System and method for promoting selective tissue in-growth for an implantable medical device

Information

  • Patent Grant
  • 6704604
  • Patent Number
    6,704,604
  • Date Filed
    Thursday, April 5, 2001
    23 years ago
  • Date Issued
    Tuesday, March 9, 2004
    20 years ago
Abstract
Disclosed is an improved system and method to selectively promote tissue in-growth on, or adjacent to, an implantable medical device. In one embodiment, at least one surface of the housing of a medical device is in contact with a first portion of a porous PTFE having a pore size adapted to prevent substantially all tissue in-growth. This first portion, or layer, of porous PTFE material is further in contact at predetermined locations with an additional porous PTFE layer having a pore size adapted to selectively promote tissue in-growth only at the predetermined locations. Each of the PTFE layers may be formed of porous PTFE tubing or tape. Alternatively, the two layers may comprise a single composite structure that has a more porous material exposed on a first surface, and a less porous, more dense, material on a second surface. Another embodiment of the invention involves forming the layers of PTFE into a removable member that is adjacent to at least one surface of the implantable medical device. The removable member may take the form of a sleeve that surrounds a portion of a the medical device and is adapted to remain in the body during an extraction process. For example, during the removal of a lead, the sleeve remains within the body and is capable of receiving a replacement lead, making it unnecessary to disturb tissue in-growth attached to the sleeve.
Description




FIELD OF THE INVENTION




The present invention relates generally to implantable medical devices; and more particular, relates to implantable devices that include an exterior structure to selectively promote tissue ingrowth.




BACKGROUND OF THE INVENTION




Transvenous cardioversion and defibrillation leads typically employ cardioversion or defibrillation electrodes taking the form of elongated metal coils. These coils may be applied to the exterior surface of the lead body, as disclosed in U.S. Pat. No. 4,934,049 issued to Kiekhafer et al.




One problem associated with defibrillation coils of the type discussed in the '049 patent involves the occurrence of tissue in-growth around the coil structure of the electrode. This is particularly true when the coil electrode is formed around the lead body so as to create an enlarged profile at the location of the coil as compared to the rest of the lead body. Tissue attachment that occurs proximal to the electrode structure makes it difficult to extract distal end of the lead, including the enlarged coil.




One way to reduce the problem of tissue in-growth involves providing defibrillation coils that are isodiametric with respect to the lead body. Such isodiametric electrode coils may be molded into the electrode body or the coils may be machined to provide a flush surface. This is described in U.S. Pat. No. 4,161,952, issued to Kinney et al. Similarly, U.S. Pat. No. 5,957,970 to Shoberg discloses an isodiametric defibrillation lead manufactured by removing a portion of an extruded tubular lead body in the region of the coil so that the electrode is flush with the surface of the lead. The 6944 Model lead commercially available from the Medtronic Corporation provides an isodiametric lead of this design.




Although isodiametric coil electrodes reduce problems associated with extracting an enlarged lead portion from ingrown tissue, other problems still exist related to in-growth. For example, tissue commonly attaches around the coils of a defibrillation electrode, further increasing the difficulty associated with lead extraction.




Various methods have been attempted to overcome the problems associated with tissue in-growth around coil electrodes. One solution disclosed in the '049 patent referenced above involves injecting silicone rubber into the spaces between the individual coils of an electrode. The resulting thin coating of silicone rubber surrounding the exterior of the coils of electrode minimizes tissue in-growth between the filars of the coils, while leaving a portion of the coils exposed to deliver electrical stimulation to a patient.




Another approach to preventing tissue in-growth is disclosed in U.S. Pat. No. 5,090,422, which describes the use of a biocompatible porous materials such as woven, porous polyurethane and porous polytetrafluoroethylene that may be used to cover an electrode surface. The material is insulative when dry, but becomes conductive when bodily fluids penetrate the pores of the material. The porous covering is of adequately small pore size and fibril length to preclude substantial tissue in-growth.




Yet another method of preventing tissue in-growth is disclosed in U.S. Pat. No. 5,609,622, which describes coating a lead with a porous Polytetrafluoroethylene (PTFE) layer such as may be formed of expanded PTFE (e-PTFE), and which has a pore size of less than 10 microns or smaller so that the pore size is very small, and tissue in-growth is prevented.




