20170166755
Embodiments generally relate a chemical composition and a method using that composition to form a self decontaminating surface. In certain embodiments, the chemical composition comprises a photocatalyst. In certain embodiments, the photocatalyst comprises a titanium oxide moiety. In certain embodiments, the chemical composition comprises an organosilane.
In a publication entitled “Evaluation of Two Organosilane Products for Sustained 25764721 Antimicrobial Activity on High-Touch Surfaces in Patient Rooms, American Journal of Infection Control 42 (2014) 326-8, reports, inter alia, “[t]o the best of our knowledge, ours is the first published controlled trial of applying organosilane compounds to high-touch surfaces in patient rooms as a strategy for reducing the level of microbial contamination of environmental surfaces between daily cleanings.” Id. at 327.
The authors found the two organosilanes ineffective for any sort of sustained antimicrobial efficacy. “In conclusion, our study was not able to demonstrate sustained antimicrobial activity for either organosilane product tested when applied to high-touch surfaces.” Id. at 328.
The invention will be better understood from a reading of the following detailed description taken in conjunction with the drawings in which like reference designators are used to designate like elements, and in which:
The invention is described in preferred embodiments in the following description with reference to the Figures, in which like numbers represent the same or similar elements. Reference throughout this specification to “one embodiment,” “an embodiment,” or similar language means that a particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment of the present invention. Thus, appearances of the phrases “in one embodiment,” “in an embodiment,” and similar language throughout this specification may, but do not necessarily, all refer to the same embodiment.
The described features, structures, or characteristics of the invention may be combined in any suitable manner in one or more embodiments. In the following description, numerous specific details are recited to provide a thorough understanding of embodiments of the invention. One skilled in the relevant art will recognize, however, that the invention may be practiced without one or more of the specific details, or with other methods, components, materials, and so forth. In other instances, well-known structures, materials, or operations are not shown or described in detail to avoid obscuring aspects of the invention.
In certain embodiments of Applicants' composition and method, a coating is formed on a surface of an object, where that coating comprises a plurality of titanium-oxygen bonds, where that coating is formed by disposing on the surface a mixture of Peroxotitanium acid solution and Peroxo-modified anatase sol (collectively “Titanium-Oxygen Moieties”).
In certain embodiments, Applicants' Titanium-Oxygen Moieties comprises up to about a total of one weight percent loading of the mixture of Peroxotitanium acid solution and Peroxo-modified anatase sol. In certain embodiments, Applicants' Titanium-Oxygen Moieties comprises about 0.5 weight percent Peroxotitanium acid solution in combination with about 0.5 weight percent Peroxo-modified anatase sol.
A method to prepare both Peroxotitanium acid solution and Peroxo-modified anatase sol is disclosed in Journal of Sol-Gel Science and Technology, September 2001, Volume 22, Issue 1-2, pp 33-40. This publication discloses, inter alia, Reaction Scheme 1, shown in
In one embodiment of Applicants' composition and method, Applicants' coating formulation comprises a mixture of Peroxotitanium acid solution and Peroxo-modified anatase sol. In another embodiment of Applicants' composition and method, a coating is formed on a surface of an object, where that coating comprises a plurality of titanium-oxygen bonds in combination with a plurality of silicon-oxygen bonds, and where that coating is formed by disposing a mixture of Peroxotitanium acid solution and Peroxo-modified anatase sol, in combination with an organosilane onto the surface.
In certain embodiments, a coating comprising a plurality of titanium-oxygen bonds in combination with a plurality of silicon-oxygen bonds is formed by first disposing on the surface an organosilane followed by disposing a mixture of Peroxotitanium acid solution and Peroxo-modified anatase sol onto the organosilane.
In certain embodiments, a coating comprising a plurality of titanium-oxygen bonds in combination with a plurality of silicon-oxygen bonds is formed by first disposing a mixture of Peroxotitanium acid solution and Peroxo-modified anatase sol on the surface followed by disposing an organosilane onto the mixture of Peroxotitanium acid solution and Peroxo-modified anatase sol. In certain embodiments, a coating comprising a plurality of titanium-oxygen bonds in combination with a plurality of silicon-oxygen bonds is formed by simultaneously disposing a mixture of Peroxotitanium acid solution and Peroxo-modified anatase sol and an organosilane onto the surface.
In certain embodiments, Applicants' organosilane comprises organosilane 1.
In certain embodiments, both R1 and R2 are alkyl. In other embodiments R1 is alkyl and R2 is alkyl with an amino moiety. In still other embodiments, R1 is alkyl and R2 comprises a quarternary ammonium group. In still other embodiments, R1 is alkyl and R2 comprises a chlorine moiety. In still other embodiments, R1 is alkyl and R2 is selected from the group consisting of —O—CH3 and —O—CH2—CH3.
