Systems and methods for tissue sterilization

Abstract

Systems and methods for sterilization of tissue are provided.

Description

The present disclosure relates to the field of tissue sterilization.

Present methods for sterilization of tissues include gamma-irradiation, e-beam, and ethylene oxide (EO). Among them, gamma-irradiation and e-beam are known to alter the structure and characteristics of biomaterials through crosslinking and/or degradation of collagen matrix. EO sterilization typically operates at temperatures around 60° C., which is above the melting temperature of the collagen matrix in biological materials, such as, for example, dermal tissues. EO is also a recognized carcinogen, and its residual in biological materials can cause hemolysis and other toxic reactions. Further, gamma-irradiation and e-beam can eliminate or significantly reduce osteoinductivity of demineralized bone matrix.

Accordingly, there is a need for improved systems and methods for sterilization of tissues, including acellular tissue matrices.

This discussion of the background disclosure is included to place the present disclosure in context. It is not an admission that any of the background material previously described was published, known, or part of the common general knowledge at the priority date of the present disclosure and claims.

According to certain embodiments, a method of terminal sterilization is disclosed that includes treating a demineralized bone matrix in a supercritical carbon dioxide (SC—CO₂) chamber with a sterilant, wherein the demineralized bone matrix is osteoinductive after sterilization and storage for at least 12 months at ambient conditions.

According to certain embodiments, a dimineralized bone matrix is provided, wherein the demineralized bone matrix is produced by a method comprising treating the demienralized bone matrix with super critical CO₂ and a sterilant to sterilize the demineralized bone matrix, wherein the demineralized bone matrix is osteoinductive after sterilization and storage at ambient temperatures for at least 12 months.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a phase diagram of CO₂.

FIG. 2 is a diagram of process pressure vs. time flow, for a sterilization process, according to certain embodiments.

FIG. 3 is a log-kill plot of model resistant bioburden, according to certain embodiments.

FIG. 4 is a photomicrograph of demineralized bone matrix after sterilization and storage for 6 months under ambient conditions, followed by intramuscular implantation within a rat, according to certain embodiments.

FIG. 5 is a photomicrograph of demineralized bone matrix after sterilization and storage for 6 months under ambient conditions, followed by intramuscular implantation within a rat, according to certain embodiments.

FIG. 6 is a photomicrograph of demineralized bone matrix after sterilization and storage for 12 months under ambient conditions, followed by intramuscular implantation within a rat, according to certain embodiments.

FIG. 7 is a photomicrograph of demineralized bone matrix after sterilization and storage for 12 months under ambient conditions, followed by intramuscular implantation within a rat, according to certain embodiments.

DESCRIPTION OF EXEMPLARY EMBODIMENTS

In this application, the use of the singular includes the plural unless specifically stated otherwise. In this application, the use of “or” means “and/or” unless stated otherwise. Furthermore, the use of the term “including,” as well as other forms, such as “includes” and “included,” is not limiting. Also, terms such as “element” or “component” encompass both elements and components comprising one unit and elements and components that comprise more than one subunit, unless specifically stated otherwise. Also, the use of the term “portion” may include part of a moiety or the entire moiety.

All documents, or portions of documents, cited in this application, including but not limited to patents, patent applications, articles, books, and treatises, are hereby expressly incorporated by reference in their entirety for any purpose.

The term “sterilization,” as used herein, generally refers to the inactivation or elimination of viable microorganisms.

The term “bioburden,” as used herein, generally refers to the number of contaminating microbes on a certain amount of material.

The term “tissue” will be understood to refer to intact tissue or components of tissues, including acellular tissue matrices.

The term “ambient conditions” will be understood to refer to temperatures ranging from 20−30° C. and conditions that are basically dry.

