Patent Grant
10968292
The present invention relates to a synthetic polymer film whose surface has a microbicidal activity, a photocurable resin composition for use in formation of the synthetic polymer film, a manufacturing method of the synthetic polymer film, and a sterilization method with the use of the surface of the synthetic polymer film.
Recently, it was reported that surficial nanostructures of black silicon, wings of cicadas and dragonflies have a bactericidal activity (Ivanova, E. P. et al., “Bactericidal activity of black silicon”, Nat. Commun. 4:2838 doi: 10.1038/ncomms3838 (2013)). Reportedly, the physical structure of the nanopillars that black silicon and wings of cicadas and dragonflies have produces a bactericidal activity.
According to Ivanova, E. P. et al., black silicon has the strongest bactericidal activity on Gram-negative bacteria, while wings of dragonflies have a weaker bactericidal activity, and wings of cicadas have a still weaker bactericidal activity. Black silicon has 500 nm tall nanopillars. Wings of cicadas and dragonflies have 240 nm tall nanopillars. The static contact angle (hereinafter, also simply referred to as “contact angle”) of the black silicon surface with respect to water is 80°, while the contact angles of the surface of wings of dragonflies and cicadas with respect to water are 153° and 159°, respectively. It is estimated that black silicon is mainly made of silicon, and wings of dragonflies and cicadas are made of chitin. According to Ivanova, E. P. et al., the composition of the surface of black silicon is generally a silicon oxide, and the composition of the surface of wings of dragonflies and cicadas is generally a lipid.
The mechanism of killing bacteria by nanopillars is not clear from the results described in Ivanova, E. P. et al. It is also not clear whether the reason why black silicon has a stronger bactericidal activity than wings of dragonflies and cicadas resides in the difference in height or shape of nanopillars, in the difference in surface free energy (which can be evaluated by the contact angle), in the materials that constitute nanopillars, or in the chemical properties of the surface.
The bactericidal activity of black silicon is difficult to utilize because black silicon is poor in mass productivity and is hard but brittle so that the shapability is poor.
A major object of the present invention is to provide a synthetic polymer film whose surface has a microbicidal activity, a photocurable resin composition for use in formation of the synthetic polymer film, a synthetic polymer film production method, and a sterilization method with the use of the surface of the synthetic polymer film.
A synthetic polymer film of an embodiment of the present invention is a synthetic polymer film whose surface has a plurality of raised or recessed portions, wherein the synthetic polymer film has a crosslink structure, and the crosslink structure does not contain any nitrogen element that is a constituent of a urethane bond, the synthetic polymer film contains an organic carboxylic acid, and an amount of water required for dissolving 1 g of the organic carboxylic acid is equal to or greater than 10 mL and less than 10000 mL, and at the lapse of 5 minutes since placing a 200 μL drop of water on the surface of the synthetic polymer film, a pH of an aqueous solution is not more than 5, and an area equivalent circle diameter of the aqueous solution is not less than 20 mm.
As for the solubility of the organic carboxylic acid in water, the amount of water required for dissolving 1 g of the organic carboxylic acid is preferably not less than 100 mL, more preferably not less than 200 mL, and is preferably less than 2000 mL.
In one embodiment, when viewed in a normal direction of the synthetic polymer film, a two-dimensional size of the plurality of raised or recessed portions is in the range of more than 20 nm and not more than 1 μm.
In one embodiment, when viewed in the normal direction of the synthetic polymer film, the two-dimensional size of the plurality of raised or recessed portions is less than 500 nm.
In one embodiment, when viewed in the normal direction of the synthetic polymer film, the two-dimensional size of the plurality of raised or recessed portions is not less than 500 nm.
In one embodiment, the synthetic polymer film further contains an acid stronger than the organic carboxylic acid. The acid stronger than the organic carboxylic acid is, for example, phosphoric acid or sulfonic acid.
In one embodiment, the organic carboxylic acid is 2,4,6-trimethylbenzoic acid, suberic acid or sebacic acid. The amount of water required for dissolving 1 g of these organic carboxylic acids is equal to or greater than 200 mL and less than 2000 mL.
In one embodiment, the synthetic polymer film is made of a photocurable resin, and the organic carboxylic acid is generated by photodecomposition of a photopolymerization initiator contained in the photocurable resin.
In one embodiment, the photopolymerization initiator contains bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide.
In one embodiment, the photopolymerization initiator further contains diphenyl (2,4,6-trimethylbenzoyl) phosphine oxide.
In one embodiment, the crosslink structure contains an ethylene oxide unit.
A liquid sterilization method of an embodiment of the present invention is a method for sterilizing a liquid including water by bringing the liquid into contact with the surface of the synthetic polymer film as set forth in any of the foregoing paragraphs.
A photocurable resin composition of an embodiment of the present invention is a photocurable resin composition for use in production of a synthetic polymer film whose surface has a microbicidal activity, including: a photocurable resin; and an organic carboxylic acid or a photoacid generator which generates the organic carboxylic acid, wherein an amount of water required for dissolving 1 g of the organic carboxylic acid is equal to or greater than 10 mL and less than 10000 mL.
In one embodiment, the photocurable resin is radically polymerizable. In one embodiment, the photocurable resin is an acrylic resin. In one embodiment, the photocurable resin is a UV-curable resin.
A method for producing a synthetic polymer film whose surface has a microbicidal activity according to an embodiment of the present invention includes a step of mixing water in the photocurable resin composition as set forth in any of the foregoing paragraphs and thereafter irradiating the resultant photocurable resin composition with light. The amount of the water with respect to the entirety of the photocurable resin composition is equal to or greater than 1 mass % and not more than 10 mass %.
According to an embodiment of the present invention, a synthetic polymer film whose surface has a microbicidal activity, a photocurable resin composition for use in formation of the synthetic polymer film, a synthetic polymer film production method, and a sterilization method with the use of the surface of the synthetic polymer film are provided.
Hereinafter, a synthetic polymer film whose surface has a microbicidal effect and a sterilization method with the use of the surface of the synthetic polymer film according to embodiments of the present invention are described with reference to the drawings.
In this specification, the following terms are used.
“Sterilization” (or “microbicidal”) means reducing the number of proliferative microorganisms contained in an object, such as solid or liquid, or a limited space, by an effective number.
“Microorganism” includes viruses, bacteria, and fungi.
“Antimicrobial” generally includes suppressing and preventing multiplication of microorganisms and includes suppressing dinginess and slime which are attributed to microorganisms.
The present applicant conceived a method for producing an antireflection film (an antireflection surface) which has a moth-eye structure with the use of an anodized porous alumina layer. Using the anodized porous alumina layer enables manufacture of a mold which has an inverted moth-eye structure with high mass-productivity.
The present inventors developed the above-described technology and arrived at a synthetic polymer film whose surface has a microbicidal effect (see, for example, WO 2015/163018, WO 2016/080245 and WO 2016/208540). The entire disclosures of WO 2015/163018, WO 2016/080245 and WO 2016/208540 are incorporated by reference in this specification.
The configuration of a synthetic polymer film according to an embodiment of the present invention is described with reference to
A film 50A shown in
The synthetic polymer film 34A shown in
A film 50B shown in
When viewed in a normal direction of the synthetic polymer film 34B, the two-dimensional size of the raised portions 34Bp, Dp, is in the range of more than 20 nm and less than 500 nm. The typical adjoining distance of the raised portions 34Bp, Dint, is more than 20 nm and not more than 1000 nm, and Dp<Dint holds. That is, in the synthetic polymer film 34B, there is a flat portion between adjoining raised portions 34Bp. The raised portions 34Bp have the shape of a cylinder with a conical portion on the air side. The typical height of the raised portions 34Bp, Dh, is not less than 50 nm and less than 500 nm. The raised portions 34Bp may be arranged regularly or may be arranged irregularly. When the raised portions 34Bp are arranged regularly, Dint also represents the period of the arrangement. This also applies to the synthetic polymer film 34A, as a matter of course.
