Patent Application
20240413407
Embodiments described herein relate to electrochemical cells formulated to minimize damage from dendrite formation.
Dendrite formation in electrochemical cells can lead to short circuiting and heat generation. Heat generation in electrochemical cells is a safety issue that can have dangerous results. Thermal runaway can lead to fires and thermal decomposition of the electrochemical cell materials. By minimizing the size to which dendrites can grow, significant safety issues can be avoided.
Embodiments described herein relate to electrochemical cells with dendrite prevention mechanisms, and methods of producing and operating the same. In some aspects, an electrochemical cell can include an anode disposed on an anode current collector, a cathode disposed on a cathode current collector, the cathode having a first thickness at a proximal end of the cathode and a second thickness at a distal end of the cathode, the second thickness greater than the first thickness, a first separator disposed on the anode, a second separator disposed on the cathode, an interlayer disposed between the first separator and the second separator, the interlayer including electroactive material and having a proximal end and a distal end, and a power source electrically connected to the proximal end of the cathode and the proximal end of the interlayer, the power source configured to maintain a voltage difference between the cathode and the interlayer below a threshold value. In some embodiments, the threshold value can be about 0.01 V. In some embodiments, the cathode can include at least In some embodiments, the interlayer can include Li(1−x)xNMC wherein x is an integer. In some embodiments, the anode can include graphite. In some embodiments, the second thickness can be greater than the first thickness by about 500 nm to about 5 μm.
Embodiments described herein relate to cells with interlayers, and methods of operating the same. An interlayer can include a layer of electroactive material placed between an anode and a cathode of an electrochemical cell. The interlayer can be disposed between a first separator and a second separator. Interlayers can be used to detect dendrites before they grow too large, such that the dendrites would cause safety hazards. A battery management system (BMS) can be connected to the electrochemical cell to detect when a dendrite enters the interlayer and safely discharge the remaining energy in the electrochemical cell. In some embodiments, the discharge energy can be used to power other devices, such as heaters, removing cell energy to create a safe condition.
In some embodiments, the BMS can be used to draw energy through the interlayer, causing the dendrite to dissolve. This effectively removes the dendrite from the electrochemical cell. In some embodiments, energy for dissolution of the dendrite can be produced via a power supply in the BMS. In some embodiments, energy for dissolution of the dendrite can be produced by drawing energy from the cathode to increase the interlayer voltage relative to the anode.
In some embodiments, the BMS can be used to detect the voltage of the interlayer with respect to the anode, in order to detect the formation of the dendrite. The detection can include the estimation of the relative voltage of the interlayer to both the anode and the cathode. If the voltage of the interlayer decreases with respect to the cathode (e.g., if the voltage difference between the interlayer and the cathode is greater than about 0.1 V, greater than about 0.2 V, greater than about 0.3 V, greater than about 0.4 V, greater than about 0.5 V, greater than about 0.6 V, greater than about 0.7 V, greater than about 0.8 V, greater than about 0.9 V, greater than about 1 V, greater than about 1.5 V, greater than about 2 V, greater than about 2.5 V, or greater than about 3 V, inclusive of all values and ranges therebetween), a signal can be provided to a vehicle housing the electrochemical cell to set a warning that the vehicle needs service. The threshold voltage can be a function of the design of the electrochemical cell and the interlayer. In some embodiments, the voltage difference between the interlayer and the anode can be used to trigger the service warning. In some embodiments, a combination of voltages between the anode, cathode, and/or the interlayer can be used to trigger the service warning. In some embodiments, a rate of change of the voltage of the interlayer can be used to evaluate warnings and faults in the electrochemical cell and/or in the vehicle. In some embodiments, the rate of change of the interlayer voltage can be used to perform control functions to eliminate the dendrite.
In some embodiments, a significant voltage difference between the interlayer and the cathode (e.g., at least about 0.5 V, at least about 1 V, at least about 1.5 V, at least about 2 V, at least about 2.5 V, at least about 3 V, at least about 3.5 V, at least about 4 V, at least about 4.5 V, at least about 5 V, at least about 5.5 V, or at least about 6 V, inclusive of all values and ranges therebetween) can trigger a warning signal that electrochemical cell failure and/or vehicle failure is imminent. In some embodiments, the BMS can limit discharge current of the electrochemical cell to create a reduction of power to the vehicle. This can be by directly limiting power and/or by communication of limits to a vehicle controller or another controller in the vehicle, depending on the vehicle's design.
In some embodiments, voltage can be measured between the anode and the interlayer. In some embodiments, the voltage can be measured between the cathode and the interlayer. In some embodiments, the voltages can be measured via a proportional-integral (PI) loop. The voltage between the anode and the interlayer and the voltage between the cathode and the interlayer preferably remain consistent throughout a charging process. In some embodiments, an external component can be used to maintain the interlayer near the cathode voltage. In some embodiments, the external component can include a diode, a resistor, a fuse, a transistor (Bi junction, field-effect transistor (FET), etc.), or any combination thereof.
In some embodiments, the interlayer can be chemically configured to remove the dendrite as the dendrite protrudes into the interlayer. For example, a high potential applied to the interlayer can oxidize and dissolve the dendrite. In some embodiments, the interlayer can include one or more solid layers that physically block dendrites from penetrating the interlayer. In some embodiments, the solid layer can include a solid-state electrolyte.
In some embodiments, a resistance can be applied to the interlayer. The resistance can provide a continuous excitation of the interlayer such that a dendrite would not be able to form across the dendrite and both separator layers. Such a prevention method can be used as part of an overall control strategy where the voltage potential, current, resistance to interlayer could be changed based on a control algorithm.
A control system can act in an active prevention mode, where the potential of the interlayer is modulated or changed to apply different voltage potentials. The voltage potentials can be increased (i.e., changed to be more similar to cathode side) or decreased (changed to be more similar to anode side) to maintain the cell function. When the dendrite forms and interfaces with the interlayer, the voltage of the interlayer is increased to be more similar to the cathode potential, with respect to the anode. The dendrite is dissolved or remediated, and the voltage potential of the interlayer returns to near the voltage potential of the cathode with respect to the anode.
Dendrite growth in lithium cells is often detected via a thermal event (i.e., a sudden spike in temperature). In many cases, cell damage has already occurred once the thermal event is detected. Embodiments described herein relate to measurement of voltage potential of a separator layer (i.e., including an interlayer) relative to the anode and/or the cathode. Voltage potential is used to detect dendrite growth into the separator layer. Dendrite growth causes a voltage change in the separator layer relative to the anode and/or the cathode. Detection of the voltage change allows direct sensing of the dendrite growth before a safety event occurs. In some embodiments, the voltage potential of the interlayer can be altered or modulated to stop the growth of the dendrite or make the dendrite shrink. The voltage can be actively changed by a control system to remediate the dendrite formation at a separator layer. Voltage increases relative to an anode can prevent dendritic growth through a separator. Voltage decreases relative to an anode can dissolve dendritic growth in the active area. Modulation of the voltage on the interlayer separator can affect the ability of the electrodes to flow current into the cell. For example, inputting a voltage to the separator layer that is greater than the anode can reduce, or prevent charge current from flowing into the cell. This will provide a means to control current flow within the cell without utilizing an traditional external switching device, or as a primary or secondary means of current flow control.
Further descriptions of electrochemical cells with multiple separators and interlayers can be found in U.S. Patent Publication No. 2022/0352597 (“the '597 publication”), filed Apr. 29, 2022 and titled “Electrochemical Cells with Multiple Separators and Methods of Producing the Same,” the disclosure of which is hereby incorporated by reference in its entirety.
In some embodiments, electrodes described herein can include conventional solid electrodes. In some embodiments, the solid electrodes can include binders. In some embodiments, electrodes described herein can include semi-solid electrodes. Semi-solid electrodes described herein can be made: (i) thicker (e.g., greater than 100 μm-up to 2,000 μm or even greater) due to the reduced tortuosity and higher electronic conductivity of the semi-solid electrode, (ii) with higher loadings of active materials, and (iii) with a simplified manufacturing process utilizing less equipment. These relatively thick semi-solid electrodes decrease the volume, mass and cost contributions of inactive components with respect to active components, thereby enhancing the commercial appeal of batteries made with the semi-solid electrodes. In some embodiments, the semi-solid electrodes described herein are binderless and/or do not use binders that are used in conventional battery manufacturing. Instead, the volume of the electrode normally occupied by binders in conventional electrodes, is now occupied by: 1) electrolyte, which has the effect of decreasing tortuosity and increasing the total salt available for ion diffusion, thereby countering the salt depletion effects typical of thick conventional electrodes when used at high rate, 2) active material, which has the effect of increasing the charge capacity of the battery, or 3) conductive additive, which has the effect of increasing the electronic conductivity of the electrode, thereby countering the high internal impedance of thick conventional electrodes. The reduced tortuosity and a higher electronic conductivity of the semi-solid electrodes described herein, results in superior rate capability and charge capacity of electrochemical cells formed from the semi-solid electrodes. Since the semi-solid electrodes described herein, can be made substantially thicker than conventional electrodes, the ratio of active materials (i.e., the semi-solid cathode and/or anode) to inactive materials (i.e., the current collector and separator) can be much higher in a battery formed from electrochemical cell stacks that include semi-solid electrodes relative to a similar battery formed form electrochemical cell stacks that include conventional electrodes. This substantially increases the overall charge capacity and energy density of a battery that includes the semi-solid electrodes described herein.
In some embodiments, the electrode materials described herein can be a flowable semi-solid or condensed liquid composition. In some embodiments, the electrode materials described herein can be binderless or substantially free of binder. A flowable semi-solid electrode can include a suspension of an electrochemically active material (anodic or cathodic particles or particulates), and optionally an electronically conductive material (e.g., carbon) in a non-aqueous liquid electrolyte. Said another way, the active electrode particles and conductive particles are co-suspended in an electrolyte to produce a semi-solid electrode. Examples of battery architectures utilizing semi-solid suspensions are described in International Patent Publication No. WO 2012/024499, entitled “Stationary, Fluid Redox Electrode,” and International Patent Publication No. WO 2012/088442, entitled “Semi-Solid Filled Battery and Method of Manufacture,” the entire disclosures of which are hereby incorporated by reference.
As used in this specification, the singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, the term “a member” is intended to mean a single member or a combination of members, “a material” is intended to mean one or more materials, or a combination thereof.
The term “substantially” when used in connection with “cylindrical,” “linear,” and/or other geometric relationships is intended to convey that the structure so defined is nominally cylindrical, linear or the like. As one example, a portion of a support member that is described as being “substantially linear” is intended to convey that, although linearity of the portion is desirable, some non-linearity can occur in a “substantially linear” portion. Such non-linearity can result from manufacturing tolerances, or other practical considerations (such as, for example, the pressure or force applied to the support member). Thus, a geometric construction modified by the term “substantially” includes such geometric properties within a tolerance of plus or minus 5% of the stated geometric construction. For example, a “substantially linear” portion is a portion that defines an axis or center line that is within plus or minus 5% of being linear.
As used herein, the term “set” and “plurality” can refer to multiple features or a singular feature with multiple parts. For example, when referring to a set of electrodes, the set of electrodes can be considered as one electrode with multiple portions, or the set of electrodes can be considered as multiple, distinct electrodes. Additionally, for example, when referring to a plurality of electrochemical cells, the plurality of electrochemical cells can be considered as multiple, distinct electrochemical cells or as one electrochemical cell with multiple portions. Thus, a set of portions or a plurality of portions may include multiple portions that are either continuous or discontinuous from each other. A plurality of particles or a plurality of materials can also be fabricated from multiple items that are produced separately and are later joined together (e.g., via mixing, an adhesive, or any suitable method).
As used herein, the term “semi-solid” refers to a material that is a mixture of liquid and solid phases, for example, such as a particle suspension, a slurry, a colloidal suspension, an emulsion, a gel, or a micelle.
In some embodiments, the anode 110 and/or the cathode 130 can include at least about 0.1%, at least about 0.2%, at least about 0.3%, at least about 0.4%, at least about 0.5%, at least about 0.6%, at least about 0.7%, at least about 0.8%, at least about 0.9%, at least about 1%, at least about 2%, at least about 3%, at least about 4%, at least about 5%, at least about 6%, at least about 7%, at least about 8%, at least about 9%, at least about 10%, at least about 11%, at least about 12%, at least about 13%, at least about 14%, at least about 15%, at least about 16%, at least about 17%, at least about 18%, at least about 19%, at least about 20%, at least about 21%, at least about 22%, at least about 23%, or at least about 24% by volume of liquid electrolyte solution. In some embodiments, the anode 110 and/or the cathode 130 can include no more than about 25%, no more than about 24%, no more than about 23%, no more than about 22%, no more than about 21%, no more than about 20%, no more than about 19%, no more than about 18%, no more than about 17%, no more than about 16%, no more than about 15%, no more than about 14%, no more than about 13%, no more than about 12%, no more than about 11%, no more than about 10%, no more than about 9%, no more than about 8%, no more than about 7%, no more than about 6%, no more than about 5%, no more than about 4%, no more than about 3%, no more than about 2%, no more than about 1%, no more than about 0.9%, no more than about 0.8%, no more than about 0.7%, no more than about 0.6%, no more than about 0.5%, no more than about 0.4%, no more than about 0.3%, or no more than about 0.2% by volume of liquid electrolyte solution.
Combinations of the above-referenced volumetric percentages of liquid electrolyte solution in the anode 110 and/or the cathode 130 are also possible (e.g., at least about 0.1% and no more than about 25% or at least about 5% and no more than about 10%), inclusive of all values and ranges therebetween. In some embodiments, the anode 110 and/or the cathode 130 can include about 0.1%, about 0.2%, about 0.3%, about 0.4%, about 0.5%, about 0.6%, about 0.7%, about 0.8%, about 0.9%, about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, about 10%, about 11%, about 12%, about 13%, about 14%, about 15%, about 16%, about 17%, about 18%, about 19%, about 20%, about 21%, about 22%, about 23%, about 24%, or about 25% by volume of liquid electrolyte solution.
In some embodiments, the anode current collector 120 and/or the cathode current collector 140 can be composed of copper, aluminum, titanium, or other metals that do not form alloys or intermetallic compounds with lithium, carbon, and/or coatings comprising such materials disposed on another conductor. In some embodiments, the anode current collector 120 and/or the cathode current collector 140 can have a thickness of at least about 1 μm, at least about 5 μm, at least about 10 μm, at least about 15 μm, at least about 20 μm, at least about 25 μm, at least about 30 μm, at least about 35 μm, at least about 40 μm, or at least about 45 μm. In some embodiments, the anode current collector 120 and/or the cathode current collector 140 can have a thickness of no more than about 50 μm, no more than about 45 μm, no more than about 40 μm, no more than about 35 μm, no more than about 30 μm, no more than about 25 μm, no more than about 20 μm, no more than about 15 μm, no more than about 10 μm, or no more than about 5 μm. Combinations of the above-referenced thicknesses of the anode current collector 120 and/or the cathode current collector 140 are also possible (e.g., at least about 1 μm and no more than about 50 μm or at least about 10 μm and no more than about 30 μm), inclusive of all values and ranges therebetween. In some embodiments, the anode current collector 120 and/or the cathode current collector 140 can have a thickness of about 1 μm, about 5 μm, about 10 μm, about 15 μm, about 20 μm, about 25 μm, about 30 μm, about 35 μm, about 40 μm, about 45 μm, or about 50 μm.
In some embodiments, the anode 110 can include a first electrolyte and the cathode 130 can include a second electrolyte. In other words, and the anode 110 can include an anolyte and the cathode 130 can include a catholyte. In some embodiments, the electrochemical cell 100 can include an anolyte disposed on the anode side of the separators 150. In some embodiments, the electrochemical cell 100 can include a catholyte disposed on the cathode side of the separators 150. In some embodiments, the electrochemical cell 100 can include a selectively permeable membrane. In some embodiments, the selectively permeable membrane can be disposed between the first separator 150a and the second separator 150b. Electrochemical cells with anolytes, catholytes, and/or selectively permeable membranes are described in U.S. Pat. No. 10,734,672 (“the '672 patent”), filed Jan. 8, 2019, and titled, “Electrochemical Cells Including Selectively Permeable Membranes, Systems and Methods of Manufacturing the Same,” the disclosure of which is hereby incorporated by reference in its entirety.
As shown, the first separator 150a is disposed on the anode 110 while the second separator 150b is disposed on the cathode 130. In some embodiments, the separators 150 can be disposed on their respective electrodes during production of the electrochemical cell 100. In some embodiments, the first separator 150a and/or the second separator 150b can be composed of polyethylene, polypropylene, high density polyethylene, polyethylene terephthalate, polystyrene, a thermosetting polymer, hard carbon, a thermosetting resin, a polyimide, a ceramic coated separator, an inorganic separator, cellulose, glass fiber, a polyethylenoxide (PEO) polymer in which a lithium salt is complexed to provide lithium conductivity, Nation™ membranes which are proton conductors, or any other suitable separator material, or combinations thereof. In some embodiments, the first separator 150a can be composed of the same material as the second separator 150b. In some embodiments, the first separator 150a can be composed of a different material from the second separator 150b.
In some embodiments, the first separator 150a and/or the second separator 150b can have a porosity of at least about 10%, at least about 15%, at least about 20%, at least about 25%, at least about 30%, at least about 35%, at least about 40%, at least about 45%, at least about 50%, at least about 55%, at least about 60%, at least about 65%, at least about 70%, at least about 75%, at least about 80%, at least about 85%, or at least about 90%. In some embodiments, the first separator 150a and/or the second separator 150b can have a porosity of no more than about 95%, no more than about 90%, no more than about 85%, no more than about 80%, no more than about 75%, no more than about 70%, no more than about 65%, no more than about 60%, no more than about 55%, no more than about 50%, no more than about 45%, no more than about 40%, no more than about 35%, no more than about 30%, no more than about 25%, no more than about 20%, or no more than about 15%.
Combinations of the above-referenced porosity percentages of the first separator 150a and/or the second separator 150b are also possible (e.g., at least about 10% and no more than about 95% or at least about 20% and no more than about 40%), inclusive of all values and ranges therebetween. In some embodiments, the first separator 150a and/or the second separator 150b can have a porosity of about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, about 90%, or about 95%.
In some embodiments, the first separator 150a can have a different porosity from the second separator 150b. In some embodiments, the porosities of the first separator 150a and the second separator 150b can be selected based on the difference between the anolyte and the catholyte. For example, if the catholyte has a higher vapor pressure and faster evaporation properties than the anolyte, then the second separator 150b can have a lower porosity than the first separator 150a. The lower porosity of the second separator 150b can at least partially prevent the catholyte from evaporating during production.
In some embodiments, the first separator 150a can be composed of a different material from the second separator 150b. In some embodiments, the materials of the first separator 150a and the second separator 150b can be selected to facilitate wettability of the first separator 150a with the anolyte and the second separator 150b with the catholyte 150. For example, an ethylene carbonate/propylene carbonate-based catholyte can wet a polyethylene separator better than a polyimide separator, based on the molecular properties of the materials. An ethylene carbonate/dimethyl carbonate-based anolyte can wet a polyimide separator better than a polyethylene separator. A full wetting of the first separator 150a and the second separator 150b can give way to better transport of electroactive species via the separators 150. This transport can be facilitated particularly well when the first separator 150a physically contacts the second separator 150b.
As shown, the electrochemical cell 100 includes two separators 150. In some embodiments, the electrochemical cell 100 can include 3, 4, 5, 6, 7, 8, 9, 10, or more than about 10 separators 150. In some embodiments, a layer of liquid electrolyte (not shown) can be disposed between the first separator 150a and the second separator 150b. A layer of liquid electrolyte can promote better adhesion between the separators 150.
In some embodiments, the first separator 150a and/or the second separator 150b can have a thickness of at least about 0.5 μm, at least about 1 μm, at least about 2 μm, at least about 3 μm, at least about 4 μm, at least about 5 μm, at least about 6 μm, at least about 7 μm, at least about 8 μm, at least about 9 μm, at least about 10 μm, at least about 15 μm, at least about 20 μm, or at least about 25 μm. In some embodiments, the first separator 150a and/or the second separator 150b can have a thickness of no more than about 30 μm, no more than about 25 μm, no more than about 20 μm, no more than about 15 μm, no more than about 10 μm, no more than about 9 μm, no more than about 8 μm, no more than about 7 μm, no more than about 6 μm, no more than about 5 μm, no more than about 4 μm, no more than about 3 μm, no more than about 2 μm, or no more than about 1 μm. Combinations of the above-referenced thicknesses of the first separator 150a and/or the second separator 150b are also possible (e.g., at least about 0.5 μm and no more than about 30 μm or at least about 5 μm and no more than about 20 μm), inclusive of all values and ranges therebetween. In some embodiments, the first separator 150a and/or the second separator 150b can have a thickness of about 0.5 μm, about 1 μm, about 2 μm, about 3 μm, about 4 μm, about 5 μm, about 6 μm, about 7 μm, about 8 μm, about 9 μm, about 10 μm, about 15 μm, about 20 μm, about 25 μm, or about 30 μm. In some embodiments, the first separator 150a can have a thickness the same or substantially similar to the thickness of the second separator 150b. In some embodiments, the first separator 150a can have a thickness greater or less than a thickness of the second separator 150b.
In some embodiments, the first separator 150a, the second separator 150b, and the interlayer 160 can form a film. In some embodiments, the film can have a total thickness of at least about 5 μm, at least about 6 μm, at least about 7 μm, at least about 8 μm, at least about 9 μm, at least about 10 μm, at least about 15 μm, at least about 20 μm, at least about 25 μm, at least about 30 μm, at least about 35 μm, at least about 40 μm, or at least about 45 μm. In some embodiments, the film can have a total thickness of no more than about 50 μm, no more than about 45 μm, no more than about 40 μm, no more than about 35 μm, no more than about 30 μm, no more than about 25 μm, no more than about 20 μm, no more than about 15 μm, no more than about 10 μm, no more than about 9 μm, no more than about 8 μm, no more than about 7 μm, or no more than about 6 μm. Combinations of the above-referenced thicknesses are also possible (e.g., at least about 5 μm and no more than about 50 μm or at least about 10 μm and no more than about 40 μm), inclusive of all values and ranges therebetween. In some embodiments, the film can have a total thickness of about 5 μm, about 6 μm, about 7 μm, about 8 μm, about 9 μm, about 10 μm, about 15 μm, about 20 μm, about 25 μm, about 30 μm, about 35 μm, about 40 μm, about 45 μm, or about 50 μm.
In some embodiments, the first separator 150a and/or the second separator 150b can include a solid-state electrolyte sheet. In some embodiments, the solid-state electrolyte sheet can replace the first separator 150a and/or the second separator 150b. In some embodiments, the first separator 150a and/or the second separator 150b can be made with a separator film. In some embodiments, the first separator 150a and/or the second separator 150b can include a coating polymer, a spray polymer, and/or a print polymer. In some embodiments, the first separator 150a and/or the second separator 150b can include a ceramic powder. In some embodiments, the first separator 150a and/or the second separator 150b can be absent of a ceramic powder. In some embodiments, the first separator 150a and/or the second separator 150b can include a ceramic with a liquid electrolyte and/or a solid-state electrolyte.
The interlayer 160 can dissolve dendrites via voltage manipulation. In other words, current can be supplied to the interlayer 160, the anode 110, and/or the cathode 130 to create a potential difference between the interlayer 160 and the anode 110 or the interlayer 160 and the cathode 130 that dissolves dendrites that have formed in the interlayer 160. In some embodiments, the interlayer 160 can include a conductive layer. In some embodiments, the interlayer 160 can include a liquid electrolyte. In some embodiments, the interlayer 160 can include a solid-state electrolyte. In some embodiments, the interlayer 160 can include Ketjen Black, AA-stacked graphene, AB-stacked graphene, carbon, hard carbon, soft carbon, graphite, lithium iron phosphate (LFP), lithium manganese iron phosphate (LMFP), lithium manganese oxide (LMO), LiNiO2 (LNO), nickel manganese cobalt (NMC), lithium nickel manganese oxide (LNMO), lithium cobalt oxide (LCO), Iron (III) fluoride (FeF3), sulfur, vanadium (V) oxide (V2O5), bismuth trifluoride (BiF3), iron (IV) sulfate (FeS2), or any combination thereof. In some embodiments, the interlayer 160 can create a physical block that prevents vertical growth of the dendrite, such that the dendrite is forced to grow horizontally.
