This application relates to the technical field of batteries, and in particular, to a surface treatment composition, an electrode and a preparation method thereof, a secondary battery, and a device.
In recent years, secondary batteries have been applied wider in many fields, including energy storage power systems such as hydro, thermal, wind, and solar power stations, and other fields such as electric tools, electric bicycles, electric motorcycles, and electric vehicles, military equipment, and aerospace. The great development of the secondary batteries gives rise to higher requirements on the energy density, cycle performance, safety performance, and other performance of the batteries.
In the related art, a surface of a current collector foil is modified before being coated with an active material. However, in the related art, only a single-ingredient surface treatment agent is applied, thereby making very limited improvements to surface properties of the current collector. Therefore, better techniques for surface treatment of a current collector still need to be put forward in this field.
This application is made in view of the above problem. An objective of this application is to provide a novel surface treatment composition. The surface treatment composition is applicable to treatment of a surface of a current collector. After being treated, the current collector and an active material are improved in terms of one or more performance indicators.
To achieve the foregoing objective, a first aspect of this application provides a surface treatment composition, expressed as parts by weight, including:
Without being limited by theory, the surface treatment composition according to this application can form an intermediate layer after being applied to a surface of a current collector foil. The intermediate layer can effectively enhance performance of bonding between the current collector foil and an active material layer, thereby increasing bonding strength and conductivity of an electrode plate.
In some embodiments, the acidic group and/or a salt of the acidic group is selected from an acidic group, an acidic salt group, or a combination thereof. The acidic group is selected from a hydroxyl group, a carboxylic acid group, a sulfonic acid group, or phosphoric acid group. The acidic salt group is selected from a hydroxylate group, a carboxylate group, a sulfonate group, a phosphonate group, or a combination thereof. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, in the first ingredient, a weight percent of the acidic group and/or a salt of the acidic group is 10 wt % to 40 wt %. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, in the second ingredient, a weight percent of a polyether group is 20 wt % to 50 wt %. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, a number-average molecular weight of the first ingredient is 50,000 to 150,000. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, a number-average molecular weight of the second ingredient is 6,000,000 to 10,000,000. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, a solubility of the first ingredient in water at 25° C. is at least g/100 ml. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, a solubility of the second ingredient in water at 25° C. is at least 40 g/100 ml. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the first ingredient includes a substance represented by the following general formula:
In the formula above, one or more of R11, R12, R21, R22, R31, R32, R41, R42, R51, or R52 are the acidic group and/or a salt of the acidic group, and remaining groups are selected from hydrogen, C1 to C6 alkyl, C1 to C6 haloalkyl, and halogen; and n1 is an integer greater than or equal to 1. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, one or more of R11, R12, R21, R22, R31, R32, R41, R42, R51, or R52 are selected from a carboxylic acid group, a sulfonic acid group, a phosphoric acid group, a carboxylate group, a sulfonate group, or a phosphonate group. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, at least one of R11, R12, R21, R22, R31, R32, R41, R42, R51, or R52 is —OH, and at least one thereof is —COOH. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, one of R11, R12, R21, R22, R31, R32, R41, R42, R51, or R52 is —OH, and one thereof is —COOH. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, one of R11, R12, R21, R22, R31, R32, R41, R42, R51, or R52 is —OH, one thereof is —COOH, and the —OH and the —COOH are linked to different carbon atoms. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, one of R41 or R42 is —OH, and one of R21 or R22 is —COOH. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the second ingredient includes a substance represented by the following general formula:
In the formula above, one or more of R61 and R62 are polyether groups; and
R71 is selected from a hydrogen atom, C1 to C10 alkyl, C1 to C10 haloalkyl, and halogen; R72 is selected from carboxyl, a carboxylate group (such as a lithium carboxylate group or a sodium carboxylate group), C1 to C3 alkyl carboxyl, a C1 to C3 alkyl carboxylate group, an ester group, and a C1 to C3 alkyl ester group; and n2 is an integer greater than or equal to 1. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the polyether group is selected from a polyethylene glycol diglycidyl ether group, a polyether polyol group, and a combination thereof. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the ester group is selected from a methyl ester group, a propyl ester group, or a butyl ester group.
In some embodiments, R61 is a hydrogen atom, and R62 is a polyether polyol group. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, R71 is a hydrogen atom, and R72 is selected from a hydrogen atom, C1 to C10 alkyl, C1 to C10 haloalkyl, and halogen. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
According to a second aspect, this application provides an electrode, including:
The intermediate layer contains the surface treatment composition according to any aspect described above.
