Patent Application
20200022688
The present disclosure relates generally to the medical field, and more particularly, to systems and methods relating to the medical applications of synthetic polymer formulations. In one application, the present invention relates to systems and devices for delivering resorbable synthetic polymer formulations to the body.
A wide variety of diagnostic and/or therapeutic procedures involve the delivery of synthetic polymers to the body. One objective is to provide hemostasis of bleeding vessels and other organs. This bleeding may be internal or external in nature and from all sites on the body. Another objective is to provide the delivery of pharmaceutical agents (e.g. hemostatic agents, antibiotics, anesthetics). This delivery may be to all sites on the body, internal or external.
A recent review of U.S. battlefield deaths from 2001-2011 demonstrated that around 90% of all injury mortality occurred in the pre-medical treatment facility environment. Of the potentially survivable deaths, the vast majority were due to hemorrhage (90%), with the bleeding coming in order of frequency from the abdominopelvic, thoracic, junctional, extremity areas.
Internal bleeding (e.g. abdominopelvic and thoracic) is particularly difficulty to stop without highly specialized care facilities. Civilian studies have found that for major traumatic injuries in the abdomen, the probability of death increases approximately 1% for each 3-minute delay to surgery. American military experts have declared that the inability to stop intra-abdominal bleeding quickly in the field “signifies a clear and persistent gap in medical treatment capability that has been present for the entire history of warfare and well documented for nearly a century.”
The gold standard for severe traumatic intra-abdominal bleeding is emergent laparotomy, which requires the lengthy training and perishable skills of a trauma surgeon, as well as a sterile operating room. As the majority of the U.S. combat deaths are in the pre-medical treatment facility environment, reducing them requires a technology that personnel with limited training can deploy rapidly, in the out-of-hospital or in-hospital environments.
The literature discloses various known systems and methods related to delivering hemorrhage control to the body.
For example, U.S. Pat. No. 8,828,050 B2 to Gregory et al. describes an applicator for delivering a plurality of sponges capable of expanding upon contact with a liquid to a body cavity. Related product information from RevMedx, Inc. regarding their Xstat products describe hemostatic devices for the treatment of gunshot and shrapnel wounds that work by injecting a group of small, rapidly-expanding sponges into wound cavities using a syringe-like applicator. In the wound, the sponges expand and swell to fill the wound cavity to create a temporary barrier to blood flow and provide hemostatic pressure. However, this system is not ideally set up to inject sponges throughout the abdominal cavity. It also can only access the abdominal cavity through an existing penetrating trauma wound, therefore making it of little use in the setting of blunt abdominal trauma.
U.S. Patent Publication Nos. 2011/0202016 A1 to Zugates et al. and 2012/0107439 A1 to Sharma et al. (with related U.S. Patent Publication Nos. 2013/0110066 A1 to Sharma et al.; 2012/0265287 A1 to Sharma et al.; 2009/0041824 A1 to Zugates et al.; and, 2016/0271293 A1 to Zugates et al.) describe injecting a biodegradable synthetic polymer into a body cavity together with another agent; the polymer and other agent then subsequently combine via a chemical reaction within the body cavity to produce a hardened elastomeric polymer foam, which prevents or limits bleeding. Product information from Arsenal Medical describes a hardening foam that binds to intra-abdominal tissues to reduce and stop bleeding. The provider injects two liquid polymers from a canister, via a large naked needle, into the abdominal cavity. Upon combination inside, these ingredients react to envelop and harden around the internal organs.
However, a solidified product in the abdominal cavity may cause serious medical issues for the life of the patient. Likewise, needing to cut out a large block of hardened material after use is clearly suboptimal. Additionally, the prior art does not include any safety method for medics or others in the out-of-hospital environment to deploy a synthetic polymer intra-abdominally, except for a naked needle. Insertion of a large naked needle into the abdomen, even by highly trained surgeons in a controlled operating room environment, can easily result in bowel or other intra-abdominal injury. Thus, this method is clearly suboptimal.
U.S. Patent Publication Nos. 2014/0271531 A1, 2014/0316012 A1, 2013/0317418 A1, and 2014/0271533 A1 to Freyman et al. describe injection of prepolymer that reacts with water to cause an in-situ forming polymer foam for embolizing or occluding cavities (e.g. aneurysm, lung, vessel). However, this also becomes a hard foam that is not easily reversible. It also must react with water within the body, which may result in variable response depending on the dampness of that particular body cavity. It is further described for injection into smaller lumen cavities and not those with very large volumes, such as the peritoneal cavity. U.S. Patent Publication No. 2002/0122771 A1 to Holland et al. shows a wound dressing hydrogel that can be sprayed on as a liquid and then crosslink or otherwise thicken to form a hydrogel in situ with similar limitations.