While the foregoing approaches are directed to preventing tissue in-growth, it may be noted that some controlled tissue attachment to a lead body or electrode may actually be beneficial in stabilizing the lead, and allowing the electrode to maintain a position at a desired implant site. For example, in leads carrying defibrillation electrodes, a change in the coil placement may increase the defibrillation thresholds. Similarly, in pace/sense applications, a shift in electrode position may alter the pacing threshold and affect capture. Promoting tissue growth for stabilizing prosthesis and other implanted structures has been disclosed in the prior art. For example, U.S. Pat. No. 5,035,713 discusses use of a re-entrant biocompatible material such as polyethylene, polyethylene teraphthalate, polypropylene, polysulfone, polylactic acid and polydioxanone to promote selective tissue in-growth to stabilize an implanted structure. Similarly, U.S. Pat. No. 5,833,664 discusses promoting tissue attachment to intrabody prosthetic devices, such as catheters, to effect improved stability of the prosthesis/tissue opening site interface.




Yet a further concern associated with the use of medical electrical leads, and in particular, the use of leads carrying coiled electrode structures, involves the possibility of a coil causing abrasion to an adjacent lead structures. For example, a coiled electrode adapted for use in the right atrium may lie in close proximity to a second lead carrying an electrode placed in the right ventricle. The coiled electrode may contact the second lead, creating abrasions in the external lead surface so that an internal conductor comes in contact with body fluids. This condition may ultimately result in lead failure. Also, in applications in which leads are positioned within relatively smaller vasculature structures, such as in coronary veins, lead-to-lead contact, or lead-to-tissue contact can be exacerbated, thus increasing the likelihood of abrasion.




Therefore, what is needed is an improved lead structure that minimizes the potential for the abrasion of adjacent structures. The lead ideally promotes selective, controlled tissue attachment to stabilize lead placement, while preventing tissue in-growth that would prevent lead extraction.




SUMMARY OF THE INVENTION




The present invention provides an improved system and method of selectively promoting tissue in-growth on, or adjacent to, an implantable medical device (IMD). In one embodiment of the invention, a first portion of porous PTFE is provided adjacent to at least a first surface of the IMD. The porous PTFE, which may be an expandable PTFE (e-PTFE), has a pore size that is small enough to prevent substantially all tissue in-growth. For example, the pore size may be 10 microns or less. This first portion of PTFE is adjacent at one or more selected locations to a second portion of porous PTFE. This second portion of PTFE has a pore size adapted to promote tissue in-growth. For example, the pore size of this second portion may be 20 to 50 microns. In this manner, tissue in-growth will only occur at the first surface of the IMD in the vicinity of the second portions of PTFE. At other areas of the first surface of the IMD, all tissue in-growth will be substantially prevented.




In another embodiment of the invention, the inventive system includes a removable member that is adapted to be adjacent to at least one surface of the IMD. The removable member is formed of a first portion, or layer, of porous PTFE to substantially prevent all tissue in-growth, and one or more second portions, or layers, of porous PTFE that are provided to promote tissue in-growth in selected locations. The removable member may take the form of a sleeve, as may be adapted to slide over a portion of a lead. This sleeve may be adapted to remain in the body of a patient during a lead extraction process so that a replacement lead may be advanced within the sleeve. Because the sleeve is adapted for preventing tissue in-growth in the lead itself, the lead extraction process is greatly simplified.




According to one embodiment of the invention, each of the PTFE layers are formed of porous PTFE tubing having a thickness of 50 microns or less, and preferably less than 25 microns. The tubing may be heat-shrinkable such that it conforms to a specific surface of an electrode or other implantable medical device upon the application of heat. In yet another embodiment of the invention, the layers of porous PTFE may be formed of a tape that may be applied to the surface of the implantable medical device. In still a further embodiment of the invention, the two layers are provided by a single composite structure that has a more porous material exposed on a first surface adapted to be located adjacent tissue, and a less porous, more dense material on a second surface adapted to be situated adjacent the electrode. This type of composite structure may be formed by first creating a coating of e-PTFE having a unified density. One surface of the composite structure may then be altered to be more porous by selectably removing fibrils from this surface. Alternatively, this structure may be formed using a co-extrusion process to create the layers with different pore sizes.




