Embodiments of the disclosure generally relate to asymmetrically functionalized nanoparticles. More specifically, embodiments of the disclosure relate to a method and composition for asymmetrical polyethylenimine-functionalized silica nanoparticles for use in tertiary oil recovery.
The conventional production of crude oil generally includes three stages. The primary stage utilizes the natural pressure differential between the well and the reservoir. The secondary stage typically uses water flooding to provide an artificial pressure differential between the well and the reservoir. The tertiary stage commonly involves chemical flooding to reduce the interfacial tension between the crude oil and the injected water by utilizing bulk chemicals such as polymers, surfactants, and alkali metals to obtain mobility control of the residual crude oil after primary and secondary oil recovery.
However, tertiary oil recovery is limited by certain factors such as the price of crude oil, the potential pollution of underground water, and harsh reservoir conditions. Nanofluid flooding has received a growing amount of attention, where nanofluids involve solutions including dispersed nanoparticles. The nanoparticle concentration of the nanofluids is typically less than 0.01 wt. %, which offers economic and environmental efficiency in comparison with chemical flooding. However, the nanoparticles used in such nanofluids typically have an isotropic surface morphology that limits the stability of the emulsion or foam created by such nanoparticles.
Embodiments of the disclosure generally relate to asymmetrically functionalized nanoparticles. More specifically, embodiments of the disclosure relate to a method and composition for asymmetrical polyethylenimine-functionalized silica nanoparticles for use in tertiary oil recovery.
Advantageously, the anisotropic nature of the asymmetrically functionalized nanoparticles allows two different chemistries to take place at the same time. The unique surface property allows the asymmetrically functionalized nanoparticles to selectively adsorb at an oil-water interface at least three times greater than isotropic nanoparticles, enhancing the stability of an emulsion. The enhanced emulsion stability leads to an increased degree of oil displacement in comparison with conventional oil recovery operations.
Embodiments of the disclosure provide a method for synthesizing an asymmetrically functionalized nanoparticle. The method includes the step of surface-treating a base nanoparticle with an alcohol such that the base nanoparticle has hydroxyl groups distributed throughout an exterior of the base nanoparticle. The method includes the step of dispersing the base nanoparticle in an aqueous solvent to form an aqueous dispersion. The method includes the step of introducing a waxy material to the aqueous dispersion to form an emulsion. The emulsion is maintained at a temperature greater than a melting point of the waxy material. The emulsion includes liquid colloidosomes including the waxy material as an interior component and the base nanoparticle as an exterior component. The method includes the step of cooling the emulsion to a temperature less than the melting point of the waxy material such that solidified colloidosomes are formed. The method includes the step of chemically modifying an exposed surface of the base nanoparticle using a functionalizing material. The method includes the step of removing the waxy material to release the asymmetrically functionalized nanoparticle.
In some embodiments, the asymmetrically functionalized nanoparticle is amphiphilic. In some embodiments, the base nanoparticle has a lipophilic surface. In some embodiments, the functionalizing material is hydrophilic.
In some embodiments, the base nanoparticle includes silicon dioxide. In some embodiments, the base nanoparticle has a size ranging between 80 nm and 200 nm.
In some embodiments, the functionalizing material includes polyethylenimine. In some embodiments, a fluorophore is labeled to the polyethylenimine. In some embodiments, the fluorophore is fluoresceinisothiocyanate (FITC).
In some embodiments, the alcohol includes methanol, ethanol, propanol, combinations of the same, and aqueous solutions of the same. In some embodiments, the waxy material includes paraffin wax.
In some embodiments, the surface-treating step is conducted at a temperature ranging between 60 deg. C and 70 deg. C for a duration ranging between one hour and two hours. In some embodiments, the introducing step is conducted at a temperature ranging between 60 deg. C and 100 deg. C.
In some embodiments, the removing step includes dissolving the waxy material with an organic solvent. In some embodiments, the organic solvent includes chloroform, toluene, diethyl ether, and combinations of the same.
Embodiments of the disclosure also provide an asymmetrically functionalized nanoparticle. The asymmetrically functionalized nanoparticle includes a base nanoparticle. The base nanoparticle includes silicon dioxide. The base nanoparticle has a lipophilic surface. A portion of the surface is functionalized with polyethylenimine forming a hydrophilic portion. A remaining portion of the surface is not functionalized forming a lipophilic portion. The asymmetrically functionalized nanoparticle is amphiphilic.
