1. Field of the Invention
The present invention relates to a synthetic quartz glass member including, for example, lenses and prisms for the ultraviolet laser to be used, for example, for the excimer laser lithography, and reticle (photomask) substrates as master plates for circuit patterns of integrated circuits, and a method for producing the same.
1. Description of the Related Art
A reduction projection exposure apparatus (or photolithography apparatus) is principally used to transfer integrated circuit patterns such as IC and LSI. As for the projection optical system to be incorporated into the apparatus, it is required that a wide exposure area is secured as the integrated circuit is highly integrated progressively, and it is required that a higher resolution or resolving power is provided over the entire exposure area. In order to improve the resolving power of the projection optical system, it is conceived that the exposure wavelength is further shortened, or the numerical aperture (NA) of the projection optical system is increased.
As for the exposure wavelength, the realization of short wavelength is advanced from the KrF (248 nm) excimer laser which is principally used as the light source for the semiconductor exposure apparatus at present to the ArF (193 nm) excimer laser which is the vacuum ultraviolet light source. At present, the F2 (157 nm) laser is also investigated in order to further advance the realization of high integration.
In relation to the conventional quartz glass member for the KrF excimer laser, the following fact has been reported. That is, any defective structure of the reduced type (or the oxygen-deficient type) represented by the Si-Si bond is mixed during the production step stage, and such a structure behaves as a precursor to cause the deterioration of optical characteristics upon the irradiation with the laser. For example, the Si—Si bond is subjected to the photodegradation or photodecomposition to produce the E′ center (Si•(“•” means the lone electron)). The E′ center forms an optical absorption band at 215 nm in the vicinity of the laser wavelength. Therefore, the light-transmissive characteristics of the quartz glass member are conspicuously deteriorated. Other than the above, for example, impurities of SiOH and SiCl as well as metal ions also behave as important factors to conspicuously deteriorate the light-transmissive characteristics of the quartz glass member.
On the other hand, in the case of the ArF excimer laser and the F2 laser, the energy possessed by one photon is high as compared with the KrF excimer laser. Therefore, in this case, the damage exerted on the quartz glass is large, and the deterioration of optical characteristics, which is caused in a process different from that of the KrF excimer laser, is conspicuous. For example, the Si—H bond is subjected to the photodecomposition to form the E′ center, and/or the strained Si—O—Si bond is subjected to the photodecomposition to generate NBOHC (Si—O•). The E′ center forms a light absorption band at 215 nm, and NBOHC forms a light absorption band at 260 nm. Therefore, any quartz glass member to be used for the exposure apparatus, in which the defect as described above is generated, undergoes conspicuous deterioration of the light-transmissive performance in a region from the ultraviolet to the vacuum ultraviolet.
It is considered that the strained Si—O—Si bond has a bond angle which is largely deviated from the ordinary Si—O—Si bond angle (≈145°±10°) distribution. It is postulated that the strained Si—O—Si bond has an optical absorption band at a lower portion in the vicinity of the essential band end of the quartz glass. According to a certain theory, the bond energy of this case is small as compared with those obtained in ordinary cases, and the strained Si—O—Si bond is a chemically unstable bond. The F2 laser beam, which is planned to be applied to the exposure light source in recent years, has a wavelength of 157 nm which is extremely short. Unlike the conventional excimer laser, the F2 laser beam makes it possible to directly excite the essential band end of the quartz glass in accordance with one photon process. Therefore, when the F2 laser is used as a radiation light source, it is postulated that the strained Si—O—Si bond is drastically reacted. This fact has been reported by the inventors in OPTICS LETTERS Vol. 24, No. 13, Jul. 1, 1999 pp. 863-865. In this paper, the inventors have observed the change of the infrared absorption spectrum of SiOH and the change of the Raman spectrum of H2 by radiating the F2 excimer laser having the wavelength of 157 nm at a predetermined intensity for a predetermined period of time onto commercially available quartz glass dissolved with H2. In this paper, it is reported that the infrared absorption spectrum band of SiOH is subjected to the red shift, and the integrated intensity is increased by 73% when the F2 excimer laser is radiated. As for the Raman spectrum of H2, it is reported that the intensity of the band based on H2 in the vicinity of 4133 cm−1 is lowered to ¼. It is considered that this result is based on the excitation of the Si—O—Si bond by being irradiated with the F2 excimer laser as indicated by the following formula (1). In particular, it has been suggested in this paper by the inventors that this reaction tends to occur in relation to the strained Si—O—Si bond.
