Patent Application
20240181503
Additive fabrication, e.g. 3-dimensional (3D) printing, provides techniques for fabricating objects, typically by causing portions of a building material to solidify at specific locations. Additive fabrication techniques may include techniques categorized as vat photopolymerization, powder bed fusion, binder jetting, material jetting, sheet lamination, material extrusion, directed energy deposition, or combinations thereof. Many additive fabrication techniques build parts by forming successive layers, which are typically cross-sections of the desired object. Typically each layer is formed such that it adheres to either a previously formed layer or a substrate upon which the part is built.
In some additive fabrication technologies, parts may be fabricated by combining portions of a powder or other granular material to create fully dense parts. For example, additive fabrication techniques known as binder jetting may selectively apply a liquid to portions of a layer of powder, then a subsequent layer of powder may be deposited over the first layer, and additional liquid applied to additional portions of the new layer, and so on. At the end of such a process, the parts are disposed within a volume of the powder from which the parts must be separated.
According to some aspects, a method is provided for extracting one or more additively fabricated parts from a powder bed comprising a powder and the one or more additively fabricated parts, the method comprising inserting at least part of the powder bed into a chamber, the chamber comprising one or more inlets and one or more outlets, forming a hermetic seal around the at least part of the powder bed, directing, using one or more nozzles, one or more jets of gas onto a surface of the powder bed within the chamber, and producing, concurrently with said directing the one or more jets of gas onto the surface of the powder, a continuous flow of gas through the chamber from the one or more inlets to the one or more outlets such that powder from the powder bed is transported through at least some of the one or more outlets.
According to some aspects, an apparatus is provided for extracting one or more additively fabricated parts from a powder bed comprising a powder and the one or more additively fabricated parts, the apparatus comprising a chamber configured to receive a build box containing the powder bed and configured to form a hermetic seal around at least part of the build box such that a surface of the powder bed may be exposed within the chamber, the chamber comprising one or more nozzles each configured to direct a jet of gas onto the surface of the powder bed, one or more inlets, one or more outlets, and at least one pressure source coupled to the one or more inlets and/or to the one or more outlets and configured to create a pressure differential between the one or more inlets and the one or more outlets.
According to some aspects, a method is provided of removing powder from one or more surfaces of an additively fabricated part, the method comprising directing a plurality of solid particles onto the one or more surfaces of the additively fabricated part, the additively fabricated part comprising bound metal powder and having unbound metal powder on its surface, such that collisions between the solid particles and the one or more surfaces dislodge at least some of the unbound metal powder from the surface of the additively fabricated part, and at least some of the dislodged metal powder is carried away from the additively fabricated part by gas produced through sublimation of the solid particles.
According to some aspects, an apparatus is provided for removing powder from one or more surfaces of an additively fabricated part comprising bound metal powder and having unbound metal powder on its surface, the apparatus comprising a mounting structure configured to hold the additively fabricated part, one or more nozzles configured to receive a source material and to emit the source material in a mixture of gaseous and solid states onto one or more surfaces of the additively fabricated part.
The foregoing apparatus and method embodiments may be implemented with any suitable combination of aspects, features, and acts described above or in further detail below. These and other aspects, embodiments, and features of the present teachings can be more fully understood from the following description in conjunction with the accompanying drawings.
Various aspects and embodiments will be described with reference to the following figures. It should be appreciated that the figures are not necessarily drawn to scale. In the drawings, each identical or nearly identical component that is illustrated in various figures is represented by a like numeral. For purposes of clarity, not every component may be labeled in every drawing.
As discussed above, some additive manufacturing techniques fabricate parts from and within a granular material such as a powder. One example is binder jetting, in which parts are formed by applying a liquid (e.g., a binder) to regions of successive layers of powder, thereby producing parts (which are ‘bound’ regions of the powder) within a volume of unbound powder. Such parts are often referred to as “green” parts since they must undergo subsequent processing, such as sintering, to produce a final part. Other illustrative additive fabrication techniques that fabricate parts from a powder include direct laser melting, direct metal laser sintering, or selective laser sintering, in which regions of successive layers of a material (e.g., metal, nylon) are melted through application of directed energy.
Irrespective of how parts are formed from a powder or other granular material, subsequent to the additive fabrication process these parts are accessed by separating the parts from the material. This process of retrieving parts from a granular material in which the parts are formed is referred to herein as “depowdering,” although it will be appreciated that techniques described herein are not limited to use cases in which the additional material comprises or consists of a powder. As such, while the discussion below may focus primarily on separating parts from a powder, it will be appreciated that any discussion of depowdering may also apply to separating additively fabricated parts from other granular materials.