In certain embodiments, Applicants' organosilane comprises a trihydroxy silane 2. In certain embodiments, R2 is alkyl. In other embodiments R2 is alkyl with an amino moiety. In still other embodiments, R2 comprises a quarternary ammonium group. In still other embodiments, comprises a chlorine moiety. In still other embodiments, R2 is —OH.
In certain embodiments, Applicants' organosilane comprises a silanetriol 2, wherein R2 is alkyl. In other embodiments, Applicants' organosilane comprises a silanetriol 2, wherein R2 is alkyl with an amino moiety. In still other embodiments, Applicants' organosilane comprises a silanetriol 2, wherein R2 is alkyl with a quarternary ammonium group.
As those skilled in the art will appreciate and as shown in Equation (1), silyl esters, such as silyl ester 1, are readily hydrolysable into a corresponding silanetriol, such as silanetriol 2. Even exposure to atmospheric moisture is sufficient to hydrolyze silyl ester 1 into silanetriol 2.
A silsesquioxane is an organosilicon compound 3. In certain embodiments, R2 is alkyl. In other embodiments, R2 is alkyl with an amino moiety. In yet other embodiments, R2 is alkyl with an chlorine moiety. In still other embodiments, R2 is alkyl with a quarternary ammonium group.
In certain embodiments, after application of Applicants' silanetriol 2 to either a hard surface, i.e. wall, door, table, and the like, or a soft surface, i.e. bedding, draperies, furniture cushions, and the like, a resulting coating disposed on the hard surface/soft surface comprises a plurality of silsesquioxane 3 structures. In certain embodiments, after application of Applicants' silanetriol 2 in combination with titanium dioxide to either a hard surface, i.e. wall, door, table, and the like, or a soft surface, i.e. bedding, draperies, furniture cushions, and the like, a resulting coating disposed on the hard surface/soft surface comprises a plurality of silsesquioxane structures 3 in combination with Applicants' Titanium-Oxygen Moieties.
The following Examples are presented to further illustrate to persons skilled in the art how to make and use the invention. These Examples are not intended as limitations, however, upon the scope of the invention.
A study was conducted at the Glendale Memorial Hospital and Health Center in Glendale, Calif. (the “Glendale Memorial Hospital Study”). The Center has a 24 bed intensive care (ICU). The study was performed between May 10 and Sep. 30, 2013.
The Glendale Memorial Hospital Study was designed to assess the anti-microbial properties of Applicants' coating composition and method, wherein the method employed utilized an initial coating of Applicants' organosilane followed by an overspray of titanium dioxide. The entire ICU was subjected to the two step spray regime to treat all objects in each room including hard surfaces (beds, tray tables, bed rail, walls, etc.) and soft surfaces (drapes, cloth and vinyl covered chairs, woven fabrics, non-woven fabrics, leather goods, and the like). The goal of the Glendale Memorial Hospital Study was to assess the anti-microbial efficacy of Applicants' coating composition in a practical application in a health care environment.
Each surface was first electrostatically spray coated at room temperature using an aqueous composition formed by mixing Octadecylaminodimethyltrihydrox-ysilylpropyl Ammonium Chloride 6 at 3.6 weight percent in water.
About fifteen (15) minutes after the electrostatic spray coating using the aqueous mixture of Octadecylaminodimethyltrihydroxysilylpropyl Ammonium Chloride 6, most of the water had evaporated leaving a coating comprising at least ninety weight percent (90 wt %) Octadecylaminodimethyltrihydroxysilylpropyl Ammonium Chloride 6, Thereafter, each surface was then electrostatically spray coated at room temperature using Applicants' Titanium-Oxide Moieties. After about 15 minutes, most of the water in the second spray deposition had evaporated leaving a coating comprising at least ninety weight percent (90 wt %) Applicants' Titanium-Oxide Moieties.
The treated surfaces were maintained at room temperature during the spray deposition of the aqueous Octadecylaminodimethyltrihydroxysilylpropyl Ammonium Chloride 6, and during the spray deposition of Applicants' Titanium-Oxide Moieties. None of the treated objects were subjected to any elevated heat treatment wherein the treated surface was heated to a temperature greater than about room temperature during or after completion of Applicants' spray coating regime.
Applicants have found that using their two step, spray coating protocol described hereinabove, after evaporation of the water from the spray deposited Titanium-Oxide Moieties and evaporation of the water portion from the spray deposited aqueous Octadecylaminodimethyltrihydroxysilylpropyl Ammonium Chloride, the combined weight of Applicants' Titanium-Oxide Moieties and Octadecylaminodimethyltrihydroxysilylpropyl Ammonium Chloride disposed on a treated surface was measured as 0.76 mg/in2.
