Patent Application
20180328194
The present disclosure relates to an abrasive coating for gas turbine engine components.
Abrasive coatings often protect rotating parts during rub interaction with associated abradeable seals to establish a mating surface with the smallest possible clearance. The abrasive coatings are often utilized to form abrasive tips of rotating blades, cantilevered vanes, and knife edge seals of gas turbine engines. Polymer composite and polymer coated aluminum fan blades may suffer from wear due to frictional heating at the interface with an abradable blade outer air seal.
Both polymer bonded and thermally sprayed metal matrix abrasive coatings have been demonstrated, however, a variety of technical hurdles to cost effective implementation exist. While polymer based abrasive coatings obviate corrosion and fatigue issues, dimensional control of liquid flow polymer based abrasive coating application remain.
A rotating component according to one disclosed non-limiting embodiment of the present disclosure can include an airfoil section including a free end; and an abrasive coating sprayed onto the free end, the abrasive coating including a polymer matrix and an abrasive filler, the abrasive filler between about 50%-75% by volume of the abrasive coating.
A further embodiment of the present disclosure may include, wherein the polymer matrix provides about 3%-10% volume of the abrasive coating once cured.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the abrasive filler is zirconia.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the abrasive filler has an average particle size of 220 mesh.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the polymer matrix outgases during elevated temperature curing.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the component is a fan blade.
A system for spraying an abrasive coating onto a component according to another disclosed non-limiting embodiment of the present disclosure can include a spray gun from which a polymer matrix is atomized and propelled toward the component by an air jet such that grit particles are deposited onto the component.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the grit particles are communicated into the air jet.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the grit particles are sprayed separately onto the component.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the grit particles are coated by the polymer matrix prior to spraying by the spray gun.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the abrasive filler is zirconia.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the abrasive filler has an average particle size of 220 mesh.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the abrasive filler is between about 50%-75% by volume of the abrasive coating.
A method of fabricating an abrasive coating according to another disclosed non-limiting embodiment of the present disclosure can include spraying a polymer matrix which is atomized and propelled by an air jet and depositing grit particles with the polymer matrix forming an abrasive coating.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, codepositing the grit particles with the air jet.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the grit particles form about 50%-75% by volume of the abrasive coating.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, curing the polymer matrix such that the polymer matrix outgases through the grit particles during curing.
A further embodiment of any of the foregoing embodiments of the present disclosure may include, wherein the polymer matrix provides about 3%-10% a volume of the abrasive coating when cured.
A further embodiment of any of the foregoing embodiments of the present disclosure may include spraying the grit particles with a second air jet.
A further embodiment of any of the foregoing embodiments of the present disclosure may include spraying the abrasive coating onto a free end of a fan blade.
The foregoing features and elements may be combined in various combinations without exclusivity, unless expressly indicated otherwise. These features and elements as well as the operation thereof will become more apparent in light of the following description and the accompanying drawings. It should be understood, however, the following description and drawings are intended to be exemplary in nature and non-limiting.
Various features will become apparent to those skilled in the art from the following detailed description of the disclosed non-limiting embodiments. The drawings that accompany the detailed description can be briefly described as follows:
The engine 20 generally includes a low spool 30 and a high spool 32 mounted for rotation about an engine central longitudinal axis X relative to an engine static structure 36 via several bearing structures 38. The low spool 30 generally includes an inner shaft 40 that interconnects a fan 42, a low pressure compressor (“LPC”) 44 and a low pressure turbine (“LPT”) 46. The inner shaft 40 drives the fan 42 directly or through a geared architecture 48 to drive the fan 42 at a lower speed than the low spool 30. An exemplary reduction transmission is an epicyclic transmission, namely a planetary or star gear system.