Si—O—Si+H2→Si—O—H+H—Si (1)
In relation to the synthetic quartz glass member to be used for the projection exposure apparatus, a technique has been disclosed (for example, Japanese Patent Application Laid-open No. 7-291644 (Japanese Patent No. 3158854) and Japanese Patent Application Laid-open No. 10-53432), which prescribes, for example, the E′ center concentration generated in the quartz glass and the impurity concentration in the quartz glass. For example, in Japanese Patent Application Laid-open No. 7-291644, when the amount of change of the absorption coefficient at 215 nm corresponding to the number of radiation pulses upon the laser radiation is constant irrelevant to the repeating frequency of the laser, it is judged that a quartz glass member is obtained, which has the laser resistance wherein the E′ center is hardly generated and which is to be employed for an optical system for the high output pulse laser that is usable in a specified wavelength region of not more than 400 nm. In Japanese Patent Application Laid-open No. 10-53432, the concentration of Na contained in the quartz glass is not more than 20 wt. ppm to enhance the transmittance in the vacuum ultraviolet region in which the wavelength is not more than 220 nm.
However, in the patent documents as described above, the nonessential defect such as the reduced type defect or SiOH and/or the impurity concentration is merely prescribed. Any synthetic quartz glass member, which has the laser resistance, is not produced by taking the notice of the amount of the strain bond which essentially exists in the glass structure. When the radiation of the ArF excimer laser or the radiation of the F2 laser is performed for an extremely long period of time, then the presence of the strain bond as described above is not negligible, and there is a possibility to arrive at the deterioration of the transmissive performance of the glass. In OPTICS LETTERS Vol. 24, No. 13 reported by the inventors, the change of the strain bond amount is suggested from the spectrum change of H2 and SiOH. However, in this case, any physical characteristic change of the quartz glass itself, which is more directly concerned, is not observed.
Therefore, it is demanded to provide a correct, direct, and convenient method for judging the quartz glass which has high resistance to the vacuum ultraviolet laser beam such as ArF (193 nm) and F2 (157 nm).
A first object of the present invention is to provide a synthetic quartz glass member having excellent laser resistance to be used for a vacuum ultraviolet exposure apparatus, and a method for producing the same. A second object of the present invention is to provide a synthetic quartz glass member which scarcely involves strain bond to be used for reticle (photomask) substrates and lens members for focusing optical systems for a vacuum ultraviolet exposure apparatus. A third object of the present invention is to provide an exposure apparatus provided with an illumination optical system or a projection optical system having an optical member which makes it possible to maintain a satisfactory transmittance over a long period of time even when a high energy vacuum ultraviolet light source such as ArF laser is used.
According to a first aspect of the present invention, there is provided a synthetic quartz glass member for being irradiated with a vacuum ultraviolet light beam, wherein OH groups, which are contained in the synthetic quartz glass member, are increased by less than 100 wt. ppm, and a compaction is not more than 2 ppm, when the synthetic quartz glass member is subjected to 2×106 pulses of an F2 laser beam with a fluence of 10 mJ/cm2.
The inventors have radiated the F2 laser, which is considered to photodecompose the strain bond in one photon absorption process, onto the synthetic quartz glass member in order to estimate, in a relatively short period of time, the amount of the strained Si—O—Si bond existing in the quartz glass (hereinafter appropriately referred to as “strain bond” as well). The first requirement, in which the OH groups are increased by less than 100 wt. ppm when the F2 laser beam is radiated under the condition as described above, is derived from the fact that the strain bond is reacted in accordance with the following formula (2).
Si—O—Si (strain bond)+H2→Si—O—H+H—Si (2)
That is, when the strain bond exists in the quartz glass, the reaction is caused with the hydrogen (H2) existing in the quartz glass in the presence of the F2 laser beam to produce Si—O—H. According to this reaction, when the increase in the OH group is small, i.e., less than 100 wt. ppm even when the F2 laser beam is radiated, the amount of the strain bond is originally small in the quartz glass. In the case of such a material, the amount of Si—O—H formed after the radiation of the F2 laser beam is small. Therefore, the decrease in transmittance in the vacuum ultraviolet region, which is considered to be caused by the reaction of the strain bond, is avoided. Therefore, the satisfactory quartz glass is selected by measuring the increase in the OH group by radiating the F2 laser beam. Such quartz glass is used to produce the quartz glass member for the vacuum ultraviolet, including, for example, lenses and reticles.
