The present invention relates to optical fibers and cables, particularly fibers and cables intended for installation at customer premises.
The deployment of desktop optical network terminals (ONTs) inside the homes of network users is increasing. ONTs can be conveniently located close to a TV set top box or an Internet modem. An optical fiber routed inside the home connects the ONT to a service module usually installed at an entrance to the home by the network provider. The in-home fiber routing is preferably performed at minimal cost and with little, if any, visibility when completed.
While staples may sometimes be used to route a fiber along a wall, molding, or other supporting surface in a user's home in least time and at low cost, users often prefer instead to hide the fiber completely from view by way of special moldings or conduits. Also, if not properly struck, staples can impair or break the fiber and physically damage walls and moldings as well. Thus, for customers who prefer to hide all cables and fibers routed inside their premises entirely from view, expensive hardware and increased installation time are required.
A procedure that allows an installer to route and bond an optical fiber or cable quickly, safely, and permanently to exposed surfaces, grooves and/or corners inside a customer premises so the finished installation leaves little or no visual impact, is therefore very desirable. Materials and instructions for performing such an installation are currently available from OFS Fitel, LLC, under the registered mark InvisiLight®. See U.S. Pat. No. 8,906,178 (Dec. 9, 2014) and U.S. Pub. No. 2016/0097911 (Apr. 7, 2016), both of which are incorporated by reference. During an InvisiLight installation, a consumer grade, low odor, nonhazardous, water based adhesive is used to bond PVC buffered fibers or PVC jacketed indoor cables, to walls, ceilings, and other substrates over a routing path inside the premises. Water based adhesives are desirable since they can be applied in areas having little or no ventilation, cleaned up with soap and water, and shipped worldwide without restrictions.
As demand for indoor deployments like InvisiLight spreads from North America into Europe, regional building standards impose certain constraints on the product offering. In Europe, the Middle East, and Africa (the EMEA region), safety standards often require the use of low smoke zero halogen (LSZH) jacketed optical fibers and cables for indoor installations. Materials commonly used in the manufacture of LSZH cables are typically mineral-filled compounds based on low surface energy (LSE) plastics including thermoplastic polyolefins, thermoplastic urethanes, and thermoplastic polyester elastomers. For example, a LSZH compliant 2.0 mm diameter cable produced by OFS Fitel, LLC for use in Europe uses an olefinic outer jacket having a surface energy of less than 31 dyne/cm, while PVC cable jackets have surface energies typically in the mid to high 30's dyne/cm.
Polyolefin materials typically have a chemically inert surface that makes them useful in many applications, but their low surface energy makes it difficult to bond the materials chemically or mechanically to another surface. An adhesive for bonding a polyolefin jacketed cable to a supporting substrate must therefore be able to wet the jacket and penetrate it enough to produce a secure and permanent mechanical connection with the substrate once the adhesive cures. For the adhesive to wet the surface of the cable jacket sufficiently, it should exhibit a surface tension that is equal to or lower than that of the jacket. See, Adhesion Bonding, “Surface Wetting and Pretreatment Methods,” at www.adhesionbonding.com/2012/05/04/surface-wetting/. And while such adhesives exist, they (i) are expensive, (ii) are usually provided in two parts that must be mixed in a specific ratio, (iii) do not conform with local codes for living residences, and/or (iv) require a hot melt or other special procedure to prepare, apply, and cure. See, e.g., U.S. Pat. No. 8,921,485 (Dec. 30, 2014), and U.S. Pubs No. 2016/0075924 (Mar. 17, 2016) and No. 2016/0102230 (Apr. 14, 2016).
Surface treatment of polyolefin material by the application of ultraviolet radiation or an oxidizing gas flame to improve adhesion of ink on the material, is known. See U.S. Pat. No. 4,933,123 (Jun. 12, 1990), and No. 5,223,852 (Jun. 29, 1993). It is also known to irradiate the surface of a polyolefin article with a plasma to improve adhesion to the surface. See U.S. Pat. No. 4,465,715 (Aug. 14, 1984), and No. 5,324,771 (Jun. 28, 1994). As far as is known, however, a surface treatment for a LSE optical fiber or cable that enables a water based, consumer grade, non-flammable adhesive to bond the fiber securely on the surface of a supporting substrate has not been disclosed.
According to the invention, a method of treating a length of a buffered optical fiber or a jacketed cable having a relatively low surface energy so that the fiber or cable can be bonded to a surface on a supporting substrate at a customer premises by an adhesive, includes providing one or more burners for producing a flame, and directing the flame over a surface on the fiber or cable, thereby treating the fiber or cable by oxidizing the surface. The burners and the fiber or cable are arranged to move relative to one another at a determined rate so that the surface energy of the fiber or cable is increased by an amount sufficient for wetting by a water soluble, non-flammable adhesive for bonding the fiber or cable to a supporting substrate.