Depowdering is frequently a laborious process due to the fine nature of the powder. Handling of the powder may cause a great deal of mess and, depending on the powder material, may also present safety concerns due to inhalation or flammability. Typically, depowdering is performed in a manual process of excavation that utilizes vacuum hoses and brushes to separate the parts from the powder. This process can take a great deal of time and in cases where the parts are fragile, can result in damage to the parts during excavation. Moreover, many powders used for additive fabrication, such as metal and/or ceramic powders, may exhibit low flowability which makes moving particles of the powder difficult due to the tendency of the powder to “clump” rather than flow away from the additively fabricated parts.
While, as discussed above, there are multiple additive fabrication technologies for which depowdering is performed, the process of depowdering may not be equally straightforward for each of these technologies. For instance, direct laser melting may produce metal parts during additive fabrication so that, prior to depowdering, the parts are embedded within a metal powder. Since the parts are solid metal, there is typically not a significant risk of damage to the parts during depowdering and so a wide range of simple techniques may be effective at separating the parts from the powder. In contrast, green parts produced in binder jetting comprise regions of bound powder held together by a liquid and may be considerably more fragile than parts produced by direct laser melting. Consequently, depowdering approaches that are effective for direct laser melting or selective laser sintering may not be suitable for parts produced through binder jetting since they may cause damage to the parts.
The inventors have recognized and appreciated techniques for depowdering that separate powder from parts by directing gas onto, or near to, the powder. The approaches described herein generally mobilize the powder and separate it from the parts by utilizing the fact that powder is lighter and more movable than the parts embedded within it. While some green parts, such as green parts produced by binder jetting, may be fragile with respect to scraping or impacts, such parts may nonetheless be resistant to damage from directed gas, even if directed at a high pressure. Many of the techniques described herein for depowdering through directed application of gas may be automated, as discussed further below, thereby mitigating the above-described challenges associated with manual depowdering operations.
According to some embodiments, techniques described herein for depowdering parts through directed application of gas may be applied by a depowdering system that is separate from an additive fabrication device that fabricated the parts. This approach may provide advantages for throughput, since it may allow for an additive fabrication device to begin fabricating a second group of parts while a first group of parts is being depowdered. Moreover, in use cases in which additive fabrication takes more or less time than the subsequent depowdering step, multiple additive fabrication devices and/or depowdering systems may be employed to minimize downtime of the additive fabrication device(s) and depowdering system(s). For instance, in a simple case where additive fabrication takes half as long as depowdering, two depowdering systems could be operated in parallel so that the additive fabrication device and the two depowdering systems could be operated continuously to maximize throughput.
According to some embodiments, a depowdering system as described herein may be configured to receive a build box from an additive fabrication device and to perform depowdering on contents of the build box. As referred to herein, a “build box” includes any structure in which parts may be fabricated within a powder by an additive fabrication device, and that may be removed from the additive fabrication device subsequent to fabrication. In some embodiments, a depowdering system may be configured to receive a build box and to directly depowder parts within the build box while the parts are largely contained within the build box. In some embodiments, a depowdering system may be configured to receive a build box and to meter contents of the build box into or onto an apparatus within the depowdering system. In this case, the depowdering system may perform depowdering on successive subsections of the build box by metering a subsection, depowdering the subsection, metering another subsection, etc.
Irrespective of how a depowdering system may be configured to operate upon the contents of a build box, the depowdering system may be configured with a receptacle sized for the build box such that the build box can be removably mounted or otherwise removably attached to the depowdering system. Subsequent to depowdering, a build box may be removed from the depowdering system and reused for fabrication. At this stage in the process, the build box may, for instance, be empty or may contain only powder, depending on the particular type of depowdering operations performed as discussed below.
According to some embodiments, a depowdering system may comprise one or more nozzles configured to direct a stream of gas onto a powder and one or more sources of suction, such as vacuums. The nozzle(s) may dislodge, aerate and/or otherwise increase the flowability of regions of the powder, thereby improving the ability of the source(s) of suction to remove powder from said regions. As discussed above, many powders used for additive fabrication, such as metal and/or ceramic powders, may exhibit low flowability which makes moving particles of the powder difficult due to the tendency of the powder to “clump” rather than flow away from the additively fabricated parts. Similarly, such powders may resist separation when a source of suction is directed onto them. A depowdering system that includes one or more nozzles for directing a stream of gas onto the powder may, however, introduce gaps between particles of the powder sufficient to mitigate or overcome this resistance, leading to more ease in suctioning away the powder.
According to some embodiments, one or more nozzles configured to direct a stream of gas onto a powder may be co-located with one or more sources of suction so that both the nozzle(s) and the source(s) of suction are operating on the same region of powder. For instance, a nozzle and a source of suction may be adjacent to one another and configured to direct gas and provide suction to the same location via, for example, an angled nozzle and/or vacuum tube.
