Tackifiers and their use in pressure sensitive adhesives

The present invention relates to pressure sensitive adhesives comprising a synthetic latex and a tackifier resin and an emulsion of the tackifying resin.
Pressure sensitive adhesives are, among other applications, used in the tape and label field. A pressure sensitive adhesive may be used in a number of applications such as masking tape, electrical tape and medicinal tapes for holding dressings and the like in place. The term label covers a broad range of products and includes items such as price tags in the supermarket and labels on glass or plastic containers. In the case of "labels" two types of bonding are required namely permanent and removable. Permanent bonding is required for items such as labels on glass or plastic containers when the life of the label will be relatively long. Removable bonding is desirable for items such as price tags and peelable tape.
Pressure sensitive adhesives should have a high initial tack so that the adhesive surface merely needs to be contacted and pressed to a substrate to achieve bonding. There should be little or no requirement to hold the adhesive and substrate in position for any significant time while a bond develops. Depending upon the strength of adhesion required the bonding force of the adhesive may increase with time to provide a relatively permanent bond.
It is known to prepare at least three different types of adhesives using natural or synthetic tackifiers, natural or synthetic resins, or blends thereof, namely, hot melt adhesives, solution adhesives and aqueous based adhesives. Hot melt adhesives are made from a blend of resins and are normally solid at room temperature. Hot melt adhesives require an elevated temperature for application to a substrate necessitating some type of hot melt gun. Solution adhesives such as those described in U.S. Pat. No. 4,048,124 do not suffer from this drawback. These adhesives comprise a solution of a tackifier resin or a blend of tackifier resins in a low boiling hydrocarbon solvent. When the adhesive is applied to a substrate the solvent evaporates. Due to environmental concerns and the rising cost of hydrocarbon solvent there has been an increasing need to reduce or eliminate the hydrocarbon solvent in such adhesives. Accordingly, the adhesives industry is seeking improved aqueous based adhesive compositions. Existing aqueous based adhesive compositions usually comprise a natural or a synthetic latex in admixture with cellulose materials such as starch or natural or synthetic tackifier resins.
U.S. Pat. No. 4,189,419 to Avery International discloses a pressure sensitive adhesive comprising from about 50 to 60% by weight on a dry basis of a tackifier and from about 50 to 40% by weight on a dry basis of a carboxylated styrene butadiene polymer (SBR).
A paper entitled "Styrene Butadiene Latexes for Adhesive Applications" by Robert G. Kahn of Dow Chemical, published in Adhesives Age, Dec. of 1977 discloses a similar pressure sensitive adhesive composition which also contains butyl benzyl phthalate, as a "plasticizer". While the amount of plasticizer is relatively small the plasticizer comprises a hydrocarbon phase in the adhesive and the composition is not entirely aqueous based.
U.S. Pat. No. 4,179,415 issued Dec. 18, 1979, to Johnson and Johnson discloses a substantially aqueous based adhesive composition containing a latex having a high proportion of isoprene.
United Kingdom patent application No. 2097410A discloses novel pressure sensitive adhesives comprising a latex of a polymer and a tackifier resin the polymer being obtained from particular amounts of vinyl or vinylidene aromatic monomers and C.sub.4 -C.sub.8 conjugated diene monomers and an unsaturated carboxylic acid. Similarly European patent application publication No. 0062343 A2 discloses a latex of a copolymer obtained from a hard monomer such as styrene, a soft monomer such as butadiene and an unsaturated acid which may be blended with a tackifying resin to produce a formulation useful as a pressure sensitive adhesive.
Various resinous materials have been suggested as tackifiers for these latices. Examples of materials suggested include emulsified rosin, partially decarboxylated rosin, glyceryl esters of polymerised rosin, partially dimerised rosin, natural resins, hydrogenated wood rosin, plasticised hydrogenated rosin, aliphatic hydrocarbon resins from petroleum, aromatic petroleum resins, EVA, terpene/phenol resins, cumarone/indene resins, rosin esters, pentaerythritol esters and polydicylopentadiene resins.
In developing adhesive formulations one seeks the optimum combination of several adhesive properties and since it is not generally possible to achieve the optimum for every property it is necessary to obtain the best balance of properties for the particular use in mind. For pressure sensitive adhesives for use in the label industry one tries to optimise the loop tack and ball tack and at the same time provide an adhesive whose component will not migrate during storage leading to unsightly colouring and lowering of adhesive properties. Although the improved loop tack and ball tack can be provided by the tackifier resins of the type described above we have found that those tackifiers which provide such tack for example hydrogenated rosins such as Staybelite ester 10 and modified rosins such as Snowhite 52CF tend to migrate.
