System for the purification of exhaust gas from an internal combustion engine

Abstract

An exhaust gas cleaning system, comprising an active regenerable particulate filter and an SCR catalyst comprising a hydrothermally microporous stable zeolite having the AEI type framework and being promoted with copper, where the zeolite is SSZ-39.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to after treatment of exhaust gas from an internal combustion engine in terms of removal or reduction of harmful compounds. More particularly, the invention focus on removal of particulate matter and reduction of nitrogen oxides in engine exhaust from lean burn internal combustion engines, and in particular diesel engines.

2. Description of the Related Art

Lean burn engines are known to be energy efficient, but have the disadvantage of forming particulate matter and nitrogen oxides, which must be removed or at least reduced in the engine exhaust.

To prevent environmental pollution and to fulfil several governmental requirements, modern diesel engines are provided with an exhaust gas cleaning system comprising in series an oxidation catalyst for the removal of volatile organic compounds, a particulate filter for the removal of particulate matter and a catalyst being active in the selective reduction of nitrogen oxides (NOx).

It is also known to integrate the SCR catalyst into the particulate filter.

Selective catalytic reduction of NOx in exhaust gas is usually accomplished by reaction with ammonia introduced as such or as a precursor thereof, which is injected into the exhaust gas upstream of the SCR catalyst for the selective reduction of nitrogen oxides, mainly nitrogen dioxide and nitrogen monoxide (NOx), to nitrogen.

For this purpose numerous catalyst compositions are disclosed in the literature.

Lately, zeolites promoted with copper or iron, have found great interest, particularly for use in automotive application.

Copper containing zeolite catalysts for NH₃-SCR applications have shown high activity at low temperature. However, in certain applications the catalyst can be exposed to high temperature excursions in exhaust gases. Furthermore the exhaust gas contains high concentrations of water vapour from the combustion engine, which can deteriorate the zeolite catalyst performance. The hydrothermal stability is often an issue for Cu-based zeolites catalysts as one possible catalyst deactivation mechanism is the degradation of the zeolite framework due to its instability towards hydrothermal conditions, which is furthermore enhanced by the presence of copper.

Deactivation of copper containing zeolite catalysts in NH₃-SCR applications is typically caused by degradation of the zeolite framework due to its instability towards hydrothermal conditions, which is furthermore enhanced by the presence of copper. However the stability is especially important for automotive applications in which the catalyst will experience high temperature excursions in an exhaust stream containing water.

Deactivation of the catalyst is in particular a problem in exhaust gas cleaning systems provided with a particulate filter, which must periodically be actively regenerated in order to prevent build up of pressure over the soot laden filter.

Active regeneration is performed by burning of captured soot. The regeneration can be initiated by injection of fuel into the exhaust gas upstream the oxidation catalyst or by electrical heating of the particulate filter.

During the active regeneration exhaust gas temperature at outlet of the filter can reach more than 850° C. and a content of water vapour more than 15% and up to 100% for periods of time between 10 and 15 minutes depending on the amount of soot captured in the filter.

SUMMARY OF THE INVENTION

It is the general object of the invention to provide a system for the removal of harmful compounds lean burn internal combustion engines, such as particulate matter by means of a particulate filter and nitrogen oxides by selective catalytic reduction of nitrogen oxides in contact with catalyst being hydrothermally stable when exposed to high temperatures and water vapour concentration during active regeneration of the particulate filter.

We have found that the object of the invention can be achieved by using a zeolite or zeotype having hydrothermally stable AEI type framework, in which the structure is preserved under hydrothermal aging conditions even when copper is present in the zeolite or zeotype.

Pursuant to the above finding, this invention provides an exhaust gas cleaning system, comprising an active regenerable particulate filter and an SCR catalyst comprising a hydrothermally microporous stable zeolite and/or zeotype having the AEI type framework and being promoted with copper.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A shows the powder X-ray diffraction (PXRD) pattern of treated Cu-SSZ-39 samples.

FIG. 1B shows the powder X-ray diffraction (PXRD) pattern of treated CHA samples.

FIG. 2 is a summary of the results of Examples 1-4 with the Cu-SSZ-39 and CHA catalysts.

