, camphor, glycerol triacetate, N-ethyl-o,p-toluenesulfonamide, oxyethylene compounds, for example oxyethylene oils, especially vegetable oils, for example castor oil, hydrocarbon oils and mixtures thereof.


Preferred plasticizers are especially hydrocarbon oils.


The proportions by weight of the plasticizers in the overall nail varnish composition are preferably a range from 0% to 15% by weight, further preferably from 1% to 10% by weight, and more preferably from 5% to 10% by weight.


Antioxidants:


The nail varnish composition of the invention may additionally contain one or more antioxidants.


“Antioxidants” are understood to mean compounds that protect the constituents of the nail varnish of the invention, especially the hydrocarbon binders, from the effect of oxygen, heat, ozone and/or UV radiation. It is possible to use one or more compounds of this kind.


Examples of compounds of this kind are IRGANOX® 1010, IRGANOX® 565, IRGANOX® 1076 (from BASF) or sulfur-containing antioxidants, for example zinc dibutyldithiocarbamate (PERKACIT ZDBC (from Performance additives Italy S.p.A)).


The antioxidants are preferably used in amounts from a range from 0% to 5% by weight, further preferably from a range from 0.05% to 1% by weight, based on the overall nail varnish composition.


Further Additives:


The nail varnish composition of the invention may additionally contain customary further additives as known to those skilled in the art.


Further additives of this kind are, for example, antisettling agents, preservatives, oils, waxes, free-moiety scavengers, wetting additives, dispersing aids, wetting aids, antifoams, perfume, neutralizing agents, thickeners, UV blockers, humectants, vitamins, proteins and mixtures thereof.


In further embodiments, the nail varnish composition of the invention preferably does not contain any antisettling agents. Astonishingly, any surface-modified effect pigment that has settled out can generally be redispersed by simply shaking even without the addition of antisettling agents.


The nail varnish composition of the invention preferably has a viscosity of 10 sec to 16 sec, measured with a DIN flow cup (DIN 4 mm) according to DIN 53211.


In preferred embodiments, the nail varnish composition of the invention contains aluminum PVD effect pigments having an average thickness h50 from a range from 14 to nm, preferably from a range from 15 to 35 nm, which have been coated with phosphoric acid cetyl ester or laurylphosphonic acid as leafing additive, aromatic hydrocarbon resins as binder and a mixture of isopropanol, ethyl acetate and butyl acetate as solvent, where this solvent mixture makes up 70% to 100% by weight of the total solvent in the nail varnish composition.


In a further preferred embodiment, the nail varnish composition of the invention contains aluminum PVD effect pigments having an average thickness h50 from a range from 14 to nm, preferably from a range from 15 to 35 nm, and also at least two different aromatic hydrocarbon resins and a mixture of isopropanol, ethyl acetate and butyl acetate as solvent, where this solvent mixture makes up 70% to 100% by weight of the total solvent in the nail varnish composition. Here too, leafing additives used are preferably phosphoric acid cetyl ester or laurylphosphonic acid.


The invention further provides a process for producing the nail varnish composition of the invention, comprising the steps of


i) surface-modifying the effect pigment by means of an additive in a dispersion in a solvent,


ii) dissolving the hydrocarbon resin in a solvent or solvent mixture,


iii) mixing and homogenizing the dispersion according to i) with the binder solution according to ii).


Preference is given here to executing step i).


The dissolving of the hydrocarbon resin in a solvent is preferably effected in a mixture of at least two, preferably three, solvents. Particular preference is given to using a mixture of isopropanol, ethyl acetate and butyl glycol.


In further preferred embodiments, the solvent in step i) will likewise consist of isopropanol, ethyl acetate and butyl glycol or a mixture of these, in order not to introduce further, possibly disruptive solvents into the nail varnish.


It is further preferable, in the selection of the metallic effect pigments, to choose those that are in a paste or a dispersion of the preferred solvents isopropanol, ethyl acetate and butyl glycol, since the solvent in the metal effect pigment paste likewise gets into the nail varnish of the invention in small amounts unless complex rewetting steps are used.


The invention likewise provides a method of coating a natural or synthetic fingernail, comprising the steps of:


a) coating the natural or synthetic fingernail with a nail varnish composition of the invention and then drying the nail varnish,


b) optionally subsequently coating the nail varnish with a clearcoat.


The application of the clearcoat considerably increases the abrasion resistance of the nail varnish. Owing to the marked leafing effect of the effect pigments in the nail varnish, it naturally has comparatively low abrasion resistance.


Step a) may likewise be preceded by coating of the natural or synthetic fingernail with a clearcoat in order to establish a very even surface. This course of action is advisable if the fingernails have high roughness.


The subsequent coating with clearcoat in step b) can be conducted with the same clearcoat as or a different clearcoat than the nail varnish of the invention. However, this clearcoat in no case contains effect pigments since these would cover over the desired effect of the nail varnish of the invention.


However, the clearcoat in step b) may contain conventional color pigments or dyes. Specifically in combination with metallic PVD aluminum pigments or with thin aluminum effect pigments produced by wet grinding and having an h50 of 20 to below 100 nm, it is possible to achieve very visually appealing effects. In this case, the nail varnish compositions of the invention that have been pigmented with the effect pigments preferably have specular gloss after step a).


In a further embodiment, the nail varnish composition of the invention may be overcoated with a low-viscosity UV-curing clearcoat in order to increase the abrasion resistance of the nail varnish composition of the invention.


It is also possible with preference to use solvent-based clearcoats. Without being bound to a theory, the clearcoat is preferably based on polar binders that interact only to a minor degree with the hydrocarbon resins of the clearcoat of the invention. In particularly preferred embodiments, these clearcoats are based on binders such as polyvinyl butyral (PVB), polyvinylpyrrolidone (PVP) or mixtures thereof.


In addition, the clearcoat preferably contains solvents that do not (partly) dissolve the nonpolar hydrocarbon resins of the varnish of the invention. For example, isopropanol may be used for this purpose. Otherwise, the leafing effect pigments can also be partly dissolved again and their orientation can be disrupted, which disrupts the specular gloss effect.


Surprisingly, the clearcoats of the invention have very good bond strength on the nail varnish of the invention.


In a further aspect of the invention, the surface-modified effect pigments can be used in further cosmetic applications.


Examples of these include body powders, face powders, pressed or loose powders, powder creams, eye makeup, for example eyeshadow, mascara, eyeliner, liquid eyeliner, eyebrow pencil, lip pencil, lipstick, lip gloss, lip liner, hairstyling compositions such as hairspray, hair mousse, hair gel, hair wax, hair mascara, permanent or semipermanent hair dyes, temporary hair dyes or skincare compositions such as lotions, gels, emulsions.


The surface-modified effect pigments of the invention are combined here with raw materials, auxiliaries and active ingredients suitable for the respective application. The total concentration of surface-modified effect pigments of the invention in the cosmetic formulation may be between 0.001% by weight for rinse-off products and 40.0% by weight for leave-on products, based in each case on the total weight of the formulation.







EXAMPLES

The examples which follow serve for further description of the invention and are not supposed to be restrictive in any way. All percentages are percentages by weight. The terms NVC (nonvolatile content), proportion of solids and solids content are usable interchangeably.


