Patent Application
20110293925
1. Field of the Disclosure
The invention generally relates to insert molding and, in particular, to a system, method and apparatus for forming seals with a positive flash shut-off for the insert molding of liquid silicone rubber are disclosed.
2. Description of Related Art
Curable silicone compositions are used in a variety of applications that range from the automotive industry to medical devices. In many cases, the silicone composition is coupled to a variety of substrates such as polymeric, metallic, or glass substrates. For instance, silicone compositions may be used as a coating or a laminate over a variety of components.
Typically, a component that is overmolded with silicone produces flash, or small, unwanted, excessive fragments of silicone on the molded component. The flash must be removed from the final product, which increases the number of steps in and cost of the manufacturing process. As such, an improved system, method and apparatus for manufacturing silicone-including articles would be desirable.
Embodiments of a system, method and apparatus for forming an object with a positive flash shut-off for the insert molding of the object on a component are disclosed. For example, a mold for injection molding on the component has a base with a cavity and a port that delivers a liquid to the cavity during the injection molding process. The base has a component support structure for supporting the component and pockets formed on opposite sides of the cavity. The pockets are slightly spaced apart from the cavity by thin partitions.
Embodiments further comprise inserts located in the pockets. The inserts are formed from a polymer, such as a fluoroelastomer or a perfluoroelastomer. Both the partitions and inserts comprise the component support structure. In some embodiments, the inserts have a dimension that is smaller than that of the base and partitions so as to form a compression fit around the component during the molding process. This design reduces or eliminates flash of the mold fluid down the component during the molding process.
The foregoing and other objects and advantages of the embodiments will be apparent to those skilled in the art, in view of the following detailed description, taken in conjunction with the appended claims and the accompanying drawings.
So that the manner in which the features and advantages of the embodiments are attained and can be understood in more detail, a more particular description briefly summarized above may be had by reference to the embodiments thereof that are illustrated in the appended drawings. However, the drawings illustrate only some embodiments and therefore are not to be considered limiting of its scope as the invention may admit to other equally effective embodiments.
The use of the same reference symbols in different drawings indicates similar or identical items.
Embodiments of a system, method and apparatus for forming an object with a positive flash shut-off for the insert molding of the object on a component are disclosed. For example, some embodiments form seals with a positive flash shut-off for the insert molding of liquid silicone rubber (LSR) onto the object.
As shown in
The base 21 also has a component support structure 27 having an axis 29. In some embodiments, the component support structure 27 coaxially supports a component 101 on which one or more objects 103, 105 (
The pockets 31 are axially adjacent to the cavity 23 but axially spaced apart from the cavity 23 by respective partitions 33 extending from the base 21. Each partition 33 may comprise an axial thickness 35 (
Embodiments further comprise a pair of inserts 41 located in respective ones of the pockets 31. Thus, only the thin partitions 33 separate the inserts 41 from either axial side of the cavity 23. For example, each of the inserts 41 may be formed from a polymer that is softer than the base material. The polymer may be provided with a Shore A durometer hardness in a range of 75 to 100, or about 90 in some embodiments.
The polymer also may have an operating temperature range of 135° C. to 205° C. The polymer may comprise a fluoropolymer having a low surface energy and maintain elasticity at a temperature of up to about 300° C. At elevated temperatures, the low surface energy of the fluoropolymer provides excellent release properties relative to the other material substrate. In some embodiments, the polymer comprises a fluoroelastomer or a perfluoroelastomer, and may comprise at least 60% fluorine, and have a mold release property similar to polytetrafluoroethylene (PTFE). Other embodiments of the polymer as further described herein also may be used.
Both the partitions 33 and the inserts 31 comprise the component support structure 27 as shown. In some embodiments, the component support structure 27 has a cylindrical shape as shown. The base 21 and the partitions 33 have a base diameter 51 (
In addition, some embodiments of the base 21, partitions 33 and the inserts 41 have alignment features such as apertures 26, 28 (e.g., two horizontal apertures 26, and one vertical aperture 28 shown) that are provided for mechanical locating devices, such as pins to ensure alignment between the various parts. In one version, vertical aperture 28 is used to align an alignment pin with the hole 128 (
Clearances are provided between the alignment pins and apertures to allow movement of the inserts under compression, and the apertures may be provided as through holes. For example, clearances on the order of or less than 0.020 inches may be provided. Slots may be formed as well in order to avoid material from breaking away under compression. Without sufficient clearances, some inserts may swell due to the heat from the mold, and the insert material may be pinched during compression and shear edges where it makes contact with the surrounding steel.
