Patent Application
20210355037
Broadly, the invention relates to systems and methods of making ceramic powders. More specifically, the present disclosure relates to carbothermically synthesizing various ceramic powders in a continuous reactor such that the resulting ceramic powder product is configured with consistent, tailored characteristics and/or properties.
Through carbothermic synthesis, it is possible to make various boride, nitride, and/or carbide ceramic powders. The ceramic powders can then be processed into final ceramic products for a wide variety of applications.
In one aspect of the instant disclosure, a system comprises: a reactor body having a first end and a second end, wherein the reactor body is configured with an inner sidewall extending from the first end to the second end to define a reaction chamber; wherein the reactor body is configured with a heat source to provide a hot zone along the reaction chamber; a sweep gas inlet adjacent to the first end and configured to direct a sweep gas into the reaction chamber and a sweep gas outlet adjacent to the second end and configured to direct an exhaust gas from the reaction chamber; a plurality of containers configured in a sequentially aligned arrangement within the reactor body, wherein each container is configured to retain at least one preform, wherein each container is configured to permit the sweep gas to flow there through, wherein each preform is configured from a mixture of precursor materials for a carbothermic reaction, wherein the preform is configured to permit the sweep gas to flow there through, such that the precursor mixture is reacted in the hot zone to form a ceramic powder product having uniform properties.
In some embodiments, the reactor body is configured one of vertically or horizontally.
In some embodiments, the reactor body is configured at an angle, with the first end at a different height than the second end.
In some embodiments, the reactor further comprises a staging area configured adjacent to and in communication with the first end between a reactor inlet and a first seal, wherein the staging area is configured to accept at least one container, further wherein the staging area is configured with a valve such that a pressure differential is introduced throughout the staging area to remove and/or add gaseous species from the staging area.
In some embodiments, the staging area comprises a heat source configured to preheat the container and the preform.
In some embodiments, the system further comprises: a first seal on the first end of the reactor body, wherein the first seal is configured to provide a sealed reaction chamber adjacent to the first end; and a second seal on the second end of the reactor body to provide a sealed reaction chamber adjacent to the second end.
In some embodiments, an outer diameter of the container is less than an inner diameter of the reactor body.
In some embodiments, each of the plurality of containers is configured to support the weight of a plurality of stacked containers equipped with preforms.
In some embodiments, each of the plurality of containers comprises at least one end and a sidewall perimetrically surrounding and extending from the end.
In some embodiments, at least one of the ends and the container are configured with a mechanical device configured to attach the container sidewall to the end.
In some embodiments, at least one of the container sidewall or the container end is configured with apertures.
In some embodiments, the system is configured for repeated container insertion and removal from the reactor body.
In some embodiments, the preform is in a form selected from the group consisting of: a sphere, a rod, a plate, a brick, a block, a tetrahedron, a torus, a tube, and combinations thereof.
In some embodiments, the preform is selected from the group consisting of: a compacted solid form, an extruded form, a molded form, a cast form, and combinations thereof.
In some embodiments, the preform is configured to the height of the container.
In some embodiments, the preform is configured in a stacked vertical configuration within the container.
In some embodiments, the preform is configured as a rigid body with a porosity configured to permit the sweep gas to permeate through the preform body.
In one aspect of the instant disclosure, a method for making ceramic powder, comprises: providing an at least one preform to a reactor, the reactor comprising: a reactor body having a first end and a second end, wherein the reactor body is configured with an inner sidewall extending from the first end to the second end to define a reaction chamber; wherein the reactor body is configured with a heat source to provide a hot zone along the reaction chamber; a plurality of containers configured in sequentially aligned arrangement within the reactor body, wherein each container is configured to retain at least one preform, wherein each container is configured to permit the sweep gas to flow there through, wherein each preform is configured from a mixture of precursor materials for a carbothermic reaction, directing a sweep gas from the first end through the at least one preform and into the second end; concomitant with the directing the sweep gas step, carbothermically reacting the at least one preform in the reactor body; and forming a ceramic powder configured with uniform properties.
In some embodiments, the method further comprises preparing a precursor mixture.
In some embodiments, the method further comprises forming the preform from the precursor mixture.
In some embodiments, the forming step includes at least one of: compacting the preform mixture; molding the precursor mixture, casting the precursor mixture, extruding the precursor mixture, and combinations thereof.
In some embodiments, preparing the precursor mixture further includes one of: (a) forming a wet agglomerate having the reagents therein, or (b) dry processing the reagents with compatible materials and/or binders.
In some embodiments, the method further comprises processing the precursor mixture into a preform.
In some embodiments, the processing step includes at least one of: dehydrating the preform, curing the preform, demolding the preform, and combinations thereof.
In some embodiments, the preform is configured as a body to promote uniform heat transfer and promote communication of off gases from the preform.