According to one manner of using the current invention, a lead having at least one coil electrode is coated with an inner layer of porous PTFE such as expanded-PTFE (e-PTFE) to prevent tissue in-growth. This inner layer is surrounded by a more porous PTFE layer having a pore size selected to promote tissue in-growth. The tissue in-growth promoted by the pore size of the outer layer is controlled such that the coil electrode is stabilized at a desired implant site by the tissue attached to this layer. Tissue is prevented from adhering to any part of the coil structure itself by the inner layer.




The current invention may be adapted for selectively promoting tissue in-growth in subcutaneous electrode arrays, and in any other type of implantable lead or electrode system. In addition to promoting tissue in-growth to stabilize the location of an implantable medical device, the current system also prevents lead abrasion cause by electrode coils rubbing against adjacent lead structures when multiple leads are in close communication with one another within a patient's vascular system.











Other aspects of the invention will become apparent to those skilled in the art from the description of the invention and the accompanying drawings.




BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is a plan view of a defibrillation lead of the type in which the present invention may usefully be practiced.





FIG. 2

is an exploded side cutaway view of a defibrillation coil including silicone backfill to prevent tissue in-growth in a manner known in the art.





FIG. 3

is a side cutaway view of one embodiment of a lead according to the current invention.





FIG. 4

is a cross-sectional view of the lead of

FIG. 3

at line


4





4


.





FIG. 5

is side cutaway view of an alternative embodiment of a lead configured according to the current invention.





FIG. 6

is a diagram depicting two defibrillation leads placed within a human heart, and illustrates use of the current invention to prevent lead abrasion.





FIG. 7

illustrates a subcutaneous defibrillation electrode array that is particularly adapted for use with the current invention.





FIG. 8

is a partially cutaway side view of a lead including a defibrillation coil illustrating another embodiment of the current invention.





FIG. 9

is a side cutaway view of a lead inserted in a sleeve formed in accordance with the current invention.











DETAILED DESCRIPTIONS OF THE DRAWINGS





FIG. 1

is a plan view of a defibrillation lead of the type in which the present invention may usefully be practiced. It will be understood the lead of

FIG. 1

is merely exemplary, and the present invention may also be usefully practiced in the context of any other implantable medical electrical leads or implantable medical devices generally. The lead of

FIG. 1

is provided with an elongated insulative lead body


10


, preferably fabricated of silicone rubber, polyurethane or other biocompatible, compressible elastomer. The distal end of the lead carries an elongated defibrillation electrode


12


, a ring electrode


14


, and a tip electrode


16


. A fixation mechanism such as tines


18


may be provided to maintain electrode


16


in contact with body tissue. Electrodes


12


,


14


, and


16


may correspond to any conventionally available pacing and defibrillation electrodes.




The proximal end of the lead carries a connector assembly that includes a molded lead bifurcation sleeve


20


. This bifurcation sleeve joins the lead body


10


to two different connectors at the lead proximal end. The first connector is a bipolar, in-line assembly


24


, generally corresponding to the IS-1 connector standard for pacing leads. This connector


24


is provided with a first and second set of sealing rings


28


and


34


, and connector pin


36


. Connector pin


36


may be coupled to tip electrode


16


via an internal conductor, whereas the connector ring may be coupled in a similar manner to ring electrode


14


. The second connector, which may correspond to a standard such as DF-1, is provided to couple connector pin


36


to defibrillation electrode


12


.




Although the lead of

FIG. 1

is shown with a single defibrillation electrode


12


, the lead may further include more than one defibrillation electrode by locating additional electrodes sequentially along the length of the lead body.





FIG. 2

is an exploded side cutaway view of a defibrillation coil including silicone backfill to prevent tissue in-growth in a manner known in the art. As discussed above, prior art leads utilize an injected silicone rubber layer


200


applied between the spaces of the individual electrode coils


202


to prohibit tissue attachment around these coils. These coils may be located within a grooved region


204


of the lead


206


to provide a structure that is isodiametric, as shown in FIG.