FIG. 3 shows the results of Example 5 with the Cu-SSZ-39 catalyst.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

“Hydrothermally stable” means that the zeolite and zeotype catalyst have the ability to retain at least 80 to 90% of initial surface area and 80 to 90% microporous volume after exposure to temperatures of at least 600° C. and a water vapour content up to 100 volume % for 13 hours, and at least 30 to 40% of initial surface area and micropore volume after exposure to temperatures of at least 750° C. and a water vapour content up to 100 volume % for 13 hours.

Preferably, the hydrothermally stable zeolite or zeotype with an AEI type framework has an atomic ratio of silicon to aluminium between 5 and 50 for the zeolite or between 0.02 and 0.5 for the zeotype.

The most preferred zeolite or zeotype catalysts for use in the invention are zeolite SSZ-39 and zeotype SAPO-18 both having the “AEI” framework structures, in which copper is introduced by impregnation, liquid ion exchange or solid ion exchange.

The atomic copper to aluminium ratio is preferred to be between about 0.01 and about 1 for the zeolite. For the zeotype the preferred atomic copper to silicon ratio is correspondingly between 0.01 and about 1.

By means of the above catalysts employed in the invention, 80% of the initial NOx reduction is maintained at 250° C. after aging at 750° C. as compared to 20% for a Cu-CHA catalyst.

Thus, in an embodiment of the invention, 80% of the initial reduction of nitrogen oxides at 250° C. is maintained after the catalyst has been exposed to a temperature of 750° C. and a water vapour content of 100% in the exhaust gas for 13 hours.

In further an embodiment of the exhaust gas cleaning system according to the invention, the SCR catalyst is integrated into the particulate filter.

In the above embodiments, the SCR catalyst can be deposited on a monolithic support structure.

The Cu-SSZ-39 catalyst system has shown an improved performance compared to the typical “state-of-the-art” Cu-SSZ-13 when similar Si/A1 ratios are compared.

EXAMPLE 1

Cu-SSZ-39 Catalyst Preparation

The zeolite SSZ-39 with the framework type code AEI was synthesized in a similar way as given in U.S. Pat. No. 5,958,370 using 1,1,3,5-tetramethylpiperidinium as the organic template. A gel with the following composition: 30 Si:1.0 Al:0.51 NaOH:5.1 OSDA:600 H₂O, was autoclaved at 135° C. for 7 days, the product filtered, washed with water, dried and calcined in air. The final SSZ-39 had a Si/Al=9.1 measured by ICP-AES.

To obtain the Cu-SSZ-39 the calcined zeolite was ion exchanged with Cu(CH₃COO)₂ to obtain the final catalyst with a Cu/Al=0.52 after calcination.

The powder X-ray diffraction (PXRD) pattern of Cu-SSZ-39 after calcination is shown in FIG. 1A.

EXAMPLE 2

Catalytic Testing

The activity of the samples for the selective catalytic reduction of NO_x was tested in a fixed bed reactor to simulate an engine exhaust stream using a total flow rate of 300 mL/min consisting of 500 ppm NO, 533 ppm NH₃, 7% O₂, 5% H₂O in N₂ in which 40 mg catalyst was tested.

The NO_x present in the outlet gases from the reactor were analyzed continuously and the conversion is shown in FIG. 2.

EXAMPLE 3

Test of Hydrothermal Durability

In order to test the hydrothermal stability of the zeolites, steaming treatments were done to the samples. They were exposed to a water feed (2.2 mL/min) at 600 or 750° C. during 13 hours in a conventional oven and afterwards tested similarly to Example 2.

The catalytic results can also be seen in FIG. 2. The samples that underwent a hydrothermal treatment have been marked with 600 or 700° C., depending on the temperature used during the hydrothermal treatment.

Additional characterization has also been performed to all treated samples. PXRD patterns after hydrothermal treatments are shown in FIG. 1A, and BET surface areas, micropore areas, and micropore volumes of treated samples are summarized in Table 1 below.