Further, the inventors have found out the fact that when the first requirement is satisfied, the second requirement is almost satisfied, in which the compaction is within the predetermined range even when the F2 laser beam is radiated under the condition as described above. This fact is considered as follows. That is, the physical characteristic, i.e., the change of the compaction appears, because the strain bond is a bond structure which is unstable in view of the energy, and the average value of the angles of the strained Si—O—Si bond becomes a more stable and small angle as the F2 laser beam is radiated. In this specification, the term “compaction” means the tendency of the quartz glass to possess the high refractive index, which is represented by a value obtained by measuring the difference in optical path length between the portion irradiated with the F2 laser beam and the portion not irradiated therewith and dividing the difference in optical path length by the thickness of the sample. When the compaction is not more than 2 ppm, the quartz glass member, which is excellent in the resistance to the laser, may be obtained, because the amount of strain bond is small. The compaction may be not more than 1.8 ppm and especially may be not more than 1 ppm. The quartz glass member, which satisfies the first and second requirements, may be used for the optical system of the exposure apparatus which uses the vacuum ultraviolet light beam as the light source, because the deterioration of characteristics including the deterioration of the transmittance is reliably suppressed with respect to the vacuum ultraviolet light such as ArF and the F2 laser.
In the present invention, the increase in the OH groups can be determined according to the infrared spectroscopy or the Raman spectroscopy. For example, the increase in the OH groups is determined by observing the increase in the integrated intensity of the infrared absorption band based on the OH stretching vibration after radiating the F2 laser beam under the condition as described above. In particular, when the strain bond exists in the quartz glass, it is possible to observe the amount of the integrated intensity change, because the intensity of the infrared absorption band of SiOH appearing in the vicinity of 3660 cm−1 is clearly changed by being irradiated with the F2 laser beam. For example, when the change of the integrated intensity of the infrared absorption band of SiOH appearing in the vicinity of 3660 cm−1 is less than 10%, the increase in the OH groups may be less than 100 wt. ppm. It has been revealed in Examples described later on that the amount of the OH groups determined by the method as described above, i.e., the amount of the strain bond is strongly correlated with the laser resistance of the quartz glass.
According to a second aspect of the present invention, there is provided a synthetic quartz glass member for being irradiated with a vacuum ultraviolet light beam, wherein H2 molecules, which are contained in the synthetic quartz glass member, are decreased by less than 1×1018 molecules/cm3, and a compaction is not more than 2 ppm, when the synthetic quartz glass member is subjected to 2×106 pulses of an F2 laser beam with a fluence of 10 mJ/cm2.
The third requirement, in which the H2 molecules dissolved in the quartz glass are decreased by less than 1×1018 molecules/cm3 after being irradiating with the F2 laser beam under the condition as described above, is derived from the fact that the strain bond is reacted in accordance with the formula (2) described above. That is, when the strain bond exists in the quartz glass, then the strain bond is reacted with H2 in the quartz glass in the presence of the F2 laser beam, and the amount of H2 is decreased. Therefore, when the decrease in the H2 molecules is small, i.e., less than 1×1018 molecules/cm3 even when the F2 laser beam is radiated, it is appreciated that the amount of strain bond is originally small in the quartz glass. Therefore, the satisfactory quartz glass is selected by measuring the decrease in the H2 molecules after radiating the F2 laser beam. Further, the inventors have found out the fact that when the third requirement is satisfied, the second requirement is almost satisfied, in which the compaction of the quartz glass is not more than 2 ppm after radiating the F2 laser beam under the condition described above. This fact is considered as follows. That is, the physical characteristic of the change of the refractive index appears, because the bond angle of the strain bond is decreased. The quartz glass member, which satisfies the second and third requirements, has the durability against the vacuum ultraviolet light beam such as ArF and the F2 laser.
In the present invention, the decrease in the H2 molecules can be determined according to the infrared spectroscopy or the Raman spectroscopy. For example, the decreased in the H2 molecules is determined by observing the Raman scattering peak based on the stretching vibration of the H2 molecule when the F2 laser beam is radiated under the condition as described above. In particular, a Raman scattering peak, which is based on the H2 stretching vibration in the vicinity of 4140 cm−1, is clearly changed by being irradiated with the F2 laser beam. Therefore, according to an experiment performed by the inventors, it has been revealed that the decrease in the integrated intensity of the peak of less than 80% corresponds to the decrease in the H2 molecules of less than 1×1018 molecules/cm3.