It has been generally suggested in United Kingdom patent application No. 2097410A and European Patent application No. 0062343 that petroleum hydrocarbon resins such as those manufactured from a C.sub.9 cut of a aromatic hydrocarbon stream or a C.sub.5 cut of an aliphatic or cycloaliphatic hydrocarbon stream are useful as tackifiers. There is however no suggestion of the particular type of resin that should be used and indeed many of the resins falling within such broad descriptions are unsuitable for tackification of carboxylated styrene/butadiene lattices. Our European Patent Application No. 83300001.1 describes certain resin emulsions which may be used to tackify carboxylated styrene/butadiene rubbers but such resins have not been found to provide optimum adhesive properties and the present invention provides a further improvement in such tackifiers.

The present invention therefore provides the use as a tackifier for carboxylated styrene butadiene copolymers of a resin having a softening point from 10.degree. C. to 80.degree. C. being a copolymer of a feed which is predominantly C.sub.5 olefines and diolefines and one or more monovinyl aromatic compounds containing from 10 to 30 wt. % of the monovinyl aromatic compounds.
The invention further provides a pressure sensitive adhesive comprising from 30% to 85% by weight of a carboxylated styrene butadiene copolymer and from 15% to 70% by weight of a resin having a softening point from 10.degree. C. to 80.degree. C. being a copolymer of a feed which is predominantly C.sub.5 olefines and diolefines and one or more monovinyl aromatic compounds containing from 10 to 30 wt. % of the monovinyl aromatic compounds.
In a further embodiment the present invention provides an aqueous emulsion containing from 40% to 70% by weight of a resin having a softening point from 10.degree. C. to 80.degree. C. being a copolymer of a feed which is predominantly C.sub.5 olefines and diolefines and one or more monovinyl aromatic compounds containing from 10 to 30 wt. % of the monovinyl aromatic compounds.
Carboxylated SBR emulsions with which the resins are used in the adhesives of the present invention are commercially available from numerous suppliers. The processes for the production of these carboxylated SBR emulsions are discussed in U.S. Pat. No. 3,966,661. In brief the carboxylated SBR emulsions may be made by emulsion polymerisation of butadiene, styrene and one or more unsaturated acids (for example acrylic, methacrylic, crotonic, maleic, fumaric, itaconic and 3-butene 1, 2, 3 carboxylic acids). If desired substituted monocarboxylic acids and substituted polycarboxylic acids may be used. The quantity of carboxylic acid used, based on total monomer is about 0.5 to 5% w/w. Preferably the carboxylated SBR contains at least 1% w/w of the said carboxylic acid monomers. For example, it is preferred that it should contain about 1 to 5% w/w of the carboxylic monomer. The unsaturated acids may be ethylenically unsaturated monocarboxylic acids or polycarboxylic acids or mixtures thereof. Preferably they contain 2 to 10 carbon atoms. The invention is particularly useful with materials such as those described in United Kingdom Patent No. 2097410 and European patent application No. 0062343 and the material originally available from Polysar as D93-703 and now commercially available as PL-3703.
The carboxylated SBR used to make the emulsion preferably has not more than 50% w/w of bound styrene. For example it contains 20 to 50% w/w, preferably 35 to 50% w/w of bound styrene. If the bound styrene content of the SBR is less than 20% w/w the bond strength of the resulting pressure sensitive adhesive product is reduced to an unacceptable extent and conversely if it exceeds about 50% w/w the tack on the resulting adhesive is reduced.
In the SBR an anionic or nonionic emulsifier is desirably present. Anionic emulsifiers are desirable in order to obtain high mechanical stability under the high shear conditions which are apt to occur in certain types of pumping and coating equipment. Particularly suitable examples are synthetic anionic emulsifiers such as alkaline metal soaps of rosin acids. It is well known rosin is a natural product obtained from pine trees and is a product extracted either from the growing tree or from the stump. The main constituents of rosin are abietic acid and premaric acid type resin acids which have the general formula C.sub.19 H.sub.29 COOH and contain the phenanthrene nucleus.