In this specification, the “moth-eye structure” includes not only surficial nanostructures that have an excellent antireflection function and that are formed by raised portions which have such a shape that the cross-sectional area (a cross section parallel to the film surface) increases as do the raised portions 34Ap of the synthetic polymer film 34A shown in
A mold for forming the moth-eye structure such as illustrated in
A manufacturing method of a moth-eye mold 100A that is for production of the synthetic polymer film 34A is described with reference to
Firstly, a mold base 10 is provided which includes an aluminum base 12, an inorganic material layer 16 provided on a surface of the aluminum base 12, and an aluminum film 18 deposited on the inorganic material layer 16 as shown in
The aluminum base 12 used may be an aluminum base whose aluminum purity is not less than 99.50 mass % and less than 99.99 mass % and which has relatively high rigidity. The impurity contained in the aluminum base 12 may preferably include at least one element selected from the group consisting of iron (Fe), silicon (Si), copper (Cu), manganese (Mn), zinc (Zn), nickel (Ni), titanium (Ti), lead (Pb), tin (Sn) and magnesium (Mg). Particularly, Mg is preferred. Since the mechanism of formation of pits (hollows) in the etching step is a local cell reaction, the aluminum base 12 ideally does not contain any element which is nobler than aluminum. It is preferred that the aluminum base 12 used contains, as the impurity element, Mg (standard electrode potential: −2.36 V) which is a base metal. If the content of an element nobler than aluminum is 10 ppm or less, it can be said in terms of electrochemistry that the aluminum base 12 does not substantially contain the element. The Mg content is preferably 0.1 mass % or more of the whole. It is, more preferably, in the range of not more than about 3.0 mass %. If the Mg content is less than 0.1 mass %, sufficient rigidity cannot be obtained. On the other hand, as the Mg content increases, segregation of Mg is more likely to occur. Even if the segregation occurs near a surface over which a moth-eye mold is to be formed, it would not be detrimental in terms of electrochemistry but would be a cause of a defect because Mg forms an anodized film of a different form from that of aluminum. The content of the impurity element may be appropriately determined depending on the shape, thickness, and size of the aluminum base 12, in view of required rigidity. For example, when the aluminum base 12 in the form of a plate is prepared by rolling, the appropriate Mg content is about 3.0 mass %. When the aluminum base 12 having a three-dimensional structure of, for example, a hollow cylinder is prepared by extrusion, the Mg content is preferably 2.0 mass % or less. If the Mg content exceeds 2.0 mass %, the extrudability deteriorates in general.
The aluminum base 12 used may be an aluminum pipe in the shape of a hollow cylinder which is made of, for example, JIS A1050, an Al—Mg based alloy (e.g., JIS A5052), or an Al—Mg—Si based alloy (e.g., JIS A6063).
The surface of the aluminum base 12 is preferably a surface cut with a bit. If, for example, abrasive particles are remaining on the surface of the aluminum base 12, conduction will readily occur between the aluminum film 18 and the aluminum base 12 in a portion in which the abrasive particles are present. Not only in the portion in which the abrasive particles are remaining but also in a portion which has a roughened surface, conduction is likely to occur locally between the aluminum film 18 and the aluminum base 12. When conduction occurs locally between the aluminum film 18 and the aluminum base 12, there is a probability that a local cell reaction will occur between an impurity in the aluminum base 12 and the aluminum film 18.
The material of the inorganic material layer 16 may be, for example, tantalum oxide (Ta2O5) or silicon dioxide (SiO2). The inorganic material layer 16 can be formed by, for example, sputtering. When a tantalum oxide layer is used as the inorganic material layer 16, the thickness of the tantalum oxide layer is, for example, 200 nm.
The thickness of the inorganic material layer 16 is preferably not less than 100 nm and less than 500 nm. If the thickness of the inorganic material layer 16 is less than 100 nm, there is a probability that a defect (typically, a void; i.e., a gap between crystal grains) occurs in the aluminum film 18. If the thickness of the inorganic material layer 16 is not less than 500 nm, insulation is likely to occur between the aluminum base 12 and the aluminum film 18 due to the surface condition of the aluminum base 12. To realize anodization of the aluminum film 18 by supplying an electric current from the aluminum base 12 side to the aluminum film 18, the electric current needs to flow between the aluminum base 12 and the aluminum film 18. When employing a configuration where an electric current is supplied from the inside surface of the aluminum base 12 in the shape of a hollow cylinder, it is not necessary to provide an electrode to the aluminum film 18. Therefore, the aluminum film 18 can be anodized across the entire surface, while such a problem does not occur that supply of the electric current becomes more difficult as the anodization advances. Thus, the aluminum film 18 can be anodized uniformly across the entire surface.
To form a thick inorganic material layer 16, it is in general necessary to increase the film formation duration. When the film formation duration is increased, the surface temperature of the aluminum base 12 unnecessarily increases, and as a result, the film quality of the aluminum film 18 deteriorates, and a defect (typically, a void) occurs in some cases. When the thickness of the inorganic material layer 16 is less than 500 nm, occurrence of such a problem can be suppressed.
The aluminum film 18 is, for example, a film which is made of aluminum whose purity is not less than 99.99 mass % (hereinafter, also referred to as “high-purity aluminum film”) as disclosed in WO 2011/125486. The aluminum film 18 is formed by, for example, vacuum evaporation or sputtering. The thickness of the aluminum film 18 is preferably in the range of not less than about 500 nm and not more than about 1500 nm. For example, the thickness of the aluminum film 18 is about 1 μm.
The aluminum film 18 may be an aluminum alloy film disclosed in WO 2013/183576 in substitution for the high-purity aluminum film. The aluminum alloy film disclosed in WO 2013/183576 contains aluminum, a metal element other than aluminum, and nitrogen. In this specification, the “aluminum film” includes not only the high-purity aluminum film but also the aluminum alloy film disclosed in WO 2013/183576.
Using the above-described aluminum alloy film can realize a specular surface whose reflectance is not less than 80%. The average grain diameter of crystal grains that form the aluminum alloy film when viewed in the normal direction of the aluminum alloy film is, for example, not more than 100 nm, and that the maximum surface roughness Rmax of the aluminum alloy film is not more than 60 nm. The content of nitrogen in the aluminum alloy film is, for example, not less than 0.5 mass % and not more than 5.7 mass %. It is preferred that the absolute value of the difference between the standard electrode potential of the metal element other than aluminum which is contained in the aluminum alloy film and the standard electrode potential of aluminum is not more than 0.64 V, and that the content of the metal element in the aluminum alloy film is not less than 1.0 mass % and not more than 1.9 mass %. The metal element is, for example, Ti or Nd. The metal element is not limited to these examples but may be such a different metal element that the absolute value of the difference between the standard electrode potential of the metal element and the standard electrode potential of aluminum is not more than 0.64 V (for example, Mn, Mg, Zr, V, and Pb). Further, the metal element may be Mo, Nb, or Hf. The aluminum alloy film may contain two or more of these metal elements. The aluminum alloy film is formed by, for example, a DC magnetron sputtering method. The thickness of the aluminum alloy film is also preferably in the range of not less than about 500 nm and not more than about 1500 nm. For example, the thickness of the aluminum alloy film is about 1 μm.
Then, a surface 18s of the aluminum film 18 is anodized to form a porous alumina layer 14 which has a plurality of recessed portions (micropores) 14p as shown in
The porous alumina layer 14 is formed by, for example, anodizing the surface 18s in an acidic electrolytic solution. The electrolytic solution used in the step of forming the porous alumina layer 14 is, for example, an aqueous solution which contains an acid selected from the group consisting of oxalic acid, tartaric acid, phosphoric acid, sulfuric acid, chromic acid, citric acid, and malic acid. For example, the surface 18s of the aluminum film 18 is anodized with an applied voltage of 80 V for 55 seconds using an oxalic acid aqueous solution (concentration: 0.3 mass %, solution temperature: 10° C.), whereby the porous alumina layer 14 is formed.
Then, the porous alumina layer 14 is brought into contact with an alumina etchant such that a predetermined amount is etched away, whereby the opening of the recessed portions 14p is enlarged as shown in
Then, the aluminum film 18 is again partially anodized such that the recessed portions 14p are grown in the depth direction and the thickness of the porous alumina layer 14 is increased as shown in
Thereafter, when necessary, the porous alumina layer 14 may be brought into contact with an alumina etchant to be further etched such that the pore diameter of the recessed portions 14p is further increased. The etching solution used in this step may preferably be the above-described etching solution. Practically, the same etching bath may be used.