The synthetic quartz glass member of the present invention may contain hydrogen in an amount corresponding to a hydrogen molecule concentration of not less than 2×1017 molecules/cm3 in the synthetic quartz glass member, in order to improve the laser resistance in the vacuum ultraviolet region.
The synthetic quartz glass member of the present invention may contain OH groups by 500 wt. ppm to 1,300 wt. ppm. Owing to the OH groups, the glass viscosity is appropriately lowered, and the structural load on the Si—O—Si bond is reduced. Therefore, when the OH groups are contained within the concentration range as described above, it is possible to suppress the occurrence of the strain bond.
The synthetic quartz glass member of the present invention may contain fluorine by not less than 300 wt. ppm. Owing to the fluorine, the glass viscosity is lowered, and the structural load on the Si—O—Si bond is reduced. Therefore, when the fluorine is contained by not less than 300 wt. ppm, it is possible to effectively suppress the occurrence of the strain bond.
In the synthetic quartz glass member of the present invention, an internal transmittance in a direction perpendicular to an optical axis, which is obtained after radiating 2×106 pulses of the F2 laser beam with the fluence of 10 mJ/cm2, may be not less than 90% per a thickness of {fraction (1/4)} inch (about 0.64 cm), and a difference between maximum and minimum values of the internal transmittance may be within 1.0% in an irradiated area. On this condition, the decrease in the transmittance in the vacuum ultraviolet region, which is considered to be caused by the reaction of the strain bond, is scarcely caused, and the uniformity of the transmittance is maintained. Therefore, it is possible to provide the synthetic quartz glass member for the vacuum ultraviolet having the excellent laser resistance.
According to a third aspect of the present invention, there is provided a method for producing a synthetic quartz glass member, comprising the steps of: producing a base material of synthetic quartz glass; sampling a part of the base material; and processing the base material to prepare the synthetic quartz glass member on condition that OH groups, which are contained in the part of the base material, are increased by less than 100 wt. ppm, and a compaction is not more than 2 ppm, when the part of the sampled base material is subjected to 2×106 pulses of an F2 laser beam with a fluence of 10 mJ/cm2. In the method of the present invention, the quartz base material, which is preferably usable for the vacuum ultraviolet light, can be selected by radiating the F2 laser beam onto the part of the base material under the condition as described above to detect the increase in the OH groups and the compaction.
In the method of the present invention, the increase in the OH groups can be determined by the infrared or Raman spectroscopy. For example, the increase in the OH groups may be determined in accordance with increase in an integrated intensity of an infrared absorption band based on OH stretching vibration. In order to allow the increase in the OH groups to be less than 100 wt. ppm, the increase in the integrated intensity of the infrared absorption band of SiOH based on the OH stretching vibration, which appears in the vicinity of 3660 cm−1, may be less than 10%.
According to a fourth aspect of the present invention, there is provided a method for producing a synthetic quartz glass member, comprising the steps of: producing a base material of synthetic quartz glass; sampling a part of the base material; and processing the base material to prepare the synthetic quartz glass member on condition that H2 molecules, which are contained in the part of the base material, are decreased by less than 1×1018 molecules/cm3, and a compaction is not more than 2 ppm, when the part of the sampled base material is subjected to 2×106 pulses of an F2 laser beam with a fluence of 10 mJ/cm2. In the method of the present invention, the quartz glass material, which is preferably usable for the vacuum ultraviolet light, can be selected by radiating the F2 laser beam onto the part of the base material under the condition as described above to detect the decrease in the H2 molecules and the compaction.
Usually, the quartz glass for the ArF laser contains a large amount of OH groups, through which the F2 laser beam having a wavelength of 157 nm is hardly transmitted. Therefore, even when the ArF laser is directly radiated onto the quartz glass to perform any durability test, then a long period of time is required, and it is impossible to expect any correct judgment. In the present invention, the F2 laser beam is used as the light source to observe the decrease in the H2 molecules, and thus the strain bond can be observed correctly in a short period of time. Accordingly, the quartz glass base material for the ArF laser, which has satisfactory transmittance characteristics, has been obtained with ease.