In some embodiments, the method further comprises: flowing the sweep gas (i) through the preform body; (ii) around the preform body; and combinations thereof.
In one aspect of the instant disclosure, a system, comprises: a reactor body having a first end and a second end, wherein the reactor body is configured with an inner sidewall extending from the first end to the second end to define a reaction chamber; wherein the reactor body is configured with a heat source to provide a hot zone along the reaction chamber; a sweep gas inlet adjacent to the first end and configured to direct a sweep gas into the reaction chamber and a sweep gas outlet adjacent to the second end and configured to direct an exhaust gas from the reaction chamber; a plurality of preforms configured in a sequentially aligned arrangement within the reactor body, wherein each preform is configured with (1) at least one gas channel configured to extend from the top to the bottom of the preform, parallel to the direction of gas flow; and (2) a plurality of voids defining a porosity within the preform body sufficient to permit the sweep gas to flow therethrough; wherein each preform is configured from a mixture of precursor materials for a carbothermic reaction, such that the precursor mixture is reacted in the hot zone to form a ceramic powder product having uniform properties.
In some embodiments, the gas channel is configured as an area fraction from 0.05 area fraction to not greater than 0.8 area fraction of a cross-sectional area of the reaction chamber.
In some embodiments, the preform is configured from a plurality of granules, wherein each granule is configured from the precursor mixture.
In some embodiments, the voids are configured as intra-granule porosity in the preform.
In some embodiments, the intra-granule porosity is configured as an area fraction from 0 to not greater than 0.6 area fraction of a cross-sectional area of the preform.
In some embodiments, the voids are configured as inter-granule porosity in the preform.
In some embodiments, the inter-granule porosity is configured as an area fraction from 0 to not greater than 0.6 area fraction of a cross-sectional area of the preform exclusive of the gas channel.
In some embodiments, the voids are configured as a combination of inter-granule porosity and intra-granule porosity in the preform.
In some embodiments, at least one preform is configured within a container, and wherein the container is configured to permit the sweep gas to pass therethrough.
In one aspect of the instant disclosure, a system, comprises: a reactor body having a first end and a second end, wherein the reactor body is configured with an inner sidewall extending from the first end to the second end to define a reaction chamber; wherein the reactor body is configured with a heat source to provide a hot zone along the reaction chamber; a sweep gas inlet adjacent to the first end and configured to direct a sweep gas into the reaction chamber and a sweep gas outlet adjacent to the second end and configured to direct an exhaust gas from the reaction chamber; a powder configured from a mixture of precursor materials for a carbothermic reaction, the powder configured in the reactor chamber to permit sweep gas to flow there through, such that the precursor mixture is reacted in the hot zone to form a ceramic powder product having uniform properties.
To facilitate understanding, identical reference numerals have been used, where possible, to designate identical elements that are common to the figures. The figures are not drawn to scale and may be simplified for clarity. It is contemplated that elements and features of one embodiment may be beneficially incorporated in other embodiments without further recitation.
The present invention will be further explained with reference to the attached drawings, wherein like structures are referred to by like numerals throughout the several views. The drawings shown are not necessarily to scale, with emphasis instead generally being placed upon illustrating the principles of the present invention. Further, some features may be exaggerated to show details of particular components
The figures constitute a part of this specification and include illustrative embodiments of the present invention and illustrate various objects and features thereof. Further, the figures are not necessarily to scale, some features may be exaggerated to show details of particular components. In addition, any measurements, specifications and the like shown in the figures are intended to be illustrative, and not restrictive. Therefore, specific structural and functional details disclosed herein are not to be interpreted as limiting, but merely as a representative basis for teaching one skilled in the art to variously employ the present invention.
Among those benefits and improvements that have been disclosed, other objects and advantages of this invention will become apparent from the following description taken in conjunction with the accompanying figures. Detailed embodiments of the present invention are disclosed herein; however, it is to be understood that the disclosed embodiments are merely illustrative of the invention that may be embodied in various forms. In addition, each of the examples given in connection with the various embodiments of the invention which are intended to be illustrative, and not restrictive.
Throughout the specification and defined embodiments, the following terms take the meanings explicitly associated herein, unless the context clearly dictates otherwise. The phrases “in one embodiment” and “in some embodiments” as used herein do not necessarily refer to the same embodiment(s), though it may. Furthermore, the phrases “in another embodiment” and “in some other embodiments” as used herein do not necessarily refer to a different embodiment, although it may. Thus, as described below, various embodiments of the invention may be readily combined, without departing from the scope or spirit of the invention.
The term “based on” is not exclusive and allows for being based on additional factors not described, unless the context clearly dictates otherwise. In addition, throughout the specification, the meaning of “a,” “an,” and “the” include plural references. The meaning of “in” includes “in” and “on.
