The present invention relates in general to the field of composite structures, and more particularly, to a method of replacing dams with an innovative ply stackup that creates a profile taper.
Composite materials have been employed in the fabrication of a wide variety of components for aircraft, e.g., rotorcraft rotor system components. In comparison to a machined metal forging, composite materials have more favorable fatigue characteristics resulting in longer useful life.
Commonly, open-faced tooling is used to form composite parts, in which dams are positioned around the profile of the part.
Another manner in which composite parts are made is by curing in a rigid, closed mold that forms the overall shape of the rotor yoke. One of the problems encountered concerning large parts made in a rigid, closed mold is the distortion or “marcelling” of the fibers in the composite part during the curing process. Because the uncured part is forced to conform to the cavity in the mold, mechanical stresses can be induced in the uncured part. The fibers are substantially unconstrained during certain portions of the curing cycle when the resin matrix in which the fibers are disposed is in a semi-liquid or liquid state. The induced stress in the part is relieved via movement or distortion of the fibers within the resin matrix. The fibers can be captured in their distorted or marcelled state when the resin crosslinks in thermosetting composite materials or when the resin is cooled in thermoplastic composite materials.
As such, a need remains for improved methods for making composite parts that eliminate the problems of the prior art.
In one embodiment the present invention includes a method of preparing a composite structure comprising: placing a first ply of a fibrous material with a curable material on a layup tool; adding one or more additional plies on the first ply, wherein each of the one or more additional plies has a perimeter that is different in size around the perimeter than a previous ply to form a taper; and curing the composite structure, wherein the curable material is selected to minimize, limit, or eliminate the outflow of the curable material along the perimeter of the composite structure during the curing step. In one aspect, the perimeter of each of the one or more additional plies is smaller than the previous ply by about a thickness of the previous ply to form a tapered edge about the perimeter of the composite structure. In another aspect, the perimeter of each of the one or more additional plies is smaller than the previous ply and the taper has a 5 to 90 degree taper, including fractions of degrees, along one or more edges of the composite structure. In another aspect, the perimeter of each of the one or more additional plies is smaller than the previous ply and the taper has a 28 to 60 degree taper along one or more edges of the composite structure. In another aspect, the taper comprises a linear taper, a concave taper, a convex taper, a variable shape taper, a complex taper, a pyramidal taper, a trapezoidal taper, an inverse taper, or multiple tapers. In another aspect, the curable material is defined further as a low-flow curable resin that generally does not flow beyond the perimeter of the composite structure under vacuum during the curing step. In another aspect, the fibrous material comprises at least one of a glass fiber, a carbon fiber, a natural fiber, a cellulose fiber, a chemical fiber, a plastic fiber, a ceramic fiber, or a polymeric fiber. In another aspect, the method further comprises cooling the composite structure; transferring the cured composite structure to a machining tool configured to machine the stack; and constructing a final composite component by machining the cured composite structure using the machining tool. In another aspect, the method further comprises forming the composite structure by placing a semi-rigid caul on top of the plies to apply specific pressures at specific locations of the composite structure and without one or more tooling dams along the edge that forms the taper. In another aspect, the composite structure has no external support along one or more sides of the composite structure during the curing step except a vacuum bag or layer. In another aspect, the method further comprises cutting the first ply and the one or more additional plies prior to assembly. In another aspect, the method further comprises cutting the first ply and the one or more additional plies in situ. In another aspect, the method further comprises curing the composite structure includes applying at least one of heat, pressure, and time. In another aspect, the plies can be laid up by hand or by machine, but not a fiber placement machine.
