Claims
- 1. A method for the conversion of synthesis gas comprising:
- contacting synthesis gas which comprises hydrogen and carbon monoxide with a catalytically effective amount of a crystalline ferroborosilicate composition, under conversion conditions effective to provide ethane selectivity of at least 40%, said borosilicate composition represented in terms of mole ratios as follows: (0.2 to 15) M.sub.2/m O:(0.2 to 10) Z.sub.2 O .sub.3 : (5 to 1000) SiO.sub.2 : Fe.sub.2/n O: (0 to 2000) H.sub.2 O wherein M comprises a cation of a quaternary ammonium, metal, ammonium, hydrogen and mixtures thereof, m is the valence of said cation, n is the valence of the iron cation, and Z is boron, said composition containing ion-exchanged palladium or palladium impregnated onto said composition.
- 2. A method according to claim 1 wherein the composition is substantially sodium free.
- 3. A method for the conversion of synthesis gas comprising:
- contacting synthesis gas which comprises hydrogen and carbon monoxide with a catalytically effective amount of a crystalline ferroborosilicate composition, under conversion conditions effective to provide ethane selectivity of at least 40%, said ferroborosilicate composition being prepared by a method which comprises:
- (a) heating a reaction mixture capable of forming a crystalline product, said reaction mixture comprising quaternary ammonium compound, a source of boron, an oxide of silicon, an alkali metal hydroxide, a source of iron oxide and water;
- (b) recovering the crystalline product;
- (c) heating the recovered crystalline product in an inert atmosphere or air at 200.degree.-900.degree. C. for 1 to 60 hours, and
- (d) ion-exchanging the heat treated crystalline product with a palladium salt solution to provide a palladiumm ion-exchanged crystalline ferroborosilicate.
- 4. A method according to claim 3 wherein said reaction mixture additionally contains a chelating agent.
- 5. A method according to claim 4 wherein said chelating agent is 8-hydroxyquinoline-5-sulfonic acid.
- 6. A method according to claim 3 wherein said quaternary ammonium compound is tetrapropylammonium bromide, said source of aluminum oxide is aluminum chloride or aluminum hydroxide, said source of boron oxide is boric acid, said oxide of silicon is fumed silica, said alkali metal hydroxide is sodium hydroxide and said source of iron oxide is ferrous chloride, ferric chloride or mixtures thereof.
- 7. A method according to claim 3, including the following additional step:
- (e) calcining the palladium ion-exchanged crystalline ferroborosilicate in air at a temmperature of about 300.degree. C. to about 600.degree. C. for at least 4 hours.
- 8. A method according to claim 7, including the following additional steps:
- (f) heating the calcined palladium ferroborosilicate in the presence of hydrogen from ambient temperature to an elevated temperature of about 300.degree. C. to about 400.degree. C. at a rate of temperature increase of about 0.5 to about 2.0.degree. C. per minute;
- (g) maintaining said borosilicate at said temperature for about 0.75 to about 1.25 hour; and
- (h) cooling said borosilicate to ambient temperature in the presence of hydrogen.
- 9. A method according to claim 3, including the following additional step:
- (i) mixing said siicate with a methanol synthesis catalyst.
- 10. A method according to claim 9 wherein said methanol catalyst comprises chromium oxide-zinc oxide or copper oxide-zinc oxide.
CROSS-REFERENCE TO RELATED APPLICATIONS
This application is a continuation of copending application Ser. No. 751,168, filed on July 2, 1985, now abandoned, which is a continuation-in-part of application Ser. No. 256,308 filed April 22, 1981 now abandoned which is a continuation-in-part of application Ser. No. 092,127, filed Nov. 7, 1979, now U.S. Pat. No. 4,331,641.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
4208305 |
Kouwenhuven et al. |
Jun 1980 |
|
4269813 |
Klotz |
May 1981 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
751168 |
Jul 1985 |
|
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
256308 |
Apr 1981 |
|
Parent |
92127 |
Nov 1979 |
|