According to some embodiments, one or more nozzles configured to direct a stream of gas onto a powder and one or more sources of suction may be automatically controlled by a suitable robotic system, which may for instance include a gantry, one or more robotic arms, etc. In some embodiments, individual nozzles or sources of suction, or groups of nozzles and/or sources of suction, may be separately movable to desired locations so that powder may be removed from multiple regions of powder simultaneously. Instructions to automatically operate such a system may be generated in advance of depowdering and may be based upon known locations of parts within the powder as discussed further below.
According to some embodiments, a depowdering system may comprise a chamber with one or more inlets and one or more outlets that may be moved over a portion of powder so as to create a seal around the powder. A flow of gas may be produced within the chamber by creating a pressure differential across inlets and outlets of the chamber, thereby causing powder to be extracted from the chamber while leaving the parts within the chamber. In some use cases, the seal may be created around a build box so that portions of powder are removed from the build box through the one or more outlets of the chambers. In some use cases, the seal may be created around another structure onto which powder and parts have been deposited.
According to some embodiments, a depowdering system may comprise a chamber that includes one or more nozzles for directing a flow of gas into the chamber. As described above, a nozzle may dislodge, aerate and/or otherwise increase the flowability of regions of the powder, thereby improving the ability of the gas flowing through the chamber to carry away powder.
The above illustrative embodiments are examples of techniques in which depowdering operations are applied to parts embedded within powder. Generally, subsequent to excavation of such parts additional powder may still be adhered to the surface and additional depowdering may be necessary to produce a completely clean part. These two different types of depowdering are referred to herein as “coarse” and “fine” depowdering, wherein “coarse” depowdering broadly refers to excavating parts from powder and “fine” depowdering broadly refers to removing comparatively small amounts of powder from the surface of an excavated part. It will be appreciated that, the use of these terms notwithstanding, depowdering operations need not be rigidly categorized into purely coarse or purely fine depowdering operations. As such, these terms are used merely to aid description of the types of effects that may be produced by the techniques described herein, and should not be viewed as limiting.
According to some embodiments, a depowdering system may comprise a source of solid particles that may be directed at speed onto a part to dislodge surface powder from the part (as per the above, this may be considered an example of fine depowdering). In some cases, the solid particles may comprise a material that evaporates or sublimates at an ambient temperature (e.g., room temperature). The stream of solid particles may thereby collide with powder on the surface of a part, thereby dislodging powder from the part, and may additionally produce gas that carries away dislodged powder. One example of a suitable material is solid CO2 (dry ice).
Following below are more detailed descriptions of various concepts related to, and embodiments of, techniques for depowdering additively fabricated parts via gas flow. It should be appreciated that various aspects described herein may be implemented in any of numerous ways. Examples of specific implementations are provided herein for illustrative purposes only. In addition, the various aspects described in the embodiments below may be used alone or in any combination, and are not limited to the combinations explicitly described herein.
In the example of
As one non-limiting example of a suitable additive fabrication device 110, the additive fabrication device may include a material deposition mechanism which be operated to deposit source material onto a powder, and a print head which may be controlled to move across the powder to deliver liquid such as a binder onto the powder. In some cases, an additional device such as a roller may be operated to move over the deposited source material to spread the source material evenly over the surface. The print head may include one or more orifices through which a liquid (e.g., a binder) can be delivered from the print head to each layer of the source material. In certain embodiments, the print head can include one or more piezoelectric elements, and each piezoelectric element may be associated with a respective orifice and, in use, each piezoelectric element can be selectively actuated such that displacement of the piezoelectric element can expel liquid from the respective orifice.
In this illustrative embodiment of the additive fabrication device 110, the print head may be controlled (e.g., by computing device 105) to deliver liquid such as a binder onto a powder in predetermined two-dimensional patterns, with each pattern corresponding to a respective layer of a three-dimensional part. In this manner, the delivery of the binder may perform a printing operation in which the source material in each respective layer of the three-dimensional part is selectively joined along the predetermined two-dimensional layers. After each layer of the part is formed as described above, the platform may be moved down and a new layer of powder deposited, binder again applied to the new powder, etc. until the part has been formed.
In the example of
Post-processing system 130 may include one or more devices suitable for transforming an extracted green part into a final part, which may include one or more debinding devices and/or furnaces. In systems employing a binder jetting process, extracted green parts can undergo one or more debinding processes in the post-processing system 130 to remove all or a portion of the binder system from the parts. As such, post-processing system 130 may include a thermal debinding device, a supercritical fluid debinding device, a catalytic debinding device, a solvent debinding device, or combinations thereof. In some embodiments, post-processing system 130 may include a furnace. Extracted green parts may undergo sintering in the furnace such that particles of the powder (or other granular material) combine with one another to form a finished part. In some embodiments, a furnace may be configured to perform one or more debinding processes within the furnace while extracted green parts undergo sintering.