According to another aspect of the invention, a method of treating a length of a buffered optical fiber or a jacketed cable having a relatively low surface energy so that the fiber or cable can be bonded to a surface on a supporting substrate at a customer premises by an adhesive, includes producing a blown-ion discharge and directing the discharge over a surface on the fiber or cable, thereby treating the wire or cable by removing contamination and micro-etching the surface. The blown-ion discharge and the fiber or cable are arranged to move relative to one another at a determined rate so that the surface energy of the fiber or cable is increased by an amount sufficient for wetting by a water soluble, non-flammable adhesive for bonding the fiber or cable to a supporting substrate.
According to yet another aspect of the invention, a length of fiber optic cable includes an outer cable jacket of a low smoke zero halogen (LSZH) material selected from among polyolefins, urethanes, and polyester elastomers, wherein the material is treated to have an increased surface energy capable of wetting by a water soluble, non-flammable adhesive for bonding the cable to a supporting substrate inside a customer premises.
According to a further aspect of the invention, a length of buffered optical fiber includes a buffer layer of a low smoke zero halogen (LSZH) material selected from among polyolefins, urethanes, and polyester elastomers, wherein the material is treated to have an increased surface energy capable of wetting by a water soluble, non-flammable adhesive for bonding the cable to a supporting substrate inside a customer premises.
For a better understanding of the invention, reference is made to the following description taken in conjunction with the accompanying drawing and the appended claims.
In the drawing:
According to the invention, burner flame and blown-ion surface treatments are used to increase the surface energy of buffered optical fibers or jacketed cables including those conforming to low smoke zero halogen (LSZH) standards, so that a commercially available, non-hazardous, water-based consumer grade adhesive can be used to bond the fibers or cables permanently to surfaces of walls, ceilings, and other supporting substrates inside a customer premises with little or no visual impact. In particular, the invention permits cost effective installations to be performed at premises where LSZH compliant fibers and cables are mandated.
To enable the adhesive to wet and penetrate LSZH and other low surface energy (LSE) fibers and cables enough to bond them firmly on a supporting substrate when the adhesive cures, the fibers or cables are exposed to either a flame treatment or a plasma (a/k/a “blown-ion”) process to increase their surface energy. Flame treatment increases surface energy by causing surface oxidation which improves chemical functionality. Blown-ion treatment increases surface energy by bombarding the surface with a high speed discharge of positive ions that have a micro-etching or scrubbing effect, thereby removing contamination and increasing the polarity of the surface.
Other treatment methods are also known generally to increase the surface energy of materials, for example, solvent cleaning, priming, surface roughening, and acid etching. Flame and blown-ion treatment are preferred as being most practical and cost effective for buffered fibers and jacketed cables, since either treatment may be implemented fairly seamlessly during the course of a typical production run of a LSZH fiber or cable.
0.9 mm (900 micron) LSZH Buffered Fiber
Samples of LSZH buffered fibers were obtained by applying a tight buffer layer of PolyOne ECCOH™ 6151 polyolefin material around each of several 250 micron fibers, to obtain an outer diameter of 900 microns for each fiber. Control samples of PVC buffered fibers were also obtained.
Load results obtained during “Ramp Up” in
In the results shown in
Prior to flame treatment, sample lengths of 2.0 mm LSZH cordage having an outer jacket of AlphaGary MEGOLON™ 8142 polyolefin material were adhered on the surface of the painted wood substrate, using the above mentioned water soluble paste adhesive. In peel test results shown in
By contrast,
Blown-ion air plasma systems push pressurized air past a single electrode which discharges inside a treater head. The discharge creates positively charged ions from surrounding air particles inside the head. Air pressure supplied to the head forces the charged ions to accelerate from a tip of the head as a high velocity ion stream. When directly contacting the surface of an object, the ion stream positively charges the surface thereby increasing the surface energy.
Four types of LSZH buffered fibers were prepared by applying a tight buffer layer of one of four LSZH compounds around each of a number of 250 micron fibers, to obtain an outer diameter of 900 microns for each fiber. The LSZH compounds included polyolefin, polyester, and urethane. Blown-ion surface treatments were performed on each of the buffered fibers using an Enercon Industries blown-ion plasma surface treater. The fibers moved through the ion discharge from the treatment head of the treater at a line speed of approximately 50 meters per minute. Peel tests were then performed on each of the four types of buffered fibers (i) before treatment, (ii) after a length of the fiber passed once through the ion discharge from surface treater, and (iii) after the fiber passed three times through the ion discharge.
