1. Technical Field
The present application relates to a system and method of manufacturing a structure. The system and method of the present application is particularly useful for manufacturing an aerodynamic structure for a rotor blade of an aircraft. Further, the system and method is particularly well suited for manufacturing with a high performance metal alloy, such as titanium.
2. Description of Related Art
In general, certain aircraft structures may require a high level of precision, as well as a plurality of complex manufacturing steps configured to achieve the requisite high level of precision. For example, it is well known that chemical milling is a manufacturing process commonly used to manufacture parts having complex contours and tapered surfaces. However, chemically milling has shortcomings, such as surfaces pitting, tolerance variation, labor intensive masking, material limitations, and toxic material risks, to name a few.
Further, it can be particularly desirable to use high performance metal alloys, such a titanium alloy, in aircraft structures due their high strength to weight ratios, and other qualities. However, the machining and forming of high performance metal alloys has proven particularly challenging.
Hence, there is a need for an improved manufacturing system and method that improves structure quality and accuracy, while also decreasing labor hours and part rework. Further, there is a need for a system and method of machining and forming a high performance metal alloy, such as titanium.
The novel features believed characteristic of the system and method of the present application are set forth in the appended claims. However, the system and method themselves, as well as a preferred mode of use, and further objectives and advantages thereof, will best be understood by reference to the following detailed description when read in conjunction with the accompanying drawings, wherein:
Illustrative embodiments of the system and method are described below. In the interest of clarity, all features of an actual implementation may not be described in this specification. It will of course be appreciated that in the development of any such actual embodiment, numerous implementation-specific decisions must be made to achieve the developer's specific goals, such as compliance with system-related and business-related constraints, which will vary from one implementation to another. Moreover, it will be appreciated that such a development effort might be complex and time-consuming but would nevertheless be a routine undertaking for those of ordinary skill in the art having the benefit of this disclosure.
In the specification, reference may be made to the spatial relationships between various components and to the spatial orientation of various aspects of components as the devices are depicted in the attached drawings. However, as will be recognized by those skilled in the art after a complete reading of the present application, the devices, members, apparatuses, etc. described herein may be positioned in any desired orientation. Thus, the use of terms such as “above,” “below,” “upper,” “lower,” or other like terms to describe a spatial relationship between various components or to describe the spatial orientation of aspects of such components should be understood to describe a relative relationship between the components or a spatial orientation of aspects of such components, respectively, as the device described herein may be oriented in any desired direction.
The present application includes a system and method for efficiently manufacturing structures having a complex surfaces and precision located features. For example, the system and method of the present application is particularly well suited for manufacturing a leading edge abrasion strip member of a rotor blade, the abrasion strip member having an exterior airfoil surface and an interior portion, each having precision located features. However, it should be fully appreciated that the system and method may be used to manufacture any variety of structures; for example, wing members, nose cones, tip-caps, and tail rotor blades, are examples of other structures that may be manufactured using the method and system of the present application.
Further, the system and method of the present application is particularly well suited for machining and forming a thin sheet of a high performance metal alloy, such as titanium. However, it should be appreciated that the system and method of the present application may also be used for machining and forming a thin metal of other materials, such as stainless steel, for example.
Referring to
Referring now also to
Referring now to
Step 303 includes a step 311 for calculating the scaled location of the machined features. In step 305, the part is formed through in a stretch forming and/or brake forming procedure that deforms and moves features of the part. As such, step 311 involves calculating the scaled size and location of the features so that the features will be in the proper location subsequent forming step 305. In the preferred embodiment, step 311 is performed by first machining the features in the part, then brake forming and stretch forming the part, then measuring the dimension dislocation and distortion of the machined features. Data pertaining to the measured dimension dislocation and distortion of the machined features is statistically evaluated to confirm relative uniformity of feature movement within context of allowable tolerances for both measurement capability and final part assembly. In an alternative embodiment, the calculation of the scaled size and location of the machined features is performed analytically, such that the scaled size and location of the machined features is determined by analytically predicting the dislocation and distortion of the machined features in the forming step 305.
Step 309 includes programming the machining tool with the data developed in step 311. It is well known in the art that machining tools, such as a CNC machining tool, are typically programmable with a set of instructions for machining the part. As such, step 309 includes programming the machining tool to machine the desired part features in accordance with the scaled feature size and location determined in step 311.