Initial microbial sampling of various fomites was conducted to assess the levels of bacteria on various hospital surfaces before selecting study sites. After review, 95 sites were selected for the study in the ICU. Each of the ninety-five (95) specific sites in the ICU were selected for recurring sampling at weeks 1, 2, 4, 8, and 15, after application of Applicants' composition. Those selected sites included bed rails, bed controls, tray tables, and walls above sinks. Samples were also collected from the two ICU nursing stations and waiting lobby including countertops, phones, computer keyboards, chair armrests and end tables. All movable items were inconspicuously tagged and coded over the course of the study so that the same objects could be sampled.
Each of the sites was cultured prior to application of Applicants' method and at 1 week (6-8 days), 2 weeks (13-17 days), 4 weeks (29-32 days), 8 weeks (59-62 days), 15 weeks (104-107 days) after application. Some objects were removed and were not available for culture at some of the subsequent time points.
Areas of 100 cm2 were sampled using a sponge stick containing Letheen broth (3M, St. Paul, Minn.) to neutralize any residual disinfectant. After collection the samples were immediately placed on ice packs and sent overnight to the University of Arizona. Upon receipt the broth was extracted from the sponge stick by manual agitation, and then 4 mL of extracted broth was assayed using selective media for isolation of the various bacteria. Samples were cultured for total bacteria, Clostridium difficile, methicillin-resistant Staphylococcus aureus (MRSA), vancomycin resistant enterococcus (VRE), and carbapenemase resistant Enterobacteriaceae (CRE). Test methods for each organism are presented in Table 5.
C. difficile
The average number of total bacteria detected per 100 cm2 at all locations and percent reductions in total bacterial numbers after treatment are shown in Table 6.
on 100 cm2 from
indicates data missing or illegible when filed
As can be seen bacterial numbers were always 99.9% less after the treatment for four weeks, 99% after eight weeks and still almost 99% after 15 weeks.
Also, significantly the number of sites containing more than 10,000 CFU/100 cm2 was reduced from 71.5% of the sites before treatment to zero for the next eight weeks and after even 15 weeks only 11.1% of the sites exceeded this number as shown in Table 7.
Bootstrapping Analysis of Variance (ANOVA) was conducted for each stage between the baseline concentrations for the sampled fomites and the intervention concentrations for the same fomites to determine statistical significant differences based on a rejection region of 5%. Based on the p-values (<0.0005) there was a statistical significance difference between the baseline concentrations and the fomite concentrations during the entire 15 weeks of the study.
The percent of samples in which antibiotic resistant bacteria were isolated at the different sites sampled is shown in Table 8.
C. difficile
Antibiotic resistant bacteria were isolated from all study areas during the baseline sampling, except C. difficile. VRE was the most commonly isolated organism.
Prior to treatment antibiotic resistant bacteria were isolated from 25% of the sites sampled. After treatment, no antibiotic bacteria were isolated until week 8, when VRE in 1 sample (from a chair armrest) of 64 samples (1.5%) was found.
The present study demonstrates that the use of Applicants' method reduced the numbers of bacteria on fomites by greater than 99% for 8 weeks after a single treatment (Table 6).
Levels of bacteria were reduced by 99.9% at 4 weeks post-treatment. Overall average levels of bacteria never returned to those observed before treatment. Bacterial numbers increased between 8 and 15 weeks post-treatment but the average bacterial count on all treated surfaces was still less than 90% after 15 weeks. No values above 10,000 CFU/100 cm2 were seen for 4 weeks after treatment vs. 25.2% pre-treatment and even after 15 weeks only 11.1% of the values exceeded this amount.
No antibiotic resistant bacteria were isolated until 8 weeks after the treatment, and then at levels below that seen before the treatment (Table 8). No MRSA or CRE were isolated even after 15 weeks post-treatment and VRE only after 8 weeks. No C. difficile were isolated during the baseline or after the treatment. However, C. difficile was isolated in the initial screening used to select the sampling sites.
In conclusion, the anti-microbial effects resulting from use of Applicants' composition and method was found to have persisted over 15 weeks in reducing the total number of bacteria and antibiotic resistant bacteria on both hard surfaces and soft surfaces within an ICU. The hard surfaces included bare metal surfaces, painted metal surfaces, epoxy-coated surfaces, unpainted wood surfaces, painted wood surfaces, and glass.
The fifteen weeks antimicrobial efficacy demonstrates that Applicants' composition forms a coating on a treated surface, where that coating is both antifouling and antimicrobial. Applicants' composition and the resulting coating formed therefrom can generate self-decontaminating surfaces that comprise both antifouling and antimicrobial properties, thereby, providing a cost-effective route to minimize transmission of disease via high touch surfaces in healthcare and industrial applications.