In this way, by alternately repeating the anodization step and the etching step as described above through multiple cycles (e.g., 5 cycles: including 5 anodization cycles and 4 etching cycles), the moth-eye mold 100A that includes the porous alumina layer 14 which has the inverted moth-eye structure is obtained as shown in
The porous alumina layer 14 (thickness: tp) shown in
The recessed portions 14p of the porous alumina layer 14 may have, for example, a conical shape and may have a stepped lateral surface. It is preferred that the two-dimensional size of the recessed portions 14p (the diameter of a circle equivalent to the area of the recessed portions 14p when viewed in a normal direction of the surface), Dp, is more than 20 nm and less than 500 nm, and the depth of the recessed portions 14p, Dd, is not less than 50 nm and less than 1000 nm (1 μm). It is also preferred that the bottom portion of the recessed portions 14p is acute (with the deepest part of the bottom portion being pointed). When the recessed portions 14p are in a densely packed arrangement, assuming that the shape of the recessed portions 14p when viewed in a normal direction of the porous alumina layer 14 is a circle, adjacent circles overlap each other, and a saddle portion is formed between adjacent ones of the recessed portions 14p. Note that, when the generally-conical recessed portions 14p adjoin one another so as to form saddle portions, the two-dimensional size of the recessed portions 14p, Dp, is equal to the adjoining distance Dint. The thickness of the porous alumina layer 14, tp, is not more than about 1 μm.
Under the porous alumina layer 14 shown in
The manufacturing method of the moth-eye mold illustrated herein enables manufacture of a mold which is for production of antireflection films disclosed in Japanese Laid-Open Patent Publication No. 2009-166502, WO 2011/125486 and WO 2013/183576. Since an antireflection film used in a high-definition display panel is required to have high uniformity, selection of the material of the aluminum base, specular working of the aluminum base, and control of the purity and components of the aluminum film are preferably carried out as described above. However, the above-described mold manufacturing method can be simplified because the microbicidal activity can be achieved without high uniformity. For example, the surface of the aluminum base may be directly anodized. Even if, in this case, pits are formed due to impurities contained in the aluminum base, only local structural irregularities occur in the moth-eye structure of the finally-obtained synthetic polymer film 34A, and it is estimated that there is little adverse influence on the microbicidal activity.
According to the above-described mold manufacturing method, a mold in which the regularity of the arrangement of the recessed portions is low, and which is suitable to production of an antireflection film, can be manufactured. In the case of utilizing the microbicidal ability of the moth-eye structure, it is estimated that the regularity of the arrangement of the raised portions does not exert an influence. A mold for formation of a moth-eye structure which has regularly-arranged raised portions can be manufactured, for example, as described in the following section.
For example, after formation of a porous alumina layer having a thickness of about 10 μm, the formed porous alumina layer is removed by etching, and then, anodization may be performed under the conditions for formation of the above-described porous alumina layer. A 10 μm thick porous alumina layer is realized by extending the anodization duration. When such a relatively thick porous alumina layer is formed and then this porous alumina layer is removed, a porous alumina layer having regularly-arranged recessed portions can be formed without being influenced by irregularities which are attributed to grains that are present at the surface of an aluminum film or aluminum base or the process strain. Note that, in removal of the porous alumina layer, using a chromic/phosphoric acid solution is preferred. Although continuing the etching for a long period of time sometimes causes galvanic corrosion, the chromic/phosphoric acid solution has the effect of suppressing galvanic corrosion.
A moth-eye mold for production of the synthetic polymer film 34B shown in
Firstly, in the same way as illustrated with reference to
Then, the porous alumina layer 14 is brought into contact with an alumina etchant such that a predetermined amount is etched away, whereby the opening of the recessed portions 14p is enlarged as shown in
Then, the aluminum film 18 is again partially anodized such that the recessed portions 14p are grown in the depth direction and the thickness of the porous alumina layer 14 is increased as shown in
Thereafter, the etching step and the anodization step are alternately repeated through multiple cycles in the same way as illustrated with reference to
The size of the microorganisms varies depending on their types. For example, the size of P. aeruginosa is about 1 μm. However, the size of the bacteria ranges from several hundreds of nanometers to about five micrometers. The size of fungi is not less than several micrometers. For example, it is estimated that raised portions whose two-dimensional size is about 200 nm have a microbicidal activity on a microorganism whose size is not less than about 0.5 μm, but there is a probability that the raised portions are too large to exhibit a sufficient microbicidal activity on a bacterium whose size is several hundreds of nanometers. The size of viruses ranges from several tens of nanometers to several hundreds of nanometers, and many of them have a size of not more than 100 nm. Note that viruses do not have a cell membrane but have a protein shell called capsid which encloses virus nucleic acids. The viruses can be classified into those which have a membrane-like envelope outside the shell and those which do not have such an envelope. In the viruses which have an envelope, the envelope is mainly made of a lipid. Therefore, it is expected that the raised portions likewise act on the envelope. Examples of the viruses which have an envelope include influenza virus and Ebola virus. In the viruses which do not have an envelope, it is expected that the raised portions likewise act on this protein shell called capsid. When the raised portions include nitrogen element, the raised portions can have an increased affinity for a protein which is made of amino acids.
In view of the above, the configuration and production method of a synthetic polymer film having raised portions which can exhibit a microbicidal activity against a microorganism of not more than several hundreds of nanometers are described below.
In the following description, raised portions of the above-described synthetic polymer film which have a two-dimensional size in the range of more than 20 nm and less than 500 nm are referred to as “first raised portions”. Raised portions which are superimposedly formed over the first raised portions are referred to as “second raised portions”. The two-dimensional size of the second raised portions is smaller than the two-dimensional size of the first raised portions and does not exceed 100 nm. Note that when the two-dimensional size of the first raised portions is less than 100 nm, particularly less than 50 nm, it is not necessary to provide the second raised portions. Recessed portions of the mold corresponding to the first raised portions are referred to as “first recessed portions”, and recessed portions of the mold corresponding to the second raised portions are referred to as “second recessed portions”.
When the method of forming the first recessed portions which have predetermined size and shape by alternately performing the anodization step and the etching step as described above is applied without any modification, the second recessed portions cannot be formed successfully.
In view of the above, a method for manufacturing a mold which is used in production of a synthetic polymer film according to an embodiment of the present invention includes: (a) providing an aluminum base or an aluminum film deposited on a support; (b) the anodization step of applying a voltage at the first level while a surface of the aluminum base or aluminum film is kept in contact with an electrolytic solution, thereby forming a porous alumina layer which has the first recessed portions; (c) after step (b), the etching step of bringing the porous alumina layer into contact with an etching solution, thereby enlarging the first recessed portions; and (d) after step (c), applying a voltage at the second level that is lower than the first level while the porous alumina layer is kept in contact with an electrolytic solution, thereby forming the second recessed portions in the first recessed portions. For example, the first level is higher than 40 V, and the second level is equal to or lower than 20 V.
Specifically, an anodization step is carried out with the voltage at the first level, whereby the first recessed portions are formed which have such a size that is not influenced by the grains of the aluminum base or aluminum film. Thereafter, the thickness of the barrier layer is decreased by etching, and then, another anodization step is carried out with the voltage at the second level that is lower than the first level, whereby the second recessed portions are formed in the first recessed portions. When the second recessed portions are formed through such a procedure, the influence of the grains is avoided.
A mold which has first recessed portions 14pa and second recessed portions 14pb formed in the first recessed portions 14pa is described with reference to
As shown in
The porous alumina layer shown in
The aluminum film used was an aluminum film which contains Ti at 1 mass %. The anodization solution used was an oxalic acid aqueous solution (concentration: 0.3 mass %, solution temperature: 10° C.). The etching solution used was a phosphoric acid aqueous solution (concentration: 10 mass %, solution temperature: 30° C.). After the anodization was carried out with a voltage of 80 V for 52 seconds, the etching was carried out for 25 minutes. Then, the anodization was carried out with a voltage of 80 V for 52 seconds, and the etching was carried out for 25 minutes. Thereafter, the anodization was carried out with a voltage of 20 V for 52 seconds, and the etching was carried out for 5 minutes. Further, the anodization was carried out with a voltage of 20 V for 52 seconds.
As seen from
When a synthetic polymer film is produced using such a mold, the produced synthetic polymer film has raised portions whose configuration is the inverse of that of the first recessed portions 14pa and the second recessed portions 14pb shown in
The thus-produced synthetic polymer film which has the first raised portions and the second raised portions superimposedly formed over the first raised portions has a microbicidal activity on various microorganisms, ranging from relatively small microorganisms of about 100 nm to relatively large microorganisms of not less than 5 μm.