According to some embodiments, the production of parts by system 100 may be partially or fully automated. In particular, the system may be configured to move parts embedded within powder from the additive fabrication device 110 to the depowdering system 120, and/or may be configured to move parts from the depowdering system 120 to the post-processing system 130. Automated motion may comprise one or more robotics system and/or conveyor belts, which may be configured to move parts (or parts embedded within powder) between devices in system 100, which may include motion between the three stages 110, 120 and 130 depicted in
In some embodiments, the additive fabrication device 110 may fabricate parts within a build box, which may be automatically transferred from the additive fabrication device to the depowdering system 120. Depowdering system 120 may, as discussed above, be configured to receive a build box and to directly depowder parts within the build box while the parts are largely contained within the build box. In some embodiments, a depowdering system may be configured to receive a build box and to meter contents of the build box into or onto an apparatus within the depowdering system. In this case, the depowdering system may perform depowdering on successive subsections of the build box by metering a subsection, depowdering it, metering another subsection, etc.
According to some embodiments, automated movement as described above may be controlled by computing device 105. In the example of
According to some embodiments, computing device 105 may be configured to generate two-dimensional layers that may each comprise sections of an object. Instructions may then be generated from this layer data to be provided to additive fabrication device 110 that, when executed by the device, fabricates the layers and thereby fabricates the object. Such instructions may be communicated via a communication link 106, which may comprise any suitable wired and/or wireless communications connection. In some embodiments, a single housing may hold the computing device 105 and additive fabrication device 110 such that the link 106 is an internal link connecting two modules within the housing of the device.
According to some embodiments, computing device 105 may be configured to receive, access, or otherwise obtain instructions generated to cause the additive fabrication device 110 to fabricate one or more parts, and may execute said instructions, thereby causing the additive fabrication device to fabricate the one or more parts. For instance, the instructions may control one or more motors of the additive fabrication device 110 to move components of the device to deposit powder, deposit liquid binder onto a layer of the powder, etc.
According to some embodiments, computing device 105 may be configured to generate instructions that, when executed by the depowdering system 120, automatically performs depowdering operations, examples of which are described below. Such instructions may be communicated via a communication link 107, which may comprise any suitable wired and/or wireless communications connection. In some embodiments, a single housing may hold the computing device 105 and depowdering system 120 such that the link 107 is an internal link connecting two modules within the housing of a device of the system.
In some embodiments, instructions to be executed by the depowdering system 120 may be generated based on the geometry of parts to be fabricated (or that were fabricated) by the additive fabrication device 120. As discussed further below, certain depowdering techniques may be based on, or may be improved by, removing powder from locations having a known relative location to parts within the powder. In some cases, instructions to be executed by the depowdering system 120 may be generated based on the locations of parts within the powder bed of the additive fabrication device 110 (or the expected locations after fabrication). As such, instructions to cause the additive fabrication device 110 to fabricate one or more parts may be generated by the computing device 105 as part of the same operation in which instructions are generated to be executed by the depowdering system 120. For example, computing device 105 may perform computational operations to arrange one or more parts to be fabricated within a three-dimensional volume representing the build volume of the additive fabrication device. The computing device 105 may then perform slicing of the parts in the volume and generate instructions for the additive fabrication device 110 to form successive layers of the parts, and in addition, may also generate instructions to be executed by the depowdering system based on the location and geometry of the parts within the volume.
As discussed above, a depowdering system may be perform depowdering on contents of a build box, either by directly depowdering parts within the build box while the parts are largely contained within the build box, or by metering contents of the build box into or onto an apparatus within the depowdering system. As examples of these two types of approaches,
In each of the examples of
In the example of
In the example of
In the example of
In the example of
In the example of
In each of the examples of
In the example of
In the example of
According to some embodiments, depowdering system 300 may comprise multiple nozzles 310 and/or multiple vacuums 350. The nozzles and vacuums may be arranged and operated in any suitable way, including by operating pairs of a nozzle and a vacuum together, or by operating individual nozzles and vacuums independently. The number of nozzles in depowdering system 300 need not be equal to the number of vacuums in the system.
According to some embodiments, the nozzle 310 and vacuum 350 may each be individually controllable by depowdering system 300. In some cases, the depowdering system 300 may automatically direct nozzle 310 to locations of the powder bed based on known locations of parts within the powder bed. For instance, in the case of the powder bed being a portion of a build box, the depowdering system may operate the nozzle 310 by executing instructions that control motion of the nozzle and that were generated based on known locations of the parts within the build box.
