Patent Application
20190062871
The present disclosure relates generally to the production of metallic materials and, more particularly, to the production of high strength metallic alloys, such as aluminum alloys, by the addition of grain refiners to a metal alloy for grain refinement and crack suppression during additive manufacturing.
Additive manufacturing is utilized to fabricate 3-dimensional (3D) parts or products by adding layer-upon-layer of material. Additive manufacturing systems utilize 3D-modeling (Computer-Aided Design or CAD) software, computer-controlled additive-manufacturing equipment, and raw materials (feed stocks) in powder, wire or liquid form. Additive manufacturing encompasses a wide variety of technologies and incorporates a wide variety of techniques, such as, for example, laser freeform manufacturing (LFM), laser deposition (LD), direct metal deposition (DMD), laser metal deposition, laser additive manufacturing, laser engineered net shaping (LENS), stereolithography (SLA), selective laser sintering (SLS), fused deposition modeling (FDM), multi jet modeling (MJM), 3D printing, rapid prototyping, direct digital manufacturing, layered manufacturing, and additive fabrication. Moreover, a variety of raw materials may be used in additive manufacturing to create products. Examples of such materials include plastics, metals, concrete, and glass.
One example of an additive-manufacturing system is a laser additive-manufacturing system. Laser additive manufacturing includes spraying or otherwise injecting a powder or a liquid into a focused beam of a high-power laser or nexus of a plurality of high-powered lasers under controlled atmospheric conditions, thereby creating a weld pool. The resulting deposits may then be used to build or repair articles for a wide variety of applications.
Additive manufacturing is a process reliant on solidification dynamics similarly to welds and castings. However, additive manufacturing of high strength aluminum alloys (e.g., 2000 and 7000 series aluminum alloys) has previously resulted in solidification cracking. For example, due to crack susceptibility during solidification, conventional aluminum alloys for wrought products are unsuitable for the additive manufacturing process, in particular for laser directed energy based processes. Cast aluminum alloy grades fair better, but generally have low strengths and thus are not usable for many applications requiring high strength. For low strength alloys addition of silicon prevents cracking but this is not a suitable approach for aerospace HS aluminum. Accordingly, improved high strength alloys for use in additive manufacturing would be a welcome addition to the art.
In an example, there is a method for modifying a metal alloy for use in additive manufacturing, comprising: providing a metal alloy; providing at least one grain refiner; forming a melt pool comprising the at least one metal alloy and the at least one grain refiner; and solidifying at least a portion the melt pool to form a modified alloy.
In another example, there is an article comprising a modified alloy, wherein the modified alloy is formed according to the method for modifying the metal alloy for use in additive manufacturing. The method comprising: providing a metal alloy; providing at least one grain refiner; forming a melt pool comprising the at least one metal alloy and the at least one grain refiner; and solidifying at least a portion of the melt pool to form the modified alloy.
In another example, there is a powder for use in additive manufacturing, comprising: a plurality of particles. The plurality of particles comprises metal alloy particles comprising at least one metal alloy and grain refiner particles comprising at least one grain refiner. The plurality of particles comprises up to about 5% by weight of the grain refiner particles.
Advantages of the examples will be set forth in part in the description which follows, and in part will be understood from the description, or may be learned by practice of the examples. The advantages will be realized and attained by means of the elements and combinations particularly pointed out in the appended claims.
It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the examples, as claimed.
The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate examples of the present teachings and together with the description, serve to explain the principles of the disclosure.
Reference will now be made in detail to the present examples, examples of which are illustrated in the accompanying drawings. Wherever possible, the same reference numbers will be used throughout the drawings to refer to the same or like parts.
Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the examples are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contains certain errors necessarily resulting from the standard deviation found in their respective testing measurements. Moreover, all ranges disclosed herein are to be understood to encompass any and all sub-ranges subsumed therein. For example, a range of “less than 10” may include any and all sub-ranges between (and including) the minimum value of zero and the maximum value of 10, that is, any and all sub-ranges having a minimum value of equal to or greater than zero and a maximum value of equal to or less than 10, e.g., 1 to 5. In certain cases, the numerical values as stated for the parameter may take on negative values. In this case, the example value of range stated as “less than 10” may assume negative values, e.g. −1, −2, −3, −10, −20, −30, etc.