In some embodiments, the electrode is a negative electrode. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, a material of the current collector includes copper or a copper alloy. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
According to a third aspect, this application provides a secondary battery, including the electrode according to any aspect described above. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
According to a fourth aspect, this application provides a device, including the secondary battery according to any aspect described above. The secondary battery is configured to provide electrical energy to the device. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
Beneficial Effects
One or more embodiments of this application have achieved one or more of the following benefits:
Battery pack 1; upper box 2; lower box 3; battery module 4; secondary battery 5; housing 51; electrode assembly 52; top cap assembly 53; current collector 11; first side 111; second side 112; unwinder 81; first sprayer 82; first active material slurry applicator 83; first dryer 84; second sprayer 85; second active material slurry applicator 86; second dryer 87; rewinder 88.
The following describes and discloses in detail a negative active material and a preparation method thereof, a positive electrode plate, a negative electrode plate, a secondary battery, a battery module, a battery pack, and an electrical device according to this application with due reference to drawings. However, unnecessary details may be omitted in some cases. For example, a detailed description of a well-known matter or repeated description of an essentially identical structure may be omitted. That is intended to prevent the following descriptions from becoming unnecessarily lengthy, and to facilitate understanding by a person skilled in the art. In addition, the drawings and the following descriptions are intended for a person skilled in the art to thoroughly understand this application, but not intended to limit the subject-matter set forth in the claims.
A “range” disclosed herein is defined in the form of a lower limit and an upper limit. A given range is defined by a lower limit and an upper limit selected. The selected lower and upper limits define the boundaries of a particular range. A range so defined may be inclusive or exclusive of the end values, and a lower limit of one range may be arbitrarily combined with an upper limit of another range to form a range. For example, if a given parameter falls within a range of 60 to 120 and a range of 80 to 110, it is expectable that the parameter may fall within a range of 60 to 110 and a range of 80 to 120 as well. In addition, if lower-limit values 1 and 2 are listed, and if upper-limit values 3, 4, and 5 are listed, the following ranges are all expectable: 1 to 3, 1 to 4, 1 to 5, 2 to 3, 2 to 4, and 2 to 5. Unless otherwise specified herein, a numerical range “a to b” is a brief representation of a combination of any real numbers between a and b inclusive, where both a and b are real numbers. For example, a numerical range “0 to 5” herein means all real numbers recited between 0 and 5 inclusive, and the expression “0 to 5” is just a brief representation of a combination of such numbers. In addition, a statement that a parameter is an integer greater than or equal to 2 is equivalent to a disclosure that the parameter is an integer such as 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, and so on.
Unless otherwise expressly specified herein, any embodiments and optional embodiments hereof may be combined with each other to form a new technical solution.
Unless otherwise expressly specified herein, any technical features and optional technical features hereof may be combined with each other to form a new technical solution.
Unless otherwise expressly specified herein, all steps described herein may be performed in sequence or at random, and in some embodiments in sequence. For example, that the method includes steps (a) and (b) indicates that the method may include steps (a) and (b) performed in sequence, or steps (b) and (a) performed in sequence. For example, that the method may further include step (c) indicates that step (c) may be added into the method in any order. For example, the method may include steps (a), (b), and (c), or may include steps (a), (c), and (b), or may include steps (c), (a), and (b), and so on.
Unless otherwise expressly specified herein, “include” and “comprise” mentioned herein mean open-ended inclusion. For example, the terms “include” and “comprise” may mean inclusion of other items that are not recited.
Unless otherwise expressly specified herein, the term “or” is inclusive. For example, the expression “A or B” means “A alone, B alone, or both A and B”. More specifically, any one of the following conditions satisfies the condition “A or B”: A is true (or existent) and B is false (or absent); A is false (or absent) and B is true (or existent); and, both A and B are true (or existent).
[Surface Treatment Composition]
In some embodiments, this application provides a surface treatment composition, expressed as parts by weight, including:
Without being limited by theory, the surface treatment composition according to this application can form an intermediate layer after being applied to a surface of a current collector foil. The intermediate layer can effectively enhance performance of bonding between the current collector foil and an active material layer, thereby increasing bonding strength and conductivity of an electrode plate.
In some embodiments, expressed as parts by weight, the content of the first ingredient in the surface treatment composition is 1 to 3 parts, 3 to 5 parts, 5 to 7 parts, 7 to 9 parts, 9 to 11 parts, 11 to 13 parts, 13 to 15 parts, 15 to 17 parts, 17 to 19 parts, 19 to 21 parts, 21 to 23 parts, 23 to 25 parts, 25 to 27 parts, 27 to 29 parts, or 29 to 30 parts.