U.S. Pat. No. 8,668,899 B2 to Dowling et al. describes a sprayable polymeric foam hemostat for both compressible and non-compressible (intracavitary) acute wounds. This foam comprises a hydrophobically-modified polymer (e.g. hm-chitosan) or related amphiphilic polymers that anchor themselves within the membrane of cells in the vicinity of the wound. However, this polymer is not easily washed away and needs to be broken down before excretion from the body. Chitosan and related substances are additionally not synthetically formulated, which may lead to quality control issues and difficulty in manufacturing. Finally, this product and related hemostatic foams do not have a means for inducing physical tamponade within the body from the controllable transmission of higher pressures.
Prior art includes multiple uses of polymers for hemostasis. These include examples of gels, putties, and waxes to assist with tamponade of bleeding. Examples include U.S. Pat. No. 8,497,408 B2 to Winek et al. U.S. Patent Publication Nos. 2004/0013715A1 to Winek et al., 2003/0095945 A1 to Levey et al., 2006/0100370 A1 to Wellisz et al., 2009/0286886 A1 to Fisher et al., 2006/0193899 A1 Sawhney, 2016/0256170 A1 to Busold et al., 2003/0203044 A1 to Moravec, and U.S. Pat. No. 9,616,088 B2 to Diehn et al. However, these polymers are directly applied to the site of injury and do not foam to be sprayed on or spread throughout a body cavity.
The literature additionally discloses prior art regarding inverse thermosensitive polymers (i.e. inverse or reverse thermosensitive, thermosetting, phase, or thermally viscosifying polymers) as a means of providing hemostasis. Several publications describe use of inverse thermosensitive polymers to provide temporary embolization of a vessel via intravascular gel injection, such as U.S. Patent Publication No. 2005/0008610 A1 to Schwarz et al., 2005/0147585 A1 to Schwarz, 2011/0087207 A1 to Vogel et al, and 2008/0181952 A1 to Vogel et al. However, these do not spread via foam to provide hemostasis throughout a larger area and volume. Similarly, U.S. Patent Publication No. 2007/0191768 A1 to Kolb (with related U.S. Pat. No. 8,062,282) provides a method for occluding a body lumen by placing the tip of a catheter into a lumen, spraying thermosensitive polymer, and then withdrawing the tip. However, this requires at least partial withdrawal of the catheter tip while spraying directly in the area of interest. Likewise, U.S. Patent Publication No. 2008/0208163 A1 to Wilkie discloses the use of an inverse thermosensitive polymer to control biological fluid flow by an in situ formed polymer plug. However, this gel or solution also needs to be directly injected through a catheter to a specific site. Additionally, U.S. Patent Publication No. 2008/0031847 A1 to Cohn et al. (with related U.S. Patent Publication No. 2013/0158589) describes a method and kit for treating lacerations and puncture wounds using an inverse thermosensitive polymer. However, this polymer does not foam and is rather a liquid that becomes a gel after spraying it from a syringe or tube. These are thus not amenable to spread throughout a larger area or volume (e.g. via injection into a large body cavity, such as the peritoneal cavity).
The prior art additionally discloses multiple uses of inverse thermosensitive polymers for the delivery of different pharmaceutical agents, although not specifically utilized with foam delivery. These include U.S. Pat. No. 4,474,752 to Haslam et al. and 6,316,011 B1 to Ron et al., and U.S. Patent Publication No. 2011/0294760 A1 to Bahulekar et al.
Each of the patents and published patent applications mentioned above are hereby incorporated by reference.
The present invention overcomes and substantially alleviates the deficiencies in the prior art by providing improved systems and methods relating to synthetic polymer formulations.
In several embodiments, the present invention relates to systems and devices for delivering synthetic polymers to a body cavity (e.g. abdominal cavity) to reduce and/or stop bleeding. Under some of these embodiments, the synthetic polymer formulation may be provided in the form of an aqueous solution, gel, or foam. In some of these embodiments, the synthetic polymer formulation can be cleared by the body, such that there is no need for subsequent physical removal (e.g. resorbable).
In several embodiments, emergency personnel can rapidly deploy the system to deliver polymer formulation to the body to reduce or stop bleeding in the out-of-hospital or in-hospital environments, including under battlefield and mass casualty conditions.
Under some embodiments, the polymer may be used externally. Under other embodiments, an initial percutaneous access pathway into a body cavity is surgically established (e.g. laparotomy trocar, open surgical procedure) and connected to a delivery apparatus. Under other embodiments, an initial percutaneous access pathway is formed similar to the device and/or method described in U.S. patent application Ser. Nos. 13/961,422 and 14/581,339, previously incorporated by reference herein. In one of these embodiments, such a delivery device uses a probe and needle mechanism that automatically stops the advance of the device upon insertion into a body cavity or space (e.g. abdominal cavity), which minimizes user error and improves patient safety.