In the method of the present invention, the decrease in the H2 molecules can be determined by the infrared spectroscopy or the Raman spectroscopy. For example, the decrease in the H2 molecules dissolved in the quartz glass may be determined by observing a Raman scattering spectrum based on stretching vibration of the H2 molecules in the vicinity of 4140 cm−1. In this procedure, when the decrease in the peak in the vicinity of 4140 cm−1 is less than 80%, it is possible to judge that the H2 molecules are decreased by less than 1×1018 molecules/cm3.
The burner 2 is installed to an upper portion of a furnace chamber 14 with its tip directed toward the target 4. Although not shown, for example, a discharge tube for discharging the exhaust gas to the outside of the furnace chamber 14 after the combustion is provided on a side wall of the furnace chamber 14.
The target 4 is rotated at an appropriate speed about the vertical axis by being driven by the driving unit 6, and the target 4 makes swinging movement in the leftward and rightward directions along the sheet surface of
The raw material supply unit 8 is provided with a flow rate-regulating section 8a. The high purity silicon tetrachloride as the raw material is spouted from a center tube of the burner 2 together with the carrier gas. When silicon tetrafluoride is used as another raw material, it is possible to obtain fluorine-doped type quartz glass.
The fuel supply unit 10 is provided with a flow rate-regulating section 10a. The fuel supply unit 10 supplies the hydrogen as the raw material to an outer tube of the burner 2. The oxygen supply unit 12 is also provided with a flow rate-regulating section 12a. The oxygen, which is to be mixed with the fuel, is supplied by the oxygen supply unit 12 to the outer tube of the burner 2.
An explanation will be made about the production of the synthetic quartz glass based on the use of the synthesizing furnace shown in
The laser pulses in the vacuum ultraviolet region of 157 nm are outputted from the laser light source 22. The intensity of the laser pulse outputted from the laser light source 22 is regulated on the basis of a control signal supplied from the control unit 28. The radiating optical system 24 regulates the beam shape and the energy density of the laser pulse to be come into the sample SA.
The control unit 28 outputs the control signal to the laser light source 22 so that the fluence of the laser pulse to be radiated onto the sample SA is regulated to be 10 mJ/cm2. The reason, why the fluence is 10 mJ/cM2, is that this value is the maximum power of the laser beam immediately radiated from a commercially available F2 laser apparatus. Further, the control unit 28 can regulate the number of laser pulses to be radiated onto the sample SA to be 2×106 by counting the number of pulses. The reason, why the number of laser pulses is 2×106, is that this value resides in a period of time required for the reaction of the formula (2) to distinctly appear. That is, the laser power (fluence) and the number of pulses are the values selected to effectively execute the accelerating test based on the use of the F2 laser.
An explanation will be made below about the operation for radiating the laser beam by using the laser-radiating apparatus shown in
In this embodiment, the light source 32 includes an exciting laser oscillator (Ar gas laser) for inducing the Raman scattering of H2. An exciting light beam having a wavelength of 514 nm is outputted at an appropriate intensity. The radiating optical system 34 regulates the beam shape and the energy density of the exciting light beam to be allowed to come into the sample SA. The light-collecting optical system 36 collects the Raman scattering light generated in the sample SA so that the light is allowed to come into the spectrometer 38. The spectrometer 38 detects the Raman scattering light collected by the light-collecting optical system 36 to measure the spectrum component intensity thereof. The control computing unit 39 controls the spectrometer 38 by outputting the control signal thereto to measure the spectroscopic intensity of the Raman scattering light outgoing from the sample SA and determine the peak intensity thereof.
In this embodiment, the light source 32 includes a halogen lamp which serves as an infrared illumination light source unit. Infrared illumination light having wavelengths of 2.5 to 2.9 μm, which includes the absorption band based on the OH group, is outputted at an appropriate intensity. The spectrometer 33 continuously switches the wavelength of the infrared illumination light to be supplied to the sample SA. The detector 35 measures the intensity of the light transmitted through the sample SA. The control computing unit 37 outputs the control signal to the spectrometer 33 and the detector 35 to determine the integrated intensity by measuring the spectrometric intensity of the transmitted light for the sample SA.