The following examples are described for illustrative purposes only with reference to the Figures. Those of skill in the art will appreciate that the following description is exemplary in nature, and that various modifications to the parameters set forth herein could be made without departing from the scope of the present examples. It is intended that the specification and examples be considered as exemplary only. The various examples are not necessarily mutually exclusive, as some examples may be combined with one or more other examples to form new examples. It will be understood that the structures depicted in the figures may include additional features not depicted for simplicity, while depicted structures may be removed or modified.
High strength alloy may be utilized for forming a structural component which may be incorporated in a larger structure such as a land-based vehicle, an aircraft, a space vehicle, or a waterborne vehicle. The high strength alloy may be formed by additive manufacturing. As described above, however, many conventional alloys cannot be used for additive manufacturing processes due to cracking upon solidification. As described herein, addition of intermetallic and/or ceramic particles (e.g., grain refiners) to a metal alloy melt can lead to refinement of the primary solidified grain structure. Thus, the addition of grain refiners to metal alloys allows such alloys having poor solidification characteristics to be adapted for usability in additive manufacturing processes, for example, as used in manufacturing and service methods of manned or unmanned vehicles, including for aircraft.
Generally, aspects of the present disclosure include modification of metal alloys, including conventional or “off-the-shelf” alloy, for use in additive manufacturing. Accordingly, modified alloy compositions (hereafter “modified alloy”) may be formed according to various implementations.
In an implementation, the modification of a metal alloy is performed in situ in that a melt pool comprising feedstock raw materials (e.g., at least one metal alloy and at least one grain refiner) is formed contemporaneously with the depositing of at least a portion of the melt pool in a predetermined pattern and the forming of the modified alloy. For example, a modified alloy may be formed via a method executed by an additive manufacturing system such as additive manufacturing system 200 of
An implementation of a method for the in situ modifying of a metal alloy is depicted in the flow-chart 100 of
In an implementation, the grain refiner and metal alloy are provided as separate powder feedstocks that are combined by the additive manufacturing system to form a mixed feedstock. The mixed feedstock may comprise less than or equal to about 5% by weight of the grain refiner. In an example of a mixed feedstock, a powder comprising a plurality of particles is provided. The plurality of particles comprise metal alloy particles and grain refiner particles. The grain refiner particles comprise up to about 5% by weight of the plurality of particles in the powder. Other amounts of grain refiner particles in the mixed feedstock may include in the range of between from about 1.5% to about 3.5% of the plurality of particles, including from about 2% to about 3% by weight of the plurality of particles. The additive manufacturing system forms a melt pool comprising the grain refiner and the metal alloy and deposits at least a portion of the melt pool in a predetermined pattern as part of an additive manufacturing process 102. For example, the additive manufacturing system may expose the combined grain refiner and metal alloy feedstocks to an energy source that melts at least the metal alloy to form a metal alloy melt pool comprising the at least one grain refiner and the at least one metal alloy melt pool at 105. In an example, at least some of the grain refiner(s) combined with the metal alloy(s) mix in the metal alloy melt at 105. The melt pool is then deposited in a predetermined pattern at 107 via, for example, additive manufacturing. In an example, the additive manufacturing system deposits the melt pool in a predetermined pattern, layer-by-layer, to form a 3-Dimensional (3D) article, between surfaces to form a weld-like joint, or as an ingot. As the deposited melt pool cools, it solidifies, for example, by eutectic or peritectic reaction at the interface between the mixed grain refiner constituent elements and metal alloy melt, forming a modified alloy. The resulting modified alloy comprises grain refiners in an amount of equal to or less than 5% by weight of the modified alloy.
While the method of flow-chart 100 shows that the at least one grain refiner and the at least one metal alloy are separately provided to an additive manufacturing system, for example, as separate feedstocks, other implementations are not so limited. For example, a method for in situ modifying a metal alloy depicted in the flow-chart 110 of
In an implementation, the grain refiners and metal alloys are available as separate powder feedstocks that are combined into a mixed feedstock prior to being introduced to an additive manufacturing system. The mixed feedstock may, therefore, be a powder for use in additive manufacturing comprising a plurality of particles. The plurality of particles comprises metal alloy particles comprising at least one metal alloy and grain refiner particles comprising at least one grain refiner. The plurality of particles may comprise less than or equal to about 5% by weight of the grain refiner particles. The additive manufacturing system forms a melt pool comprising the grain refiner and the metal alloy contemporaneously with depositing at least a portion of the melt pool in a predetermined pattern and the forming of the modified alloy as part of an additive manufacturing process 102 as described above. A modified alloy comprising grain refiners, for example, in an amount of equal to or less than 5% by weight of the modified alloy, may be formed in situ via the additive manufacturing process 102 as described above.