As a matter of course, only raised portions whose two-dimensional size is in the range of more than 20 nm and less than 100 nm may be formed according to the size of a target microorganism. The mold for formation of such raised portions can be manufactured, for example, as described below.
The anodization is carried out using a neutral salt aqueous solution (ammonium borate, ammonium citrate, etc.), such as an ammonium tartrate aqueous solution, or an organic acid which has a low ionic dissociation degree (maleic acid, malonic acid, phthalic acid, citric acid, tartaric acid, etc.) to form a barrier type anodized film. After the barrier type anodized film is removed by etching, the anodization is carried out with a predetermined voltage (the voltage at the second level described above), whereby recessed portions whose two-dimensional size is in the range of more than 20 nm and less than 100 nm can be formed.
For example, an aluminum film which contains Ti at 1 mass % is anodized at 100 V for 2 minutes using a tartaric acid aqueous solution (concentration: 0.1 mol/L, solution temperature: 23° C.), whereby a barrier type anodized film is formed. Thereafter, the etching is carried out for 25 minutes using a phosphoric acid aqueous solution (concentration: 10 mass %, solution temperature: 30° C.), whereby the barrier type anodized film is removed. Thereafter, the anodization and the etching are alternatively repeated as described above, specifically through 5 anodization cycles and 4 etching cycles. The anodization was carried out at 20 V for 52 seconds using an oxalic acid aqueous solution (concentration: 0.3 mass %, solution temperature: 10° C.) as the anodization solution. The etching was carried out for 5 minutes using the above-described etching solution. As a result, recessed portions whose two-dimensional size is about 50 nm can be uniformly formed.
Moth-eye molds which are capable of forming various moth-eye structures can be manufactured as described above.
Next, a method for producing a synthetic polymer film with the use of a moth-eye mold 100 is described with reference to
First, a moth-eye mold 100 in the shape of a hollow cylinder is provided. Note that the moth-eye mold 100 in the shape of a hollow cylinder is manufactured according to, for example, the manufacturing method described with reference to
As shown in
Thereafter, the moth-eye mold 100 is separated from the base film 42, whereby a synthetic polymer film 34 to which the inverted moth-eye structure of the moth-eye mold 100 is transferred is formed on the surface of the base film 42. The base film 42 which has the synthetic polymer film 34 formed on the surface is wound up by an unshown winding roller.
The surface of the synthetic polymer film 34 has the moth-eye structure obtained by inverting the surficial nanostructures of the moth-eye mold 100. According to the surficial nanostructure of the moth-eye mold 100 used, the synthetic polymer films 34A and 34B shown in
The microbicidal ability of a synthetic polymer film which has the moth-eye structure over its surface has not only a correlation with the physical structure of the synthetic polymer film but also a correlation with the chemical properties of the synthetic polymer film. For example, the present applicant found correlations with chemical properties, such as a correlation with the contact angle of the surface of the synthetic polymer film (WO 2015/163018), a correlation with the concentration of the nitrogen element contained in the surface (WO 2016/080245), and a correlation with the content of ethylene oxide units (—CH2CH2O—) in addition to the nitrogen element concentration (WO 2016/208540).
As seen from these SEM images, the tip end portions of the raised portions enter the cell wall (exine) of a P. aeruginosa bacterium. In
The present inventors further studied a synthetic polymer film which is suitably used for sterilization of a liquid including water and found that the synthetic polymer films disclosed in WO 2015/163018, WO 2016/080245 and WO 2016/208540 still have room for improvement in mass productivity (transferability). One of the possible reasons is that the synthetic polymer films disclosed in WO 2015/163018, WO 2016/080245 and WO 2016/208540 are formed using a photocurable resin which contains an acrylate which has a urethane bond. The acrylate which has a urethane bond has relatively high viscosity and is therefore likely to deteriorate the mold releasability. Thus, for example, such an acrylate causes deterioration of the productivity in mass production based on a roll-to-roll method.
From the viewpoint of mass productivity and water resistance, a synthetic polymer film which includes none of a nitrogen element and a fluorine element is preferred as disclosed in International Application No. PCT/JP2018/030788 of the present applicant. A compound including a quaternary ammonium salt, an amino group, or an amide group, which contains a nitrogen element, has high permeability to the mold releasing agent. Therefore, there is a concern that the compound may deteriorate the mold releasability. Thus, for example, it causes deterioration of the productivity in mass production based on a roll-to-roll method. Also, the compound which contains a nitrogen element has high polarity and therefore disadvantageously affects the water resistance. Note that, of the amino groups (amines), the tertiary amino group (tertiary amine) has lower polarity than the primary and secondary amino groups (amines) and therefore exerts a smaller adverse influence on the mass productivity (transferability) and/or water resistance. On the other hand, when an acrylate which contains a fluorine element is used, the acrylate advantageously affects the mold releasability but the synthetic polymer film has high water repellency so that water is unlikely to permeate the acrylate. As a result, there is a concern that the effect of sterilizing a liquid including water may decrease. The entire disclosure of International Application No. PCT/JP2018/030788 is incorporated by reference in this specification.
Since the nitrogen element has a characteristic which improves the microbicidal activity, there is a concern that a synthetic polymer film which does not contain the nitrogen element may have a decreased microbicidal activity. However, as disclosed in International Application No. PCT/JP2018/030788, a synthetic polymer film whose surface has a microbicidal activity and of which the crosslink structure contains none of a nitrogen element and a fluorine element can be obtained.
The present inventors formed synthetic polymer films using photocurable resins of different compositions and evaluated the synthetic polymer films as to the microbicidal ability. The present inventors found that, when a synthetic polymer film contains a certain type of organic carboxylic acid, the microbicidal ability achieved by the surface which has the moth-eye structure improves. The organic carboxylic acid only needs to be contained in the synthetic polymer film. The photocurable resin may generate an organic carboxylic acid by photodecomposition. A compound which generates an organic carboxylic acid by photodecomposition may be an initiator (photopolymerization initiator) or may be a compound which does not function as an initiator (herein referred to as “photoacid generator”). When a radically-polymerizable photocurable resin is used as the photocurable resin, a photoacid generator which generates an organic carboxylic acid without generating a radical may be used.
The organic carboxylic acid and/or the compound which generates an organic carboxylic acid by photodecomposition (initiator and/or photoacid generator) may be mixed in the photocurable resin composition such that the proportion of the organic carboxylic acid and/or the compound to the entirety of the photocurable resin composition is generally equal to or greater than 1 mass % and not more than 10 mass %. If the proportion is less than 1 mass %, the effect of improving the microbicidal ability cannot be achieved sometimes. If the proportion is more than about 10 mass %, there is a concern that the organic carboxylic acid may deteriorate the physical properties of the cured material (photocured resin composition). To suppress the influence on the physical properties of the cured material, it is preferred that the proportion is not more than about 5 mass %. Specifically, according to the type of the photocurable resin and the type of the organic carboxylic acid and/or the compound which generates an organic carboxylic acid by photodecomposition, the amount of the contained organic carboxylic acid and/or compound may be properly adjusted.
An organic carboxylic acid of a certain type has a microbicidal ability (or antimicrobial ability) and is used as, for example, food preservatives. It is supposed that the organic carboxylic acid exhibits the microbicidal ability (antimicrobial ability) through various mechanisms. The mechanisms include (1) decreasing the pH in the environment; and (2) allowing undissociated acid to pass through a cell membrane such that the pH inside the cell decreases. In mechanism (2), a weaker acid (an acid having a smaller dissociation constant) contributes more greatly. See, for example, Rosa M. Raybaudi-Massilia et al., “Control of Pathogenic and Spoilage Microorganisms in Fresh-cut Fruits and Fruit Juices by Traditional and Alternative Natural Antimicrobials”, COMPREHENSIVE REVIEWS IN FOOD SCIENCE AND FOOD SAFETY, Vol. 8, pp. 157-180, 2009 (particularly, p. 162).
As will be described later with experimental examples, it is supposed that the microbicidal ability of a synthetic polymer film of an embodiment of the present invention which contains an organic carboxylic acid is improved by the above-described mechanisms (1) and (2).
A synthetic polymer film of an embodiment of the present invention can be mass-produced according to a roll-to-roll method. Therefore, in consideration of the mass productivity, it is preferred to use a synthetic polymer film of which the crosslink structure does not contain any nitrogen element (that is a constituent of a urethane bond) as described above. However, the synthetic polymer film of an embodiment of the present invention is not limited to this example but can be produced by various methods, and therefore, the crosslink structure may contain a nitrogen element.