In some embodiments, expressed as parts by weight, the content of the second ingredient in the surface treatment composition is 1 to 3 parts, 3 to 5 parts, 5 to 7 parts, 7 to 9 parts, 9 to 11 parts, 11 to 13 parts, 13 to 15 parts, 15 to 17 parts, 17 to 19 parts, 19 to 21 parts, 21 to 23 parts, 23 to 25 parts, 25 to 27 parts, 27 to 29 parts, or 29 to 30 parts.
In some embodiments, the term “polyether-modified” means “containing a polyether group” or “grafted with a polyether group”.
In some embodiments, the term “polyether group” means a repeating —(ORB—)nORA group. For example, the term “polyether” may include —O-alkyl-O-alkyl-O-alkyl-O-alkyl-ORA. The polyether may include 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10 repeating units. RA may be hydrogen, alkyl, alkenyl, alkynyl, cycloalkyl, cycloalkenyl, aryl, heteroaryl, heterocyclyl, cycloalkyl(alkyl), aryl(alkyl), heteroaryl(alkyl), or heterocyclyl(alkyl). RB may be a substituted or unsubstituted C1 to C6 alkylidene. RA may be further substituted or unsubstituted independently.
In some embodiments, the term “polyether polyol” means a group in which a main chain contains ether linkages (—R—O—R—, where R is an alkane or an aromatic hydrocarbon group) and in which an end-group or pendant group contains more than 2 hydroxyl groups (—OH).
In some embodiments, the polyether is prepared from a raw material by a polyaddition reaction in the presence of a catalyst, where the raw material is ethylene oxide (EO), propylene oxide (PO), butylene oxide (BO), or the like.
In some embodiments, the acidic group and/or a salt of the acidic group is selected from: an acidic group, an acidic salt group, or a combination thereof.
In some embodiments, the first ingredient is selected from: a polycaprolactone modified with an acidic group, a polycaprolactone modified with a salt of the acidic group, or a combination thereof.
In some embodiments, the acidic group and/or a salt of the acidic group is selected from an acidic group, an acidic salt group, or a combination thereof. The acidic group is selected from a hydroxyl group, a carboxylic acid group, a sulfonic acid group, or phosphoric acid group. The acidic salt group is selected from a hydroxylate group, a carboxylate group, a sulfonate group, a phosphonate group, or a combination thereof. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the acidic group is selected from: a carboxylic acid group, a sulfonic acid group, a phosphoric acid group, or a combination thereof.
In some embodiments, the salt of the acidic group is selected from: a carboxylate group, a sulfonate group, a phosphonate group, or a combination thereof.
In some embodiments, the salt of the acidic group is selected from: a lithium hydroxylate group, a lithium carboxylate group, a lithium sulfonate group, a lithium phosphonate group, a sodium hydroxylate group, a sodium carboxylate group, a sodium sulfonate group, a sodium phosphonate group, or a combination thereof.
In some embodiments, the acidic group and/or a salt of the acidic group is selected from: carboxylic acid group, a sulfonic acid group, a phosphoric acid group, a carboxylate group, a sulfonate group, a phosphonate group, or a combination thereof. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the surface treatment composition further includes a solvent. The solvent may be water, for example.
In some embodiments, the surface treatment composition is a surface treatment solution, such as an aqueous solution.
In some embodiments, a concentration of the first ingredient in the surface treatment solution is 1 wt % to 50 wt %, for example, 1 wt % to 10 wt %, 10 wt % to 20 wt %, 20 wt % to 30 wt %, 30 wt % to 40 wt %, or 40 wt % to 50 wt %.
In some embodiments, a weight percent of the second ingredient in the surface treatment solution is 1 wt % to 50 wt %, for example, 1 wt % to 10 wt %, 10 wt % to 20 wt %, 20 wt % to 30 wt %, 30 wt % to 40 wt %, or 40 wt % to 50 wt %.