Next, an explanation will be made about a method for measuring the compaction. The amount of compaction was measured by using a commercially available Fizeau laser interferometer. An He—Ne laser (wavelength: 633 nm) was used as the light source. The laser beam from the light source was converted into a parallel light beam by allowing the laser beam to pass through a divergent lens, a beam splitter, and a collimator lens, and the light beam was allowed to arrive at a plane glass plate polished highly accurately and referred to as “fiducial plate”. A part of the light beam is reflected by a reference surface of the fiducial plate. The remaining light beam is transmitted through the sample, the light beam arrives at a mirror installed at the back surface of the sample, and the light beam is reflected. The reflected light beam from the reference surface and the reflected light beam from the mirror reversely travel along the original optical path, and they cause the interference followed by being introduced into an image pickup device (CCD) by the aid of a beam splitter. Thus, an interference fringe image is obtained. The interference fringes are subjected to the image analysis by the fringe scan method to obtain the optical path length (nL) distribution of the sample. In this expression, n represents the refractive index, and L represents the thickness of the sample. When the compaction is caused, the refractive index of the sample is raised by a slight amount (Δn). The optical path length is not changed for the non-irradiated portion. Therefore, the difference in optical path length between the irradiated portion and the non-irradiated portion is ΔnL. This value was divided by the thickness of the sample, and thus the compaction amount Δn was obtained.
At first, the ingot IN of the synthetic quartz glass is produced by using the synthesizing furnace shown in
Subsequently, the sample SA is prepared by cutting out a test piece from the ingot IN obtained in Step S10 (Step S11).
Subsequently, the accelerating radiation test is performed with the F2 laser for the sample SA by using the laser-radiating apparatus shown in
Subsequently, the Raman scattering characteristic based on H2 of the sample SA is measured by using the analyzer shown in
In this procedure, it is possible to estimate the changes of the peak intensity of the Raman scattering light and the integrated intensity of the infrared absorption band by preparing a pair of a sample SA treated with the apparatus shown in
Subsequently, it is judged whether or not the values of the intensity of the H2 Raman scattering light, the integrated intensity of the OH infrared absorption band, and the compaction obtained in Step S13 satisfy the predetermined performance conditions (Step S14). Specifically, it is judged whether or not the peak intensity of the H2 Raman scattering light in relation to the sample SA after the treatment with the laser-radiating apparatus shown in
Further, it is judged whether or not the integrated intensity of the OH infrared absorption band in relation to the sample SA after the treatment with the apparatus shown in
If the peak intensity of the H2 Raman scattering light is decreased by not less than 80% (if the H2 molecules dissolved in the sample are decreased by not less than 1×1018/cm3), if the integrated intensity of the OH infrared absorption band is increased by not less than 10% (if the H2 molecules dissolved in the sample are decreased by not less than 1×1018 molecules/cm3), or if the compaction is more than 2 ppm, then it is considered that the laser resistance of the ingot IN obtained in Step S10 is insufficient, and the process comes to an end. On the other hand, if the peak intensity of the H2 Raman scattering light is decreased by less than 80% (if the H2 molecules dissolved in the sample are decreased by less than 1×1018 molecules/cm3), if the integrated intensity of the OH infrared absorption band is increased by less than 10% (if the H2 molecules dissolved in the sample are decreased by less than 1×1018 molecules/cm3), or if the compaction is not more than 2 ppm, then it is considered that the laser resistance of the ingot IN obtained in Step S10 is sufficient, and the routine proceeds to the next Step S15.
In Step S15, a glass piece for an optical material is cut out from the ingot IN obtained in Step S10. In other words, a plurality of blocks corresponding to the shape of the objective optical member such as the lens and the prism are cut out from the ingot IN.
Subsequently, the blocks obtained in Step S15 are processed and polished (Step S16). Specifically, the plurality of blocks cut out in Step S15 are subjected to the cutting and the optical surface polishing respectively. If necessary, a coating is applied to the optical surface to obtain the optical member.
Finally, the obtained optical member is fixed to an appropriate position of a holding member such as a lens barrel to complete the synthetic quartz glass member such as the reduction projection lens (Step S17).
(1) Sample Preparation
At first, a large block for preparing an optical member having a thickness of φ250 mm×60 mm was cut out from the quartz glass ingot obtained by using the synthesizing furnace shown in
(2) Observation of Raman Scattering Spectrum
It was confirmed by the Raman spectroscopy that each of the obtained samples contained the OH groups in an amount of 1,000 wt. ppm and the hydrogen molecules in an amount of 1×1018 molecuels/cm3. 2×106 pulses of the F2 laser with the fluence of 10 mJ/cm2 were radiated on an area of φ60 mm on the surface of the sample at room temperature. The Raman scattering spectrum of the sample was observed after the radiation of the F2 laser.