Another aspect of the present invention includes a method of preparing a composite structure comprising: obtaining a plurality of fibrous material impregnated plies with a low-flow curable resin or a thermoplastic material, wherein each of the plies has a perimeter and a thickness, wherein each additional ply after the first ply has a perimeter that is different in a total surface area and that forms a tapered edge that is a linear taper, a concave taper, a convex taper, a variable shape taper, a complex taper, a pyramidal taper, a trapezoidal taper, an inverse taper, or has multiple tapers; and curing the composite structure under vacuum and heat conditions that cure the resin, wherein the reduced-flow resin is selected to minimize, limit, or eliminate the outflow of the resin along the perimeter of each ply of the composite structure during the curing step. In one aspect, the perimeter of each of the one or more additional plies has a perimeter that is smaller than the previous ply to form a tapered edge with about a 45 degree taper along one or more edges of the composite structure. In another aspect, the low-flow curable resin or the thermoplastic material comprises a resin that generally does not flow beyond the perimeter of the composite structure under vacuum during the curing step. In another aspect, the fibrous material comprises at least one of a glass fiber, a carbon fiber, a natural fiber, a cellulose fiber, a chemical fiber, a plastic fiber, a ceramic fiber, or a polymeric fiber. In another aspect, the method further comprises cooling the composite structure; transferring the cured composite structure to a machining tool configured to machine the stack; and constructing a final composite component by machining the cured composite structure using the machining tool. In another aspect, the method further comprises forming the composite structure by placing a semi-rigid caul on top of the plies to apply specific pressures at specific locations of the composite structure and without one or more tooling dams. In another aspect, the composite structure has no external support along one or more sides of the composite structure or a top of the composite structure during the curing step except a vacuum bag or layer. In another aspect, the plies of the composite structure are pre-cut prior to assembly.
In yet another embodiment the present invention includes a method of preparing a composite structure without a tooling dam comprising: obtaining a plurality of fibrous material impregnated plies with a low-flow curable resin or a thermo-plastic material, wherein each of the plies has a perimeter and a thickness, wherein each additional ply after the first ply has a perimeter or a surface area that is smaller or larger than a perimeter or a surface area of a previous ply, wherein each ply has about the same thickness, wherein the sides of the plies forms a tapered edge between about 5 and 90 degrees or has a complex shape; placing a rigid or semi-rigid caul on top of the plies of the composite structure; and curing the composite structure under vacuum and heat conditions that cure the resin or thermo-plastic material, wherein the low-flow curable resin or thermo-plastic material is selected to minimize, limit, or eliminate the outflow of the resin along the perimeter of each ply of the composite structure during the curing step. In another aspect, the taper comprises a linear taper, a concave taper, a convex taper, a variable shape taper, a complex taper, a pyramidal taper, a trapezoidal taper, an inverse taper, or multiple tapers.
The novel features believed characteristic of the present application are set forth in the appended claims. However, the system itself, as well as a preferred mode of use, and further objectives and advantages thereof, will best be understood by reference to the following detailed description when read in conjunction with the accompanying drawings, in which the leftmost significant digit(s) in the reference numerals denote(s) the first figure in which the respective reference numerals appear, wherein:
While the system of the present application is susceptible to various modifications and alternative forms, specific embodiments thereof have been shown by way of example in the drawings and are herein described in detail. It should be understood, however, that the description herein of specific embodiments is not intended to limit the present application to the particular forms disclosed, but on the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the present application as defined by the appended claims.
To facilitate the understanding of this invention, a number of terms are defined below. Terms defined herein have meanings as commonly understood by a person of ordinary skill in the areas relevant to the present invention. Terms such as “a”, “an” and “the” are not intended to refer to only a singular entity, but include the general class of which a specific example may be used for illustration. The terminology herein is used to describe specific embodiments of the invention, but their usage does not delimit the invention, except as outlined in the claims.
Illustrative embodiments of the present application are described below. In the interest of clarity, not all features of an actual implementation are described in this specification. It will of course be appreciated that in the development of any such actual embodiment, numerous implementation-specific decisions must be made to achieve the developer's specific goals, such as compliance with system-related and business-related constraints, which will vary from one implementation to another. Moreover, it will be appreciated that such a development effort might be complex and time-consuming but would nevertheless be a routine undertaking for those of ordinary skill in the art having the benefit of this disclosure.
