Surgical filament from polypropylene blended with polyethylene

Abstract

Surgical filaments such as sutures and ligatures are made from a blend of polypropylene and linear low density polyethylene.

Description

This invention relates to surgical filaments made from a polypropylene-polyethylene blend.

BACKGROUND OF THE INVENTION

Surgical filaments such as sutures and ligatures have been made from a variety of different materials. Some of these are degraded in the tissue after a certain period. Others remain unchanged. Polypropylene sutures are preferred by the medical profession on account of their extreme inertness. The properties can be summarized as follows:

a. they resist breakdown and do not promote infection; b. they maintain their in vivo tensile strength over extended periods; c. they show minimal reaction with body tissue; d. they have high tensile strength; e. they pass easily through body tissue; and f. they have good knot security.

The preferred polypropylene suture used in the medical profession today is described by Listner in U.S. Pat. No. 3,630,205.

The suture described by Listner has the following properties:

______________________________________Tensile Strength 3.9-8.9 g/den about 320-730 N/mm.sup.2Knot Strength 3.3-7.9 g/den about 270-650 N/mm.sup.2Break Elongation 36-62%Young's Modulus 2200-3680 N/mm.sup.2______________________________________

As good as the current polypropylene sutures are, there is some room for improvement. In particular, it would be desirable to increase the compliance, limpness, or flexibility of polypropylene sutures in order to make them easier to tie and to improve their knot security. The problem is that previous efforts to accomplish this have occasioned a concomitant undesirable decrease in strength properties.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 shows flexibility determination of the sutures according to the invention using an Instron tester equipped with a special adapter.

Recent developments have led to improved properties by using copolymers of propylene and ethylene (U.S. patent application Ser. No. 531,246). This material contains a few ethylene moieties in the polypropylene main chain. These moieties increase the flexibility.

In another approach it has been tried to add polyethylene to polypropylene because polyethylene has some of the desired properties. For these mixtures, conventional high density polyethylenes were used.

A description of commercially available polyethylene sutures is given in several patents (U.S. Pat. Nos. 3,105,493 and 3,359,983). They show good flexibility and limpness, but have poor in vivo strength retention and have in general tensile values which are about 50% lower than those found for polypropylene. In addition, these sutures show elongations which are more than twice as high as polypropylene. This is undesirable as it impedes tie down properties.

In sutures which are made of mixtures of polyethylene and polypropylene, the flexbility is indeed markedly increased. But at the same time some strength is lost, which is not acceptable for the surgeon. So these materials have never become important commercially.

Therefore, a new material was sought, which combines high compliance or flexibility, good knot security, and easy handling properties, along with the inertness of polypropylene. Polypropylene is a suture that is mainly used for applications where long-term stability and long-term wound support is required. Therefore, inertness, low tissue reaction, and above all, high level strength retention, are of extreme importance.

DETAILED DESCRIPTION OF THE INVENTIONS

According to this invention, mixtures of linear low density polyethylene (LLDPE) and polypropylene are used to make surgical filaments such as sutures and ligatures. It is surprising to note that when this special type of polyethylene is added in small amounts to polypropylene, the tensile strength is not lowered. It is significantly better than with pure polypropylene, but even more surprisingly, sharp decrease in stiffness or increase in compliance is observed. Break elongation is somewhat higher than for polypropylene, but far lower than for polyethylene. Interestingly enough, the Young's Modulus is also much lower for this new material than for either pure polypropylene or mixtures of polypropylene with conventional polyethylenes.

Linear low density polyethylene is a known material that is commercially available. It has a density of from 0.91 to 0.95 gram/cubic centimeter, and a melting point of 115.degree.-130.degree. C.

The polymer blend which was employed to extrude the suture consisted of high-molecular weight polypropylene which was preferably isotactic. Melt flow indexes (MFI 230/2.16) ranged from about 0.3 to about 11. Preferred are MFI values in the range of 0.3 to 3 in order to obtain high tensile strengths. The linear low density polyethylene used had melt flow indexes in the range of MFI (230/2.16) 0.3 to 70.

Polyethylene was used in concentrations of 0.1% to 25% by weight, preferably ranging from 1% to 16%. The polymer blend can contain colorants such as dyes or pigments, and stabilizers against heat, ultraviolet radiation and oxidation. Antistatic or antiblock additives, and lubricants may also be added, as well as radiopaque components such as barium sulfate (in amounts up to about 60 percent, by weight, i.e., up to about 25 percent, by volume).