2


. Alternatively, the coils may be located around the outer diameter of the lead such that the coil has a diameter that is larger than the diameter of the remainder of the lead.




The injection of silicone around the defibrillation coils involves a process that must be closely controlled. If too much silicone is injected around the coils, the conductive capability of the defibrillation electrode may be comprised. If too little silicone is injected, tissue in-growth may not be prevented, making lead extraction difficult or impossible.





FIG. 3

is a side cutaway view of one embodiment of a lead


300


utilizing the current invention. The lead body


302


includes a grooved region


304


that retains defibrillation coil


306


which may be of any construction known in the art. Adjacent defibrillation coil is a layer


308


of a porous PTFE having a pore size that is adequately small to preclude tissue in-growth. A material particularly suited for this purpose is expanded PTFE (e-PTFE), which is known to be chemically inert and biocompatible. In one embodiment, the pore size of the porous PTFE material of layer


308


is less than 10 microns. In a preferred embodiment, the pore size is between 3 and 5 microns to prevent substantially all tissue growth associated with coil


306


.




As noted above, the porous PTFE used in the construction of the inventive lead is preferably porous expanded PTFE (e-PTFE) having a microstructure of nodes interconnected by fibrils. Porous expanded PTFE may be manufactured according to the processes disclosed in U.S. Pat. Nos. 4,187,390, 3,953,566, 5,609,622, 4,096,227, 4,187,390, 4,985,296 and 5,148,806, all incorporated herein by reference. The porous PTFE may contain a carbon filler used for the surface of the conductive portion of the electrode. As is known in the art, porous PTFE may be specified by pore size, which, in turn, is generally described as a function of the fibril length of the material. The fibril length of porous expanded PTFE is measured as taught by U.S. Pat. No. 4,972,846.




Returning now to

FIG. 3

, an outer layer


310


of porous PTFE such as e-PTFE surrounds inner layer


308


. The material of layer


310


has a pore size (fibril length) adapted to selectively promote tissue in-growth. In one embodiment, the pore size of the material included in layer


310


is between 20 and 50 microns. The tissue in-growth promoted by the pore size of layer


310


is controlled such that the defibrillation coil is stabilized at a desired implant site by the tissue attached to this layer. However, tissue is prevented from adhering to any part of the coil structure itself by inner layer


308


so that tissue in-growth around the coil does not prohibit lead extraction. Because both layers


310


and


308


are porous, body fluids that are retained within the pores allows these layers to conduct electricity when the lead is implanted.




According to one aspect of the invention, layer


310


may be treated, or infused, with of drugs to minimize thrombosis as well as to reduce the threat of infection.




In one embodiment, layers


308


and


310


are cut from tubing commercially-available from the Zeus Corporation of Orangeburg, S.C. In this embodiment, each of the layers may be very thin, having a thickness of 50 microns or less, and preferably less than 25 microns.




The tubing of both layers may be sized to fit grooved region


304


. Layers


308


and


310


may be held in place using any type of biocompatible adhesive such as silicone adhesive. Alternatively, the adhesive may be a thermoplastic adhesive such as a dispersion of water and fluorinated ethylene propylene in the form of a particulate and a surfactant. A layer of non-conductive polymeric adhesive produces good adhesion with little additional electrical resistance. Alternatively, conductive fillers such as carbon black may be added to this dispersion in order to make it electrically conductive. This dispersion, both with, or without conductive fillers, may be used to adhere the electrically conductive polymeric material of the electrode surface to the underlying coil


306


.




Layers


308


and


310


may be bonded together using an ultrasonic welding process, as is known in the art. In another embodiment tubing may be sized larger than grooved region


304


such that edges of layers


308


and


310


extend over regions


312


A and


314


A of the lead body.