In some embodiments, in the first ingredient, a weight percent of the acidic group and/or a salt of the acidic group is 10 wt % to 40 wt % (for example, 10% to 15%, 15% to 20%, 20% to 25%, 25% to 30%, 30% to 35%, or 35% to 40%). In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, in the second ingredient, a weight percent of the polyether group is 20 wt % to 50 wt % (for example, 20% to 25%, 25% to 30%, 30% to 35%, 35% to 40%, 40% to 45%, or 45% to 50%). In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, a number-average molecular weight of the first ingredient is 50,000 to 150,000 (for example, 50,000 to 80,000, 80,000 to 110,000, 110,000 to 140,000, or 140,000 to 150,000). In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, a number-average molecular weight of the second ingredient is 6,000,000 to 10,000,000 (for example, 6,000,000 to 6,500,000, 6,500,000 to 7,000,000, 7,000,000 to 7,500,000, 7,500,000 to 8,000,000, 8,000,000 to 8,500,000, 8,500,000 to 9,000,000, 9,000,000 to 9,500,000, or 9,500,000 to 10,000,000). In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, a solubility of the first ingredient in water at 25° C. is at least g/100 ml (for example, 40 g/100 ml to 50 g/100 ml, 50 g/100 ml to 60 g/100 ml, 60 g/100 ml to 70 g/100 ml, 70 g/100 ml to 80 g/100 ml, 80 g/100 ml to 90 g/100 ml, or 90 g/100 ml to 100 g/100 ml). In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, a solubility of the second ingredient in water at 25° C. is at least 40 g/100 ml (for example, 40 g/100 ml to 50 g/100 ml, 50 g/100 ml to 60 g/100 ml, 60 g/100 ml to 70 g/100 ml, 70 g/100 ml to 80 g/100 ml, 80 g/100 ml to 90 g/100 ml, or 90 g/100 ml to 100 g/100 ml). In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the first ingredient includes a substance represented by the following general formula:
In the formula above, one or more of R11, R12, R21, R22, R31, R32, R41, R42, R51, or R52 are the acidic group and/or a salt of the acidic group, and remaining groups are selected from hydrogen, C1 to C6 alkyl, C1 to C6 haloalkyl, and halogen; and n1 is an integer greater than or equal to 1. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the C1 to C6 alkyl is methyl, ethyl, propyl, butyl, pentyl, or hexyl.
In some embodiments, one or more of R11, R12, R21, R22, R31, R32, R41, R42, R51, or R52 are selected from a carboxylic acid group, a sulfonic acid group, a phosphoric acid group, a carboxylate group, a sulfonate group, a phosphonate group, or a combination thereof.
In some embodiments, at least one of R11, R12, R21, R22, R31, R32, R41, R42, R51, or R52 is —OH, and at least one thereof is —COOH. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, at least one of R11R12, R21, R22, R31, R32, R41, R42, R51, or R52 is —OH, and at least one thereof is selected from a carboxylic acid group, a sulfonic acid group, a phosphoric acid group, a carboxylate group, a sulfonate group, a phosphonate group, or a combination thereof. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, one of R11, R12, R21, R22, R31, R32, R41, R42, R51, or R52 is —OH, and one thereof is —COOH. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, one of R11, R12, R21, R22, R31, R32, R41, R42, R51, or R52 is —OH, one thereof is —COOH, and the —OH and the —COOH are linked to different carbon atoms. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, one of R41 or R42 is —OH, and one of R21 or R22 is —COOH. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the second ingredient includes a substance represented by the following general formula:
In the formula above, one or more of R61 and R62 are polyether groups; and
R71 is selected from a hydrogen atom, C1 to C10 alkyl, C1 to C10 haloalkyl, and halogen; R72 is selected from carboxyl, a carboxylate group (such as a lithium carboxylate group or a sodium carboxylate group), C1 to C3 alkyl carboxyl, a C1 to C3 alkyl carboxylate group, an ester group, and a C1 to C3 alkyl ester group; and n2 is an integer greater than or equal to 1. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the C1 to C3 alkyl carboxyl includes methyl carboxyl, ethyl carboxyl, or propyl carboxyl.
In some embodiments, the polyether group is selected from a polyethylene glycol diglycidyl ether group, a polyether polyol group, and a combination thereof. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, R61 is a hydrogen atom, and R62 is a polyether polyol group. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, R71 is a hydrogen atom, and R72 is selected from a hydrogen atom, C1 to C10 alkyl, C1 to C10 haloalkyl, and halogen. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
According to a second aspect, this application provides an electrode, including:
The intermediate layer contains the surface treatment composition according to any aspect described above.
