This invention belongs to the technical field of specialty glass production. It is, in detail, related to a surface-textured conductive glass for solar cells, and preparation method and application thereof.
Conductive glass is a special type of glass having one side coated with a transparent conductive film, thus having features of being both transparent and electrically conductive. Besides being applied in LCD and warm-keeping doors and windows, conductive glass also serves as an essential part for solar cells, for it can be used as the transparent electrode and superstrate. The photoelectric quality of the glass directly affects the performance of the solar cells, thus conductive glass is a key material for preparing Amorphous Silicon, Microcrystalline Silicon, Cadmium Telluride, CIGS (Copper Indium Gallium Selenide) thin film solar cells. The issue of how to produce high-quality low-cost surface-textured conductive glass for solar cells is essential to produce low-cost high-efficiency solar cells for cost-effective solar power generation.
Currently, we have the following types of specialty conductive glass used for producing solar cells and their preparation methods:
1) ITO (indium tin oxide) conductive glass made by magnetron sputtering;
2) AZO (aluminum-doped zinc oxide) conductive glass made by magnetron sputtering;
3) FTO (fluorine-doped tin oxide) conductive glass made by Atmospheric Pressure Chemical Vapor Deposition (APCVD);
4) BZO (boron-doped zinc oxide) or AZO (aluminum-doped zinc oxide) conductive glass made by Low Pressure Chemical Vapor Deposition (LPCVD);
To enhance light absorption, the transparent conductive film should have a certain degree of texture, namely unevenness, at nano/micro-scale, so as to enable diffuse scattering (usually measured by haze value) during light incidence and extend optical path for light propagation inside the cell (As shown in Draw. 1).
Among conductive glass samples in lab, we mainly have the following three kinds of surface texture:
1) AZO conductive glass made by hydrochloric acid wet etching after magnetron sputtering (as shown in Draw. 2);
2) FTO conductive glass made by APCVD (as shown in Draw. 3);
3) BZO or AZO conductive glass made by LPCVD (as shown in Draw. 4).
Meanwhile, the surface feature of the transparent conductive film must ensure that the quality of the absorption layer of the solar cell remains free of negative influences from its unevenness. As a cell is usually prepared layer-by-layer in a sequential order, the transparent conductive film serves as the direct substrate on which the absorption layer grows, and its shape directly affects the growth mode and the quality of the absorption layer. Taking microcrystalline silicon absorption layers for instance (as shown in Draw. 5), different surface texture shapes of transparent conductive films have led to microcrystalline silicon absorption layers with different qualities.
When the textured surface of the transparent conductive film takes on a V-shape (Draw. 5A), the microcrystalline silicon absorption layer on top is easy to have fissure, which severely affects the performances of the solar cells. The microcrystalline silicon absorption layer has less fissure (Draw. 5B) or even no fissure (Draw. 5C) when the surface texture takes on a U-shape. Besides, cadmium telluride absorption layers have stricter requirements than microcrystalline silicon absorption layers on surface texture morphology, which requires the surface texture to totally consist of shallower U-shaped pits.
For the above three types of samples, only AZO conductive glass made by hydrochloric acid wet etching after magnetron sputtering and BZO (or AZO) conductive glass made by LPCVD may meet the requirement on U-shaped surface texture morphology. During industrial volume production, however, due to the uneasy control of wet etching, problems like uneven, unstable products and low yield do exist in the former, while the later needs long time of plasma etching, and thus both render too high cost for industrial production. Up to now, it is still a gap in the world to find an industrialized low-cost method to produce U-shaped surface-textured conductive glass for microcrystalline silicon and cadmium telluride thin film solar cells. Due to facts stated above, the production cost for microcrystalline silicon thin film solar cells remains high and the production of cadmium telluride thin film solar cells has only to use planar FTO conductive glass which almost has no surface texture.
To overcome the shortcomings of the existing technologies, this invention mainly aims at providing a low-cost surface-textured conductive glass for solar cells, having a textured surface over which nano-scopic U-shaped pits uniformly distributed.