According to one construction of a lead employing the current invention, sleeves


312


and


314


, which may be formed of silicone or other biocompatible material, may be applied over the edges of the layers


308


and


310


and held in place by an adhesive to further secure these structures. Alternatively, a tubing structure, including heat-shrinkable tubing, may be used for this purpose. Bonding of sleeves


312


and


314


to the lead body may be enhanced by etching regions


312


A and


314


A of the lead body


302


using a plasma or corona etching process, or by using a chemical surface modification process such as is commercially performed by the Zeus Corporation. This creates a surface that more readily adheres to adjacent materials, allowing a superior bond to form between the lead body surface and the sleeves


312


and


314


. Yet another approach to improving the bond involves utilizing an ultrasonic welding process to bond the sleeves to the surface of lead body


302


.




It may be noted that the body of lead


302


may be of any conventional lead construction known in the art in the manner discussed above. For example, the exterior of lead may be formed of a silicone, a polyurethane, or a non-porous or dense PTFE. These materials do not promote tissue in-growth in the manner discussed above with respect to porous PTFE. For this reason, only limited tissue in-growth occurs along the primary portion of the lead body, with more substantial in-growth being selectively promoted only where an additional degree of stability is desired, as at the electrode.





FIG. 4

is a cross-sectional view of the lead of

FIG. 3

at line


4





4


. This view shows grooved region


304


surrounded by coil


306


. The inner and outer porous PTFE layers


308


and


310


, respectively, encircle the coil


306


. In one embodiment, sleeve


312


may further surround layer


308


.





FIG. 5

is an alternative embodiment of a lead according to the current invention. In this embodiment, lead body


500


does not include a grooved portion. Instead, coil


502


encircles the outer diameter of the lead body. According to one method of manufacturing this embodiment, tubing may be employed to form porous PTFE layers


504


and


506


. Inner layer


504


is formed of a porous PTFE tubing having a pore size of less than 10 microns, whereas the tubing of layer


506


is formed of porous PTFE having a pore size of between 20 and 50 microns in the manner discussed above. Such tubing is commercially available from the Zeus Corporation. The tubing may be heat-shrinkable, making use of an adhesive unnecessary. Alternatively, a medical grade adhesive may be utilized to affix layers


504


and


506


to the lead. The lead may further include sleeves


510


and


512


encircling the edges of the porous PTFE layers


504


and


506


to aid in attaching these layers to the lead body


500


.




In yet another embodiment of lead


302


or


502


, the layers of porous PTFE may be formed of a tape that may be applied to the surface of the electrical conductor. For example, a porous PTFE may be formed into a thin sheet. A layer of continuous or discontinuous thermoplastic adhesive may be applied to one side of the sheet, and the material may then be cut to form tape. The tape forming the inner layer is wrapped about the conductor wire surface with the adhesive side of the composite contacting the conductor. In one embodiment, the conductor wire surface is helically wrapped with the tape, and is then heated to a temperature above the melt point of the thermoplastic adhesive to cause effective bonding of the composite tape to the conductor surface. This process may be repeated with a second tape formed using a less-dense PTFE.




The above-described embodiments contemplate the use of two individual layers of porous PTFE to selectively control tissue in-growth. An inner layer prevents substantially all in-growth, while the surrounding, outer layer selectively promotes in-growth. In one embodiment of the invention, the two layers are combined into a composite structure that has a more porous material exposed on a first surface adapted to be located adjacent tissue, and a less porous, more dense material on a second surface adapted to be situated adjacent the electrode. For example, a heat-shrinkable, tubular structure that is adapted to be positioned around defibrillation electrode


12


may have an outer surface formed of a more porous e-PTFE, with the inner surface coated with a less porous e-PTFE. Such a structure may be formed initially of a dense e-PTFE. The outer surface may then be altered to be more porous by selectably removing fibrils from the outer surface using the techniques described in U.S. Pat. No. 5,462,781 incorporated herein by reference.





FIG. 6

is a diagram depicting two defibrillation leads placed within a human heart, and illustrates yet another advantage of the current invention. A first lead


600


carries a defibrillation electrode


602


that is located within the right atrium, wherein a second lead


604


carries an electrode


606


positioned in the right ventricle. Both leads are shown coupled to implantable pulse generator


601


. Electrode


602


is in close proximity to the body of lead


604


such that abrasion of the lead outer surface by the coil


602


is likely. This abrasion may be minimized using the current inventive lead, which provides multiple layers of the porous PTFE material over the electrode. These layers form a lubricious, non-abrasive surface over electrode


602


such that wear on adjacent lead structures may be substantially eliminated. This is important for chronically-implanted leads adapted for long-term use.