The present disclosure relates to systems and methods for sterilization of tissues. Some exemplary embodiments relate to sterilization using supercritical carbon dioxide (SC—CO₂). Supercritical carbon dioxide sterilization involves the use of SC—CO₂, alone or with the addition of one or more sterilants, for bioburden reduction. Supercritical carbon dioxide has unique properties that make it an appealing medium for sterilization. Its high diffusion characteristics allow for deep penetration into materials. In addition, it is nontoxic and can easily be removed by depressurization and out-gassing. Further, SC—CO₂ can be effective at inactivating a variety of microorganisms.

In some exemplary embodiments, SC—CO₂ may be used to sterilize bone or bone components. In certain embodiments, the bone or bone components include demineralized bone (DBM). In certain embodiments, the DBM is osteoinductive after sterilization. In certain embodiments, the DBM is stored in dry form to maintain osteoinductivity. In some embodiments, the DBM is dried before or after sterilization. Further, in certain embodiments, the DBM may be combined with one or more other materials, such as particulate or fibrous acellular soft tissues, including dermis. One such acellular soft tissue is CYMETRA®, which is a particulate acellular dermal material. Further, the DBM may be sterilized alone or when mixed with other materials. Particulate acellular tissues, DBM, combinations of DBM and other materials, and methods for freeze-drying and storing such materials are further described in U.S. Pat. No. 6,933,326 and US Patent Publication Numbers 2007/0248575 and 2003/0143207.

In some embodiments, the DBM, acellular tissue matrix, or combination thereof may be treated with SC—CO₂ and at least one sterilant, which can further enhance the inactivation of microbes. Such sterilants may include, for example, peracetic acid (PAA), which can be bactericidal, fungicidal, virucidal, and sporicidal. Use of a sterilant in conjunction with SC—CO₂, in various embodiments disclosed herein, may facilitate achieving industrial level sterilization with a Sterility Assurance Level of 10⁻⁶ (i.e., a probability of 1 in 1,000,000 of finding a non-sterile device). In some embodiments, combining SC—CO₂ with a sterilant may facilitate achieving industrial sterilization of DBM or DBM in combination with other materials without affecting the osteoinductivity of the DBM.

The DBM products discussed herein can be packaged in a variety of ways. For example, the products can be packaged using systems that permit sterilization using SC—CO₂ and a sterilant, but prevent contamination of samples after sterilization. In some embodiments, the products are sterilized and packaged using a packaging system having multiple components. For example, a suitable system can include an outer package having a first portion that is permeable to SC—CO₂ and a sterilant. The first portion can also be impermeable to bacteria and therefore will function as a sterile barrier. The outer package can also include a second portion that is impermeable to moisture. The second portion can be used to seal the package within a moisture tight enclosure subsequent to sterilization without transferring the device to a separate container. In some cases, the packaging will also include an inner package, which will be permeable to SC—CO₂ and a sterilant, and may comprise, for example, TYVEK®.

Exemplary Sterilization Process

In certain embodiments, super-critical carbon dioxide (SC—CO₂) can serve as an inert carrier for the delivery of sterilants. In some embodiments, the sterilants can include, peracetic acid (PAA) and/or hydrogen peroxide (H₂O₂). SC—CO₂ exhibits properties of both the gaseous and liquid physical states. It has the viscosity of a liquid and the transport efficiency of a gas which allow for efficient delivery with high penetration properties.

FIG. 1 displays the phase diagram for the conversion of CO₂ to the super-critical state. The super-critical state is a unique physical state that is achieved at a specific temperature and pressure combination defined as the “critical point”. The super-critical state is absolute once the critical point is reached within the environment and the pressure and temperature are uniform throughout a super-critical environment.

In certain embodiments, during the sterilization process, the CO₂ is pumped into the chamber, and the pressure and temperature are modulated until the critical point is surpassed, yielding the super-critical state within the chamber. The pressure and temperature are monitored to maintain the required super-critical state pressure/temperature values for the duration of the processing run. If either the pressure or temperature range falls out of the required metric, the run is registered as a failure. The real-time measurements of the temperature and pressure values are recorded and can be produced as a hard-copy printout.