The sutures can be produced by extruding the polymer into filaments and subsequently orienting and annealing. Filament size can range from 1 denier for yarns up to size metric 5 (Ph. Eur.) (2 USP). Examples are given below. The sutures can then be attached to needles by common procedures. The filaments can also be braided, woven or knitted to form sutures or other devices for medical applications. The finished articles can be packed and sterilized for surgical applications.

EXAMPLE 1

The polymer blend contained 16% linear low density polyethylene of MFI (230/2.16) 1.0 and 84% polypropylene of MFI (230/2.16) 1.8, the percentages being based on weight of polyethylene plus polypropylene.

The material was processed as follows:

______________________________________Extrusion Orientationtemperature 240.degree. C. Draw Ratio 8.0die diameter 1 mm oven temperature 150.degree. C.pump pressure 7 MPaAnnealingrelaxation ratio 0.82oven temperature 150.degree. C.residence time 40 sec.______________________________________

The resulting suture was 3.5 metric in size (#0 USP). The properties are shown below in Table I.

EXAMPLES 2 TO 5

Further samples were prepared as described above, from the same polyethylene and polypropylene. Conditions are summarized in Table III. They are compared to values for conventional polypropylene sutures which are commercially available (Table II).

TABLE I______________________________________Physical Properties of Sutures According to Invention flex- knot straight break ural Di- intrin- intrin- elonga- modu- PE ameter, sic, sic, tion, lus, content,Sample .mu.m N/mm.sup.2 N/mm.sup.2 % N/mm.sup.2 %______________________________________1 380 360 410 46 1600 162 304 405 430 30 2500 43 247 425 465 39 4480 84 173 510 550 33 4090 25 137 530 620 28 4320 12______________________________________ TABLE II______________________________________Physical Properties of Commercially AvailablePolypropylene flex- knot straight break ural Di- intrin- intrin- elonga- modu- PE ameter, sic, sic, tion, lus, content,Sample .mu.m N/mm.sup.2 N/mm.sup.2 % N/mm.sup.2 %______________________________________-- 375 340 360 31 2870 ---- 319 400 360 33 3840 ---- 245 420 390 26 10,100 ---- 182 410 420 30 13,100 ---- 139 440 490 29 14,800 --______________________________________

The improved compliance, as illustrated by a reduction in flexural modulus, is striking.

TABLE III______________________________________Experimental Conditions Sample Sample Sample Sample Sample 1 2 3 4 5______________________________________Extrusiontemperature 240 250 250 250 240(.degree.C.)Die Diameter 1 1 0.75 0.5 0.5(mm)Pump Pressure 7 7 7 7 7(MPa)Orientationdraw ratio 8.0 9.0 9.0 9.0 8.5oven temper- 150 150 150 150 150ature (.degree.C.)Annealingrelaxation 0.82 0.77 0.77 0.77 0.82ratiooven temper- 150 130 130 130 150ature (.degree.C.)residence 40 40 70 70 40(sec.)______________________________________

Methods

Tensile strengths in straight pulls were tested on an Instron tester with a crosshead speed of 200 mm/min and a gauge 100 mm in length. Knot pull tensile strength was tested identically except that a single knot (Ph. Eur.) was thrown before the test.

Melt flow properties were assayed in an apparatus as described in DIN 53735 at 230.degree. C. with a load of 21.6N (this corresponds to ASTM 1238, Cond. L). Flexibilities were determined with an Instron tester which was equipped with a special adapter. A piece of suture 10 was mounted between two pins (12 and 14) (FIG. 1).

The suture 10 was then bent, using a hook, to the position shown in dotted lines as 16. This hook was driven by the crosshead of the Instron. The bending force F, as measured by the Instron, was recorded as a function of the distance f. The flexural modulus E can be calculated by using the following equation:

Claims

1. A drawn and oriented, strong and compliant, surgical filament comprising a physical blend of polypropylene and linear low density polyethylene, wherein the filament contains from about 0.1 to 25 weight percent linear low density polyethylene, based on weight of polyethylene plus polypropylene.

2. The surgical filament of claim 1 attached to a needle.

3. The surgical filament of claim 1 having the following properties:

______________________________________tensile strength 350 to 900 N/mm.sup.2intrinsic knot strength 300 to 800 N/mm.sup.2break elongation 23 to 53 percentflexural modulus 1200 to 5000 N/mm.sup.2______________________________________

4. The surgical filament of claim 1, 2, or 3, wherein the filament contains from about 1 to 16 weight percent linear low density polyethylene, based on weight of polyethylene plus polypropylene.

5. The surgical filament of claim 1, 2, or 3 in sterile condition.