I Production of the Surface-Modified Effect Pigments of the Invention that are to be Used with Preference in a Nail Varnish Composition and Production of the Surface-Modified Effect Pigments


Examples 1 to 7

In a 1 L jacketed reactor, 300 g of the aluminum effect pigment METALURE A 41010 AE (dispersion in ethyl acetate, solids content 10%, D50 (Horiba LA-930)=9.5 μm to 10.5 μm, from ECKART GmbH) in a solvent according to table 2 below were dispersed at 200 rpm/min and heated to 40° C. Subsequently, the phosphoric acid cetyl ester additive (CAS number: 3539-43-3, Hostaphat CC 100, from Clariant) according to table 2 below, dissolved in 30 g of the solvent used for dispersion, was added to the aluminum effect pigment dispersion. After stirring at 90° C. for 6 hours, the mixture was cooled down and filtered through a Büchner funnel. Surface-modified aluminum effect pigments were obtained in the form of 5-25% dispersions, which, after incorporation into the clearcoat according to IIa (pigmentation level: 0.4% by weight, based on total weight of the clearcoat), application to a synthetic fingernail and subsequent drying, gave a nail varnish having mirror-like gloss.













TABLE 2







Amount of
Amount of
NVC


Example
Solvent
solvent [g]
additive [g]
[%]1)



















1
butyl acetate 85/100
0
3
10


2
butyl acetate 85/100
50
3
9


3
butyl acetate 85/100
100
3
11


4
butyl acetate 85/100
200
3
7


5
butyl acetate 85/100
300
3
23


6
butyl acetate 85/100
300
6
21


7
ethyl acetate
200
5.4
6






1)Nonvolatile content of the surface-modified effect pigment.







Examples 8 to 12

In a 1 L jacketed reactor, 300 g of the aluminum effect pigment METALURE A 41506 EN (dispersion in ethanol, solids content 15%, D50 (Horiba LA-930)=5.5 μm to 6.5 μm, from ECKART GmbH) were dispersed in 300 g of solvent according to table 3 below at 200 rpm/min and heated to 40° C. Subsequently, the additive according to table 3 below in 30 g of the appropriate solvent was added to the aluminum effect pigment dispersion. After stirring at 90° C. for 6 hours, the mixture was cooled down and filtered through a Büchner funnel. Surface-modified aluminum effect pigments were obtained in each case in the form of a 10-20% dispersion, which, after incorporation into the clearcoat according to IIa (pigmentation level: 0.4% by weight, based on total weight of the clearcoat), application to a synthetic fingernail and subsequent drying, gave a nail varnish having mirror-like gloss.













TABLE 3





Ex-


Amount
NVC


ample
Solvent
Additive
[g]
[%]







 8
butyl acetate 85/100
Hostaphat CC 1002)
3
18


 9
butyl acetate 85/100
Hostaphat CC 100
6
15


10
methoxypropanol
Hostaphat CC 100
9
18


11
methoxypropanol
laurylphosphonic acid3)
6
14


12
butyl acetate 85/100
laurylphosphonic acid
6
15






2)Phosphoric acid cetyl ester, CAS number: 3539-43-3, from Clariant.




3)From Rhodia.







Example 13

In a 1 L jacketed reactor, 300 g of the aluminum effect pigment METALURE A 41010 AE (dispersion in ethyl acetate, solids content 10%, D50 (Horiba LA-930)=9.5 μm to 10.5 μm, from ECKART GmbH) were dispersed in 50 g of butyl acetate 85/100 at 200 rpm/min and heated to 80° C. Subsequently, 3 g of the phosphoric acid cetyl ester additive (CAS number: 3539-43-3, Hostaphat CC 100, from Clariant) in 30 g of butyl acetate 85/100 were added to the aluminum effect pigment dispersion. After stirring at 40° C. for 6 hours, the mixture was cooled down and filtered through a Büchner funnel. A surface-modified aluminum effect pigment was obtained in the form of a 15% dispersion, which, after incorporation into the clearcoat according to IIa (pigmentation level: 0.4% by weight, based on total weight of the clearcoat), application to a synthetic fingernail and subsequent drying, gave a nail varnish with mirror-like gloss.


Example 14

In a 1 L jacketed reactor, 300 g of the aluminum effect pigment METALURE A 41010 AE (dispersion in ethyl acetate, solids content 10%, D50 (Horiba LA-930)=9.5 μm to 10.5 μm, from ECKART GmbH) were dispersed in 50 g of butyl acetate 85/100 at 200 rpm/min and heated to 60° C. Subsequently, 3 g of the phosphoric acid cetyl ester additive (CAS number: 3539-43-3, Hostaphat CC 100, from Clariant) in 30 g of butyl acetate 85/100 were added to the aluminum effect pigment dispersion. After stirring at 40° C. for 6 hours, the mixture was cooled down and filtered through a Büchner funnel. A surface-modified aluminum effect pigment was obtained in the form of a 10% dispersion, which, after incorporation into the clearcoat according to IIa (pigmentation level: 0.4% by weight, based on total weight of the clearcoat), application to a synthetic fingernail and subsequent drying, gave a nail varnish with mirror-like gloss.


Examples 15 to 18

In a 1 L jacketed reactor, 300 g of effect pigment according to table 4 below were dispersed in 300 g of solvent according to table 4 below at 200 rpm/min and heated to 90° C. Subsequently, the phosphoric acid cetyl ester additive (CAS number: 3539-43-3, Hostaphat CC 100, from Clariant) in 30 g of the appropriate solvent was added to the effect pigment dispersion. After stirring at 40° C. for 6 hours, the mixture was cooled down and filtered through a Büchner funnel. Surface-modified effect pigments were obtained in each case as a dispersion which, after incorporation into the clearcoat according to IIa (pigmentation level: 0.4% by weight, based on total weight of the clearcoat), application to a synthetic fingernail and subsequent drying, gave a nail varnish, the visual appearance of which was attributable to the effect pigment used in each case.













TABLE 4







Additive

NVC


Example
Effect pigment
[g]
Solvent
[%]







15
SILVERSHINE
3
monopropylene glycol
35



S 15004)

monornethyl ether8)



17
SYNCRYSTAL
3
monopropylene glycol
72



Silk Blue5)

monomethyl ether



17
METALURE A
3
butyl acetate 85/100
12



31017 AE6)





18
METALURE A
6
butyl acetate 85/100
12



31017 AE6)






4)Aluminum effect pigment paste, solids content 23% to 27%, D50 (CILAS 1064) = 12 μm to 18 μm, from ECKART GmbH.




5)Titanium dioxide-coated pearlescent pigment with blue interference color, D50 (Malvern Mastersizer 2000) = 13 μm, from ECKART GmbH.




67)Aluminum effect pigment, dispersion in ethyl acetate, solids content 10%, D50 (Horiba LA-930) = 17 μm, from ECKART GmbH.







Examples 19 to 24

In a 1 L jacketed reactor, 300 g of the aluminum effect pigment METALURE L 55350 AE (dispersion in ethyl acetate, solids content 10%, D50 (Horiba LA-930)=11 μm to 12 μm, from ECKART GmbH) were dispersed in 300 g of solvent according to table 5 below at 200 rpm/min and heated to 40° C. Subsequently, the additive used in each case in 30 g of butyl acetate 85/100 was added to the aluminum effect pigment dispersion. After stirring at 100° C. for 6 hours, the mixture was cooled down and filtered through a Büchner funnel. Surface-modified aluminum effect pigments were obtained in each case in the form of a 11-20% dispersion, which, after incorporation into the clearcoat according to IIa (pigmentation level: 0.4% by weight, based on total weight of the clearcoat), application to a synthetic fingernail and subsequent drying, gave a nail varnish with mirror-like gloss.