As described above, many conventional alloys are not available for use in additive manufacturing due to, among other reasons, cracking susceptibility. Accordingly, the methods described herein may be used for forming a modified alloy that is usable in additive manufacturing applications. For example, a modified alloy comprising grain refiners may be used as the raw material feedstock for forming 3D articles or weld-like joints between surfaces via additive manufacturing. In an implementation, the modified alloy formed according to the methods depicted in flow-charts 100 and 110 of
In an implementation, the modified alloy provided at 111′ is provided as an ingot of the material; i.e., a modified alloy ingot. The modified alloy ingot may be subject to an optional processing at 104 in an appropriate system to form the modified alloy feedstock at 113 prior to being introduced to an additive manufacturing system. For example, an ingot comprising the modified alloy provided at 111′ may be subject to processing by a gas atomizer into the form of a powder. However, an additive manufacturing system may require the feedstock to be processed into another form appropriate to the needs of the additive manufacturing system of choice.
Similar to the methods depicted in flow-charts 100 and 110 of
Additive manufacturing may be performed by powder bed, powder fed, wire fed, and binder jet systems. Additive manufacturing methods may include laser freeform manufacturing (LFM), directed energy deposition, laser cladding, laser deposition (LD), direct metal deposition (DMD), laser metal deposition (LMD) including laser melting deposition-powder (LMD-p) and laser melting deposition-wire (LMD-w), laser additive manufacturing, laser engineered net shaping (LENS), stereolithography (SLA), selective laser sintering (SLS), selective layer melting (SLM), fused deposition modeling (FDM), electron beam melting (EBM), Laser Powder Bed Fusion (L-PBF), and binder jet printing.
Turning now to
In one implementation, the forming of the melt pool according to the methods described herein comprises exposing at least a portion of the metal alloy to a beam of focused energy. Examples of focused energy include electron beam, laser beam, and thermal radiation. For example, a laser source generates a laser beam and transmits it to one or more laser outputs of an additive-manufacturing head for emission. The laser beam, emitted from the one or more laser outputs, is concentrated into a nexus or convergence. Accordingly, the deposition device 201 may include an energy source (not shown) for emitting to the feedstock provided by the material supply. In an example, the deposition device 201 provides a focused beam of energy from the energy source to form a melt pool from the feedstock provided by the material supply 203, 203′. In an implementation, raw material is released from the one or more material outputs described above and enters the nexus or convergence of the one or more laser outputs, where at least a portion of material is melted to form a melt pool.
The melt pool is deposited layer-by-layer. That is, deposited layers 205 are formed on base tray 209. The deposited layers 205 are deposited in a pre-determined pattern and cool as a modified-alloy in the form of an article 207. In other words, as the additive-manufacturing head advances relative to the product being formed, the melted material of the melt pool begins to cool and harden (i.e., solidify) once the material is out of the weld pool, for example, upon being deposited onto a substrate or onto layers of previously deposited melt pool material.
To assist forming layers 205 on the base tray 209, the deposition device 201 may translate along a lateral stage 211, and the base tray 209 may translate along an axial, or vertical, stage 213. The system 200 optionally comprises a fabrication chamber 215 which encloses the deposition device 201, the base tray 209, and the layers 205 as formed.
The deposition device 201 may be configured to move away from the base tray 209 and the in-process part 207, leaving a clear path for non-contact. Additionally or alternatively, the deposition device 201 may afford a clear path to a portion of the in-process article 207 and may move relative to the in-process article 207 to sequentially expose all portions of the in-process article 207. The whole additive manufacturing system 200 is controlled by a controller 217, which is optionally a computer 219. The controller 217 coordinates the operation of the deposition device 201, and may be programmed to perform any of the manufacturing methods 100, 110, 120 previously described.
Additive manufacturing devices may be available or modifiable to accomplish grain refinement in the same chamber as additive manufacturing. Grain refinement may occur while adding grain refiners to a melt pool of the metal alloy matrix. Some additive manufacturing processes involve melting feed stock to add material. Melting may include exposure to electron beam, plasma, electric arc, laser energy, touch flame, etc.