[Synthetic Polymer Film]
Sample films which had the same configuration as the film 50A shown in
Sample films of the synthetic polymer films of Reference Example which contained a nitrogen element as the synthetic polymer films disclosed in WO 2015/163018, WO 2016/080245 and WO 2016/208540, Examples 1 to 16 of an embodiment of the present invention, and Comparative Examples 1 to 6 were produced. The composition of Reference Example is shown in TABLE 2. The compositions of Examples 1 to 16 are shown in TABLE 3. The compositions of Comparative Examples 1 to 6 are shown in TABLE 4. In Example 15, the resin composition used was prepared by adding water to the same UV-curable resin composition as that used in Example 3. Since it is expected that water hardly remains in the synthetic polymer film, it is not included in the composition shown in TABLE 3. The amount of the added water was 5 g with respect to 100 g acrylic monomer (M280). Assuming that all the constituents of the composition including water constitute 100%, the composition was M280: 93.9%, 819: 1.4%, water: 4.7%.
As the base film 42A, a 50 μm thick PET film (A4300 manufactured by TOYOBO CO., LTD.) was used. The same synthetic polymer film production method as that previously described with reference to
In TABLE 1, the numbers in the column of “Water Solubility” for the organic acids represent the solubility index defined below.
The solubility of a solute in water at about 20° C. to about 25° C. are represented based on the amount of water required for dissolving 1 g or 1 mL of the solute using the solubility index (1 to 7) and the terms shown below.
1: Very soluble
2: Freely soluble
3: Soluble
4: Sparingly soluble
5: Slightly soluble
6: Very slightly soluble
7: Practically insoluble
Evaluation results of the respective sample films as to the microbicidal ability, the transferability and the film surface properties are shown in TABLE 5 to TABLE 7. TABLE 5 shows the results of Reference Example. TABLE 6 shows the results of Examples 1 to 16. TABLE 7 shows the results of Comparative Examples 1 to 6. The evaluated film surface properties were the spreadability of a water drop over the surface of the synthetic polymer film and the change of the pH of the water drop.
[Evaluation of Microbicidal Ability]
The sample films were evaluated as to the microbicidal ability for the bacterial solution (water) sprinkled over the sample films. The sample films to which the bacterial solution was applied and which were left in atmospheric air at room temperature were evaluated as to the microbicidal ability. Herein, the microbicidal ability for Staphylococcus aureus was evaluated. A specific evaluation method is described in the following paragraphs. For each sample film, an experiment was carried out with N=3.
Beforehand, each sample film was left for two weeks in an environment of 25° C. and RH 50% or in an environment of 60° C. and RH 90%. Thereafter, the surface of the sample film was wiped with a BEMCOT wiper (cupro continuous-filament nonwoven fabric manufactured by Asahi Kasei Corporation) impregnated with ethanol.
(1) A bacterial solution including Staphylococcus aureus was prepared using 1/500 NB culture medium such that the initial bacteria count was 1E+06 CFU/mL.
(2) On each sample film (a square of 5 cm on each side), 10 μL of the above-described bacterial solution was dropped.
(3) The sample films were left in atmospheric air at room temperature (about 25° C.) for 15 minutes and, thereafter, a SCDLP culture medium was flowed over the sample films to wash away the bacteria (post-wash solution).
(4) The post-wash solution was appropriately diluted with PBS and cultured in the standard agar medium, and the number of bacteria was counted.
The microbicidal ability was evaluated relative to the microbicidal ability of a reference film. The reference film used was a 50 μm thick PET film (A4300 manufactured by TOYOBO CO., LTD.) which was used as the base film. For the PET film, the number of bacteria was counted through the above-described procedure. Each of the sample films was evaluated as to the microbicidal ability in the proportion (%) of the number of bacteria on each sample film to the number of bacteria on the PET film. Specifically, the bacteria survival rate was calculated by the following formula:
Bacteria Survival Rate (%)=Number of bacteria on each sample film (aggregate of N=3)/Number of bacteria on PET film (aggregate of N=3)×100
The criteria for judgement as to the microbicidal ability were based on the bacteria survival rate for each of the condition of 25° C. and RH 50% and the condition of 60° C. and RH 90% such that •: 0%, ∘: more than 0% and less than 10%, A: not less than 10% and less than 50%, x: not less than 50%. Specifically, when the bacteria survival rate was less than 50%, the sample film was judged to be usable.
[Evaluation of Transferability]
For evaluation of the transferability, an aluminum film (thickness: about 1 μm) was formed on a glass substrate (about 5 cm×about 5 cm), and anodization and etching were performed alternately and repeatedly on the aluminum film, whereby a porous alumina layer (Dp was about 200 nm, Dint was about 200 nm, and Dh was about 150 nm) which is the same as that previously described was formed. The surface of the resultant porous alumina layer was subjected to oxygen plasma cleaning (100 W, 25 seconds) such that the contact angle with respect to water was adjusted to 125° to 130°. This is for the purpose of reducing the mold releasability of the mold surface with respect to the UV-curable resin.
A synthetic polymer film was formed ten times on a PET film using a UV-curable resin. Forming a synthetic polymer film on a PET film is represented as “transferring a synthetic polymer film on a PET film”. In the ultraviolet light irradiation, a UV lamp manufactured by Fusion UV Systems (product name: LIGHT HANMAR6J6P3) was used. The exposure amount was about 200 mJ/cm2 (on the basis of light at the wavelength of 375 nm). The transfer was manually carried out ten times. The lightness in transfer (the magnitude of the force required to pull off the mold from the synthetic polymer film) and the state of the surface of the mold in transfer were considered as indices.
•: The mold was lightly removed from the first transfer to the tenth transfer.
∘: The mold was lightly removed in the early transfers, but subsequently the removal gradually became heavier.
Δ: Removal of the mold was already heavy in the early transfers but a failure, such as remaining of the synthetic polymer film (UV-curable resin) on the mold surface, did not occur.
x: In the ten transfers, a failure occurred, such as remaining of the synthetic polymer film on the mold surface.
When •, ∘ or Δ, the synthetic polymer film was judged to be usable.
[Evaluation of Film Surface Properties: Degree of Spread of Water Over Synthetic Polymer Film and pH Measurement]
Deionized water was adjusted to pH=7.0±0.1 using 0.01 mol/L hydrochloric acid solution and 0.011 mol/L sodium hydroxide solution. That is, neutral water was prepared in this way.
On the surface of each sample film, a 0.2 cc (200 μL) drop of the above-described pH-adjusted water was placed using a micropipette. Thereafter, the maximum spread diameter (area equivalent circle diameter) up to 5 min was measured, and the average value for five measurements from each sample film was evaluated.
The measurement of the pH was carried out as follows.
In the same way as that described above, on the surface of each sample film, a 0.2 cc (200 μL) drop of the above-described pH-adjusted water was placed using a micropipette. After the passage of 5 minutes, the aqueous solution (water in which an extract from the synthetic polymer film was dissolved) on the surface of each sample film was measured using an electrode for flat samples which is described below, and the average value for five measurements from each sample film was evaluated.
Note that a sample film over which the spread of the water was less than 20 mm was evaluated using a sampling sheet otherwise the diameter of the water drop increased in the pH measurement.
Electrode: pH electrode, product number: 0040-10D (semiconductor sensor) manufactured by HORIBA, Ltd.
Sampling sheet: sampling sheet B, product number: Y011A manufactured by HORIBA, Ltd.
[Identification of Acid]
An acid extracted from each sample film to water was identified as described below using GC-MS (gas chromatograph mass spectrometer).
10 mL THF per 100 cm2 of each sample film was put into a glass container. The sample film was immersed in THF at 50° C. for 3 days. Then, THF was passed through a 0.45 μm membrane filter.
0.1 mL of the filtered solution was condensed in a pyrolysis sample cup. The condensed solution was methylated by adding a 10 μL methylating agent (Tetramethylammonium Hydroxide) aqueous solution. Thereafter, the measurement was carried out under the following conditions.
Pyrolyzer: EGA/PY-3030D manufactured by FRONTIER LAB
Conditions: 400° C./30 sec
GC-MS apparatus: 7890A(GC) 5975C(MS) manufactured by Agilent Technologies
Column: UA5HT-30M-0.1F manufactured by FRONTIER LAB
Conditions: Oven 40° C.->320° C. (20° C./min)
Column flow rate: 1 mL/min
Split ratio: 100:1
The sample film of Reference Example shown in TABLE 5 has poor transferability because the synthetic polymer film has a urethane bond. Therefore, the sample film of Reference Example is poor in mass productivity although the microbicidal ability is excellent.