This invention also aims at providing a preparation method for surface-textured conductive glass for solar cells mentioned above. The preparation method comprises: coating a transparent conductive film (ITO, AZO, etc.) by magnetron sputtering, then absorbing nano/micro-spheres onto the surface of the transparent conductive film as a mask by using an immersion coating method, followed by increasing the thickness of the transparent conductive film in gaps among the nano/micro-spheres (dia. 10 nm-100 μm) by magnetron sputtering, and finally removing the nano/micro-spheres by mechanical or chemical means such as the ultrasonic vibration method, so as to extensively realize the low-cost production of the conductive glass with U-shaped surface texture.
Still, this invention aims at providing the application of surface-textured conductive glass for solar cells mentioned above.
The purposes of this invention can be realized via the following technical solutions.
A surface-textured conductive glass for solar cells, with the following structure and composition: a transparent conductive film coated on a glass substrate, the upper surface of which is a textured surface with nano/micro-scopic U-shaped surface texture.
The thickness of the said transparent conductive film is 100-5,000 nm.
The said transparent conductive film adopts one of the following materials: ITO, AZO or other materials (isoelectric point>3).
The preparation method of said surface-textured conductive glass for solar cells, including the following procedures (as shown in Draw. 6):
(1) Conductive glass A is derived after coating the transparent conductive film on a glass substrate by magnetron sputtering.
(2) Prepare the monodispersed nano/micro-sphere suspension and adjust its pH value to 3-7; immerse conductive glass A in the suspension for 2-15 minutes, and then take it out and wash it with water, and then conductive glass B is derived.
Due to the fact that the transparent conductive films such as ITO and AZO have higher isoelectric points (usually 6-10), and nano/micro-spheres of silicon dioxide or polystyrene have lower isoelectric points (usually 2-4), when the conductive glass is immersed into the neutral (pH=7) or acidic (pH=3-6) suspension containing nano/micro-spheres, the surface of the transparent conductive film carries negative electrical charges while the surface of the nano/micro-spheres carry positive electrical charges, and thus the electrostatic attraction is resulted in between the two materials. After certain time, the surface of the transparent conductive film is almost totally covered by a monolayer of nano/micro-spheres. The area coverage of nano/micro-spheres on conductive glass depends on the concentration and the pH value of the nano/micro-sphere suspension, and the immersion coating time.
(3) Taking nano/micro-spheres as a mask, a transparent conductive film is coated on conductive glass B by magnetron sputtering, and thus conductive glass C is derived. The thickness of the film newly coated should not exceed the radius of the nano/micro-spheres, and the total thickness of the transparent conductive film is 100-5,000 nm.
The reason for using magnetron sputtering to coat the second film again lies in that the coated materials can, during magnetron sputtering, reach the side positions below the nano/micro-spheres, and form a U-shaped textured surface without sharp edges and corners (as shown in Draw. 7).
(4) Remove the nano/micro-spheres by an ultrasonic vibration method to form a surface texture of U-shaped nano/micro-scopic pits on the surface of conductive glass C, and thus the surface-textured conductive glass for solar cells is derived. The transmittance in the visible spectrum of the conductive glass is more than 80%, and the sheet resistance is less than 10 Ω.
The magnetron sputtering as stated in procedure (1) and (3) has the following conditions: base vacuum pressure: <1×10−5 Torr; working pressure: 1-10 mTorr; working gas: Ar+O2; sputtering plasma source: direct current or radio frequency 13.56 MHz; power: 100-1,000 W; substrate temperature: 20-500° C.; deposition rate: 10-100 nm/min.
The diameters of the nano/micro-spheres as stated in procedure (2) are within the range of 10 nm-100 μm.
The material of the nano/micro-spheres as stated in procedure (2) is either silicon dioxide or polystyrene.
The weight/volume (w/v) concentration of nano/micro-spheres in the suspension as stated in procedure (2) is 0.01-1%.