The resins used as tackifier according to the present invention are prepared by the polymerisation of a mixture of a petroleum cracked distillate generally boiling in the range 25.degree. C. to 80.degree. C. and a monovinyl aromatic monomer in the proportions to yield a resin containing from 10 to 30 wt. % of the monovinyl aromatic compound as determined by Nuclear Magnetic Resonance analysis. The petroleum cracked distillate comprises a mixture of saturated and unsaturated monomers the unsaturated monomers being mono-olefines and diolefines and although the unsaturated materials are predominantly C.sub.5 some higher and lower materials such as C.sub.6 olefines and diolefines may be present. The distillate may also contain saturated or aromatic materials which can act as polymerisation solvent.
The preferred monovinyl aromatic monomer is styrene which may be substituted in the aromatic group. Alternatively .alpha.,methyl styrene or vinyl toluene may be used. It is however preferred to use the pure monomer rather than the commercially available mixtures of vinyl aromatic monomers.
The resins are conveniently prepared by Friedel-Crafts catalysed polymerisation in which the mixture of cracked distillate and monovinyl aromatic monomer are treated with 0.25-2.5 wt. % of a catalyst such as aluminium chloride, alum.inium bromide, or solutions, slurries or complexes thereof or borontrifluoride. These reactions are generally carried out at temperatures in the range 0.degree. to 120.degree. C., preferably 0.degree. to 70.degree. C. more preferably 20.degree. to 55.degree. C. the conditions being controlled to yield a resin of the required softening point. Residual catalyst is quenched by suitable methods such as addition of methyl alcohol and subsequent filtration followed by water and/or caustic washing. The final solution may then be stripped of unreacted hydrocarbons and low molecular weight oils by vacuum or steam distillation.
The resins contain from 10 to 30 wt. % of the monovinyl aromatic monomer, preferably from 15 to 25 wt. % and have a softening point from 10.degree. C. to 80.degree. C. The optimum softening point depends on the nature of the carboxylated latex with which it is to be used but we prefer it be in the range 30.degree. C. to 60.degree. C. since at higher softening points the adhesive properties can deteriorate whilst use of lower softening point materials can result in migration of the tackifier. The resins are conveniently supplied as aqueous emulsions and the emulsions may readily be produced by mixing with water and an anionic or nonionic emulsifer of the type described above or a mixture of both in relation to the carboxylated latex and obtaining the emulsion by inversion. We prefer that the emulsion contain about 50 wt. % of the resin. The emulsions may conveniently be obtained by the process described in our European Patent application No. 83300001.1.
The latex and the tackifier may be blended using conventional blenders to provide a homogenous mixture. The tackifier resin may be added to the latex in an amount of from about 20 to about 100 parts by weight per hundred parts of polymer in the latex, more, preferably the tackifier resins is added to the latex in an amount from about 50 to about 150 parts by weight per 100 parts of polymer in the latex. It is preferred that the tackifier be added to the latex as an aqueous emulsion to provide the amounts of tackifier resin per amount of polymer given above.
The adhesive compositions of the present invention may be applied to a substrate and then dried using conventional substrates and procedures. The substrate used depends upon the use envisaged but it is usually relatively thin material, usually no greater than about 3.2 mm in thickness and in the manufacture of tapes and labels the substrate is a relatively thin sheet material. The sheet material may be a polymeric material which is flexible at about room temperature. The sheet material may be a homo-polymer of an ethylenically unsaturated monomer such as ethylene, propylene or vinyl chloride, or be polyester or polyamide provided it has sufficient flexibility for the desired end use. Alternatively the substrate may be made from cellulosic or reconstituted cellulosic material such as rayon. The substrate need not be a sheet material but may be composed of fibers which may be woven, or non woven as is the case in paper. Woven substrates may be made from cellulosic material, such as cotton or from fibers of any of the above mentioned polymers.
The composition is applied to the substrate using conventional coating techniques such as roller coaters, blade coaters, meyer rods or air coaters. The coated substrate is then dried usually by passing it through a heating tunnel or oven through which may be circulating hot air or the tunnel or oven may contain infrared lamps to dry the coated substrate. The drying time will be a function of a number of factors such as the heat capacity of the substrate, the type of heating, the oven temperature, air velocities (if circulating air is used) and the rate of passage of the substrate through the heater.
The substrate should be coated with sufficient composition to provide a dry coat weight from about 16 to about 57 g/cm.sup.2. Generally in the manufacture of tapes using a continuous sheet polymeric substrate a dry coat weight of about 15-30 g/m2 is used. In the manufacture of labels a dry coat weight from about 15 to 30 g/cm.sup.2 is usually used. In the manufacture of masking tape a dry coat weight from about 35 to about 65 g/cm.sup.2 is usually used.