TABLE 5








Amount
NVC


Example
Additive
Solvent
[g]
[%]



















19
laurylphosphonic acid
butyl acetate 85/100
3
18


20
laurylphosphonic acid
butyl acetate 85/100
6
18


21
laurylphosphonic acid
monopropylene glycol
6
18.5




monomethyl ether




22
Hostaphat CS 1206)
butyl acetate 85/100
6
15


23
Hostaphat CS 120
butyl acetate 85/100
15
15


24
Hostaphat CC 100
butyl acetate 85/100
3
11.7






6)Phosphoric acid stearyl ester, CAS number: 39471-52-8, from Clariant.







Examples 25 to 31, Comparative Example 1

In a 1 L jacketed reactor, 200 g of Silverdream Moonlight 50IL (solids content 50%, D50 (CILAS 1064)=15 μm to 20 μm, from ECKART GmbH) were dispersed in 525 g of butyl acetate 85/100 at 200 rpm/min and heated to 40° C. Subsequently, the additive used according to table 6 in 30 g of butyl acetate 85/100 was added to the aluminum effect pigment dispersion. After stirring at 90° C. for 6 hours, the mixture was cooled down and filtered through a Büchner funnel. Surface-modified aluminum effect pigments were obtained in the form of a 45-60% dispersion, which, after incorporation into the clearcoat according to IIa (pigmentation level: 0.4% by weight, based on total weight of the clearcoat), application to a synthetic fingernail and subsequent drying, in the case of use of the surface-modified aluminum effect pigments from examples 26 to 32 gave a nail varnish having mirror-like gloss, or in the case of use of the surface-modified aluminum effect pigment from comparative example 1 gave a nail varnish without mirror-like gloss, with a matt aluminum gray hue.












TABLE 6





Example/





comparative example
Additive
Amount [g]
NVC [%]


















Example 25
Hostaphat CC 100
2.5
50


Example 26
Hostaphat CC 100
5
53


Example 27
Hostaphat CC 100
7.5
53


Example 28
Hostaphat CC 100
20
61


Example 29
Hostaphat CS 120
5
55


Example 30
Hostaphat CS 120
10
53


Example 31
Amphisor7)
10
46


Comparative example 1
Hostaphat CS 120
20
58






7)1-Hexadecanol phosphate, 2,2'-iminobis[ethanol] 1:1, CAS 69331-39-1, from DSM.







Comparative Examples 2 to 8

In a 1 L jacketed reactor, 300 g of the aluminum effect pigment METALURE L 55350 AE (dispersion in ethyl acetate, solids content 10%, D50 (Horiba LA-930)=11 μm to 12 μm, from ECKART GmbH) were dispersed in 300 g of butyl acetate 85/100 at 200 rpm/min and heated to 100° C. Subsequently, the additive used according to table 7 in 30 g of butyl acetate 85/100 was added to the aluminum effect pigment dispersion. After stirring at 40° C. for 6 hours, the mixture was cooled down and filtered through a Büchner funnel. Surface-modified aluminum effect pigments were each obtained in the form of a 10-20% dispersion, which, after incorporation into the clearcoat according to IIa (pigmentation level: 0.4% by weight, based on total weight of the clearcoat), application to a synthetic fingernail and subsequent drying, gave a nail varnish without mirror-like gloss, but rather a nail varnish with a matt aluminum gray hue.














TABLE 7







Comparative

Amount
NVC



example
Additive
[g]
[%]





















2
SilCare Silicone41M808)
3
18



3
SilCare Silicone 41M80
15
15



4
Hostaphat KW340 D9)
3
13



5
Hostaphat KW340 D
15
13



6
Hostaphat KL 340 D10)
3
16



7
hostaphat KL 340 D
15
14








8)INCI: C24-28 Alkyl Dimethicone, CAS number: 192230-29-8. from Aako BV or from Clariant.





9)Mono-, di- and tri(alkyl tetraglycol ether) o-phosphoric ester, CAS number: 119415-05-3, from Clariant.





10)Mono-, di- and tri(alkyl tetraglycol ether) o-phosphoric ester, CAS number: 121158-63-2; 121158-61-0; 121158-62-1, from Clariant.







Comparative Examples 9 to 11

In a 1 L jacketed reactor, 300 g of Silverdream Moonlight 50IL (solids content 50%. D50 (CILAS 1064)=15 μm to 20 μm, from ECKART GmbH) were dispersed in 470 g of butyl acetate 85/100 at 200 rpm/min and heated to 90° C. Subsequently, the additive used in table 8 in 30 g of butyl acetate 85/100 was added to the aluminum effect pigment dispersion. After stirring at 40° C. for 6 hours, the mixture was cooled down and filtered through a Büchner funnel. Surface-modified aluminum effect pigments were obtained in the form of a 55-65% dispersion, which, after incorporation into the clearcoat according to IIa (pigmentation level: 1.5% by weight, based on total weight of the clearcoat), application to a synthetic fingernail and subsequent drying, gave a nail varnish without mirror-like gloss and/or without leafing effect.












TABLE 8





Comparative





example
Additive
Amount [g]
NVC [%]


















 8
Hostaphat CK 10011)
7.5
59


 9
Hostaphat CK 100
15
61


10
Hostaphat CK 100
30
59


11
Hostaphat CC 100
75
57






11)Potassium hexadecylhydrogenphosphate, CAS 19035-79-1, Hostaphat CK 100; from Clariant.







Comparative Example 12

PVD aluminum pigment dispersion in ethyl acetate METALURE A-41010 AE, from ECKART GmbH, NVC: 10%, D50=9.50 μm to 10.50 μm.


Comparative Example 13

PVD aluminum pigment dispersion in ethyl acetate METALURE L-55350 AE, from ECKART GmbH. NVC: 10%, D50=11.00 μm to 12.00 μm.


Comparative Example 14

PVD aluminum pigment dispersion in ethyl acetate METALURE A-31017 AE, from ECKART GmbH, NVC: 10%, D50=9.50 to 10.50 μm.


Comparative Example 15

Aluminum pigment paste SILVERSHINE S2100, from ECKART GmbH, NVC: 48.0% to 52.0%, D50=17.0 μm to 23.0 μm.


Comparative Example 16

Mixture of 13% by weight of METALURE A-41010 AE, from ECKART GmbH and 0.2% by weight of Hostaphat CS 120, from Clariant.


II Production of the Nail Varnish Compositions of the Invention


IIa Production of the Clearcoat:


In a suitable stirred vessel, a 70% by weight binder solution F100 was produced. For this purpose, 70 g of the binder Kristalex F100 Hydrocarbon Resin (from Eastman) were added to an initial charge of 30 g of butyl acetate 98/100 while stirring and cooling (12° C.) with the Dispermat CN2 dissolver (from Getzmann GmbH), and then the mixture was stirred at 3000 to 4000 rpm/min for a further 30 minutes.


In a second suitable stirred vessel, a 60% by weight binder solution 5140 was produced. For this purpose, 60 g of the binder Kristalex 5140 Hydrocarbon Resin (from Eastman) were added to an initial charge of 40 g of butyl acetate 98/100 while stirring and cooling (12° C.) with the Dispermat CNf2 dissolver (from Getzmann GmbH), and then the mixture was stirred at 3000 to 4000 rpm/min for a further 30 minutes.


The nonvolatile content (binder solids content) of the above-described binder solutions was determined according to DIN EN ISO 3251:2008.