In some embodiments, the polyethylenimine is labeled with a fluorophore. In some embodiments, the fluorophore is FITC.
In some embodiments, the base nanoparticle has a size ranging between 80 nm and 200 nm. In some embodiments, the asymmetrically functionalized nanoparticle is configured to form a continuous phase in a Winsor III type system including an oil phase and a water phase.
Embodiments of the disclosure also provide a method for hydrocarbon recovery using an asymmetrically functionalized nanoparticle. The method includes the step of introducing the asymmetrically functionalized nanoparticle to a subterranean formation. The subterranean formation includes crude oil and water forming an interface. The asymmetrically functionalized nanoparticle reduces interfacial tension between the crude oil and the water at the interface.
In some embodiments, the asymmetrically functionalized nanoparticle is formed by the step of surface-treating a base nanoparticle with an alcohol such that the base nanoparticle has hydroxyl groups distributed throughout an exterior of the base nanoparticle. The asymmetrically functionalized nanoparticle is formed by the step of dispersing the base nanoparticle in an aqueous solvent to form an aqueous dispersion. The asymmetrically functionalized nanoparticle is formed by the step of introducing a waxy material to the aqueous dispersion to form an emulsion. The emulsion is maintained at a temperature greater than a melting point of the waxy material. The emulsion includes liquid colloidosomes including the waxy material as an interior component and the base nanoparticle as an exterior component. The asymmetrically functionalized nanoparticle is formed by the step of cooling the emulsion to a temperature less than the melting point of the waxy material such that solidified colloidosomes are formed. The asymmetrically functionalized nanoparticle is formed by the step of chemically modifying an exposed surface of the base nanoparticle using a functionalizing material. The asymmetrically functionalized nanoparticle is formed by the step of removing the waxy material to release the asymmetrically functionalized nanoparticle.
In some embodiments, the asymmetrically functionalized nanoparticle is amphiphilic. In some embodiments, the base nanoparticle has a lipophilic surface. In some embodiments, the functionalizing material is hydrophilic.
In some embodiments, the base nanoparticle includes silicon dioxide. In some embodiments, the base nanoparticle has a size ranging between 80 nm and 200 nm.
In some embodiments, the functionalizing material includes polyethylenimine. In some embodiments, a fluorophore is labeled to the polyethylenimine. In some embodiments, the fluorophore is FITC.
So that the manner in which the previously-recited features, aspects, and advantages of the embodiments of this disclosure as well as others that will become apparent are attained and can be understood in detail, a more particular description of the disclosure briefly summarized previously may be had by reference to the embodiments that are illustrated in the drawings that form a part of this specification. However, it is to be noted that the appended drawings illustrate only certain embodiments of the disclosure and are not to be considered limiting of the disclosure's scope as the disclosure may admit to other equally effective embodiments.
In the accompanying Figures, similar components or features, or both, may have a similar reference label.
The disclosure refers to particular features, including process or method steps and systems. Those of skill in the art understand that the disclosure is not limited to or by the description of embodiments given in the specification. The subject matter of this disclosure is not restricted except only in the spirit of the specification and appended claims.
Those of skill in the art also understand that the terminology used for describing particular embodiments does not limit the scope or breadth of the embodiments of the disclosure. In interpreting the specification and appended claims, all terms should be interpreted in the broadest possible manner consistent with the context of each term. All technical and scientific terms used in the specification and appended claims have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs unless defined otherwise.
Although the disclosure has been described with respect to certain features, it should be understood that the features and embodiments of the features can be combined with other features and embodiments of those features.
Although the disclosure has been described in detail, it should be understood that various changes, substitutions, and alternations can be made without departing from the principle and scope of the disclosure. Accordingly, the scope of the present disclosure should be determined by the following claims and their appropriate legal equivalents.
As used throughout the disclosure, the singular forms “a,” “an,” and “the” include plural references unless the context clearly indicates otherwise.
As used throughout the disclosure, the word “about” includes +/−5% of the cited magnitude. The word “substantially” includes +/−5% of the cited magnitude.