Applicants have found that they can dispose Octadecylaminodimethyltrihydrox-ysilylpropyl Ammonium Chloride and. Applicants Titanium-Oxide Moieties, by spray deposition or by dip coating, onto a dressing prior to use of that dressing to cover a wound. As those skilled in the art will appreciate, a dressing is a sterile pad or compress applied to a wound to promote healing and/or prevent further harm. A dressing is designed to be in direct contact with the wound, as distinguished from a bandage, which is most often used to hold a dressing in place. In certain embodiments, Applicants' wound dressings including the following: alginates and other fiber gelling dressings including ropes and sheets, composite dressings, foam dressings with and without adhesive border, gauze with and without adhesive border, hydrocolloids, specialty absorptive dressings with and without adhesive borders, transparent films, collagen dressings sheets and ropes, hydrogel sheets with and without adhesive border, cotton packing strips, roll gauze, paper tape, silk tape, compression bandages (elastic, knitted/woven), self-adherent bandage (elastic, non-knitted/non-woven).
This Example II disposes the components of Applicants' composition onto a target surface in a reverse order. More specifically in this Example II, Applicants' first dispose Applicants' Titanium-Oxide Moieties onto the target surface, the aqueous portion of the first spray deposition is evaporated, and then dispose Octadecylatninodimethyltrihydroxysilylpropyl Ammonium Chloride 6 over the earlier-disposed Titanium-Oxide Moieties.
The test coupons of this Example II were prepared and using the Procedure recited immediately hereinbelow. In certain embodiments, the treated coupons were stored for at least four (4) weeks prior to inoculation with various organisms.
TABLE 9 recites efficacy data for the treated coupons after inoculation with E. coli. TABLE 10 recites efficacy data for the treated coupons after inoculation with MS-2. TABLE 11 recites efficacy data for the treated coupons after inoculation with MRSA.
In summary, TABLEs 9, 10, and 11, demonstrates that first disposing Applicants' Titanium-Oxide Moieties onto a target surface followed by disposing Octadecylaminodimethyltrihydroxysilylpropyl Ammonium Chloride 6 over the earlier-formed Titanium-Oxide Moieties coating, generates a self-decontaminating surface.
Put on sterile gloves.
Prepare the test coupons by wiping them first with ISP Alcohol and allowing to dry.
Clean the test coupons with surface cleaner using a microfiber cloth.
Hold sprayer about eight (8) inches from surface to be cleaned.
Spray on let stand for 1-3 minutes and wipe it off, if the area is extremely dirty allow cleaner to stand longer, or apply a second spray and wipe.
Wipe surface with a clean, damp sponge or cloth.
Allow surface to completely dry.
With gloved hands examine coupons for consistency.
Add Applicants' Titanium-Oxide Moieties to the applicator container.
Fasten the Liquid Hose/Bottle cap assembly tightly on the container.
Connect the air hose from compressor to air fitting on the spray applicator.
Connect the liquid hose to the liquid fitting on the spray applicator.
Plug the power cord into an appropriate receptacle. Turn on the air compressor.
Optimal spraying distance is at least 36 to 48 inches away from the target surface.
Hold the spray gun at right angles to the target surface and spray.
Target surface should just barely glisten with the spray. Do not over-saturate the surface.
Rinse spray gun with distilled water prior to applying Applicants' Titanium-Oxide Moieties (unless using 2 sprayers, one for each product).
Add the Octadecylaminodimethyltrihydroxysilylpropyl Ammonium Chloride 6 to applicator container.
Fasten the Liquid Hose/Bottle cap assembly tightly on the container.
Connect the air hose from compressor to air fitting on the spray applicator.
Connect the liquid hose to the liquid fitting on the spray applicator.
Plug the power cord into an appropriate receptacle. Turn on the air compressor.
Optimal spraying distance is at least 36 to 48 inches away from the target surface.
Hold the spray gun at right angles to the target surface and spray.
Target surface should just barely glisten with the spray. Do not over-saturate the surface.
Allow surface to completely dry.
Clean the spray gun with distilled water per manufactures' specifications after each day of use.
E. coli testing on Formica chips
This Example III simultaneously disposes a mixture of Applicants' organosilane and Applicants' Titanium-Oxide Moieties onto the surface of a plurality of test coupons. More specifically in this Example III, Applicants' simultaneously dispose Applicants' Titanium-Oxide Moieties and Octadecylaminodimethyltrihydroxysilylpropyl Ammonium Chloride 6 onto a surface of each test coupon.
The test coupons of this Example III were prepared and using the Procedure recited immediately hereinbelow. In certain embodiments, the treated coupons were stored for at least four (4) weeks prior to inoculation with various organisms.
TABLE 12 recites efficacy data for the treated coupons after inoculation with E. coli. TABLE 13 recites efficacy data for the treated coupons after inoculation with MS-2. TABLE 14 recites efficacy data for the treated coupons after inoculation with MRSA.
In summary, TABLES 12, 13, and 14, demonstrates that simultaneously disposing Applicants' Titanium-Oxygen Moieties and Applicants' organosilane onto a target surface generates a self-decontaminating surface.
Put on sterile gloves.