Under some of these embodiments, the probe of the delivery device is hollow and allows transmission of a synthetic polymer formulation with or without additional substances from a holding chamber or canister to flow through the device and hollow probe into the patient's anatomic cavity or space of interest. Under some embodiments, the polymer is initially contained within a canister, from which it is dispensed via tubing and/or other mechanism. Canisters for delivering substances under pressure are well known in the art and different embodiments utilize different types of expansion tanks, which under some embodiments contain one or more of the following features: aerosol, screw-on, easy click on, pierceable. These deliver the polymer in a pre- and/or post-foaming gel configuration. Under several embodiments, these canisters contain one or more propellent gases, as is well established in the art. Under several embodiments, the propellent gas is kept separate from the polymer to be delivered by a membrane and/or bag, so that it can transmit pressure but does not directly mix with the agent to be delivered to the body.
Under various embodiments, the synthetic polymer formulation expands once reaching the body cavity or space (e.g. abdominal cavity) to reduce and/or stop bleeding. Under some of these embodiments, the injected material does not need to chemically react inside the abdominal cavity, rather its innate properties and/or a propellant pushing the material into the cavity causes it to expand once reaching the desired space. The polymer formulation expands to partially or fully fill the cavity and provide pressure, physical tamponade, and/or deliver bioactive substances to prevent, reduce, and/or stop bleeding.
Some of these embodiments include one or more valves (e.g. control, regulator, pressure, vent, relief, head pressure, dispensing, one-way, poppet), which automatically senses the appropriate pressure and terminate the insertion of the polymer formulation into the cavity at the desired pressure. Examples include both single and double stage regulators. They can be an integral device with an output pressure setting, a restrictor and a sensor all in the one body, or consist of a separate pressure sensor, controller and flow valve. Under many embodiments, there is also a main on-off valve (e.g. ball valve) that may be manually (e.g. turning of valve lever, pushing of electronic button) or automatically (e.g. connect to a countdown clock, tied to a more complex electronic algorithm) engaged. Under some embodiments, the insertion of polymer formulation into the cavity terminates at a set volume. Under some embodiments, the system controls pressure so as to maximize hemostasis while minimizing injury from high pressure (e.g. abdominal compartment syndrome, intestinal injury, high peak lung pressure). Under various embodiments, the system allows controlled pressure to be delivered and/or maintained to a selected body area (e.g. body cavity) by the user (e.g. under manual and/or automated control). Under one example of an embodiment wherein pressure is under manual control, the user utilizes an incorporated pressure gauge to determine how much formulation and thus pressure to deliver. Under another example of an embodiment wherein pressure is under manual control, the user opens the main on-off valve of the system, which then delivers formulation to maintain a set pressure within a cavity being treated while open. Under other embodiments, the system is set for a specific pressure profile and it automatically stops delivery at a peak pressure and/or adds additional polymer at lower pressures to deliver the desired pressure profile.
For example, under some embodiments, the device delivers polymer to a body cavity to a peak pressure of 60 mmHg, at which time it automatically stops additional polymer delivery. For the first 5 minutes of delivery, the device works to maintain a pressure between 50-60 mmHg (e.g. above the patient's mean arterial pressure), delivering more polymer if the pressure falls below the lower cutoff (i.e. 50 mmHg) and stopping delivery if it reaches the maximum set (i.e. 60 mmHg). Under some embodiments, the device then has other pressure settings for one or more subsequent time periods (e.g. pressure set to 5-10 mmHg for the next 60 minutes). Under some embodiments there is additionally a pathway through a needle to remove gas and reduce the pressure if it is too high. The exact pressure and time duration settings vary under different embodiments and thus this invention is not limited to specific pressures or time periods as these can easily be changed by a person having ordinary skill in the art.
Under some embodiments, the present invention contains one or more additional substances to assist with preventing, slowing, and/or stopping bleeding. These include, but are not limited to, components of the intrinsic clotting pathway (e.g. factors XI, IX, VIII); components of the extrinsic clotting pathway (e.g. transmembrane receptor tissue factor, plasma factor, factor VII/VIIa); tranexamic acid and other amino acids and their analogs; epinephrine and other vasoconstrictors; thrombin; fibrinogen; potassium ferrate; cellulose, including oxidized and/or regenerated cellulose; kaolin; smectite granules; zeolite; chitosan; sodium carboxymethylcellulose; amylopectin; microfibrillar collagen; propyl gallate; aluminum sulfate; fully acetylated poly-N-acetyl glucosamine; related substances; and other clotting agents, platelet aggregators, and substances that reduce or stop bleeding.
Under some embodiments, the present invention contains one or more additional substances to assist with preventing, slowing, and/or stopping bacterial and/or other infections. These include, but are not limited to, antimicrobial agents (e.g. antibiotics), disinfectants (e.g. alcohols, aldehydes, oxidizing agents, phenolics, quaternary ammonium compounds, silver-based products, copper-based produces, and/or other disinfectants), and/or other agents (e.g. antifungals). Under some embodiments, a synthetic polymer with one or more of these additional substances is delivered into a body cavity. Under other embodiments, a synthetic polymer with one or more of these additional substances is sprayed or otherwise delivered to an external wound or area.