FIG. 2 is a diagram of process pressure vs. time flow, according to certain embodiments. During the treatment process, an instrument provides heat to a treatment chamber to maintain a constant temperature of ˜35° C., while the pressure is increased to above the critical point. Once the preset super-critical state (P=1346 psi, T=35° C.) is achieved, the sterilization time is initiated. In various embodiments, during the validated sterilization process, under super-critical conditions, both the pressure and temperature are constant. In some embodiments, the only variable for the sterilization process is the exposure time.

As FIG. 2 illustrates, there is a pre-sterilization time frame while the critical pressure is achieved. After that time, the pressure and temperature are held constant at values within the super-critical phase requirements. The sterilization time is then initiated, and the required exposure time is executed (t_sc). Following the completion of the sterilization exposure phase, the chamber pressure is reversed to allow retrieval of the sterile samples. The complete process of achieving the super-critical phase and its reversal are represented by the total process time (t_total).

Sterilant Components

The sterilant component of the sterilization system consists of a stock solution that contains PAA and H₂O₂ (Sigma Cat No #269336) that is diluted with sterile distilled water at the time of use. In some embodiments, the PAA and H₂O₂ in the sterilant have concentrations of 12%±2.0% and 2.0%±1.0% w/v, respectively. The working concentrations of PAA and H₂O₂ inside the sterilization chamber are about 54 ppm and 9 ppm, respectively. PAA and H₂O₂ working concentration ranges inside the chamber can be 1-1000 ppm and 1-1000 ppm, respectively. The preferred ranges are 20-100 ppm and 1-20 ppm.

At the onset of the sterilization process, the sterilant is placed into the SC—CO₂ chamber. The presence of PAA/H₂O₂ throughout the chamber can be confirmed by PAA and H₂O₂ test strips placed at different locations of the chamber during the IQ/OQ validation of the equipment. In various embodiments, the process can achieve SAL=10⁻⁶ sterilization.

Example 1: Sterilization of Demineralized Bone Matrix

A non-conventional sterilization method that uses super-critical carbon dioxide with peracetic acid sterilant (SC—CO₂-PAA) has been developed, as described above. The purpose of this study was to investigate if this sterilization method can be used for demineralized bone matrix (DBM) without significantly affecting DBM's osteoinductivity. The DBM used in this study was from LifeLink Tissue Bank (Tempa, Fla.). Two lots of DBM dry particulates were sterilized using SC—CO₂-PAA, and their osteoinductivities were evaluated using a nude rat intramuscular implant model. The DBM particulates were stored in dry form during ambient storage.

Two lots of DBM particulates (labeled 366-45-1 and 366-45-2 in tables below) were packaged in Tyvek pouches (1.1-1.2 g/pouch) and then treated with SC—CO₂-PAA for 30 min (Run Time), using the concentrations and conditions described above, in the SC—CO₂ chamber (Nova 2200, NovaSterilis), NY After treatment, the samples were placed in a nitrogen atmosphere for 24 hours before being sealed in foil pouches. Untreated DBMs were used as controls.

Both lots of DBM were implanted intramuscularly in nude rats at time 0 to evaluate their osteoinductivity. Samples from the first lot (labeled 366-45-1 in the tables below) were also implanted intramuscularly into rats after 6 and 12 months ambient storage to evaluate osteoinductivity. Four rats were used to test samples from each lot. Untreated DBM was implanted intramuscularly at one control site for each rat (Tables 1A, 1 B, and 1C).

TABLE 1A
Implantation of Test and Control Samples at Time 0
Animal
Number	Left Leg/Lot #	Right Leg/Lot #
1-4	366-45-1 test	366-45-1 control
5-8	366-45-2 test	366-45-2 control

TABLE 1B
Implantation of Test and Control Samples at 6-month Ambient Storage
Animal
Number	Left Leg/Lot #	Right Leg/Lot #
1-4	366-45-1 test	366-45-1 control

TABLE 1C
Implantation of Test and Control Samples at 12-month Ambient Storage
Animal
Number	Left Leg/Lot #	Right Leg/Lot #
1-4	366-45-2 control	366-45-2 test

At 6 month and 12 month storage time points, approximately 250 mg of DBM was hydrated prior to the implantation. The hydrated DBM was then placed into a pocket created intramuscularly, and the muscular pocket and skin were closed. After 28 days, the animals were sacrificed, and the implant sites removed. The tissues were fixed in 10% neutral buffered formalin and were then processed for histologic evaluation. Sections were cut and stained with hematoxylin and eosin. Histological slides from the time 0 explants were examined under a microscope by a pathologist using the scoring system shown in Table 2.