In
In the embodiment of
Embodiments of a method of overmolding a component 101 comprise providing a pair of bases 21, each having a cavity 23 and a port 25. Pockets 31 are formed in the bases 21 on opposite sides of respective one of the cavities 23. The pockets 31 are adjacent to the cavities 23 but spaced apart from the cavities 23 by respective partitions 33 extending from the bases 21.
The method also comprises installing inserts 41 in respective ones of the pockets 33, with each of the inserts 41 being formed from a polymer that is softer than a base material used to form the bases 21; defining a component support structure 27 in each of the bases 21, partitions 33 and inserts 41 to support the component 101; placing the component 101 on one of the bases 21 such that the component 101 is supported by the component support structure 27 of said one of the bases 21; pressing the other base 21 onto said one of the bases 21 such that the component 101 seats in the component support structure 27 of said other base 21, and the inserts 41 in both bases 21 are compressed, such as in a radial direction with respect to an axis of the component 101. A liquid is delivered to the cavity 23 through the port 25 to form at least one object 103, 105 on the component 101.
In other embodiments, the method comprises forming each partition with a thickness in a range of 0.002 to 0.050 inches, approximately 0.010 inches, and/or forming the partitions from the base material. Other embodiments comprise forming the polymer with a Shore A durometer hardness in a range of 75 to 100, or about 90, and/or an operating temperature in a range of 135° C. to 205° C. The polymer may be formed from a fluoropolymer, a fluoroelastomer or a perfluoroelastomer, or at least 60% fluorine.
In still other embodiments, the method may comprise defining the component support structure as a cylindrical shape, the bases and the partitions have a base diameter for the cylindrical shape, the inserts have an insert diameter for the cylindrical shape, and the insert diameter is smaller than the base diameter; defining the component support structure of at least one of the inserts with a neck that tapers radially along an axial direction of the neck, and the neck provides a mechanical stop and positioning feature for the component; forming each of the inserts with a top, two sides and chamfers extending between the top and two sides on opposite sides of the component support structure; and/or forming the bases, partitions and inserts with alignment features that respectively align with other.
Other Insert Materials
Some embodiments of the inserts may comprise fluoroelastomers from the FKM family of rubbers designed for high temperature operation. Examples include Dai-El, Fluorel, Technoflon and Viton®. They can operate continuously in excess of 200° C. depending on the grade, and intermittently to temperatures on the order of 300° C. They have outstanding resistance to chemical attack by oxidation, acids and fuels, and good oil resistance. However, at high operating temperatures they are relatively weaker, so adequate support against applied forces may be provided. They have limited resistance to steam, hot water, methanol, and other highly polar fluids. They are attacked by amines, strong alkalis and many Freons. There are standard and special grades, and the latter may be designed to have special properties such as improved low-temperature resistance.
Other embodiments of the inserts may comprise perfluoro elastomers in the FFKM family of rubbers. Examples include Chemraz, Kalrez®, Perfluor, Simriz and Zalak. These materials have even greater heat and chemical resistance than the fluoroelastomers. They can be used in extreme conditions up to temperatures around 300° C. or more with special compounding. Their disadvantages are difficult processing, cost, poorer physical properties at high temperature, and their high glass transition temperatures which limit their use at low temperatures. Some materials cannot be used below 0° C., and even at normal ambient temperatures their creep properties may be limited.
Other exemplary fluoropolymers that may be used to form the inserts include a homopolymer, copolymer, terpolymer, or polymer blend formed from a monomer, such as tetrafluoroethylene, hexafluoropropylene, chlorotrifluoroethylene, trifluoroethylene, vinylidene fluoride, vinyl fluoride, perfluoropropyl vinyl ether, perfluoromethyl vinyl ether, or any combination thereof. Exemplary fluoropolymers layers may be cast, skived, or extruded. In an embodiment, cast and extruded fluoropolymer layers may include multilayered structures such that the composition of the surfaces of the film may or may not match.