Under some embodiments, the present invention contains one or more of the previously mentioned additional substances at normal concentrations for administration in the body. Under some embodiments, the present invention contains one or more of the previously mentioned additional substances at concentrations higher than could be used via oral and/or parenteral administration because it is delivered directly to a cavity and/or space. Thus, the body cavity and/or space has a high concentration of the additional substance, but there is a lower concentration systemically or away from that cavity and/or space. This allows a high concentration at the needed site but a lower concentration away from it, which minimizes systemic and/or more distal side effects. For example, a clotting agent could be used at very high concentration when administered directly to the abdominal cavity, to cause clotting of any traumatic bleeding vessels there, when administering such a high concentration of the agent is not possible via oral and/or parenteral rout because it would cause systemic clotting of healthy vessels in the body. Similarly, an antibiotic such as gentamicin could be deployed at very high concentrations in the abdominal cavity, which if given via parenteral route would have toxic effects.
Under various embodiments, the present invention has one or more of the following characteristics: it is field-adapted with a small size, easily fitting into a medical field kit; it has a delivery device for safe and rapid deployment by medics or other non-surgeon providers; it is stable without need for refrigeration, with the ability to maintain activity under the environmental extremes experienced in military operations; it is rapidly applied to penetrate deep into intra-abdominal injuries of all shapes and sizes; it induces hemostasis; it provides a delivery mechanism for a wide range of additional bioactive clotting agents; it prevents bacterial adhesion and/or biofilm formation; it inhibits drug-resistance mechanisms in multidrug-resistant strains of bacteria; it is partially or fully resorbable by the body; it has a low risk of complications; it is not exothermic and/or has minimal risk of iatrogenic thermal injury to organs; it is transparent does not discolor the abdominal organs; it is water soluble; it may be quickly and easily washed away for easy removal if needed for emergent laparotomy surgery; it contains no toxic substances or materials with potential for adverse environmental effects; it uses expanding and/or propellant components that are non-ozone depleting; and/or it is made in whole or part from synthetic, inert polymers that are already FDA and EU-approved for pharmaceutical applications.
Under several embodiments, the synthetic polymer formulation comprises a solution of one or more copolymers of ethylene oxide (EO) and propylene oxide (PO) (e.g. in an aqueous solution), in combination with one or more volatile or gaseous expanding and/or propelling components which is dissolved in, or evenly dispersed throughout, said copolymer solution. Such copolymers may be a random or block copolymer of EO and PO having an average molecular mass of about 1 kg/mol to about 100 kg/mol, and a mass ratio of EO to PO of between 5:95 to 95:5. In some of these embodiments, the block copolymer is a poloxamer. Poloxamers are linear A-B-A triblock copolymers of EO and PO having the general formula (EO)x(PO)y(EO)x, where x and y represent the number of EO and PO monomer units in the block. Different poloxamers having a molecular mass in the range of about 1 kg/mol to about 15 kg/mol and EO:PO ratios by mass of between 8:2 and 1:9 are commercially available, (e.g., PLURONIC® copolymers from BASF). In certain advantageous embodiments, the block copolymer is a poloxamer produced in NF grade for medical applications, and which is approved for pharmaceutical use. Examples include poloxamers P188, P237, P338 and P407, also known as Pluronic® F68, F87, F108 and F127; the ranges of molecular mass and mass % of EO (as oxyethylene) for each of these poloxamers is shown in
Under several embodiments, the one or more volatile expanding and/or propelling components is a compressed gas or volatile liquid that is dissolved within or evenly dispersed throughout the polymer solution under elevated pressure. The compressed gas or volatile liquid expands and/or evaporates into a gaseous form due to the decrease in pressure as it is released from its storage container, thereby causing the polymer solution to foam (e.g. within the body cavity). This gas or volatile liquid may be any one of the many medical grade gases suitable to be delivered to the body. Under several embodiments, this gas or volatile liquid is one or more organohalide compound, such as a fluorinated hydrocarbon (i.e. hydrofluorocarbon, or HFC) or a perfluorocarbon. For example, under some embodiments, the synthetic polymer formulation is mixed with 1,1,1,2-tetrafluoroethane (i.e. norflurane, R-134a) in liquid form under a pressure of 100 pounds per square inch (psi). This mixture of polymer and hydrofluorocarbon provides a foaming polymer solution once discharged from the storage canister. Thus, under multiple embodiments, no chemical reaction with any components within the body (e.g. water) is required to cause the synthetic polymer formulation to foam.
Under several embodiments, the synthetic polymer formulation is an aqueous solution of a block copolymer (e.g. a poloxamer) of a suitable type and in an adequate concentration to exhibit reverse phase change properties, such that the solution increases markedly in viscosity (e.g. forming a strong gel when it is warmed) and decreases in viscosity when it is cooled. By selecting the type of block copolymer and an appropriate concentration in solution, this reverse phase change can be tailored to occur over a desired temperature range such that the solution is a low viscosity liquid at temperatures below that anticipated to occur in the body, for example less than about 5-10 □C but is a highly viscous gel at temperatures above about 20-30 □C.