For production of the clearcoat, the 70% by weight binder solution F100 and the 60% by weight binder solution 5140 were combined according to the table below while stirring at 900 rpm/min with the IKA RW 20 Digital laboratory stirrer (from IKA) at room temperature and stirred for a further 5 to 10 minutes. Subsequently, the solvents according to the respective table below were added successively while stirring at 600 rpm/min.


IIb Production of the Nail Varnish Compositions of the Invention


For production of the inventive nail varnish compositions of examples 32 to 35, 96 g of the clearcoat were added to an initial charge of 4 g of the respective surface-modified effect pigment according to tables 9, 10 and 11 below with stirring at 600 rpm/min.









TABLE 9







The inventive nail varnish compositions of examples 32 to 35 had a


binder solids content of 30% by weight,


based on the total weight of the clearcoat.














Weight



Example

Product name
(g)
Weight ratio














Example
Clearcoat
Kristalex F100
22.3
Kristalex


32

Hydrocarbon Resin, 70%

F100




by weight in butyl acetate

Hydrocarbon




Kristalex 5140
26.0
Resin:




Hydrocarbon Resin, 60%

Kristalex




by weight in butyl acetate

5140




Isopropanol
5.0
Hydrocarbon




Ethyl acetate
18.7
Resin 1:1




Butyl acetate 98/100
28.0





Effect pigment according
4.0





to example 5, NVC: 23%




Example
Clearcoat
Kristalex F100
14.8
Kristalex


33

Hydrocarbon Resin, 70%

F100




by weight in butyl acetate

Hydrocarbon




Kristalex 5140
34.6
Resin:




Hydrocarbon Resin, 60%

Kristalex




by weight in butyl acetate

5140




Isopropanol
4.5
Hydrocarbon




Ethyl acetate
19.0
Resin 1:2




Butyl acetate 98/100
27.5





Effect pigment according
4.0





to example 5, NVC: 23%




Example
Clearcoat
Kristalex F100
8.9
Kristalex


34

Hydrocarbon Resin, 70%

F100




by weight in butyl acetate

Hydrocarbon




Kristalex 5140
41.6
Resin:




Hydrocarbon Resin, 60%

Kristalex




by weight in butyl acetate

5140




Isopropanol
4.5
Hydrocarbon




Ethyl acetate
19.0
Resin 1:4




Butyl acetate 98/100
26.0





Effect pigment according
4.0





to example 5, NVC: 23%




Example
Clearcoat
Kristalex F100
4.8
Kristalex


35

Hydrocarbon Resin, 70%

F100




by weight in butyl acetate

Hydrocarbon




Kristalex 5140
46.3
Resin:




Hydrocarbon Resin, 60%

Kristalex




by weight in butyl acetate

5140




Isopropanol
4.5
Hydrocarbon




Ethyl acetate
17.9
Resin 1:8




Butyl acetate 98/100
26.5





Effect pigment according
4.0





to example 5, NVC: 23
















TABLE 10







The inventive nail varnish compositions of examples 36 to 39


had a binder solids content of 40% by weight,


based on the total weight of the clearcoat.











Ex-


Weight



ample

Product name
(g)
Weight ratio














Ex-
Clear-
Kristalex F100 Hydrocarbon
27.9
Kristalex


ample
coat
Resin, 70% by weight in butyl

F100


36

acetate

Hydrocarbon




Kristalex 5140 Hydrocarbon
32.5
Resin:




Resin, 60% by weight in butyl

Kristalex




acetate

5140




Isopropanol

Hydrocarbon




Ethyl acetate
3.0
Resin 1:1




Butyl acetate 98/100
11.6





Effect pigment according to
25.0





example 5, NVC: 23%
4.0



Ex-
Clear-
Kristalex F100 Hydrocarbon
19.8
Kristalex


ample
coat
Resin, 70% by weight in butyl

F100


37

acetate

Hydrocarbon




Kristalex 5140 Hydrocarbon
46.3
Resin:




Resin, 60% by weight in butyl

Kristalex




acetate

5140




Isopropanol
3.1
Hydrocarbon




Ethyl acetate
12.3
Resin 1:2




Butyl acetate 98/100
18.5





Effect pigment according to
4.0





example 5, NVC: 23%




Ex-
Clear-
Kristalex F100 Hydrocarbon
11.8
Kristalex


ample
coat
Resin, 70% by weight in butyl

F100


38

acetate

Hydrocarbon




Kristalex 5140 Hydrocarbon
55.4
Resin:




Resin, 60% by weight in butyl

Kristalex




acetate

5140




Isopropanol
2.9
Hydrocarbon




Ethyl acetate
11.9
Resin 1:4




Butyl acetate 98/100
20.0





Effect pigment according to
4.0





example 5, NVC: 23%




Ex-
Clear-
Kristalex F100 Hydrocarbon
6.7
Kristalex


ample
coat
Resin, 70% by weight in butyl

F100


39

acetate

Hydrocarbon




Kristalex 5140 Hydrocarbon
61.5
Resin:




Resin. 60% by weight in butyl

Kristalex




acetate

5140




Isopropanol
2.9
Hydrocarbon




Ethyl acetate
11.5
Resin 1:8




Butyl acetate 98/100
17.4





Effect pigment according to
4.0





example 5, NVC: 23%
















TABLE 11







The inventive nail varnish compositions of examples


40 to 43 had a binder solids content of 60% by weight,


based on the total weight of the clearcoat.











Weight






Ex-


Weight
Weight


ample

Product name
(g)
ratio














Ex-
Clear-
Kristalex F100 Hydrocarbon Resin,
42.9
Kristalex


ample
coat
70% by weight in butyl acetate

F100


40

Kristalex 5140 Hydrocarbon Resin,
50.0
Hydro-




60% by weight in butyl acetate

carbon




Isopropanol
0.6
Resin:




Ethyl acetate
2.6
Kristalex




Butyl acetate 98/100
3.9
5140




Effect pigment according to
4.0
Hydro-




example 5, NVC: 23%

carbon






Resin 1:1


Ex-
Clear-
Kristalex F100 Hydrocarbon Resin,
28.6
Kristalex


ample
coat
70% by weight in butyl acetate

F100


41

Kristalex 5140 Hydrocarbon Resin,
66.7
Hydro-




60% by weight in butyl acetate

carbon




Isopropanol
0.4
Resin:




Ethyl acetate
1.7
Kristalex




Butyl acetate 98/100
2.6
5140




Effect pigment according to
4.0
Hydro-




example 5, NVC: 23%

carbon






Resin 1:2


Ex-
Clear-
Kristalex F100 Hydrocarbon Resin,
17.1
Kristalex


ample
coat
70% by weight in butyl acetate

F100


42

Kristalex 5140 Hydrocarbon Resin,
80.0
Hydro-




60% by weight in butyl acetate

carbon




Isopropanol
0.2
Resin:




Ethyl acetate
1.0
Kristalex




Butyl acetate 98/100
1.7
5140




Effect pigment according to
4.0
Hydro-




example 5, NVC: 23%

carbon






Resin 1:4


Ex-
Clear-
Kristalex F100 Hydrocarbon Resin,
9.6
Kristalex


ample
coat
70% by weight in butyl acetate

F100


43

Kristalex 5140 Hydrocarbon Resin,
88.8
Hydro-




60% by weight in butyl acetate

carbon




Isopropanol
0.1
Resin:




Ethyl acetate
0.6
Kristalex




Butyl acetate 98/100
0.9
5140




Effect pigment according to
4.0
Hydro-




example 5, NVC: 23%

carbon






Resin 1:8









The visual appearance of the inventive nail varnish compositions of examples 32 to 43 was determined after application to a synthetic fingernail and subsequent drying by the surface-modified effect pigment from example 5 used in each case. The surface-modified effect pigment used in each case, in the clearcoat produced according to IIa, showed marked leafing characteristics and in some cases marked specular gloss. With regard to application characteristics, it was found that the nail varnish compositions of the invention with a binder solids content of 60% by weight, based on the total weight of the clearcoat, owing to their high viscosity, have poorer applicability than the nail varnish applications of the invention with a binder solids content of 30% by weight or 40% by weight, based in each case on the total weight of the clearcoat.


