This disclosure relates to construction materials and, more particularly, to a method for making and applying construction materials.
Existing approaches in the fields of sewer refurbishing and concrete restoration may involve the application of shotcrete, which may be pneumatically projected towards the surface in need of repair. This shotcrete includes materials found in basic concrete, such as, sand, Portland cement, and water. At a particular job site, this shotcrete may take the form of either a dry-mix or a wet-mix application. The phrase “dry-mix” typically involves the pneumatic transfer of some or all of the materials in a dry state, through a hose, to a nozzle where an operator may control the application of water to the dry-mix at the nozzle prior to the projection of the substance. In contrast, the phrase “wet-mix” typically involves the transfer of a previously mixed concrete, including water, through a hose prior to projection.
Some companies have attempted to alter the material composition of the shotcrete in order to obtain certain benefits. Accordingly, some approaches may involve the use of geopolymers. However, these materials are often subject to corrosion as a result of the organic material inherent in these products. For example, Milliken® manufactures various products under their GeoSpray™ and GeoSpray™ AMS line of products. The AMS product may be applied as a pre and/or post-treatment to the GeoSpray™ product. GeoSpray is Portland cement-based and contains only a small portion of a geopolymer. This mixture is not acid stable. AMS contains organics to combat the effects of acids on Portland cement based concrete and of organics and microbial induced corrosion that happens with Portland cement based coatings.
In a first implementation, a method for applying a construction material is provided. The method may include mixing blast furnace slag material, geopolymer material, alkali-based powder, and sand at a mixing device to generate a non-Portland cement-based material. The method may also include transporting the non-Portland cement-based material from the mixing device, through a conduit to a nozzle and combining the transported non-Portland cement-based material with water at the nozzle to generate a partially liquefied non-Portland cement-based material. The method may further include pneumatically applying the partially liquefied non-Portland cement-based material to a surface.
One or more of the following features may be included. In some embodiments, the geopolymer material is at least one of volcano rock flour and fly ash. The alkali-based powder may include silicate. Mixing may be performed as a dry-mix. The non-Portland cement-based material may be inorganic. Mixing may be performed at a mobile sewer refurbishing vehicle. The non-Portland cement-based material may include at least one of clay, gneiss, granite, liparite, andesite, picrite, potassic feldspar, albite, pumice and zeolite. Mixing may include mixing at a portable gun, which is configured to receive the non-Portland cement-based material from the mixing device. The components of the non-Portland cement-based material may include a Blaine fineness value of approximately 3500 cm2/g.
In another implementation, a system for applying a construction material is provided. The system may include a mixing device configured to mix blast furnace slag material, geopolymer material, alkali-based powder, and sand to generate a non-Portland cement-based material. The system may also include a conduit configured to transport the non-Portland cement-based material from the mixing device. The system may further include a nozzle configured to receive the non-Portland cement-based material and combine the transported non-Portland cement-based material with water to generate a partially liquefied non-Portland cement-based material, wherein the nozzle is further configured to pneumatically apply the partially liquefied non-Portland cement-based material to a surface.
One or more of the following features may be included. In some embodiments, the geopolymer material may be at least one of volcano rock flour and fly ash. The alkali-based powder may include silicate. Mixing may be performed as a dry-mix. The non-Portland cement-based material may be inorganic. Mixing may be performed at a mobile sewer refurbishing vehicle. The non-Portland cement-based material may include at least one of clay, gneiss, granite, liparite, andesite, picrite, potassic feldspar, albite, pumice and zeolite. Mixing may include mixing at a portable gun, which is configured to receive the non-Portland cement-based material from the mixing device. The components of the non-Portland cement-based material may include a Blaine fineness value of approximately 3500 cm2/g.
In another implementation, a non-Portland cement-based construction material is provided. The non-Portland cement-based construction material blast furnace slag material, volcano rock flour, alkali-based powder, and sand. In some embodiments, the alkali-based powder may be silicate.
The details of one or more implementations are set forth in the accompanying drawings and the description below. Other features and advantages will become apparent from the description, the drawings, and the claims.
Like reference symbols in the various drawings may indicate like elements.
Embodiments of the present disclosure are directed towards a construction material having an alkali-activated binder (i.e. non-Portland cement based) and a system and method for making and applying the same. Although many of the examples included herein are discussed in the context of concrete rehabilitation it should be noted that the construction material described herein may be used in any suitable application. Some of these may include, but are not limited to, sewer rehabilitation projects, paint spray gun applications, onsite mobile batch plants, any concrete structure undergoing an acid attack, etc.