According to some embodiments, the nozzle 310 and vacuum 350 may be automatically controlled at least in part based on feedback obtained during removal of powder from the powder bed. As one example, depowdering system 300 may include a computer vision system configured to identify parts or other features of the powder bed as powder is removed from the powder bed. The nozzle and/or vacuum may then be directed to particular locations on the powder bed based on information obtained by the computer vision system.
As shown in
In the example of
According to some embodiments, the ambient vacuum may be implemented as one or more sources of propelled gas, such as one or more blowers. For instance, one or more blowers may be coupled to an enclosure around the chamber, thereby pulling gas through the apertures in all the faces of the chamber. In the example of
According to some embodiments, the chamber 520 may be a build box. As discussed above, a build box may be installed within an additive fabrication device and parts fabricated within the build box, which may then be transferred to a depowdering system for automated removal of powder from the build box. In the example of
As shown in the example of
In the example of
In some embodiments, the combination nozzle and vacuum device 660 may be coupled to an automated gantry configured to move the device 660 along multiple axes. In some cases, the combination nozzle and vacuum device 660 may also be coupled to one or more rotational actuators to produce rotational movement of the device in addition to motion produced by the gantry. For instance, the gantry may produce motion along the x-axis and/or y-axis, whereas said rotational actuator(s) may be configured to rotate the device around the x-axis and/or y-axis. In some cases, a container holding powder bed 632 may be configured to be rotatable by the depowdering system to produce rotation of the powder bed relative to the combination nozzle and vacuum device 660. For instance, the gantry may produce motion along the x-axis and/or y-axis, whereas the container is configured to be rotated around the x-axis and/or y-axis.
According to some embodiments, the chamber 710 may be arranged to form a seal with a surface 745. Such a seal may increase the effectiveness of the powder removal process by ensuring that the gas in the chamber flows to the outlet 712 and not through any gaps between the chamber 710 and the surface 745. A seal between the chamber and a surface may be produced via any suitable sealing device or devices, including but not limited to crush seals, gaskets, rtv caulking material, o-ring seals, bulb seals, labyrinth seals, or combinations thereof.
According to some embodiments, the surface 745 may represent an exterior surface of a build box with the powder bed 732 being an exposed portion of the full powder bed contained within the build box. For instance,
According to some embodiments, the surface 745 may be a flat surface onto which the powder bed 732 has been deposited. For instance,
According to some embodiments, gas flow through the chamber 710 may be produced by generating an ambient gas pressure difference between the inlet 711 and outlet 712 via any suitable means. In some cases, inlet 711 may be coupled to an ambient pressure (e.g., the air) and outlet 712 coupled to a source of comparatively low pressure such as a vacuum. In some cases, outlet 712 may be coupled to an ambient pressure (e.g., the air) and inlet 711 coupled to a source of comparatively high pressure such as an air compressor pump or a source of compressed gas. In some cases, inlet 711 may be coupled to a source of comparatively high pressure and outlet 712 coupled to a source of comparatively low pressure. The gas pressure within the chamber during operation may be above or below atmospheric pressure. Sources of pressure may be operated continuously to produce a continuous flow of gas from the inlet to the outlet within chamber 710. According to some embodiments, during operation the chamber may comprise air, although any suitable gas may be conveyed through the chamber to cause powder from the chamber to escape through the outlet 712. As one non-limiting example, the inlet may be coupled to a high pressure source of compressed air, while the outlet is coupled to the ambient environments.
While, in the example of
According to some embodiments, the outlet 712 may be coupled to the inlet 711 of chamber 710. As such, the depowdering system may form a closed loop. In such cases, a source of moving gas, such as a blower, may be arranged within the chamber, inlet, and/or outlet to produce a pressure differential at some point within the closed loop and thereby produce circulation of gas (and powder) around the loop.
According to some embodiments, depowdering system 700 may optionally comprise one or more disruptors 720 which direct a flow of gas into the chamber and thereby disrupt powder within the powder bed 732. As described above, a flow of gas may dislodge, aerate and/or otherwise increase the flowability of regions of the powder, thereby improving the ability of the gas flowing through the chamber to carry away powder. Any of the nozzles described above in relation to
According to some embodiments, disruptor 720 may be coupled to a motion system, such as a gantry configured to direct the disruptor nozzle(s) (and/or direct gas flow from the nozzle(s)) onto desired locations on the powder bed. A nozzle in a disruptor may be configured to have an gas output profile of any desired type, including a jet, a cone, a square, etc. In some cases, the disruptor may be configured to be inserted into the powder bed 732 to aerate the powder as in the example of
According to some embodiments, depowdering system 700 may comprise one or more filtration systems coupled to the outlet 712 and configured to filter particles of the powder removed from the powder bed 732. For instance, the depowdering system 700 may include a cyclone separator coupled to the outlet 712. The filtration system may be arranged so that gas exiting the chamber through the outlet may pass through the filtration system while at least some of the particles of powder carried by the gas are captured by the filtration system.