As used herein, reference may be made to the spatial relationships between various components and to the spatial orientation of various aspects of components as the devices are depicted in the attached drawings. However, as will be recognized by those skilled in the art after a complete reading of the present application, the devices, members, apparatuses, etc. described herein may be positioned in any desired orientation. Thus, the use of terms such as “above,” “below,” “upper,” “lower,” or other like terms to describe a spatial relationship between various components or to describe the spatial orientation of aspects of such components should be understood to describe a relative relationship between the components or a spatial orientation of aspects of such components, respectively, as the device described herein may be oriented in any desired direction.
This invention is generally in the field of composite parts or structures, e.g., those that are assembled by hand or by machine, and relates specifically to flexible design method for composite parts or structures that results in use of fewer tools in the manufacturing, shortens program schedules, and reduces cost. This invention can be used on all composite parts thick or thin that uses open cavity tooling. In certain non-limiting examples, the method is suited for thicker composite parts that have hundreds of plies.
The system of the present application can be used to make, e.g., a composite rotor yoke for a rotorcraft. In one embodiment, the composite rotor yoke is laid-up using an automated fiber placement process, but may also be laid-up by hand. After curing, the cured composite rotor yoke may be machined to add any desired features.
Hard tools, a.k.a dams, placed around the perimeter of composite parts produce net molded part planar geometry. In certain embodiments dams are not necessarily hard and can be made of silicon or other rubbery materials. Precision machining of such tools consumes valuable schedule and significant budget for most composite development programs. In a typical development program, machining of high dollar and long lead-time tools commences after successful completion of critical-design-review (CDR) of the parts. After that point, the part geometry is fixed, and any changes to the part geometry that would change the tool geometry are discouraged. This invention disclosure proposes a design method that eliminates the need for perimeter tooling or coffins for composite part manufacturing. By doing so, it eliminates those physical toolings from the part build tooling family; it shortens the program schedule, reduces the budget requirement and makes design changes viable after CDR without imparting negative impact to the program. It also introduces additional error proofing during layup by preventing ply layup at wrong levels.
The present invention incorporates a tapered edge to the composite part as a design improvement (feature) that eliminates the need for dams. Previous methods have relied on metallic tooling dams, which introduce additional complexities during cure. Using a yoke as a non-limiting example, the present invention includes a novel tooling approach that uses tapered edges to achieve the same effect as a dam without the use of an actual dam tool.
Uncured low-flow composite materials for use with the present invention include, but are not limited to, glass or other fibers disposed in an uncured epoxy, in the form of a prepreg, although the present application contemplates other materials for the composite structure, such as a molded rotor yoke. The present invention can also use thermo-plastic materials. An example of low-flow composite material is HexPly® 8552 made by Hexcel Composites. For this application, the term “prepreg” is typically sheets of fibers impregnated in uncured epoxy or adhesive. Uncured low-flow composite material can then be cut to size and laid onto the tool, either by hand or with fiber placement machine. Low-flow composite material can be used in the absence of high-flow adhesive, and could be any composite material that has such a high viscosity that could possibly produce marcels when subjected to a curing process inside, e.g., a closed cavity tool. The method of the present invention allows for the formation of the composite structure without the use of any tooling dams. Further, the present invention is able to eliminate “marcels”, which are wrinkles in the fiber structure of a composite that severely compromise the structural integrity of a composite part. Marcels are often created when low-flow composite material, if used in the absence of high-flow adhesive, is forced to conform to inside surfaces of a closed cavity tool, causing the highly viscous epoxy to flow and distort fibers. Complete curing of the distorted fibers, or marcels, causes the fibers to be permanently fixed in the marcelled state. In certain embodiments, a low flow resin system is not required with the present invention. For example, a high flow resin system can also be used with the present invention.