The type and chemistry of the at least one metal alloy may vary. For example, the composition of the metal alloy may include mixtures of microcrystalline elemental and/or prealloyed and/or partially alloyed powder that may be commercially available. Examples of the metal alloy comprise aluminum, aluminum alloy, iron, iron alloy, steel, steel alloy, nickel, nickel-based alloy, copper, copper-based alloy, beryllium, beryllium-based alloy, cobalt, cobalt-based alloy, molybdenum, molybdenum-based alloy, complex concentrated alloys, titanium, titanium-alloy, tungsten, and tungsten-based alloy and any other alloy or combination thereof
Examples of aluminum alloy comprise alloys in the 2XXX, 5XXX, 6XXX, 7XXX, or 8XXX series. In an implementation, the metal alloy comprises an aluminum alloy. The aluminum alloy may be selected from the cast-grade aluminum alloys (e.g., A201). The aluminum alloys may comprise one or more of Al, Cu, Si, Mg and Zn. For example, the aluminum alloy may be selected from 2000 series aluminum alloys such as 2014, 2024, and/or 2099 aluminum alloy, or from 7000 series aluminum alloys, such as 7007, 7047, 7050, 7055, and/or 7150 aluminum alloy.
The at least one metal alloy may comprise more than one metal alloy, for example, a first metal alloy, a second metal alloy, a third metal alloy up to an nth metal alloy. In the case of a plurality of metal alloys, the different metal alloys may be provided together or separately from one another. The plurality of metal alloys may comprise different metal alloys. In an example, a plurality of different metal alloys may be provided for the purpose of functionally grading articles formed via additive manufacturing. In an example, a plurality of different metal alloys are provided as feed stock in powder form to a powder feed system and processed according to pre-determined processing requirements for forming functionally graded articles. In an example, a plurality of different metal alloys are provided as feed stock in wire form to a wire feed system and processed according to pre-determined processing requirements for forming functionally graded articles.
The metal alloy may be provided in the form of a wire, powder or liquid comprising the metal alloy, or a combination thereof. Metal alloy wire may be provided in any size or combination of sizes without limitation. In an example, metal alloy wire may be provided in up to ⅛-inch size. Powder may comprise metal alloy particles. The metal alloy particles may be provided in any size or combination of sizes, without limitation. For example, the raw metal alloy may be in powder form comprising particles in a size of from about 10 microns to about 250 microns, such as from about 45 microns to about 105 microns, including from about 10 microns to about 45 microns. However, the raw metal alloy powder may be provided in sizes smaller than 10 microns or larger than 250 microns. The metal alloy particles may be provided in any shape or combination of shapes, without limitation. For example, the raw metal alloy particles may be in powder form comprising particles of spherical, sponge, flake and the like.
As described above, addition of grain refiner(s) can improve the crack susceptibility of metal alloys. Accordingly, the addition of grain refiners can adapt conventional metal alloys for additive manufacturing processes. Because the resulting modified alloys can be formed in situ, this allows for rapid retrofitting of the conventional metal alloys on an as-needed basis.
The type and chemistry of the at least one grain refiner may vary. For example, the composition of the at least one grain refiner may include any one or more grain refiner that does not become part of a solid solution formed by heat treating of a matrix alloy. The at least one grain refiner may be selected from intermetallic and/or ceramic grain refiner, for example, grain refiner comprising one or more of titanium, aluminum, carbon, boron or mixtures thereof. Examples of grain refiner include, but are not limited to, TiB2, TiC, TiAl, AlB2 and mixtures thereof. Other grain refiner comprising titanium may be used depending on the desired properties of the final alloy.
In an example, grain refiner comprise up to about 5% by weight of the modified alloy. Other amounts of grain refiner in the modified alloy are possible such as in the range of between from about 1.5% to about 3.5% by weight of the modified alloy, including from about 2% to about 3% by weight of the modified alloy formed according to the methods described above. In an example, depending on the grain refiner used, the amount of grain refiner in the modified alloy is not less than 0.1% as such smaller amounts may not allow the grain refiner to serve the purpose of a nucleate in an additive manufacturing process for forming the modified alloy. In an example, the amount of grain refiner in the modified alloy does not exceed 5% by weight of the modified alloy as such larger amounts could cause deleterious effects in the modified alloy formed by additive manufacturing, such as from brittle/hard intermetallic phases to poor mechanical performance.