Under many embodiments, the reverse phase properties of such a block copolymer solution provide a key advantage of the current invention, such that after delivery to the body (e.g. into the an internal cavity, sprayed externally) that the synthetic polymer formulation is as viscous as possible and have the form of a highly viscous gel in order to exert the maximum hemostatic effect by physical tamponade (i.e., by providing a physical barrier to resist the flow of blood from damaged blood vessels). However, in practice (e.g. use in acute abdominal hemorrhage) it is also necessary to deliver the solution to the patient rapidly to stop the bleeding as soon as possible and ideally through a small diameter tube or needle, which would be difficult or impossible to achieve if the solution were a highly viscous gel during delivery. The use of a synthetic polymer formulation with appropriately tailored reverse phase properties in conjunction with a suitable choice of expanding gas provides a simple solution to these conflicting requirements. In many embodiments, the reverse phase characteristics of the polymer solution and the properties of the expanding gas are arranged such that the cooling effect due to expansion of the gas as the solution is discharged ensures that the polymer solution is in low viscosity liquid form as it exits the storage container, thereby facilitating rapid delivery to the patient. After it is delivered, the body temperature of the patient causes the polymer solution to increase in viscosity, forming a highly viscous gel foam, which provides a much stronger tamponing effect than could be achieved if the polymer solution remained in the liquid form. An additional advantage of the reverse phase properties of the polymer solution is that the viscous gel can later be easily removed, if necessary, by cooling (e.g. by irrigation with cool water or normal saline within the abdominal cavity) whereupon it reverts to liquid form.
From the foregoing, it can be seen that the present invention provides systems and methods relating to synthetic polymer formulations within animals, especially humans. Moreover, it should also be apparent that the device can be made in varying lengths, sizes and capacities, and the precise composition of the synthetic polymer formulation, the amount delivered and the rate and pressure at which it is delivered may be varied appropriately to treat adults, children, and infants. While the invention has been described with a certain degree of particularity, it is manifest that many changes may be made in the details of construction and the arrangement of components without departing from the spirit and scope of this disclosure. It is understood that the invention is not limited to the embodiments set forth herein for purposes of exemplification and that elements of certain embodiments can be combined with elements of other embodiments. Additional objects, advantages, and novel features of the invention will be set forth in the description which follows, and will become apparent to those skilled in the art upon examination of the following detailed description and figures. It should be understood that not all of the features described need be incorporated into a given system or method.
Referring to the drawings,
Under this embodiment, stabilizer 30 initially extends distally from holder 40 along the tract of needle 20, to provide a mechanism for automatically halting the forward movement of needle tip 22 and probe tip 52 upon penetration into a body cavity (e.g. peritoneal cavity). Holder 40 has one or more phalanges 49 that are resiliently biased medially, but when pushed laterally by probe holder 60 are caused to interact with grooves 34 on rods 32 so as to halt the movement of stabilizer 30 in respect to holder 40.
Biased by spring 80, in its distal position probe holder 60 extends tip 52 of probe 50 out distally from tip 22 of needle 20. Additionally, this pushes phalange(s) 49 laterally to reversibly lock with grooves 34 and inhibit the movement of rod(s) 32 and thus stabilizer 30 in relation to the rest of device 10.
When needle 20 pierces the skin and enters into a cavity (e.g. peritoneal cavity), probe tip 52 to moves proximally in reference to needle tip 22. This causes holder 60 on probe 50 to also move proximally in reference to housing 40. This in turn allows phalanges 49, which are biased medially, to move medially and thus unlock from groove(s) 34 to allow rod 32 and thus stabilizer 30 to move in relation to housing 40. Thus, when a general distal biasing of the device is provided by the user, stabilizer 30 remains flush with skin of the body while the rest of the device moves distally, thus inserting needle 20 further into the cavity.
Once probe tip 52 and needle tip 22 have reached a body cavity, spring 80 is free to move probe tip 52 distally in reference to needle tip 22, which allows holder 60 to move distally in reference to housing 40 and thus forces phalange(s) 49 laterally to again lock with grooves 34 and inhibit the movement of rod(s) 32 and thus stabilizer 30 in relation to housing 40. This, in turn, prevents needle tip 22 from moving further into the cavity, thus minimizing the chances of injuring vital structures. Under one embodiment, there is an airtight seal between probe 50 and housing hole 42, which may include the use of an O-ring and/or other sealing mechanisms.
When probe tip 52 has entered the cavity, there is then a contiguous pathway between connection port 90 with luer lock groove 48 through the device and into probe tip 52. Reversibly or irreversibly connected to connection port 90, in some embodiments via standard luer lock, is a standard, high-pressure, tapered, or otherwise configured tube (not shown) from a delivery container, such as one shown in
A key feature of this embodiment is that the driving gas in the lower space 104 is physically separated from the synthetic polymer formulation in the upper space 110. An advantage of this embodiment is that the pressure of the driving gas in the lower space 104 can be arranged to always exceed the pressure of the expanding gas in the upper space 110 until the contents of upper space 110 have been sufficiently discharged from the container, thereby maintaining the expanding gas in a compressed form until the synthetic polymer formulation has been released via the valve mechanism 114 into the exit nozzle 116.