TABLE 2
Criteria for Microscopic Evaluation of Osteoinduction per Implant Site
Semi-Quantitative Analysis
Grade Estimated Cross-Section Area
0     0%, No evidence of new bone formation
1     1-25% of field shows evidence of new bone formation
2     26-50% of field shows evidence of new bone formation
3     51-75% of field shows evidence of new bone formation
4     76-100% of field shows evidence of new bone formation

The explants at the 6 and 12 month time points were divided into halves. One set was processed and evaluated by a pathology test facility using the scoring system shown in Table 2, and the other set was processed and evaluated blindly by an experienced scientist at LifeCell Corporation. All of the implant sites showed evidence of new bone formation, as summarized in Tables 3 and 4.

TABLE 3
Summary of Pathologist Results (AppTec)
		Scores
		0-month	6-month	12-month
Lot #	Treatment	Average ± SD	Average ± SD	Average ± SD
366-45-1	Control	2.0 ± 0.8	3.0 ± 0.0	1.0 ± 0.0
	Treated	1.5 ± 0.6	1.5 ± 0.6	1.0 ± 0.0

TABLE 4
Summary of Pathologist Results (LifeCell)
		% of new bone area
		0-month	6-month	12-month
Lot #	Treatment	Average ± SD	Average ± SD	Average ± SD
366-45-1	Control	25 (±1) %	34 (±10) %	24 (±3) %
	Treated	24 (±1) %	30 (±1) %	24 (±4) %

DBM can retain its osteoinductivity after sterilization with super-critical carbon dioxide and PAA sterilant, and no significant change in osteoinductivity was evident after 12-months ambient storage.

In addition, the light microscopy evaluations of samples after 6- and 12-months of storage are summarized in Tables 5A and 5B. Both tables include the average percent of field showing new bone formation for all animals. A 20× objective lens was used, and four fields on each slide were examined. The evaluator was blinded to the treatments. FIGS. 4 and 5 are representative photomicrographs of demineralized bone matrix that was implanted after being sterilized and stored for 6 months. FIG. 4 is the untreated control while FIG. 5 is the test sample. FIGS. 6 and 7 are representative micrographs after 12 months, with FIG. 6 as the test sample and FIG. 7 as the control. All micrographs show new bone formation.

TABLE 5A
Percent of Field Showing New Bone Formation After 6-
Months Storage
Sample ID*	20x field-	20x field-	20x field-	20x field-
2009H016	1	2	3	4	Average
1	30%	25%	25%	30%	28%
2	20%	30%	30%	20%	25%
3	50%	25%	20%	30%	31%
4	60%	50%	50%	30%	48%
5	45%	35%	20%	20%	30%
6	30%	30%	30%	30%	30%
7	50%	35%	25%	15%	31%
8	50%	25%	30%	25%	33%
Note:
Samples 1, 3, 5 and 7 are treated samples, and 2, 4, 6 and 8 are controls.