Prepare the test coupons by wiping them first with ISP Alcohol and allowing to dry.
Clean the test coupons with surface cleaner using a microfiber cloth.
Hold sprayer about eight (8) inches from surface to be cleaned.
Spray on let stand for 1-3 minutes and wipe it off, if the area is extremely dirty allow cleaner to stand longer, or apply a second spray and wipe.
Wipe surface with a clean, damp sponge or cloth.
Allow surface to completely dry.
With gloved hands examine coupons for consistency.
In a measured container combine 50% Octadecylaminodimethyltrihydroxysilylpropyl Ammonium Chloride aqueous mixture and 50% Applicants' Titanium-Oxide Moieties aqueous mixture.
Mix thoroughly.
Add the mixture from [00092] to applicator container.
Fasten the Liquid Hose/Bottle cap assembly tightly on the container.
Connect the air hose from compressor to air fitting on the spray applicator.
Connect the liquid hose to the liquid fitting on the spray applicator.
Plug the power cord into an appropriate receptacle. Turn on the air compressor.
Optimal spraying distance is at least 36 to 48 inches away from the target surface.
Hold the spray gun at right angles to the target surface and spray.
Target surface should just barely glisten with the spray. Do not over-saturate the surface.
Allow surface to completely dry.
Clean the spray gun with distilled water per manufactures' specifications after each day of use.
E. coli testing on Formica chips
This Example IV utilizes (3-Aminopropyl)trimethoxysilane in water as the only organosilane. This being the case, this Example VI utilizes NO organosilane(s) comprising a quaternary ammonium moiety. (3-Aminopropyl)trimethoxysilane is rapidly hydrolyzed to (3-Aminopropyl)trihydroxysilane) 7 when mixed with water.
The test coupons of this Example IV were prepared and using the Procedure recited immediately hereinbelow. In certain embodiments, the treated coupons were stored for at least four (4) weeks prior to inoculation with various organisms.
Applicants have found that using their two step, spray coating protocol described hereinbelow, after evaporation of the water from the spray deposited Titanium-Oxide Moieties and evaporation of the water portion from the spray deposited aqueous (3-Aminopropyl)trihydroxysilane), the combined weight of Applicants' Titanium-Oxide Moieties and (3-Aminopropyl)trihydroxysilane) disposed on a treated surface was measured as 1.22 mg/in2.
Applicants have found that they can dispose (3-Aminopropyl)trihydroxysilane and Applicants Titanium-Oxide Moieties, by spray deposition or by dip coating, onto a dressing prior to use of that dressing to cover a wound. As those skilled in the art will appreciate, a dressing is a sterile pad or compress applied to a wound to promote healing and/or prevent further harm. A dressing is designed to be in direct contact with the wound, as distinguished from a bandage, which is most often used to hold a dressing in place. In certain embodiments, Applicants' wound dressings including the following: alginates and other fiber gelling dressings including ropes and sheets, composite dressings, foam dressings with and without adhesive border, gauze with and without adhesive border, hydrocolloids, specialty absorptive dressings with and without adhesive borders, transparent films, collagen dressings sheets and ropes, hydrogel sheets with and without adhesive border, cotton packing strips, roll gauze, paper tape, silk tape, compression bandages (elastic, knitted/woven), self-adherent bandage (elastic, non-knitted/non-woven).
TABLES 15, 16, and 17, recite efficacy data for the treated coupons after inoculation with E. coli. In summary, TABLES 15, 16, and 17, demonstrate that disposing a 3-Aminopropyl)trihydroxysilane coating onto a target surface, and then disposing TiO2 over that 3-Aminopropyl)trihydroxysilane coating generates a self-decontaminating surface.
Put on sterile gloves.
Prepare the test coupons by wiping them first with ISP Alcohol and allowing to dry.
Clean the test coupons with surface cleaner using a microfiber cloth.
Hold sprayer about eight (8) inches from surface to be cleaned.
Spray on let stand for 1-3 minutes and wipe it off, if the area is extremely dirty allow cleaner to stand longer, or apply a second spray and wipe.
Wipe surface with a clean, damp sponge or cloth.
Allow surface to completely dry.
With gloved hands examine coupons for consistency.
Prepare a 10% solution of 3-Aminopropyl)triethoxysilane in Methanol (MeOH) (10 ml silane in 100 ml MeOH).
Prepare Triethanolamine as a 10% solution in MeOH.
Combine the triethanolamine solution and 3-Aminopropyl)triethoxysilane solution in a 1:1 ratio on a stir plate at room temperature (ie-100 ml triethanolamine solution added to 100 ml 3-Aminopropyl)triethoxysilane solution.
Add the mixture from [000116] to the applicator container.
Fasten the Liquid Hose/Bottle cap assembly tightly on the container.
Connect the air hose from compressor to air fitting on the spray applicator.
Connect the liquid hose to the liquid fitting on the spray applicator.