FIG. 7

illustrates a subcutaneous defibrillation electrode array that is particularly adapted for use with the current invention. Such an electrode array is designed to be positioned under a patient's skin, and may be used in conjunction with the system and method described in U.S. Pat. No. 5,314,430. The electrode array includes multiple elongated lead structures


700


,


702


, and


704


that each couples to an implantable pulse generator using a common connector


706


. Although the exemplary electrode array shows three lead structures, more than three may be provided. Each of the lead structures carries a respective defibrillation electrode shown as electrodes


700


A through


704


A. According to the configuration of

FIG. 7

, common connector


706


and the electrodes of shorter leads


700


and


704


may be implanted under the skin of a patient's chest, for example. Longer lead


702


may be tunneled under the skin around the patient's side, and extending under the skin of the patient's back. This positioning of the electrodes both on the chest and back of the patient allows a lower defibrillation threshold to be achieved. However, the configuration also promotes lead abrasion. For example, the electrode coils on leads


700


and


704


may abrade the surface of lead


702


. The current invention may be readily adapted for use with a subcutaneous defibrillation electrode array of the type shown in

FIG. 7

so that abrasion is reduced.




Variations and modifications to the present invention may be possible given the above disclosure. For example, a composite structure comprising a first dense layer of porous PTFE surrounded by a second, less dense, layer of porous PTFE may be positioned adjacent to an outer surface of any implantable medical device, and is not limited to use with electrodes carried on leads. For example, the enclosure (can) of an implantable medical device may employ the current invention system to promote tissue in-growth over a portion of the can, if desired. Alternatively, predetermined portions of the lead body itself may employ the inventive system and method to selectively promote tissue in-growth.




According to another manner of practicing the current invention, the various layers of PTFE may be staggered such that only a portion of the first, porous layer of PTFE is coated by an outer layer of less dense PTFE. In this manner, tissue in-growth is only selectively promoted at predetermined areas of the device, while being entirely absent at other areas of the device. For example, a medical lead may be coated with a layer of more dense e-PTFE over the entire length of the lead. The lead may then be coated with an additional outer layer formed of a less dense material over only selected portions of the lead to allow selective tissue in-growth in only certain areas, such as adjacent to an electrode to stabilize electrode positioning. This enables lead extraction to be accomplished with less tissue damage.




According to yet another aspect of the invention, a sleeve having two layers of porous PTFE according to the current invention may be provided to encase a medical device. The sleeve may be formed of an inner layer of a porous PTFE having a pore size adapted to prevent substantially all tissue in-growth. An outer layer formed of the less porous PTFE in the manner discussed above may be provided over the entire surface, or only over predetermined portions, of the inner layer to selectively promote tissue in-growth. The sleeve may be positioned over the implantable medical device prior to implant. After implant, tissue in-growth occurs at the predetermined portions of the sleeve wherein the more porous PTFE material resides. No tissue attaches to the medical device itself. Therefore, the medical device may be readily replaced. For example, a lead may be withdrawn from the sleeve and a new lead inserted into the sleeve without disrupting the in-grown tissue, greatly simplifying the lead extraction process. Moreover, the stability of the implanted medical device is enhanced by the existence of the in-grown tissue and the sleeve. It may be noted that because the sleeve is porous, current is conducted through the sleeve when the pores are filled with fluid. Therefore, a lead inserted into a sleeve and implanted within a patient may deliver electrical stimulation to the patient through the PTFE layers.