Each of the sample films of Examples and Comparative Examples is excellent in transferability because the synthetic polymer film does not have a urethane bond.
The synthetic polymer films of Examples 1 to 16 were formed using a UV-curable resin composition which contained an acrylic monomer (M280) having an ethylene oxide unit (EO unit). Therefore, the synthetic polymer films of Examples 1 to 16 have appropriate hydrophilicity, and the surface that has the moth-eye structure is a superhydrophilic surface. The synthetic polymer films of Examples 10 to 13 contain ACMO (monofunctional acrylic monomer). This is for the purpose of making the acrylic monomer constituent comparable with the synthetic polymer film of Comparative Example 2 in which ACMO was added for dissolving the dodecanedioic acid. Although ACMO contains a nitrogen element, the nitrogen element is a constituent of a tertiary amine, and its polarity is not strong as compared with primary and secondary amines.
The synthetic polymer film of Comparative Example 6 does not contain an ethylene oxide unit and is therefore poor in hydrophilicity. This can be seen from TABLE 7 showing that the degree of spread of water (area equivalent circle diameter) is small, specifically not more than 20 mm.
Also in Comparative Example 5, the degree of spread of water is small. Comparative Example 5 is different from Example 16 only in the type of the mold releasing agent, and the composition of the other constituents is the same as that of Example 16. It can be seen from this that, when a fluorine-containing mold releasing agent is used, the microbicidal ability deteriorates although the transferability improves. Also, it can be seen that the degree of spread of water is a significant factor in the microbicidal ability. Among the samples which were judged to have a microbicidal ability, the degree of spread of water was the smallest in Reference Example (28.5 mm). It is supposed that the degree of spread of water is preferably at least not less than 20 mm, more preferably not less than 30 mm. On the other hand, in Example 16 in which the silicone-based surfactant was used, the transferability improved while the degree of spread of water increased, and the microbicidal ability was excellent. The mold releasing agent is preferably an agent which is locally present on the surface so that the degree of spread of water can increase and the transferability can improve, such as a silicone-based surfactant.
It can be seen from the comparison between Examples and Comparative Examples that the microbicidal ability has not only a correlation with the degree of spread of water but also a correlation with the pH of the aqueous solution.
First, compare Example 1 with Comparative Example 1. The difference between Example 1 and Comparative Example 1 is only the type of the polymerization initiator. Polymerization initiator 819 used in Example 1 generates 2,4,6-trimethylbenzoic acid (TMBA) by photodecomposition. This was verified by GC-MAS. On the other hand, polymerization initiator OXE02 used in Comparative Example 1 does not generate an acid by photodecomposition. As a result, Comparative Example 1 does not have a microbicidal ability because the pH is 7.2, although the degree of spread of water is 30 mm, which is comparable to the degree of spread of water of Example 1 (31.5 mm).
Polymerization initiator 819 used in Examples 1 to 4 generates TMBA by photodecomposition. Polymerization initiator TPO used in Examples 5 and 6 generates TMBA and diphenyl phosphoric acid (DPPA). Polymerization initiator OXE01 used in Examples 7 and 8 generates benzoic acid (BA). Therefore, the pH of the aqueous solution of the synthetic polymer films of Examples 1 to 8 is not more than 5, and the degree of spread of water is not less than 30 mm, so that the synthetic polymer films of Examples 1 to 8 have an excellent microbicidal ability. Polymerization initiator 819 used in Examples 1 to 4 can generate two TMBA molecules at the maximum per one molecule of the polymerization initiator and is therefore preferred. As seen from the results of Examples 1 to 4, it is preferred that the proportion of the contained polymerization initiator 819 to the entirety of the photocurable resin composition is not less than 2 mass %.
In Examples 9 to 14, polymerization initiator OXE02 which does not generate an acid was used, and in addition, an organic carboxylic acid was added. Each of Examples 9 to 14 has an excellent microbicidal ability. As for the solubility of the organic carboxylic acid in water, in each of Examples 9 to 14, the amount of water required for dissolving 1 g of the organic carboxylic acid is not less than 10 mL and less than 10000 mL (solubility index: 3 to 6). The amount of water is preferably not less than 100 mL, more preferably not less than 200 mL, and is preferably less than 2000 mL. If the solubility of the organic carboxylic acid in water is excessively high, the microbicidal effect in a high-temperature, high-humidity environment decreases earlier.
Example 14 is equal to the composition of Example 9 except the addition of phenyl phosphoric acid (PPA) and has a better microbicidal ability than Example 9. This is probably because the addition of PPA, which is a stronger acid than TMBA, suppressed dissociation of TMBA and, as a result, TMBA was taken into a cell so that a microbicidal activity was exhibited.
As seen from the foregoing, the fast spreading of water dropped onto the surface of the synthetic polymer film advantageously affects the microbicidal ability. In this process, due to an acid extracted into water, the pH of the aqueous solution (water drop) decreases (becomes acidified) within a relatively short time period. A microbicidal activity which is attributed to this decrease of the pH effectively works. At the lapse of 5 minutes, the pH is preferably not more than 5. If the pH is not more than 5, a microbicidal activity which is attributed to taking of an undissociated organic carboxylic acid into a cell effectively works. If an acid stronger than the organic carboxylic acid, such as phosphoric acid or sulfonic acid, is contained, dissociation of the organic carboxylic acid is further suppressed. Thus, such an acid is preferred to be contained.
The solubility of dodecanedioic acid of Comparative Example 2 in water is very low (solubility index 7). Therefore, Comparative Example 2 does not exhibit a microbicidal effect which is attributed to the organic carboxylic acid. On the other hand, the acetic acid of Comparative Example 3 and the phenyl phosphoric acid of Comparative Example 4 have extremely high solubility in water (solubility index 1). Therefore, Comparative Example 3 and Comparative Example 4 have a low microbicidal ability and, particularly, have a low microbicidal ability in a high-temperature, high-humidity environment.
Examples of the organic carboxylic acid suitably used in the synthetic polymer film of an embodiment of the present invention are as follows:
fatty acids, such as pentanoic acid, hexanoic acid, heptanoic acid, octanoic acid;
aromatic carboxylic acids, such as benzoic acid, 2,4,6-trimethylbenzoic acid, salicylic acid; and
diprotic acids, such as succinic acid, fumaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, o-phthalic acid.
From the viewpoint of solubility and safety, suberic acid, sebacic acid and 2,4,6-trimethylbenzoic acid are preferably used. The amount of water required for dissolving 1 g of these organic carboxylic acids is not less than 200 mL and less than 2000 mL.
The organic carboxylic acid only needs to be contained in the synthetic polymer film. The photocurable resin may generate an organic carboxylic acid by photodecomposition. The compound which generates an organic carboxylic acid by photodecomposition may be an initiator or may be a photoacid generator which does not function as the initiator as described above. When a radically-polymerizable photocurable resin is used as the photocurable resin, a photoacid generator which generates an organic carboxylic acid without generating a radical can be used. The compound which generates an organic carboxylic acid by photodecomposition is, advantageously, unlikely to deteriorate the transferability. Also, advantageously, the compound can simultaneously generate the organic carboxylic acid and another water-soluble organic acid (an acid stronger than carboxylic acid).
The photoacid generator which generates an organic carboxylic acid may be selected from known photoacid generators. Examples of the photoacid generator include naphthalene diazides such as 6-diazo-5,6-dihydro-5-oxo-1-naphthalene sulfonic acid, benzophenones such as 2,3,4-trihydroxybenzophenone, and polyphenols such as 4-{4-[1,1-bis(4-hydroxyphenyl)ethyl]-α,α-dimethyl benzyl} phenol.
As described above, the resin composition used in Example 15 was equal to the UV-curable resin composition of Example 3 except the addition of water. As seen from the results of TABLE 6, Example 15 has a better microbicidal ability than Example 3. By adding water to the UV-curable resin composition used in Example 3, the organic carboxylic acid was more readily extracted so that the pH decreased, and the hydrophilicity of the surface increased so that the degree of spread of water increased.