In some embodiments, the interlayer 160 can include an intercalate cathode (e.g., LMOP, LNO, NMC, LFP, LNMO, LCO, and/or LMFP). In some embodiments, the interlayer 160 can include a convertible cathode (e.g., FeF3, sulfur, V2O5, BiF3, FeS2). In some embodiments, the interlayer 160 can include a high voltage bearable anode. In some embodiments, the interlayer 160 can include a traditional anode (e.g., hard carbon, graphite, and/or silicon). In some embodiments, the interlayer 160 can include a metal. In some embodiments, the interlayer 160 can include a metal alloy. In some embodiments, the metal alloy can include lithium, tin, aluminum, silver, and/or copper. In some embodiments, the interlayer 160 can include a metal oxide. In some embodiments, the metal oxide can include silicon oxide (SiO), zinc oxide (ZnO), copper oxide (Cu2O), lithium titanate (LTO), and/or titanium (IV) oxide (TiO2). In some embodiments, the interlayer 160 can include a semi-solid electrode. In some embodiments, the interlayer 160 can include a coating, a spray, and/or a print polymer. In some embodiments, the interlayer 160 can include a ceramic powder. In some embodiments, the interlayer 160 can include a premade film with a solid-state electrolyte.
In some embodiments, the interlayer 160 can include conductive materials. In some embodiments, the interlayer 160 can include allotropes of carbon including activated carbon, hard carbon, soft carbon, Ketjen, carbon black, graphitic carbon, carbon fibers, carbon microfibers, vapor-grown carbon fibers (VGCF), fullerenic carbons including “buckyballs”, carbon nanotubes (CNTs), multiwall carbon nanotubes (MWNTs), single wall carbon nanotubes (SWNTs), graphene, graphene sheets or aggregates of graphene sheets, and materials comprising fullerenic fragments, or any combination thereof. In some embodiments, the interlayer 160 can include a solid-state electrode material. In some embodiments, the solid-state electrolyte can include an oxide-based electrolyte. In some embodiments, the solid-state electrolyte material can include lithium lanthanum zirconium oxide (LLZO), Li1.3Al0.3Ti1.7(PO4)3 (LATP), lithium phosphorus oxynitride (LiPON), li-ion conducting solid-state electrolyte ceramics (LLTO), and/or Li3BO3—Li2SO4—Li2CO3 (LiBSCO). In some embodiments, the solid-state electrolyte material can include one or more oxide-based solid electrolyte materials including a garnet structure, a perovskite structure, a phosphate-based Lithium Super Ionic Conductor (LISICON) structure, a glass structure such as La0.51Li0.34TiO2.94, Li1.3Al0.3Ti1.7(PO4)3, Li1.4Al0.4Ti1.6(PO4)3, Li7La3Zr2O12, Li6.66La3Zr1.6Ta0.4O12.9 (LLZO), 50Li4SiO4·50Li3BO3, Li2.9PO3.3N0.46 (lithium phosphorousoxynitride, LiPON), Li3.6Si0.6P0.4O4, Li3BN2, Li3BO3—Li2SO4, and/or sulfide containing solid electrolyte materials including a thio-LISICON structure, a glassy structure and a glass-ceramic structure such as Li1.07Al0.69Ti1.46(PO4)3, Li1.5Al0.5Ge1.5(PO4)3, Li10GeP2S12 (LGPS), 30Li2S·26B2S3·44LiI, 63Li2S·36SiS2·1Li3PO4, 57Li2S·38SiS2·5Li4SiO4, 70Li2S·30P2S5, 50Li2S·50GeS2, Li7P3S11, Li3.25P0.95S4, and Li9.54Si1.74P1.44S11.7C0.3, and/or closo-type complex hydride solid electrolyte, LiBH4—LiI, LiBH4—LiNH2, LiBH4—P2S5, Li(CBXHX+1)—LiI, Li(CB9H10)—and/or LiI. In some embodiments, the solid-state electrolyte material can be sulfide-based. In some embodiments, the solid-state electrolyte can include lithium phosphorus sulfide (LPS), Li10GeP2S12 (LGPS), lithium tin phosphorus sulfide (LSPS), and/or Li5.5PS4.5Cl1.5 (LPSCI). In some embodiments, the solid-state electrolyte material can include a complex hydride solid electrolyte. In some embodiments, the solid-state electrolyte material can include LiBH4—LiI and/or LiBH4—P2S5.
In some embodiments, when the interlayer 160 includes a solid-state electrolyte, the interlayer 160 can have a porosity of at least about 0%, at least about 5%, at least about 10%, at least about 15%, at least about 20%, at least about 25%, at least about 30%, at least about 35%, at least about 40%, at least about 45%, at least about 50%, at least about 55%, at least about 60%, at least about 65%, at least about 70%, at least about 75%, at least about 80%, at least about 85%, or at least about 90%. In some embodiments, when the interlayer 160 includes a solid-state electrolyte, the interlayer 160 can have a porosity of no more than about 95%, no more than about 90%, no more than about 85%, no more than about 80%, no more than about 75%, no more than about 70%, no more than about 65%, no more than about 60%, no more than about 55%, no more than about 50%, no more than about 45%, no more than about 40%, no more than about 35%, no more than about 30%, no more than about 25%, no more than about 20%, no more than about 15%, no more than about 10%, or no more than about 5%. Combinations of the above-referenced porosities are also possible (e.g., at least about 0% and no more than about 95% or at least about 10% and no more than about 50%), inclusive of all values and ranges therebetween. In some embodiments, when the interlayer includes a solid-state electrolyte, the interlayer 160 can have a porosity of about 0%, about 5%, about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, about 90%, or about 95%.
In some embodiments, when the interlayer 160 includes a liquid electrolyte, the interlayer 160 can have a porosity of at least about 10%, at least about 15%, at least about 20%, at least about 25%, at least about 30%, at least about 35%, at least about 40%, at least about 45%, at least about 50%, at least about 55%, at least about 60%, at least about 65%, at least about 70%, at least about 75%, at least about 80%, at least about 85%, or at least about 90%. In some embodiments, when the interlayer 160 includes a liquid electrolyte, the interlayer 160 can have a porosity of no more than about 95%, no more than about 90%, no more than about 85%, no more than about 80%, no more than about 75%, no more than about 70%, no more than about 65%, no more than about 60%, no more than about 55%, no more than about 50%, no more than about 45%, no more than about 40%, no more than about 35%, no more than about 30%, no more than about 25%, no more than about 20%, or no more than about 15%. Combinations of the above-referenced porosities are also possible (e.g., at least about 0% and no more than about 95% or at least about 10% and no more than about 50%), inclusive of all values and ranges therebetween. In some embodiments, when the interlayer includes a liquid electrolyte, the interlayer 160 can have a porosity of about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, about 90%, or about 95%.
In some embodiments, the interlayer 160 can be pre-coated onto the first separator 150a and/or the second separator 150b. In some embodiments, the interlayer 160 can aid in identifying a contamination amount of lithium or another metal via a BMS. The BMS can then add more voltage and current to the interlayer 160 to dissolve the contamination. The BMS can keep the state of charge (SOC) of the interlayer 160 between a lower bound (e.g., about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, or about 40%, inclusive of all values and ranges therebetween) and an upper bound (e.g., about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, or about 90%, inclusive of all values and ranges therebetween). Keeping the interlayer 160 between a lower bound and an upper bound of voltage can aid in diminishing dendrite formation while the electrochemical cell 100 is not in use (i.e., via addition of voltage and/or current). In some embodiments, the interlayer 160 can include a tab (not shown) that can be used to monitor the voltage of the interlayer 160 while the electrochemical cell is hot pressed (e.g., via a two-sided hot press or a four-sided hot press with a jelly roll design to fit into a prismatic can).
In some embodiments, the voltage between the anode 110 and the interlayer 160 (and/or the voltage between the anode 110 and the cathode 130) can be kept above a threshold (e.g., about 2 V, about 2.1 V, about 2.2 V, about 2.3 V, about 2.4 V, about 2.5 V, about 2.6 V, about 2.7 V, about 2.8 V, about 2.9 V, about 3 V, about 3.1 V, about 3.2 V, about 3.3 V, about 3.4 V, about 3.5 V, about 3.6 V, about 3.7 V, about 3.8 V, about 3.9 V, about 4 V, about 4.1 V, about 4.2 V, about 4.3 V, about 4.4 V, about 4.5 V, about 4.6 V, about 4.7 V, about 4.8 V, about 4.9 V, about 5 V, about 5.1 V, about 5.2 V, about 5.3 V, about 5.4 V, about 5.5 V, about 5.6 V, about 5.7 V, about 5.8 V, about 5.9 V, or about 6 V, inclusive of all values and ranges therebetween). Keeping the cell voltage above a threshold can prevent dendrite formation. The inclusion of a high-stability salt in the electrolyte can facilitate the application of a high voltage (i.e., at least about 5 V) between the anode 110 and the interlayer 160.
In some embodiments, a high salt concentration (e.g., at least about 2 M, at least about 2.1 M, at least about 2.2 M, at least about 2.3 M, at least about 2.4 M, at least about 2.5 M, at least about 2.6 M, at least about 2.7 M, at least about 2.8 M, at least about 2.9 M, at least about 3 M, at least about 3.1 M, at least about 3.2 M, at least about 3.3 M, at least about 3.4 M, at least about 3.5 M, at least about 3.6 M, at least about 3.7 M, at least about 3.8 M, at least about 3.9 M, at least about 4 M, at least about 4.1 M, at least about 4.2 M, at least about 4.3 M, at least about 4.4 M, at least about 4.5 M, at least about 4.6 M, at least about 4.7 M, at least about 4.8 M, at least about 4.9 M, or at least about 5 M) in the electrolyte can cause side reactions at higher voltages. Maintaining the voltage difference between the anode 110 and the interlayer 160 can prevent these side reactions. Higher stability carbons in the interlayer 160 (e.g., ketjen, graphite, graphene, CNT, and/or hard carbon). In some embodiments, a high-voltage stable metal (e.g., aluminum, gold, platinum) can be used to promote stability in the interlayer 160.
At a low state of charge (SOC), the interlayer 160 can have a voltage lower than a voltage necessary to dissolve dendrites. In some embodiments, a BMS can be activated to provide extra voltage to the interlayer 160 to ensure the voltage is high enough for metal dissolution. If no extra power is available to deliver to the interlayer 160, cycling conditions can be narrowed (e.g., to about 5%, about 10%, about 15%, or about 20% SOC, inclusive of all values and ranges therebetween) in order to limit the formation of dendrites. In some embodiments, the voltage between the anode 110 and the interlayer 160 can be kept above the threshold value by monitoring the potential of the anode 110 and the interlayer 160 and controlling the SOC (i.e., by monitoring and adjusting the cycling). In some embodiments, the voltage between the anode 110 and the interlayer 160 can be maintained by keeping a fixed SOC (e.g., at least about 15%, at least about 20%, at least about 25%, inclusive of all values and ranges therebetween).
As shown, a voltage V1 is measured between the anode current collector 220 and the interlayer 260, a voltage V2 is measured between the anode current collector 220 and the cathode current collector 240. As shown, a diode D is coupled to the interlayer 260 and the cathode current collector 240 to direct the flow of current in a single direction from the interlayer 260 to the cathode current collector 240. In some embodiments, the diode D can be replaced by a resistor, a fuse, and/or a transistor (e.g., a bi-junction transistor, FET). The anode current collector 220 is coupled to the cathode current collector 240 via a resistor R1 and a switch S.
In
In
In some embodiments, multiple electrochemical cells can be connected in series and/or in parallel. As shown, when the switch S closes, a hardware triggered discharge can easily be used to automatically apply an external load to quickly discharge the electrochemical cell 200. This discharge can benefit the functional safety of the electrochemical cell 200. The Failure-in-time (FIT) number of the electrochemical cell 200 or multiple electrochemical cells can be detected for the reliability of detection of dendrites (e.g., based on a contaminant concentration (ppm) value corresponding to a particular voltage). Each electrochemical cell connected in parallel can require a separate monitor. This would increase the controls cost of such a system without individual hardware detection. In some embodiments all of the interlayers from parallel cells can be connected in parallel. Using a switching device can allow duplication of single components (i.e., single transistors are cheaper than BMS monitoring chips). When electrochemical cells are connected fully in series, a battery measurement chip can be used, connecting V1 to a first channel and connecting V2 to a next higher channel. In some embodiments, the BMS can measure/calculate a voltage Vf, equal to V2−V1 to allow a control decision to be made to protect the system. The BMS can react to a short circuit detection via standard balance circuitry or through additional controls. Low integration level monitors can be appropriate for such measurements, as they have a lower controls overhead and cost than more automated BMS devices. Using multiple chip sets can also create redundant safety measurements for voltage and temperature sensing giving additional flexibility to the safety design.
The resistor R1 eases or reduces the flow of current through a direct path between the anode 210 and the cathode 230. In some embodiments, the current flowing along the closed switch S can be used to power an external device. In some embodiments, the current flowing along the closed switch S can be used to provide heat to an external device or heater. As shown, the diode D connects the interlayer 260 to the cathode current collector 240. In some embodiments, the diode D can connect the interlayer 260 to the anode current collector 220 while the voltage is measured between the interlayer 260 and the cathode current collector 240. In other words, the electrochemical energy can flow in the opposite direction to what is depicted in
In some embodiments, the anode 210 can include a semi-solid anode. In some embodiments, the anode 210 can include a conventional solid anode (i.e., with a binder). In some embodiments, the cathode 230 can include a semi-solid cathode. In some embodiments, the cathode 230 can include a conventional solid cathode (i.e., with a binder).
In some embodiments, the electrochemical cell 200 can be subject to high-potential (hipot) testing. In some embodiments, the cathode 230 can be subject to hipot testing. In some embodiments, the anode 210 can be subject to hipot testing. In some embodiments, a full hipot of the electrochemical cell 200 can be conducted with the interlayer 260 acting as a reference layer. In some embodiments, the hipot testing can be conducted with conventional electrode layers.
In some embodiments, the first separator 250a and/or the second separator 250b can be composed of a material that has minimal heat deformation. For example, the first separator 250a and/or the second separator 250b can be composed of cellulose, a cellulosic compound, a thermos-cured resin, a high melting temperature polymer, polyimide, or any combination thereof. In some embodiments, the first separator 250a and/or the second separator 250b can have a melting temperature of at least about 100° C., at least about 110° C., at least about 120° C., at least about 130° C., at least about 140° C., at least about 150° C., at least about 160° C., at least about 170° C., at least about 180° C., at least about 190° C., at least about 200° C., at least about 210° C., at least about 220° C., at least about 230° C., at least about 240° C., at least about 250° C., at least about 260° C., at least about 270° C., at least about 280° C., at least about 290° C., or at least about 300° C.
This level of heat resistance prevents shrinkage by the first separator 250a and/or the second separator 250b. In some embodiments, the electrochemical cell 200 can be formed such that the first separator 250a and the second separator 250b do not contact pouch film encasing the electrochemical cell 200. Since dendrite formation is prevented, the first separator 250a and the second separator 250b need not extend substantially outward from the anode current collector 220 or the cathode current collector 240.
In some embodiments, the interlayer 260 can have a thickness of at least about 500 nm, at least about 1 μm, at least about 2 μm, at least about 3 μm, at least about 4 μm, at least about 5 μm, at least about 6 μm, at least about 7 μm, at least about 8 μm, at least about 9 μm, at least about 10 μm, at least about 20 μm, at least about 30 μm, at least about 40 μm, at least about 50 μm, at least about 60 μm, at least about 70 μm, at least about 80 μm, at least about 90 μm, at least about 100 μm, at least about 150 μm, at least about 200 μm, at least about 250 μm, at least about 300 μm, at least about 350 μm, at least about 400 μm, at least about 450 μm, at least about 500 μm, at least about 550 μm, at least about 600 μm, at least about 650 μm, at least about 700 μm, at least about 750 μm, at least about 800 μm, at least about 850 μm, at least about 900 μm, or at least about 950 μm. In some embodiments, the interlayer 260 can have a thickness of no more than about 1,000 μm, no more than about 950 μm, no more than about 900 μm, no more than about 850 μm, no more than about 800 μm, no more than about 750 μm, no more than about 700 μm, no more than about 650 μm, no more than about 600 μm, no more than about 550 μm, no more than about 500 μm, no more than about 450 μm, no more than about 400 μm, no more than about 350 μm, no more than about 300 μm, no more than about 250 μm, no more than about 200 μm, no more than about 150 μm, no more than about 100 μm, no more than about 90 μm, no more than about 80 μm, no more than about 70 μm, no more than about 60 μm, no more than about 50 μm, no more than about 40 μm, no more than about 30 μm, no more than about 20 μm, no more than about 10 μm, no more than about 9 μm, no more than about 8 μm, no more than about 7 μm, no more than about 6 μm, no more than about 5 μm, no more than about 4 μm, no more than about 3 μm, no more than about 2 μm, or no more than about 1 μm. Combinations of the above-referenced thickness values are also possible (e.g., at least about 500 nm and no more than about 1,000 μm or at least about 200 μm and no more than about 700 μm), inclusive of all values and ranges therebetween.
In some embodiments, the interlayer 260 can have a thickness of about 10 μm, about 20 μm, about 30 μm, about 40 μm, about 50 μm, about 60 μm, about 70 μm, about 80 μm, about 90 μm, about 100 μm, about 150 μm, about 200 μm, about 250 μm, about 300 μm, about 350 μm, about 400 μm, about 450 μm, about 500 μm, about 550 μm, about 600 μm, about 650 μm, about 700 μm, about 750 μm, about 800 μm, about 850 μm, about 900 μm, about 950 μm, or about 1,000 μm.
In some embodiments, the interlayer 260 can have a conductivity of at least about 1×10-3 S/m, at least about 2×10−3 S/m, at least about 3×10−3 S/m, at least about 4×10−3 S/m, at least about 5×10−3 S/m, at least about 6×10−3 S/m, at least about 7×10−3 S/m, at least about 8×10−3 S/m, at least about 9×10−3 S/m, at least about 1×10−2 S/m, at least about 2×10−2 S/m, at least about 3×10−2 S/m, at least about 4×10−2 S/m, at least about 5×10−2 S/m, at least about 6×10−2 S/m, at least about 7×10−2 S/m, at least about 8×10−2 S/m, at least about 9×10−2 S/m, at least about 0.1 S/m, at least about 0.2 S/m, at least about 0.3 S/m, at least about 0.4 S/m, at least about 0.5 S/m, at least about 0.6 S/m, at least about 0.7 S/m, at least about 0.8 S/m, at least about 0.9 S/m. In some embodiments, the interlayer 260 can have a conductivity of no more than about 1 S/m, no more than about 0.9 S/m, no more than about 0.8 S/m, no more than about 0.7 S/m, no more than about 0.6 S/m, no more than about 0.5 S/m, no more than about 0.4 S/m, no more than about 0.3 S/m, no more than about 0.2 S/m, no more than about 0.1 S/m, no more than about 9×10−2 S/m, no more than about 8×10−2 S/m, no more than about 7×10−2 S/m, no more than about 6×10−2 S/m, no more than about 5×10−2 S/m, no more than about 4×10−2 S/m, no more than about 3×10−2 S/m, no more than about 2×10−2 S/m, no more than about 1×10−2 S/m, no more than about 9×10−3 S/m, no more than about 8×10−3 S/m, no more than about 7×10−3 S/m, no more than about 6×10−3 S/m, no more than about 5×10−3 S/m, no more than about 4×10−3 S/m, no more than about 3×10−3 S/m, or no more than about 2×10−3 S/m. Combinations of the above-referenced conductivity values are also possible (e.g., at least about 1×10−3 S/m and no more than about 1 S/m or at least about at least about 2×10−3 S/m and no more than about 0.1 S/cm), inclusive of all values and ranges therebetween. In some embodiments, the interlayer 260 can have a conductivity of about 1×10−3 S/m, about 2×10−3 S/m, about 3×10−3 S/m, about 4×10−3 S/m, about 5×10−3 S/m, about 6×10−3 S/m, about 7×10−3 S/m, about 8×10−3 S/m, about 9×10−3 S/m, about 1×10−2 S/m, about 2×10−2 S/m, about 3×10−2 S/m, about 4×10−2 S/m, about 5×10−2 S/m, about 6×10−2 S/m, about 7×10−2 S/m, about 8×10−2 S/m, about 9×10−2 S/m, about 0.1 S/m, about 0.2 S/m, about 0.3 S/m, about 0.4 S/m, about 0.5 S/m, about 0.6 S/m, about 0.7 S/m, about 0.8 S/m, about 0.9 S/m, or about 1 S/m.
In some embodiments, the interlayer 260 can be electrically coupled to a cathode external to the electrochemical cell 200. In some embodiments, the external cathode can have a higher resistance than the interlayer 260. In some embodiments, the interlayer 260 can be electrically coupled to an anode external to the electrochemical cell 200. In some embodiments, the external anode can have a higher resistance than the interlayer 260. In some embodiments, the interlayer 260 can be electrically connected to an external electrochemical cell. In some embodiments, the interlayer 260 can be electrically connected to an external capacitor. In some embodiments, the interlayer 260 can be electrically connected to an external resistor.
In some embodiments, the potential of the interlayer 260 can be manipulated to dissolve or oxidize the dendrite 225 as the dendrite 225 penetrates the interlayer 260. This is particularly valid when the interlayer 260 includes cathode materials therein. In some embodiments, the voltage difference between the anode 210 and the interlayer 260 can be tuned to at least about 1 V, at least about 1.5 V, at least about 2 V, at least about 2.5 V, at least about 3 V, at least about 3.5 V, at least about 4 V, or at least about 4.5 V. In some embodiments, the voltage difference between the anode 210 and the interlayer 260 can be tuned to no more than about 5 V, no more than about 4.5 V, no more than about 4 V, no more than about 3.5 V, no more than about 3 V, no more than about 2.5 V, no more than about 2 V, or no more than about 1.5 V. Combinations of the above-referenced voltage ranges are also possible (e.g., at least about 1 V and no more than about 5 V or at least about 2 V and no more than about 4 V), inclusive of all values and ranges therebetween. In some embodiments, the voltage difference between the anode 210 and the interlayer 260 can be tuned to about 1 V, about 1.5 V, about 2 V, about 2.5 V, about 3 V, about 3.5 V, about 4 V, about 4.5 V, about 5 V, about 5.5 V, or about 6 V.
In some embodiments, the voltage difference between the cathode 230 and the interlayer 260 can be tuned to at least about 1 V, at least about 1.5 V, at least about 2 V, at least about 2.5 V, at least about 3 V, at least about 3.5 V, at least about 4 V, at least about 4.5 V, at least about 5 V, or at least about 5.5 V. In some embodiments, the voltage difference between the cathode 230 and the interlayer 260 can be tuned to no more than about 6 V, no more than about 5.5 V, no more than about 5 V, no more than about 4.5 V, no more than about 4 V, no more than about 3.5 V, no more than about 3 V, no more than about 2.5 V, no more than about 2 V, or no more than about 1.5 V. Combinations of the above-referenced voltage ranges are also possible (e.g., at least about 1 V and no more than about 5 V or at least about 2 V and no more than about 4 V), inclusive of all values and ranges therebetween. In some embodiments, the voltage difference between the cathode 230 and the interlayer 260 can be tuned to about 1 V, about 1.5 V, about 2 V, about 2.5 V, about 3 V, about 3.5 V, about 4 V, about 4.5 V, about 5 V, about 5.5 V, or about 6 V.