Peel test results were obtained after adhering specimens of each type of buffered fiber to a painted wood substrate using the one part, water-soluble, consumer grade indoor adhesive noted above. As mentioned, 900 micron non-LSZH, PVC buffered fibers were adhered to a painted wood substrate with the same adhesive to act as a control sample. The adhesive was allowed to cure for 24 hours, and the load needed to pull each of the adhered fibers away from the substrate at a 90-degree angle was measured. The results for the PVC control samples are shown in
Buffered 900 micron fibers were prepared each with a PolyOne ECCOH™ 6151 LSZH polyolefin tight buffer layer, and the fibers were adhered without surface treatment to the wood substrate together with the PVC buffered control fiber as described above. After allowing the adhesive to cure 24 hours, the following results were obtained:
Buffered 900 micron fibers were prepared each with a PolyOne ECCOH 6151 LSZH polyolefin tight buffer layer, and passed once through the blown-ion discharge from the surface treater as noted above. The treated fibers were adhered to the wood substrate. After allowing the adhesive to cure 24 hours, the following results were obtained:
Buffered 900 micron fibers were prepared with a PolyOne ECCOH 6151 LSZH polyolefin tight buffer layer, and passed three times through the blown-ion discharge from the surface treater as noted above. The treated fibers were adhered to the wood substrate. After allowing the adhesive to cure 24 hours, the following results were obtained:
Buffered 900 micron fibers were prepared with a tight buffer layer of a polyester elastomer comprised of a blend of DuPont HYTREL® 6356 with HYTREL 52R added at 10 wt %, and adhered without surface treatment to the wood substrate. After allowing the adhesive to cure 24 hours, the following results were obtained:
Buffered 900 micron fibers were prepared with a tight buffer layer of a polyester elastomer comprised of a blend of DuPont HYTREL 6356 with HYTREL 52R added at 10 wt %, and passed once through the blown-ion discharge from the surface treater as noted above. The treated fibers were adhered to the wood substrate. After allowing the adhesive to cure 24 hours, the following results were obtained:
Buffered 900 micron fibers were prepared with a tight buffer layer of a polyester elastomer comprised of a blend of DuPont HYTREL® 6356 with HYTREL 52R added at 10 wt %, and passed three times through the blown-ion discharge from the surface treater as noted above. The treated fibers were adhered to the wood substrate. After allowing the adhesive to cure 24 hours, the following results were obtained:
Buffered 900 micron fibers were prepared with an AlphaGary MEGOLON™ 8142 LSZH polyolefin tight buffer layer, and adhered without surface treatment to the wood substrate. After allowing the adhesive to cure 24 hours, the following results were obtained:
Buffered 900 micron fibers were prepared with an AlphaGary MEGOLON 8142 LSZH polyolefin tight buffer layer, and passed once through the blown-ion discharge from the surface treater as noted above. The treated fibers were adhered to the wood substrate. After allowing the adhesive to cure 24 hours, the following results were obtained:
Buffered 900 micron fibers were prepared with an AlphaGary MEGOLON 8142 LSZH polyolefin tight buffer layer, and passed three times through the blown-ion discharge from the surface treater as noted above. The treated fibers were adhered to the wood substrate. After allowing the adhesive to cure 24 hours, the following results were obtained:
Buffered 900 micron fibers were prepared with a Huntsman Corp. IROGRAN® A95P5003 LSZH urethane tight buffer layer, and adhered without surface treatment to the wood substrate. After allowing the adhesive to cure 24 hours, the following results were obtained:
Buffered 900 micron fibers were prepared with a Huntsman Corp. IROGRAN A95P5003 LSZH urethane tight buffer layer, and passed once through the blown-ion discharge from the surface treater as noted above. The treated fibers were adhered to the wood substrate. After allowing the adhesive to cure 24 hours, the following results were obtained:
Buffered 900 micron fibers were prepared with a Huntsman Corp. IROGRAN A95P5003 LSZH urethane tight buffer layer, and passed three times through the blown-ion discharge from the surface treater as noted above. The treated fibers were adhered to the wood substrate. After allowing the adhesive to cure 24 hours, the following results were obtained:
The foregoing Examples demonstrate that all four types of untreated LSZH buffered fibers exhibit virtually no adhesion to the wood substrate when the applied adhesive cures, since the adhesive does not sufficiently “wet out” and penetrate the buffer layers of the untreated fibers. By contrast, the same adhesive bonds the PVC buffered control fiber very well to the substrate because of the higher surface energy of the fiber.
When treated, however, all of the four types of LSZH buffered fibers are compatible with the applied adhesive and bond to the wood substrate in varying degrees, as follows:
The ECCOH and HYTREL samples (Examples One to Six) exhibit significant responses, on average, to the 1× and 3× blown-ion surface treatments by bonding to the substrate with somewhat less strength than the PVC buffered control fibers.
The MEGOLON samples (Examples Seven to Nine) exhibit noteworthy responses, on average, to the 1× and 3× blown-ion treatments by bonding to the substrate with about half the strength as the PVC buffered control fibers.
The IROGRAN 1× and 3× blown-ion treated samples (Examples Ten to Twelve) bond to the substrate noticeably better than the untreated samples, but with less than half the strength of the PVC buffered control fibers.
When treated as described herein, the ability of LSZH optical fibers and cables to be installed at customer premises by the use of an inexpensive, water-based consumer grade adhesive will act to expand the number of premises worldwide in which installations like InvisiLight can be performed. The installation is simple, leaves little or no visual impact, and is likely to be accepted by most customers to be carried out at their premises.
While the foregoing represents preferred embodiments of the present invention, it will be understood by persons skilled in the art that various changes, modifications, and additions can be made without departing from the spirit and scope of the invention, and that the invention includes all such changes, modifications, and additions that are within the scope of the following claims.
This application claims priority under 35 U.S.C. §119(e) of U.S. Provisional Patent Application No. 62/327,712 filed Apr. 26, 2016, titled “Surface Treated Cables for Installation at Customer Premises,” the entire contents of which are incorporated by reference.