As used throughout the disclosure, the words “comprise,” “has,” “includes,” and all other grammatical variations are each intended to have an open, non-limiting meaning that does not exclude additional elements, components or steps. Embodiments of the present disclosure may suitably “comprise,” “consist,” or “consist essentially of” the limiting features disclosed, and may be practiced in the absence of a limiting feature not disclosed. For example, it can be recognized by those skilled in the art that certain steps can be combined into a single step.
As used throughout the disclosure, the words “optional” or “optionally” means that the subsequently described event or circumstances can or may not occur. The description includes instances where the event or circumstance occurs and instances where it does not occur.
Where a range of values is provided in the specification or in the appended claims, it is understood that the interval encompasses each intervening value between the upper limit and the lower limit as well as the upper limit and the lower limit. The disclosure encompasses and bounds smaller ranges of the interval subject to any specific exclusion provided.
Where reference is made in the specification and appended claims to a method comprising two or more defined steps, the defined steps can be carried out in any order or simultaneously except where the context excludes that possibility.
As used throughout the disclosure, terms such as “first” and “second” are arbitrarily assigned and are merely intended to differentiate between two or more components of an apparatus. It is to be understood that the words “first” and “second” serve no other purpose and are not part of the name or description of the component, nor do they necessarily define a relative location or position of the component. Furthermore, it is to be understood that that the mere use of the term “first” and “second” does not require that there be any “third” component, although that possibility is contemplated under the scope of the present disclosure.
As used throughout the disclosure, spatial terms described the relative position of an object or a group of objects relative to another object or group of objects. The spatial relationships apply along vertical and horizontal axes. Orientation and relational words such are for descriptive convenience and are not limiting unless otherwise indicated.
As used throughout the disclosure, the terms “Janus nanoparticle” and “asymmetrically functionalized nanoparticle” can be used interchangeably.
As used throughout the disclosure, the terms “hydrophobic” and “lipophilic” can be used interchangeably.
As used throughout the disclosure, the “amphiphile” refers to a chemical composition possessing both hydrophilic and lipophilic properties. Non-limiting examples of an amphiphile include surfactants and Janus nanoparticles.
As used throughout the disclosure, the term “microemulsion” refers to a system of oil, water, and an amphiphile which is a single, optically isotropic, and thermodynamically stable liquid solution.
As used throughout the disclosure, the term “Pickering emulsion” refers to an emulsion that is stabilized by solid particles (for example, colloidal silica) which adsorb onto the interface between two phases. For example, oil and water can be mixed to form microsized oil droplets dispersed throughout the water. Eventually, the droplets will coalesce in the absence of solid particles. However, the presence of solid particles prevents the droplets from coalescing where the solid particles bind to the surface of the interface, stabilizing the emulsion.
As used throughout the disclosure, the terms “wax” or “waxy material” refer to a water-insoluble organic material that is solid or semi-solid at room temperature, has a density less than water, and can transition to a molten state at a temperature greater than room temperature to form a liquid.
As used throughout the disclosure, the term “liquid colloidosome” refers to a colloid-sized droplet of a first liquid in a second liquid having particles at the interface formed between the first liquid and the second liquid. The term “solidified colloidosome,” in which the first liquid is solidified, refers to a colloid-sized solid droplet having particles attached on or embedded to its surface.
Winsor type phase behavior terminology is used to distinguish among three phase behaviors of an oil-water-amphiphile system forming a microemulsion. In a Winsor I type system, the amphiphile is soluble in water and forms an oil-in-water (o/w) microemulsion. The amphiphile-rich water phase coexists with the oil phase separated by an oil-water interface. In a Winsor II type system, the amphiphile is soluble in oil and forms a water-in-oil (w/o) microemulsion. The amphiphile-rich oil phase coexists with the water phase separated by an oil-water interface. In a Winsor III type system, the amphiphile is soluble in both oil and water and forms a microemulsion as a separate, continuous phase. The amphiphile-rich continuous phase forms a layer that separates the oil phase and the water phase. The amphiphile-rich continuous phase includes the amphiphile, oil, and water. The Winsor III type system is favored for tertiary oil recovery, as the system exhibits reduced interfacial tension between hydrocarbon and water in reservoir conditions after secondary oil recovery.