EXAMPLE 4

Comparative Example with Cu-CHA (Cu-SSZ-13)

A Cu-CHA zeolite was prepared from a gel with the molar composition: SiO₂:0.033 Al₂O₃:0.50 OSDA:0.50 HF:3 H₂O, where the OSDA is N,N,N-trimethyl-1-adamantamonium hydroxide.

The gel was autoclaved at 150° C. for 3 days under tumbling to give a final zeolite product with a Si/Al=12.7 after washing, drying and calcination.

To obtain the Cu-CHA the calcined zeolite was ion exchanged with Cu(CH₃COO)₂ to obtain the final catalyst with a Cu/Al=0.54.

The powder X-ray diffraction (PXRD) pattern of Cu-CHA after calcination is shown in FIG. 1B.

This catalyst was also tested according to example 2, and the hydrothermal durability evaluated similarly to example 3. The catalytic results are summarized in FIG. 2 of the drawings. PXRD patterns of treated-CHA samples are shown in FIG. 1B, and textural properties (BET surface area, micropore volume, and micropore area) are summarized on Table 1.

TABLE 1
			Volume mi-
	BET surface	Micropore	cropore
Sample	area (m2/g)	area (m2/g)	(cm3/g)
SSZ-39_Calc	571	568	0.28
SSZ-39_600° C.	554	551	0.28
SSZ-39_750° C.	565	563	0.28
Cu-SSZ-39_600° C.	465	463	0.24
Cu-SSZ-39_750° C.	158	152	0.09
CHA_calc	675	637	0.32
CHA_600° C.	687	645	0.32
CHA_750° C.	674	623	0.31
Cu-CHA_600° C.	633	585	0.29
Cu-CHA_750° C.	50	35	0.02

EXAMPLE 5

Cu-SAPO-18

Silicoaluminophosphate SAPO-18 with the framework type code AEI was synthesized according to [J. Chen, J. M. Thomas, P. A. Wright, R. P. Townsend, Catal. Lett. 28 (1994) [241-248] and impregnated with 2 wt. % Cu. The final Cu-SAPO-18 catalyst was hydrothermally treated in 10% H₂O and 10% O₂ at 750° C. and tested under the same conditions as given in Example 2. The results are shown in FIG. 3 of the drawings.

Claims

1. An exhaust gas cleaning system, comprising an active regenerable particulate filter and an SCR catalyst comprising a hydrothermally microporous stable zeolite with the AEI type framework and being promoted with copper, wherein the microporous stable zeolite of the AEI type framework is SSZ-39, wherein the SCR catalyst retains 80% of the initial reduction of nitrogen oxides at 250° C. after the catalyst has been exposed to a temperature of 750° C. and a water vapor content of 100% in the exhaust gas for 13 hours.

2. The exhaust gas cleaning system of claim 1, wherein the SCR catalyst is integrated into the particulate filter.

3. The exhaust gas cleaning system of claim 1, wherein the atomic copper to aluminium ratio in the zeolite is between about 0.01 and about 1.

4. The exhaust gas cleaning system of claim 1, wherein the atomic ratio of silicon to aluminium in the SCR catalyst is between 5 and 50 for the zeolite.

5. The exhaust gas cleaning system of claim 1, wherein the SCR catalyst is deposited on a monolithic support structure.

6. An exhaust gas cleaning system, comprising an active regenerable particulate filter and an SCR catalyst comprising a hydrothermally microporous stable zeolite with the AEI type framework and being promoted with copper, wherein the microporous stable zeolite of the AEI type framework is SSZ-39, wherein the SCR catalyst retains at least 80% to 90% of the initial microporosity after aging at 600° C., and at least 30% to 40% of the initial microporosity after aging at 750° C.

7. The exhaust gas cleaning system of claim 6, wherein the SCR catalyst is integrated into the particulate filter.

8. The exhaust gas cleaning system of claim 6, wherein the atomic copper to aluminium ratio in the zeolite is between about 0.01 and about 1.

9. The exhaust gas cleaning system of claim 6, wherein the atomic ratio of silicon to aluminium in the SCR catalyst is between 5 and 50 for the zeolite.

10. The exhaust gas cleaning system of claim 6, wherein the SCR catalyst is deposited on a monolithic support structure.