Plug the power cord into an appropriate receptacle. Turn on the air compressor.
Optimal spraying distance is at least 36 to 48 inches away from the target surface.
Hold the spray gun at right angles to the target surface and spray.
Target surface should just barely glisten with the spray. Do not over-saturate the surface.
Rinse spray gun with distilled water prior to applying Applicants' Titanium Oxide Moieties (unless using 2 sprayers, one for each product).
Add Applicants' Titanium Oxide Moieties to the applicator container.
Fasten the Liquid Hose/Bottle cap assembly tightly on the container.
Connect the air hose from compressor to air fitting on the spray applicator.
Connect the liquid hose to the liquid fitting on the spray applicator.
Plug the power cord into an appropriate receptacle. Turn on the air compressor.
Optimal spraying distance is at least 36 to 48 inches away from the target surface.
Hold the spray gun at right angles to the target surface and spray.
Target surface should just barely glisten with the spray. Do not over-saturate the surface.
Allow surface to completely dry.
Clean the spray gun with distilled water per manufactures' specifications after each day of use.
E. coli
E. coli
3.35E+06
3.61E+06
3.90E+06
a“≦”: no bacterial colonies observed, therefore counts at or below limit of detection (based on 0.1 ml plating volume)
E. coli
2.80E+05
3.91E+05
5.45E+05
a“≦”: no bacterial colonies observed, therefore counts at or below limit of detection (based on 0.1 ml plating volume)
This Example V mixes (3-Chloropropyl)trimethoxysilane in water. (3-Chloropropyl)trimethoxysilane is immediately hydrolyzed to (3-Chloropropyl)trihydroxysilane 8 when mixed with water.
This being the case, this Example V utilizes NO organosilane(s) comprising a quaternary ammonium moiety. Furthermore, this Example VII utilizes NO organosilane(s) comprising an amino moiety.
The test coupons of this Example V were prepared using the Procedure recited immediately hereinbelow. In certain embodiments, the treated coupons were stored for at least four (4) weeks prior to inoculation with various organisms.
Applicants have found that they can dispose (3-Chloropropyl)trihydroxysilane and Applicants Titanium-Oxide Moieties, by spray deposition or by dip coating, onto a dressing prior to use of that dressing to cover a wound. As those skilled in the art will appreciate, a dressing is a sterile pad or compress applied to a wound to promote healing and/or prevent further harm. A dressing is designed to be in direct contact with the wound, as distinguished from a bandage, which is most often used to hold a dressing in place. In certain embodiments, Applicants' wound dressings including the following: alginates and other fiber gelling dressings including ropes and sheets, composite dressings, foam dressings with and without adhesive border, gauze with and without adhesive border, hydrocolloids, specialty absorptive dressings with and without adhesive borders, transparent films, collagen dressings sheets and ropes, hydrogel sheets with and without adhesive border, cotton packing strips, roll gauze, paper tape, silk tape, compression bandages (elastic, knitted/woven), self-adherent bandage (elastic, non-knitted/non-woven).
TABLES 18, 19, and 20, recite efficacy data for the treated coupons after inoculation with E. coli. In summary, TABLES 18, 19, and 20, demonstrates that disposing a (3-Chloropropyl)trihydroxysilane coating on a target surface followed by disposing Applicants' Titanium Oxide Moieties onto the (3-Chloropropyl)trihydroxysilane coating generates a self-decontaminating surface.
Put on sterile gloves.
Prepare the test coupons by wiping them first with ISP Alcohol and allowing to dry.
Clean the test coupons with surface cleaner using a microfiber cloth.
Hold sprayer about eight (8) inches from surface to be cleaned.
Spray on let stand for 1-3 minutes and wipe it off, if the area is extremely dirty allow cleaner to stand longer, or apply a second spray and wipe.
Wipe surface with a clean, damp sponge or cloth.
Allow surface to completely dry.
With gloved hands examine coupons for consistency.
Prepare Organosilane Dilution for (3-Chloropropyl)trimethoxy silane
Prepare a 10% solution of (3-Chloropropyl)trimethoxy silane in Methanol (MeOH) (10 ml. silane in 100 ml. MeOH).
Prepare Triethanolamine solution as a 10% solution in MeOH.
Combine the triethanolamine solution and (3-Chloropropyl)trimethoxy silane solution in a 1:1 ratio on a stir plate at room temperature (ie-100 ml. trethanolamine added to 100 ml. (3-Chloropropyl)trimethoxy silane).
Add the mixture of [000149] to the applicator container.
Fasten the Liquid Hose/Bottle cap assembly tightly on the container.
Connect the air hose from compressor to air fitting on the spray applicator.
Connect the liquid hose to the liquid fitting on the spray applicator.
Plug the power cord into an appropriate receptacle. Turn on the air compressor.