The high spool 32 includes an outer shaft 50 that interconnects a high pressure compressor (“HPC”) 52 and high pressure turbine (“HPT”) 54. A combustor 56 is arranged between the high pressure compressor 52 and the high pressure turbine 54. The inner shaft 40 and the outer shaft 50 are concentric and rotate about the engine central longitudinal axis X which is collinear with their longitudinal axes.
Core airflow is compressed by the LPC 44 then the HPC 52, mixed with the fuel and burned in the combustor 56, then expanded over the HPT 54 and the LPT 46. The turbines 54, 46 rotationally drive the respective low spool 30 and high spool 32 in response to the expansion. The main engine shafts 40, 50 are supported at a plurality of points by bearing structures 38 within the static structure 36.
The engine 20, in one example, is a high-bypass geared aircraft engine. In a further example, the engine 20 bypass ratio is greater than about six (6), with an example embodiment being greater than about ten (10), the geared architecture 48 is an epicyclic gear train, such as a planetary gear system or other gear system, with a gear reduction ratio of greater than about 2.3 and the low pressure turbine 46 has a pressure ratio that is greater than about five.
In one disclosed embodiment, the engine 20 bypass ratio is greater than about ten (10:1), the fan diameter is significantly larger than that of the low pressure compressor 44, and the low pressure turbine 46 has a pressure ratio that is greater than about five (5:1). Low pressure turbine 46 pressure ratio is pressure measured prior to inlet of low pressure turbine 46 as related to the pressure at the outlet of the low pressure turbine 46 prior to an exhaust nozzle. The geared architecture 48 may be an epicycle gear train, such as a planetary gear system or other gear system, with a gear reduction ratio of greater than about 2.3:1. It should be understood, however, that the above parameters are only exemplary of one embodiment of a geared architecture engine and that the present invention is applicable to other gas turbine engines including direct drive turbofans.
A significant amount of thrust is provided by the bypass flow B due to the high bypass ratio. The fan section 22 of the engine 20 is designed for a particular flight condition—typically cruise at about 0.8 Mach and about 35,000 feet. The flight condition of 0.8 Mach and 35,000 ft, with the engine at its best fuel consumption—also known as “bucket cruise Thrust Specific Fuel Consumption” (TSFC)—which is the industry standard parameter of lbm of fuel being burned divided by lbf of thrust the engine produces at that operating point. “low fan pressure ratio” is the pressure ratio across the fan blade alone, without a Fan Exit Guide Vane (“FEGV”) system. The low fan pressure ratio as disclosed herein according to one non-limiting embodiment is less than about 1.45. “Low corrected fan tip speed” is the actual fan tip speed in ft/sec divided by an industry standard temperature correction of [(Tram ° R)/(518.7° R)]0.5. The “Low corrected fan tip speed” as disclosed herein according to one non-limiting embodiment is less than about 1150 ft/second.
With reference to
The fan case 77 is annular in shape and circumscribes the blades 62. The fan section 22 is arranged so that the abrasive tips 78 of the fan blades 62 rub against an abradable seal 80 mounted on a radially inner side of the fan case 77. The abradable seal 80 may be formed of a polymeric-based material, such as a polymer matrix composite. In one further example, the polymer matrix composite includes an epoxy matrix and silica-containing filler dispersed through the matrix. In a further example, the silica-containing filler is or includes hollow glass microspheres. An example is 3M™ Scotch-Weld™ Structural Void Filling Compound EC-3555.
When two components are in rubbing contact, at least one of the components may wear. The term “abradable” refers to the one of the two components that wears, while the other component is “abrasive” and does not wear or wears less. Thus, when the abrasive tips 78 of the fan blades 62 rub against the abradable seal 80, the abradable seal 80 will be worn whereas the abrasive tips 78 will not wear, or will wear less, than the abradable seal 80. The word “abrasive” thus also implies that there is, or can be, contact with an abradable component.