The method can also be modified for the use of high-flow materials. For high-flow materials, the process takes into account resin flow or resin bleed to help extract volatiles from a part during curing. The process is modified to include tooling and bagging that allows the resin to flow out and away from the part as it is cured. All other tooling and the process for low-flow, intermediate-flow, and high-flow material processing for use with the present invention is the same.
As such, the skilled artisan will understand that certain specific materials are listed herein, however, following the teachings herein other equivalent materials from different sources or manufacturers can be used with the present invention. A non-limiting material for use with the present invention, and for which there are numerous known equivalents includes, for example, the low-flow material: HEXPLY® 8552. A non-limiting example of a high-flow material for use with the present invention, and for which there are numerous known equivalents includes, for example, the high-flow material: CYCOM® E773. In another non-limiting example, an intermediate-flow material can be used. For example, certain intermediate-flow materials begin as a high-flow material, that when exposed to high temperature, becomes intermediate-flow, and eventually a low flow material. In this example, the temperature will generally be near and above the resin glass-transition temperature. The present invention can also use a wet layup, which can be done with any fiber and/or any resin. The wet layup then follows the same stacking and methodology taught herein. A non-limiting example of a thermoplastic, and for which there are numerous known equivalents includes, for example, EPLASTICS® PEEK. Again, the skilled artisan will understand how to select and replace materials within the scope of the invention.
The skilled artisan will also recognize that each of the above non-limiting examples can be considered tape, where all the fibers run in the same direction in a given ply, fabric, where there is a weave pattern of fibers, or chopped fiber, which is either tape or fabric material chopped into pieces and randomly placed to create a randomized ply. Depending on the application, the skilled artisan will recognize that the type and orientation of the fibers in each of the plies can all be of the same type or can be of different combinations depending on the final mechanical characteristics sought in the composite structure.
One aspect of the selection process of the low-flow resin for use in the composite structure is the reduction or elimination of any bleeding of the resin during the cure process. However, as shown in
For example, in
Referring to
It is contemplated that any embodiment discussed in this specification can be implemented with respect to any method of the invention, and vice versa. Furthermore, various fibrous materials, resins, adhesives, thermoplastic materials and the like can be used to achieve the methods of the invention.
It will be understood that particular embodiments described herein are shown by way of illustration and not as limitations of the invention. The principal features of this invention can be employed in various embodiments without departing from the scope of the invention. Those skilled in the art will recognize, or be able to ascertain using no more than routine experimentation, numerous equivalents to the specific procedures described herein. Such equivalents are considered to be within the scope of this invention and are covered by the claims.
All publications and patent applications mentioned in the specification are indicative of the level of skill of those skilled in the art to which this invention pertains. All publications and patent applications are herein incorporated by reference to the same extent as if each individual publication or patent application was specifically and individually indicated to be incorporated by reference.
The use of the word “a” or “an” when used in conjunction with the term “comprising” in the claims and/or the specification may mean “one,” but it is also consistent with the meaning of “one or more,” “at least one,” and “one or more than one.” The use of the term “or” in the claims is used to mean “and/or” unless explicitly indicated to refer to alternatives only or the alternatives are mutually exclusive, although the disclosure supports a definition that refers to only alternatives and “and/or.” Throughout this application, the term “about” is used to indicate that a value includes the inherent variation of error for the device, the method being employed to determine the value, or the variation that exists among the study subjects.
As used in this specification and claim(s), the words “comprising” (and any form of comprising, such as “comprise” and “comprises”), “having” (and any form of having, such as “have” and “has”), “including” (and any form of including, such as “includes” and “include”) or “containing” (and any form of containing, such as “contains” and “contain”) are inclusive or open-ended and do not exclude additional, unrecited elements or method steps. In embodiments of any of the compositions and methods provided herein, “comprising” may be replaced with “consisting essentially of” or “consisting of”. As used herein, the phrase “consisting essentially of” requires the specified integer(s) or steps as well as those that do not materially affect the character or function of the claimed invention. As used herein, the term “consisting” is used to indicate the presence of the recited integer (e.g., a feature, an element, a characteristic, a property, a method/process step or a limitation) or group of integers (e.g., feature(s), element(s), characteristic(s), propertie(s), method/process steps or limitation(s)) only.