In some embodiments, the binder contained in the active material layer may include at least one selected from: styrene butadiene rubber (SBR), acrylonitrile butadiene rubber, acrylic rubber, butyl rubber, fluororubber, carboxymethyl cellulose (CMC), starch, hydroxypropyl cellulose, regenerated cellulose, polyvinyl alcohol (PVA), polyacrylic acid (PAA), polyethylene glycol (PEG), polyacrylonitrile (PAN), and polyacrylamide (PAM). In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the active material layer contains at least a binder styrene-butadiene rubber. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the electrode is a negative electrode. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, a material of the current collector includes copper or a copper alloy. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
In some embodiments, the method for preparing an electrode includes:
According to a third aspect, this application provides a secondary battery, including the electrode according to any aspect described above. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
According to a fourth aspect, this application provides a device, including the secondary battery according to any aspect described above. The secondary battery is configured to provide electrical energy to the device. In this way, the surface treatment composition can improve the bonding force between the current collector foil and the active material layer and enhance the bonding performance more effectively.
[Secondary Battery]
A secondary battery, also known as a rechargeable battery or storage battery, is a battery that is reusable after an active material in the battery is activated by charging the battery that has been discharged.
Generally, a secondary battery includes a positive electrode plate, a negative electrode plate, a separator, and an electrolytic solution. During charge and discharge of the battery, active ions (such as lithium ions) are shuttled between the positive electrode plate and the negative electrode plate by intercalation and deintercalation. Disposed between the positive electrode plate and the negative electrode plate, the separator primarily serves to prevent a short circuit between the positive electrode plate and the negative electrode plate, and is penetrable by the active ions. The electrolytic solution is located between the positive electrode plate and the negative electrode plate, and primarily serves to conduct the active ions.
[Positive Electrode Plate]
A positive electrode plate generally includes a positive current collector and a positive film layer that overlays at least one surface of the positive current collector. The positive film layer includes a positive active material. A surface treatment composition may be disposed between the positive current collector and the positive film layer.
As an example, the positive current collector includes two surfaces opposite to each other in a thickness direction of the positive current collector. The positive film layer is disposed on either or both of the two opposite surfaces of the positive current collector.
In some embodiments, the positive current collector may be a metal foil or a composite current collector. For example, the metal foil may be an aluminum foil. The composite current collector may include a polymer material substrate and a metal layer formed on at least one surface of the polymer material substrate. The composite current collector may be formed by overlaying the polymer material substrate with a metal material (for example, aluminum, aluminum alloy, nickel, nickel alloy, titanium, titanium alloy, silver, and silver alloy). The polymer material substrate may be, for example, polypropylene (PP), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polystyrene (PS), or polyethylene (PE).
In some embodiments, the positive active material may be a positive active material that is well known for use in a battery in the art. As an example, the positive active material may include at least one of the following materials: olivine-structured lithium-containing phosphate, lithium transition metal oxide, and a modified compound thereof. However, this application is not limited to such materials, and other conventional materials usable as a positive active material of a battery may be used instead. One of the positive active materials may be used alone, or at least two thereof may be used in combination. Examples of the lithium transition metal oxide may include, but without being limited to, at least one of lithium cobalt oxide (such as LiCoO2), lithium nickel oxide (such as LiNiO2), lithium manganese oxide (such as LiMnO2 and LiMn2O4), lithium nickel cobalt oxide, lithium manganese cobalt oxide, lithium nickel manganese oxide, lithium nickel cobalt manganese oxide (such as LiNi1/3Co1/3Mn1/3O2 (briefly referred to as NCM333), LiNi0.5Co0.2Mn0.3O2 (briefly referred to as NCM523), LiNi0.5Co0.25Mn0.25O2 (briefly referred to as NCM211), LiNi0.6Co0.2Mn0.2O2 (briefly referred to as NCM622), LiNi0.8Co0.1Mn0.1O2 (briefly referred to as NCM811)), lithium nickel cobalt aluminum oxide (such as LiNi0.85Co0.15Al0.05O2), or a modified compound thereof. Examples of the olivine-structured lithium-containing phosphate may include, but without being limited to, at least one of lithium iron phosphate (such as LiFePO4 (briefly referred to as LFP)), a composite of lithium iron phosphate and carbon, lithium manganese phosphate (such as LiMnPO4), a composite of lithium manganese phosphate and carbon, lithium manganese iron phosphate, or a composite of lithium manganese iron phosphate and carbon.
In some embodiments, the positive film layer further optionally includes a surface treatment composition. As an example, the surface treatment composition may include at least one of polyvinylidene difluoride (PVDF), polytetrafluoroethylene (PTFE), poly(vinylidene fluoride-co-tetrafluoroethylene-co-propylene), poly (vinylidene fluoride-co-hexafluoropropylene-co-tetrafluoroethylene), poly(tetrafluoroethylene-co-hexafluoropropylene), or fluorinated acrylate resin.