The solvent of the suspension as stated in procedure (2) is water, methanol or ethanol.
The preferable immersion time for the conductive glass in the suspension as stated in procedure (2) is 8-10 minutes.
The surface-textured conductive glass for solar cells stated above can be used as the transparent electrode or superstrate for solar cells.
The said nano/micro-spheres in this invention refer to the nano-scopic spheres or micron-scopic spheres, and the nano/micro refers to nanometer or micrometer.
This invention has the following advantages and effects comparing with the existing technologies:
From the angle of industrial production, the techniques adopted in this method, including planar glass panel magnetron sputtering, immersion coating and cleaning, are all well matched with the presently standard industrial processing techniques. It has the advantages of higher producing efficiency, larger applicable glass area, higher repeatability, and higher yield. Also, the nano/micro-spheres used are of low cost. As a result, this invention is very suitable for producing the low-cost and high-quality conductive glass for solar cells.
We hereby make more detailed descriptions of this invention in combination with embodiments and drawings, but the embodiments of this invention are not limited to these ones.
A preparation method for surface-textured conductive glass for solar cells, including the following procedures (As shown in Draw. 6):
(1) An AZO transparent conductive film is coated on a glass substrate by magnetron sputtering, and conductive glass A is derived. The conditions for magnetron sputtering are: base vacuum pressure: 0.8×10−5 Torr; working pressure: 1 mTorr; working gas: Ar+O2; sputtering plasma source: direct current or radio frequency 13.56 MHz; power: 1,000 W; substrate temperature: 20° C.; deposition rate: 100 nm/min;
(2) Prepare a suspension (0.25% w/v) of polystyrene nano-spheres (dia. 1,000 nm) in water, and adjust its pH value to 4; immerse conductive glass A in the suspension for 2 minutes, and then take it out and wash it with water, and then conductive glass B is derived;
As shown in Draw. 8, conductive glass B is coated with a monolayer of nano-spheres;
(3) Taking nano-spheres as a mask, an AZO transparent conductive film is coated on conductive glass B by magnetron sputtering (the magnetron sputtering conditions are the same as those in Procedure (1)), and thus conductive glass C is derived. The thickness of the film newly coated should not exceed the radius of nano-spheres, and the total thickness of the transparent conductive film is 2,000 nm;
(4) Remove the nano-spheres deposited on the surface of the transparent conductive film by using an ultrasonic vibration method, and thus the surface-textured conductive glass for solar cells is derived. The surface features of conductive glass after removing nano-spheres are shown in Draw. 14 and Draw. 15. The pits on the textured surface present a smooth curvature and thus an obvious U-shape, and also, these pits are uniformly distributed over the surface of the conductive glass. The transmittance in the visible spectrum of the conductive glass is 82%, and surface resistance is 3 Ω. This conductive glass can be used as the transparent electrode or superstrate for solar cells.
A preparation method for surface-textured conductive glass for solar cells, including the following procedures (As shown in Draw. 6):
(1) An AZO transparent conductive film is coated on a glass substrate by magnetron sputtering, and conductive glass A is derived. The conditions for magnetron sputtering are: base vacuum pressure: 0.7×10−5 Torr; working pressure: 10 mTorr; working gas: Ar+O2; sputtering plasma source: direct current or radio frequency 13.56 MHz; power: 100 W; substrate temperature: 500° C.; deposition rate: 100 nm/min;
(2) Prepare a suspension (0.5% w/v) of silicon dioxide nano-spheres (dia. 1,000 nm) in ethanol, and adjust its pH value to 7; immerse conductive glass A in the suspension for 4 minutes, and then take it out and wash it with water, and then conductive glass B is derived;
As shown in Draw. 9, conductive glass B is coated with a monolayer of nano-spheres;
(3) Taking nano/micro-spheres as a mask, an AZO transparent conductive film is coated on conductive glass B by magnetron sputtering (the magnetron sputtering conditions are the same as those in Procedure (1)), and thus conductive glass C is derived. The thickness of the film newly coated should not exceed the radius of the nano/micro-sphere, and the total thickness of the transparent conductive film is 3,000 nm;
(4) Remove the nano/micro-spheres deposited on the surface of the transparent conductive film by an ultrasonic vibration method, so as to form the surface texture consisting of U-shaped nano/micro-scopic pits on the surface of conductive glass C, and thus the surface-textured conductive glass for solar cells is derived. The transmittance in the visible spectrum of the conductive glass is 83%, and the sheet resistance is 4 Ω. This conductive glass can be used as the transparent electrode or superstrate for solar cells.