After drying the coated substrate is cut to the required dimension. In the manufacture of tape the substrate is cut into strips and rolled to provide a finished product. The substrate may also be cut into shaped items to provide labels or medicinal tapes.
The invention is illustrated by the following Examples in which the feed used had the following composition.
______________________________________Component (Wt. %)______________________________________ C.sub.5 paraffin 1 C.sub.5 olefins 22 C.sub.6 paraffins 3 C.sub.6 olefins 5 C.sub.6 diolefins 3.5 Isoprene 14 Pentadienes 19 CPD 1.5 Benzene 31 Total Olefins: 27 Total Diolefins: 38______________________________________
This feed was copolymerised with varying amounts of C.sub.5 olefin streams and styrene using 7.5 grams of an aluminium trichloride catalyst at a temperature of 40.degree. C. The feed and catalyst were added to the reactor over 45 minutes and left for a further 15 minutes, after polymerisation the materials were hydrolysed, then neutralised with ammonium hydroxide, and stripped to remove volatiles.
The C.sub.5 olefin stream used had the following compositions
______________________________________ C.sub.5 Stream 1 2 3 4______________________________________C.sub.4 Olefins + diol -- -- -- 0.13-Me--butene-1 0.3 0.3 0.3 0.3Pentadiene 1.4 -- -- -- 0.03i-Pentane 2.5 2.6 2.75 2.2Pentene-1 2.3 2.3 2.45 1.92-Me--butene-1 6.3 6.2 6.5 5.0Isoprene 0.2 0.2 0.2 0.1N--pentane 8.7 8.2 8.4 6.3Pentene-2 trans 23.4 22.1 22.55 17.4Pentene-2 cis 8.5 8.0 8.0 6.62-Me--butene-2 27.7 26.0 26.2 20.5Pentadiene-1.3 tris & trans 0.3 0.3 0.3 0.1CPD 0.9 0.7 0.9 1.5Cyclopentene 12.9 13.6 13.1 13.2Cyclopentane 5.5 8.8 7.9 14.7C.sub.6 Olefins 5.7C.sub.6 Diolefins --C.sub.7 Olefins 0.3Benzene 0.5______________________________________
The materials used and the properties of the resins obtained are set out below.
__________________________________________________________________________EXAMPLE A B C D E F G__________________________________________________________________________Feed Composition (Gms)Feed 150 150 200 220 300 300 200C.sub.5 Olefins 350 350 300 280 200 200 300 Stream 4 Stream 4 Stream 4 Stream 3 Stream 3 Stream 1 Stream 1Styrene 25 25 25 35 35 50 50Olefins (gms) 292 292 269 280 242 242 297Diolefins (gms) 62 62 79 85.5 114 114 78Resin PropertiesSoftening Point (.degree.C.) 60 44.5 43 42 60 65 51Styrene Content (wt. %) 15.0 15.6 12.3 15.3 20.3 22.1 22.3Colour (Gardner) 7 7.5 6.5 6 6 5+ 6-Yield (wt. %) 27 36.6 34.3 37.1 32.5 39.0 35.0__________________________________________________________________________EXAMPLE H I J K L M__________________________________________________________________________Feed Composition (Gms)Feed 200 200 300 200 200 150C.sub.5 Olefins 350 300 200 300 300 350 Stream 2 Stream 1 Stream 1 Stream 2 Stream 2 Stream 3Styrene 35 50 70 70 70 70Olefins (gms) 328 297 242 288 288 317Diolefins (gms) 78 78 114 78 78 61Resin PropertiesSoftening Point (.degree.C.) 50 39 70 53 44 40Styrene Content (wt. %) 22.2 23.3 33.0 31.5 30.4 36.6Colour (Gardner) 6- 6+ 6- 6- 6 5Yield (wt. %) 31.5 43 44 38.6 42 42.7__________________________________________________________________________
The resins were emulsified in an equal weight of water by the process of European Patent Application No. 83300001.1 using 5.5 parts of the commercially available emulsifier Atlox 3404FB and their properties as tackifiers for carboxylated styrene butadiene copolymer rubber lattices determined by mixing 100 parts of the resin emulsion with 100 parts of the latex commercially available from Polysar as D93-703 (known as PL-3703) and that available from Doverstrand as 97D40. The adhesive system so obtained was coated onto "Mylar" (Registered Trade Mark) film to give a covering of 25 grams/square metre and the 180.degree. peel strength, loop tack on metal and glass and the ball tack were measured as well as the shear on metal and the results compared with systems containing the commercially available Escorez 2101 aromatic modified C.sub.5 resin of softening point 90-95.degree. C. and the hydrogenated rosin commercially available as Staybelite ester 10 and the modified rosin commercially available as Snowhite 52 CF.