FIG. 8

is a partially cutaway side view of a lead


800


including a defibrillation coil


802


illustrating another embodiment of the current invention. In this embodiment, defibrillation coil is in contact with a first layer


804


of e-PTFE that is very porous, having a pore size which may range between 50 and 100 microns. In one embodiment, this first layer


804


may be 50 microns or more thick. Because of the very porous nature of this first layer, the first layer is able to absorb gas such as oxygen that is created by electrolysis during the delivery of electrical stimulation to the body. In other words, the porous layer bleeds the gas created during the delivery of a cardioversion/defibrillation shock from the surface of the electrode


802


. This is important because applicants have shown that the build-up of gas around an electrode increases the effective impedance of the surrounding area, decreasing the current delivered during the shock pulses. This could affect shock efficacy. Providing the very porous layer prevents this increase of impedance from occurring.




The very porous first layer


804


may be coated with a second layer


806


of porous material having a pore size that substantially prevents all tissue in-growth in the manner discussed above. Layer


806


has a thickness which may be relatively small in comparison to layer


804


. For example, the pore size of this layer may be 10 microns or less, with a layer thickness that may be 10 microns or less. Providing a second layer that is relatively thin reduces overall lead dimensions.




The inventive lead of

FIG. 8

may, but need not, also include yet a third layer


806


of biocompatible material. This third layer may include predetermined portions


810


of porous material such as e-PTFE having a pore size to selectively promote tissue in-growth in a manner discussed above. For example, the pore size may range between 20 and 50 microns. This third layer therefore serves to maintain lead stability while not promoting in-growth to the extent that would hamper lead extraction. In one embodiment, this layer is as thin as possible, with a thickness of 50 microns or less, to reduce overall lead size.




The lead of

FIG. 8

may be constructed using any of the methods and materials, and may further include any of the aspects, of the inventive leads discussed above.





FIG. 9

is a side cutaway view of a lead inserted in a sleeve formed in accordance with the current invention. Sleeve


900


includes an inner layer


902


of porous PTFE having a very small pore size to prevent substantially all tissue in-growth. An outer layer of PTFE may then be provided having a larger pore size. This outer layer may be formed over the inner layer


902


at selected locations


904


in the manner shown in

FIG. 9

, or over the entire sleeve. In one embodiment, the selected locations


904


are created by selectively removing fibrils from the more dense inner layer


902


in the manner discussed above. In another embodiment, cutaway regions are formed in the inner layer


902


into which a less dense PTFE material is inlaid and affixed with medical grade, electrically-conductive, adhesive.





FIG. 9

further illustrates a lead


908


inserted into sleeve


900


. Lead may have one or more electrodes such as distal tip electrode


910


which may provide electrical stimulation to a body through the sleeve when the sleeve pores are filled with body fluid. The lead could also carry any of the many physiological sensors known in the art for monitoring physiological signals. In one embodiment, the proximal end of lead


912


includes fastening means such as small ring members


914


for fastening the sleeve to the lead as with surgical suture material


916


, for example. Any other fastening means could be used for this purpose. Fastening means may be readily detached prior to the lead extraction procedure. In another embodiment, sleeve


900


is sized to only cover the lead distal end portion. It will be understood the sleeve length could be varied in any manner desired.




The sleeve of

FIG. 9

may, in one embodiment, include an additional inner layer adapted to be positioned adjacent the lead formed of a porous PTFE having a pore size adapted to bleed gas away from the surface of the lead in the manner described above. If desired, this sleeve may include only the additional inner layer and the more dense layer


902


, while omitting the less-dense layers


904


that are adapted to selectively promote tissue in-growth.




As noted above, although

FIG. 9

illustrates use of a sleeve with a lead, such a sleeve may be adapted for use with any medical device adapted for implantation within a body. All such variations and modifications are intended to be within the scope of the invention claimed by this letters patent.