Under some embodiments, the synthetic polymer formulation is delivered by opening the releasing valve by pushing a button, pulling a tab, or other manually-activated releasing mechanism. Under other embodiments, the delivery of the synthetic polymer formulation may be controlled automatically or semi-automatically by sensing when the probe has entered the cavity space, or in response to absolute pressure or changes in pressure within the cavity (e.g. by a sensor mechanism within the cavity itself or connected to the dispersal path earlier within the system). Such control mechanisms may be used to initiate the delivery of the polymer formulation, to override user-activated delivery under some circumstances (e.g. stopping delivery after a certain amount of time), and/or to control the polymer formulation flow rate or the maximum or minimum pressure developed within the body cavity (e.g. through a regulator mechanism). Such control mechanisms may also allow for adjustment of the pressure developed within the body cavity by administering additional polymer formulation or by venting any excess, either manually or in an automated manner under feedback control.
Some of these embodiments include one or more valves (e.g. control, regulator, pressure, vent, relief, head pressure, dispensing, one-way, poppet), which automatically sense the appropriate pressure and terminate the insertion of the polymer formulation into the cavity at the desired pressure. Examples include both single and double stage regulators. They can be an integral device with an output pressure setting, a restrictor and a sensor all in the one body, or consist of a separate pressure sensor, controller and flow valve. Under many embodiments, there is also a main on-off valve (e.g. ball valve) that may be manually (e.g. turning of valve lever, pushing of electronic button) or automatically (e.g. connect to a countdown clock, tied to a more complex electronic algorithm) engaged.
Under some embodiments, the delivery container is partially or completely integrated into the delivery device, to minimize parts.
The following examples more particularly describe certain embodiments of the invention but are intended for illustrative purposes only, since modifications and variations will be apparent to those skilled in the art.
For a series of experiments to study the physical properties of the foaming synthetic polymer formulation (Examples 1 and 2 below), a delivery container (
Aqueous solutions of poloxamers P188, P338, and P407 (Pluronic® F68, F108, and F127 respectively) at concentrations from 25% w/w to 45% w/w were blended with from 2.5% to 10% by weight of 1,1,1,2-tetrafluoroethane (aka Norflurane, HFC-134a) in liquid form under pressure using a delivery container with the design illustrated in
Preparation of Poloxamer Solutions:
Reverse osmosis purified water was chilled in a laboratory refrigerator to approximately 4° C. before use. The required mass of chilled water was first weighed into a suitable laboratory pail and the calculated amount of poloxamer was then slowly added to the pail under constant mixing using a high-shear mechanical stirrer. After all the poloxamer had been added, a lid was placed onto the pail and it was transferred to a refrigerator. Periodically, the pail was removed from the refrigerator and the contents were re-mixed using the mechanical stirrer, after which it was returned to the refrigerator. The process was repeated until the poloxamer was completely dissolved, which required up to 2 days for the highest concentration solutions.
Filling of Delivery Container:
Poloxamer Solution:
Both delivery container valves 114 (upper valve) and 120 (lower valve) were opened and positive air pressure was applied to the upper valve to cause the piston to move to the bottom of the container. The delivery container was placed on a balance and tared. Approximately 450 mL of the cold poloxamer solution (at approximately 4° C.) was then added to the upper space 110 of the delivery container through the upper valve, and the total mass of the added solution was recorded. A positive air pressure was then applied via the lower valve to move the piston upwards sufficiently to expel any remaining air from the upper space, after which both valves were closed.
A pressurized cylinder of 1,1,1,2-tetrafluoroethane (TFE) was attached to the exit nozzle 116 via a length of flexible high-pressure tubing, and the delivery container was replaced on the balance and tared again. The upper valve of the delivery container was then opened, and liquid 1,1,1,2-tetrafluoroethane was dispensed slowly from the pressurized cylinder until the desired mass of TFE had been transferred into the delivery container. The upper valve was then closed, and the delivery container was pressurized to 100 psi with air via the lower valve to ensure that all the added TFA, which has a vapor pressure of 71 psi at 20 □C, was compressed back into liquid form.
Mixing of Poloxamer Solution and TFE:
After both the cold poloxamer solution and the TFE were added, they were mixed together under pressure using the stirring paddle 122 attached to an electric drill. During mixing, care was taken to ensure the temperature always remained below the gelation temperature for the species of poloxamer being used and its concentration in solution (
Foam Height Testing:
The volume and stability of the foam produced by each foaming polymer formulation was assessed using a simple foam height testing apparatus as shown in
In use, the delivery container was attached via a flexible tube to the port 202 and the foaming polymer formulation was introduced into the testing apparatus after which the input port was closed (
Test Design:
The principal goal of the experiments presented herein was to evaluate the potential utility of the foaming polymer formulations to control noncompressible hemorrhage within a specific body cavity (i.e. noncompressible intra-abdominal hemorrhage within the peritoneal cavity). Therefore, the height of the water column (and hence the pressure resisting the expansion of the foam) was set at approximately 13.5 cm to simulate the upper limit of normal intra-abdominal pressure (i.e. approximately 10 mmHg). For all studies TFA was used as the expanding gas. Each polymer formulation was evaluated in triplicate.