Further exemplary fluoropolymers include a polytetrafluoroethylene (PTFE), fluorinated ethylene propylene copolymer (FEP), a copolymer of tetrafluoroethylene and perfluoropropyl vinyl ether (PFA), a copolymer of tetrafluoroethylene and perfluoromethyl vinyl ether (MFA), a copolymer of ethylene tetrafluoroethylene (ETFE), a copolymer of ethylene and chlorotrifluoroethylene (ECTFE), polychlorotrifluoroethylene (PCTFE), poly vinylidene fluoride (PVDF), a terpolymer including tetrafluoroethylene, hexafluoropropylene, and vinylidenefluoride (THV), or any blend, mixture, or alloy thereof. In an embodiment, the fluoropolymer layer may include a polytetrafluoroethylene (PTFE), fluorinated ethylene propylene copolymer (FEP), or blends, mixtures, or alloys thereof. In an exemplary embodiment, the fluoropolymer may be a polymer crosslinkable through radiation, such as e-beam. An exemplary crosslinkable fluoropolymer may include ETFE, THV, PVDF, or any combination thereof. A THV resin is available from Dyneon 3M Corporation Minneapolis, Minn. An ECTFE polymer is available from Ausimont Corporation (Italy) under the trade name Halar. Other fluoropolymers may be obtained from Daikin (Japan) and DuPont (USA). In particular, FEP fluoropolymers are commercially available from Daikin, such as NP-12X.
Liquid Silicone Rubber (LSR) Materials
In an exemplary embodiment, the silicone base polymer may include a non-polar silicone polymer. The silicone base polymer may, for example, include polyalkylsiloxanes, such as silicone polymers formed of a precursor, such as dimethylsiloxane, diethylsiloxane, dipropylsiloxane, methylethylsiloxane, methylpropylsiloxane, or combinations thereof. In a particular embodiment, the polyalkylsiloxane includes a polydialkylsiloxane, such as polydimethylsiloxane (PDMS). In a particular embodiment, the polyalkylsiloxane is a silicone hydride-containing polydimethylsiloxane. In a further embodiment, the polyalkylsiloxane is a vinyl-containing polydimethylsiloxane. In yet another embodiment, the silicone base polymer is a combination of a hydride-containing polydimethylsiloxane and a vinyl-containing polydimethylsiloxane. In an example, the silicone base polymer is non-polar and is free of halide functional groups, such as chlorine and fluorine, and of phenyl functional groups. Alternatively, the silicone base polymer may include halide functional groups or phenyl functional groups. For example, the silicone base polymer may include fluorosilicone or phenylsilicone. Typically, the silicone base polymer is elastomeric. For example, the durometer (Shore A) of the silicone base polymer may be less than about 75, such as about 1 to 70, about 20 to about 50, about 30 to about 50, about 40 to about 50, or about 1 to about 5.
The silicone base polymer may further include a catalyst and other optional additives. Exemplary additives may include, individually or in combination, fillers, inhibitors, colorants, and pigments. In an embodiment, the silicone base polymer is platinum catalyzed. Alternatively, the silicone base polymer may be peroxide catalyzed. In another example, the silicone base polymer may be a combination of platinum catalyzed and peroxide catalyzed. The silicone base polymer may be a room temperature vulcanizable (RTV) formulation or a gel. In an example, the silicone base polymer may be a high consistency gum rubber (HCR) or a liquid silicone rubber (LSR). In an example, the silicone base polymer is an HCR, such as SE6035, SE6075 available from Momentive, MF135 available from Bluestar silicone, and Silastic® Q7-4535, Silastic® Q7-4550 available from Dow Corning.