In conjunction with the above disclosure,



Claims
  • 1. A system for use with an implantable medical device (IMD) to selectively promote tissue in-growth, comprising:a lead having a lead body including an outer surface; an electrode having an electrode surface and positioned along the lead body; a first inner layer of porous Polytetrafluoroethylene (PTFE) adjacent to the electrode, the first inner layer of porous PTFE having a fibril length adapted to prevent substantially all tissue in-growth along the electrode surface; at least one outer layer of porous PTFE adjacent to at least a predetermined portion of the first inner layer, the outer layer of porous PTFE having a fibril length adapted to selectively promote tissue in-growth along the lead body adjacent to the electrode; and a sleeve member fixedly engaged against the outer surface of the lead body and extending over and fixedly engaging the first inner layer and the at least one outer layer within the lead body, wherein the first inner layer, the at least one outer layer, and the electrode are isodiametric with the outer surface of the lead body.
  • 2. The system of claim 1, wherein the first inner layer of porous PTFE is an expanded PTFE (e-PTFE).
  • 3. The system of claim 2, wherein the at least one outer layer of porous PTFE is an expanded PTFE (e-PTFE).
  • 4. The system of claim 3, wherein the first inner layer of porous PTFE has a fibril length of less than 10 microns.
  • 5. The system of claim 4, wherein the at least one outer layer of porous PTFE has a fibril length of between 20 and 50 microns.
  • 6. The system of claim 5 wherein the first inner layer and the at least one outer layer of porous PTFE are formed of porous PTFE tubing.
  • 7. The system of claim 6 wherein the porous PTFE tubing is heat-shrink tubing.
  • 8. The system of claim 5 wherein the first inner layer and the at least one outer layer are formed of tape.
  • 9. The system of claim 5 wherein the at least one outer layer of porous PTFE is formed by removing a predetermined number of fibrils from the predetermined portion of the first inner layer.
  • 10. The system of claim 1 wherein the outer layer is coextensive with the first inner layer.
  • 11. The system of claim 1, wherein the first inner layer is adjacent to the entire surface of the electrode to prevent substantially all tissue in-growth around the electrode.
  • 12. The system of claim 1, wherein the electrode is a defibrillation coil, and the first inner layer and the at least one outer layer of porous PTFE are isodiametric with the outer surface of the medical electrical lead.
  • 13. A system for use with an implantable medical device (IMD) to selectively promote tissue in-growth, comprising:a lead having a lead body; an electrode having an electrode surface and positioned along the lead body; a first inner layer of porous Polytetrafluoroethylene (PTFE) adjacent to the electrode, the first inner layer of porous PTFE having a fibril length adapted to prevent substantially all tissue in-growth along the electrode surface; at least one outer layer of porous PTFE adjacent to at least a predetermined portion of the first layer, the outer layer of porous PTFE having a fibril length adapted to selectively promote tissue in-growth along the lead body adjacent to the electrode; and a sleeve member fixedly engaging the first inner layer and the at least one outer layer with the lead body, wherein the lead body includes an outer surface and the electrode is positioned along the outer surface of the lead body.
RELATED APPLICATIONS

This application claims priority to provisionally-filed U.S. patent application Ser. No. 60/258,647 filed Dec. 28, 2000 entitled “Implantable Medical Device Adapted to Promote Selected Tissue In-Growth and Method for Making the Same”, which is incorporated herein by reference in its entirety.

US Referenced Citations (26)
Number Name Date Kind
3953566 Gore Apr 1976 A
4096227 Gore Jun 1978 A
4161952 Kinney et al. Jul 1979 A
4187390 Gore Feb 1980 A
4573480 Hirschberg Mar 1986 A
4934049 Kiekhafer et al. Jun 1990 A
4972846 Owens et al. Nov 1990 A
4985296 Mortimer, Jr. Jan 1991 A
5035713 Friis Jul 1991 A
5090422 Dahl et al. Feb 1992 A
5148806 Fukui et al. Sep 1992 A
5314430 Bardy May 1994 A
5358516 Myers et al. Oct 1994 A
5437900 Kuzowski Aug 1995 A
5462781 Zukowski Oct 1995 A
5466252 Soukup et al. Nov 1995 A
5609622 Soukup et al. Mar 1997 A
5626561 Butler et al. May 1997 A
5716394 Bruchman et al. Feb 1998 A
5782898 Dahl et al. Jul 1998 A
5833664 Seare, Jr. Nov 1998 A
5957970 Shoberg et al. Sep 1999 A
6058332 Dahl May 2000 A
6330464 Colvin et al. Dec 2001 B1
6406420 McCarthy et al. Jun 2002 B1
6546292 Steinhaus et al. Apr 2003 B1
Provisional Applications (1)
Number Date Country
60/258647 Dec 2000 US