For the inventive nail varnish compositions of examples 44 to 48, the clearcoat was produced as described below under IIa. For production of the inventive nail varnish compositions of examples 44 to 48, 96 g of the clearcoat were added to an initial charge of 4 g of the respective surface-modified effect pigment according to table 12 below with stirring at 600 rpm/min.













TABLE 12





Pigmen-






tation,


Weight
Weight


samples

Product name
(g)
ratio







Ex-
Clear-
Kristalex F100 Hydrocarbon Resin,
22.3
Kristalex


ample
coat
70% by weight in butyl acetate

F100


44

Kristalex 5140 Hydrocarbon Resin,
26.0
Hydro-




60% by weight in butyl acetate

carbon




Isopropanol
4.7
Resin:




Ethyl acetate
19.0
Kristalex




Butyl acetate 98/100
28.0
5140




Effect pigment according to
4.0
Hydro-




example 5, NVC: 23%

carbon






Resin 1:1


Ex-
Clear-
Kristalex F100 Hydrocarbon Resin,
22.3
Kristalex


ample
coat
70% by weight in butyl acetate

F100


45

Kristalex 5140 Hydrocarbon Resin,
26.0
Hydro-




60% by weight in butyl acetate

carbon




Isopropanol
4.7
Resin:




Ethyl acetate
19.0
Kristalex




Butyl acetate 98/100
28.0
5140




Effect pigment according to
4.8
Hydro-




example 5, NVC: 23%

carbon






Resin 1:1


Ex-
Clear-
Kristalex F100 Hydrocarbon Resin,
22.3
Kristalex


ample
coat
70% by weight in butyl acetate

F100


46

Kristalex 5140 Hydrocarbon Resin,
26.0
Hydro-




60% by weight in butyl acetate

carbon




Isopropanol
4.7
Resin:




Ethyl acetate
19.0
Kristalex




Butyl acetate 98/100
28.0
5140




Effect pigment according to
2.0
Hydro-




example 5, NVC: 23%

carbon






Resin 1:1


Ex-
Clear-
Kristalex F100 Hydrocarbon Resin,
22.3
Kristalex


ample
coat
70% by weight in butyl acetate

F100


47

Kristalex 5140 Hydrocarbon Resin,
26.0
Hydro-




60% by weight in butyl acetate

carbon




Isopropanol
4.7
Resin:




Ethyl acetate
19.0
Kristalex




Butyl acetate 98/100
28.0
5140




Effect pigment according to
7.0
Hydro-




example 5, NVC: 23%

carbon






Resin 1:1


Ex-
Clear-
Kristalex F100 Hydrocarbon Resin,
22.3
Kristalex


ample
coat
70% by weight in butyl acetate

F100


48

Kristalex 5140 Hydrocarbon Resin,
26.0
Hydro-




60% by weight in butyl acetate

carbon




Isopropanol
4.7
Resin:




Ethyl acetate
19.0
Kristalex




Butyl acetate 98/100
28.0
5140




Effect pigment according to
9.0
Hydro-




example 5, NVC: 23%

carbon






Resin 1:1









For the inventive nail varnish compositions of examples 49 to 64, the clearcoat according to table 13 was produced as described above under IIa.









TABLE 13







Clearcoat for examples 49 to 64 and comparative examples 24 to 30












Weight




Product name
(g)
Weight ratio













Clearcoat
Kristalex F100 Hydrocarbon Resin,
19.8
Kristalex F100


for
70% by weight in butyl acetate

Hydrocarbon


examples
Kristalex 5140 Hydrocarbon Resin,
46.3
Resin:


49 to 64
60% by weight in butyl acetate

Kristalex 5140


and
Isopropanol
3.1
Hydrocarbon


comparative
Ethyl acetate
12.3
Resin 1:2


examples
Butyl acetate 98/100
18.5









For production of the inventive nail varnish compositions of examples 49 to 64, the clearcoat from table 13 was added according to table 14 below to an initial charge of the respective surface-modified effect pigment according to table 14, with stirring at 600 rpm/min. The inventive nail varnish compositions of examples 50 to 66 had a binder solids content of 40% by weight, based on the total weight of the clearcoat.









TABLE 14







Weights of effect pigment dispersion and clearcoat for examples 49 to 64.











Weight


Example
Nail varnish composition
(g)












49
Effect pigment according to example 1, NVC: 10%
13.20



Clearcoat from table 13
86.80





50
Effect pigment according to example 15, NVC: 35%
3.80



Clearcoat from table 13
96.20





51
Effect pigment according to example 14, NVC: 10%
14.60



Clearcoat from table 13
85.40





52
Effect pigment according to example 11, NVC: 14%
9.65



Clearcoat from table 13
90.35





53
Effect pigment according to example 12, NVC: 15%
9.65



Clearcoat from table 13
90.35





54
Effect pigment according to example 10; NVC: 18%
7.65



Clearcoat from table 13
92.35





55
Effect pigment according to example 21, NVC: 18.5%
7.36



Clearcoat from table 13
92.64





56
Effect pigment according to example 45, NVC: 11.7%
11.64



Clearcoat from table 13
88.36





57
Effect pigment according to example 17, NVC: 12%
11.44



Clearcoat from table 13
88.56





58
Effect pigment according to example 18, NVC: 12%
11.44



Clearcoat from table 13
88.56





59
Effect pigment according to example 5, NVC: 23%
6.00



Clearcoat from table 13
94.00





60
Effect pigment according to example 26, NVC: 53%
2.60



Clearcoat from table 13
97.40





61
Effect pigment according to example 28, NVC: 61%
2.23



Clearcoat from table 13
97.70





62
Effect pigment according to example 29, NVC: 55%
2.47



Clearcoat from table 13
97.53





63
Effect pigment according to example 25, NVC: 50%
2.72



Clearcoat from table 13
97.28





64
Effect pigment according to example 27, NVC: 53%
2.57



Clearcoat from table 13
97.43









Comparative Examples

For the nail varnish compositions of comparative examples 17 to 20, the clearcoat was produced as described above under IIa. For production of the nail varnish compositions of comparative examples 18 to 20, 96 g of the clearcoat were added to an initial charge of 4 g of the respective surface-modified effect pigment according to table 15 below with stirring at 600 rpm/min.