The results were as follows:
__________________________________________________________________________ COMPARATIVE TACKIFIER Esco- Stay- Sno- PRODUCT OF EXAMPLE rez belite white A B C D E F G H I J K L M 2101 Ester 52CF__________________________________________________________________________WITH DOVERSTRAND97040100.degree. Peel Strength 440 760 710 735 620 510 780 860 780 600 780 500 260 630 660 700(g/cm)Loop Tack metal 5.0 13.0 10.5 8.0 5.6 5.8 9.8 11.2 7.6 50 8.2 5.6 2.0 8.5 13.5 17(N/25 mm)Loop Tack glass 1.5 14.0 3.0 13.5 0 1.0 11.0 12.0 9.0 1.8 9.1 6.8 2.4(N/25 mm)Ball tack (cm) >20 5 >20 8 >20 >20 12.5 8 9 >20 >20 >20 16 >20 10 5.5Sheet on metal (hours) 0.4 0.5 0.4 0.3 1.5 1.2 1.1 0.7 0.8 2.0 0.8 0.7 0.4 2.1 1.0 0.3WITH POLYSARD93-703100.degree. Peel Strength 465 500 480 560 650 500 790 805 620(g/cm)Loop Tack metal 10.5 21 18.0 18.5 14 15.0 16 16 17(N/25 mm)Loop Tack glass 20 13.5 17.5 24 26 25 of 6 18 22(N/25 mm)Ball tack (cm) 1.5 2 1.5 1.5 2 1.5 >20 8.5 2.5Sheer on metal (hours) 0.35 0.2 0.20 0.35 0.5 0.25 1.2 2.0 0.15__________________________________________________________________________
For comparison the properties of the carboxylated lattices when used on their own were.
______________________________________ Doverstrand Polysar 970 40 D93 703______________________________________180.degree. C. Peel Strength g/cm 400 280Loop Tack Metal (N/25 cm) 7 3.4Loop Tack Glass (N/25 cm) 6 6.5Ball Tack (cm) 15 5.5Shear on Metal (hrs) >200 >200______________________________________
The migration characteristics of some of the adhesives were determined by storing samples in an oven at 70.degree. C. and 50% relative humidity for 3 weeks and making a visual examination after each week and rating the migration on a scale of 0 to 5, 0 being no migration and 5 the worst.
The results were as follows:
__________________________________________________________________________DOVERSTRAND POLYSAR D93-703 PlusAdhesive 970-40 Escorez Stabelite SnowhiteFormulation Plus D B C D F G H I 2101 Ester 10 52CF__________________________________________________________________________1 week stage 1 0 0 1 0 0 0 0 0 0 02 weeks stage 1 1 1 1 0 0 0 1 0 0 13 weeks stage 1 1 1 1 0 0 0 1 0 1__________________________________________________________________________
In a further example the ratio of latex to resin was varied using resins B and G with the following results.
__________________________________________________________________________Parts Resin B 50 100 150 50 100 150100 parts Latex POLYSAR D93 703 DOVERSTRAND 970 40__________________________________________________________________________180.degree. Peel Strength (g/cm) 780 500 550 730 600 560Loop Tack on Metal (10/25 mm) 8.5 21 28 9.5 12.5 9.5Glass (10/25 mm) 12.5 23 26 8.5 12 8Ball Tack (cm) 2.5 1.5 1-1.5 3.5 5 16Shear PSTC-7 (Hours) 1.35 0.20 0.10 1.05 0.50 0.35Parts of Resin G 50 100Parts Polysar D93-703 100 100180.degree. Peel Strength (g/cm) 560 660Loop Tack on Metal (N/25 mm) 12.5 15.5Glass (N/25 mm) 13 2.3Ball Tack (cm) 2.5 0.40__________________________________________________________________________

Tackifiers and their use in pressure sensitive adhesives

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

Foreign Referenced Citations (1)