When water is added to and mixed in the UV-curable resin composition, the stability decreases. Therefore, the addition of water is preferably carried out immediately before the light irradiation step in the above-described manufacturing method. The amount of water is preferably not less than 1 mass % and not more than 10 mass % with respect to the entirety of the photocurable resin composition. If the amount of water is less than 1 mass %, the effect of the addition cannot be achieved sometimes. If the amount of water is more than 10 mass %, a homogeneous composition cannot be obtained sometimes.
The sample films of Examples 17 to 19 were produced with different types of polymerization initiators contained in the UV-curable resin. The compositions of Examples 17 to 19 are shown in TABLE 8. The sample films of Examples 17 to 19 were produced by the same method as that previously described for Examples 1 to 16 and evaluated as to the microbicidal ability, the transferability and the film surface properties by the same method as that previously described for Examples 1 to 16. The evaluation results of the sample films of Examples 17 to 19 as to the microbicidal ability, the transferability and the film surface properties are shown in TABLE 9.
Examples 17 to 19 are different from one another only in the type of the polymerization initiator. In Example 17, 819 was used as the polymerization initiator. In Example 18, TPO was used as the polymerization initiator. In Example 19, 819 and TPO were used as the polymerization initiator. In each of Examples 17 to 19, the proportion of the contained polymerization initiator to the entirety of the photocurable resin composition was 2 mass %.
In each of the synthetic polymer films of Examples 17 to 19, the pH of the aqueous solution at the lapse of 5 minutes was not more than 5 and the degree of spread of water was not less than 20 mm. Thus, the synthetic polymer films of Examples 17 to 19 have an excellent microbicidal ability. None of the synthetic polymer films of Examples 17 to 19 has a urethane bond. Thus, the synthetic polymer films of Examples 17 to 19 are excellent in transferability. As seen from the results of TABLE 9, Example 19 has a better microbicidal ability than Example 17. It is estimated that since Example 19 further contained DPPA which is an stronger acid than TMBA in addition to TMBA, dissociation of TMBA was suppressed, and Example 19 exhibited an excellent microbicidal ability. Although Example 18 also contains TMBA and DPPA, Example 19 has a better microbicidal ability than Example 18. Polymerization initiator TPO can generate one TMBA molecule at the maximum per one molecule of the polymerization initiator, while polymerization initiator 819 can generate two TMBA molecules at the maximum per one molecule of the polymerization initiator. Therefore, it is estimated that Example 19 which contains both polymerization initiators 819 and TPO has an excellent microbicidal ability. For example, it is preferred that the proportion of the contained polymerization initiator 819 to the entirety of the photocurable resin composition is not less than 1 mass % and the proportion of the contained polymerization initiator TPO to the entirety of the photocurable resin composition is not less than 1 mass %.
In the foregoing, a synthetic polymer film which has a moth-eye structure over the surface has been described, although an embodiment of the present invention is not limited to this example. A synthetic polymer film of an embodiment of the present invention may have a plurality of raised portions over the surface, and the two-dimensional size of the plurality of raised portions may be not less than 500 nm when viewed in the normal direction of the synthetic polymer film. The synthetic polymer film having such a structure can also achieve the same effects as those achieved by the synthetic polymer film which has the moth-eye structure over the surface. The surface structure is not limited to the raised portions but may be recessed portions. A synthetic polymer film of an embodiment of the present invention may have a plurality of raised or recessed portions over the surface, and the two-dimensional size of the plurality of raised or recessed portions may be not less than 500 nm when viewed in the normal direction of the synthetic polymer film.
The sample films of Examples 20 and 21 were produced using UV-curable resins whose compositions are shown in TABLE 10. The compositions of Examples 20 and 21 are shown in TABLE 10. The sample films of Examples 20 and 21 are different from the film 50A shown in
As disclosed in WO 2016/084745 of the present applicant, by adjusting the composition and/or the film formation conditions (e.g., the thickness of the aluminum alloy layer) of the aluminum alloy layer which contains Al and Ti, the crystal grain diameter of a plurality of crystal grains which are present at the surface of the aluminum alloy layer can be adjusted. Also, as disclosed in WO 2011/052652 of the present applicant, by adjusting the film formation conditions of an aluminum film which is to be formed on a substrate (e.g., glass substrate), the crystal grain diameter of a plurality of crystal grains which are present at the surface of the aluminum film can be adjusted. When a porous alumina layer obtained by alternately performing anodization and etching on the thus-obtained aluminum alloy layer or aluminum film is used as the mold, an antireflection film which can perform an antiglare function can be formed. Note that, however, the mold samples for formation of the sample films of Examples 20 and 21 were obtained without performing anodization or etching on a high-purity aluminum layer. The entire disclosures of WO 2016/084745 and WO 2011/052652 are incorporated by reference in this specification.
As shown in
The sample films of Examples 20 and 21 each has a shape obtained by inverting the surface shape of the mold sample. The “two-dimensional size” of Examples 20 and 21 shown in TABLE 11 refers to the two-dimensional size of a plurality of raised portions at the surface of the mold samples of Examples 20 and 21.
The sample films of Examples 20 and 21 were evaluated as to the microbicidal ability, the transferability and the film surface properties by the same method as that previously described for Examples 1 to 16. The evaluation results of the sample films of Examples 20 and 21 as to the microbicidal ability, the transferability and the film surface properties are shown in TABLE 11.
In each of the synthetic polymer films of Examples 20 and 21, the pH of the aqueous solution at the lapse of 5 minutes was not more than 5 and the degree of spread of water was not less than 20 mm. Thus, the synthetic polymer films of Examples 20 and 21 have an excellent microbicidal ability. None of the synthetic polymer films of Examples 20 and 21 has a urethane bond. Thus, the synthetic polymer films of Examples 20 and 21 are excellent in transferability.
As seen from the results of Examples 20 and 21, a synthetic polymer film of an embodiment of the present invention has an excellent microbicidal ability so long as a plurality of recessed portions at the surface of the synthetic polymer film are in the range of, for example, not less than 500 nm and not more than 1 μm. That is, it is estimated that so long as the pH of the aqueous solution at the lapse of 5 minutes is not more than 5 and the degree of spread of water is not less than 20 mm, the synthetic polymer film has an excellent microbicidal ability irrespective of whether the structure at the surface of the synthetic polymer film is a plurality of raised portions or a plurality of recessed portions. In this case, it is estimated that the two-dimensional size of the plurality of raised portions or the plurality of recessed portions only needs to be in the range of more than 20 nm and not more than 1 μm.
The mold samples of Examples 20 and 21 can be obtained only by forming crystal grains of a desired shape (e.g., the average grain diameter is not less than 500 nm and not more than 1 μm). That is, it is not necessary to perform anodization as in formation of the moth-eye mold. Thus, the mold samples of Examples 20 and 21 can be manufactured at a low cost. Also, advantageously, the mold samples of Examples 20 and 21 are excellent in transferability.
Herein, the UV-curable resin has been described, although a resin which can be cured with visible light can be used. Note that, however, the UV-curable resin is preferred because it can be stored and handled easily.
A synthetic polymer film of an embodiment of the present invention is capable of sterilizing water adhered to the surface of the film within a short time period. Therefore, by placing the synthetic polymer film on the inner surface of a space of a hand dryer into which a hand is to be inserted, infection can be suppressed and prevented.
A synthetic polymer film according to an embodiment of the present invention is suitably applicable to uses which require sterilization of water within a short time period.
While the present invention has been described with respect to exemplary embodiments thereof, it will be apparent to those skilled in the art that the disclosed invention may be modified in numerous ways and may assume many embodiments other than those specifically described above. Accordingly, it is intended by the appended claims to cover all modifications of the invention that fall within the true spirit and scope of the invention.
