Claims
- 1. In a method for the surface treatment of a rolling mill roll, including depositing on the roll surface a layer of a material which is at least partly metallic, directing an intermittent laser beam at the surface of said layer while rotating said roll about its longitudinal axis, melting the layer surface in each successive impact zone of the laser beam, forming in said impact zone a microcrater surrounded by a rim and solidifying the rim, the successive microcraters being distributed according to a determined pattern in order to impart a controlled roughness to said surface, the improvement comprising providing the material of said layer with at least one hardening component or at least one component which can react with at least one constituent of the material of said roll to form said hardening component, melting also the material of said roll surface in the successive impact areas of the laser beam, alloying said molten roll material with said molten layer material in said impact areas, and forming an alloyed rim around each of said microcraters.
- 2. The method of claim 1 wherein said hardening component is a carbide or a nitride.
- 3. The method of claim 1 wherein said roll is a roll for a cold rolling mill.
- 4. The process of claim 1, in which the metallic substance is selected from the group consisting of nickel, chromium, cobalt, and alloys of at least two of these metals.
- 5. The process of claim 1, in which the coating comprises at least one metallic oxide.
- 6. The process of claim 5, in which the coating comprises a metal and an oxide of the metal.
- 7. The process of claim 1, in which the coating is applied in a plurality of layers.
Priority Claims (1)
| Number |
Date |
Country |
Kind |
| 6/48029 |
Nov 1984 |
BEX |
|
BACKGROUND OF THE INVENTION
This is a continuation of application Ser. No. 797,439, filed Nov. 13, 1985 now abandoned.
1. Field of Invention
The present invention relates to rolling mill rolls and to process for the surface treatment of such rolls. It relates more particularly to a process for marking cold strip mill rolls so as to provide steel strip with controlled roughness.
2. Description of Prior Art
A process for marking the surface of a rolling mill roll by means of an intermittent laser beam is already known from a number of prior publications by the assignees of the applicants, in particular their Belgian Pat. No. 870,609. This known process brings about the formation of micro-craters on the surface which are distributed according to a predetermined pattern and which, being impressed into the surface of the steel, provide the required roughness. Very good results have been obtained with rolls treated in this way.
When the roughness has worn away, the rolls have to be reconditioned in order for the surface to return to its original condition. A worn roll has to be removed from the rolling mill, ground, and re-marked, then re-assembled in the rolling mill. These operations and the work and adjustment which they require are costly and this affects the cost of the roll. It would therefore be preferable to increase the period of time between reconditionings, i.e. to decrease the rate of wear of the roughness.
What is desired is a process which allows this objective to be attained.
The invention is based on the discovery that in the impact zone of the laser beam, the roll surface is the point of localised fusion, forcing back the molten metal towards the edge of this zone. Thus a metal rim which solidifies very quickly is formed around the micro-crater obtained, as a result of the very short duration of the laser pulse which causes it to occur. The said rim is of great importance in forming the controlled roughness of the steel strip rolled by means of the said roll. The applicants have devised original means for increasing the hardness of the rim, taking advantage of its method of formation, and thus for improving the useful life of the roll itself. The process can, incidentally, be used to harden the entire region affected by laser radiation.
To this end, the invention provides a surface treatment process for a rolling mill roll, in which the surface of the said roll is marked by means of an intermittent laser beam, and in which, before the said markings is carried out, a coating which comprises at least in part a metallic substance, is applied to the said surface.
According to a particular embodiment of the process of the invention, a metallic coating comprising nickel, chromium, cobalt, or an alloy of at least two of these metals, is applied to the surface of the roll.
According to another embodiment, a coating comprising at least one metal and at least one metallic oxide is applied to the surface of the roll. The metallic oxide may be derived from a different metal from that which is used in the composition of the coating. It has, however, proved to be advantageous to use an oxide of a metal which is also present in the coating. For example, the presence of nickel oxide associated with nickel increases the amount of energy from the laser beam absorbed by the surface. The result of this is, on the one hand, increased depth of fusion and consequently increased depth of roughness, and on the other hand improved alloying of the metal of the roll with the nickel and greater hardness of the solidified rim.
According to a further embodiment of the process of the invention, a coating or a powder comprising at least one hardening constituent, such as a carbide or a nitride, and/or at least one constituent which reacts with at least one constituent of the material of the said roll to form the said hardening constituent.
The coating may be applied using any method known per se which is appropriate to the coating material used. By way of non-limiting example, known coating methods which can be used include, in particular, electrolysis, electrophoresis, vapor deposition, or ion implantation. A powder may also be deposited using a suitable method.
From the characteristics which have just been discussed, it can be seen that, in the case of the invention, the coating applied to the surface of the said roll advantageously comprises a substance, or at least one component, which can be alloyed with the locally melted material of the roll and/or can react with at least one of the components of the said material.
In these conditions, the above-mentioned hardening effect which results from the alloying or reaction is localised substantially in the rims which surround the micro craters, i.e. in those regions which are used for impressing the roughness into the laminated steel via the said roll. This embodiment therefore provides maximum efficiency of the process of the invention.
US Referenced Citations (4)
| Number |
Name |
Date |
Kind |
|
281596 |
Wilmot |
Jul 1883 |
|
|
3177558 |
Gronholz et al. |
Apr 1965 |
|
|
4433032 |
Nakamura et al. |
Feb 1984 |
|
|
4507366 |
Wergiun et al. |
Mar 1985 |
|
Foreign Referenced Citations (3)
| Number |
Date |
Country |
| 0090428 |
Oct 1983 |
EPX |
| 2086561 |
Dec 1971 |
FRX |
| 0002661 |
Jan 1985 |
JPX |
Continuations (1)
|
Number |
Date |
Country |
| Parent |
797439 |
Nov 1985 |
|
Patent Grant
4850089