A preparation method for surface-textured conductive glass for solar cells, including the following procedures (As shown in Draw. 6):
(1) An ITO transparent conductive film is coated on a glass substrate by magnetron sputtering, and conductive glass A is derived. The conditions for magnetron sputtering are: base vacuum pressure: 0.9×10−5 Torr; working pressure: 4 mTorr; working gas: Ar+O2; sputtering plasma source: direct current or radio frequency 13.56 MHz; power: 800 W; substrate temperature: 100° C.; deposition rate: 80 nm/min;
(2) Prepare a suspension (0.1% w/v) of polystyrene nano-spheres (dia. 1,000 nm) in water, and adjust its pH value to 6; immerse conductive glass A in the suspension for 6 minutes, and then take it out and wash it with water, and then conductive glass B is derived;
As shown in Draw. 10, conductive glass B is coated with a monolayer of nano-spheres;
(3) Taking nano/micro-spheres as a mask, an ITO transparent conductive film is coated on conductive glass B by magnetron sputtering (the magnetron sputtering conditions are the same as those in Procedure (1)), and thus conductive glass C is derived. The thickness of the film newly coated should not exceed the radius of the nano/micro-spheres, and the total thickness of the transparent conductive film is 1,000 nm;
(4) Remove the nano/micro-spheres deposited on the surface of the transparent conductive film by an ultrasonic vibration method, so as to form the surface texture consisting of U-shaped nano/micro-scopic pits on the surface of conductive glass C, and thus the surface-textured conductive glass for solar cells is derived. The transmittance in the visible spectrum of the conductive glass is 81%, and surface resistance is 2 Ω. This conductive glass can be used as the transparent electrode or superstrate for solar cells.
A preparation method for surface-textured conductive glass for solar cells, including the following procedures (As shown in Draw. 6):
(1) An AZO transparent conductive film is coated on a glass substrate by magnetron sputtering, and conductive glass A is derived. The conditions for magnetron sputtering are: base vacuum pressure: 0.5×10−5 Torr; working pressure: 6 mTorr; working gas: Ar+O2; sputtering plasma source: direct current or radio frequency 13.56 MHz; power: 200 W; substrate temperature: 400° C.; deposition rate: 40 nm/min;
(2) Prepare a suspension (0.75% w/v) of polystyrene nano-spheres (dia. 1,000 nm) in water, and adjust its pH value to 3; immerse conductive glass A in the suspension for 8 minutes, and then take it out and wash it with water, and then conductive glass B is derived;
As shown in Draw. 11, conductive glass B is coated with a monolayer of nano-spheres, the surface area coverage of which is more than 90%;
(3) Taking nano/micro-spheres as a mask, an AZO transparent conductive film is coated on conductive glass B by magnetron sputtering (the magnetron sputtering conditions are the same as those in Procedure (1)), and thus conductive glass C is derived. The thickness of the film newly coated should not exceed the radius of nano/micro-spheres, and the total thickness of the transparent conductive film is 100 nm;
(4) Remove the nano/micro-spheres deposited on the surface of the transparent conductive film by an ultrasonic vibration method, so as to form the surface texture consisting of U-shaped nano/micro-scopic pits on the surface of conductive glass C, and thus the surface-textured conductive glass for solar cells is derived. The transmittance in the visible spectrum of the conductive glass is 84%, and the sheet resistance is 5 Ω. This conductive glass can be used as the transparent electrode or superstrate for solar cells.