In the example of
In the example of
In the example of
In the example of
In the example of
Moreover, in the example of
According to some embodiments, belts 1030 may be coupled to a source of vibration, such as one or more actuators, and vibrated during operation of the depowdering system 1000. Such vibration may cause powder from the powder bed to fall between belts of the belts 1030, even absent the motion of gas within the hood portion 1010. Operating the belts 1030 to vibrate may be performed at the same time as operating the sources of comparatively lower pressure coupled to outlets 1012 and 1022, or may be performed while either or both of said pressure sources are inactive.
According to some embodiments, since the depowdering system 1000 of
According to some embodiments, the belts 1030 may comprise an abrasion resistant material, such as, but not limited to, polytetrafluoroethylene (PTFE), a PTFE-coated substrate, glass reinforced PTFE, Delrin, polyamides, glass reinforced polyamides, polyurethane, urethane, ethylene propylene diene terpolymer (EPDM), nitrile, butyl rubber, thermoplastic elastomers, or combinations thereof. According to some embodiments, the belts 1030 may be configured with a cross-sectional shape that inhibits powder from resting on the belts. For instance, the belts may include a wedge-shaped upper surface such that there are no flat surfaces on which powder may reside. This may aid in avoiding powder build up on the belts, which may cause abrasion of the belt material over time.
In the example of
When the solid particles produced from the nozzle 1114 are incident upon the part 1120, they may dislodge unbound powder from the surface of the part due to momentum transfer from the solid particles and particles of the unbound particles. In addition, the high velocity stream of gas also produced from the nozzle may carry dislodged particles away from the part.
According to some embodiments, the solid particles may sublimate or evaporate at an ambient temperature of the depowdering system 1100. Sublimation of the particles may have a benefit of leaving no contaminating material on the surface of part 1120 which may occur with blasting of other types of media. In the example of solid particles of CO2 for instance, solid CO2 sublimates at room temperature, such that operating the depowdering system 1100 in a room temperature environment may cause all of the solid particles produced from the nozzle to sublimate to gas at some time subsequent to being output from the nozzle 1114.
In the example of
According to some embodiments, mount 1125 may be configured to automatically move part 1120. The mount 1125 may be coupled to and/or may comprise one or more actuators that may be operated to move (translate and/or rotate) the part 1120. Such motion may be continuous while the source of solid particles 1110 directs solid particles onto part 1120, and/or may be periodic (e.g., the part may be held stationary while the source of solid particles 1110 directs solid particles onto part 1120, then moved to a new location/orientation, followed by additional direction of solid particles, etc.).
According to some embodiments, the mount 1125 may comprise elastic material to apply force to the part 1120 when the part is held in the mount. For instance, the mount may comprise a mesh or web of elastic material that stretches around the part 1120 when the part is held in the mount, and thereby applies a force to the part. As discussed above, the 1120 may have a complex shape and may be fragile. As such, a compliant material such as elastic may enable the mount to apply various magnitudes of forces to hold a wide range of parts yet without applying a high-enough force to damage such parts.
According to some embodiments, mount 1125 may be configured to magnetically attach to part 1120. Since the part 1120 may comprise a bound metal powder, a magnet may produce a force with respect to the part when placed in proximity to the part. As one example, a magnet may be attached to a piston within a cylinder. The part may be placed on one end of the cylinder and the magnet moved toward that end by actuating the piston and thereby magnetically holding the part against the cylinder and/or the magnet. In some cases, the walls of the cylinder may be sufficiently thick (e.g., thicker than the magnetic field lines of the magnet) so that the part may only be successfully held at the end of the cylinder. In some cases, the magnet may be operated to contact the part when holding the part. Alternatively, the magnet may be attached to a low-friction material (e.g., a thin piece of plastic) that contacts the magnet and the part when the mount is holding the part to ease separation of the part from the mount subsequent to depowdering.