In some embodiments, the precursor mixture is formed by mixing the reagents (e.g. as set out in Table 1), with optional diluents and/or binders. In some embodiments, forming the precursor mixture further comprises one of: (a) forming a wet agglomerate (i.e. a mixture of the raw material reagents and a solvent such as water) having the reagents therein or (b) dry processing the reagents with compatible materials and/or binder, including but not limited to polyvinyl alcohol or ethyl cellulose, to form an agglomerate.
Referring to Table 1 below, examples of reagents and ceramic powder products are provided for three classes of ceramic powder products: borides, carbides, and nitrides. As shown in Table 1, the reagents that are combinable to form the precursor mixture are depicted in the first 1-4 columns, with the ceramic powder product identified to the right of the arrow (where the arrow denotes a carbothermic reaction of the precursor mixture to form the specified ceramic powder product). It is noted that carbonaceous gases such as carbon monoxide (not shown) are also produced via carbothermic reduction of the precursor materials.
Oxide
Carbide
Carbide
Oxide
Carbide
Oxide
Diboride
Oxide
Diboride
Oxide
Diboride
Oxide
Monoboride
Oxide
Nitride
Oxide
Nitride
Oxide
Nitride
indicates data missing or illegible when filed
In some embodiments, the amount of the titanium dioxide is 20 weight percent (wt. %) to 50 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the titanium dioxide is 25 wt. % to 50 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the titanium dioxide is 30 wt. % to 50 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the titanium dioxide is 35 wt. % to 50 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the titanium dioxide is 40 wt. % to 50 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the titanium dioxide is 45 wt. % to 50 wt. % based on a total weight of the precursor mixture.
In some embodiments, the amount of the titanium dioxide is 20 wt. % to 45 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the titanium dioxide is 20 wt. % to 40 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the titanium dioxide is 20 wt. % to 35 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the titanium dioxide is 20 wt. % to 30 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the titanium dioxide is 20 wt. % to 25 wt. % based on a total weight of the precursor mixture.
In some embodiments, the amount of the titanium dioxide is 25 wt. % to 45 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the titanium dioxide is 30 wt. % to 40 wt. % based on a total weight of the precursor mixture.
In some embodiments, the amount of the carbon source is 10 wt. % to 35 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the carbon source is 15 wt. % to 35 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the carbon source is 20 wt. % to 35 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the carbon source is 25 wt. % to 35 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the carbon source is 30 wt. % to 35 wt. % based on a total weight of the precursor mixture.
In some embodiments, the amount of the carbon source is 10 wt. % to 30 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the carbon source is 10 wt. % to 25 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the carbon source is 10 wt. % to 20 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the carbon source is 10 wt. % to 15 wt. % based on a total weight of the precursor mixture.
In some embodiments, the amount of the carbon source is 15 wt. % to 30 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the carbon source is 15 wt. % to 25 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of the carbon source is 20 wt. % to 25 wt. % based on a total weight of the precursor mixture.
In some embodiments, the amount of boric acid is 30 wt. % to 70 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 30 wt. % to 65 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 30 wt. % to 60 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 30 wt. % to 55 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 30 wt. % to 50 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 30 wt. % to 45 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 30 wt. % to 40 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 30 wt. % to 35 wt. % based on a total weight of the precursor mixture.
In some embodiments, the amount of boric acid is 35 wt. % to 70 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 40 wt. % to 70 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 45 wt. % to 70 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 50 wt. % to 70 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 55 wt. % to 70 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 60 wt. % to 70 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 65 wt. % to 70 wt. % based on a total weight of the precursor mixture.
In some embodiments, the amount of boric acid is 35 wt. % to 65 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 40 wt. % to 60 wt. % based on a total weight of the precursor mixture. In some embodiments, the amount of boric acid is 45 wt. % to 55 wt. % based on a total weight of the precursor mixture.
In some embodiments, the precursor mixture is formed into a preform. As used herein, “preform” means a shaped mixture of precursor materials configured to enable/permit gas to flow through the preform.
In one non-limiting example, forming of the precursor mixture into at least one preform includes adding the pliable, hydrated precursor mixture into a mold, compacting the mixture in the mold (e.g. in the target shape of the preform), followed by dehydrating the mixture at elevated temperatures (e.g. at sufficient temperature and time to (1) drive off water from the precursor mixture and (2) configure the preform in a hardened, stable shape).
In one non-limiting example, forming of the precursor mixture into at least one preform includes casting (pouring and/or directing) the flowable, hydrated precursor mixture into a mold, and processing the precursor mixture into the preform by (1) removing excess water from the precursor mixture to configure the preform from the as-cast shape.
In one non-limiting example, forming of the precursor mixture into at least one preform includes directing the pliable, hydrated precursor mixture into an extrusion press, and extruding the precursor mixture through an extrusion die in order to form an extrudate, followed by processing the extrudate to remove any excess water and provide a preform from the extruded precursor mixture.