The base particle used for the asymmetrically functionalized nanoparticle 122 can include particles in the microscale and nanoscale. For example, the size of the base particle can range between about 1 nanometer (nm) and about 100 microns, alternately between about 10 nm and about 10 microns, alternately between about 50 nm and about 1 micron, or alternately between about 80 nm and about 200 nm. In at least one embodiment, the base particle can have size ranging between about 80 nm and about 110 nm. The base particle can have a variety of three-dimensional shapes, including but not limited to, spherical, ellipsoidal, rod-like, helical, and oblate. The base particle can be solid or hollow. The material used for the base particle includes silicon dioxide (or silica). Silicon dioxide can be provided in any form including but not limited to, pristine silica, quartz, tridymite, cristobalite, keatite, moganite, coesite, stishovite, seifertite, melanophlogite, sand, glass, fumed silica, and precipitated silica. One skilled in the art would recognize that the hydrophobicity of silicon dioxide depends on its crystalline form. In at least one embodiment, the base particle has a lipophilic surface.
The functionalized surface 126 can be chemically modified with a functional group 130 including polyethylenimine forming the functionalized portion 132 of the asymmetrically functionalized nanoparticle 122. The non-functionalized surface 128 is in the absence of polyethylenimine forming the non-functionalized portion 134 of the asymmetrically functionalized nanoparticle 122. Polyethylenimine can be linear or branched. Optionally, the functional group 130 can be labeled with a fluorescent dye. The fluorescent dye can include FITC. In at least one embodiment, the functionalized portion 132 of the asymmetrically functionalized nanoparticle 122 is hydrophilic. In at least one embodiment, the non-functionalized portion 134 of the asymmetrically functionalized nanoparticle 122 is lipophilic.
In step 202, the base nanoparticle undergoes surface treatment. Treating the surface of the base nanoparticle enables one to chemically modify the surface in a controlled manner. The surface treatment can be conducted by immersing the base nanoparticle in an alcohol-based solvent (optionally combined with water). The alcohol-based solvent can include methanol, ethanol, propanol, and combinations of the same. The temperature of the alcohol-based solvent can be maintained at a temperature ranging between about 50 deg. C and about 80 deg. C or alternately between about 60 deg. C and about 70 deg. C for about one to two hours. In at least one embodiment, the temperature of the alcohol-based solvent is maintained at about 65 deg. C for about one to two hours. In other embodiments, the surface treatment can be conducted by immersing the base nanoparticle in an aqueous sodium hydroxide solution. The sodium hydroxide solution can have a concentration ranging between about 20 wt. % and about 70 wt. %. In at least one embodiment, the sodium hydroxide solution has a concentration of about 60 wt. %. The temperature of the sodium hydroxide solution can be maintained at a temperature ranging between about 50 deg. C and about 80 deg. C or alternately between about 60 deg. C and about 70 deg. C for about one to two hours. In at least one embodiment, the temperature of the sodium hydroxide solution is maintained at about 65 deg. C for about one to two hours. The surface treating step ensures that the surface of the base nanoparticle has hydroxyl groups evenly distributed throughout the entirety of the surface in preparation for functionalization. The surface treated base nanoparticles can be further filtrated, washed, and dried for purification. The surface treated base nanoparticles are dispersed in an aqueous solvent (such as water) forming an aqueous dispersion. The aqueous dispersion is maintained at a temperature ranging between about 50 deg. C and about 80 deg. C or alternately between about 60 deg. C and about 70 deg. C. In at least one embodiment, the temperature of the aqueous dispersion is maintained at about 65 deg. C.
In step 204, the aqueous dispersion including the surface treated base nanoparticles are combined with a waxy material to form an emulsion at a temperature greater than the melting point of the waxy material. The emulsion is maintained at a temperature ranging between about 50 deg. C and about 120 deg. C or alternately between about 60 deg. C and about 100 deg. C. In at least one embodiment, the temperature of the aqueous dispersion is maintained at about 85 deg. C. The waxy material can have a concentration ranging between about 4.1 wt. % and about 16.6 wt. % of the total weight of the emulsion. Optionally, a surfactant can be added to supplement the stability of the emulsion. The waxy material forms colloidal droplets in the aqueous environment, essentially forming an o/w microemulsion. A liquid-liquid interface is formed between the colloidal droplet and the aqueous environment, and the surface treated base nanoparticles are adsorbed at the liquid-liquid interface forming a liquid colloidosome. The liquid colloidosome includes the waxy material as the interior component and the surface treated base nanoparticles as the exterior component.