In some embodiments, the impedance through the structural components of the electrochemical cell 200 (i.e., the anode 210, the anode current collector 220, the cathode 230, the cathode current collector 240, and the separator 250) can be less than the impedance through the resistor R1. In some embodiments, the impedance through the structural components of the electrochemical cell 200 can be less than the impedance through the diode D. In some embodiments, the ratio of the impedance through the structural components of the electrochemical cell 200 to the impedance through the resistor R1 can be less than about 1:2, less than about 1:3, less than about 1:4, less than about 1:5, less than about 1:6, less than about 1:7, less than about 1:8, less than about 1:9, less than about 1:10, less than about 1:20, less than about 1:30, less than about 1:40, less than about 1:50, less than about 1:60, less than about 1:70, less than about 1:80, less than about 1:90, or less than about 1:100. In some embodiments, the ratio of the impedance through the structural components of the electrochemical cell 200 to the impedance through the diode D can be less than about 1:2, less than about 1:3, less than about 1:4, less than about 1:5, less than about 1:6, less than about 1:7, less than about 1:8, less than about 1:9, less than about 1:10, less than about 1:20, less than about 1:30, less than about 1:40, less than about 1:50, less than about 1:60, less than about 1:70, less than about 1:80, less than about 1:90, or less than about 1:100.
In some embodiments, the first separator 250a can have a first length and the second separator 250b can have a second length, the second length greater than the first length. In some embodiments, the first separator 250a can have a first width and the second separator 250b can have a second width, the second width greater than the first width. In some embodiments, the interlayer 260 can have a length and/or width greater than the first width and/or the second width, such that a portion of the interlayer 260 is adjacent to the second separator 250b but not the first separator 250a. In some embodiments, a tab (not shown) can be attached (e.g., via welding) to the interlayer 260. In some embodiments, the tab can be attached to a portion of the interlayer 260 extending beyond the first separator 250a.
In some embodiments, a portion of the first separator 250a and/or the second separator 250b can be removed (e.g., the first separator 250a and/or the second separator 250b can be punched), such that the tab can be attached to the interlayer 260 through the removed section of the first separator 250a and/or the second separator 250b. In some embodiments, the electrochemical cell 200 can be contained inside a pouch (not shown). In some embodiments, the pouch can include a first film attached to the anode current collector 220 and a second film attached to the cathode current collector 240. In some embodiments, portion of the pouch can be removed (e.g., punched), such that the tab can be attached to the interlayer 260 through the removed section of the pouch.
As shown, a voltage V1 is measured between the anode current collector 320 and the interlayer 360, a voltage V2 is measured between the anode current collector 320 and the cathode current collector 340. As shown, the anode current collector 320 is coupled to the cathode current collector 340 via a resistor R1 and a switch S. As shown, a resistor R2 is coupled to the interlayer 360 and the cathode current collector 340 to resist current flow in a direction from the interlayer 360 to the cathode current collector 340.
In
As shown, the resistor R1 connects the interlayer 360 to the cathode current collector 340. In some embodiments, the resistor R1 can connect the interlayer 360 to the anode current collector 320 while the voltage is measured between the interlayer 360 and the cathode current collector 340. In other words, the electrochemical energy can flow in the opposite direction to what is depicted in
As shown, a voltage V1 is measured between the anode current collector 420 and the second interlayer 460b. A voltage V2 is measured between the second interlayer 460b and the first interlayer 460a. As shown, a first diode D1 is coupled to the second interlayer 460b and the cathode current collector 440 to direct the flow of current in a single direction from the second interlayer 460 to the cathode current collector 440. As shown, a second diode D2 is coupled to the first interlayer 460a and the cathode 440. The anode current collector 420 is coupled to the cathode current collector 440 via a resistor R1 and a switch S.
In
As shown, the electrochemical cell 400 includes 3 separators 450a, 450b, 450c (collectively referred to as separators 450). In some embodiments, the electrochemical cell 400 can include at least about 3, at least about 4, at least about 5, at least about 6, at least about 7, at least about 8, at least about 9, at least about 10, at least about 15, at least about 20, at least about 25, at least about 30, at least about 35, at least about 40, at least about 45, at least about 50, at least about 55, at least about 60, at least about 65, at least about 70, at least about 75, at least about 80, at least about 85, at least about 90, or at least about 95 separators 450. In some embodiments, the electrochemical cell 400 can include no more than about 100, no more than about 95, no more than about 90, no more than about 85, no more than about 80, no more than about 75, no more than about 70, no more than about 65, no more than about 60, no more than about 55, no more than about 50, no more than about 45, no more than about 40, no more than about 35, no more than about 30, no more than about 25, no more than about 20, no more than about 15, no more than about 10, no more than about 9, no more than about 8, no more than about 7, no more than about 6, no more than about 5, or no more than about 4 separators 450. Combinations of the above-referenced numbers of separators 450 are also possible (e.g., at least about 3 and no more than about 100 or at least about 10 and no more than about 40), inclusive of all values and ranges therebetween. In some embodiments, the electrochemical cell 400 can include about 3, about 4, about 5, about 6, about 7, about 8, about 9, about 10, about 15, about 20, about 25, about 30, about 35, about 40, about 45, about 50, about 55, about 60, about 65, about 70, about 75, about 80, about 85, about 90, about 95, or about 100 separators 450.
As shown, the electrochemical cell 400 includes 2 interlayers 460a, 460b (collectively referred to as interlayers 460). Multiple interlayers 460 allow for multiple points along the electrochemical cell, where voltages and voltage differences can be measured. In some embodiments, the electrochemical cell 400 can include at least about 2, at least about 3, at least about 4, at least about 5, at least about 6, at least about 7, at least about 8, at least about 9, at least about 10, at least about 15, at least about 20, at least about 25, at least about 30, at least about 35, at least about 40, at least about 45, at least about 50, at least about 55, at least about 60, at least about 65, at least about 70, at least about 75, at least about 80, at least about 85, at least about 90, or at least about 95 interlayers 460. In some embodiments, the electrochemical cell 400 can include no more than about 100, no more than about 95, no more than about 90, no more than about 85, no more than about 80, no more than about 75, no more than about 70, no more than about 65, no more than about 60, no more than about 55, no more than about 50, no more than about 45, no more than about 40, no more than about 35, no more than about 30, no more than about 25, no more than about 20, no more than about 15, no more than about 10, no more than about 9, no more than about 8, no more than about 7, no more than about 6, no more than about 5, no more than about 4, or no more than about 3 interlayers 460. Combinations of the above-referenced numbers of interlayers 460 are also possible (e.g., at least about 3 and no more than about 100 or at least about 10 and no more than about 40), inclusive of all values and ranges therebetween. In some embodiments, the electrochemical cell 400 can include about 3, about 4, about 5, about 6, about 7, about 8, about 9, about 10, about 15, about 20, about 25, about 30, about 35, about 40, about 45, about 50, about 55, about 60, about 65, about 70, about 75, about 80, about 85, about 90, about 95, or about 100 interlayers 460.
As shown, the diode D1 connects the second interlayer 460b to the cathode current collector 440 and the diode D2 connects the first interlayer 460a to the cathode current collector 440. In some embodiments, the diode D1 can connect the first interlayer 460a to the anode current collector 420 and the diode D2 can connect the second interlayer 460b to the anode current collector 420 while voltage is measured between the first interlayer 460a and the second interlayer 460b and between the first interlayer 460a and the cathode 430. In other words, the electrochemical energy can flow in the opposite direction to what is depicted in
In some embodiments, the separator 450a, the separator 450b, and/or the separator 450c can include a solid-state electrolyte. In some embodiments, the solid-state electrolyte layer can be incorporated into the electrochemical cell 400 instead of the separator 450a, the separator 450b, and/or the separator 450c. In some embodiments, the separator 450b can have a lower melting temperature than the separator 450a. In some embodiments, the separator 450c can have a lower melting temperature than the separator 450a. In some embodiments, the separator 450c can have a lower melting temperature than the separator 450a. In some embodiments, the separator 450a, the separator 450b, and/or the separator 450c can include a gel electrolyte. In some embodiments, the gel electrolyte can be included in the electrochemical cell 400 instead of either of the separators 450. In some embodiments, either of the separators 450 can include non-ionic conductive powders.
In some embodiments, the resistance across the diode D1 can be greater than the resistance across the diode D2. This allows more current to flow through the interlayer 460a than through the interlayer 460b, which can cause a dendrite that has penetrated the interlayer 460b to dissipate more rapidly. In some embodiments, a V1 measurement of zero can cause a ‘caution’ alert to be sent to a user (e.g., via a BMS). For example, the caution can be a yellow light. In some embodiments, a V2 measurement of zero can cause a ‘warning’ or ‘danger’ alert to be sent to the user. For example, a red light can be switched on for the user to see. In some embodiments, a V2 measurement of zero can trigger safety actions. In some embodiments, the safety actions can include an external short circuit through a BMS. In some embodiments, the safety actions can include a rerouting of current through a heater (e.g., via a BMS).
In some embodiments, the separator 450b and/or the separator 450c can have a thickness of at least about 0.2 μm, at least about 0.3 μm, at least about 0.4 μm, at least about 0.5 μm, at least about 0.6 μm, at least about 0.7 μm, at least about 0.8 μm, at least about 0.9 μm, at least about 1 μm, at least about 1.5 μm, at least about 2 μm, or at least about 2.5 μm. In some embodiments, the separator 450b and/or the separator 450c can have a thickness of no more than about 3 μm, no more than about 2.5 μm, no more than about 2 μm, no more than about 1.5 μm, no more than about 1 μm, no more than about 0.9 μm, no more than about 0.8 μm, no more than about 0.7 μm, no more than about 0.6 μm, no more than about 0.5 μm, no more than about 0.4 μm, or no more than about 0.3 μm. Combinations of the above-referenced thickness values are also possible (e.g., at least about 0.2 μm and no more than about 3 μm or at least about 0.5 μm and no more than about 1 μm), inclusive of all values and ranges therebetween. In some embodiments, the separator 450b and/or the separator 450c can have a thickness of about 0.2 μm, about 0.3 μm, about 0.4 μm, about 0.5 μm, about 0.6 μm, about 0.7 μm, about 0.8 μm, about 0.9 μm, about 1 μm, about 1.5 μm, about 2 μm, about 2.5 μm, or about 3 μm.
In some embodiments, the separator 450b and/or the separator 450c can be excluded from the electrochemical cell 400. For example, the electrochemical cell 400 can include lithium metal anodes with or without mesh type current collectors. Lithium metal can be filled into the mesh current collector. In such a case, the V1 monitoring capability is lost, but V2 can still be monitored for safety purposes.
As shown, the cathode 530 has a non-uniform thickness. Without the interlayer 560, the SOC of the anode 510 and/or the cathode 530 can become varied due to coating thicknesses or impedance variations. Lithium ions are drawn to move inside the electrode to equalize the same potential. However, cathode materials (e.g., LNO or NMC) can have a greater potential slope than anode materials (e.g., graphite), depending on SOC, and lithium ions can move faster in the cathode material than in the anode material. Adding a lithium-reduced NMC (e.g., Li(1-x) NMC) in the interlayer 560 can reduce the SOC difference inside the cathode 530. In charging, electrons can go through the interlayer 560, but in discharging, the material does not move. The interlayer 560 can become a buffer capacity to equalize the SOC difference inside the cathode 530. In some embodiments, the thickness of the cathode 530 can be made non-uniform to balance distribution of lithium ions. In other words, the lithium ions can have a uniform or near uniform (e.g., within about 5%, within about 4%, within about 3%, within about 2%, or within about 1%) volumetric density of lithium ions (i.e., lithium ions per unit volume of electrode material) throughout the length of the cathode 530.
As shown, a first side of the cathode 530 has a first thickness t1 and a second side of the cathode 530 has a second thickness t2. The variable thickness of the cathode 530 (t1 and t2) can facilitate cathode and anode alignment and avoid misalignment when the electrochemical cell 500 when the electrochemical cell 500 is rolled (i.e., in a jelly roll format and placed into a can). In some embodiments, the first side of the cathode 530 can be adjacent to a tab where voltage is measured. In some embodiments, the second side of the cathode 530 can be adjacent to a tab where voltage is measured. In other words, the cathode 530 can be thicker on the side proximal to where voltage is measured, or the cathode 530 can be thicker on the side distal to where the voltage is measured.
In some embodiments, t1 can be at least about 100 μm, at least about 150 μm, at least about 200 μm, at least about 250 μm, at least about 300 μm, at least about 350 μm, at least about 400 μm, at least about 450 μm, at least about 500 μm, at least about 550 μm, at least about 600 μm, at least about 650 μm, at least about 700 μm, at least about 750 μm, at least about 800 μm, at least about 850 μm, at least about 900 μm, at least about 950 μm, at least about 1,000 μm, at least about 1,100 μm, at least about 1,200 μm, at least about 1,300 μm, at least about 1,400 μm, at least about 1,500 μm, at least about 1,600 μm, at least about 1,700 μm, at least about 1,800 μm, or at least about 1,900 μm. In some embodiments, t1 can be no more than about 2,000 μm, no more than about 2,000 μm, no more than about 2,000 μm, no more than about 1,900 μm, no more than about 1,800 μm, no more than about 1,700 μm, no more than about 1,600 μm, no more than about 1,500 μm, no more than about 1,400 μm, no more than about 1,300 μm, no more than about 1,200 μm, no more than about 1,100 μm, no more than about 1,000 μm, no more than about 950 μm, no more than about 900 μm, no more than about 850 μm, no more than about 800 μm, no more than about 750 μm, no more than about 700 μm, no more than about 650 μm, no more than about 600 μm, no more than about 550 μm, no more than about 500 μm, no more than about 450 μm, no more than about 400 μm, no more than about 350 μm, no more than about 300 μm, no more than about 250 μm, no more than about 200 μm, or no more than about 150 μm. Combinations of the above-referenced thicknesses are also possible (e.g., at least about 100 μm and no more than about 2,000 μm or at least about 150 μm and no more than about 500 μm), inclusive of all values and ranges therebetween. In some embodiments, t1 can be about 100 μm, about 150 μm, about 200 μm, about 250 μm, about 300 μm, about 350 μm, about 400 μm, about 450 μm, about 500 μm, about 550 μm, about 600 μm, about 650 μm, about 700 μm, about 750 μm, about 800 μm, about 850 μm, about 900 μm, about 950 μm, about 1,000 μm, about 1,100 μm, about 1,200 μm, about 1,300 μm, about 1,400 μm, about 1,500 μm, about 1,600 μm, about 1,700 μm, about 1,800 μm, about 1,900 μm, or about 2,000 μm.
In some embodiments, t2 can be at least about 100 μm, at least about 150 μm, at least about 200 μm, at least about 250 μm, at least about 300 μm, at least about 350 μm, at least about 400 μm, at least about 450 μm, at least about 500 μm, at least about 550 μm, at least about 600 μm, at least about 650 μm, at least about 700 μm, at least about 750 μm, at least about 800 μm, at least about 850 μm, at least about 900 μm, at least about 950 μm, at least about 1,000 μm, at least about 1,100 μm, at least about 1,200 μm, at least about 1,300 μm, at least about 1,400 μm, at least about 1,500 μm, at least about 1,600 μm, at least about 1,700 μm, at least about 1,800 μm, or at least about 1,900 μm. In some embodiments, t2 can be no more than about 2,000 μm, no more than about 2,000 μm, no more than about 2,000 μm, no more than about 1,900 μm, no more than about 1,800 μm, no more than about 1,700 μm, no more than about 1,600 μm, no more than about 1,500 μm, no more than about 1,400 μm, no more than about 1,300 μm, no more than about 1,200 μm, no more than about 1,100 μm, no more than about 1,000 μm, no more than about 950 μm, no more than about 900 μm, no more than about 850 μm, no more than about 800 μm, no more than about 750 μm, no more than about 700 μm, no more than about 650 μm, no more than about 600 μm, no more than about 550 μm, no more than about 500 μm, no more than about 450 μm, no more than about 400 μm, no more than about 350 μm, no more than about 300 μm, no more than about 250 μm, no more than about 200 μm, or no more than about 150 μm. Combinations of the above-referenced thicknesses are also possible (e.g., at least about 100 μm and no more than about 2,000 μm or at least about 150 μm and no more than about 500 μm), inclusive of all values and ranges therebetween. In some embodiments, t2 can be about 100 μm, about 150 μm, about 200 μm, about 250 μm, about 300 μm, about 350 μm, about 400 μm, about 450 μm, about 500 μm, about 550 μm, about 600 μm, about 650 μm, about 700 μm, about 750 μm, about 800 μm, about 850 μm, about 900 μm, about 950 μm, about 1,000 μm, about 1,100 μm, about 1,200 μm, about 1,300 μm, about 1,400 μm, about 1,500 μm, about 1,600 μm, about 1,700 μm, about 1,800 μm, about 1,900 μm, or about 2,000 μm.
In some embodiments, t2 can be larger than t1 by at least about 50 nm, at least about 100 nm, at least about 200 nm, at least about 300 nm, at least about 400 nm, at least about 500 nm, at least about 600 nm, at least about 700 nm, at least about 800 nm, at least about 900 nm, at least about 1 μm, at least about 2 μm, at least about 3 μm, at least about 4 μm, at least about 5 μm, at least about 6 μm, at least about 7 μm, at least about 8 μm, at least about 9 μm, at least about 10 μm, at least about 15 μm, at least about 20 μm, at least about 25 μm, at least about 30 μm, at least about 35 μm, at least about 40 μm, or at least about 45 μm. In some embodiments, t2 can be larger than t1 by no more than about 50 μm, no more than about 45 μm, no more than about 40 μm, no more than about 35 μm, no more than about 30 μm, no more than about 25 μm, no more than about 20 μm, no more than about 15 μm, no more than about 10 μm, no more than about 9 μm, no more than about 8 μm, no more than about 7 μm, no more than about 6 μm, no more than about 5 μm, no more than about 4 μm, no more than about 3 μm, no more than about 2 μm, no more than about 1 μm, no more than about 900 nm, no more than about 800 nm, no more than about 700 nm, no more than about 600 nm, no more than about 500 nm, no more than about 400 nm, no more than about 300 nm, no more than about 200 nm, or no more than about 100 nm. Combinations of the above-referenced thickness differences are also possible (e.g., at least about 50 nm and no more than about 50 μm or at least about 500 nm and no more than about 10 μm), inclusive of all values and ranges therebetween.
In some embodiments, t2 can be greater than t1 by at least about 0.1%, at least about 0.2%, at least about 0.3%, at least about 0.4%, at least about 0.5%, at least about 0.6%, at least about 0.7%, at least about 0.8%, at least about 0.9%, at least about 1%, at least about 2%, at least about 3%, at least about 4%, at least about 5%, at least about 6%, at least about 7%, at least about 8%, or at least about 9%. In some embodiments, t2 can be greater than t1 by no more than about 10%, no more than about 9%, no more than about 8%, no more than about 7%, no more than about 6%, no more than about 5%, no more than about 4%, no more than about 3%, no more than about 2%, no more than about 1%, no more than about 0.9%, no more than about 0.8%, no more than about 0.7%, no more than about 0.6%, no more than about 0.5%, no more than about 0.4%, no more than about 0.3%, or no more than about 0.2%. Combinations of the above-referenced thickness differences are also possible (e.g., at least about 0.1% and no more than about 10% or at least about 0.5% and no more than about 5%), inclusive of all values and ranges therebetween. In some embodiments, t2 can be greater than t1 by about 0.1%, about 0.2%, about 0.3%, about 0.4%, about 0.5%, about 0.6%, about 0.7%, about 0.8%, about 0.9%, about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, or about 10%.
As shown, the cathode 530 has a non-uniform thickness. In some embodiments, the anode 510 can have a non-uniform thickness. In some embodiments, the first separator 550a and/or the second separator 550b can have a non-uniform thickness to conform to the non-uniform thickness of the cathode 530 and/or the anode 510. In other words, the first separator 550a and/or the second separator 550b can have a smaller thickness on the side of the electrochemical cell 200 including t1 and a larger thickness on the side of the electrochemical cell 200 including t2. In some embodiments, the first separator 550a and/or the second separator 550b can include a malleable structure, such that the non-uniform thickness of the cathode 530 and/or the anode 510 are absorbed and do not affect the uniformity of the thickness of the electrochemical cell 500.
The lithium metal layer 670 is positioned adjacent to the anode 610. In some embodiments, the lithium metal layer 670 can aid in even electron distribution in the anode 610. In some embodiments, the anode 610 can include hard carbon coated onto the lithium metal layer 670. In some embodiments, the anode 610 can include silicon coated onto the lithium metal layer 670. In some embodiments, the anode 610 can include graphite coated onto the lithium metal layer 670. In some embodiments, the anode 610 can include indium coated onto the lithium metal layer 670.
In some embodiments, the lithium metal layer 670 can have a thickness of at least about 50 μm, at least about 60 μm, at least about 70 μm, at least about 80 μm, at least about 90 μm, at least about 100 μm, at least about 150 μm, at least about 200 μm, at least about 250 μm, at least about 300 μm, at least about 350 μm, at least about 400 μm, or at least about 450 μm. In some embodiments, the lithium metal layer 670 can have a thickness of no more than about 500 μm, no more than about 450 μm, no more than about 400 μm, no more than about 350 μm, no more than about 300 μm, no more than about 250 μm, no more than about 200 μm, no more than about 150 μm, no more than about 100 μm, no more than about 90 μm, no more than about 80 μm, no more than about 70 μm, or no more than about 60 μm. Combinations of the above-referenced thicknesses are also possible (e.g., at least about 50 μm and no more than about 500 μm or at least about 100 μm and no more than about 400 μm), inclusive of all values and ranges therebetween. In some embodiments, the lithium metal layer 670 can have a thickness of about 50 μm, about 60 μm, about 70 μm, about 80 μm, about 90 μm, about 100 μm, about 150 μm, about 200 μm, about 250 μm, about 300 μm, about 350 μm, about 400 μm, about 450 μm, or about 500 μm.
The frame 762 is disposed around an outside edge of the interlayer 760. In some embodiments, the frame 762 is composed of a conductive material. In some embodiments, the frame 762 can be composed of aluminum, copper, conductive ceramic, a conductive polymer, carbon fiber paper, nickel, titanium, or any combination thereof. In some embodiments, the frame 762 can be coupled to the first separator 750a and/or the second separator 750b via an adhesive.
In some embodiments, the adhesive can be applied during the electrochemical cell manufacturing process. In some embodiments, the adhesive can be electrically conductive. In some embodiments, the tab 763 can be welded to the frame 762. In some embodiments, the tab 763 can be ultrasonically welded to the frame 762. In some embodiments, the tab 763 can be coupled to a pouch tab (not shown) via an adhesive. In some embodiments, the interlayer 760 can have multiple layers. In some embodiments, the interlayer 760 can include gold, carbon, indium, tin, or any combination thereof. In some embodiments, the interlayer 760 can be coated to the tab 763, the first separator 750a, and/or the second separator 750b. In some embodiments, the tab 763 can be directly welded to the interlayer 760, the first separator 750a, and/or the second separator 750b.
As shown, the frame 762 overlaps the interlayer 760 by an overlapping width w. The width w can vary to reduce the resistance of the frame 762 and can be tuned based on the material of the frame 762, the thickness of the frame 762, and/or the capacity of the electrochemical cell. In some embodiments, w can be at least about 250 μm, at least about 500 μm, at least about 750 μm, at least about 1 mm, at least about 1.5 mm, at least about 2 mm, at least about 2.5 mm, at least about 3 mm, at least about 3.5 mm, at least about 4 mm, at least about 4.5 mm, at least about 5 mm, at least about 5.5 mm, at least about 6 mm, at least about 6.5 mm, at least about 7 mm, at least about 7.5 mm, at least about 8 mm, at least about 8.5 mm, at least about 9 mm, or at least about 9.5 mm. In some embodiments, w can be no more than about 10 mm, no more than about 9.5 mm, no more than about 9 mm, no more than about 8.5 mm, no more than about 8 mm, no more than about 7.5 mm, no more than about 7 mm, no more than about 6.5 mm, no more than about 6 mm, no more than about 5.5 mm, no more than about 5 mm, no more than about 4.5 mm, no more than about 4 mm, no more than about 3.5 mm, no more than about 3 mm, no more than about 2.5 mm, no more than about 2 mm, no more than about 1.5 mm, no more than about 1 mm, no more than about 750 μm, or no more than about 500 μm. Combinations of the above-referenced values of w are also possible (e.g., at least about 250 μm and no more than about 10 mm or at least about 1 mm and no more than about 5 mm), inclusive of all values and ranges therebetween. In some embodiments, the width w can be about 250 μm, about 500 μm, about 750 μm, about 1 mm, about 1.5 mm, about 2 mm, about 2.5 mm, about 3 mm, about 3.5 mm, about 4 mm, about 4.5 mm, about 5 mm, about 5.5 mm, about 6 mm, about 6.5 mm, about 7 mm, about 7.5 mm, about 8 mm, about 8.5 mm, about 9 mm, about 9.5 mm, or about 10 mm.