In some embodiments, the preform is removed from the mold or cast support prior to being directed into the reactor body.
In some embodiments, the compacting step is conducted with a compaction tool.
In some embodiments, the dehydration step is conducted using air (or other gas) or heat (e.g. a furnace).
In some embodiments the preform is configured with (a) at least one gas channel and (b) macro-porosity in at least a portion of the preform body (e.g. where macro-porosity refers to sufficiently sized voids to permit gas to permeate through the preform).
In some embodiments, the preform is configured to take up 0.2 to 0.95 area fraction when viewing a cross-sectional area across the reaction chamber. In some embodiments, the preform is configured to take up: 0.5 to 0.95 area fraction; 0.55 to 0.95 area fraction; 0.6 to 0.95 area fraction; 0.65 to 0.95 area fraction; 0.7 to 0.95 area fraction; 0.75 to 0.95 area fraction; 0.8 to 0.95 area fraction; 0.85 to 0.95 area fraction; or 0.9 to 0.95 area fraction, when viewing a cross-sectional area across the reaction chamber.
In some embodiments, the preform is configured to take up: 0.2 to 0.90 area fraction; 0.2 to 0.85 area fraction; 0.2 to 0.80 area fraction; 0.2 to 0.75 area fraction; 0.2 to 0.70 area fraction; 0.2 to 0.65 area fraction; 0.2 to 0.60 area fraction; 0.2 to 0.55 area fraction; 0.2 to 0.50 area fraction; or 0.2 to 0.40 area fraction, when viewing a cross-sectional area across the reaction chamber.
In some embodiments, the preform is configured to take up 0.2 area fraction to not greater than 0.95 area fraction of a cross-sectional area taken across the reaction chamber. In some embodiments, the preform is configured to take up 0.6 area fraction to not greater than 0.95 area fraction of a cross-sectional area taken across the reaction chamber. In some embodiments, the preform is configured to take up 0.75 area fraction to not greater than 0.95 area fraction of a cross-sectional area taken across the reaction chamber.
In some embodiments, the preform is configured from a plurality of granules. In some embodiments, the preform is configured with inter-granule porosity, which is measured between granules of a single preform.
In some embodiments, the inter-granule porosity is configured to take up 0 to 0.6 area fraction when viewing a cross-sectional area across the preform exclusive of gas channels. In some embodiments, the inter-granule porosity is configured to take up: 0.1 to 0.6 area fraction; 0.2 to 0.6 area fraction; 0.3 area to 0.6 fraction; 0.4 to 0.6 area fraction; or 0.5 to 0.6 area fraction, when viewing a cross-sectional area across the preform, exclusive of gas channels.
In some embodiments, the inter-granule porosity is configured to take up: 0 to 0.5 area fraction; 0 to 0.4 area fraction; 0 to 0.3 area fraction; 0 to 0.2 area fraction; 0 to 0.1 area fraction, when viewing a cross-sectional area across the preform, exclusive of gas channels.
In some embodiments, the inter-granule porosity is configured to take up 0 area fraction to not greater than 0.6 area fraction of a cross-sectional area taken across the preform, exclusive of gas channels. In some embodiments, the preform is configured to take up 0.2 area fraction to not greater than 0.6 area fraction of a cross-sectional area taken across the preform, exclusive of gas channels. In some embodiments, the preform is configured to take up 0.3 area fraction to not greater than 0.6 area fraction of a cross-sectional area taken across the preform, exclusive of gas channels.
In some embodiments, the preform is configured with intra-granule porosity, which is measured within a single granule (e.g. porosity between precursor mixture/reagents).
In some embodiments, there is inter-granule porosity and no intra-granular porosity (0 area fraction). In some embodiments, there is intra-granule porosity and no inter-granule porosity.
In some embodiments, the intra-granule porosity is configured to take up not greater than 0 area fraction; not greater than 0.05 area fraction; not greater than 0.1 area fraction; not greater than 0.2 area fraction; not greater than 0.3 area fraction; not greater than 0.4 area fraction; not greater than 0.5 area fraction; or not greater than 0.6 area fraction, when viewing a cross-sectional area across the preform.
In some embodiments, the intra-granule porosity is configured to take up 0 area fraction to not greater than 0.6 area fraction of a cross-sectional area taken across the preform. In some embodiments, the intra-granule porosity is configured to take up 0 area fraction to not greater than 0.5 area fraction of a cross-sectional area taken across the preform. In some embodiments, the intra-granule porosity is configured to take up 0 area fraction to not greater than 0.4 area fraction of a cross-sectional area taken across the preform. In some embodiments, the intra-granule porosity is configured to take up 0 area fraction to not greater than 0.3 area fraction of a cross-sectional area taken across the preform.
In some embodiments, the preform is configured with at least one gas channel.