According to some embodiments, the depowdering system 1110 may operate nozzle 1114 by moving the nozzle to direct solid particles output from the nozzle in different directions. The nozzle 1114 may be coupled to and/or may comprise one or more actuators that may be operated by the depowdering system 1110 to move (translate and/or rotate) the nozzle. Operation of the actuator(s) to move the nozzle may be performed continuously (e.g., scanning a path over the surface of the part 1120), and/or may be directed to a plurality of desired locations on the surface of the part 1120 in turn. In the case of operating the nozzle 1114 to desired locations on the surface of part 1120, such operation may be based upon the geometry of the part. For instance, certain surface shapes may tend to retain unbound powder more than other shapes. The depowdering system 1100 may be programmed to operate automatically based on such geometry and accordingly direct solid particles onto some surface regions of the part 1120 to a greater extent than other regions based on the geometry. As discussed above, such programming may be performed when slicing a model for additive fabrication or may be independently generated by the depowdering system 1100.
According to some embodiments, solid particles directed onto the part 1120 may produce liquid on the surface of the part. In some cases, the liquid may include a liquid form of the solid particles, with the solid particles having melted either on the surface of the part or during motion from the nozzle 1114 to the part 1120. In some cases, the liquid may alternatively or additionally include condensed gas from the ambient environment which may condense onto the part 1120 due to the temperature of the solid particles and/or stream of gas output from the nozzle 1114 being at a lower temperature than the ambient environment. For example, when the depowdering system 1100 is operated in an air environment, water vapor may condense onto the part 1120 when the solid particles and/or stream of gas output from the nozzle 1114 is colder than the ambient temperature.
According to some embodiments, production of liquid on the surface of part 1120 may be mitigated or avoided by utilizing a source material for the solid particles that sublimates in the ambient environment of depowdering system 1100 (thereby avoiding a liquid phase), and/or by operating the depowdering system 1100 in an inert environment that will not produce any condensation. As an example of the latter, the depowdering system 1100 may be operated within a chamber filled with an inert gas, such as argon.
In the context of
In the example of
In some embodiments, a depowdering system as shown in
In the example of
In some embodiments, nozzle 1114 of depowdering system 1100 shown in
In the example of
Nozzle 1430 shown in
An illustrative implementation of a computer system 1600 that may be used to perform any of the techniques described above is shown in
In connection with techniques described herein, code used to, for example, generate instructions that, when executed, cause an additive fabrication device to fabricate one or more parts, cause a depowdering system to automatically perform depowdering operations (e.g., metering a powder bed, activating/deactivating a pressure source, etc.) may be stored on one or more computer-readable storage media of computer system 1600. Processor 1610 may execute any such code to perform any of the above-described techniques as described herein. Any other software, programs or instructions described herein may also be stored and executed by computer system 1600. It will be appreciated that computer code may be applied to any aspects of methods and techniques described herein. For example, computer code may be applied to interact with an operating system to transmit instructions to an additive fabrication device or depowdering system through conventional operating system processes.
The various methods or processes outlined herein may be coded as software that is executable on one or more processors that employ any one of a variety of operating systems or platforms. Additionally, such software may be written using any of numerous suitable programming languages and/or programming or scripting tools, and also may be compiled as executable machine language code or intermediate code that is executed on a virtual machine or a suitable framework.
In this respect, various inventive concepts may be embodied as at least one non-transitory computer readable storage medium (e.g., a computer memory, one or more floppy discs, compact discs, optical discs, magnetic tapes, flash memories, circuit configurations in Field Programmable Gate Arrays or other semiconductor devices, etc.) encoded with one or more programs that, when executed on one or more computers or other processors, implement the various embodiments of the present invention. The non-transitory computer-readable medium or media may be transportable, such that the program or programs stored thereon may be loaded onto any computer resource to implement various aspects of the present invention as discussed above.
The terms “program,” “software,” and/or “application” are used herein in a generic sense to refer to any type of computer code or set of computer-executable instructions that can be employed to program a computer or other processor to implement various aspects of embodiments as discussed above. Additionally, it should be appreciated that according to one aspect, one or more computer programs that when executed perform methods of the present invention need not reside on a single computer or processor, but may be distributed in a modular fashion among different computers or processors to implement various aspects of the present invention.
Computer-executable instructions may be in many forms, such as program modules, executed by one or more computers or other devices. Generally, program modules include routines, programs, objects, components, data structures, etc. that perform particular tasks or implement particular abstract data types. Typically, the functionality of the program modules may be combined or distributed as desired in various embodiments.
Also, data structures may be stored in non-transitory computer-readable storage media in any suitable form. Data structures may have fields that are related through location in the data structure. Such relationships may likewise be achieved by assigning storage for the fields with locations in a non-transitory computer-readable medium that convey relationship between the fields. However, any suitable mechanism may be used to establish relationships among information in fields of a data structure, including through the use of pointers, tags or other mechanisms that establish relationships among data elements.