Referring to
In some embodiments, mobile sewer refurbishing vehicle 100 may be configured to mix and apply a non-Portland cement-based construction material. This material may be mixed at the vehicle (e.g. within mixing device 106) or prior to being placed within second container 108. This material may be transported to nozzle 214, where it may be mixed with liquid from storage unit 104, prior to being applied to the surface in need of repair. The specifics of the non-Portland cement based construction material are discussed in further detail herein below.
In some embodiments, the non-Portland cement based construction material described herein may have better strength values as compared to existing materials, a high resistance and no reactivity versus inorganic and organic acids and additionally high early strength values. The material may include a dry mix of blast furnace slag material, geopolymer material, alkali-based powder, and sand at a mixing device to generate the non-Portland cement-based material.
In some embodiments, the non-Portland cement based construction material may include various types of geopolymer material. Some of these may include, but are not limited to, pozzolanic material, which may react with strong alkali and mixing that blend with the sand and/or grit. In some embodiments, the pozzolanic material may include active silicates like slag sand or fly ash. Natural material like volcano rocks or some others may also be used, however, these may be more desirable if used in smaller portions as very fine powder.
In some embodiments, the non-Portland cement based construction material may include any number of pozzolanic materials, some of which may include, but are not limited to finely ground clay, gneiss, granite, liparite, andesite, picrite, potassic feldspar, albite, pumice, zeolite, etc., as well as mixtures thereof. These materials may be used in a ground form, calcinated and/or noncalcinated. Additionally and/or alternatively, all raw materials containing sufficient amounts of reactive (e.g., metastable, vitreous) SiO2 and Al2O3, including, but not limited to, ashes, puzzolans, slags may also be suitable for embodiments of the present disclosure.
In some embodiments, the non-Portland cement based construction material may include an alkali-based powder material and/or various mixing liquids. Some possible mixing liquids may include, but are not limited to, potassium and sodium water glass, alkali hydroxides, etc.
In some embodiments, the reaction between the SiO2/Al2O3 containing components and the alkaline mixing liquid may result in alumino-silicates having a tridimensional structure. These framework structures allow for the creation of a construction material requiring no Portland cement in the compound.
In operation, the ingredients may be thoroughly mixed (e.g., wholly or partially at vehicle 100) and then delivered to portable gun 212. The non-Portland cement based construction material may be carried via compressed air through the conduit 216 to nozzle 214. In one particular embodiment, potassium silicate, solid content 48%, density 1.52 g/ml, wt SiO2:K2O 1,14, and some water may be added and thoroughly mixed inside nozzle 214 in a short period of time (e.g., less than 1 second) before the partially liquefied mixture may be pneumatically applied to the surface of interest.
In one particular example, the non-Portland cement based construction material may be comprised of the following mixture:
In some embodiments, the components of the mixture may have a Blaine fineness of approximately 3500 cm2/g.
In another example, the non-Portland cement based construction material may be comprised of the following mixture:
1-2
In another example, the non-Portland cement based construction material may be comprised of the following mixture:
Embodiments of the non-Portland cement based construction material produced an unanticipated result as the reaction time of the alkaline ingredients with the rock flour was sufficient to generate a sticky compound. Through numerous tests, this compound was found to adhere extremely well on a vertical surface, builds a tide bonding and hardens within 3 days with compressive strength values above 50 N/mm2 (8000 psi).
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the disclosure. As used herein, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.
The corresponding structures, materials, acts, and equivalents of all means or step plus function elements in the claims below are intended to include any structure, material, or act for performing the function in combination with other claimed elements as specifically claimed. The description of the present disclosure has been presented for purposes of illustration and description, but is not intended to be exhaustive or limited to the disclosure in the form disclosed. Many modifications and variations will be apparent to those of ordinary skill in the art without departing from the scope and spirit of the disclosure. The embodiment was chosen and described in order to best explain the principles of the disclosure and the practical application, and to enable others of ordinary skill in the art to understand the disclosure for various embodiments with various modifications as are suited to the particular use contemplated.
Having thus described the disclosure of the present application in detail and by reference to embodiments thereof, it will be apparent that modifications and variations are possible without departing from the scope of the disclosure defined in the appended claims.
This is a divisional of U.S. patent application Ser. No. 17/229,008, filed 13 Apr. 2021, which is a continuation of U.S. patent application Ser. No. 15/856,857, filed 28 Dec. 2017, which is a divisional of U.S. patent application Ser. No. 14/705,534 filed on 6 May 2015, now U.S. Pat. No. 9,896,379, Issued 20 Feb. 2018, entitled System and Method for Making and Applying a Non-Portland Cement-Based Material, the contents of which are all incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 17229008 | Apr 2021 | US |
| Child | 17835059 | US | |
| Parent | 14705534 | May 2015 | US |
| Child | 15856857 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15856857 | Dec 2017 | US |
| Child | 17229008 | US |