This application is based on Japanese Patent Applications No. 2017-185204 filed on Sep. 26, 2017 and No. 2017-226887 filed on Nov. 27, 2017, the entire contents of which are hereby incorporated by reference.
| Number | Date | Country | Kind |
|---|---|---|---|
| JP2017-185204 | Sep 2017 | JP | national |
| JP2017-226887 | Nov 2017 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 9781924 | Yamada et al. | Oct 2017 | B2 |
| 9781925 | Yamada et al. | Oct 2017 | B2 |
| 9781926 | Yamada et al. | Oct 2017 | B2 |
| 10136638 | Yamada et al. | Nov 2018 | B2 |
| 20030164326 | Eberl et al. | Sep 2003 | A1 |
| 20030205475 | Sawitowski | Nov 2003 | A1 |
| 20050163854 | Hartman | Jul 2005 | A1 |
| 20070159698 | Taguchi et al. | Jul 2007 | A1 |
| 20080145390 | Taylor | Jun 2008 | A1 |
| 20090252825 | Taguchi et al. | Oct 2009 | A1 |
| 20100009137 | Kodama | Jan 2010 | A1 |
| 20100203161 | Gehri et al. | Aug 2010 | A1 |
| 20100234323 | Holzl et al. | Sep 2010 | A1 |
| 20100263793 | Ylitalo | Oct 2010 | A1 |
| 20110038910 | Faucher et al. | Feb 2011 | A1 |
| 20110235181 | Hayashibe et al. | Sep 2011 | A1 |
| 20110281068 | David et al. | Nov 2011 | A1 |
| 20120218639 | Minoura | Aug 2012 | A1 |
| 20120318772 | Minoura et al. | Dec 2012 | A1 |
| 20130057958 | Minoura et al. | Mar 2013 | A1 |
| 20130260096 | Shiki | Oct 2013 | A1 |
| 20130344290 | Yu et al. | Dec 2013 | A1 |
| 20140004304 | Yu et al. | Jan 2014 | A1 |
| 20140077418 | Otani et al. | Mar 2014 | A1 |
| 20150009571 | Chin | Jan 2015 | A1 |
| 20150140154 | Isurugi | May 2015 | A1 |
| 20150168610 | Fukui | Jun 2015 | A1 |
| 20150273755 | Yee et al. | Oct 2015 | A1 |
| 20160113274 | Yamada et al. | Apr 2016 | A1 |
| 20160194778 | Shakagoori | Jul 2016 | A1 |
| 20160212989 | Juodkazis et al. | Jul 2016 | A1 |
| 20170258081 | Yamada et al. | Sep 2017 | A1 |
| 20170285468 | Kitagawa | Oct 2017 | A1 |
| 20180036995 | Okazaki et al. | Feb 2018 | A1 |
| 20180134859 | Yamada et al. | May 2018 | A1 |
| 20180163056 | Okazaki | Jun 2018 | A1 |
| 20190161636 | Gokhale | May 2019 | A1 |
| Number | Date | Country |
|---|---|---|
| 2323719 | Apr 2001 | CA |
| 201329050 | Oct 2009 | CN |
| 19950452 | Apr 2001 | DE |
| H08-024843 | Jan 1996 | JP |
| H08-300549 | Nov 1996 | JP |
| H11-010724 | Jan 1999 | JP |
| 2001-219464 | Aug 2001 | JP |
| 2001-310412 | Nov 2001 | JP |
| 2002-012257 | Jan 2002 | JP |
| 2005-055114 | Mar 2005 | JP |
| 2008-197217 | Aug 2008 | JP |
| 4265729 | Feb 2009 | JP |
| 2009-166502 | Jul 2009 | JP |
| 2010-000719 | Jan 2010 | JP |
| 2010-079200 | Apr 2010 | JP |
| 2012-078438 | Apr 2012 | JP |
| 2012-514239 | Jun 2012 | JP |
| 2012-208169 | Oct 2012 | JP |
| 2013-033287 | Feb 2013 | JP |
| 2013-078573 | May 2013 | JP |
| 2013-208817 | Oct 2013 | JP |
| 2014-005341 | Jan 2014 | JP |
| 2014-029391 | Feb 2014 | JP |
| 2014-066975 | Apr 2014 | JP |
| 2014-509967 | Apr 2014 | JP |
| 2014-511779 | May 2014 | JP |
| 2014-202955 | Oct 2014 | JP |
| 2015-024549 | Feb 2015 | JP |
| 2015-152659 | Aug 2015 | JP |
| 5788128 | Sep 2015 | JP |
| 2016-026546 | Feb 2016 | JP |
| 2016-093939 | May 2016 | JP |
| 2016-104545 | Jun 2016 | JP |
| 2016-210164 | Dec 2016 | JP |
| 2017-048132 | Mar 2017 | JP |
| 2007097454 | Aug 2007 | WO |
| 2011019834 | Feb 2011 | WO |
| 2011052652 | May 2011 | WO |
| 2011125486 | Oct 2011 | WO |
| 2011148721 | Dec 2011 | WO |
| 2012161315 | Nov 2012 | WO |
| 2013183576 | Dec 2013 | WO |
| 2013191092 | Dec 2013 | WO |
| 2014021376 | Feb 2014 | WO |
| 2014171365 | Oct 2014 | WO |
| 2015031956 | Mar 2015 | WO |
| 2015163018 | Oct 2015 | WO |
| 20161080245 | May 2016 | WO |
| 2016084745 | Jun 2016 | WO |
| 2016143778 | Sep 2016 | WO |
| 2016175170 | Nov 2016 | WO |
| 2016182444 | Nov 2016 | WO |
| 2016208540 | Dec 2016 | WO |
| 2017090661 | Jun 2017 | WO |
| 2017168893 | Oct 2017 | WO |
| 2018154843 | Aug 2018 | WO |
| Entry |
|---|
| Machine translation of JP 2016/104545 A, obtained from the JPO (Year: 2019). |
| Co-pending letter regarding related co-pending U.S. Appl. No. 14/771,833, filed Sep 1, 2015 et al. |
| Non-Final Rejection dated Nov. 24, 2017 for U.S. Appl. No. 14/897,252. |
| Non-Final Rejection dated Dec. 11, 2017 for U.S. Appl. No. 15/592,922. |
| Non-Final Office Action dated Jan. 24, 2018 for U.S. Appl. No. 15/126,078. |
| Espeel Pieter, et al. “One-pot, additive-free preparation of functionalized polyurethanes via amine—thiol—ene conjugation”, Polymer Chemistry, 2013, 4(8):2449-2456. |
| Pogodin Sergey, et al. “Biophysical model of bacterial cell interactions with nanopatterned cicada wing surfaces”, Biophysical Journal, 2013, 104(4):835-840. |
| Compound Summary for CID 3086063, Tecoflex from PubChem, accessed Jan. 17, 2018. |
| Final Office Action dated Apr. 13, 2018 for U.S. Appl. No. 14/897,252. |
| Final Office Action dated Jun. 14, 2018 for U.S. Appl. No. 15/592,922. |
| Non-Final Office Action dated Jul. 13, 2018 for U.S. Appl. No. 15/784,771. |
| Elena P. Ivanova, et al, “Bactericidal activity of black silicon”, Nature Communications, Jun. 7, 2013, Article No. 2838 (2013), DOI: 10.1038/ncomms3838. |
| Alexander K. Epstein, et al, “Liquid-infused structured surfaces with exceptional anti-biofouling performance”, Proc Natl Acad Sci U S A. Aug. 14, 2012; 109(33): 13182-13187. doi: 10.1073/pnas.1201973109. |
| Elena P. Ivanova, et al, Natural Bactericidal Surfaces: Mechanical Rupture of Pseudomonas aeruginosa Cells by cicada Wings,Small. Aug. 20, 2012;8(16):2489-94. doi: 10.1002/smll.201200528. |
| Hang Yao, Thomas J. Webster, Matthew Hedrick,“Decreased bacteria density on nanostructured polyurethane”, J Biomed Mater Res Part A 2014:102A:1823-1828. |
| Cleaning Guide—How to Clean Surface,http://www.goodhousekeeping.com/home/cleaning/tips/a18875/how-to-clean, Sep 7, 2011. |
| MIT's anti-microbial ‘paint ’kills flu,bacteria,Anne Trafton, Nov. 30, 2006,http://chemistry.mit.edu/mits-anti-microbial-paint-kills-flu-bacteria. |
| Rosa M. Raybaudi-Massilia et al. “Control of Pathogenic and Spoilage Microorganisms in Fresh-cut Fruits and Fruit Juices by Traditional and Alternative Natural Antimicrobials”, Comprehensive Reviews in Food Science and Food Safety, 2009, 8:157-180. |
| Jafar Hasan et al., “Antibacterial surfaces: the quest for a new generation of biomaterials”, Trends in Biotechnology, vol. 31, Issue 5, May 2013, pp. 295-304. |
| Alexander K. Epstein et al., “Liquid-infused structured surfaces with exceptional anti-biofouling performance”, PNAS, vol. 109, No. 33, Aug. 14, 2012, pp. 13182-13187. |
| Number | Date | Country | |
|---|---|---|---|
| 20190092883 A1 | Mar 2019 | US |