As shown, the interlayer 760 includes an active area 761. A distance from the inside edge of the frame to the outside edge of the active area is represented as da. In some embodiments, the distance da can be at least about 1 mm, at least about 1.5 mm, at least about 2 mm, at least about 2.5 mm, at least about 3 mm, at least about 3.5 mm, at least about 4 mm, at least about 4.5 mm, at least about 5 mm, at least about 5.5 mm, at least about 6 mm, at least about 6.5 mm, at least about 7 mm, at least about 7.5 mm, at least about 8 mm, at least about 8.5 mm, at least about 9 mm, or at least about 9.5 mm. In some embodiments, the distance da can be no more than about 10 mm, no more than about 9.5 mm, no more than about 9 mm, no more than about 8.5 mm, no more than about 8 mm, no more than about 7.5 mm, no more than about 7 mm, no more than about 6.5 mm, no more than about 6 mm, no more than about 5.5 mm, no more than about 5 mm, no more than about 4.5 mm, no more than about 4 mm, no more than about 3.5 mm, no more than about 3 mm, no more than about 2.5 mm, no more than about 2 mm, or no more than about 1.5 mm. Combinations of the above-referenced distances for da are also possible (e.g., at least about 1 mm and no more than about 10 mm or at least about 2 mm and no more than about 8 mm), inclusive of all values and ranges therebetween. In some embodiments, the distance da can be about 1 mm, about 1.5 mm, about 2 mm, about 2.5 mm, about 3 mm, about 3.5 mm, about 4 mm, about 4.5 mm, about 5 mm, about 5.5 mm, about 6 mm, about 6.5 mm, about 7 mm, about 7.5 mm, about 8 mm, about 8.5 mm, about 9 mm, about 9.5 mm, or about 10 mm.
In some embodiments, the wire 862 can be composed of aluminum. In some embodiments, the wire 862 can be composed of copper. In some embodiments, the gauge of the wire 862 can be selected based on the capacity of the electrochemical cell (i.e., a thicker wire can be incorporated into an electrochemical cell with a higher capacity). In some embodiments, the wire 862 can have 32 American Wire Gauge (AWG), 31 AWG, 30 AWG, 29 AWG, 28 AWG, 27 AWG, 26 AWG, 25 AWG, 24 AWG, 23 AWG, 22 AWG, 21 AWG, 20 AWG, 19 AWG, or 18 AWG, inclusive of all sizes therebetween. In some embodiments, the wire 862 can be attached to the first separator 850a and/or the second separator 850b via an adhesive. In some embodiments, the adhesive can be applied to the wire 862 during the electrochemical cell manufacturing process. In some embodiments, the adhesive can be electrically conductive.
In some embodiments, a coating can be molded around the wire 862. In some embodiments, the coating can include a polymer coating. In some embodiments, the coating can include polyethylene. In some embodiments, the wire 862 can be connected directly to a diode (not shown). In some embodiments, the wire 862 can be connected to a diode via soldering, butt splicing, or any other suitable connection. In some embodiments, an electrochemical cell that includes the wire 862 can have a lower mass than an electrochemical cell that includes a frame (e.g., the frame 762, as described above with reference to
As shown, the wire 862 is offset from the edge of the interlayer 860 by an offset distance d. In some embodiments, d can be the same or substantially similar on all sides of the interlayer 860. In some embodiments, d can vary from one side of the interlayer 860 to another. In some embodiments, the wire 862 can be positioned on the edge of the interlayer 860, such that d is about 0 mm. In some embodiments, d can be at least about 0 mm, at least about 0.5 mm, at least about 1 mm, at least about 1.5 mm, at least about 2 mm, at least about 2.5 mm, at least about 3 mm, at least about 3.5 mm, at least about 4 mm, at least about 4.5 mm, at least about 5 mm, at least about 5.5 mm, at least about 6 mm, at least about 6.5 mm, at least about 7 mm, at least about 7.5 mm, at least about 8 mm, at least about 8.5 mm, at least about 9 mm, or at least about 9.5 mm. In some embodiments, d can be no more than about 10 mm, no more than about 9.5 mm, no more than about 9 mm, no more than about 8.5 mm, no more than about 8 mm, no more than about 7.5 mm, no more than about 7 mm, no more than about 6.5 mm, no more than about 6 mm, no more than about 5.5 mm, no more than about 5 mm, no more than about 4.5 mm, no more than about 4 mm, no more than about 3.5 mm, no more than about 3 mm, no more than about 2.5 mm, no more than about 2 mm, no more than about 1.5 mm, no more than about 1 mm, or no more than about 0.5 mm. Combinations of the above-referenced values of d are also possible (e.g., at least about 0 mm and no more than about 10 mm or at least about 1 mm and no more than about 5 mm), inclusive of all values and ranges therebetween. In some embodiments, d can be about 0 mm, about 0.5 mm, about 1 mm, about 1.5 mm, about 2 mm, about 2.5 mm, about 3 mm, about 3.5 mm, about 4 mm, about 4.5 mm, about 5 mm, about 5.5 mm, about 6 mm, about 6.5 mm, about 7 mm, about 7.5 mm, about 8 mm, about 8.5 mm, about 9 mm, about 9.5 mm, or about 10 mm.
In some embodiments, the pattern of the wire 962 can be optimized to decrease resistance of the electrochemical cell. For example, the pattern the wire 962 follows along the interlayer 960 can minimize the distance from a dendrite to the wire 962 to a diode, a resistor, a resistor, a fuse, a transistor, or any combination thereof. This can minimize the amount of growth a dendrite can experience in the interlayer 960, before redirecting the current and discharging the electrochemical cell. As shown, the wire 962 is formed in serpentine pattern with rounded edges. In some embodiments, the wire 962 can be formed in a serpentine pattern with sharp edges. In some embodiments, the wire 962 can be formed in a spiral pattern.
The conductive coating 1065 is disposed on the interlayer 1060. In some embodiments, the conductive coating 1065 can be composed of a conductive polymer. In some embodiments, the conductive coating 1065 can be composed of poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS), polyaniline (PANI), polypyrrole (PPy), or any combination thereof. In some embodiments, the tab 1063 can be in the form of a wire (e.g., the same or substantially similar to the tab 963, as described above with reference to
In some embodiments, the conductive coating 1065 can be coated onto the second separator 1050b. In some embodiments, the tab 1063 can be adhered to the first separator 1050a and/or the second separator 1050b and in conduct with the conductive coating 1065. In some embodiments, the tab 1063 can be coupled to a diode (not shown) via soldering, welding, butt splicing, or any other suitable coupling means. In some embodiments, the tab 1063 can be welded to a pouch tab (not shown) and connected to the diode. In some embodiments, the conductive coating 1065 can cover the entire active area of the interlayer 1065. In some embodiments, the conductive coating 1065 can be installed without a frame (e.g., the frame 762, as described above with reference to
In some embodiments, the tab 1163 can be composed of aluminum, copper, conductive ceramic, conductive polymer, carbon fiber paper, or any combination thereof. In some embodiments, the tab 1163 can be pressed into the interlayer 1160. For example, the interlayer 1160 can include a carbon/binder slurry and the tab 1163 can be pressed into the carbon/binder slurry with such a force that the tab 1163 and/or the interlayer 1160 yields. In some embodiments, the tab 1163 can be attached to the either of the separators 1150 via an adhesive, a staple, ultrasonic welding, adhesive tape, adhesive glue, or any combination thereof. In some embodiments, the tab 1163 can be in contact with the interlayer 1160 via pressure applied to the electrochemical cell. In some embodiments, the configuration shown in
In some embodiments, the distance from the sealing/adhesive area of the tab 1163 to the edge of the interlayer 1160 can be at least about 1 mm, at least about 1.5 mm, at least about 2 mm, at least about 2.5 mm, at least about 3 mm, at least about 3.5 mm, at least about 4 mm, at least about 4.5 mm, at least about 5 mm, at least about 5.5 mm, at least about 6 mm, at least about 6.5 mm, at least about 7 mm, at least about 7.5 mm, at least about 8 mm, at least about 8.5 mm, at least about 9 mm, or at least about 9.5 mm. In some embodiments, the distance from the sealing/adhesive area of the tab 1163 to the edge of the interlayer 1160 can be no more than about 10 mm, no more than about 9.5 mm, no more than about 9 mm, no more than about 8.5 mm, no more than about 8 mm, no more than about 7.5 mm, no more than about 7 mm, no more than about 6.5 mm, no more than about 6 mm, no more than about 5.5 mm, no more than about 5 mm, no more than about 4.5 mm, no more than about 4 mm, no more than about 3.5 mm, no more than about 3 mm, no more than about 2.5 mm, no more than about 2 mm, or no more than about 1.5 mm. Combinations of the above-referenced distances are also possible (e.g., at least about 1 mm and no more than about 10 mm or at least about 2 mm and no more than about 8 mm), inclusive of all values and ranges therebetween. In some embodiments, the distance from the sealing/adhesive area of the tab 1163 to the edge of the interlayer 1160 can be about 1 mm, about 1.5 mm, about 2 mm, about 2.5 mm, about 3 mm, about 3.5 mm, about 4 mm, about 4.5 mm, about 5 mm, about 5.5 mm, about 6 mm, about 6.5 mm, about 7 mm, about 7.5 mm, about 8 mm, about 8.5 mm, about 9 mm, about 9.5 mm, or about 10 mm.
In some embodiments, the width of the sealing/adhesive area of the tab 1163 (i.e., the distance along the length of the tab 1163, or in the direction up and down the page in
As shown, the interlayer 1160 includes an active area 1161. In some embodiments, the distance from the edge of the tab 1163 to the edge of the active area 1161 can be at least about 1 mm, at least about 1.5 mm, at least about 2 mm, at least about 2.5 mm, at least about 3 mm, at least about 3.5 mm, at least about 4 mm, at least about 4.5 mm, at least about 5 mm, at least about 5.5 mm, at least about 6 mm, at least about 6.5 mm, at least about 7 mm, at least about 7.5 mm, at least about 8 mm, at least about 8.5 mm, at least about 9 mm, or at least about 9.5 mm. In some embodiments, the distance from the edge of the tab 1163 to the edge of the active area 1161 can be no more than about 10 mm, no more than about 9.5 mm, no more than about 9 mm, no more than about 8.5 mm, no more than about 8 mm, no more than about 7.5 mm, no more than about 7 mm, no more than about 6.5 mm, no more than about 6 mm, no more than about 5.5 mm, no more than about 5 mm, no more than about 4.5 mm, no more than about 4 mm, no more than about 3.5 mm, no more than about 3 mm, no more than about 2.5 mm, no more than about 2 mm, or no more than about 1.5 mm. Combinations of the above-referenced distances are also possible (e.g., at least about 1 mm and no more than about 10 mm or at least about 2 mm and no more than about 8 mm), inclusive of all values and ranges therebetween. In some embodiments, the distance from the edge of the tab 1163 to the edge of the active area 1161 can be about 1 mm, about 1.5 mm, about 2 mm, about 2.5 mm, about 3 mm, about 3.5 mm, about 4 mm, about 4.5 mm, about 5 mm, about 5.5 mm, about 6 mm, about 6.5 mm, about 7 mm, about 7.5 mm, about 8 mm, about 8.5 mm, about 9 mm, about 9.5 mm, or about 10 mm.
Measuring the voltage between the first electrode and the second electrode at step 11 determines the voltage, at which the electrochemical cell is operating. Measuring the voltage between the first electrode and the first interlayer at step 12 provides a basis of comparison for detection of dendrites. If the voltage between the first electrode and the first interlayer decreases to less than a threshold value, this can be an indication of a short circuit between the first electrode and the first interlayer. In response, a circuit is closed between the first electrode and the second electrode at step 15. In some embodiments, the threshold voltage can be a voltage difference between the first electrode and the first interlayer. In some embodiments the threshold voltage can be about 0.001 V, about 0.002 V, about 0.003 V, about 0.004 V, about 0.005 V, about 0.006 V, about 0.007 V, about 0.008 V, about 0.009 V, about 0.01 V, about 0.02 V, about 0.03 V, about 0.04 V, about 0.05 V, about 0.06 V, about 0.07 V, about 0.08 V, about 0.09 V, about 0.1 V, about 0.2 V, about 0.3 V, about 0.4 V, about 0.5 V, about 0.6 V, about 0.7 V, about 0.8 V, about 0.9 V, or about 1 V, inclusive of all values and ranges therebetween. In some embodiments, the threshold voltage can be a threshold voltage fraction of the voltage measured between the first electrode and the interlayer to the voltage measured between the first electrode and the second electrode. In some embodiments, the threshold voltage fraction can be about 0.001, about 0.002, about 0.003, about 0.004, about 0.005, about 0.006, about 0.007, about 0.008, about 0.009, about 0.01, about 0.02, about 0.03, about 0.04, about 0.05, about 0.06, about 0.07, about 0.08, about 0.09, about 0.1, about 0.2, about 0.3, about 0.4, or about 0.5, inclusive of all values and ranges therebetween.
The method 10 optionally includes measuring the voltage between the first interlayer and the second electrode at step 13. In some embodiments, the circuit is closed at step 15 in response to the voltage measured between the first interlayer and the second electrode at step 13. In some embodiments, the closing of the circuit at step 15 can be in response to the voltage measured between the first interlayer and the second electrode decreasing to less than a threshold value. In some embodiments, the threshold voltage can be a voltage difference between the first electrode and the second interlayer. In some embodiments, the threshold voltage can be a voltage difference between the first interlayer and the second electrode. In some embodiments the threshold voltage can be about 0.001 V, about 0.002 V, about 0.003 V, about 0.004 V, about 0.005 V, about 0.006 V, about 0.007 V, about 0.008 V, about 0.009 V, about 0.01 V, about 0.02 V, about 0.03 V, about 0.04 V, about 0.05 V, about 0.06 V, about 0.07 V, about 0.08 V, about 0.09 V, about 0.1 V, about 0.2 V, about 0.3 V, about 0.4 V, about 0.5 V, about 0.6 V, about 0.7 V, about 0.8 V, about 0.9 V, or about 1 V, inclusive of all values and ranges therebetween. In some embodiments, the threshold voltage can be a threshold voltage fraction of the voltage measured between the first electrode and the second interlayer and the voltage measured between the first electrode and the second electrode. In some embodiments, the threshold voltage can be a threshold voltage fraction of the voltage measured between the fist interlayer and the second electrode and the voltage measured between the first electrode and the second electrode. In some embodiments, the threshold voltage fraction can be about 0.001, about 0.002, about 0.003, about 0.004, about 0.005, about 0.006, about 0.007, about 0.008, about 0.009, about 0.01, about 0.02, about 0.03, about 0.04, about 0.05, about 0.06, about 0.07, about 0.08, about 0.09, about 0.1, about 0.2, about 0.3, about 0.4, or about 0.5, inclusive of all values and ranges therebetween.
Step 15 includes closing a circuit between the first electrode and the second electrode. In some embodiments, closing the circuit can include redirecting current through a resistor. In some embodiments, closing the circuit can include redirecting current through a separate device (e.g., a lightbulb, an additional electrochemical cell, etc.).
As shown, the tab 1363 protrudes from the pouch 1380. such that the tab 1363 can connect to a voltage source, a voltage measurement point, a diode, a resistor, a transistor, a fuse, or any combination thereof. The staple 1367 encircles the separators 1350 and the tab 1363, such that the staple 1367 presses the separators 1350 and the tab 1363 together. In some embodiments, the staple 1367 partially encircles the separators 1350 and the tab 1363. In some embodiments, the staple 1367 fully encircles the separators 1350 and the tab 1363. In some embodiments, the staple 1367 can add structural stability to the tab 1363 and the separators 1350, such that the 1367 aids in preventing the tab 1363 from being removed from the electrochemical cell 1300. As shown, the staple 1367 is positioned inside the first film 1380a and the second film 1380b. In other words, the staple 1367 is inside the pouch 1380. In some embodiments, the staple 1367 can be positioned outside the pouch 1380. In some embodiments, the staple 1367 can be composed of metal. In some embodiments, the staple 1367 can be composed of plastic. In some embodiments, the staple 1367 can create a sealing area around the separators 1350 and the tab 1363. In some embodiments, the sealing area can be formed via heat sealing. In some embodiments, the sealing area can be formed via pressing the staple 1367 onto the separators 1350 at a high pressure. In some embodiments, the sealing area can be formed via an adhesive between the staple 1367 and the separators 1350. In some embodiments, the sealing area can be formed via an adhesive between the staple 1367 and the pouch 1380.
As shown, the tab 1363 is positioned between the interlayer 1360 and the first separator 1350a. In some embodiments, the tab 1363 can be positioned between the interlayer 1360 and the second separator 1350b. In some embodiments, the tab 1363 can be sealed to the interlayer 1360, the first separator 1350a, and/or the second separator 1350b (e.g., via an adhesive, heat sealing, etc.). In some embodiments, the tab 1363 can be coupled to the interlayer 1360 before assembly of the electrochemical cell 1300. In some embodiments, the tab 1363 can be coupled to the interlayer 1360 after assembly of the electrochemical cell 1300. In some embodiments, the tab 1363 can protrude through a hole in the pouch 1380. In some embodiments, the hole can be cut into the pouch 1380 before installing the tab 1363. In some embodiments, the first film 1380a and/or the second film 1380b can be cut into a desired shape prior to coupling the first film 1380a and/or the second film 1380b to the anode current collector 1320 and/or the cathode current collector 1340. The anode current collector 1320 and the cathode current collector 1340 can also have tabs connected thereto. In some embodiments, the tabs connected to the anode current collector 1320 and the cathode current collector 1340 can penetrate precut holes in the first film 1380a and/or the second film 1380b.
In some embodiments, the first sealing region 1468a and/or the second sealing region 1468b (collectively referred to as heat sealing regions 1468) can include a heat seal. In some embodiments, the sealing regions 1468 can include an adhesive layer bonding the tab 1463 to the pouch 1480. In some embodiments, the sealing regions 1468 can include tape. In some embodiments, the tape can be wrapped around the outside of the first film 1480a and/or the second film 1480b. In some embodiments, the separators 1450 can include ceramic separators. The stiffer ceramic materials can improve the stability of the sealing regions 1468 and the tab 1463 in general.
As shown, the interlayer 1760 includes a solid-state electrolyte layer 1762.
As shown, the electrochemical cell 1800 includes a circuit between the cathode 1830 and the interlayer 1860, enabling the transfer of electrical energy between the cathode 1830 and the interlayer 1860. By connecting the cathode 1830 and the interlayer 1860 electrically, the voltage in the interlayer 1860 can be increased to such a level that dissolves and/or oxidizes dendrites that have penetrated into the interlayer 1860. As shown, a voltage V1 is measured between the anode current collector 1820 and the interlayer 1860 and a voltage V2 is measured between the anode current collector 1820 and the cathode current collector 1840. Current flows from the interlayer 1860 to the cathode current collector 1840 via an electrical pathway that includes a resistor R1. The current can follow a path that includes a switch S. The current can also follow a path that includes a diode D and a resistor R2. In some embodiments the switch can be closed during current flow allowing normal charge and discharge to happen in the cell. In some embodiments, the switch S can be opened during a controlled charge. During charge, when the switch S is open, the voltage potential of the interlayer can increase by the same value of the voltage drop of the diode D and the resistor R2. In some embodiments, the diode D can be selected and placed for a specific forward or reverse breakdown voltage. In some embodiments, the breakdown voltage of the diode D can be about 0.4 V, about 0.5 V, about 0.6 V, about 0.7 V, about 0.8 V, about 0.9 V, about 1 V, about 1.5 V, about 2 V, about 2.5 V, about 3 V, about 3.5 V, about 4 V, about 4.5 V, about 5 V, about 5.5 V, or about 6 V, inclusive of all values and ranges therebetween.
In some embodiments, the resistance of the resistor R1 can be the same or substantially similar to the resistance of the resistor R2. In some embodiments, the resistance of the resistor R1 can be different from the resistance of the resistor R2. In some embodiments, the resistor R1 and the resistor R2 can have resistances that represent other impedances inherent to the electrochemical cell 1800. In some embodiments, the switch S can be replaced with a diode, a metal oxide silicon field effect transistor (MOSFET), a bipolar junction transistor (BJT), or any other suitable component. In some embodiments, the switch S can bypass the function of the diode D, creating a selective dendrite treatment mode or normal operation.
As shown, flow of current from the interlayer 1960 to the cathode current collector 1940 can be controlled via a transistor Q. As shown, a voltage V1 is measured between the anode current collector 1920 and the cathode current collector 1940 and a voltage V2 is measured between the anode current collector 1920 and the interlayer 1960. Current can flow from the interlayer 1960 to the cathode current collector 1940 via the transistor Q (and an optional resistor R). The transistor Q can act as a switching device. In some embodiments, the transistor Q can be controlled by a BMS. In some embodiments, the transistor Q can be controlled by a local hardware circuit or other system control apparatus. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 1900. In some embodiments, the transistor Q can include a BJT. In some embodiments, the transistor Q can be replaced with a diode. In some embodiments, the transistor Q can include a junction field effect transistor (FET). In some embodiments, the transistor Q can include a MOSFET. In some embodiments, the transistor Q can be replaced with a switch.
As shown, flow of current between the interlayer 1960 and the cathode current collector 1940 can be controlled via a diode D. In the event the current through the diode D falls below a threshold value, the diode D can ‘turn off,’ preventing continuous current flow to the interlayer 1960. As shown, a voltage V1 is measured between the anode current collector 2020 and the cathode current collector 2040 and a voltage V2 is measured between the anode current collector 2020 and the interlayer 2060. If the voltage of the interlayer 2060 decreases to a value below the diode forward voltage, current can flow through the diode D (and an optional resistor R), increasing the potential of the interlayer 2060. In some embodiments, the resistance value can represent other impedances inherent to the electrochemical cell 2000.
As shown, the electrochemical cell 2100 is configured as a voltage doubling mechanism, commonly called a ‘charge pump’. Common components such as SEMTECH SC632A can be used to accomplish this or similar functions. As shown, a voltage V1 is measured between the anode current collector 2120 and the cathode current collector 2140. The electrochemical cell 2100 includes switches S1 and S2, resistor R, and capacitors C1 and C2. A voltage V2 is measured between the anode current collector 2120 and the interlayer 2160. As shown, switch S1 and switch S2 control the flow of current through the electrochemical cell 2100. Through control of the switching sequence of the switch S1 and the switch S2, a voltage equal to or double the voltage of the cathode 2130 relative to the anode 2110 can be applied to the interlayer 2160. For example, the switch S1 can be switched to the up position while the switch S2 is switched to the down position to charge the capacitor C1. The capacitor C2 can charge continuously via the resistor R. In order to apply a doubling voltage, the switch S1 can be moved to the down position, connecting to the interlayer 2160, and the switch S2 is moved to the up position, electrically connecting the capacitor C1 to the top side of the capacitor C2. In such a case, the total voltage applied to the interlayer 2160 is equal to C1×V1+C2×V1, where V1 is the voltage applied to the interlayer 2160. In cases where C1 is equal to C2, this equates to 2×V1. For example, if only cell voltage V1 is applied, then the switch S2 can remain in the down position and the switch S1 can alternate between the up and the down position. In some embodiments, the input voltage can be taken from the electrochemical cell 2100 or from another source. The capacitor C2 can also be replaced with a secondary voltage source, either galvanically isolated from the cell or on a common reference.
The energy transferred to the interlayer 2160 can be controlled via the resistance of the components of the electrochemical cell 2100 (including the resistor R) and/or via other resistors (not shown). In some embodiments, the energy transferred to the interlayer 2160 can be controlled via selection of the capacitor C1 or use of other types of active components. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 2100. In some embodiments, the switch S1 and/or the switch S2 can be replaced by a diode, a MOSFET, a BJT, or any other suitable device.