Presentation of Data:
Example results from the foam height testing are shown in graphical form in
In each Figure, the upper graph shows the Foam Ratio (FR) over time for a two-hour period. Each foaming polymer solution rapidly expanded after it was dispensed into the tube, reaching a maximum foam height within 0-2 minutes, after which the foam height gradually declined over time. For a numerical comparison, the maximum Foam Ratio (FRPeak) and the Foam Ratio after 60 minutes (FR60) were recorded; these data are shown in
The lower panel of each Figure shows the Specific Volume (SV) of the foam over the two-hour observation period. SV is a measure of the total volume of the foam normalized for the mass of the formulation that was dispensed and is therefore a function of both the overall volume of the expanding gas and the proportion of the expanding gas that is contained within the foam at any given time. For highly stable foams, the SV will increase slightly over time as the system reaches equilibrium temperature and the total gas volume continues to slowly expand. In contrast, for poorly-stable foams the SV decreases over time because the rate of collapse exceeds any increase in volume due to thermal effects. (Note that the FR is a ratio of the total foam volume to the total gas volume and therefore is not affected in the same way by changes in temperature). For a numerical comparison, the maximum Specific Volume (SVPeak) and Specific Volume after 60 minutes (SV60) are shown in
Results:
The effects of using a different proportion of TFE to expand the foam is illustrated in
As shown in
The effects of using a different proportion of TFE to expand the Pluronic F127 foam is illustrated in
Visual inspection of the foams was consistent with the experimental findings: the Pluronic F68 formulations produced homogeneous-looking foams with small uniform bubbles, whereas those produced using Pluronic F127 at all concentrations had a more heterogeneous structure, with significant variability in the size of the bubbles and occasional voids.
Selected results for the three different Pluronics are compared in
Overall it was found that aqueous solutions of each type of Pluronic tested will produce a foam when blended with TFE, but the foams exhibited different characteristics in terms of volume and rate of collapse. The results suggest that the foam properties could be tailored to a specific application, for example if a foam with a longer or shorter lifetime were desired, by selecting the most suitable Pluronic type.
Based upon the findings in the foregoing examples, a foaming Pluronic F68-based formulation was selected for evaluation as a potential interventional treatment in a porcine model of acute traumatic non-compressible abdominal hemorrhage.
These following studies were performed using the laparoscopic swine model of non-compressible torso hemorrhage (NCTH) developed by Dr James Ross, as described in “A Laparoscopic Swine Model of Non-Compressible Torso Hemorrhage” James D. Ross Ph D, et al. J Trauma Acute Care Surg, Volume 77, Number 3, Supplement 2, which is hereby incorporated by reference. The laparoscopic approach maintains both the integrity of the peritoneum and the natural tamponade effect of an intact abdominal wall while preserving the intrinsic physiologic responses to hemorrhage and therefore provides a model of NCTH that reflects clinically relevant physiology in trauma and uncontrolled hemorrhage. For splenectomized animals without intervention, the mortality rate in this model was 67%.
Preparation of Foaming Pluronic F68 Formulation: Since a larger volume was required for the in vivo studies, a larger delivery container was used that was functionally equivalent to that shown in
Experimental Design:
The foaming Pluronic F68 formulation was evaluated in six anesthetized adult male Yorkshire swine. All animals were splenectomized prior to the study, and a pressure sensor was placed laparoscopically into the abdomen to allow monitoring the intra-abdominal pressure (IAP). At the start of the experiment (T=0) a Grade V liver injury was created in each animal by laparoscopically transecting a lobe of the liver. To simulate a typical “pre-hospital” care scenario, the injured liver was allowed to bleed for 10 minutes prior to intervention. At T=10, the foaming Pluronic F68 formulation was delivered to the abdominal cavity via a laparoscopic trocar until the IAP reached 60 mmHg, which was achieved in approximately 1-2 minutes. The delivery was then halted, and the pressure was monitored. Additional foaming Pluronic F68 formulation was delivered as necessary to maintain the IAP approximately 60 mmHg for a minimum of 5 minutes. To avoid ischemic damage to the abdominal organs, the IAP was then allowed to naturally collapse over time. The experiment was terminated one hour after injury (T=60) after which the animals were euthanized, and necropsy performed.
Results:
At necropsy, the foaming Pluronic F68 formulation was found to have formed a thick viscous translucent gel in contact with the intra-abdominal organs. The gel did not interfere with the visibility of, or access to, the damaged organ and was easily removed by hand or by irrigation with cold liquid.