With reference to
In one example, the abrasive coating 100 may be a polymer matrix that outgases during elevated temperature curing and supports abrasive filler. The polymer matrix includes one or more epoxies, polyimides, polyurethanes, cyanoacrylates, acrylics, etc., and combinations thereof, with suitable abrasive fillers such as zirconia, alumina, silica, cubic boron nitride (CBN), various metal alloys, and mixtures thereof. One suitable abrasive is sold by Washing Mills under the trademark DURALUM ATZ II W, 220 mesh. More specifically, zirconia having an average particle size of 220 mesh may be effective, although the particle size may vary.
With reference to
In another embodiment, the grit particles 208 are communicated by an air jet 220 from a separate spray gun (
In still another embodiment, the abrasive coating 100 includes grit particles 230 that are pre-coated with a polymer matrix 232 (
The sprayed application advantageously facilitates the deposition of low polymer content mixtures, produce a porous deposit, and controls the wicking and flow of the polymer. Since the grit and polymer matrix is applied via the sprayed application, and the polymer matrix is not utilized to carry the grit, relatively high grit loading is readily achieved. In one example, about 50%-75% by volume of the abrasive coating 100 is grit. At such a high grit loading, capillary action advantageously facilitates the retention of the polymer matrix into the crevices between the grit particles without undue excess polymer matrix that may flow to unwanted areas.
In one example, the polymer matrix provides about 3%-10% volume of the abrasive coating once cured. The relatively low polymer matrix content maintains porosity between the grit particles that allows the escape of gas produced during curing as well as the solvents used to thin un-cured polyimide and other high performance polymers. That is, the polyimide process is itself facilitated by high grit loading and low polymer content that results in porosity that allows evolved gasses to escape.
It should be appreciated that various masking methods that may include silicone thermal spray masking tape in combination with rubber sheets may be utilized to mask portions of the airfoil section 64. Masking may additionally or alternatively include shadow masking where the shadow mask is spaced apart from the tip. In shadow masking, the gun may be traversed relative to the part. During a portion of the traversal, the mask partially occludes a portion of the deposition area leading to a relatively thick coating in the center of the area, thinning toward the periphery.
The sprayed application facilitates the use of a relatively low cost form of the constituents, is flexible to part geometry changes, uses low cost masking/tooling and increases the available level of grit loading. The increased grit loading also results in a more desirable wear ratio with the abradable and allows cost effective application of polyimide.
The use of the terms “a,” “an,” “the,” and similar references in the context of description (especially in the context of the following claims) are to be construed to cover both the singular and the plural, unless otherwise indicated herein or specifically contradicted by context. The modifier “about” used in connection with a quantity is inclusive of the stated value and has the meaning dictated by the context (e.g., it includes the degree of error associated with measurement of the particular quantity). All ranges disclosed herein are inclusive of the endpoints, and the endpoints are independently combinable with each other. It should be appreciated that relative positional terms such as “forward,” “aft,” “upper,” “lower,” “above,” “below,” and the like are with reference to normal operational attitude and should not be considered otherwise limiting.
Although the different non-limiting embodiments have specific illustrated components, the embodiments of this invention are not limited to those particular combinations. It is possible to use some of the components or features from any of the non-limiting embodiments in combination with features or components from any of the other non-limiting embodiments.
It should be appreciated that like reference numerals identify corresponding or similar elements throughout the several drawings. It should also be appreciated that although a particular component arrangement is disclosed in the illustrated embodiment, other arrangements will benefit herefrom.
Although particular step sequences are shown, described, and claimed, it should be understood that steps may be performed in any order, separated or combined unless otherwise indicated and will still benefit from the present disclosure.
The foregoing description is exemplary rather than defined by the limitations within. Various non-limiting embodiments are disclosed herein, however, one of ordinary skill in the art would recognize that various modifications and variations in light of the above teachings will fall within the scope of the appended claims. It is therefore to be understood that within the scope of the appended claims, the disclosure may be practiced other than as specifically described. For that reason the appended claims should be studied to determine true scope and content.