As shown, the circuitry in the electrochemical cell 2200 can have a bias circuit. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 2200. As shown, a voltage V1 is measured between the anode current collector 2220 and the cathode current collector 2240 and a voltage V2 is measured between the anode current collector 2220 and the cathode current collector 2240. When the voltage of the interlayer 2260 decreases to a value of less than the voltage of the cathode current collector 2240, current can be routed to flow from the cathode current collector 2240 to the interlayer 2260, thereby increasing the potential of the interlayer 2260. As shown, a resistor R is placed between the interlayer 2260 and the cathode current collector 2240. In some embodiments, the resistance of the resistor R can be large enough to prevent self-discharge of the electrochemical cell 2200.
As shown, the circuitry in the electrochemical cell 2300 can have a bias circuit. A first voltage V1 is measured between the anode current collector 2320 and the cathode current collector 2340. A second voltage V2 is measured between the interlayer 2360 and the cathode current collector 2340. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance can represent other impedances inherent to the electrochemical cell 2300. As shown a resistor R and a diode D are placed between the interlayer 2360 and the cathode current collector 2340. When the voltage of the interlayer 2360 decreases below the voltage of the current collector 2340, leakage current can flow through the diode D, allowing the potential of the interlayer 2360 to increase. In some embodiments, the diode D can include a rectification diode (a diode not intended to function in reverse breakdown voltage). In embodiments where the diode D includes a rectification diode, current can be restricted in two ways. Reverse bias leakage current of the diode D (e.g., as defined by the manufacturer of the diode D) can be limited by specification of the diode D. Use of a standard diode can ensure that only reverse recovery current (as specified by the manufacturer of the diode) can flow through the circuit. When the recovery current is reached, the diode D can open, allowing only leakage current (as specified by the manufacturer). Also, the reverse recovery current of the diode D (e.g., as defined by the manufacturer of the diode D) can be limited by resistor R. In the event that the voltage of the interlayer 2360 exceeds the voltage of the cathode 2340, the diode D can allow a full rated current to flow, clamping the voltage potential to the voltage of the cathode 2340 and the forward voltage of the diode D.
As shown, the electrochemical cell 2400 can act as an isolated DC-DC cell. A first voltage V1 is measured between the anode current collector 2420 and the cathode current collector 2440. A second voltage V2 is measured between the interlayer 2460 and the cathode current collector 2440. As shown, the electrochemical cell 2400 includes a resistor R and a converter BB powered by a module M. The converter can be configured based on the needs of the system as a buck type converter, a boost type converter or a buck-boost style converter. As used in reference to
As shown, the electrochemical cell 2500 can have an isolated AC-DC converter attached to the cell. A first voltage V1 is measured between the anode current collector 2520 and the cathode current collector 2540. A second voltage V2 is measured between the interlayer 2560 and the cathode current collector 2540. As shown, the electrochemical cell 2500 includes a resistor R and a converter BB powered by an AC device. The converter can be configured based on the needs of the system as a buck type converter, a boost type converter or a buck-boost style converter. As used in reference to
As shown, the electrochemical cell 2600 can have a voltage regulator. A first voltage V1 is measured between the anode current collector 2620 and the cathode current collector 2640. A second voltage V2 is measured between the interlayer 2660 and the cathode current collector 2640. Current can flow from the interlayer 2660 to the cathode current collector 2640 via a regulator RG (with optional resistors R1 and R2 on either side of the regulator RG). In some embodiments, the regulator RG can include a linear regulator. In some embodiments, the regulator RG can include a switching or active regulator. When the voltage of the interlayer 2660 decreases below a defined level (e.g., about 1 V, about 1.5 V, about 2 V, about 2.5 V, about 3 V, about 3.5 V, about 4 V, about 4.5 V, about 5 V, about 5.5 V, or about 6 V, inclusive of all values and ranges therebetween), the regulator RG can cause current to flow to the interlayer 2660 to increase or decrease the voltage of the interlayer 2660. In some embodiments, the regulator RG can be controlled by a BMS, a local hardware circuit, or any other suitable system control mechanism. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 2600.
In some embodiments, the resistances R1 and R2 can be representative of other impedances inherent to the system. When the voltage of the interlayer 2660 decreases to below a threshold value, current from the regulator RG can flow (e.g., via a BMS), causing a voltage potential to be applied to the interlayer 2660. In some embodiments, the regulator RG can be controlled via BMS or by local hardware circuit or another system control method.
As shown, the electrochemical cell 2700 includes a voltage amplification system, including switches S1, S2, S3, S4. This circuit represents devices referred to as “charge pumps” and boost converters used in switching power supply applications such as the LT 3482 and the MAX633. These converters are used to create a boosted voltage for use in electronic devices. For representation, a basic functionality of a simplified charge pump is described herein. A capacitor C1 is placed between the switch S1 and the switch S2. A capacitor C2 is placed between the switch S3 and the switch S4. The electrochemical cell 2700 further includes a capacitor C3 and a resistor R on a current flow pathway. A first voltage V1 is measured between the anode current collector 2720 and the cathode current collector 2740. A second voltage V2 is measured between the interlayer 2660 and the anode current collector 2740. Depending on how the switches S1, S2, S3, S4 are configured, a voltage of at least about 2, or at least about 3 times the voltage difference between the anode current collector 2720 and the cathode current collector 2740 can be applied to the interlayer 2760. For example, with switch S1 and switch S3 in the up position while switch S2 and switch S4 are in the down position, the capacitors C1 and C2 charge. Then, switching the switch S1 and the switch S3 to the down position while switching the switch S2 and the switch S4 to the up position, triple the voltage V1 is applied to the interlayer 2760. This can be referred to as a “charge pump” procedure. In some embodiments, any of the switches S1, S2, S3, S4 can be replaced with a diode, a MOSFET, a BJT, or any other suitable device. In some embodiments, any of the switches S1, S2, S3, S4 can be controlled by a BMS, a hardware device, a control chip, an oscillator, or any other suitable controller device.
In some embodiments, the energy transferred to the interlayer 2760 can be controlled by the resistance of the system, or other resistors. In some embodiments, the energy transferred to the interlayer 2760 can be controlled by the selection of the capacitance or use of other types of active components. In some embodiments, additional stages of voltage amplification can be added to increase the total voltage applied to the interlayer 2760. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 2700.
As shown, current flow and voltage potential between the cathode current collector 2840 and the interlayer 2860 can be controlled via a transistor Q1 (and optional resistor R1). As shown, flow of current between the interlayer 2860 and the cathode current collector 2840 can be controlled via a transistor Q2 (and optional resistor R2). As shown, a voltage V1 is measured between the anode current collector 2820 and the cathode current collector 2840 and a voltage V2 is measured between the anode current collector 2820 and the interlayer 2860. In some embodiments, the transistor Q1 and/or the transistor Q2 can act as a switching device. In some embodiments, the transistor Q1 and/or the transistor Q2 can be controlled by a BMS. In some embodiments, the transistor Q1 and/or the transistor Q2 can be controlled by a local hardware circuit or other system control apparatus. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 2800. In some embodiments, the transistor Q1 and/or the transistor Q2 can include a BJT in a PNP or NPN configuration. In some embodiments, the transistor Q1 and/or the transistor Q2 can be replaced with a diode. In some embodiments, the transistor Q1 and/or the transistor Q2 can include a FET. In some embodiments, the transistor Q1 and/or the transistor Q2 can include a MOSFET. In some embodiments, the transistor Q1 and/or the transistor Q2 can be replaced with a switch. In some embodiments, the transistor Q1 can be the same type of transistor or circuit device as the transistor Q2. In some embodiments, the transistor Q1 can be a different type of transistor or circuit device from the transistor Q2. In some embodiments, the transistor Q1 and the transistor Q2 can be operated independently. In some embodiments, the transistor Q1 and the transistor Q2 can be operated in concert. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 2800.
As shown, a voltage V1 is measured between the anode current collector 2920 and the cathode current collector 2940 and a voltage V2 is measured between the anode current collector 2920 and the interlayer 2960. As shown, the electrochemical cell 2900 includes transistors Q1, Q2 and resistors R1, R2. As shown, the resistor R2 is positioned upstream of the transistor Q2 while the resistor R2 is located downstream of the transistor Q1. This differs from
As shown, the electrochemical cell includes transistors Q1, Q2 and resistors R1, R2, R3.
This circuit is commonly called a ‘push-pull’ amplifier. V1 is measured between the anode current collector 3020 and the cathode current collector 3040 and a voltage V2 is measured between the anode current collector 3020 and the interlayer 3060. As shown, the resistor R1 is located upstream of the transistor Q1 and the resistor R2 is located downstream of the transistor Q2. The resistor R3 limits the flow of current through a base of the transistor Q1 and the transistor Q2. The emitters connect to the interlayer 3060 in order to flow current into the interlayer 3060 relative to the cathode current collector 3040 and the anode current collector 3020. The circuit can be used to set any voltage potential desired between the cathode current collector 3040 and the anode current collector 3020 by selection of the voltage potential of and the current applied through the resistor R3. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 3000.
As shown, a diode D is positioned in a circuit between the cathode current collector 3140 and the interlayer 3160 to provide a continuous bias potential and a transistor Q is positioned in a circuit between the interlayer 3160 and the anode current collector 3120 (with optional resistors R1, R2) to provide a variable potential. As shown, a voltage V1 is measured between the anode current collector 3120 and the cathode current collector 3140 and a voltage V2 is measured between the anode current collector 3120 and the interlayer 3160. The circuit can be used to shift the potential of the interlayer 3160 closer to the current collector 3120. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 3100.
As shown, a transistor Q is positioned in a circuit between the interlayer 3160 and the anode current collector 3120 (with optional resistors R1, R2). As shown, a voltage V1 is measured between the anode current collector 3220 and the cathode current collector 3240 and a voltage V2 is measured between the anode current collector 3220 and the interlayer 3260. The electrochemical cell 3200 does not include a diode. Otherwise, the components of the electrochemical cell 3200 can be the same or substantially similar to the electrochemical cell 3100, as described above with reference to
As shown, the electrochemical cell 3300 includes diodes D1, D2. An optional switch S can bypass the diode D2, creating a selective dendrite treatment mode or normal operation. In some embodiments, the electrochemical cell can be absent of the switch S. In some embodiments, the switch S can be replaced with a transistor, a MOSFET, a JFET, or any other device that can bypass the diode D2. As shown, a voltage V1 is measured between the anode current collector 3320 and the cathode current collector 3340 and a voltage V2 is measured between the anode current collector 3320 and the interlayer 3360. As shown, a voltage V1 is measured between the anode current collector 3320 and the cathode current collector 3340 and a voltage V2 is measured between the anode current collector 3320 and the interlayer 3360. As shown, the circuit design of the electrochemical cell 3300 can act as a charge diode with a bypass. In some embodiments, the switch S can be opened during a controlled charge method. The diode D2 can cause a voltage drop of the interlayer 3360 relative to the cathode 3330 equal to the forward voltage drop of the diode D2. In some embodiments, the voltage drop can be about 0.1 V, about 0.2 V, about 0.3 V, about 0.4 V, about 0.5 V, about 1 V, about 1.5 V, about 2 V, about 2.5 V, about 3 V, about 3.5 V, about 4 V, about 4.5 V, about 5 V, about 5.5 V, or about 6 V, inclusive of all values and ranges therebetween. The diode D1 can cause a voltage drop of the interlayer 3360 relative to the cathode 3330 equal to the forward voltage drop of the diode D2 plus the voltage of the cathode current collector 3340 making the voltage of the interlayer 3360 higher than the voltage of the cathode current collector 3340. In some embodiments, the voltage drop can be about 0.1 V, about 0.2 V, about 0.3 V, about 0.4 V, about 0.5 V, about 1 V, about 1.5 V, about 2 V, about 2.5 V, about 3 V, about 3.5 V, about 4 V, about 4.5 V, about 5 V, about 5.5 V, or about 6 V, inclusive of all values and ranges there between. The switch S cand be closed to allow normal flow of current to the electrochemical cell 3300 without imparting voltage changes to the interlayer 3360. The switch S can be replaced by a diode, a MOSFET, a JFET, or any other suitable device or combinations thereof. The switch S can also be eliminated from the circuit using only the Diodes or other devices to apply the voltage potential on current flow. In some embodiments, the diodes D1 and D2 can also be replaced with switches diode, a MOSFET, a JFET, or any other suitable device or combinations thereof. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 3300.
As shown, a voltage V1 is measured between the anode current collector 3420 and the cathode current collector 3440, a voltage V2 is measured between the anode current collector 3420 and the interlayer 3460a, and a voltage V3 is measured between the anode current collector 3440 and the interlayer 3460b. As shown, the electrochemical cell 3400 includes switches S1a, S1b, S2a, S2b and optional resistors R1, R2, R3, R4. As shown, the switch S1a controls the flow of current between the anode current collector 3440 and the interlayer 3460a. As shown, the switch S1b controls the flow of current between the anode current collector 3440 and the interlayer 3460b. As shown, the switch S2a controls the flow of current between the interlayer 3460a and the cathode current collector 3420. As shown, the switch S2b controls the flow of current between the interlayer 3460b and the cathode current collector 3420.
In some embodiments, either of the switches S1a, S1b, S2a, S2b can be replaced with a diode, a MOSFET, a JFET, or any other suitable device or combinations thereof. In some embodiments, the switches S1a, S1b, S2a, S2b can each be replaced with the same device. In some embodiments, either of the switches S1a, S1b, S2a, S2b can be replaced with different devices. In some embodiments, either of the switches S1a, S1b, S2a, S2b can be controlled by a BMS. In some embodiments, either of the switches S1a, S1b, S2a, S2b by a local hardware circuit or other system control method. In some embodiments, the interlayers 3460 can be controlled in concert, electrically connecting any of the anode 3410, the cathode 3440, the interlayer 3460a, and/or the interlayer 3460b. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 3400.
As shown, a voltage V1 is measured between the anode current collector 3520 and the cathode current collector 3540, a voltage V2 is measured between the anode current collector 3520 and the interlayer 3560a, and a voltage V3 is measured between the anode current collector 3540 and the interlayer 3560b. As shown, the electrochemical cell 3500 includes transistors Q1, Q2, Q3, Q4 and optional resistors R1, R2, R3, R4, R5, R6. The emitters connect to the interlayer 3560a in order to flow current into the interlayer 3560a relative to the anode current collector 3520 and the cathode current collector 3540. The circuit can be used to set any voltage potential desired between the cathode current collector 3540 and the anode current collector 3520 by selection of the voltage potential of and the current applied through R3. The emitters connect to the interlayer 3560b in order to flow current into the interlayer 3560b relative to the cathode current collector 3540 and the anode current collector 3520. The circuit can be used to set any voltage potential desired between the cathode current collector 3540 and the anode current collector 3520 by selection of the voltage potential of and the current applied through R3. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 3600. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 3000, as described above with reference to
As shown, a voltage V1 is measured between the anode current collector 3620 and the cathode current collector 3640, a voltage V2 is measured between the anode current collector 3620 and the interlayer 3660a, and a voltage V3 is measured between the anode current collector 3640 and the interlayer 3660b. As shown, the electrochemical cell 3500 includes transistors Q1, Q2, Q3, Q4 and optional resistors R1, R2, R3, R4, R5, R6. The resistor R2 controls the flow of current between the transistor Q1 and the transistor Q2. The resistor R3 controls the flow of current between the transistor Q3 and the transistor Q4. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 3600.
As shown, a voltage V1 is measured between the anode current collector 3720 and the cathode current collector 3740, a voltage V2 is measured between the anode current collector 3720 and the interlayer 3760a, and a voltage V3 is measured between the anode current collector 3740 and the interlayer 3760b. As shown, the electrochemical cell 3700 includes transistors Q1, Q2, and optional resistors R1, R2, R3, R4. As shown, the transistor Q1 and the resistor R3 are placed on a circuit between the interlayer 3760a and the anode current collector 3720. As shown, the transistor Q2 and the resistor R4 are placed on a circuit between the interlayer 3760b and the anode current collector 3720. As shown, the resistor R1 is placed on a circuit between the cathode current collector 3740 and the interlayer 3760a. As shown, the resistor R2 is placed on a circuit between the cathode current collector 3740 and the interlayer 3760b. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 3700. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 3200, as described above with reference to
As shown, a voltage V1 is measured between the anode current collector 3820 and the cathode current collector 3840, a voltage V2 is measured between the anode current collector 3820 and the interlayer 3860a, and a voltage V3 is measured between the anode current collector 3840 and the interlayer 3860b. As shown, the electrochemical cell 3800 includes transistors Q1, Q2, and optional resistors R1, R2, R3, R4. As shown, the transistor Q1 and the resistor R1 are placed on a circuit between the interlayer 3860a and the cathode current collector 3840. As shown, the transistor Q2 and the resistor R2 are placed on a circuit between the interlayer 3860b and the cathode current collector 3840. As shown, the resistor R3 is placed on a circuit between the anode current collector 3820 and the interlayer 3860a. As shown, the resistor R4 is placed on a circuit between the anode current collector 3820 and the interlayer 3860b. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 3800.
As shown, a voltage V1 is measured between the anode current collector 3920 and the cathode current collector 3940, a voltage V2 is measured between the anode current collector 3920 and the interlayer 3960a, and a voltage V3 is measured between the anode current collector 3940 and the interlayer 3960b. As shown, the electrochemical cell 3900 includes transistors Q1, Q2, diodes D1, D2 and optional resistors R1, R2, R3, R4. As shown, the diode D1 and the resistor R1 are placed on a circuit between the interlayer 3960a and the cathode current collector 3940. As shown, the diode D2 and the resistor R2 are placed on a circuit between the interlayer 3960b and the cathode current collector 3940. As shown, the resistor R3 and the transistor Q1 are placed on a circuit between the anode current collector 3920 and the interlayer 3960a. As shown, the transistor Q2 and the resistor R4 are placed on a circuit between the anode current collector 3920 and the interlayer 3960b. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 3900. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 3100, as described above with reference to
As shown, a voltage V1 is measured between the anode current collector 4020 and the cathode current collector 4040, a voltage V2 is measured between the anode current collector 4020 and the interlayer 4060a, and a voltage V3 is measured between the anode current collector 4040 and the interlayer 4060b. As shown, the electrochemical cell 4000 includes transistors Q1, Q2, diodes D1, D2 and optional resistors R1, R2, R3, R4. As shown, the transistor Q1 and the resistor R1 are placed on a circuit between the interlayer 4060a and the cathode current collector 4040. As shown, the transistor Q2 and the resistor R2 are placed on a circuit between the interlayer 4060b and the cathode current collector 4040. As shown, the resistor R3 and the diode D1 are placed on a circuit between the anode current collector 4020 and the interlayer 4060a. As shown, the diode D2 and the resistor R4 are placed on a circuit between the anode current collector 4020 and the interlayer 4060b. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 4000.
As shown, a voltage V1 is measured between the anode current collector 4120 and the cathode current collector 4140, a voltage V2 is measured between the anode current collector 4120 and the interlayer 4160a, and a voltage V3 is measured between the anode current collector 4140 and the interlayer 4160b. As shown, the electrochemical cell 4100 includes resistors R1, R2. As shown, the resistor R1 is placed on a circuit between the interlayer 4160a and the cathode current collector 4140. As shown, the transistor Q2 and the resistor R2 are placed on a circuit between the interlayer 4160b and the cathode current collector 4140. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 4100. When the voltage of either of the interlayers 4160 decreases to a voltage less than the voltage of the cathode 4130, current can flow from the cathode 4130 to either of the interlayers 4160, allowing the potential of the interlayers 4160 to increase.
As shown, a voltage V1 is measured between the anode current collector 4220 and the cathode current collector 4240, a voltage V2 is measured between the anode current collector 4220 and the interlayer 4260a, and a voltage V3 is measured between the anode current collector 4240 and the interlayer 4260b. As shown, the electrochemical cell 4200 includes regulators RG1, RG2 and optional resistors R1, R2, R3. In some embodiments, the regulator RG1 and/or the regulator RG2 can include a buck converter, a buck-boost converter, and/or a boost converter. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 4200. When the voltage of either of the interlayers 4260 decreases to below a defined level, the regulator RG1 and/or the regulator RG2 can cause a current to flow, causing a voltage potential to be applied to one or more of the interlayers 4260. In some embodiments, the switching of the regulators RG1, RG2 can be controlled by a BMS or by a local hardware circuit or other system control method. In some embodiments, the regulators RG1, RG2 can be operated in concert. In some embodiments, the regulators RG1, RG2 can be operated independently. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 2500, as described above with reference to
In some embodiments, the resistances R1, R2, R3 can be representative of actual resistors, or can represent impedances inherent to the system (i.e., the electrochemical cell 4200). When the voltage of the interlayer 4260 decreases to less than a threshold value, current can flow from the regulators RG1, RG2, causing a potential to be applied to the interlayer 4260. The regulator RG1 and/or the regulator RG2 can be controlled via one or more switching devices (not shown). In some embodiments, the switching devices can be controlled by a BMS or by a local hardware circuit or other system control method. In some embodiments, each of the components of the electrochemical cell 4200 can be operated in concert, or independently. In some embodiments, the voltage V1, the voltage V2, and/or the voltage V3 can be monitored in real time.
As shown, a voltage V1 is measured between the anode current collector 4320 and the cathode current collector 4340, a voltage V2 is measured between the anode current collector 4320 and the interlayer 4360a, and a voltage V3 is measured between the anode current collector 4340 and the interlayer 4360b. The electrochemical cell 4300 includes isolated DC circuits. As shown, the electrochemical cell 4300 includes buck-boosts BB1, BB2 and optional resistors R1, R2. As shown, the buck-boosts BB1, BB2 are coupled to modules M1, M2. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 4300. When the voltage of either of the interlayers 4360 decreases to below a defined level, the buck-boost BB1 and/or the buck-boost BB2 can cause a current to flow, causing a voltage potential to be applied to one or more of the interlayers 4360. In some embodiments, either of the buck-boosts BB1, BB2 can be replaced with a buck, a boost, a charge pump, a voltage multiplier and/or a diode ladder. In some embodiments, the switching of the buck-boosts BB1, BB2 can be controlled by a BMS or by a local hardware circuit or other system control method. In some embodiments, the buck-boosts BB1, BB2 can be operated in concert. In some embodiments, the buck-boosts BB1, BB2 can be operated independently. In some embodiments, either of the modules M1, M2 can include a battery or a battery pack, or any other source of DC energy. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 2400, as described above with reference to
As shown, a voltage V1 is measured between the anode current collector 4420 and the cathode current collector 4440, a voltage V2 is measured between the anode current collector 4420 and the interlayer 4460a, and a voltage V3 is measured between the anode current collector 4440 and the interlayer 4460b. The electrochemical cell 4400 includes isolated DC circuits. As shown, the electrochemical cell 4400 includes buck-boosts BB1, BB2 and optional resistors R1, R2. As shown, the buck-boosts BB1, BB2 are coupled to AC power sources. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 4400. When the voltage of either of the interlayers 4460 decreases to below a defined level, the buck-boost BB1 and/or the buck-boost BB12 can cause a current to flow, causing a voltage potential to be applied to one or more of the interlayers 4460. In some embodiments, the switching of the AC power sources can be controlled by a BMS or by a local hardware circuit or other system control method. In some embodiments, the AC power sources can be operated in concert. In some embodiments, the AC power sources can be operated independently. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 2500, as described above with reference to
As shown, a voltage V1 is measured between the anode current collector 4520 and the cathode current collector 4540, a voltage V2 is measured between the anode current collector 4520 and the interlayer 4560a, and a voltage V3 is measured between the anode current collector 4540 and the interlayer 4560b. As shown, the electrochemical cell 4500 includes switches S1a, S1b, S2a, S2b, capacitors C1, C2, C3, and optional resistor R. As shown, the electrochemical cell 4500 is configured as a voltage doubling mechanism. Through control of the switching sequence of the switches S1a, S1b, S2a, S2b, a voltage equal to or double the voltage of the cathode 4530 relative to the anode 4510 can be applied to the interlayer 4560a and/or the interlayer 4560b. For example, the switch S1a can be switched to the up position while the switch S1b is switched to the down position to charge the capacitor C1. The capacitor C3 can charge continuously via the resistor R. In order to apply a doubling voltage, the switch S1a can be moved to the down position, connecting to the interlayer 4560a, and the switch S1b is moved to the up position, electrically connecting the capacitor C1 to the top side of the capacitor C3. In such a case, the total voltage applied to the interlayer 4560a is equal to C1×V1+C2×V1, where V1 is the voltage applied to the interlayer 4560a. In cases where C1 is equal to C3, this equates to 2×V1. For example, if only cell voltage V1 is applied, then the switch S1b can remain in the down position and the switch S1a can alternate between the up and the down position.