In some embodiments, the positive film layer further optionally includes a conductive agent. As an example, the conductive agent may include at least one of superconductive carbon, acetylene black, carbon black, Ketjen black, carbon dots, carbon nanotubes, graphene, or carbon nanofibers.
In some embodiments, the positive electrode plate may be prepared according to the following method: dispersing the ingredients of the positive electrode plate such as the positive active material, the conductive agent, the surface treatment composition, and any other ingredients into a solvent (such as N-methyl-pyrrolidone) to form a positive slurry, coating a positive current collector with the positive slurry, and performing steps such as drying and cold calendering to obtain the positive electrode plate.
[Negative Electrode Plate]
The negative electrode plate includes a negative current collector and a negative film layer disposed on at least one surface of the negative current collector. The negative film layer includes a negative active material. A surface treatment composition may be disposed between the negative current collector and the negative film layer.
As an example, the negative current collector includes two surfaces opposite to each other in a thickness direction of the negative current collector. The negative film layer is disposed on either or both of the two opposite surfaces of the negative current collector.
In some embodiments, the negative current collector may be a metal foil or a composite current collector. For example, the metal foil may be a copper foil. The composite current collector may include a polymer material substrate and a metal layer formed on at least one surface of the polymer material substrate. The composite current collector may be formed by overlaying the polymer material substrate with a metal material (for example, copper, copper alloy, nickel, nickel alloy, titanium, titanium alloy, silver, and silver alloy). The polymer material substrate may be, for example, polypropylene (PP), polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polystyrene (PS), or polyethylene (PE).
In some embodiments, the negative active material may be a negative active material well known for use in a battery in the art. As an example, the negative active material may include at least one of the following materials: artificial graphite, natural graphite, soft carbon, hard carbon, silicon-based material, tin-based material, lithium titanium oxide, and the like. The silicon-based material may be at least one selected from simple-substance silicon, a silicon-oxygen compound, a silicon-carbon composite, a silicon-nitrogen composite, and a silicon alloy. The tin-based material may be at least one selected from simple-substance tin, a tin-oxygen compound, or a tin alloy. However, this application is not limited to such materials, and other conventional materials usable as a negative active material of a battery may be used instead. One of the negative active materials may be used alone, or at least two thereof may be used in combination.
In some embodiments, the negative film layer further optionally includes a surface treatment composition. As an example, the surface treatment composition may be at least one selected from styrene-butadiene rubber (SBR), polyacrylic acid (PAA), polyacrylic acid sodium (PAAS), polyacrylamide (PAM), polyvinyl alcohol (PVA), sodium alginate (SA), polymethyl acrylic acid (PMAA), and carboxymethyl chitosan (CMCS).
In some embodiments, the negative film layer further optionally includes a conductive agent. As an example, the conductive agent may be at least one selected from superconductive carbon, acetylene black, carbon black, Ketjen black, carbon dots, carbon nanotubes, graphene, or carbon nanofibers.
In some embodiments, the negative film layer further optionally includes other agents, such as a thickener (for example, sodium carboxymethyl cellulose (CMC-Na)).
In some embodiments, the negative electrode plate may be prepared according to the following method: dispersing the ingredients of the negative electrode plate such as the negative active material, the conductive agent, the surface treatment composition, and any other ingredients in a solvent (such as deionized water) to form a negative slurry, coating a negative current collector with the negative slurry, and performing steps such as drying and cold calendering to obtain a negative electrode plate.
[Electrolyte]
The electrolyte serves to conduct ions between the positive electrode plate and the negative electrode plate. The type of the electrolyte is not particularly limited in this application, and may be selected as required. For example, the electrolyte may be in a liquid state or gel state, or all solid state.
In some embodiments, the electrolyte is in a liquid state and includes an electrolyte salt and a solvent.
In some embodiments, the electrolyte salt may be at least one selected from lithium hexafluorophosphate, lithium tetrafluoroborate, lithium perchlorate, lithium hexafluoroarsenate, lithium bisfluorosulfonimide, lithium bistrifluoromethanesulfonimide, lithium trifluoromethanesulfonate, lithium difluorophosphate, lithium difluoro(oxalato)borate, lithium bis(oxalato)borate, lithium difluoro(bisoxalato)phosphate, and lithium tetrafluoro(oxalato)phosphate.