As used herein, “gas channel” refers to the open space/volume that is not taken up by the preform (and/or the container, if a container is utilized), in the cross-sectional area of the reaction chamber. In some embodiments, the gas channel is configured in a direction parallel to the gas flow through the preform body.
In some embodiments, the gas channel is configured to take up 0.05 to 0.8 area fraction when viewing a cross-sectional area across the reaction chamber. In some embodiments, the gas channel is configured to take up: 0.1 to 0.8 area fraction; 0.1 to 0.7 area fraction; 0.1 to 0.6 area fraction; 0.1 to 0.5 area fraction; 0.1 to 0.4 area fraction; 0.1 to 0.3 area fraction; or 0.1 to 0.2 area fraction, when viewing a cross-sectional area across the reaction chamber.
In some embodiments, the gas channel is configured to take up: 0.1 to 0.8 area fraction; 0.2 to 0.8 area fraction; 0.3 to 0.8 area fraction; 0.4 to 0.8 area fraction; 0.5 to 0.8 area fraction; 0.6 to 0.8 area fraction; or 0.7 to 0.8 area fraction, when viewing a cross-sectional area across the reaction chamber.
In some embodiments, the gas channel is configured to take up from at least 0.05 area fraction to not greater than 0.8 area fraction, of a cross-sectional area taken across the reaction chamber. In some embodiments, the gas channel is configured to take up at least 0.1 area fraction to not greater than 0.8 area fraction, of a cross-sectional area taken across the reaction chamber. In some embodiments, the gas channel is configured to take up from at least 0.2 area fraction to not greater than 0.8 area fraction, of a cross-sectional area taken across the reaction chamber. In some embodiments, the gas channel is configured to take up from at least 0.3 area fraction to not greater than 0.8 area fraction, of a cross-sectional area taken across the reaction chamber.
In some embodiments, when the preform is sized such that one or more preforms fit into a container, one or more gas channels are configured from the container (e.g. a mesh wall defining a vertical gas channel within the plurality of preforms, see, e.g.
In some embodiments, the diameter of the preform is 2 inches to 48 inches. In some embodiments, the diameter of the preform is 2 inches to 42 inches. In some embodiments, the diameter of the preform is 2 inches to 36 inches. In some embodiments, the diameter of the preform is 2 inches to 30 inches. In some embodiments, the diameter of the preform is 2 inches to 24 inches. In some embodiments, the diameter of the preform is 2 inches to 18 inches. In some embodiments, the diameter of the preform is 2 inches to 12 inches. In some embodiments, the diameter of the preform is 2 inches to 10 inches. In some embodiments, the diameter of the preform is 2 inches to 8 inches. In some embodiments, the diameter of the preform is 2 inches to 6 inches. In some embodiments, the diameter of the preform is 2 inches to 4 inches.
In some embodiments, the diameter of the preform is 4 inches to 48 inches. In some embodiments, the diameter of the preform is 6 inches to 48 inches. In some embodiments, the diameter of the preform is 8 inches to 48 inches. In some embodiments, the diameter of the preform is 10 inches to 48 inches. In some embodiments, the diameter of the preform is 12 inches to 48 inches. In some embodiments, the diameter of the preform is 18 inches to 48 inches. In some embodiments, the diameter of the preform is 24 inches to 48 inches. In some embodiments, the diameter of the preform is 30 inches to 48 inches. In some embodiments, the diameter of the preform is 36 inches to 48 inches. In some embodiments, the diameter of the preform is 42 inches to 48 inches.
In some embodiments, the diameter of the preform is 4 inches to 6 inches. In some embodiments, the diameter of the preform is 4 inches to 8 inches. In some embodiments, the diameter of the preform is 4 inches to 10 inches. In some embodiments, the diameter of the preform is 6 inches to 12 inches. In some embodiments, the diameter of the preform is 12 inches to 24 inches. In some embodiments, the diameter of the preform is 24 inches to 36 inches. In some embodiments, the diameter of the preform is 36 inches to 48 inches.
In some embodiments, the “diameter of the at least one opening” means either the diameter of each opening or the sum of the diameters of all the openings in the preform. In some embodiments, the diameter of the at least one opening is 0 inches to 46 inches. In some embodiments, the diameter of the at least one opening is ¼ inch to 46 inches. In some embodiments, the diameter of the at least one opening is 2 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 3 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 4 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 5 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 8 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 12 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 16 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 20 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 24 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 28 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 32 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 36 inches to 46 inches. In some embodiments, the diameter of the at least one opening is 40 inches to 46 inches.