Having thus described several aspects of at least one embodiment of this invention, it is to be appreciated that various alterations, modifications, and improvements will readily occur to those skilled in the art.
Such alterations, modifications, and improvements are intended to be part of this disclosure, and are intended to be within the spirit and scope of the invention. Further, though advantages of the present invention are indicated, it should be appreciated that not every embodiment of the technology described herein will include every described advantage. Some embodiments may not implement any features described as advantageous herein and in some instances one or more of the described features may be implemented to achieve further embodiments. Accordingly, the foregoing description and drawings are by way of example only.
The above-described embodiments of the technology described herein can be implemented in any of numerous ways. For example, the embodiments may be implemented using hardware, software or a combination thereof. When implemented in software, the software code can be executed on any suitable processor or collection of processors, whether provided in a single computer or distributed among multiple computers. Such processors may be implemented as integrated circuits, with one or more processors in an integrated circuit component, including commercially available integrated circuit components known in the art by names such as CPU chips, GPU chips, microprocessor, microcontroller, or co-processor. Alternatively, a processor may be implemented in custom circuitry, such as an ASIC, or semi-custom circuitry resulting from configuring a programmable logic device. As yet a further alternative, a processor may be a portion of a larger circuit or semiconductor device, whether commercially available, semi-custom or custom. As a specific example, some commercially available microprocessors have multiple cores such that one or a subset of those cores may constitute a processor. Though, a processor may be implemented using circuitry in any suitable format.
The above-described techniques may be embodied as a computer readable storage medium (or multiple computer readable media) (e.g., a computer memory, one or more floppy discs, compact discs (CD), optical discs, digital video disks (DVD), magnetic tapes, flash memories, circuit configurations in Field Programmable Gate Arrays or other semiconductor devices, or other tangible computer storage medium) encoded with one or more programs that, when executed on one or more computers or other processors, perform methods that implement the various embodiments of the invention discussed above. As is apparent from the foregoing examples, a computer readable storage medium may retain information for a sufficient time to provide computer-executable instructions in a non-transitory form. Such a computer readable storage medium or media can be transportable, such that the program or programs stored thereon can be loaded onto one or more different computers or other processors to implement various aspects of the present invention as discussed above. As used herein, the term “computer-readable storage medium” encompasses only a non-transitory computer-readable medium that can be considered to be a manufacture (i.e., article of manufacture) or a machine. Alternatively or additionally, the invention may be embodied as a computer readable medium other than a computer-readable storage medium, such as a propagating signal.
Various aspects of the present invention may be used alone, in combination, or in a variety of arrangements not specifically discussed in the embodiments described in the foregoing and is therefore not limited in its application to the details and arrangement of components set forth in the foregoing description or illustrated in the drawings. For example, aspects described in one embodiment may be combined in any manner with aspects described in other embodiments.
Also, the invention may be embodied as a method. The acts performed as part of the method may be ordered in any suitable way. Accordingly, embodiments may be constructed in which acts are performed in an order different than illustrated, which may include performing some acts simultaneously, even though shown as sequential acts in illustrative embodiments.
Further, some actions are described as taken by a “user.” It should be appreciated that a “user” need not be a single individual, and that in some embodiments, actions attributable to a “user” may be performed by a team of individuals and/or an individual in combination with computer-assisted tools or other mechanisms.
Use of ordinal terms such as “first,” “second,” “third,” etc., in the claims to modify a claim element does not by itself connote any priority, precedence, or order of one claim element over another or the temporal order in which acts of a method are performed, but are used merely as labels to distinguish one claim element having a certain name from another element having a same name (but for use of the ordinal term) to distinguish the claim elements.
The terms “approximately” and “about” may be used to mean within ±20% of a target value in some embodiments, within ±10% of a target value in some embodiments, within ±5% of a target value in some embodiments, and yet within ±2% of a target value in some embodiments. The terms “approximately” and “about” may include the target value. The term “substantially equal” may be used to refer to values that are within 20% of one another in some embodiments, within 10% of one another in some embodiments, within 5% of one another in some embodiments, and yet within 2% of one another in some embodiments.
Also, the phraseology and terminology used herein is for the purpose of description and should not be regarded as limiting. The use of “including,” “comprising,” or “having,” “containing,” “involving,” and variations thereof herein, is meant to encompass the items listed thereafter and equivalents thereof as well as additional items.
The present application is a Division of U.S. application Ser. No. 16/983,138, filed Aug. 3, 2020, which claims the benefit under 35 U.S.C. § 119(e) of U.S. Provisional Application No. 62/882,703, filed Aug. 5, 2019, which is hereby incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62882703 | Aug 2019 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16983138 | Aug 2020 | US |
| Child | 18441951 | US |