In a particular embodiment, the silicone base polymer is a platinum catalyzed LSR. In a further embodiment, the silicone base polymer is an LSR formed from a two-part reactive system. The silicone base polymer may be a conventional, commercially prepared silicone base polymer. The commercially prepared silicone base polymer typically includes the non-polar silicone polymer, a catalyst, a filler, and optional additives. Particular embodiments of conventional, commercially prepared LSR include Wacker Elastosil® LR 3003/50 by Wacker Silicone of Adrian, Mich. and Silbione® LSR 4340 by Bluestar Silicones of Ventura, Calif.
In an exemplary embodiment, a commercially prepared silicone base polymer is available as a one-part or two-part reactive system. With a two-part reactive system, part 1 typically includes a vinyl-containing polydialkylsiloxane, a filler, and catalyst. Part 2 typically includes a hydride-containing polydialkylsiloxane and optionally, a vinyl-containing polydialkylsiloxane and other additives. A reaction inhibitor may be included in Part 1 or Part 2. Mixing Part 1 and Part 2 by any suitable mixing method produces the silicone base polymer. With a one-part system or two-part system, the excess hydride-containing siloxane is typically added to the commercially prepared silicone base polymer prior to vulcanization. In an embodiment, the excess hydride-containing siloxane is added to the mixed two-part system or during the process of mixing the two-part system prior to vulcanization. In an exemplary embodiment, the silicone base polymer and the excess hydride-containing siloxane are mixed in a mixing device. In an example, the mixing device is a mixer in an injection molder. In another example, the mixing device is a mixer, such as a dough mixer, Ross mixer, two-roll mill, or Brabender mixer.
The embodiments described herein have numerous advantages over prior solutions. The compression of the inserts forms a pre-load and tight seal around the component to form a positive shut-off and prevent excess flash from forming axially down the component during the molding process. The inserts may be installed at the parting lines of the mold to create the positive shut-off and eliminate flash on the component, “as molded” or “as formed”. No subsequent flash removal operation is required for the insert molded components. This system is compatible with both hot runner and cold runner mold operations.
This written description uses examples to disclose the embodiments, including the best mode, and also to enable those of ordinary skill in the art to make and use the invention. The patentable scope is defined by the claims, and may include other examples that occur to those skilled in the art. Such other examples are intended to be within the scope of the claims if they have structural elements that do not differ from the literal language of the claims, or if they include equivalent structural elements with insubstantial differences from the literal languages of the claims.
Note that not all of the activities described above in the general description or the examples are required, that a portion of a specific activity may not be required, and that one or more further activities may be performed in addition to those described. Still further, the order in which activities are listed are not necessarily the order in which they are performed.
In the foregoing specification, the concepts have been described with reference to specific embodiments. However, one of ordinary skill in the art appreciates that various modifications and changes can be made without departing from the scope of the invention as set forth in the claims below. Accordingly, the specification and figures are to be regarded in an illustrative rather than a restrictive sense, and all such modifications are intended to be included within the scope of invention.
As used herein, the terms “comprises,” “comprising,” “includes,” “including,” “has,” “having” or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a process, method, article, or apparatus that comprises a list of features is not necessarily limited only to those features but may include other features not expressly listed or inherent to such process, method, article, or apparatus. Further, unless expressly stated to the contrary, “or” refers to an inclusive-or and not to an exclusive-or. For example, a condition A or B is satisfied by any one of the following: A is true (or present) and B is false (or not present), A is false (or not present) and B is true (or present), and both A and B are true (or present).
Also, the use of “a” or “an” are employed to describe elements and components described herein. This is done merely for convenience and to give a general sense of the scope of the invention. This description should be read to include one or at least one and the singular also includes the plural unless it is obvious that it is meant otherwise.
Benefits, other advantages, and solutions to problems have been described above with regard to specific embodiments. However, the benefits, advantages, solutions to problems, and any feature(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as a critical, required, or essential feature of any or all the claims.
After reading the specification, skilled artisans will appreciate that certain features are, for clarity, described herein in the context of separate embodiments, may also be provided in combination in a single embodiment. Conversely, various features that are, for brevity, described in the context of a single embodiment, may also be provided separately or in any subcombination. Further, references to values stated in ranges include each and every value within that range.
This non-provisional application claims priority to and the benefit of U.S. Provisional App. No. 61/347,871, filed May 25, 2010, and is incorporated herein by reference in its entirety.