In some embodiments, the diameter of the at least one opening is 0 inches to 42 inches. In some embodiments, the diameter of the at least one opening is 0 inches to 36 inches. In some embodiments, the diameter of the at least one opening is 0 inches to 32 inches. In some embodiments, the diameter of the at least one opening is 0 inches to 28 inches. In some embodiments, the diameter of the at least one opening is 0 inches to 24 inches. In some embodiments, the diameter of the at least one opening is 0 inches to 20 inches. In some embodiments, the diameter of the at least one opening is 0 inches to 16 inches. In some embodiments, the diameter of the at least one opening is 0 inches to 12 inches. In some embodiments, the diameter of the at least one opening is 0 inches to 10 inches. In some embodiments, the diameter of the at least one opening is 0 inches to 8 inches. In some embodiments, the diameter of the at least one opening is 0 inches to 6 inches. In some embodiments, the diameter of the at least one opening is 0 inches to 4 inches.
In some embodiments, the diameter of the at least one opening is 1 inches to 3 inches. In some embodiments, the diameter of the at least one opening is 3 inches to 8 inches. In some embodiments, the diameter of the at least one opening is 6 inches to 24 inches. In some embodiments, the diameter of the at least one opening is 10 inches to 30 inches. In some embodiments, the diameter of the at least one opening is 12 inches to 36 inches.
In some embodiments, the diameter of the at least one opening is based, at least in part, on achieving substantially uniform heating throughout the preform (i.e. throughout the volume of the preform).
In some embodiments, the height of the preform is 2 inches to 48 inches. In some embodiments, the height of the preform is 4 inches to 48 inches. In some embodiments, the height of the preform is 6 inches to 48 inches. In some embodiments, the height of the preform is 8 inches to 48 inches. In some embodiments, the height of the preform is 12 inches to 48 inches. In some embodiments, the height of the preform is 16 inches to 48 inches. In some embodiments, the height of the preform is 20 inches to 48 inches. In some embodiments, the height of the preform is 24 inches to 48 inches. In some embodiments, the height of the preform is 28 inches to 48 inches. In some embodiments, the height of the preform is 32 inches to 48 inches. In some embodiments, the height of the preform is 36 inches to 48 inches. In some embodiments, the height of the preform is 40 inches to 48 inches. In some embodiments, the height of the preform is 44 inches to 48 inches.
In some embodiments, the height of the preform is 2 inches to 44 inches. In some embodiments, the height of the preform is 2 inches to 40 inches. In some embodiments, the height of the preform is 2 inches to 36 inches. In some embodiments, the height of the preform is 2 inches to 32 inches. In some embodiments, the height of the preform is 2 inches to 28 inches. In some embodiments, the height of the preform is 2 inches to 24 inches. In some embodiments, the height of the preform is 2 inches to 20 inches. In some embodiments, the height of the preform is 2 inches to 16 inches. In some embodiments, the height of the preform is 2 inches to 12 inches. In some embodiments, the height of the preform is 2 inches to 8 inches. In some embodiments, the height of the preform is 2 inches to 6 inches. In some embodiments, the height of the preform is 2 inches to 4 inches.
In some embodiments, the height of the preform is 4 inches to 8 inches. In some embodiments, the height of the preform is 8 inches to 16 inches. In some embodiments, the height of the preform is 12 inches to 24 inches. In some embodiments, the height of the preform is 8 inches to 42 inches. In some embodiments, the height of the preform is 4 inches to 8 inches. In some embodiments, the height of the preform is 16 inches to 28 inches. In some embodiments, the height of the preform is 6 inches to 24 inches.
Next, at 104, the method 100 comprises directing a sweep gas from a first end of the reactor, through the at least one preform, and into the second end of the reactor.
In some embodiments, when the ceramic powder is a carbide, the sweep gas is selected from the group of: argon or any other noble gas, carbon monoxide, carbon dioxide, and/or combinations thereof.
In some embodiments, when the ceramic powder is a nitride, the sweep gas is nitrogen or combinations of nitrogen and noble gas. In some embodiments, when the ceramic powder is a boride, the sweep gas is argon or any other noble gas.
In some embodiments, the flow rate of the sweep gas is sufficient to remove or reduce the concentration of the reaction byproducts in the reactor and/or sufficient to manage atmospheric chemistry in the reactor. In some embodiments, the sweep gas flow rate is based, at least in part, on the reactor geometry, the desired ceramic powder, the temperature profile within the reactor and/or other process conditions related to the powder production.
In some embodiments, the sufficient time is dependent on type of reagents and powder and the sufficient temperature. In some embodiments, the sufficient time is 0.5 hour to 12 hours. In some embodiments, the sufficient time is 0.5 hour to 11 hours. In some embodiments, the sufficient time is 0.5 hour to 10 hours. In some embodiments, the sufficient time is 0.5 hour to 9 hours. In some embodiments, the sufficient time is 0.5 hour to 8 hours. In some embodiments, the sufficient time is 0.5 hour to 7 hours. In some embodiments, the sufficient time is 0.5 hour to 6 hours. In some embodiments, the sufficient time is 0.5 hour to 5 hours. In some embodiments, the sufficient time is 0.5 hour to 4 hours. In some embodiments, the sufficient time is 0.5 hour to 3 hours. In some embodiments, the sufficient time is 0.5 hour to 2 hours. In some embodiments, the sufficient time is 0.5 hour to 1 hours.