TABLE 15





Com-






parative


Weight



example

Product name
(g)
Weight ratio



















Com-
Clear-
Kristalex F100 Hydrocarbon
22.25
Kristalex


parative
coat
Resin, 70% by weight in butyl

F100


example

acetate

Hydrocarbon


17

Kristalex 5140 Hydrocarbon
26.0
Resin:




Resin, 60% by weight in butyl

Kristalex 5140




acetate

Hydrocarbon




Isopropanol
14.31
Resin 1:1




Ethyl acetate






Butyl acetate 98/100
37.44





Effect pigment according to
4.0





example 5




Com-
Clear-
Kristalex F100 Hydrocarbon
19.13
Kristalex


parative
coat
Resin, 70% by weight in butyl

F100


example

acetate

Hydrocarbon


18

Kristalex 5140 Hydrocarbon
19.13
Resin:




Resin, 60% by weight in butyl

Kristalex 5140




acetate

Hydrocarbon




Isopropanol
22.33
Resin 1:1




Ethyl acetate
39.42





Butyl acetate 98/100






Effect pigment according to
4.0





example 5




Com-
Clear-
Kristalex F100 Hydrocarbon
14.87
Kristalex


parative
coat
Resin, 70% by weight in butyl

F100


example

acetate

Hydrocarbon


19

Kristalex 5140 Hydrocarbon
34.63
Resin:




Resin, 60% by weight in butyl

Kristalex 5140




acetate

Hydrocarbon




Isopropanol
18.5
Resin 1:2




Ethyl acetate
32.0





Butyl acetate 98/100






Effect pigment according to
4.0





example 5




Com-
Clear-
Kristalex F100 Hydrocarbon
14.9
Kristalex


parative
coat
Resin, 70% by weight in butyl

F100


example

acetate

Hydrocarbon


20

Kristalex 5140 Hydrocarbon
34.69
Resin:




Resin, 60% by weight in butyl

Kristalex 5140




acetate

Hydrocarbon




Isopropanol
4.6
Resin 1:2




Ethyl acetate
15.18





Butyl acetate 98/100
27.5





Acetone
3.12





Effect pigment according to
4.0





example 5









The nail varnish compositions of comparative examples 17 to 20, after application to a synthetic fingernail and subsequent drying, showed a distinctly poorer visual appearance than the nail varnish compositions of the invention, which is probably attributable to the omission of one of the solvents (comparative example 17) and/or an excessively high relative proportion of the solvents isopropanol and/or ethyl acetate in relation to butyl acetate (comparative examples 18 and 19). Moreover, the addition of an additional solvent (acetone in comparative example 20) has an adverse effect. The nail varnish applications of the comparative examples were affected by white bloom and were cloudy, probably owing to excessively rapid drying. The exact compositions of the nail varnishes of the inventive examples and comparative examples can also be found in table 18.


For the nail varnish compositions of comparative examples 21 to 24, the clearcoat was produced as described above under IIa. For production of the nail varnish compositions of comparative examples 21 to 24, 96 g of the clearcoat were added to an initial charge of 4 g of the respective surface-modified effect pigment according to table 16 below with stirring at 600 rpm/min.


The nail varnish compositions of comparative examples 21 to 24 had a binder solids content of 20% by weight, based on the total weight of the clearcoat.













TABLE 16





Com-






parative


Weight



example

Product name
(g)
Weight ratio



















Com-
Clear-
Kristalex F100 Hydrocarbon
14.3
Kristalex


parative
coat
Resin, 70% by weight in butyl

F100


example

acetate

Hydrocarbon


21

Kristalex 5140 Hydrocarbon
16.6
Resin:




Resin, 60% by weight in butyl

Kristalex 5140




acetate

Hydrocarbon




Isopropanol
6.3
Resin 1:1




Ethyl acetate
25.1





Butyl acetate 98/100
37.9





Effect pigment according to
4.0





example 5, NVC: 23%




Com-
Clear-
Kristalex F100 Hydrocarbon
9.6
Kristalex


parative
coat
Resin, 70% by weight in butyl

F100


example

acetate

Hydrocarbon


22

Kristalex 5140 Hydrocarbon
22.2
Resin:




Resin, 60% by weight in butyl

Kristalex 5140




acetate

Hydrocarbon




Isopropanol
6.2
Resin 1:2




Ethyl acetate
24.8





Butyl acetate 98/100
37.2





Effect pigment according to
4.0





example 5, NVC: 23%




Com-
Clear-
Kristalex F100 Hydrocarbon
57
Kristalex


parative
coat
Resin, 70% by weight in butyl

F100


example

acetate

Hydrocarbon


23

Kristalex 5140 Hydrocarbon
26.6
Resin:




Resin, 60% by weight in butyl

Kristalex 5140




acetate

Hydrocarbon




Isopropanol
6.1
Resin 1:4




Ethyl acetate
24.4





Butyl acetate 98/100
37.0





Effect pigment according to
4.0





example 5, NVC: 23%




Com-
Clear-
Kristalex F100 Hydrocarbon
3.1
Kristalex


parative
coat
Resin, 70% by weight in butyl

F100


example

acetate

Hydrocarbon


24

Kristalex 5140 Hydrocarbon
29.6
Resin:




Resin, 60% by weight in butyl

Kristalex 5140




acetate

Hydrocarbon




Isopropanol
6.1
Resin 1:8




Ethyl acetate
24.5





Butyl acetate 98/100
36.7





Effect pigment according to
4.0





example 5, NVC: 23%









The nail varnish compositions of comparative examples 21 to 24, after application to a synthetic fingernail and subsequent drying, showed a much poorer visual appearance than the nail varnish applications of the invention applied, which is probably attributable to the excessively low binder solids content of about 20% by weight, based on the total weight of the clearcoat. The surface-modified effect pigment was probably wetted by the solvent present in the clearcoat, and for that reason the effect pigment was unable to adopt an orientation at the surface of the clearcoat on or after application.


For production of the nail varnish compositions of comparative examples 25 to 30, the clearcoat from table 13 was added according to table 17 below to an initial charge of the respective surface-modified effect pigment according to table 17 with stirring at 600 rpm/min. The nail varnish compositions of comparative examples 25 to 30 had a binder solids content of 40% by weight, based on the total weight of the clearcoat.











TABLE 17





Comparative

Weight


example
Nail varnish composition
(g)

















25
Effect pigment according to comparative
2.30



example 10, NVC: 59%




Clearcoat from table 13
97.70





26
Effect pigment according to comparative
2.40



example 1, NVC: 58%




Clearcoat from table 13
97.60





27
Effect pigment according to comparative
2.70



example 15, NVC: 48-52%




Clearcoat from table 13
97.30





28
Effect pigment according to comparative
13.00



example 12, NVC: 10%




Clearcoat from table 13
87.00





29
Effect pigment according to comparative
13.00



example 13, NVC: 10%




Clearcoat from table 13
87.00





30
Effect pigment according to comparative
13.00



example 14, NVC: 10%




Clearcoat from table 13
87.00









Table 18 summarizes the calculated compositions of the inventive examples and comparative examples that address the variation of the nail varnish parameters (always with the same effect pigment from example 5).






