In some embodiments, the solvent may be at least one selected from ethylene carbonate, propylene carbonate, ethyl methyl carbonate, diethyl carbonate, dimethyl carbonate, dipropyl carbonate, methyl propyl carbonate, ethylene propyl carbonate, butylene carbonate, fluoroethylene carbonate, methyl formate, methyl acetate, ethyl acetate, propyl acetate, methyl propionate, ethyl propionate, propyl propionate, methyl butyrate, ethyl butyrate, 1,4-butyrolactone, sulfolane, methyl sulfonyl methane, ethyl methyl sulfone, and (ethyl sulfonyl)ethane.
In some embodiments, the electrolytic solution further optionally includes an additive. As an example, the additive may include a negative film-forming additive or a positive film-forming additive. The additive may further include an additive capable of improving some performance of the battery, for example, an additive for improving overcharge performance of the battery, or an additive for improving high- or low-temperature performance of the battery.
[Separator]
In some embodiments, the secondary battery further includes a separator. The type of the separator is not particularly limited in this application, and may be any well-known porous separator that is highly stable both chemically and mechanically.
In some embodiments, the separator may be made of a material that is at least one selected from glass fiber, non-woven fabric, polyethylene, polypropylene, or polyvinylidene difluoride. The separator may be a single-layer film or a multilayer composite film, without being particularly limited. When the separator is a multilayer composite film, materials in different layers may be identical or different, without being particularly limited.
In some embodiments, the positive electrode plate, the negative electrode plate, and the separator may be made into an electrode assembly by winding or stacking.
In some embodiments, the secondary battery may include an outer package. The outer package may be configured to package the electrode assembly and the electrolyte.
In some embodiments, the outer package of the secondary battery may be a hard shell such as a hard plastic shell, an aluminum shell, a steel shell, or the like. Alternatively, the outer package of the secondary battery may be a soft package such as a pouch-type soft package. The soft package may be made of plastic such as polypropylene, polybutylene terephthalate, or polybutylene succinate.
The shape of the secondary battery is not particularly limited in this application, and may be cylindrical, prismatic or any other shape. For example,
In some embodiments, referring to
In some embodiments, the secondary battery may be assembled into a battery module. The battery module may include one or more secondary batteries, and the specific number of secondary batteries in a battery module may be selected by a person skilled in the art depending on practical applications and capacity of the battery module.
Optionally, the battery module 4 may further include a shell that provides an accommodation space. The plurality of secondary batteries 5 are accommodated in the accommodation space.
In some embodiments, the battery module may be assembled to form a battery pack. The battery pack may include one or more battery modules, and the specific number of battery modules in a battery pack may be selected by a person skilled in the art depending on practical applications and capacity of the battery pack.
Further, this application provides an electrical device. The electrical device includes at least one of the secondary battery, the battery module, or the battery pack according to this application. The secondary battery, the battery module, or the battery pack may be used as a power supply of the electrical device, or used as an energy storage unit of the electrical device. The electrical device may include, but without being limited to, a mobile device (such as a mobile phone or a laptop computer), an electric vehicle (such as a battery electric vehicle, a hybrid electric vehicle, a plug-in hybrid electric vehicle, an electric bicycle, an electric scooter, an electric golf cart, or an electric truck), an electric train, a ship, a satellite system, or an energy storage system.
The secondary battery, the battery module, or the battery pack may be selected for use in the electrical device according to practical requirements of the electrical device.
The following describes embodiments of this application. The embodiments described below are illustrative, and are merely intended to construe this application but not to limit this application. Unless other techniques or conditions are expressly specified in an embodiment hereof, the techniques or conditions described in the literature in this field or in an instruction manual of the product may apply. A reagent or instrument used herein without specifying the manufacturer is a conventional product that is commercially available in the market.
I. Details of Raw Materials
The raw materials used in some embodiments are shown below:
Ingredients 1 and 2 are a polycaprolactone modified with an acid group, represented by a general formula:
In the formula above, n1 is an integer greater than or equal to 1.
The groups R11, R12, R21, R22, R31, R32, R41, R42, R51, and R52 of ingredients 1.1 to 1.9 are shown in the following table:
The ingredient 2 is a polyether-modified polyacrylic ester, and is represented by a general formula:
In the formula above, n2 is an integer greater than or equal to 1.
The groups R61, R62, R71, and R72 of ingredients 2.1 to 2.5 are shown in the following table:
The structural formula of the polyether polyol group in Table 3 is:
In the formula above, n3 is an integer greater than or equal to 1.