Optimal spraying distance is at least 36 to 48 inches away from the target surface.
Hold the spray gun at right angles to the target surface and spray.
Target surface should just barely glisten with the spray. Do not over-saturate the surface.
Rinse spray gun with distilled water prior to applying Applicants' Titanium Oxide Moieties (unless using 2 sprayers, one for each product).
Add Applicants' Titanium Oxide Moieties to the applicator container.
Fasten the Liquid. Hose/Bottle cap assembly tightly on the container.
Connect the air hose from compressor to air fitting on the spray applicator.
Connect the liquid hose to the liquid fitting on the spray applicator.
Plug the power cord into an appropriate receptacle. Turn on the air compressor.
Optimal spraying distance is at least 36 to 48 inches away from the target surface.
Hold the spray gun at right angles to the target surface and spray.
Target surface should just barely glisten with the spray, Do not over-saturate the surface.
Allow surface to completely dry.
Clean the spray gun with distilled water per manufactures' specifications after each day of use.
E. coli
E. coli
a“≦”: No bacterial colonies observed, therefore counts at or below limit of detection (based on 0.1 ml plating volume)
E. coli
2.80E+05
3.91E+05
5.45E+05
a“≦”: No bacterial colonies observed, therefore counts at or below limit of detection (based on 0.1 ml plating volume)
This Example VI utilizes three (3) coating formulations without any Titanium-Oxide containing compounds. A first of the three coating formulations identified in this Example VI as ABS 2015E utilizes Octadecylaminodimethyltrihydrox-ysilylpropyl Ammonium Chloride 6 as the organosilane. A second of the three coating formulations identified in this Example VI as ABS 2020E utilizes (3-Aminopropyl)trihydroxysilane) 7 as the organosilane. A third of the three coating formulations identified in this Example VI as ABS 2030E utilizes (3-Chloropropyl)trihydroxysilane) 8 as the organosilane.
The method of Example IV from Paragraph [000105] through Paragraph [000124] relating to spray deposition of a silane onto test coupons was utilized in this Example VI. The method of Paragraph [000125] through and including Paragraph [000134] relating to spray deposition of the Titanium-Oxygen Moieties was not utilized in this Example VI.
TABLE 21 recites CFU/mL data for each of the three coating formulations, wherein each formulation did not include one or more titanium-oxide moieties. TABLE 22 recites Log Reduction data for the three formulations evaluated, wherein each formulation did not include one or more titanium-oxide moieties. TABLE 23 recites Percent Reduction data for the three formulations utilized, wherein each formulation did not include one or more titanium-oxide moieties.
In coating formulations ABS 2015E, 2020E, and 2030E, depending on the stoichiometry of the mixture of triethanolamine and the organosilane, one or polymeric species are formed on a treated surface. In certain embodiments, and as shown in Reaction Scheme 2, triethanolamine 9 and organosilane 1 react to form a linear polymer 10.
In other embodiments, and as shown in Reaction Scheme 3, triethanolamine 9 and organosilane 1 react to form a branched polymer 11.
In other embodiments, and as shown in Reaction Scheme 4, triethanolamine 9 and organosilane 1 react to form a cross-linked polymer 12.
In certain embodiments, Applicants' organosilane comprises tetraethylorthosilicate 13. In certain embodiments and as shown in Reaction Scheme 5 and depending on the stoichiometry of the starting materials 9 and 13, Applicants cross-linked polymeric material 14 is formed by reaction of tetraethylorthosilicate 13 and triethanolamine 9. Reaction Scheme 5 illustrates a single Si atom having four (4) different polymer chains originating therefrom. Those skilled in the art will appreciate that Applicants' cross-linked polymer material 14 comprises a very high cross-link density.
In certain embodiments and as shown in Reaction Scheme 6 and depending on the stoichiometry of the starting materials 15 and 13, Applicants cross-linked polymeric material 16 is formed by reaction of tetraethylorthosilicate 13 and diethanolamine 13. Reaction Scheme 6 illustrates a single Si atom having four (4) different polymer chains originating therefrom. Those skilled in the art will appreciate that Applicants' cross-linked polymer material 16 comprises a very high cross-link density.
Stainless steel carriers were coated with the solutions containing 7.5% of one of three different choline 16 compounds in H2O, wherein R3 is selected from the group consisting of —H and —CO—CH3. Cholines used included Choline Chloride, Choline Bitartrate, and Acetylcholine Chloride. Carriers were coated by dipping into solution using forceps and allowing to drip-dry overnight. Carriers were still not completely dry even after 24 hours drying time. Twenty (20) microliters of 0/N cultures of E. coli 25592 (grown at 37 C for 18 hours) were added to each carrier. Following inoculation of the carriers, the carriers were swabbed with D/E neutralizing broth and processed for the zero hour time point. This was repeated for the 1 and 4 hour time points.