Referring now also to
The preferred embodiment of step 303 is particularly well suited for the machining of a high performance alloy, such as a titanium alloy sheet. Referring briefly to
Still referring to
Step 905 includes preventing chatter, flutter, and harmonic coupling of the sheet metal during machining by using a vacuum fixture. Referring briefly to
Step 907 can include machining using a climbing cutting pattern starting at an interior of the metal sheet 401. A climbing cut refers to the rotational direction of the end mill in relation to the direction of travel of the end mill. Starting the milling process at in the inner portion of the sheet metal further reduces the chance of chatter, flutter, and harmonic coupling of the sheet metal. Further, the end mill is preferably operated at an approximate 70% step-over (overlap), such that the area of each pass of the end mill includes 30% of previously machined area.
Step 909 includes using a halide free cutting fluid during machining. An exemplary cutting fluid is S761-B, marketed by Ecocool. However, it should be appreciated that other cutting fluids may be used.
Referring to
Referring again to
Next, stretch forming step 315 is performed with precision to reproducibly distort the part. The stretch forming is performed in a controlled manner so as to control the strain-rate applied to the metal. Lubrication can be used to prevent any sudden slippage or jerking that might otherwise happen if the part were to bind with the stretch forming tool. Further, tooling pins may be located in tooling holes 505 to assure positive location of the part during stretch forming. Preferably, the jaws of the stretch forming tool are attached to the previously braked formed machine article 501 at the frame 503 that is intentionally produced in the machining step 303. Preferably, frame 503 has a constant thickness and sufficient width to provide grip on the entire jaw-plate of the stretch form grips or jaws. Strain rate is controlled and consistent during the stretch forming so as to prevent the part from distorting in an undesired manner. Further, the over-press part of the stretch forming tool can also be controlled to form the part.
As further noted herein, method 301 is particularly useful for manufacturing with a high performance metal alloy, such as a titanium alloy sheet. When using a titanium alloy sheet, it is preferable that step 315 includes stretch forming with a heated mandrel, as discussed further below. Cold forming (room temperature) titanium has severe limitations due to the lack of ductility of titanium. Traditional hot forming requires large and expensive presses that heat the entire environment, and further require an etching process after the hot forming process. However, the method of the present application includes the realization that the apparent ductility of titanium can be improved if the metal is slightly heated above room temperature and the strain rate is controlled at a low enough rate to match the imparted plasticity resulting from the slight elevation of temperature.
Referring now also to
Heated mandrels 1101 and 1201 provide the ability to stretch form the metal sheet while minimizing strain at an atomic level, while erasing metal memory and partially stress relieving the metal sheet while it is being stretch formed. The metal sheet parts can be formed consistently with less risk of defect despite normal variations in material stock. The heating of the sheet metal by the heated mandrel minimizes the risk of non-uniform movement as the atoms more readily move (or dislocate) at elevated temperatures. The circulation of a working fluid in heated mandrel promotes temperature uniformity, not only in the mandrel, but also in the metal sheet part as it comes into contact with the heated mandrel. The precise temperature of the working fluid is implementation specific. However, in an exemplary embodiment, an oil is used as the working fluid, the oil being heated to approximately 350-400° F. It should be appreciated that other fluids and temperatures may be used. For example, a highly engineered heat transfer fluid having a temperature capacity of approximately 1300° F. may be used.
During stretch forming, the metal sheet is gradually stretched using a controlled strain rate while the heated mandrel transfers heat to the surface of the metal sheet, thereby relaxing the material to stimulate movement of the metal during stretching, while also improving the uniformity of metal movement, reducing metal-memory, and at least partially stress-relieving the material by preventing stress build-up during the stretch forming process.
It should be appreciated that heated mandrels 1101 and 1201 may be used in stretch forming sheet metal of other material compositions, other than titanium.