In some embodiments, the sufficient time is 1 hour to 12 hours. In some embodiments, the sufficient time is 2 hours to 12 hours. In some embodiments, the sufficient time is 3 hours to 12 hours. In some embodiments, the sufficient time is 4 hours to 12 hours. In some embodiments, the sufficient time is 5 hours to 12 hours. In some embodiments, the sufficient time is 6 hours to 12 hours. In some embodiments, the sufficient time is 7 hours to 12 hours. In some embodiments, the sufficient time is 8 hours to 12 hours. In some embodiments, the sufficient time is 9 hours to 12 hours. In some embodiments, the sufficient time is 10 hours to 12 hours. In some embodiments, the sufficient time is 11 hours to 12 hours.
In some embodiments, the sufficient time is 1 hour to 8 hours. In some embodiments, the sufficient time is 1 hour to 6 hours. In some embodiments, the sufficient time is 1 hour to 4 hours. In some embodiments, the sufficient time is 1 hour to 2 hours. In some embodiments, the sufficient time is 2 hour to 11 hours. In some embodiments, the sufficient time is 3 hour to 10 hours. In some embodiments, the sufficient time is 4 hour to 9 hours. In some embodiments, the sufficient time is 5 hour to 8 hours. In some embodiments, the sufficient time is 6 hour to 7 hours.
In some embodiments, the powder is titanium diboride and the sufficient time is 1 hour to 6 hours. In some embodiments, the powder is titanium diboride and the sufficient time is 1 hour to 5 hours. In some embodiments, the powder is titanium diboride and the sufficient time is 1 hour to 4 hours. In some embodiments, the powder is titanium diboride and the sufficient time is 1 hour to 3 hours. In some embodiments, the powder is titanium diboride and the sufficient time is 1 hour to 2 hours. In some embodiments, the powder is titanium diboride and the sufficient time is 2 hour to 6 hours. In some embodiments, the powder is titanium diboride and the sufficient time is 3 hour to 6 hours. In some embodiments, the powder is titanium diboride and the sufficient time is 4 hour to 6 hours. In some embodiments, the powder is titanium diboride and the sufficient time is 5 hour to 6 hours.
In some embodiments, the sufficient temperature and sufficient time are combinations of the temperatures and times detailed above.
Next, at 106, the method 100 comprises carbothermically reacting the at least one preform within the reactor body, concomitant with directing the sweep gas. In some embodiments, carbothermically reacting the at least one preform within the reactor body, concomitant with directing the sweep gas comprises: directing the at least one preform (e.g. housed/retained in a container) through the reactor body, and heating the at least one preform (comprising a precursor mixture) to a sufficient temperature for a sufficient time to form a ceramic powder product via carbothermic reaction of the reagents in the precursor mixture. Non-limiting examples of carbothermic reactions forming ceramic powders are shown in Table 1
As used herein, the term “carbothermic reaction” means a reaction that includes the reduction of substances using carbon as the reducing agent at elevated temperatures typically ranging from about 500 to about 2,500 degrees Celsius. In some embodiments, the sufficient temperature (to carbothermically react the precursor mixture) is dependent on the type of reagents and powder utilized to form the precursor mixture.
Next, at 108, the method 100 comprises forming a ceramic powder product configured with uniform and/or consistent properties. In some embodiments, the method 100 continuously produces the ceramic powder products in the heated reactor, including as non-limiting examples: borides, nitrides, and/or carbides. In some embodiments, the ceramic powder is any powder described herein. In some embodiments, the ceramic powder product includes, but is not limited to, titanium diboride, boron carbide, boron nitride, aluminum nitride, silicon aluminum nitride, zirconium diboride, aluminum nitride, silicon aluminum oxy-nitride, titanium carbide, silicon carbide, titanium nitride, and aluminum carbide.
As used herein, “consistent properties” means: that preforms that are directed through the carbothermic reactor (e.g. at different times and/or in different containers) exhibit properties including but not limited to particle size distribution, surface area, chemical composition, and particle shape, that are measurably indistinguishable and/or compatible with the specification for the final ceramic powder product (e.g. where properties are analytically determined and/or evaluated).
As used herein, “uniform properties” means: that the properties (e.g. qualitatively measured and/or quantitatively measured) are generally unchanging and/or invariable in form or character (e.g. in comparing ceramic powder product recovered from one preform to ceramic powder product recovered from another preform).
In some embodiments, the method further comprises removing the ceramic powder product from the reactor. In some embodiments, the ceramic powder product is removed from the reactor in a receiving unit having an inert atmosphere so as to maintain an inert environment in the vertical reactor.