The waxy material can include various fatty alcohols and fatty acids, and esters of such fatty alcohols and fatty acids, having greater than ten carbon atoms. The fatty alcohols and fatty acids can be saturated or unsaturated. The fatty alcohols and fatty acids can be linear or branched. Non-limiting examples of saturated fatty acids include capric, lauric, myristic, palmitic, margaric, stearic, arachidic, behenic, tetracosanic, lignoceric, cerotic, and melis sic. Non-limiting examples of unsaturated fatty acids include tiglic, hypogaeic, gaidic, physetoleic, elaidic, oleic, isooleic, erudic, brassidic, and isoerudic. Non-limiting examples of fatty alcohols include octadecyl, carnaubyl, ceryl, melissyl, and phytol. Non-limiting examples also include sterols such as cholesterol, and glycerols.
The waxy material can include natural and modified natural waxes. Non-limiting examples of natural or modified natural waxes include various plant derived waxes, grease, and oils including carnauba wax, cranberry wax, ouricuri wax, candelilla wax, raphia wax, apple, cotton and cactus waxes. Non-limiting examples of natural or modified natural waxes include waxes and greases produced by bacteria (for example, cetyl stearate), waxes and greases produced by fungi, protozoa and algae, invertebrate waxes and greases including insect waxes such as beeswaxes (for example, triacontyl palmitate, palmatyl palmitate), and Coccus sp. derived waxes (for example, lac, cochineal and Chinese insect), and animal fats (for example, triglycerides) and animal waxes including spermaceti (for example, cetyl palmitate), lanolin and wool grease.
The waxy material can include natural and synthetic hydrocarbons. Non-limiting examples of natural and synthetic hydrocarbons include white waxes, paraffin waxes, ceresins, silicon greases and waxes, polychlorinated and polyfluorinated hydrocarbons, aromatic hydrocarbons (such as naphthalene and durene(1,2,4,5-tetramethylbenzene)), polyether waxes, and polyester waxes. Waxes can include waxy polymers, which are polymers that have wax-like chemical or physical properties alone or when combined with other waxes. Non-limiting examples of waxy polymers include polyethylenes and polypropylenes.
In step 206, the liquid colloidosome-containing emulsion is cooled to a temperature less than the melting point of the waxy material. In at least one embodiment, the liquid colloidosome-containing emulsion is cooled to room temperature. The waxy material forming the interior of the liquid colloidosome solidifies to form a solidified colloidosome. As the waxy material solidifies, the surface treated base nanoparticles are either attached on or partially (but not fully) embedded in the exterior surface of the solid waxy material. In this manner, the surface treated base nanoparticles of the solidified colloidosome have two different surfaces, where one surface is exposed to the exterior environment (the portion of the surface to be functionalized) and the other surface is not exposed to the exterior environment (the remaining portion of the surface to be left intact). The solidified colloidosome can be further filtrated, washed, and dried for purification.
In step 208, the solidified colloidosome is re-dispersed in a solvent forming a dispersion.
Non-limiting examples of the solvent include water, methanol, and ethanol. In some embodiments, the solvent includes aqueous ethanol having an ethanol concentration ranging between about 65 wt. % and about 90 wt. %.
In step 210, a functionalizing material is introduced to the solidified colloidosome dispersion to chemically modify the exposed surface of the base nanoparticle. In at least one embodiment, the functionalizing material is polyethylenimine. The functionalizing material can include a fluorophore labeled to the functionalizing material. In at least one embodiment, the fluorophore is FITC. The non-exposed surface of the base nanoparticle maintains contact with the solid waxy material and is not affected by the functionalizing material. The chemically modified, solidified colloidosomes can be further filtrated and washed for purification.