The collected samples were then diluted in PBS and 100 microliters were plated on to TSA plates and left overnight at 37° C. before counting and calculating cfu/ml. All carriers were tested in duplicate and two experiments were performed (A and B in data tables) in tandem. All data is represented as the mean+/−the SEM (standard error) when applicable.
When calculated relative to the timed control, choline bitartrate showed the greatest surface-kill, with a 2.39 log reduction in bacteria. Acetylcholine chloride and choline chloride showed a 1.85 and 1.40 log reduction, respectively. When compared with the results of aqueous solutions of Aminopropyl triethoxysilane (APTES) and the cholines at the same concentration, it is clear that these solutions are much more antimicrobial than the cholines on their own. APTES+Choline Chloride and APTES+Choline Bitartrate showed a 3.36 and 3.38 log reduction, respectively, at the 1 hour time point.
TABLE 24 recites antimicrobial efficacy data for the above-described choline formulations at time T0, i.e. immediately after inoculation. TABLE 25 recites antimicrobial data at one (1) hour after inoculation.
E. coli
E. coli
Stainless steel carriers were coated with solutions containing 7.5% of each choline compound and 5% Aminopropyltriethoxysilane in H2O (ABS-2040 contains choline chloride, while ABS-2041 contains choline bitartrate). Carriers were coated using an electrostatic sprayer and then allowed to dry. Carriers were still not completely dry even after 2 days of drying time. Twenty (20) microliters cultures of E. coli grown at 37° C. for 18 hours) were added to each carrier. Following inoculation of the carriers, the carriers were swabbed with neutralizing broth and processed for the zero hour time point. This was repeated for the 1 hour time point.
The collected samples were then diluted in PBS and 100 microliters were plated on to TSA plates and left 0/N at 37° C. before counting and calculating cfu/ml. All carriers were tested in duplicate and two experiments were performed (A and B in data table) in tandem. All data is represented as the mean+/−the SEM (standard error) when applicable. It is worth noting that colonies on the Choline Bitartrate plates were significantly smaller than the others.
Table 26 recites antimicrobial efficacy data at time T0, i.e. immediately after inoculation. TABLE 27 recites antimicrobial data at one (1) hour after inoculation. TABLE 28 recites antimicrobial data at four (4) hours after inoculation.
E. coli
E. coli
E. coli
Stainless steel carriers were coated with solutions containing 15% of each choline compound and 5% Aminopropyltriethoxysilane in H2O (ABS-2040 contains choline chloride, while ABS-2041 contains choline bitartrate). Carriers were coated using an electrostatic sprayer and then allowed to dry. Carriers were still not completely dry even after 2 days of drying time. 20 microliters of cultures of E. coli 25592 grown at 37° C. for 18 hours were added to each carrier. Following inoculation of the carriers, the carriers were swabbed with D/E neutralizing broth and processed for the zero hour time point. This was repeated for the 1 and 4 hour time points.
The collected samples were then diluted in PBS and 100 microliters were plated on to TSA plates and left 0/N at 37° C. before counting and calculating cfu/ml. All carriers were tested in duplicate and two experiments were performed (A and B in data table) in tandem. All data is represented as the mean+/−the SEM (standard error) when applicable.
Table 29 recites antimicrobial efficacy data at time T0, i.e. immediately after inoculation. TABLE 30 recites antimicrobial data at one (1) hour after inoculation. TABLE 31 recites antimicrobial data at four (4) hours after inoculation.
E. coli
E. coli
E. coli
Referring now to
Side 320 is similarly formed to include a plurality of UV emitters, where each of those UV emitters face the interior, i.e. walking space portion, of sterilizing station 300. The plurality of UV emitters disposed on the interior portion of side 310 have a facing relationship with the plurality of UV emitters disposed on the interior portion of side 320.
Further in the illustrated embodiment of
The illustrated embodiment of
While the preferred embodiments of the present invention have been illustrated in detail, it should be apparent that modifications and adaptations to those embodiments may occur to one skilled in the art without departing from the scope of the present invention as set forth herein.
This application is a continuation of, claims priority to and the benefit of, U.S. Ser. No. 14/932,840, filed Nov. 4, 2015 and entitled COMPOSITION AND METHOD TO FORM A SELF-DECONTAMINATING SURFACE. The '840 application claims priority to, and the benefit of, U.S. Provisional Application No. 62/114,998 filed Feb. 11, 2015 and entitled ANTI-MICROBIAL COATING AND METHOD TO FORM SAME. The '840 application also claims priority to, and the benefit of, U.S. Provisional Application No. 62/075,020 filed Nov. 4, 2014 and entitled COMPOSITION AND METHOD TO FORM A SELF-DECONTAMINATING SURFACE. All of the aforementioned applications are incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62114998 | Feb 2015 | US | |
| 62075020 | Nov 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14932840 | Nov 2015 | US |
| Child | 15432567 | US |