The energy transferred to the interlayer 4560a and/or the interlayer 4560b can be controlled via the resistance of the components of the electrochemical cell 4500 (including the resistor R) and/or via other resistors (not shown). In some embodiments, the energy transferred to the interlayers 4560 can be controlled via selection of the capacitor C1, C2, or use of other types of active components. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 4500. In some embodiments, any of the switches S1a, S1b, S2a, S2b, can be replaced by a diode, a MOSFET, a BJT, or any other suitable device. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 2100, as described above with reference to
As shown, a voltage V1 is measured between the anode current collector 4620 and the cathode current collector 4640, a voltage V2 is measured between the anode current collector 4620 and the interlayer 4660a, and a voltage V3 is measured between the anode current collector 4640 and the interlayer 4660b. As shown, the electrochemical cell 4600 includes switches S1a, S1b, S2a, S2b, S3a, S3b, S4a, S4b, capacitors C1, C2, C3, C4, C5, and optional resistor R. The capacitor C5 can charge continuously via the resistor R.
Depending on how the switches S1a, S1b, S2a, S2b, S3a, S3b, S4a, S4b, are configured, a voltage of at least about 2, or at least about 3 times the voltage difference between the anode current collector 4620 and the cathode current collector 4640 can be applied to the interlayer 4660a and/or the interlayer 4660b. For example, with switch S1a and switch S2a in the up position while switch S1b and switch S2b are in the down position, the capacitors C1 and C2 charge. Then, switching the switch S1a and the switch S2a to the down position while switching the switch S1b and the switch S2b to the up position, triple the voltage V1 is applied to the interlayer 4660. This is a charge pump procedure. In some embodiments, any of the switches S1a, S1b, S2a, S2b, S3a, S3b, S4a, S4b, can be replaced with a diode, a MOSFET, a BJT, or any other suitable device. In some embodiments, any of the switches Sla, S1b, S2a, S2b, S3a, S3b, S4a, S4b, can be controlled by a BMS, a hardware device, a control chip, an oscillator, or any other suitable controller device. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 4600. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 2700, as described above with reference to
As shown, a voltage V1 is measured between the anode current collector 4720 and the cathode current collector 4740, a voltage V2 is measured between the anode current collector 4720 and the interlayer 4760a, and a voltage V3 is measured between the anode current collector 4740 and the interlayer 4760b. As shown, the electrochemical cell 4700 includes diodes D1, D2 and optional resistors R1, R2. As shown, the diodes D1, D2 direct current from the cathode current collector 4740 to the interlayer 4760a and from the cathode current collector 4740 to the interlayer 4760b, respectively. The electrochemical cell 4700 acts as a diode conductance cell. When the voltage of the interlayer 4760a and/or the interlayer 4760b decreases to a value of less than the forward voltage of the diodes D1, D2, current can flow through either of the diodes D1, D2, increasing the potential of the interlayer 4760a and/or the interlayer 4760b. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 4700. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 200, as described above with reference to
As shown, a voltage V1 is measured between the anode current collector 4820 and the cathode current collector 4840, a voltage V2 is measured between the anode current collector 4820 and the interlayer 4860a, and a voltage V3 is measured between the anode current collector 4840 and the interlayer 4860b. As shown, the electrochemical cell 4800 includes diodes D1, D2 and optional resistors R1, R2. As shown, the diodes D1, D2 direct current from the interlayer 4860a to the cathode current collector 4840 and from the interlayer 4680b to the cathode current collector 4840, respectively. The electrochemical cell 4800 includes a backflow circuit bias. When the voltage of the interlayer 4860a and/or the interlayer 4860b decreases to a value of less than the forward voltage of the diodes D1, D2, current can flow through either of the diodes D1, D2, increasing the potential of the interlayer 4860a and/or the interlayer 4860b. In some embodiments, if either of the diodes D1, D2 includes a rectification diode (i.e., a diode not intended to function in a reverse breakdown voltage), the current can be restricted in two ways. First the reverse bias leakage current can be defined by the manufacturer of the component. Second the reverse recovery current of the diode D1 and/or the diode D2 can be defined by the manufacturer of the component. In the event the current exceeds a threshold value, the diode D1 and/or the diode D2 can switch off, preventing excess current flow to the interlayer 4860a and/or the interlayer 4860b. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 4800. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 200, as described above with reference to
As shown, the electrochemical cell 4900 includes diodes D1 and D2 and optional resistors R1, R2, R3. The electrochemical cell 4900 includes charge diode capability. The diode D2 can cause a voltage drop of the interlayer 4960a relative to the cathode 4930 equal to the forward voltage drop of the diode D2. This voltage drop can be about 0.1, about 0.2, about 0.3, about 0.4, about 0.5, about 0.6, about 0.7, about 0.8, about 0.9, or about 1 times the full voltage difference between the cathode 4930 and the anode 4910, inclusive of all values and ranges therebetween. The diode D2 can operate in forward breakdown, reverse breakdown, and/or any other topology. The diode D1 can be selected for a specific forward or reverse voltage and can be placed for forward or reverse voltage and can be placed for forward or reverse breakdown voltage. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 4900. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 3300, as described above with reference to
As shown, the electrochemical cell 5000 includes diodes D1 and D2, switch S and optional resistors R1, R2, R3. The electrochemical cell 5000 includes charge diode capability. The diode D2 can cause a voltage drop of the interlayer 5060a relative to the cathode 5030 equal to the forward voltage drop of the diode D2. This voltage drop can be about 0.1, about 0.2, about 0.3, about 0.4, about 0.5, about 0.6, about 0.7, about 0.8, about 0.9, or about 1 times the full voltage difference between the cathode 5030 and the anode 5010, inclusive of all values and ranges therebetween. The diode D2 can operate in forward breakdown, reverse breakdown, and/or any other topology. The diode D1 can be selected for a specific forward or reverse voltage and can be placed for forward or reverse voltage and can be placed for forward or reverse breakdown voltage. During charge, when the switch S is open, the voltage of the interlayer 5060a and/or the interlayer 5060b can increase by the same value as the voltage drop across any of the diodes D1, D2 or the resistors R1, R2, R3. In some embodiments, the switch S can bypass the function of the diodes D1, D2, creating a selective dendrite treatment mode or normal operation. In some embodiments, the switch S2 can be replaced with a transistor, a MOSFET, a JFET, or any other devices used to bypass the function of the diodes D1 D2. In some embodiments, the resistances through each current flow path can be the same or substantially similar. In some embodiments, the resistances through each current flow path can be different from each other. In some embodiments, the resistance values can be from separate components, or they can represent other impedances inherent to the electrochemical cell 5000. In some embodiments, the functionality of the circuit can be the same or substantially similar to that of the electrochemical cell 3000, as described above with reference to
As shown in
During initial cycling and gas formation depicted in
As shown in
While the anode 5210 is electrically connected to the interlayer 5260, lithium ions and electrons pass from the anode 5210 to the interlayer 5260. As shown, in
In
In some embodiments, the sequence depicted in
A tab 5363 is welded to the metal section 5364 via a weld area W. In some embodiments, the welding can be via ultrasonic welding. In some embodiments, the tab 5363 can be a mesh tab. The mesh tab can be light to avoid the tear of welding on the separator 5350. In some embodiments, the tab 5363 can include PE or a conductive polymer to be heat treated and then laminated to an interlayer. In some embodiments, the tab 5363 can be laminated to the separator 5350. In some embodiments, the tab 5363 can be stitched to the interlayer via a wire or thread, including metal wire, polyamide thread, polyester thread, or other polymer based material. In some embodiments, a male/female pinch can be used and a bolt can be tightened to fix the tab 5363 to the separator 5350.
In some embodiments, the interlayer tab 5863 can extend from a coupling to a carbon coated separator, as depicted in
As shown in
In some embodiments, the distance d can be at least about 50 μm, at least about 100 μm, at least about 200 μm, at least about 300 μm, at least about 400 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 1.1 mm, at least about 1.2 mm, at least about 1.3 mm, at least about 1.4 mm, at least about 1.5 mm, at least about 1.6 mm, at least about 1.7 mm, at least about 1.8 mm, or at least about 1.9 mm. In some embodiments, the distance d can be no more than about 2 mm, no more than about 1.9 mm, no more than about 1.8 mm, no more than about 1.7 mm, no more than about 1.6 mm, no more than about 1.5 mm, no more than about 1.4 mm, no more than about 1.3 mm, no more than about 1.2 mm, no more than about 1.1 mm, no more than about 1 mm, no more than about 900 μm, no more than about 800 μm, no more than about 700 μm, no more than about 600 μm, no more than about 500 μm, no more than about 400 μm, no more than about 300 μm, no more than about 200 μm, or no more than about 100 μm. Combinations of the above-referenced distances d are also possible (e.g., at least about 50 μm and no more than about 2 mm or at least about 100 μm and no more than about 1 mm), inclusive of all values and ranges therebetween. In some embodiments, the distance d can be about 50 μm, about 100 μm, about 200 μm, about 300 μm, about 400 μm, about 500 μm, about 600 μm, about 700 μm, about 800 μm, about 900 μm, about 1 mm, about 1.1 mm, about 1.2 mm, about 1.3 mm, about 1.4 mm, about 1.5 mm, about 1.6 mm, about 1.7 mm, about 1.8 mm, about 1.9 mm, or about 2 mm.
In some embodiments, the anodes 5910, the anode current collector 5920, the cathodes 5930, the cathode current collectors 5940, the separators 5950a, 5950b, 5950c, 5950d (collectively referred to as separators 5950), and the interlayers 5960 can be oriented in a single sheet stacking orientation (as shown), a z-stacking configuration, a cylindrical winding configuration, or a prismatic winding configuration. Each of these configurations can allow for the contact to occur between the interlayers 5960 and an adjacent electrode. As shown, the interlayer 5960a contacts one of the cathodes 5930. In some embodiments, the short circuit can be caused by contact between one of the interlayers 5960 and one of the anodes 5910.
As shown, the interlayer 6060a extends beyond the separator 6050a by a distance d, while the interlayer 6060b is not offset from its adjacent separator 6050c. Such a configuration allows for the detection of electrode misalignments adjacent only to the interlayer 6060a and not to the interlayer 6060b. In some embodiments, the distance d can be any of the distances d described above with reference to
As shown, the interlayer 6160a and the separator 6150b are offset from the separator 6150a by a distance d1. As shown, the interlayer 6160b and the separator 6150c are offset from the separator 6150b by a distance d2. This double offset allows for both the interlayer 6160a and the interlayer 6160b to contact the cathode 6130 in the case of a misalignment. In some embodiments, the interlayer 6160a and/or the interlayer 6160b can extend by offset distances on the side adjacent to the anode 6110, such that a misalignment between the anode 6110 and either of the interlayers 6160 is detectable.
In some embodiments, the distance d1 and/or the distance d2 can be at least about 50 μm, at least about 100 μm, at least about 200 μm, at least about 300 μm, at least about 400 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 1.1 mm, at least about 1.2 mm, at least about 1.3 mm, at least about 1.4 mm, at least about 1.5 mm, at least about 1.6 mm, at least about 1.7 mm, at least about 1.8 mm, or at least about 1.9 mm. In some embodiments, the distance d1 and/or the distance d2 can be no more than about 2 mm, no more than about 1.9 mm, no more than about 1.8 mm, no more than about 1.7 mm, no more than about 1.6 mm, no more than about 1.5 mm, no more than about 1.4 mm, no more than about 1.3 mm, no more than about 1.2 mm, no more than about 1.1 mm, no more than about 1 mm, no more than about 900 μm, no more than about 800 μm, no more than about 700 μm, no more than about 600 μm, no more than about 500 μm, no more than about 400 μm, no more than about 300 μm, no more than about 200 μm, or no more than about 100 μm. Combinations of the above-referenced distances d are also possible (e.g., at least about 50 μm and no more than about 2 mm or at least about 100 μm and no more than about 1 mm), inclusive of all values and ranges therebetween. In some embodiments, the distance d1 and/or the distance d2 can be about 50 μm, about 100 μm, about 200 μm, about 300 μm, about 400 μm, about 500 μm, about 600 μm, about 700 μm, about 800 μm, about 900 μm, about 1 mm, about 1.1 mm, about 1.2 mm, about 1.3 mm, about 1.4 mm, about 1.5 mm, about 1.6 mm, about 1.7 mm, about 1.8 mm, about 1.9 mm, or about 2 mm.
In some embodiments, the carbon layer 6261 can include conductive carbon. In some embodiments, the carbon layer 6261 can include binder. In some embodiments, the carbon layer 6261 can include about 5 wt %, about 10 wt %, about 15 wt %, about 20 wt %, about 25 wt %, about 30 wt %, about 35 wt %, about 40 wt %, about 45 wt %, about 50 wt %, about 55 wt %, about 60 wt %, about 65 wt %, about 70 wt %, about 75 wt %, about 80 wt %, about 85 wt %, about 90 wt %, about 95 wt %, or about 100 wt % conductive carbon, inclusive of all values and ranges therebetween. In some embodiments, the carbon layer 6261 can include about 5 wt %, about 10 wt %, about 15 wt %, about 20 wt %, about 25 wt %, about 30 wt %, about 35 wt %, about 40 wt %, about 45 wt %, about 50 wt %, about 55 wt %, about 60 wt %, about 65 wt %, about 70 wt %, about 75 wt %, about 80 wt %, about 85 wt %, about 90 wt %, about 95 wt %, or about 100 wt % binder, inclusive of all values and ranges therebetween.
In some embodiments, the binder can include polyvinylidene chloride (PVDC). In some embodiments, the binder can include PVDF. In some embodiments, the binder and the conductive carbon can be bound together via melting and/or polymerizing (e.g., crosslinking) the binder and physically connecting the binder to the conductive carbon. In some embodiments, the binder and the conductive carbon can be melt-mixed together. In some embodiments, the binder can be melted via heating, ultrasonic application, and/or ultraviolet application. In some embodiments, the binder can be melted under pressure. In some embodiments, the mixing and/or melting of the binder with the conductive carbon can occur inside an electrochemical cell (i.e., after the electrochemical cell has been built). In some embodiments, the mixing and/or melting of the binder with the conductive carbon can occur outside of an electrochemical cell (e.g., in the construction of individual unit cells).
In some embodiments, the carbon layer 6261 can be mixed with a solvent before disposing the carbon layer 6261 onto the separator 6250. In some embodiments, the binder in the coating 6262 can be mixed with a solvent. In some embodiments, the carbon layer 6261 can include a first solvent and the coating 6262 can include a second solvent, the second solvent different from the first solvent. In some embodiments, the second solvent can be the same as the first solvent. In some embodiments, the carbon layer 6261 can be coated onto the separator 6250 with water, carboxymethyl cellulose (CMC), or any combination thereof. In some embodiments, the coating 6262 can include PVDF, n-methyl pyrrolidone (NMP), or any combination thereof.
As shown in
Series voltage monitors can be used to detect the interlayer voltage relative to the anode or the cathode. Differential voltage monitors can also be used based on system implementation. The electrochemical cell system 63000 can compare the interlayer voltage to the voltage of an anode or a cathode. If he voltage, relative to the cathode, is within a defined range (e.g., about −0.2 V to about −1 V, about −0.1 V, about −0.2 V, about −0.3 V, about −0.4 V, about −0.5 V, about −0.6 V, about −0.7 V, about −0.8 V, about −0.9 V, about −1 V, about −1.1 V, about −1.2 V, about −1.3 V, about −1.4 V, or about −1.5 V, inclusive of all values and ranges therebetween), then no dendritic growth has been detected. If the voltage, relative to the cathode is below a defined level (e.g., less than about −0.5 V, less than about −0.6 V, less than about −0.7 V, less than about −0.8 V, less than about −0.9 V, less than about −1 V, less than about −1.1 V, less than about −1.2 V, less than about −1.3 V, less than about −1.4 V, or less than about −1.5 V, inclusive of all values and ranges therebetween), then dendritic growth has been detected.
In testing, dendritic growth has created perturbations of the interlayer voltage. The system controller 6301 can sense the voltage of the electrodes and also use advanced filtering and waveform evolution to detect dendritic growth. This filtering can be in the form of active hardware filtering or digital filters of various types. Hardware for filtering can include high pass, low pass, band pass, proportional, integration, differential, amplitude, frequency conversion, or other types of active or passive designs. A hardware filtering can be via an external circuit (e.g., a BMS), that can detect the voltage and current change and quantify the variations. The digital filtering can be done in a standard processor, a field-programmable gate array (FPGA), or a digital system processor (DSP) using compact, low speed, or high-speed filtering methods. The model used for digital filter can include finite impulse response (FIR), infinite impulse response (IIR), S model, Fast Fourier Transform (FFT), advanced Fast Fourier Transform (AFFT), or any other appropriate filtering or detection model method or combinations thereof in order to isolate the characteristic event.
In some embodiments, a device can be added to one or more of the electrochemical cells 6300 or to the system controller 6301 that can apply a constant potential, resistance, or current to the interlayer of the electrochemical cells 6300. In some embodiments, the device can provide a continuous excitation of the interlayer, such that a dendrite would not be able to form across the separator layer. In some embodiments, the device can be similar to devices described in the '597 publication. In some embodiments, the device can incorporate a single passive device, or any number of components in an electrical control methodology. In some embodiments, a prevention method can be used as part of an overall control strategy, in which the voltage potential, current, and resistance passing through the interlayer can be changed based on a control algorithm. In some embodiments, dendrites can be detective via actively modulating, pulsing, and/or alternating a controlled potential of the interlayer to remediate or prevent a dendrite from forming.
In some embodiments, the potential of the interlayers can be changed, depending on how the dendritic growth is dissolved or blocked. A high potential, close to or exceeding the cathode voltage can be effective to dissolve a metallic dendrite including lithium, iron, nickel, chromium, and/or copper. A low potential, close to or below the anode voltage can be effective to store the lithium ion in the hard carbon layer for pre-lithiation purposes. The system controller 6301 can act in an active prevention mode, where the potential of the interlayer can be modulated or changed to apply different voltage potentials and either increasing the voltage potentials (cathode side) or decreasing the voltage potentials (anode side) to maintain a cell function or health.
The battery functions can include, but are not limited to: a current/power limit algorithm, a cell voltage algorithm, a cell balance control, a state of charge (SOC)/state of health (SOH)/state of function (SOF) monitor, thermal control, dendrite detection, and a dendrite control algorithm. The current/power limit algorithm limits the amount of current that can flow through the electrochemical cells by onboard control or through the system interface. The cell voltage algorithm limits the maximum voltage of either of the electrodes with respect to the other electrodes in the electrochemical cells. The cell balance control prevents significant variations in cell voltage. The SOC/SOH/SOF monitor screens the general health of the electrochemical cells. The thermal control subsystem adjusts the movement of current based on the temperatures of the electrochemical cells and interfaces to heaters/chillers (not shown) as needed to heat and cool the electrochemical cell system 67000. The dendrite detection and dendrite control algorithms monitor voltage in the interlayers of the electrochemical cells and adjust current or potential to prevent or remove dendrites.
The cell interfaces can include, but are not limited to: current measurement, cell balance, cell voltage measurement, cell temperature measurement, interlayer measurement, and interlayer control algorithms. The current measurement algorithm measures the movement of current between electrochemical cells. The cell balance algorithm shifts the movement of current based on imbalances in the cells. The cell voltage measurement and cell temperature measurement algorithms measure the voltage and temperature of the cells. The interlayer measurement algorithm measures the voltage of the interlayers in the electrochemical cells. The interlayer control algorithm controls movement of current or potential into and out of the interlayers.
A first voltage V1 is measured between the anode current collector 6820 and the interlayer 6860. A second voltage V2 is measured between the anode current collector 6820 and the anode current collector 6820 and the cathode current collector 6840. The pre-lithiation layer 6855 can be a functional layer. In some embodiments, the pre-lithiation layer 6855 can be coated on the separator 6850a. In some embodiments, the pre-lithiation layer 6855 can include functional lithium-containing materials with a high specific capacity and a low decomposition potential.
During initial charge, the pre-lithiation layer 6855 can decompose to provide extra lithium ions for pre-lithiation of the anode 6810. In some embodiments, the pre-lithiation layer 6855 can include LiFePO4, Li5FeO4, or any combination thereof. During operation, a continuous charge and discharge with an interlayer potential greater than about 1V can diminish a lithium dendrite that has penetrated the interlayer 6860 and revert charge back to the pre-lithiation layer 6855.
The PTC layer 6965 can resist the flow of current therethrough when the PTC layer 6965 takes on heat. In some embodiments, the PTC layer 6965 can have a temperature-dependent electrical resistance. In some embodiments, the PTC layer 6965 can be composed of poly-crystalline materials, conductive polymers, barium carbonate, titanium oxide, tantalum, silica, manganese, activated carbon, hard carbon, graphite, carbon grains, or any combination thereof. In some embodiments, the PTC layer 6965 can include a polymer with carbon grains embedded therein. In some embodiments, the PTC layer 6965 can include any of the properties of the PTC materials described in U.S. Patent Publication No. 2023/0022329 (“the '329 publication”), filed Jul. 20, 2022 and titled “Electrodes and Electrochemical Cells with Positive Temperature Coefficient Materials and Methods of Producing the Same,” the disclosure of which is hereby incorporated by reference in its entirety.
As shown, the PTC layer 6965 is disposed between the interlayer 6960 and the separator 6950a. In some embodiments, the PTC layer 6965 can be disposed between the interlayer 6960 and the separator 6950b. In some embodiments, the PTC layer 6965 can be disposed between the separator 6950a and the cathode 6930. In some embodiments, the PTC layer 6965 can be disposed between the separator 6950b and the anode 6910.
In use, a short circuit is detected (i.e., via the interlayer 6960). Energy is then directed away from the positive electrode to reduce the SOC of the electrochemical cell 6900. The voltage is then reduced. In other words, an external short circuit is initiated. Activation of the PTC layer 6965 is slow during an internal short circuit, and the PTC layer 6965 does not react fast enough to stop the flow of current through the electrochemical cell 6900. The external short circuit provides enough heat through the cell to induce the PTC layer 6965 to substantially increase its electrical resistance.
As shown, a voltage V1 is measured between the anode current collector 7020 and the interlayer 7060, a voltage V2 is measured between the anode current collector 7020 and the cathode current collector 7040. As shown, a switch S1 and a resistor R1 control a cell drain control module. The drain control module is effectively a cell shutdown module. By engaging the switch S1, the electrochemical cell 7000 is shut down and the voltage is drained to zero or near zero. The drain control module can be used if other efforts to prevent or remediate a detected dendrite are unsuccessful.
A switch S2 and resistors R2 and R3 control a dendrite prevention and remediation control module. The switch S2 is closed to create a circuit with the resistor R3 to activate the prevention control module. The switch S2 is closed to create a circuit with the resistor R2 to activate the remediation control module. The prevention control module pulls up the voltage of the interlayer 7060 to be more similar to the voltage of the cathode 7030. This prevents dendrites from forming or growing through the interlayer 7060. The remediation control module also pulls up the voltage of the interlayer 7060 to be closer to that of the cathode 7030. This shrinks and aids in eliminating dendrites that have already formed in the interlayer 7060. The resistance of the resistor R2 is less than the resistance R3, so that more energy from the dendrites can flow through the resistor R2, as compared to prevention. In some embodiments, the resistor R2 can have a resistance less than that of the resistor R3 by a factor of about 1.1, about 1.2, about 1.3, about 1.4, about 1.5, about 1.6, about 1.7, about 1.8, about 1.9, about 2, about 3, about 4, about 5, about 6, about 7, about 8, about 9, about 10, about 20, about 30, about 40, about 50, about 60, about 70, about 80, about 90, or about 100, inclusive of all values and ranges therebetween.
A switch S3 and resistor R4 control a cell remediation pulldown control module. The controller 7005 receives information about voltage V1 and V2 and controls switches S1, S2, S3 as well as an air transport switch.