A preparation method for surface-textured conductive glass for solar cells, including the following procedures (As shown in Draw. 6):
(1) An AZO transparent conductive film is coated on a glass substrate by magnetron sputtering, and conductive glass A is derived. The conditions for magnetron sputtering are: base vacuum pressure: 0.6×10−5 Torr; working pressure: 8 mTorr; working gas: Ar+O2; sputtering plasma source: direct current or radio frequency 13.56 MHz; power: 400 W; substrate temperature: 300° C.; deposition rate: 20 nm/min;
(2) Prepare a suspension (1% w/v) of polystyrene nano-spheres (dia. 1,000 nm) in methanol, and adjust its pH value to 3; immerse conductive glass A in the suspension for 10 minutes, and then take it out and wash it with water, and then conductive glass B is derived;
As shown in Draw. 12, conductive glass B is coated with a monolayer of nano spheres, the surface area coverage is more than 90%;
(3) Taking nano/micro-spheres as a mask, an AZO transparent conductive film is coated on conductive glass B by magnetron sputtering (the magnetron sputtering conditions are the same as those in Procedure (1)), and thus conductive glass C is derived. The thickness of the film newly coated should not exceed the radius of nano/micro-spheres, and the total thickness of the transparent conductive film is 5,000 nm;
(4) Remove the nano/micro-spheres deposited on the surface of the transparent conductive film by an ultrasonic vibration method, so as to form the surface texture consisting of U-shaped nano/micro-scopic pits on the surface of conductive glass C, and thus the surface-textured conductive glass for solar cells is derived. The transmittance in the visible spectrum of conductive glass is 82%, and the sheet resistance is 3 Ω. This conductive glass can be used as the transparent electrode or superstrate for solar cells.
A preparation method for surface-textured conductive glass for solar cells, including the following procedures (As shown in Draw. 6):
(1) An AZO transparent conductive film is coated on a glass substrate by magnetron sputtering, and conductive glass A is derived. The conditions for magnetron sputtering are: base vacuum pressure: 0.4×10−5 Torr; working pressure: 2 mTorr; working gas: Ar+O2; sputtering plasma source: direct current or radio frequency 13.56 MHz; power: 600 W; substrate temperature: 200° C.; deposition rate: 60 nm/min;
(2) Prepare a suspension (0.01% w/v) of polystyrene nano-spheres (dia. 1,000 nm) in methanol, and adjust its pH value to 4; immerse conductive glass A in the suspension for 15 minutes, and then take it out and wash it with water, and then conductive glass B is derived;
As shown in Draw. 13, conductive glass B is coated with a monolayer of nano-spheres;
(3) Taking nano/micro-spheres as a mask, an AZO transparent conductive film is coated on conductive glass B by magnetron sputtering (the magnetron sputtering conditions are the same as those in Procedure (1)), and thus conductive glass C is derived. The thickness of the film newly coated should not exceed the radius of nano/micro-spheres, and the total thickness of the transparent conductive film is 4,000 nm;
(4) Remove the nano/micro-spheres deposited on the surface of the transparent conductive film by an ultrasonic vibration method, so as to form the surface texture consisting of U-shaped nano/micro-scopic pits on the surface of conductive glass C, and thus the surface-textured conductive glass for solar cells is derived. The transmittance in the visible spectrum of the conductive glass is 82%, and the sheet resistance is 3 Ω. This conductive glass can be used as the transparent electrode or superstrate for solar cells.
Above introduced embodiments are preferable ones for this invention, but the implementation methods of this inventions are not limited by above embodiments. Any other alternation, embellishment, substitution, combination or simplification which complies with the spirit and principle of this invention falls into the protection of this invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201110141276.8 | May 2011 | CN | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/CN12/70984 | 9/2/2012 | WO | 00 | 2/28/2014 |