Method 301 further includes a post processing step 307 for upgrading and trimming the part. For example, step 307 includes trimming off frame 503 and touching up any surface finish blemishes. Step 307 can also include a dye-penetrant check to confirm the absence of cracks and pits in the part. Referring now also to
Referring now to
The system 801 can include an input/output (I/O) interface 803, an analysis engine 805, and a database 807. Alternative embodiments can combine or distribute the input/output (I/O) interface 803, analysis engine 805, and database 807, as desired. Embodiments of the system 801 can include one or more computers that include one or more processors and memories configured for performing tasks described herein. This can include, for example, a computer having a central processing unit (CPU) and non-volatile memory that stores software instructions for instructing the CPU to perform at least some of the tasks described herein. This can also include, for example, two or more computers that are in communication via a computer network, where one or more of the computers include a CPU and non-volatile memory, and one or more of the computer's non-volatile memory stores software instructions for instructing any of the CPU(s) to perform any of the tasks described herein. Thus, while the exemplary embodiment is described in terms of a discrete machine, it should be appreciated that this description is non-limiting, and that the present description applies equally to numerous other arrangements involving one or more machines performing tasks distributed in any way among the one or more machines. It should also be appreciated that such machines need not be dedicated to performing tasks described herein, but instead can be multi-purpose machines, for example computer workstations, that are suitable for also performing other tasks.
The I/O interface 803 provides a communication link between external users, systems, and data sources and components of the system 801. The I/O interface 803 can be configured for allowing one or more users to input information to the system 801 via any known input device. Examples can include a keyboard, mouse, touch screen, and/or any other desired input device. The I/O interface 803 can be configured for allowing one or more users to receive information output from the system 801 via any known output device. Examples can include a display monitor, a printer, and/or any other desired output device. The I/O interface 803 can be configured for allowing other systems to communicate with the system 801. For example, the I/O interface 803 can allow one or more remote computer(s) to access information, input information, and/or remotely instruct the system 801 to perform one or more of the tasks described herein. The I/O interface 803 can be configured for allowing communication with one or more remote data sources. For example, the I/O interface 803 can allow one or more remote data source(s) to access information, input information, and/or remotely instruct the system 801 to perform one or more of the tasks described herein.
The database 807 provides persistent data storage for system 801. While the term “database” is primarily used, a memory or other suitable data storage arrangement may provide the functionality of the database 807. In alternative embodiments, the database 807 can be integral to or separate from the system 801 and can operate on one or more computers. The database 807 preferably provides non-volatile data storage for any information suitable to support the operation of the system 801, including various types of data discussed further herein.
The analysis engine 805 can be configured for calculating and predicting the scaled location of machined features in step 311, programming the scaled machining operation in step 309, as well as other concepts disclosed herein. For example, the analysis engine 805 can be configured to analytically predict the dimension dislocation and distortion of the machined features during the forming procedures, thereby analytically calculating the scaled location of the features for machining. The analysis engine 805 can include various combinations of one or more processors, memories, and software components.
The system and method of the present application provide significant advantages, including: 1) creating the critical and complex surface features prior to brake forming and stretch forming; 2) calculating the scaled location of the machined features so that a subsequent forming step translates and deforms the machined features into the desired location; 3) providing a manufacturing method which does not require the chemical milling; 4) providing a method for machining high performance metal alloy, such as titanium; and 5) providing a heated mandrel for applying heat to a high performance metal alloy, such as titanium, during stretch forming.
It is apparent that a system and method having significant advantages has been described and illustrated. Although the system and method of the present application are shown in a limited number of forms, they are not limited to just these forms, but are amenable to various changes and modifications without departing from the spirit thereof.
The particular embodiments disclosed above are illustrative only, as the system and method may be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. Modifications, additions, or omissions may be made to the system and method described herein without departing from the scope of the invention. The components of the system may be integrated or separated. Moreover, the operations of the system may be performed by more, fewer, or other components.
Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. It is therefore evident that the particular embodiments disclosed above may be altered or modified and all such variations are considered within the scope and spirit of the application. Accordingly, the protection sought herein is as set forth in the claims below.
To aid the Patent Office, and any readers of any patent issued on this application in interpreting the claims appended hereto, applicants wish to note that they do not intend any of the appended claims to invoke paragraph 6 of 35 U.S.C. §112 as it exists on the date of filing hereof unless the words “means for” or “step for” are explicitly used in the particular claim.
| Number | Date | Country | |
|---|---|---|---|
| 61547156 | Oct 2011 | US |