TABLE 18














Total













Pigment

binder



Total









acc. to

content
Total

Total
butyl



Kristallex
Kristalex
Iso-
Ethyl
Butyl
Further
example

in % by
effect
Total
ethyl
acetate


Sample
F100
5140
propanol
acetate
acetate
solvent
5:
Total
weight
pigment
iso
acetate
content




























Example 32
22.3
26
5
18.7
28

4
104
30.0
0.88
6.96
26.02
67.02


Example 33
14.8
34.6
4.5
19
27.5

4
104.4
29.8
0.88
6.22
26.26
67.52


Example 34
8.9
41.6
4.5
19
26

4
104
30.0
0.88
6.26
26.43
67.31


Example 35
4.8
46.3
4.5
17.9
26.5

4
104
29.9
0.88
6.26
24.88
68.86


Example 36
27.9
32.5
3
11.6
25

4
104
37.5
0.88
4.68
18.11
77.21


Example 37
19.8
46.3
3.1
12.3
18.5

4
104
40.0
0.88
5.05
20.02
74.93


Example 38
11.8
55.4
2.9
11.9
20

4
106
39.2
0.87
4.56
18.72
76.72


Example 39
6.7
61.5
2.9
11.5
17.4

4
104
40.0
0.88
4.72
18.70
76.58


Example 40
42.9
50
0.6
2.6
3.9

4
104
57.7
0.88
1.39
6.04
92.57


Example 41
28.6
66.7
0.4
1.7
2.6

4
104
57.7
0.88
0.93
3.95
95.12


Example 42
17.1
80
0.2
1
1.7

4
104
57.7
0.88
0.46
2.32
97.22


Example 43
9.6
88.8
0.1
0.6
0.9

4
104
57.7
0.88
0.23
1.39
98.38


Example 44
22.3
26
4.7
19
28

4
104
30.0
0.88
6.54
26.44
67.02


Example 45
22.3
26
4.7
19
28

4.8
104.8
29.8
1.05
6.48
26.21
67.30


Example 46
22.3
26
4.7
19
28

2
102
30.6
0.45
6.68
27.02
66.30


Example 47
22.3
26
4.7
19
28

7
107
29.2
1.50
6.34
25.61
68.05


Example 48
22.3
26
4.7
19
28

9
109
28.6
1.90
6.21
25.09
68.70


Comparative
22.25
26
14.31
0
37.44

4
104
30.0
0.88
19.90
0.00
80.10


example 17















Comparative
19.13
19.13
22.33
39.42
0

4
104.01
23.9
0.88
28.55
50.40
21.06


example 18















Comparative
14.87
23.63
18.5
32
0

4
93
26.4
0.99
27.41
47.41
25.18


example 19















Comparative
14.9
34.69
4.6
15.18
27.5
3.12
4
103.99
30.0
0.88
6.40
21.13
68.12


example 20





(acetone)









Comparative
14.3
16.6
6.3
25.1
37.9

4
104.2
19.2
0.88
7.56
30.13
62.31


example 21















Comparative
9.6
22.2
6.2
24.8
37.2

4
104
19.3
0.88
7.47
29.87
62.67


example 22















Comparative
5.7
26.6
6.1
24.4
37

4
103.8
19.2
0.89
7.36
29.42
63.22


example 23















Comparative
3.1
29.6
6.1
24.5
36.7

4
104
19.2
0.88
7.34
29.46
63.20


example 24









III Characterization of the Surface-Modified Effect Pigments of the Invention for Use with Preference in a Nail Varnish Composition and of the Surface-Modified Effect Pigments


IIIa Measurement of Particle Size


The size distribution curve of the surface-modified effect pigments of the invention that are to be used with preference in a nail varnish composition, of the surface-modified effect pigments and of the pigments from the comparative examples, based in each case on nonmetallic substrates in platelet form, was determined with the Malvern Mastersizer 2000 instrument according to the manufacturer's instructions.


For this purpose, about 0.1 g of the respective pigment in the form of an aqueous suspension without addition of dispersing aids, with constant stirring, was introduced by means of a Pasteur pipette into the sample preparation cell of the instrument and analyzed repeatedly. The individual measurement results were used to form the averages. The scattered light signals were evaluated by the Fraunhofer method.


The size distribution curve of the surface-modified effect pigments of the invention that are to be used with preference in a nail varnish composition, of the surface-modified effect pigments and of the pigments from the comparative examples, based in each case on metallic substrates in platelet form, was measured with the Quantachrome Cilas 1064 instrument or the Horiba LA-930 instrument, in each case according to manufacturer's instructions.


For this purpose, about 50 ml of the respective pigment were suspended in isopropanol, treated in an ultrasound bath for 300 seconds (instrument: Sonorex IK 52, from Bandelin) and then introduced by means of a Pasteur pipette into the sample preparation cell of the instrument and analyzed repeatedly. The individual measurement results were used to form the averages. The scattered light signals were evaluated by the Fraunhofer method.


In the context of this invention, average particle size D50 is understood to mean the D50 of the cumulative frequency distribution of the volume-averaged size distribution function as obtained by laser diffraction methods. The D50 means that 50% of the pigments have a volume-averaged diameter less than or equal to the value specified, for example 20 μm. Correspondingly, the D10 and D90 values mean that, respectively, 10% and 90% of the pigments have a volume-averaged diameter equal to or less than the respective measurement.


The span ΔD, defined as








Δ

D

=



D
90

-

D
10



D
50



,





indicates the range of the particle size distribution. With regard to the visual appearance of the surface-modified effect pigments of the invention that are to be used with preference in a nail varnish composition, or of the surface-modified effect pigments, preference is given to a small value of ΔD, i.e. a small span.


IIIb Determination of the Average Thickness of the Metallic or Nonmetallic Substrates in Platelet Form, Determination of the Average Total Thickness of the Surface-Modified Effect Pigment


The average thicknesses h50 of the surface-modified effect pigments of the invention that are to be used with preference in a nail varnish composition, the surface-modified effect pigments and the pigments from the comparative examples were determined by the method described in WO 2004/087816 A2 (pages 24 and 25) by means of SEM.


IIIc Determination of the Metal Oxide Content of the Synthetic Mica Platelets


The metal oxide contents of the synthetic mica platelets were determined by means of x-ray fluorescence analysis (XRF). For this purpose, the synthetic mica platelets were incorporated into a lithium tetraborate glass tablet, fixed in solid sample measurement cups and analyzed therefrom. The instrument used was the Thermo Scientific Advantix ARL instrument.


IV Optical Characterization of the Nail Varnish Compositions of the Invention


IVa Determination of Gloss (20° Geometry) and Haze


For objective determination of the visual appearance of the nail varnish compositions of the invention and of the nail varnish compositions from the comparative examples, the respective nail varnish composition was applied to glass plates in a wet film thickness of 110 μm by means of a bar applicator (Erichsen System Wasag Model 288 film applicator, from Erichsen) and then dried at room temperature. The gloss value (20° geometry) and the haze value (H log) of the nail varnish compositions thus applied were measured with the haze gloss instrument (from BYK Gardner).


For the measurement of gloss, the 20° geometry for high-gloss surfaces was employed (Byk-Gardner, digital catalog “Qualitätskontrolle für Lacke and Kunststoffe”, page 16). Both the gloss (20° geometry) and the haze (H log) were determined at at least 5 different points in the nail varnish application. Table 18 below lists the averages formed therefrom for gloss (20° geometry) and haze (H log).


V Results:


Table 19 lists the gloss and haze values for selected examples and comparative examples. In addition, the pigmentation levels, the binder concentrations and the compositions of the solvents in the nail varnish compositions have been calculated.


The gloss and haze values listed in table 19 should not be considered independently of one another. Thus, a nail varnish composition having a high haze value and simultaneously a low gloss value can nevertheless have a mirror-like effect.


After application, the inventive nail varnish compositions of examples 48 to 64 showed marked leafing characteristics up to and including a mirror-like effect.


The nail varnish applications of the highest visual quality with an excellent mirror effect were obtained through the use of PVD pigments coated with phosphoric acid cetyl ester (Hostaphat CC 100) (examples 49, 51, 54, 56, 57, 58 and 59).