In an implementation, the at least one grain refiner is provided in powder form, in wire form or both depending on the additive manufacturing system in which a modified metal alloy is formed. In an example, a mixed feedstock in powder form comprises a plurality of particles. The plurality of particles comprises metal alloy particles and grain refiner particles. The grain refiner particles comprise up to about 5% by weight of the plurality of particles. Other amounts of grain refiner in the plurality of particles are possible such as in the range of between from about 1.5% to about 3.5% by weight of the plurality of particles, including from about 2% to about 3% by weight of the plurality of particles formed according to the methods described above. In an example, depending on the grain refiner used, the amount of grain refiner in the plurality of particles is not less than 0.1% by weight of the plurality of particles as such smaller amounts may not serve the purpose of a nucleate in an additive manufacturing process for forming a modified alloy from powder feedstock. In an example, the amount of grain refiner in the plurality of particles does not exceed 5% by weight of the plurality of particles as such larger amounts may cause deleterious effects in the modified alloy formed by additive manufacturing, such as from brittle/hard intermetallic phases to poor mechanical performance.
The modified alloy comprising grain refiners as described herein may have a greatly refined grain size relative to the grain size of the unmodified metal alloy. For example, the modified alloy may comprise an average grain size that is smaller, such as about an order of magnitude smaller, than the average grain size of the metal alloy.
Examples of the disclosure may be described in the context of an aircraft manufacturing and service method 300 as shown in
Each of the processes of method 300 may be performed or carried out by a system integrator, a third party, and/or an operator (e.g., a customer). For the purposes of this description, a system integrator may include without limitation any number of aircraft manufacturers and major-system subcontractors; a third party may include without limitation any number of vendors, subcontractors, and suppliers; and an operator may be an airline, leasing company, military entity, service organization, and so on.
As shown in
In this example, the aircraft 302 includes a fuselage 301 including wing assemblies 303, a tail assembly 305, and a landing assembly 307. The aircraft 302 further includes one or more propulsion units 309, a control system 311 (not visible), and a host of other systems and subsystems, such as those described above as high-level systems, that enable proper operation of the aircraft 302. In general, the various components and subsystems of the aircraft 302 may be of known construction and, for the sake of brevity, will not be described in detail herein.
Although the aircraft 302 shown in
Modified alloy(s) and method(s) for modifying alloy(s) described herein may be employed during any one or more of the stages of method 300. For example, components or subassemblies corresponding to component and subassembly manufacturing (block 308) may be fabricated or manufactured in a manner similar to components or subassemblies produced while aircraft 302 is in service (block 314). Also, one or more examples of the modified alloy(s), method(s) for modifying alloy(s), or combination thereof may be utilized during production stages (block 308 and block 310), for example, by substantially expediting assembly of or reducing the cost of aircraft 302. Similarly, one or more examples of the method(s) for modifying alloy(s) may be utilized, for example and without limitation, while aircraft 302 is in service (block 314) and/or during maintenance and service (block 316).
While the examples have been illustrated respect to one or more implementations, alterations and/or modifications may be made to the illustrated examples without departing from the spirit and scope of the appended claims. In addition, while a particular feature of the examples may have been disclosed with respect to only one of several implementations, such feature may be combined with one or more other features of the other implementations as may be desired and advantageous for any given or particular function. For example, it will be appreciated that while the process is described as a series of acts or events, the present teachings are not limited by the ordering of such acts or events. Some acts may occur in different orders and/or concurrently with other acts or events apart from those described herein. Also, not all process stages may be required to implement a methodology in accordance with one or more aspects or embodiments of the present teachings. It will be appreciated that structural components and/or processing stages may be added or existing structural components and/or processing stages may be removed or modified.
Further, in the discussion and claims herein, the term “on” used with respect to two materials, one “on” the other, means at least some contact between the materials, while “over” means the materials are in proximity, but possibly with one or more additional intervening materials such that contact is possible but not required. Neither “on” nor “over” implies any directionality as used herein. The term “conformal” describes a coating material in which angles of the underlying material are preserved by the conformal material. The term “about” indicates that the value listed may be somewhat altered, as long as the alteration does not result in nonconformance of the process or structure to the illustrated embodiment. Finally, “exemplary” indicates the description is used as an example, rather than implying that it is an ideal.
Furthermore, to the extent that the terms “including”, “includes”, “having”, “has”, “with”, or variants thereof are used in either the detailed description and the claims, such terms are intended to be inclusive in a manner similar to the term “comprising.” As used herein, the phrase “one or more of”, for example, A, B, and C means any of the following: either A, B, or C alone; or combinations of two, such as A and B, B and C, and A and C; or combinations of three A, B and C.
Other examples will be apparent to those skilled in the art from consideration of the specification and practice of the descriptions disclosed herein. It is intended that the specification and examples be considered as exemplary only, with a true scope and spirit of the examples being indicated by the following claims.