Claims
- 1. A method for the conversion of synthesis gas comprising:
- contacting synthesis gas which comprises hydrogen and carbon monoxide with a catalytically effective amount of a crystalline ferrometallosilicate composition represented in terms of mole ratios as follows: ##EQU3## wherein M comprises a cation of a quaternary ammonium, metal, ammonium, hydrogen and mixtures thereof, m is the valence of said cation, n is the valence of the iron cation, Z is aluminum, titanium or manganese and z is the valence of the Z cation,
- wherein said composition contains ion-exchanged palladium or palladium impregnated onto said composition, and
- said contacting is conducted under conversion conditions effective to provide an ethane selectivity of at least 45% when Z is aluminum or titanium and a C.sub.3 selectivity of at least 35% when Z is manganese.
- 2. A method according to claim 1 wherein the composition is substantially sodium free.
- 3. A method for the conversion of synthesis gas comprising:
- contacting synthesis gas which comprises hydrogen and carbon monoxide with a catalytically effective amount of a crystalline ferrometallosilicate composition prepared by a method which comprises:
- (a) heating a reaction mixture capable of forming a crystalline product under conditions effective to provide a crystalline product, said reaction mixture comprising a quaternary ammonium compound, a source of an aluminum oxide, titanium oxide or manganese oxide, an oxide of silicon, an alkali metal hydroxide, a source of iron oxide, and water,
- (b) recovering the crystalline product, and
- (c) ion-exchanging the recovered crystalline product with a palladium salt solution to provide a palladium ion-exchanged crystalline ferrometallosilicate,
- wherein said contacting is conducted under conversion conditions effective to provide an ethane selectivity of at least 45% when said reaction mixture comprises aluminum oxide or titanium oxide and a C.sub.3 selectivity of at least 35% when said reaction mixture comprises manganese oxide.
- 4. A method according to claim 3 wherein said reaction mixture additionally contains a chelating agent.
- 5. A method according to claim 4 wherein said chelating agent is 8-hydroxyquinoline-5-sulfonic acid or urea.
- 6. A method according to claim 3 wherein said quaternary ammonium compound is tetrapropylammonium bromide, said source of aluminum oxide is aluminum chloride or aluminum hydroxide, said source of titanium oxide is titanium chloride, said source of manganese oxide is manganese sulfate, manganese chloride or manganese nitrate, said oxide of silicon is fumed silica, said alkali metal hydroxide is sodium hydroxide and said source of iron oxide is ferrous chloride, ferric chloride or mixtures thereof.
- 7. A method according to claim 3, including the following additional step:
- (d) calcining the palladium ion-exchanged crystalline ferrometallosilicate in air at a temperature of about 300.degree. C. to about 600.degree. C. for at least 4 hours.
- 8. A method according to claim 7, including the following additional steps:
- (e) heating the calcined palladium ferrometallosilicate in the presence of hydrogen from ambient temperature to an elevated temperature of about 300.degree. C. to about 400.degree. C. at a rate of temperature increase of about 0.5.degree. to about 2.degree. C. per minute;
- (f) maintaining said silicate at said temperature for about 0.75 to about 1.25 hour; and
- (g) cooling said silicate to ambient temperature in the presence of hydrogen.
- 9. A method according to claim 3, including the following additional step:
- (h) mixing said silicate with a methanol synthesis catalyst.
- 10. A method according to claim 9 wherein said methanol catalyst comprises chrominum oxide-zinc oxide or copper oxide-zinc oxide.
CROSS-REFERENCE TO RELATED APPLICATIONS
This application is a continuation-in-part of application Ser. No. 256,299 filed Apr. 22, 1981 which is a continuation-in-part of application Ser. No. 092,127, filed Nov. 7, 1979, now U.S. Pat. No. 4,331,641.
US Referenced Citations (3)
Number |
Name |
Date |
Kind |
4086262 |
Chang et al. |
Apr 1978 |
|
4255349 |
Butter et al. |
Mar 1981 |
|
4337176 |
Boersma et al. |
Jun 1982 |
|