The controller 7005 can operate via a BMS to manage the growth of dendrites. In some embodiments, the controller 7005 can include main functions and function decompositions. The main functions can include (1) providing communications, (2) providing current flow control, (3) providing safe operation, (4) providing dendrite control module, and/or (5) providing cell protection. The (1) providing communications function can include (a) providing calibration and/or (b) providing operating status of the electrochemical cell 7000. The (2) providing current flow control module can include (a) providing current flow between the cathode 7030 and the interlayer 7060, (b) providing current flow between the cathode 7030 and the anode 7010, and/or (c) providing no current flow in the electrochemical cell 7000. In some embodiments, the (3) providing safe operation module can include (a) providing dendrite remediation, (b) preventing a thermal event, and/or (c) providing a safe state. In some embodiments, the (4) providing dendrite control module can include (a) providing dendrite detection, (b) providing dendrite prevention, (c) providing dendrite remediation, and/or (d) providing voltage sense. In some embodiments, the (5) providing cell protection module can include (a) providing fault protection, and/or (b) providing data logging.
In use, the electrochemical cell can practice a protocol that includes detection, prevention, and remediation. Detection can include using a PI loop to measure the voltage difference between the total cell voltage (i.e., the voltage between the anode current collector 7020 and the cathode current collector 7040) and the interlayer voltage (i.e., the voltage between the interlayer 7060 and the anode current collector 7020). If the interlayer voltage decreases to less than a set threshold value, the potential of the interlayer 7060 is increased by electrically connecting the interlayer 7060 to the cathode current collector 7040 via the switch S2 through the resistor R3. This takes advantage of the pullup control module.
Dendrite prevention can be exercised by applying a resistance to the interlayer 7060. This resistance can provide continuous excitation of the interlayer 7060, such that a dendrite cannot form across either of the separators 7050. This prevention method can be used as part of an overall control strategy where the voltage potential, current, and resistance to the interlayer 7060 can be changed based on a control algorithm (e.g., a control algorithm used by the controller 7005).
The control system can act in an active prevention mode where the potential of the interlayer 7060 is modulated or changed to apply different potentials and increasing them (i.e., to be closer to the potential of the cathode 7030) or decreasing them (i.e., to be closer to the potential of the anode 7010) via the switch S3 and the resistor R4 to maintain the functioning of the electrochemical cell 7000. When the dendrite forms and interfaces with the interlayer 7060, the voltage of the interlayer 7060 can be pulled up toward the potential of the cathode 7030. The dendrite is dissolved or remediated, and the voltage potential of the interlayer 7060 returns to near the voltage potential of the cathode 7030 with respect to the anode 7010.
As shown, the cell drain control module closes the switch S1 and runs current through the resistor R1 to drain the electrochemical energy from the electrochemical cell 7000. This module can be used after the aforementioned dendrite remediation mechanisms fail. This can be enabled in extreme situations where the controller 7005 deems that a thermal event can be pending. The dendrite prevention pullup control module can be enabled to slowly pass a current potential to the interlayer 7060 to prevent dendrites from forming. The dendrite remediation pullup control mechanism can be enabled to more rapidly pass a current potential to the interlayer 7060 to raise the voltage of the interlayer 7060 to be closer to that of the cathode 7030. This can be used to remediate any dendrites the controller 7005 identifies during a detection phase. The cell remediation pulldown control module can be used during early development testing to lower the voltage of the interlayer 7060 to be more similar to that of the anode 7010.
In some embodiments, multiple versions or iterations of the electrochemical cell 7000 can be connected in series and/or in parallel. In some embodiments, the control of the electrochemical cell 7000 or multiple electrochemical cells connected in series and/or in parallel can be via a BMS. The types of switches and resistors employed in the electrochemical cell 7000 can be implemented in many ways in the detailed circuit design. The air transport switch can be used to drain the electrochemical cell 7000 to a desired SOC (e.g., about 5%, about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, about 40%, about 45%, or about 50% SOC, inclusive of all values and ranges therebetween) for air transport or any other shipping or movement of the electrochemical cell 7000. This can reduce the probability of dangerous electrical discharges
During operation, the controller 7005 can send various signals to the components of the electrochemical cell 7000. Table 1 shows example signals that can be sent from the controller 7005 to the to the components of the electrochemical cell 7000.
In some embodiments, the controller 7005 can implement one or more software control methods. In some embodiments, the controller 7005 can implement a dendrite detection method. Using a software monitoring loop, a voltage difference is measured between the total cell voltage (i.e., the voltage between the anode 7010 and the cathode 7030) and the interlayer voltage (i.e., the voltage between the anode 7010 and the interlayer 7060). If the interlayer voltage decreases to less than a threshold value (e.g., about 1 V, about 1.5 V, about 2 V, about 2.5 V, about 3 V, about 4 V, etc.), the potential of the interlayer 7060 is increased by connecting the interlayer 7060 to the cathode 7030 (i.e., through the resistor R2 or the resistor R3).
In some embodiments, the controller 7005 can implement a prevention control method via software. In implementing the prevention control method, a resistance can be applied to the interlayer 7060. Specifically, the switch S2 can close to switch on the resistor R3 to provide current flow from the cathode 7030 to the interlayer 7060 to help prevent dendrite growth. The resistance provides a continuous excitation of the interlayer 7060, such that a dendrite would not be able to form across either of the separators 7050. The prevention method can be used as part of an overall control strategy, wherein the voltage potential, current, and resistance to the interlayer 7060 can be changed based on a software control algorithm.
In some embodiments, the controller 7005 can implement a remediation control method via software. In implementing the remediation control method, the controller 7005 can act in an active prevention mode, where the potential of the interlayer 7060 is modulated or changed to apply different potentials. The potential of the interlayer 7060 can be increased (cathode side) or decreased (anode side) to maintain the cell function. When the dendrite forms and interfaces with the interlayer 7060, the voltage of the interlayer 7060 can be pulled up to the potential of the cathode 7030, with respect to the anode 7010. The dendrite is dissolved or remediated, and the voltage potential of the interlayer 7060 can return to be more similar to the voltage potential of the cathode 7030 with respect to the anode 7010.
The software implemented by the controller 7005 can include many operating modes. In some embodiments, the controller 7005 can implement an initialization mode, which executes once the controller 7005 has powered up. The controller 7005 can implement a monitoring mode. The monitoring mode can act as a main loop, in which voltages are read and a dendrite detection algorithm is repeatedly executed. In some embodiments, the controller 7005 can implement a remediation mode, in which voltages are read and a remediation algorithm executes. In some embodiments, the controller 7005 can implement a draining mode. This discharges the cell voltage (i.e., the voltage between the anode 7010 and the cathode 7030) down to about 0 V to prevent a thermal event. This mode should be implemented to protect the safety and property of the user. In some embodiments, the controller 7005 can include a power down mode, implemented via a BMS master controller when the BMS is powering down. In some embodiments, the controller 7005 can implement a prevention mode, in which voltages are read and a prevention algorithm executes. This mode can be executed at various intervals to allow a small potential of current to flow from the cathode 7030 to the interlayer 7060 to prevent formation of dendrites.
In some embodiments, the controller 7005 can implement a fault mode. The fault mode is a state entered when a fault is detected by the controller 7005. The electrochemical cell 7000 can operate in a safe state when fault mode is entered. The safe state can be defined by the control system functional design as determined by the system architectural design of the given device. Faults can be implemented in software control systems to protect the hardware of the electrochemical cell 7000 and the safety of the user. Examples of faults can include dendrite circuit overtemperature fault, overtemperature of the electrochemical cell 7000 fault, under temperature of the electrochemical cell 7000 fault, drain cell active fault (in which the aforementioned drain functionality has been activated), dendrite remediate failed fault (in which the aforementioned remediation functionality has failed), dendrite prevention failed fault (in which the aforementioned prevention functionality has failed), interlayer voltage differential warning fault (in which the differential between the voltage of the interlayer 7060 and the anode 7010 has decreased to less than a threshold value), interlayer voltage differential critical fault (in which the differential between the voltage of the interlayer 7060 and the anode 7010 has decreased to less than a more critical threshold value), overall cell voltage overvoltage fault, and/or overall cell voltage undervoltage fault.
In some embodiments, signals from throughout the electrochemical cell 7000 can be transferred (e.g., via a controller area network (CAN) bus) to the controller 7005. In some embodiments, such signals can include overall cell voltage between the anode 7010 and the cathode 7030, maximum overall cell voltage during the current power cycle, minimum overall cell voltage during the current power cycle, dendrite detection counter, fault status, voltage difference between the anode 7010 and the interlayer 7060, maximum voltage difference between the anode 7010 and the interlayer 7060, minimum voltage difference between the anode 7010 and the interlayer 7060, drain switch status and override, prevent switch status and override, remediate switch status and override, and power down command.
In some embodiments, the software implemented by the controller 7005 can include a detection algorithm. Via the detection algorithm, the controller 7005 can use software to detect the difference between dendrite growth, a cell short circuit, and cell gas generation. Once detected, the controller 7005 can take appropriate reactionary steps to attempt to remediate and report the system status via CAN messaging.
In some embodiments, the software implemented by the controller 7005 can execute signal filtering. For voltage signal inputs, several potential software filter algorithm methods can be implemented. These can include a median filter, a moving average filter, and a low-pass filter. Such filter algorithms can also be used with other types of sensors. The proper filter can depend on factors such as signal dynamics, accuracy, and loss limit.
In some embodiments, the software implemented by the controller 7005 can include a dendrite control algorithm. For controlling the dendrite growth remediation, a closed loop control system can be used, implementing a proportional-integral-derivative (PID)_algorithm, as diagrammed in
As shown, a voltage V1 is measured between the anode current collector 7120 and the interlayer 7160a, a voltage V2 is measured between the anode current collector 7120 and the interlayer 7160b, and a voltage V3 is measured between the anode current collector 7120 and the cathode current collector 7140. As shown, a switch S1 and a resistor R1 control a cell drain control module. A switch S2 and resistors R2 and R3 control a dendrite prevention and remediation control module. A switch S3 and resistor R4 control a cell remediation pulldown control module. The controller 7105 receives information about voltage V1 and V2 and controls switches S1, S2, S3 as well as an air transport switch.
In some embodiments, the electrochemical cell 7100 and its controller 7105 can have any of the functionalities of the electrochemical cell 7000, and the controller 7005, as described above with reference to
As shown, a voltage V1 is measured between the anode current collector 7320 and the interlayer 7360a, a voltage V2 is measured between the anode current collector 7320 and the interlayer 7360b, and a voltage V3 is measured between the anode current collector 7320 and the cathode current collector 7340. A diode D1 connects the interlayer 7360b and the cathode current collector 7340. A diode D2 connects the interlayer 7360a to the cathode current collector 7340. Current can flow from the anode current collector 7320 to the cathode current collector 7340 via a switch S and a resistor R.
As shown, the interlayer 7360b is in direct contact with the anode 7310. In some embodiments, the interlayer 7360b can be directly coupled to the anode 7310. With this direct coupling, the interlayer 7360b is shorted from the beginning of the operation of the electrochemical cell 7300. In some embodiments, the interlayer 7360b can be welded and/or brazed to the anode 7310. In some embodiments, the anode 7310 can include a lithium metal. In some embodiments, the anode 7310 can include a zero-lithium anode. In use, closing the switch S can create an external short circuit in response to signals from measuring the voltage V1. The interlayer 7360b can be dedicated to its function as a coating but can be attached to the anode 7310. In some embodiments, the interlayer 7360a and/or the interlayer 7360b can include carbon. In some embodiments, the interlayer 7360a and/or the interlayer 7360b can include allotropes of carbon including activated carbon, hard carbon, soft carbon, Ketjen, carbon black, graphitic carbon, carbon fibers, carbon microfibers, vapor-grown carbon fibers (VGCF), fullerenic carbons including “buckyballs”, carbon nanotubes (CNTs), multiwall carbon nanotubes (MWNTs), single wall carbon nanotubes (SWNTs), graphene, graphene sheets or aggregates of graphene sheets, and materials comprising fullerenic fragments, or any combination thereof.
In some embodiments, the interlayer 7360b can include scarified additives to form an insulative and/or stabilized SEI layer. In some embodiments, the anode 7310 can be connected to an external circuit. The external circuit can have a high resistance sufficient to prevent a short circuit between the anode 7310 and the interlayer 7360b. In some embodiments, the resistance of the external circuit can be variable. For example, the external circuit can have a first voltage during formation and/or initial charging of the electrochemical cell 7300 and a second voltage during discharge of the electrochemical cell 7300. During formation, the resistance can be lower than during cycling in order to facilitate SEI growth. The resistance can then be increased during cycling to limit self-discharge. This can facilitate controlled deposition between the interlayer 7360b and the anode 7310, such that the deposited material does not penetrate the separator 7350b or the separator 7350a. In some embodiments, the resistance of the electrochemical cell 7300 and the components thereof can be tuned to control SEI formation with a desired speed and morphology. This control can be exercised by changing the external resistance to the interlayer 7360b and effecting direct contact between the interlayer 7360b and different hosts (e.g., carbon, metals) that alloy with lithium or polymers. In some embodiments, the electrochemical cell 7300 can include a SEI forming additive. In some embodiments, the SEI forming additives can be included in the electrolyte. In some embodiments, the SEI forming additive can include decomposition additives, such as a nitrate based salt (LiNO3, Mg(NO3)2, KNO3), and/or a sulfite based salt. In some embodiments, the SEI forming additives can include a fluorine-rich solvent or additive, such as fluorinated ether. In some embodiments, the SEI forming additive can include a carbonate, and/or an acetate. In some embodiments, the SEI forming additive can include a morphology-controlled additive such as cessium bistriflimide, and/or LiASF6. In some embodiments, the SEI forming additive can include fluoroethylene carbonate (FEC) and 2-fluoropyridine (2-FP). In some embodiments, the SEI forming additives can include vinylene carbonate (VC), dimethyl sulfate (DMS), poly(sulfur-random-1,3-diisopropenylbenzene) (PSD), N,N-dimethylethanolamine (DMEA), trimethylsilyl(fluorosulfonyl)(n-nonafluorobut-anesulfonyl)imide (TMS-FNFSI), tripropargyl phosphate (TPP), and/or tris (2, 2, 2-trifluoroethyl) borate (TTFEB). In some embodiments, the SEI forming additive can include organic salts (e.g., lithium bis(oxalato)borate (LiBOB), lithium difluoro(oxalate)borate (LiDFOB).
In some embodiments, the anode 7410 can include lithium metal. The interface between the SSE layer 7452 and a lithium metal anode delivers high coulombic efficiency without liquid electrolyte. Further, a dry interface (i.e., between a metal and a solid electrolyte layer) leads to good cycling and capacity retention. However, the dry interface alone does not necessarily stop lithium dendrite formation. Thus, the cathode 7430 includes a liquid electrolyte (i.e., a catholyte). In some embodiments, the cathode 7430 can include a semi-solid electrode. In some embodiments, the cathode 7430 can include a conventional solid electrode (i.e., with binder) with a liquid electrolyte. In some embodiments, the interlayer 7460 can include carbon and a solid-state electrolyte to act as a conductive layer. In some embodiments, the SSE layer 7452 can include sulfide. The combination of the SSE layer 7452 and the interlayer 7460 can prevent dendrites from forming. At the same time, liquid electrolyte can be prevented from entering the anode side of the electrochemical cell 7400 so the interface between the anode 7410 and the SSE layer 7452 remains dry. Also, this arrangement can prevent the liquid electrolyte from dissolving the SSE layer 7452 and the solid-state electrolyte in the interlayer 7460, particularly for sulfide-type solid-state electrolyte.
In production, carbon (e.g., activated carbon, hard carbon, soft carbon, Ketjen, carbon black, graphitic carbon, carbon fibers, carbon microfibers, VGCFs, fullerenic carbons, CNTs, MWNTs, SWNTs, graphene, graphene sheets or aggregates of graphene shetes, materials comprising fullerinic fragments, or any combination thereof), binder, are combined with a solid-state electrolyte to form the interlayer 7460. This creates a barrier with little or no porosity for preventing catholyte from migrating from the cathode 7430 to the anode 7410. This prevents dissolution of the SSE layer 7452. Alternatively, the separator 7450 can be coated with binder to produce the same effect. In some embodiments, the interlayer 7460 can have a porosity of less than about 5%, less than about 4%, less than about 3%, less than about 2%, less than about 1%, less than about 0.9%, less than about 0.8%, less than about 0.7%, less than about 0.6%, less than about 0.5%, less than about 0.4%, less than about 0.3%, less than about 0.2%, less than about 0.1%, or about 0%. In some embodiments, the separator 7450 can include a ceramic coating with a polymer.
As shown, the first separator 7550a and the interlayer 7560 extend beyond the outside edges of the second separator 7550b by an extension distance d. This allows for the interlayer 7560 to potentially contact the cathode 7530 if the cathode 7530 becomes misaligned from the anode 7510. This effectively blocks the cathode 7530 from contacting the anode 7510 and short circuiting. Rather, the cathode 7530 contacts the interlayer 7560 and short circuits. The extension of the interlayer 7560 acts as an edge detection point, and measuring the voltage between the cathode 7530 and the interlayer 7560 can detect such a short circuit (i.e., when the voltage difference is decreased to less than a threshold value). The electrochemical cell 7500 can subsequently be disabled in order to prevent a more catastrophic short circuit event.
In some embodiments, the extension distance d can be at least about 100 μm, at least about 200 μm, at least about 300 μm, at least about 400 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 1.1 mm, at least about 1.2 mm, at least about 1.3 mm, at least about 1.4 mm, at least about 1.5 mm, at least about 1.6 mm, at least about 1.7 mm, at least about 1.8 mm, or at least about 1.9 mm. In some embodiments, the extension distance d can be no more than about 2 mm, no more than about 1.9 mm, no more than about 1.8 mm, no more than about 1.7 mm, no more than about 1.6 mm, no more than about 1.5 mm, no more than about 1.4 mm, no more than about 1.3 mm, no more than about 1.2 mm, no more than about 1.1 mm, no more than about 1 mm, no more than about 900 μm, no more than about 800 μm, no more than about 700 μm, no more than about 600 μm, no more than about 500 μm, no more than about 400 μm, no more than about 300 μm, or no more than about 200 μm. Combinations of the above-referenced extension distances d are also possible (e.g., at least about 100 μm and no more than about 2 mm or at least about 300 μm and no more than about 1 mm), inclusive of all values and ranges therebetween. In some embodiments, the extension distance d can be about 100 μm, about 200 μm, about 300 μm, about 400 μm, about 500 μm, about 600 μm, about 700 μm, about 800 μm, about 900 μm, about 1 mm, about 1.1 mm, about 1.2 mm, about 1.3 mm, about 1.4 mm, about 1.5 mm, about 1.6 mm, about 1.7 mm, about 1.8 mm, about 1.9 mm, or about 2 mm.
As shown, the interlayer 7660a and the separator 7650b extend beyond the separator 7650a by an extension distance d1. As shown, the interlayer 7660b and the separator 7650c extend beyond the separator 7650d by an extension distance d2. In some embodiments, the extension distances d1 and/or d2 can be at least about 100 μm, at least about 200 μm, at least about 300 μm, at least about 400 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 1.1 mm, at least about 1.2 mm, at least about 1.3 mm, at least about 1.4 mm, at least about 1.5 mm, at least about 1.6 mm, at least about 1.7 mm, at least about 1.8 mm, or at least about 1.9 mm. In some embodiments, the extension distances d1 and/or d2 can be no more than about 2 mm, no more than about 1.9 mm, no more than about 1.8 mm, no more than about 1.7 mm, no more than about 1.6 mm, no more than about 1.5 mm, no more than about 1.4 mm, no more than about 1.3 mm, no more than about 1.2 mm, no more than about 1.1 mm, no more than about 1 mm, no more than about 900 μm, no more than about 800 μm, no more than about 700 μm, no more than about 600 μm, no more than about 500 μm, no more than about 400 μm, no more than about 300 μm, or no more than about 200 μm. Combinations of the above-referenced extension distances d1 and/or d2 are also possible (e.g., at least about 100 μm and no more than about 2 mm or at least about 300 μm and no more than about 1 mm), inclusive of all values and ranges therebetween. In some embodiments, the extension distances d1 and/or d2 can be about 100 μm, about 200 μm, about 300 μm, about 400 μm, about 500 μm, about 600 μm, about 700 μm, about 800 μm, about 900 μm, about 1 mm, about 1.1 mm, about 1.2 mm, about 1.3 mm, about 1.4 mm, about 1.5 mm, about 1.6 mm, about 1.7 mm, about 1.8 mm, about 1.9 mm, or about 2 mm.
As shown, the interlayer 7760b extends beyond the separator 7750c by an extension distance d. In some embodiments, the extension distance d can be at least about 100 μm, at least about 200 μm, at least about 300 μm, at least about 400 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 1.1 mm, at least about 1.2 mm, at least about 1.3 mm, at least about 1.4 mm, at least about 1.5 mm, at least about 1.6 mm, at least about 1.7 mm, at least about 1.8 mm, or at least about 1.9 mm. In some embodiments, the extension distance d can be no more than about 2 mm, no more than about 1.9 mm, no more than about 1.8 mm, no more than about 1.7 mm, no more than about 1.6 mm, no more than about 1.5 mm, no more than about 1.4 mm, no more than about 1.3 mm, no more than about 1.2 mm, no more than about 1.1 mm, no more than about 1 mm, no more than about 900 μm, no more than about 800 μm, no more than about 700 μm, no more than about 600 μm, no more than about 500 μm, no more than about 400 μm, no more than about 300 μm, or no more than about 200 μm. Combinations of the above-referenced extension distances d are also possible (e.g., at least about 100 μm and no more than about 2 mm or at least about 300 μm and no more than about 1 mm), inclusive of all values and ranges therebetween. In some embodiments, the extension distance d can be about 100 μm, about 200 μm, about 300 μm, about 400 μm, about 500 μm, about 600 μm, about 700 μm, about 800 μm, about 900 μm, about 1 mm, about 1.1 mm, about 1.2 mm, about 1.3 mm, about 1.4 mm, about 1.5 mm, about 1.6 mm, about 1.7 mm, about 1.8 mm, about 1.9 mm, or about 2 mm.
In
As shown, the interlayer 7860a and the separator 7850a extend beyond the separator 7850b by an extension distance d1. As shown, the interlayer 7860b and the separator 7850b extend beyond the separator 7850c by an extension distance d2. In some embodiments, the extension distances d1 and/or d2 can be at least about 100 μm, at least about 200 μm, at least about 300 μm, at least about 400 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 1.1 mm, at least about 1.2 mm, at least about 1.3 mm, at least about 1.4 mm, at least about 1.5 mm, at least about 1.6 mm, at least about 1.7 mm, at least about 1.8 mm, or at least about 1.9 mm. In some embodiments, the extension distances d1 and/or d2 can be no more than about 2 mm, no more than about 1.9 mm, no more than about 1.8 mm, no more than about 1.7 mm, no more than about 1.6 mm, no more than about 1.5 mm, no more than about 1.4 mm, no more than about 1.3 mm, no more than about 1.2 mm, no more than about 1.1 mm, no more than about 1 mm, no more than about 900 μm, no more than about 800 μm, no more than about 700 μm, no more than about 600 μm, no more than about 500 μm, no more than about 400 μm, no more than about 300 μm, or no more than about 200 μm. Combinations of the above-referenced extension distances d1 and/or d2 are also possible (e.g., at least about 100 μm and no more than about 2 mm or at least about 300 μm and no more than about 1 mm), inclusive of all values and ranges therebetween. In some embodiments, the extension distances d1 and/or d2 can be about 100 μm, about 200 μm, about 300 μm, about 400 μm, about 500 μm, about 600 μm, about 700 μm, about 800 μm, about 900 μm, about 1 mm, about 1.1 mm, about 1.2 mm, about 1.3 mm, about 1.4 mm, about 1.5 mm, about 1.6 mm, about 1.7 mm, about 1.8 mm, about 1.9 mm, or about 2 mm.