(3) Measurement of Transmittance (λ=193 nm)
An ArF excimer laser (λ=193 nm) consisting of 1×108 pulses was radiated at 10 mJ/cm2 at room temperature perpendicularly onto an area of φ60 mm on a surface of another sample not irradiated with the F2 laser. The transmittance (including the reflection loss) at 193 nm, which was 90.70% before the radiation, was changed to 90.67% at the irradiated portion. The transmittance was scarcely lowered as described above. Therefore, it was successfully confirmed that the sample of Example 1 had the satisfactory laser resistance as the glass for the ArF excimer laser.
(4) Measurement of Compaction
The compaction was measured as follows for the sample irradiated with the F2 laser under the condition as described above. At first, the optical path length distribution of a fiducial plate was measured by using a Fizeau laser interferometer without placing any sample. After that, a sample of 60 mmφ×10 mm was interposed with the fiducial plate to measure the optical path length distribution. In this procedure, in order to suppress the reflection generated at the contact surface between the sample and the fiducial plate, an oil, which had the same refractive index as the refractive index of the quartz glass, was permeated into the contact surface between the fiducial plate and the sample. The difference between the optical path length measured with the interposed sample and the optical path length measured with no interposed sample was determined to estimate the optical path length distribution of the sample. The compaction amount Δn was obtained by dividing the difference ΔnL in the optical path length between the irradiated portion and the non-irradiated portion by the thickness of the sample. As a result, the compaction amount was 1.8 ppm at the F2 laser irradiated portion.
The sample was synthesized in the same manner as in Example 1. However, in the downstream annealing step, the annealing was applied in the air at 1,200° C. for 10 hours to manufacture a comparative sample which was evaluated in the same manner as in Example 1.
According to the measurement of the Raman scattering spectrum, it was revealed that the comparative sample contained OH by 1,000 wt. ppm and the hydrogen molecules by 1×1018 molecules/cm3. 2×106 pulses of F2 laser with the fluence of 10 mJ/cm2 were radiated perpendicularly onto an area of φ60 mm on a surface of the comparative sample at room temperature. The Raman scattering spectrum of the sample was observed after the radiation of the F2 laser.
The compaction of the comparative sample was measured in the same manner as in Example 1. As a result, the compaction was 5 ppm.
The ArF excimer laser consisting of 1×108 pulses was radiated at 10 mJ/cm2 at room temperature perpendicularly onto an area of φ60 mm on a surface of another comparative sample not irradiated with the F2 laser. The transmittance at 193 nm, which was 90.68% before the radiation, was decreased to 89.50% at the irradiated portion. It is understood that the comparative sample does not have any sufficient laser resistance as the glass for the ArF excimer laser.
A sample was manufactured in accordance with approximately the same method as that used in Example 1. However, the sample contained substantially no OH group, the sample contained the hydrogen molecules in an amount of 1×1018 molecules/cm3, and the sample contained fluorine in an amount of 3,000 wt. ppm, for example, by controlling of components and the fluorine dope. The components and the composition of the sample were confirmed by the Raman scattering spectrum and the infrared absorption spectrum. 2×106 pulses of the F2 laser with a fluence of 10 mJ/cm2 were radiated at room temperature perpendicularly onto an area of φ60 mm on a surface of the sample. The Raman scattering spectrum of the sample was observed after the radiation of the F2 laser.
The transmittance was measured at 157 nm for the sample irradiated with the F2 laser. As a result, the transmittance was 79.3% (including the reflection). The transmittance was decreased by about 0.5% as compared with the transmittance of 79.8% of the sample before the radiation. However, the satisfactory laser resistance was successfully obtained as the quartz glass for the F2 laser.
Further, the compaction was measured in the same manner as in Example 1 for the sample irradiated with the F2 laser and the sample not irradiated therewith. As a result, the compaction was 1.0 ppm.
A sample was synthesized in the same manner as in Example 2 described above. However, the comparative sample doped with no fluorine was manufactured, which was evaluated in the same manner as in Example 2.
The comparative sample contained substantially no OH group, and the comparative sample contained the hydrogen molecules in an amount of 1×1018 molecules/cm3. 2×106 pulses of the F2 laser with a fluence of 10 mJ/cm2 were radiated at room temperature perpendicularly onto an area of φ60 mm on a surface of the comparative sample. As a result, as shown in
Further, the compaction was measured in the same manner as in Example 1 for the comparative sample irradiated with the F2 laser and the comparative sample not irradiated therewith. As a result, the compaction was 2.5 ppm.