By contrast, the nail varnish compositions of comparative examples 27 to 30, where no additive was used, did not show any leafing effect and in some cases even showed significant formation of specks after application. The resultant gloss and haze values were accordingly poor.


In comparative example 25, the potassium salt of cetylphosphoric ester was used, which is disadvantageous.


In comparative example 26, the application contained specks. This is probably attributable to an excessively high proportion of the additive in the production of the coated metal pigment.









TABLE 19







Results of optical studies and the most important composition parameters for selected examples and comparative examples




















Content of










the preferred










3-solvent





Example/




mixture***
Content of




Compar-
Type of

Additive/
Pigment
based on the
hydrocarbon
Gloss



ative
effect

pigment
content
total solvent
resin
(20°
Haze


example
pigment
Additive
ratio in %
[% by wt.]
content
[% by wt.]
geometry)
(Hlog)


















Example 49
PVD*
CC 100
10
1.20
71.2
57.4
624.3
1353.9


Example 50
Pt-$**
CC 100
4
1.28
95.8
63.6
137.5
1344.9


Example 51
PVD
CC 100
10
1.33
95.8
63.6
358.4
1510.7


Example 52
PVD
Laurylphos-
13.3
1.19
75.9
56.4
84.1
1289.1




phonic acid








Example 53
PVD
Laurylphos-
13.3
1.28
78.7
59.7
130.7
1415.0




phonic acid








Example 54
PVD
CC 100
20.0
1.15
90.8
59.7
221.2
1450.5


Example 55
PVD
Laurylphos-
20.0
1.13
83.3
61.0
120.2
1383.1




phonic acid








Example 56
PVD
CC 100
10.0
1.24
84.8
61.2
149.6
1390.4


Example 57
PVD
CC 100
20.0
1.14
88.5
58.4
240.1
1568.0


Example 58
PVD
CC 100
40.0
0.98
88.4
58.5
455.8
1496.1


Example 59
PVD
CC 100
10.0
1.25
88.4
58.5
176.6
1499.3


Example 60
Pt-$
CC 100
5.0
1.31
95.1
62.1
101.0
1290.0


Example 61
Pt-$
CC 100
20.0
1.13
100.0
64.4
107.0
1317.7


Example 62
Pt-$
CS 100
5.0
1.29
100.0
64.6
125.1
1366.0


Example 63
Pt-$
CC 100
2.5
1.33
100.0
64.5
121.1
1347.6


Example 64
Pt-S
CC 100
7.5
1.27
100.0
64.3
99.9
1289.0


Comparative
PVD

0
1.30
100.0
36.2
101.8
121.6


example 28










Comparative
PVD

0
1.30
100.0
36.2
19.2
565.6


example 29










Comparative
PVD

0
1.30
100.0
36.2
100.4
134.5


example 30










Comparative
Pt-$

0
1.35
96.1
40.5
104.4
175.5


example 27










Comparative
Pt-$
Hostaphat
20
1.13
100.0
64.6
73.2
1154.9


example 25

CK 100








Comparative
Pt-$
CS 120
20
1.16
100.0
64.5
125.2
1363.5


example 26





*All PVD pigments are abbreviated here merely to “PVD”; the further details can be found in the corresponding tables above.


**“Pt-$” refers in this table to all wet-ground pigments having an average thickness below 100 nm. Further details can be found in the corresponding tables above.


***Mixture of ethyl acetate, butyl acetate and isopropanol.





Claims
  • 1. A surface-modified effect pigment dispersion comprising: solvent, and a metallic substrate in platelet form, wherein the metallic substrate in platelet form is produced by a PVD method, has an average thickness h50 ranging from 13 nm to 60 nm, and comprises a surface modification formed from a starting material comprising phosphoric acid cetyl ester in an amount ranging from 10% by weight to 50% by weight based on the total weight of the metallic substrate in platelet form.
  • 2. The surface-modified effect pigment dispersion as claimed in claim 1, wherein the metallic substrate in platelet form includes an aluminum effect pigment produced by a PVD method, and has a D50 in a range from 2.5 μm to 90 μm.
  • 3. A process for producing a surface-modified effect pigment dispersion, the process comprising: suspending a metallic substrate in platelet form having an average thickness h50 ranging from 13 nm to 60 nm in at least one solvent to prepare a suspension, the metallic substrate in platelet form having been produced by a PVD method, adding to the suspension phosphoric acid cetyl ester in an amount ranging from 10% by weight to 50% by weight based on the total weight of the metallic substrate in platelet form and then stirring the suspension to obtain a surface-modified pigment.
  • 4. The surface-modified effect pigment dispersion as claimed in claim 1, wherein the metallic substrate in platelet form includes an aluminum effect pigment having a D50 in a range from 6 μm to 18 μm and an average thickness within a range from 14 nm to 40 nm.
  • 5. The surface-modified effect pigment dispersion as claimed in claim 1, wherein the solvent includes one or more of isopropanol, ethyl acetate, and butyl glycol.
  • 6. The surface-modified effect pigment dispersion as claimed in claim 1, wherein the solvent includes butyl acetate.
  • 7. The process for producing the surface-modified effect pigment dispersion of claim 3, wherein the solvent includes one or more of isopropanol, ethyl acetate, and butyl glycol.
  • 8. The process for producing the surface-modified effect pigment dispersion of claim 3, wherein the solvent includes butyl acetate.
  • 9. The surface-modified effect pigment dispersion as claimed in claim 1, wherein the metallic substrate in platelet form comprises a coating including one or more of a metal oxide, a metal hydroxide, and a metal oxide hydrate.
  • 10. The process as claimed in claim 3, Wherein the metallic substrate in platelet form comprises a coating including one or more of a metal oxide, a metal hydroxide, and a metal oxide hydrate.
  • 11. The process as claimed in claim 3, wherein adding the phosphoric acid cetyl ester to the suspension is conducted elevated temperature.
  • 12. The process as claimed in claim 3, further comprising filtering the surface-modified effect pigment.
Priority Claims (1)
Number Date Country Kind
16000855 Apr 2016 EP regional
US Referenced Citations (13)
Number Name Date Kind
6042842 Lemann Mar 2000 A
6692830 Argoitia Feb 2004 B2
6749777 Argoitia Jun 2004 B2
8911546 Henglein Dec 2014 B2
9453131 Geissler Sep 2016 B2
20010007696 Kaupp Jul 2001 A1
20040194663 Li Oct 2004 A1
20070020205 Blin Jan 2007 A1
20070207099 Erker Sep 2007 A1
20080013138 Yoshizawa Jan 2008 A1
20080050324 Thevenet Feb 2008 A1
20160007713 Gouse Jan 2016 A1
20190077963 Schilling Mar 2019 A1
Foreign Referenced Citations (14)
Number Date Country
0643745 Mar 1995 EP
1901870 Mar 2008 EP
2367889 Sep 2011 EP
2598578 Jun 2013 EP
2776512 Oct 1999 FR
2939678 Jun 2010 FR
2007513893 May 2007 JP
2009502839 Jan 2009 JP
0034395 Jun 2000 WO
2004087816 Oct 2004 WO
2005055965 Jun 2005 WO
2008007334 Jan 2008 WO
2009068462 Jun 2009 WO
2017178610 Oct 2017 WO
Related Publications (1)
Number Date Country
20200317927 A1 Oct 2020 US
Divisions (1)
Number Date Country
Parent 16093717 US
Child 16909183 US