In some embodiments, a cross-section of the reactor body is in a circle, square, rectangular, pentagon, hexagon, or any other suitable shape. In some embodiments, the reactor is graphite, silicon carbide, boron nitride, alumina, molybdenum, tungsten, or other refractory materials that are compatible with the reagents and/or byproducts.
As shown in
After the preform 36 travels through the staging area 42, the preform 36 crosses the seal 46 adjacent to the first end 14 of the reactor body and is introduced into the reaction chamber 20. The preform 36 and/or container 34 is sufficiently sized such that it is retained in close proximity with the inner sidewall 18 of the reactor 12 such that the outer diameter of the container 34 is less than the diameter of the inner sidewall 18. The preform 36 (e.g. and container) is heated in the preheat zone 44, after which the preform 36 is directed into the hot zone 24 of the reaction chamber 20. In the hot zone 24, the temperature is sufficient to promote carbothermic reaction of the precursor material 38, provided the preforms 36 are retained in the hot zone 24 for a sufficient time.
Within the reaction chamber 20, the containers 34 containing at least one preform 36 are aligned with each other such that the containers are sequentially configured throughout the reaction chamber. The ends of containers 34 are coincidental to one another such that the containers 34 are arranged in a position relative to one another such that each individual container is a component 70 of a sequentially configured container assembly in the reaction chamber 20. Thus, as depicted in
As depicted in
As the preforms reach the end of the reaction chamber 20, the preforms 36 are directed through a seal 52 (configured adjacent to the second end 16) and directed out of the reactor to the receiving unit 60. As the preforms 36 are adjacent to the second end 16 and/or seal 52, the carbothermic reaction of precursor materials is complete, yielding the ceramic powder product 40. In some embodiments, the ceramic powder product 40 is generally retained in the preform 36, such that once received in the receiving unit 60, a deagglomeration step or breaking up of the preform 36 shape may be utilized to yield a ceramic powder product 40 (e.g. deagglomerated powder).
In some embodiments, the reactor includes a lid configured to direct process gas flow into or out of the reactor. In some embodiments, the lid is configured with a plurality of openings to allow for control of the gas flow rate into and out of the reactor.
In some embodiments, the inner diameter and the height (or length) of the reactor body are selected based on the diameter, thickness and number of preforms to be positioned in the reactor. In some embodiments, the inner diameter of the reactor is sufficiently greater than the diameter of the preform so as to allow flow of the inert gas between the reactor and the preform and/or to reduce or eliminate contact of the preform with a sidewall of the reactor. In some embodiments, the reactor includes a sufficient number of preforms (e.g. configured in containers) to fill the reactor based on the height (or length if horizontal) of the reactor. In some embodiments, the number of preforms in the reactors is the height (or length if horizontal) of the reactor divided by the height of the preform.
In some embodiments, the preforms are stacked in, added to and/or removed from the reactor at a controlled rate by any suitable mechanical devices, configurations, components, and/or related means. In some embodiments, the controlled rate of stacking, adding and removing the preforms is based, at least in part, on the reaction rate of the reagents in the preform. In some embodiments, the unreacted preforms and the reacted preforms are added to and removed from the reactor through a seal (e.g. configured with a sweep gas) so that the process atmosphere is maintained within the reactor.
More specifically referring to
More specifically, D depicts a plurality of rods retained in a generally parallel configuration with sufficient vapor space in the container to promote communication of off gases from the rods and through the container end); E depicts a plurality of vertically and generally parallel stacked forms (e.g. brick preforms) in the container; F depicts a plurality of sphere preforms retained in the container; G depicts heterogeneously sized preforms in the container (spheres having different sized diameters: small, medium, and large); while H depicts a plurality of preforms that are each a compacted solid material.
In some embodiments, the preforms shown in
In some embodiments, the ceramic powders detailed herein may be used for multiple applications. In some embodiments, the ceramic powders are specifically tailored to be processed via ceramics processing techniques in order to form ceramic products (wherein the ceramic products are tailored for their application, based on the consistent and/or uniform properties of the ceramic powder product).
While a number of embodiments of the present invention have been described, it is understood that these embodiments are illustrative only, and not restrictive, and that many modifications may become apparent to those of ordinary skill in the art. Further still, the various steps may be carried out in any desired order (and any desired steps may be added and/or any desired steps may be eliminated).
This application is a continuation of U.S. patent application Ser. No. 16/241,517, filed Jan. 7, 2019, which is a continuation of International Patent Application No. PCT/US2017/041057, filed Jul. 7, 2017, which claims benefit of U.S. provisional application No. 62/360,079, filed Jul. 8, 2016, each of which is herein incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62360079 | Jul 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16241517 | Jan 2019 | US |
| Child | 17443603 | US | |
| Parent | PCT/US2017/041057 | Jul 2017 | US |
| Child | 16241517 | US |