II. Ingredients of a Surface Treatment Solution
III. Formula of an Active Material Slurry
On a dry weight basis, mixing graphite (active material), sodium carboxymethyl cellulose (dispersant), styrene-butadiene emulsion (binder), carbon black (conductive agent) at a ratio of 96.2:1.0:1.8:1.0, and stirring well to obtain an active material slurry (negative slurry).
IV. Preparing an Electrode (Negative Electrode)
Embodiments 2 to 17 differ from Embodiment 1 in that the surface treatment solution (S2 to S17) set out in Table 4 and corresponding to each embodiment is used in place of the surface treatment solution S1 used in Embodiment 1. Other steps and parameters are identical to those in Embodiment 1.
Comparative Embodiments 1 to 7 differ from Embodiment 1 in that the surface treatment solution (D1 to D5) set out in Table 4 and corresponding to each comparative embodiment is used in place of the surface treatment solution S1 used in Embodiment 1. Other steps and parameters are identical to those in Embodiment 1. The surface treatment solution D1 is pure water containing neither the ingredient 1 nor the ingredient 2.
IV. Testing the Electrode Performance
(1) Testing Surface Energy
A method for testing the surface energy is described below:
Table 5 shows the test results.
(2) Testing the Tensile Strength
A method for testing the tensile strength is described below:
Table 5 shows the test results.
(3) Testing the Bonding Strength
A method for testing the bonding strength is described below:
(4) Testing the Film Resistance
A method for testing the film resistance is described below:
Table 5 shows the test results.
The test results are analyzed below:
Considering that the surface treatment solution in Comparative Embodiment 1 contains neither the ingredient 1 nor the ingredient 2, the performance of the electrode plate in Comparative Embodiment 1 serves as a reference.
The surface treatment solution in Comparative Embodiment 2 contains the ingredient 1 (12 wt %) alone, and the increase rates of the surface energy, tensile strength, and bonding strength of the surface treatment solution are 0%, 6.7%, and 15%, respectively, in contrast to Comparative Embodiment 1.
The surface treatment solution in Comparative Embodiment 3 contains the ingredient 2 (18 wt %) alone, and the increase rates of the surface energy, tensile strength, and bonding strength of the surface treatment solution are 6.7%, 5.3%, and 10%, respectively, in contrast to Comparative Embodiment 5.
The surface treatment solution in Embodiment 3 contains both the ingredient 1 (12 wt %) and the ingredient 2 (18 wt %), and the increase rates of the surface energy, tensile strength, and bonding strength of the surface energy solution are 33.3%, 33.3%, and 65%, respectively, in contrast to Comparative Embodiment 4, and are significantly higher than a simple sum of the three values in Comparative Embodiments 1 and 2 separately. The above results indicate that a synergistic effect is achieved between the polycaprolactone modified with the acid group or with a salt of the acidic group and the polyether-modified polyacrylic ester.
The ingredients 1 and 2 in Comparative Embodiments 4 to 5 are added at a weight percent falling beyond the range specified in this application, and therefore, fail to achieve a synergistic effect, and fail to effectively improve the surface energy, tensile strength, and bonding strength of the electrode plate.
The above test results show that this application successfully provides a novel surface treatment composition that, expressed as parts by weight, includes: a first ingredient 1 to 30 parts; and a second ingredient 1 to 30 parts. The first ingredient is a polycaprolactone modified with an acidic group and/or with a salt of the acidic group; and the second ingredient is selected from polyether-modified polyolefin acid, polyether-modified polyalkenoate salt, polyether-modified polyalkenoate ester, or a combination thereof.
The novel surface treatment composition according to this application is configured to treat a current collector, and exhibits one or more of the following beneficial effects:
It is hereby noted that this application is not limited to the foregoing embodiments. The foregoing embodiments are merely examples. Any and all embodiments with substantively the same composition or exerting the same effects as the technical ideas hereof without departing from the scope of the technical solutions of this application still fall within the technical scope of this application. In addition, all kinds of variations of the embodiments conceivable by a person skilled in the art and any other embodiments derived by combining some constituents of the embodiments hereof without departing from the subject-matter of this application still fall within the scope of this application.
This application is a continuation of International Application No. PCT/CN2022/074634, filed on Jan. 28, 2022, the entire content of which is incorporated herein by reference.
Number | Date | Country | |
---|---|---|---|
Parent | PCT/CN2022/074634 | Jan 2022 | US |
Child | 18337135 | US |