Non-foaming reverse phase Pluronic solutions have been successfully employed and commercialized for control or prevention of bleeding from small blood vessels during surgical procedures, and their wider use has also been proposed for the emergency management of other types of hemorrhage, such as bleeding from deep wounds or within a body cavity, which can be difficult to control by other means such as direct compression. However, all reverse phase solutions have certain inherent characteristics which have hitherto limited their suitability for emergency use and/or for control of severe hemorrhage:
These deficiencies are addressed by the delivery of the Pluronic solution as a foam rather than as bulk liquid. The foaming formulations described herein rely upon the internal, intrinsic cooling effect of the expanding gas to reduce the temperature of the polymer solution at the instant it is dispensed. Therefore, it is not necessary to pre-chill the delivery container or to provide any external means of cooling. This is an important distinction from the prior art relating to Pluronic solutions which requires the container to be cooled before use in order to convert the polymer solution to a low viscosity liquid.
The foaming formulations described herein also require a much smaller amount of the Pluronic solution to completely fill the wound or body cavity than would be needed for a non-foaming solution. As shown in the examples, a suitable foaming polymer solution can expand at least 25-fold after it is dispensed. Consequently, the total heat capacity of the foam will be much lower than an equivalent final volume of a non-foaming solution, and therefore the amount of heat absorbed by the foamed polymer solution will also be proportionately lower. Note also that the foam has a thermal insulating effect because it greatly reduces mixing due to convection, which would otherwise occur if the solution was in liquid form. The insulating effect will tend to retain the heat in the layer of foam in contact with, or in close proximity to, the internal surfaces of the cavity, thereby promoting gelation precisely where it is required, while slowing the rate of heat transfer to the bulk of the polymer solution.
Examples have been presented herein which demonstrate the features and advantages of certain synthetic polymer formulations representing embodiments of the invention. These examples are not intended to limit the scope of the invention to any specific formulations of synthetic polymers, gases, or volatile liquids and/or concentrations or combinations thereof. It will be apparent to those skilled in the art that formulations containing other poloxamers, other synthetic polymers, other expanding gases, and optionally other components including compounds intended to build and stabilize the foam may also be used. It will also be apparent that agents to assist in the control of hemorrhage or to provide other therapeutic benefits may also be advantageously included within and delivered by the synthetic polymer formulation.
There have also been illustrated and described herein certain systems and methods for delivering said synthetic polymer formulations to the body. While particular embodiments have been described, it is not intended that the invention be limited thereto, as it is intended that the invention be as broad in scope as the art will allow and that the specification be read likewise.
Furthermore, while parts of the embodiments of the invention were described as having certain shapes, and being made of certain materials, it will be appreciated that other materials and shapes can be utilized. For example, it is evident that the system could easily be modified to deliver other therapeutic and/or diagnostic liquids, gases, solutions, and/or suspensions to the body. For another example, it is evident that the synthetic polymer formulation could be used to stop bleeding in the abdominal cavity, thoracic cavity, junctionally, externally, intravaginally, intrauterine, intracranially, intranasally, and/or into puncture or other wounds (e.g. abscess). For areas that are not naturally a contained space or could have easy spillage from within it (e.g. nares, uterus after delivery), the system may also contain a means for blocking exit of the foam from part of the cavity (e.g. an inflatable balloon, packing) to allow for use. It is also evident that the synthetic polymer formulation could be inserted into a cavity via other means (e.g. simple tubing, naked needle, Veress needle, open surgical approach, direct spray) and that the synthetic polymer formulation could be used without the delivery device or the delivery device could be used to deliver other materials. It will therefore be appreciated by those skilled in the art that yet other modifications could be made to the provided invention without deviating from its spirit and scope as so claimed.
The following references include information relevant to the devices and methods of the present invention and are hereby incorporated by reference: Eastridge et al. Death on the battlefield (2001-2011): Implications for the future of combat casualty care. J Trauma Acute Care Surg. 73(6) Sup 5.; and Clarke, J R et al. Time to Laparotomy for Intra-abdominal Bleeding from Trauma Does Affect Survival for Delays Up to 90 Minutes. Journal of Trauma-Injury Infection & Critical Care. 2002 52(3): p420-425
The present application claims the benefit of U.S. Provisional Application No. 62/643,846 filed Mar. 16, 2018, which is hereby incorporated herein in its entirety by reference. U.S. patent application Ser. No. 13/961,422, filed Aug. 7, 2013 and entitled Method and Device for Simultaneously Documenting and Treating Tension Pneumothorax and/or Hemothorax and U.S. patent application Ser. No. 14/581,339, filed Dec. 23, 2014 and entitled Percutaneous Channel System and Method, and U.S. patent application Ser. No. 17/961,422, filed Sep. 22, 2017 and titled Percutaneous Access Pathway System, all having at least one of the same inventors, are hereby incorporated by reference herein in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62643846 | Mar 2018 | US |