The transmittance was measured at a wavelength of 157 nm for the comparative sample irradiated with the F2 laser. As a result, the transmittance was 69.0% (including the reflection). The transmittance was decreased by about 9.2% as compared with the transmittance of 78.2% (including the reflection) before the radiation. This fact means that the laser resistance is insufficient for the quartz glass for the F2 laser.
A synthetic quartz glass block, which had the same composition as that in Example 2 (doped with fluorine 3,000 wt. ppm), was prepared to manufacture a reticle substrate having one side of 140 (mm) and a thickness of ¼ (inch). 2×106 pulses of the F2 laser with 10 mJ/cm2 were radiated onto the entire surface of the substrate at room temperature. After the radiation, the transmittance (λ=157 nm) was decreased by 1.0% in the vicinity of the center of the sample, and the difference between the maximum and minimum values of the transmittance was 0.8% in the plane of 140 mm×140 mm. The substrate had the satisfactory laser resistance and the uniform transmittance as the reticle substrate for the F2 laser.
Further, the compaction amount was measured in the same manner as in Example 1 for the portion irradiated with the F2 laser in relation to the sample substrate manufactured in the same manner as described above. As a result, the compaction amount of the irradiated portion was 1.0 ppm.
A sample was synthesized in the same manner as in Example 3. However, a comparative substrate doped with no fluorine was manufactured, which was evaluated in the same manner as in Example 3. 2×106 pulses of the F2 laser with 10 mJ/cm2 were radiated onto the entire surface of the substrate at room temperature. After the radiation, the transmittance at 157 nm was decreased by 10% in the vicinity of the center of the sample, and the difference between the maximum and minimum values of the transmittance was 3% in the plane of 140 mm×140 mm. It is not affirmed that the substrate has the satisfactory laser resistance as the reticle substrate for the F2 laser. Further, the compaction amount was measured in the same manner as in Example 1 for the portion irradiated with the F2 laser in relation to the sample substrate manufactured in the same manner as described above. As a result, the compaction amount of the irradiated portion was 2.5 ppm.
Next, an exposure apparatus of the present invention will be explained by way of example.
The quartz glass members produced in Example 1 described above are used for an optical lens 90 included in the illumination optical system 101 and an optical lens 92 included in the projection optical system 500 respectively. Therefore, the exposure apparatus is excellent in the resistance to the ArF laser beam supplied from the light source 100, and the satisfactory transmittance is maintained over a long period of time. Therefore, it is possible to realize a long service life of the exposure apparatus. Further, the throughput is consequently improved as well, for example, when semiconductor circuits and liquid crystal display substrates are produced. Further, the reticle R is also produced by using the quartz glass substrate produced in Example. Therefore, the deterioration of the transmittance is sufficiently suppressed during the exposure operation. The highly accurate reticle pattern is prevented from the deterioration.
The characteristic deterioration such as the deterioration of the transmittance in the vacuum ultraviolet region, which is considered to be caused by the reaction of the strained Si—O—Si bond, is suppressed in the synthetic quartz glass member of the present invention. Therefore, the synthetic quartz glass member of the present invention is preferably usable for the element such as lenses, prisms, and reticles having the excellent laser resistance to the ArF excimer laser and the F2 laser. The optical element excellent in the laser resistance in the vacuum ultraviolet region and the exposure apparatus provided with the same can be provided in accordance with the method for producing the synthetic quartz glass member of the present invention. The exposure apparatus of the present invention is provided with the synthetic quartz glass member of the present invention. Therefore, even when any vacuum ultraviolet light source such as ArF is used, it is possible to suppress the deterioration of the pattern image over a long period of time, which would be otherwise caused by the deterioration of the transmittance.
Number | Date | Country | Kind |
---|---|---|---|
2002-83476 | Mar 2002 | JP | national |
This application is a Continuation Application of International Application No. PCT/JP03/03618 which was filed on Mar. 25, 2003 claiming the conventional priority of Japanese patent Application No. 2002-083476 filed on Mar. 25, 2002.
Number | Date | Country | |
---|---|---|---|
Parent | PCT/JP03/03618 | Mar 2003 | US |
Child | 10947366 | Sep 2004 | US |