In
The distance db is larger than the distance da. This allows for an exposed region of the interlayer 7960 to act as a tab, such that a voltage measurement can be made from the exposed region of the interlayer 7960 without including a tab. As shown, the interlayer has an exposed interlayer length eil.
In some embodiments, the distance da can be at least about 100 μm, at least about 200 μm, at least about 300 μm, at least about 400 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 2 mm, at least about 3 mm, at least about 4 mm, at least about 5 mm, at least about 6 mm, at least about 7 mm, at least about 8 mm, or at least about 9 mm. In some embodiments, the distance da can be no more than about 1 cm, no more than about 9 mm, no more than about 8 mm, no more than about 7 mm, no more than about 6 mm, no more than about 5 mm, no more than about 4 mm, no more than about 3 mm, no more than about 2 mm, no more than about 1 mm, no more than about 900 μm, no more than about 800 μm, no more than about 700 μm, no more than about 600 μm, no more than about 500 μm, no more than about 400 μm, no more than about 300 μm, or no more than about 200 μm. Combinations of the above-referenced distances da are also possible (e.g., at least about 100 μm and no more than about 1 cm or at least about 500 μm and no more than about 5 mm), inclusive of all values and ranges therebetween. In some embodiments, the distance da can be about 100 μm, about 200 μm, about 300 μm, about 400 μm, about 500 μm, about 600 μm, about 700 μm, about 800 μm, about 900 μm, about 1 mm, about 2 mm, about 3 mm, about 4 mm, about 5 mm, about 6 mm, about 7 mm, about 8 mm, about 9 mm, or about 1 cm.
In some embodiments, the distance dc can be at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 2 mm, at least about 3 mm, at least about 4 mm, at least about 5 mm, at least about 6 mm, at least about 7 mm, at least about 8 mm, at least about 9 mm, at least about 1 cm, at least about 2 cm, at least about 3 cm, or at least about 4 cm. In some embodiments, the distance dc can be no more than about 5 cm, no more than about 4 cm, no more than about 3 cm, no more than about 2 cm, no more than about 1 cm, no more than about 9 mm, no more than about 8 mm, no more than about 7 mm, no more than about 6 mm, no more than about 5 mm, no more than about 4 mm, no more than about 3 mm, no more than about 2 mm, no more than about 1 mm, no more than about 900 μm, no more than about 800 μm, no more than about 700 μm, or no more than about 600 μm. Combinations of the above-referenced distances dc are also possible (e.g., at least about 500 μm and no more than about 5 cm or at least about 5 mm and no more than about 3 cm), inclusive of all values and ranges therebetween. In some embodiments, the distance dc can be about 500 μm, about 600 μm, about 700 μm, about 800 μm, about 900 μm, about 1 mm, about 2 mm, about 3 mm, about 4 mm, about 5 mm, about 6 mm, about 7 mm, about 8 mm, about 9 mm, about 1 cm, about 2 cm, about 3 cm, about 4 cm, or about 5 cm.
In some embodiments, the exposed interlayer length eil can be at least about 100 μm, at least about 200 μm, at least about 300 μm, at least about 400 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 2 mm, at least about 3 mm, at least about 4 mm, at least about 5 mm, at least about 6 mm, at least about 7 mm, at least about 8 mm, at least about 9 mm, at least about 1 cm, at least about 2 cm, or at least about 3 cm. In some embodiments, the exposed interlayer length eil can be no more than about 4 cm, no more than about 3 cm, no more than about 2 cm, no more than about 1 cm, no more than about 9 mm, no more than about 8 mm, no more than about 7 mm, no more than about 6 mm, no more than about 5 mm, no more than about 4 mm, no more than about 3 mm, no more than about 2 mm, no more than about 1 mm, no more than about 900 μm, no more than about 800 μm, no more than about 700 μm, no more than about 600 μm, no more than about 500 μm, no more than about 400 μm, no more than about 300 μm, or no more than about 200 μm.
Combinations of the above-referenced exposed interlayer lengths eil are also possible (e.g., at least about 100 μm and no more than about 4 cm or at least about 1 mm and no more than about 1 cm), inclusive of all values and ranges therebetween. In some embodiments, the exposed interlayer length eil can be about 100 μm, about 200 μm, about 300 μm, about 400 μm, about 500 μm, about 600 μm, about 700 μm, about 800 μm, about 900 μm, about 1 mm, about 2 mm, about 3 mm, about 4 mm, about 5 mm, about 6 mm, about 7 mm, about 8 mm, about 9 mm, about 1 cm, about 2 cm, about 3 cm, or about 4 cm.
As shown in
In some embodiments, the thin film resistor 80635 can have a resistance of at least about 1Ω, at least about 2Ω, at least about 3Ω, at least about 4Ω, at least about 5Ω, at least about 6Ω, at least about 7Ω, at least about 8Ω, at least about 9Ω, at least about 10Ω, at least about 20Ω, at least about 30Ω, at least about 40Ω, at least about 50Ω, at least about 60Ω, at least about 70Ω, at least about 80Ω, at least about 90Ω, at least about 100Ω, at least about 200Ω, at least about 300Ω, at least about 400Ω, at least about 500Ω, at least about 600Ω, at least about 700Ω, at least about 800Ω, or at least about 900Ω. In some embodiments, the thin film resistor 80635 can have a resistance of no more than about 1,000Ω, no more than about 900Ω, no more than about 800Ω, no more than about 700Ω, no more than about 600Ω, no more than about 500Ω, no more than about 400Ω, no more than about 300Ω, no more than about 200Ω, no more than about 100Ω, no more than about 90Ω, no more than about 80Ω, no more than about 70Ω, no more than about 60Ω, no more than about 50Ω, no more than about 40Ω, no more than about 30Ω, no more than about 20Ω, no more than about 10Ω, no more than about 9Ω, no more than about 8Ω, no more than about 7Ω, no more than about 6Ω, no more than about 5Ω, no more than about 4Ω, no more than about 3Ω, or no more than about 2Ω. Combinations of the above-referenced resistances are also possible (e.g., at least about 1Ω and no more than about 1,000Ω or at least about 5Ω and no more than about 500Ω), inclusive of all values and ranges therebetween. In some embodiments, the thin film resistor 80635 can have a resistance of about 1Ω, about 2Ω, about 3Ω, about 4Ω, about 5Ω, about 6Ω, about 7Ω, about 8Ω, about 9Ω, about 10Ω, about 20Ω, about 30Ω, about 40Ω, about 50Ω, about 60Ω, about 70Ω, about 80Ω, about 90Ω, about 100Ω, about 200Ω, about 300Ω, about 400Ω, about 500Ω, about 600Ω, about 700Ω, about 800Ω, about 900Ω, or about 1,000Ω.
In some embodiments, the interlayer tabs 8163a, 8163b, 8163c (collectively referred to as interlayer tabs 8163) can be composed of aluminum (e.g., when electrically coupled to cathode tabs 8142). In some embodiments, the interlayer tabs 8163 can be composed of copper and/or nickel (e.g., when electrically coupled to anode tabs 8122). In some embodiments, the anode current collectors (not shown) can be coated on a single side. In some embodiments, the anode current collectors can be coated on both sides. In some embodiments, the cathode current collectors (not shown can be coated on a single side. In some embodiments, the cathode current collectors can be coated on both sides. As shown, the collection of electrochemical cell stacks 81000a, 81000b, 81000c includes 3 cells arranged in parallel, with each parallel arrangement connected in series. In some embodiments, any number of electrochemical cells can be connected in series and/or parallel (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, inclusive of all values and ranges therebetween).
In some embodiments, the interlayer tabs 8263a, 8263b, 8263c (collectively referred to as interlayer tabs 8263) can be composed of aluminum (e.g., when electrically coupled to cathode tabs 8242). In some embodiments, the interlayer tabs 8263 can be composed of copper and/or nickel (e.g., when electrically coupled to anode tabs 8222). In some embodiments, the anode current collectors (not shown) can be coated on a single side. In some embodiments, the anode current collectors can be coated on both sides. In some embodiments, the cathode current collectors (not shown can be coated on a single side. In some embodiments, the cathode current collectors can be coated on both sides. As shown, the collection of electrochemical cell stacks 82000a, 82000b, 82000c includes 3 cells arranged in parallel, with each parallel arrangement connected in series. In some embodiments, any number of electrochemical cells can be connected in series and/or parallel (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, inclusive of all values and ranges therebetween).
As shown, the electrochemical cell stack 83000a includes anode tabs 8322a-i, 8322a-ii, 8322a-iii (collectively referred to as anode tabs 8322a), cathode tabs 8342a-i, 8342a-ii, 8342a-iii (collectively referred to as cathode tabs 8242a), interlayer tabs 8363a-i, 8363a-ii, 8363a-iii (collectively referred to as interlayer tabs 8363a), and casing 83480a, disposed in a pre-assembled socket 83005a. As shown, the electrochemical cell stack 83000b includes anode tabs 8322b-i, 8322b-ii, 8322b-iii, (collectively referred to as anode tabs 8322b), cathode tabs 8342b-i, 8342b-ii, 8342b-iii (collectively referred to as cathode tabs 8342b), interlayer tabs 8363b-i, 8363b-ii, 8363b-iii (collectively referred to as interlayer tabs 8363b), and casing 83480b, disposed in a pre-assembled socket 83005b.
In some embodiments, the interlayer tabs 8363a, 8363b (collectively referred to as interlayer tabs 8363) can be composed of aluminum (e.g., when electrically coupled to cathode tabs 8342). In some embodiments, the interlayer tabs 8363 can be composed of copper and/or nickel (e.g., when electrically coupled to anode tabs 8322). In some embodiments, the anode current collectors (not shown) can be coated on a single side. In some embodiments, the anode current collectors can be coated on both sides. In some embodiments, the cathode current collectors (not shown can be coated on a single side. In some embodiments, the cathode current collectors can be coated on both sides. As shown, the collection of electrochemical cell stacks 83000a, 83000b includes 3 cells arranged in parallel, with each parallel arrangement connected in series. In some embodiments, any number of electrochemical cells can be connected in series and/or parallel (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, inclusive of all values and ranges therebetween).
In some embodiments, the interlayer tab 8463 can be bonded to the pouch film 8470a. In some embodiments, the interlayer 8450 can be bonded to the pouch film 8470b. A long adhesion length between the interlayer tab 8463 and the pouch film 8470a can provide a strong adhesive bond between the interlayer tab 8463 and the pouch film 8470a. In other words, a large sealing area provides high structural integrity.
In some embodiments, the separators 8550a, 8550b (collectively referred to as separators 8550) can be wetted before or after application of the separators 8550 (e.g., as described above with respect to wettability regarding
In some embodiments, the first coating layer 8552a and/or the second coating layer 8552b can include alumina, PVDF, boehmite, polyimide, cellulose, cellulosic materials, methyl cellulose, ethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, hydroxyethyl methyl cellulose, hydroxypropyl methyl cellulose, ethyl hydroxyethyl cellulose, carboxymethyl cellulose, or any combination thereof. In some embodiments, the first coating 8552a and/or the second coating 8552b can have a thickness of at least about 1 μm, at least about 1.5 μm, at least about 2 μm, at least about 2.5 μm, at least about 3 μm, at least about 3.5 μm, at least about 4 μm, or at least about 4.5 μm. In some embodiments, the first coating 8552a and/or the second coating 8552b can have a thickness of no more than about 5 μm, no more than about 4.5 μm, no more than about 4 μm, no more than about 3.5 μm, no more than about 3 μm, no more than about 2.5 μm, no more than about 2 μm, or no more than about 1.5 μm. Combinations of the above-referenced thicknesses are also possible (e.g., at least about 1 μm and no more than about 5 μm or at least about 2 μm and no more than about 4 μm), inclusive of all values and ranges therebetween. In some embodiments, the first coating 8552a and/or the second coating 8552b can have a thickness of about 1 μm, about 1.5 μm, about 2 μm, about 2.5 μm, about 3 μm, about 3.5 μm, about 4 μm, about 4.5 μm, or about 5 μm.
After the electrochemical cell 8500 has been formed, the conductivity of the separators 8550 can be measured to confirm that micropores have not formed. In some embodiments, this determination can be conducted via a resistance measurement. In some embodiments, the resistance across the combination of the first separator 8550a, the interlayer 8560, and the second separator 8550b (including the first coating layer 8552a and/or the second coating layer 8552b) can be at least about 500 kΩ, at least about 600 kΩ, at least about 700 kΩ, at least about 800 kΩ, at least about 900 kΩ, at least about 1 MΩ, at least about 1.1 MΩ, at least about 1.2 MΩ, at least about 1.3 MΩ, at least about 1.4 MΩ, at least about 1.5 MΩ, at least about 1.6 MΩ, at least about 1.7 MΩ, at least about 1.8 MΩ, at least about 1.9 MΩ, at least about 2 MΩ, at least about 2.5 MΩ, at least about 3 MΩ, at least about 3.5 MΩ, at least about 4 MΩ, at least about 4.5 MΩ, or at least about 5 MΩ.
The metal coating layer 8670 can be coated onto the separator 8650b (or the separator 8650a) before the interlayer 8660 is applied. The metal coating layer 8670 can prevent the risk of local zero-voltage at the interlayer 8660, as the pinhole 8671 can prevent such occurrences. In some embodiments, the metal coating layer 8670 can have a thickness of at least about 10 μm, at least about 20 μm, at least about 30 μm, at least about 40 μm, at least about 50 μm, at least about 60 μm, at least about 70 μm, at least about 80 μm, at least about 90 μm, at least about 100 μm, at least about 200 μm, at least about 300 μm, at least about 400 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 1.5 mm, at least about 2 mm, at least about 2.5 mm, at least about 3 mm, at least about 3.5 mm, at least about 4 mm, or at least about 4.5 mm. In some embodiments, the metal coating layer 8670 can have a thickness of no more than about 5 mm, no more than about 4.5 mm, no more than about 4 mm, no more than about 3.5 mm, no more than about 3 mm, no more than about 2.5 mm, no more than about 2 mm, no more than about 1.5 mm, no more than about 1 mm, no more than about 900 μm, no more than about 800 μm, no more than about 700 μm, no more than about 600 μm, no more than about 500 μm, no more than about 400 μm, no more than about 300 μm, no more than about 200 μm, no more than about 100 μm, no more than about 90 μm, no more than about 80 μm, no more than about 70 μm, no more than about 60 μm, no more than about 50 μm, no more than about 40 μm, no more than about 30 μm, or no more than about 20 μm. Combinations of the above-referenced thicknesses are also possible (e.g., at least about 10 μm and no more than about 5 mm or at least about 100 μm and no more than about 600 μm), inclusive of all values and ranges therebetween. In some embodiments, the metal coating layer 8670 can have a thickness of about 10 μm, about 20 μm, about 30 μm, about 40 μm, about 50 μm, about 60 μm, about 70 μm, about 80 μm, about 90 μm, about 100 μm, about 200 μm, about 300 μm, about 400 μm, about 500 μm, about 600 μm, about 700 μm, about 800 μm, about 900 μm, about 1 mm, about 1.5 mm, about 2 mm, about 2.5 mm, about 3 mm, about 3.5 mm, about 4 mm, about 4.5 mm, or about 5 mm.
In some embodiments, the pinhole 8671 can have a width of at least about 10 μm, at least about 20 μm, at least about 30 μm, at least about 40 μm, at least about 50 μm, at least about 60 μm, at least about 70 μm, at least about 80 μm, at least about 90 μm, at least about 100 μm, at least about 200 μm, at least about 300 μm, at least about 400 μm, at least about 500 μm, at least about 600 μm, at least about 700 μm, at least about 800 μm, at least about 900 μm, at least about 1 mm, at least about 1.5 mm, at least about 2 mm, at least about 2.5 mm, at least about 3 mm, at least about 3.5 mm, at least about 4 mm, or at least about 4.5 mm. In some embodiments, the pinhole 8671 can have a width of no more than about 5 mm, no more than about 4.5 mm, no more than about 4 mm, no more than about 3.5 mm, no more than about 3 mm, no more than about 2.5 mm, no more than about 2 mm, no more than about 1.5 mm, no more than about 1 mm, no more than about 900 μm, no more than about 800 μm, no more than about 700 μm, no more than about 600 μm, no more than about 500 μm, no more than about 400 μm, no more than about 300 μm, no more than about 200 μm, no more than about 100 μm, no more than about 90 μm, no more than about 80 μm, no more than about 70 μm, no more than about 60 μm, no more than about 50 μm, no more than about 40 μm, no more than about 30 μm, or no more than about 20 μm.
Combinations of the above-referenced thicknesses are also possible (e.g., at least about 10 μm and no more than about 5 mm or at least about 100 μm and no more than about 600 μm), inclusive of all values and ranges therebetween. In some embodiments, the pinhole 8671 can have a thickness of about 10 μm, about 20 μm, about 30 μm, about 40 μm, about 50 μm, about 60 μm, about 70 μm, about 80 μm, about 90 μm, about 100 μm, about 200 μm, about 300 μm, about 400 μm, about 500 μm, about 600 μm, about 700 μm, about 800 μm, about 900 μm, about 1 mm, about 1.5 mm, about 2 mm, about 2.5 mm, about 3 mm, about 3.5 mm, about 4 mm, about 4.5 mm, or about 5 mm.
Various concepts may be embodied as one or more methods, of which at least one example has been provided. The acts performed as part of the method may be ordered in any suitable way. Accordingly, embodiments may be constructed in which acts are performed in an order different than illustrated, which may include performing some acts simultaneously, even though shown as sequential acts in illustrative embodiments. Put differently, it is to be understood that such features may not necessarily be limited to a particular order of execution, but rather, any number of threads, processes, services, servers, and/or the like that may execute serially, asynchronously, concurrently, in parallel, simultaneously, synchronously, and/or the like in a manner consistent with the disclosure. As such, some of these features may be mutually contradictory, in that they cannot be simultaneously present in a single embodiment. Similarly, some features are applicable to one aspect of the innovations, and inapplicable to others.
In addition, the disclosure may include other innovations not presently described. Applicant reserves all rights in such innovations, including the right to embodiment such innovations, file additional applications, continuations, continuations-in-part, divisionals, and/or the like thereof. As such, it should be understood that advantages, embodiments, examples, functional, features, logical, operational, organizational, structural, topological, and/or other aspects of the disclosure are not to be considered limitations on the disclosure as defined by the embodiments or limitations on equivalents to the embodiments. Depending on the particular desires and/or characteristics of an individual and/or enterprise user, database configuration and/or relational model, data type, data transmission and/or network framework, syntax structure, and/or the like, various embodiments of the technology disclosed herein may be implemented in a manner that enables a great deal of flexibility and customization as described herein.
All definitions, as defined and used herein, should be understood to control over dictionary definitions, definitions in documents incorporated by reference, and/or ordinary meanings of the defined terms.
As used herein, in particular embodiments, the terms “about” or “approximately” when preceding a numerical value indicates the value plus or minus a range of 10%. Where a range of values is provided, it is understood that each intervening value, to the tenth of the unit of the lower limit unless the context clearly dictates otherwise, between the upper and lower limit of that range and any other stated or intervening value in that stated range is encompassed within the disclosure. That the upper and lower limits of these smaller ranges can independently be included in the smaller ranges is also encompassed within the disclosure, subject to any specifically excluded limit in the stated range. Where the stated range includes one or both of the limits, ranges excluding either or both of those included limits are also included in the disclosure.
The phrase “and/or,” as used herein in the specification and in the embodiments, should be understood to mean “either or both” of the elements so conjoined, i.e., elements that are conjunctively present in some cases and disjunctively present in other cases. Multiple elements listed with “and/or” should be construed in the same fashion, i.e., “one or more” of the elements so conjoined. Other elements may optionally be present other than the elements specifically identified by the “and/or” clause, whether related or unrelated to those elements specifically identified. Thus, as a non-limiting example, a reference to “A and/or B”, when used in conjunction with open-ended language such as “comprising” can refer, in one embodiment, to A only (optionally including elements other than B); in another embodiment, to B only (optionally including elements other than A); in yet another embodiment, to both A and B (optionally including other elements); etc.
As used herein in the specification and in the embodiments, “or” should be understood to have the same meaning as “and/or” as defined above. For example, when separating items in a list, “or” or “and/or” shall be interpreted as being inclusive, i.e., the inclusion of at least one, but also including more than one, of a number or list of elements, and, optionally, additional unlisted items. Only terms clearly indicated to the contrary, such as “only one of” or “exactly one of,” or, when used in the embodiments, “consisting of,” will refer to the inclusion of exactly one element of a number or list of elements. In general, the term “or” as used herein shall only be interpreted as indicating exclusive alternatives (i.e., “one or the other but not both”) when preceded by terms of exclusivity, such as “either,” “one of,” “only one of,” or “exactly one of.” “Consisting essentially of,” when used in the embodiments, shall have its ordinary meaning as used in the field of patent law.
As used herein in the specification and in the embodiments, the phrase “at least one,” in reference to a list of one or more elements, should be understood to mean at least one element selected from any one or more of the elements in the list of elements, but not necessarily including at least one of each and every element specifically listed within the list of elements and not excluding any combinations of elements in the list of elements. This definition also allows that elements may optionally be present other than the elements specifically identified within the list of elements to which the phrase “at least one” refers, whether related or unrelated to those elements specifically identified. Thus, as a non-limiting example, “at least one of A and B” (or, equivalently, “at least one of A or B,” or, equivalently “at least one of A and/or B”) can refer, in one embodiment, to at least one, optionally including more than one, A, with no B present (and optionally including elements other than B); in another embodiment, to at least one, optionally including more than one, B, with no A present (and optionally including elements other than A); in yet another embodiment, to at least one, optionally including more than one, A, and at least one, optionally including more than one, B (and optionally including other elements); etc.
In the embodiments, as well as in the specification above, all transitional phrases such as “comprising,” “including,” “carrying,” “having,” “containing,” “involving,” “holding,” “composed of,” and the like are to be understood to be open-ended, i.e., to mean including but not limited to. Only the transitional phrases “consisting of” and “consisting essentially of” shall be closed or semi-closed transitional phrases, respectively, as set forth in the United States Patent Office Manual of Patent Examining Procedures, Section 2111.03.
While specific embodiments of the present disclosure have been outlined above, many alternatives, modifications, and variations will be apparent to those skilled in the art. Accordingly, the embodiments set forth herein are intended to be illustrative, not limiting. Various changes may be made without departing from the spirit and scope of the disclosure. Where methods and steps described above indicate certain events occurring in a certain order, those of ordinary skill in the art having the benefit of this disclosure would recognize that the ordering of certain steps may be modified and such modification are in accordance with the variations of the invention. Additionally, certain of the steps may be performed concurrently in a parallel process when possible, as well as performed sequentially as described above. The embodiments have been particularly shown and described, but it will be understood that various changes in form and details may be made.
This application claims priority to and the benefit of U.S. Provisional Patent Application No. 63/433,269, filed Dec. 16, 2022 and titled, “Systems and Methods for Minimizing and Preventing Dendrite Formation in Electrochemical Cells,” U.S. Provisional Patent Application No. 63/450,208, filed Mar. 6, 2023 and titled, “Systems and Methods for Minimizing and Preventing Dendrite Formation in Electrochemical Cells,” U.S. Provisional Patent Application No. 63/461,506, filed Apr. 24, 2023 and titled, “Systems and Methods for Minimizing and Preventing Dendrite Formation in Electrochemical Cells,” U.S. Provisional Patent Application No. 63/470,679, filed Jun. 2, 2023 and titled, “Systems and Methods for Minimizing and Preventing Dendrite Formation in Electrochemical Cells,” U.S. Provisional Patent Application No. 63/528,213, filed Jul. 21, 2023 and titled, “Systems and Methods for Minimizing and Preventing Dendrite Formation in Electrochemical Cells,” and U.S. Provisional Patent Application No. 63/546,980, filed Nov. 2, 2023 and titled, “Systems and Methods for Minimizing and Preventing Dendrite Formation in Electrochemical Cells,” the disclosures of which are hereby incorporated by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 63546980 | Nov 2023 | US | |
| 63528213 | Jul 2023 | US | |
| 63470679 | Jun 2023 | US | |
| 63461506 | Apr 2023 | US | |
| 63450208 | Mar 2023 | US | |
| 63433269 | Dec 2022 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 18543959 | Dec 2023 | US |
| Child | 18810183 | US |