The term “or combinations thereof” as used herein refers to all permutations and combinations of the listed items preceding the term. For example, “A, B, C, or combinations thereof” is intended to include at least one of: A, B, C, AB, AC, BC, or ABC, and if order is important in a particular context, also BA, CA, CB, CBA, BCA, ACB, BAC, or CAB. Continuing with this example, expressly included are combinations that contain repeats of one or more item or term, such as BB, AAA, AB, BBC, AAABCCCC, CBBAAA, CABABB, and so forth. The skilled artisan will understand that typically there is no limit on the number of items or terms in any combination, unless otherwise apparent from the context.
As used herein, words of approximation such as, without limitation, “about”, “substantial” or “substantially” refers to a condition that when so modified is understood to not necessarily be absolute or perfect but would be considered close enough to those of ordinary skill in the art to warrant designating the condition as being present. The extent to which the description may vary will depend on how great a change can be instituted and still have one of ordinary skilled in the art recognize the modified feature as still having the required characteristics and capabilities of the unmodified feature. In general, but subject to the preceding discussion, a numerical value herein that is modified by a word of approximation such as “about” may vary from the stated value by at least ±1, 2, 3, 4, 5, 6, 7, 10, 12 or 15% from the stated value. For use with the present invention, when referring to the taper, whether it is a symmetrical or asymmetrical (or complex) taper, the angle of the taper can be anything between 5 and 90 degrees, and can include fractions of degrees, in this case, ±1, 2, 3, 4, 5, 6, 7, 10, 12 or 15% of the listed angle.
All of the methods disclosed and claimed herein can be made and executed without undue experimentation in light of the present disclosure. While the methods of this invention have been described in terms of preferred embodiments, it will be apparent to those of skill in the art that variations may be applied to the methods and in the steps or in the sequence of steps of the method described herein without departing from the concept, spirit and scope of the invention. All such similar substitutes and modifications apparent to those skilled in the art are deemed to be within the spirit, scope and concept of the invention as defined by the appended claims.
Number | Name | Date | Kind |
---|---|---|---|
4568245 | Hibyan | Feb 1986 | A |
5954898 | McKague | Sep 1999 | A |
6168358 | Engwall et al. | Jan 2001 | B1 |
20080145615 | Jacobsen et al. | Jun 2008 | A1 |
20090206202 | Bolukbasi | Aug 2009 | A1 |
20090246446 | Backhouse | Oct 2009 | A1 |
20090261199 | McCarville | Oct 2009 | A1 |
20100221119 | Baskin | Sep 2010 | A1 |
20110116936 | Hiros | May 2011 | A1 |
20120201683 | Stamps | Aug 2012 | A1 |
20140010662 | Duelm | Jan 2014 | A1 |
20150106062 | Chen-Keat | Apr 2015 | A1 |
Number | Date | Country |
---|---|---|
2886311 | Jun 2015 | EP |
32487631 | Nov 2017 | EP |
402162026 | Jun 1990 | JP |
Entry |
---|
European Patent Office, European Search Report for EP Appl. No. 16173196.3 dated Oct. 30, 2017, 4 pp. |
European Patent Office, Communication pursuant to Article 94(3) EPC for EP Appl. No. 16173196.3 dated Jul. 26, 2019, 6 pp. |
European Patent Office, Communication pursuant to Article 94(3) EPC for EP Appl. No. 16173196.3 dated May 25, 2018, 5 pp. |
European Patent Office, Communication pursuant to Article 94(3) EPC for EP Appl. No. 16173196.3 dated Feb. 6, 2019, 10 pp. |
Number | Date | Country | |
---|---|---|---|
20170326808 A1 | Nov 2017 | US |