In step 212, the solid interior of the chemically modified, solidified colloidosome is removed by introducing an organic solvent capable of dissolving the waxy material. Non-limiting examples of the organic solvent include chloroform, toluene, and diethyl ether. In at least one embodiment, the organic solvent is chloroform. In this manner, the asymmetrically functionalized nanoparticle is released. In some embodiments, the solidified colloidosome can be heated to a temperature greater than the melting point of the waxy material to melt and remove the waxy material to release the asymmetrically functionalized nanoparticle. In some embodiments, the solidified colloidosome can be heated to a temperature ranging between about 40 deg. C and about 50 deg. C in the presence of the organic solvent to dissolve the waxy material to release the asymmetrically functionalized nanoparticle.
In step 214, the released asymmetrically functionalized nanoparticles can be further filtrated and washed for purification. The assymetrically functionalized nanoparticles can be stored as dried particles or re-dispsersed in deionized water.
In an example embodiment of the method, the asymmetrically functionalized nanoparticles can be introduced to a subterranean formation for tertiary oil recovery. The subterranean formation is one that typically underwent primary and secondary oil recovery where residual crude oil and water (used for secondary oil recovery) coexist in the subterranean formation. The asymmetrically functionalized nanoparticles are stable under reservoir conditions and are capable of reducing the interfacial tension between the residual crude oil and water for tertiary oil recovery.
The disclosure is illustrated by the following examples, which are presented for illustrative purposes only, and are not intended as limiting the scope of the invention which is defined by the appended claims.
Silica nanoparticles were prepared in the lab using the following procedure. 200 milliliters (mL) of a 99 wt. % ethanol (MilliporeSigma, Burlington, MA), 16.0 mL of 29 wt. % ammonium hydroxide (MilliporeSigma, Burlington, MA), and 12.2 mL of deionized water were combined and magnetically stirred at a speed of 2,100 revolutions per minute (rpm) for about 30 minutes at room temperature to form a mixture. Subsequently, 12.4 mL of tetraethyl orthosilicate (MilliporeSigma, Burlington, MA) was gradually added to the mixture in droplets under continuous magnetic stirring. The resulting mixture was kept overnight at room temperature. The opacity of the mixture changed from transparent to opaque over time indicative of forming the silica nanoparticles. The silica nanoparticles were filtrated and rinsed with deionized water to remove any residual material. Three cycles of centrifugation were conducted. The silica nanoparticles had a diameter ranging between about 80 nanometers (nm) and about 110 nm.
One gram of the silica nanoparticles was dispersed in 10 mL of a 90 wt. % methanol (or ethanol) solution and sonicated for about 3 to about 5 minutes at room temperature. The temperature was increased to about 65 deg. C and the dispersion was magnetically stirred at a speed of 2,100 rpm for about one to two hours to ensure that the surfaces of the silica nanoparticles were evenly pretreated with hydroxyl groups. The surface treated silica nanoparticles were filtrated and washed with deionized water three times. The surface treated silica nanoparticles were washed with ethanol twice. The surface treated silica nanoparticles were incubated in a vacuum oven at about 110 deg. C under vacuum for about 24 hours. The dried silica nanoparticles were dispersed in deionized water and the aqueous dispersion was sonicated for about 5-10 minutes. The aqueous dispersion was heated to a temperature of about 65 deg. C.
Pickering emulsion technique was implemented to control surface functionalization of the silica nanoparticles. Various quantities (1.0, 1.5, and 2.0 grams) of paraffin wax (locally acquired) were used as a masking agent and was gradually added to the aqueous dispersion under continuous magnetic stirring. The paraffin wax had a melting temperature of about 65 deg. C. The resulting mixture was homogenized using a homogenizer followed by increasing and maintaining the temperature at about 85 deg. C for about two hours to ensure that liquid colloidosomes are formed. The paraffin wax formed colloidal droplets in the existing aqueous environment where the silica nanoparticles were placed at the exterior of the colloidal droplets forming the liquid colloidosomes. The mixture was cooled to room temperature such that the liquid colloidosomes formed solidified colloidosomes as the paraffin wax solidified. The solidified colloidosomes were vacuum filtrated to eliminate unattached, free flowing silica nanoparticles. The filtrated, solidified colloidosomes were re-dispersed in deionized water at room temperature to form an aqueous dispersion.