TABLE 5B
Percent of Field Showing New Bone Formation After 12-
Months Storage
Sample	Field-	Field-	Field-	Field-	Field-	Field-
ID	1	2	3	4	5	6	Average
2010H062	(%)	(%)	(%)	(%)	(%)	(%)	(%)
1L	12.8	18.8	15.5	13.4	32.1	20.8	18.9
1R	12.6	38.2	37.8	22.3	21.3	20.2	25.4
2L	20.1	11.4	20.4	24.2	31.8	42.0	25.0
2R	50.9	7.8	22.7	8.0	14.8	14.0	19.7
3L	30.0	26.4	35.7	16.3	25.4	23.0	26.1
3R	21.1	42.1	25.5	20.9	20.5	12.8	23.8
4L	40.0	17.2	11.8	21.4	17.7	40.9	24.9
4R	36.9	26.3	27.6	17.9	24.4	35.6	28.1

All the samples demonstrated new bone formation after storing the DBM for 6 or 12 months after sterilization. Most of the samples showed ˜30% new bone growth at 6 months and ˜25% at 12 months. Generally, the evidence of the new bone formation or potential new bone formation found in the samples included the presence of osteoid, osteoblasts/osteoclasts, calcified cartilage matrix/hypertrophic chondrocytes, bone marrow, clusters of chondroblasts/condrorocytes and some membrane-like connective tissue (FIGS. 4-7).

Other embodiments will be apparent to those skilled in the art from consideration of the specification and practice of the invention disclosed herein. It is intended that the specification and examples be considered as exemplary only, with a true scope and spirit of the invention being indicated by the following claims.

Claims

1. A method for sterilizing tissue, comprising: packaging the tissue in an inner package prior to treatment with super critical CO2,packaging the inner package in an outer package prior to treatment with super critical CO2, the outer package comprising (i) a first portion including a material that is permeable to super critical CO2 and a sterilant, and (ii) a second portion that is impermeable to moisture,treating the tissue with super critical CO2 and the sterilant to sterilize the tissue, andsealing the first portion of the outer package with the second portion of the outer package subsequent to sterilization such that the inner package is sealed within a moisture impermeable enclosure.

2. The method of claim 1, wherein the tissue is an acellular tissue matrix.

3. The method of claim 1, wherein the tissue is intact tissue.

4. The method of claim 1, wherein the inner package is permeable to super critical CO2.

5. The method of claim 1, wherein the inner package is permeable to the sterilant.

6. The method of claim 1, wherein the first portion of the outer package is impermeable to bacteria.

7. The method of claim 1, comprising placing the tissue in a nitrogen atmosphere for 24 hours after treatment with super critical CO2 and the sterilant.

8. The method of claim 1, wherein the sterilant comprises peracetic acid (PAA).

9. The method of claim 8, wherein the sterilant further comprises a peroxide.

10. The method of claim 9, wherein the peroxide is H2O2.

11. The method of claim 10, wherein concentrations of PAA and H2O2 in the sterilant are 10-14% and 1-3%, respectively.

12. The method of claim 11, comprising treating the tissue in a chamber, wherein concentrations of PAA and H2O2 in the chamber are 1-1000 ppm and 1-1000 ppm, respectively.

13. The method of claim 12, wherein the concentrations of PAA and H2O2 in the chamber are 20-100 ppm and 1-10 ppm, respectively.

14. A method for sterilizing tissue, comprising: packaging the tissue in an inner package prior to treatment with super critical CO2, the inner package being permeable to super critical CO2 and a sterilantpackaging the inner package in an outer package prior to treatment with super critical CO2, the outer package comprising (i) a first portion including a material that is permeable to super critical CO2 and the sterilant, and (ii) a second portion that is impermeable to moisture,treating the tissue with super critical CO2 and the sterilant to sterilize the tissue, andsealing the first portion of the outer package with the second portion of the outer package subsequent to sterilization such that the inner package is sealed within a moisture impermeable enclosure.

15. The method of claim 14, wherein the tissue is an acellular tissue matrix.

16. The method of claim 14, wherein the first portion of the outer package is impermeable to bacteria.

17. The method of claim 14, comprising placing the tissue in a nitrogen atmosphere for 24 hours after treatment with super critical CO2 and the sterilant.

18. The method of claim 14, wherein the sterilant comprises peracetic acid (PAA).

19. The method of claim 14, wherein the sterilant further comprises a peroxide.

20. The method of claim 19, wherein the peroxide is H2O2.