Polyethylenimine (having an average molecular weight of about 25,000, pre-dissolved in water, MilliporeSigma, Burlington, MA) was added to the aqueous dispersion of solidified colloidosomes to asymmetrically functionalize the silica nanoparticles. The surfaces of the silica nanoparticles exposed to the aqueous environment were chemically modified with polyethylenimine. Various quantities of polyethylenimine (5.0, 7.5, and 10 wt. %) were used to determine the impact on the synthesized Janus nanoparticle morphology. The polyethylenimine was labeled with FITC by adding about 2.0-8.0 mL of 0.001 wt. % aqueous FITC (fluorescence at 490 nm, MilliporeSigma, Burlington, MA) to the reaction mixture along with a few drops of ethanol. FITC was selected as the fluorophore due to its chemical affinity to react with and bond to amine groups present in polyethylenimine. Functionalization was continued overnight at room temperature. The chemically modified, solidified colloidosomes were filtrated to eliminate excess polyethylenimine and the filtrates were washed several times with ethanol.
Chloroform was added to the chemically modified, solidified colloidosomes to dissolve the paraffin wax and to release the polyethylenimine-silica Janus nanoparticles. Three cycles of centrifugation were conducted. The polyethylenimine-silica Janus nanoparticles were collected and placed in a vacuum oven at about 70-90 deg. C under vacuum for about 48 hours.
Various quantities of paraffin wax (1.0, 1.5, and 2.0 grams) were used to determine the optimal yield of the polyethylenimine-silica Janus nanoparticles. 1.0 gram of paraffin wax produced 95.4 milligrams (mg) of Janus nanoparticles while producing 45.0 mg of non-desired, fully polyethylenimine-functionalized silica nanoparticles. 1.5 grams of paraffin wax produced 120.7 mg of Janus nanoparticles while producing 18.2 mg of non-desired, fully polyethylenimine-functionalized silica nanoparticles. 2.0 grams of paraffin wax produced 160.2 mg of Janus nanoparticles in the absence of fully polyethylenimine-functionalized silica nanoparticles.
Scanning electron microscopy (SEM) was used to investigate the morphology of the solidified colloidosomes (before functionalization) and the polyethylenimine-silica Janus nanoparticles. The results are shown in
Fourier transform infrared (FTIR) spectroscopy was conducted to investigate the chemical composition of pristine silica and the polyethylenimine-silica Janus nanoparticles. The results are shown in
Thermal gravimetric analysis (TGA) was conducted to further investigate the chemical composition of pristine silica and the polyethylenimine-silica Janus nanoparticles. The results are shown in
Experiments were conducted to determine the suitability of the polyethylenimine-silica Janus nanoparticles as a component of a nanofluid used for oil recovery. Emulsions were prepared by mixing 4.0 mL of toluene, 4.0 mL of deionized water, 1.3 mL of a sodium sulfonate surfactant (Petronate® HL/L, Sonneborn, Parsippany, NJ), and 2.0 mL of 5.0, 7.5, or 10.0 wt. % polyethylenimine-silica Janus nanoparticles dispersed in deionized water. After emulsification, the emulsions were placed still for about 24 hours to evaluate the migration of the polyethylenimine-silica Janus nanoparticles towards the oil-water interface. The water phase was dyed with Rhodamine B exhibiting a pink color. The polyethylenimine-silica Janus nanoparticle dispersion exhibited a light yellow color due to FITC labeling. The toluene phase was transparent.
Further modifications and alternative embodiments of various aspects of the disclosure will be apparent to those skilled in the art in view of this description. Accordingly, this description is to be construed as illustrative only and is for the purpose of teaching those skilled in the art the general manner of carrying out the embodiments described in the disclosure. It is to be understood that the forms shown and described in the disclosure are to be taken as examples of embodiments. Elements and materials may be substituted for those illustrated and described in the disclosure, parts and processes may be reversed or omitted, and certain features may be utilized independently, all as would be apparent to one skilled in the art after having the benefit of this description. Changes may be made in the elements described in the disclosure without departing from the spirit and scope of the disclosure as described in the following claims. Headings used described in the disclosure are for organizational purposes only and are not meant to be used to limit the scope of the description.
This application is a divisional application of U.S. patent application Ser. No. 16/849,587, filed Apr. 15, 2020, the entire disclosure of which is incorporated here by reference.
Number | Date | Country | |
---|---|---|---|
Parent | 16849587 | Apr 2020 | US |
Child | 18329857 | US |