Patent Grant
10835920
The present application claims priority from Indian patent application 201811029355 filed on Aug. 3, 2018, the entirety of which is hereby incorporated by reference.
The present subject matter described herein, in general, relates to metal coatings; more specifically relates to coating the metal and other material substrates with swarf particles.
In the domain of surface engineering, there exist several techniques to develop surface coatings. One of the well-known coating processes is known as Thermal Spraying (TS). It may be noted that TS is an industrial coating process that consists of a heat source (flame or other) and a coating material in a powder or wire form that is melted into tiny droplets and then sprayed onto the surface at high speed. TS may facilitate in coating the surface as necessitated; however, it may require several costly hardware components (such as nozzle, gun and feedstock powder particles) and high skill for engineering applications. In addition to the above limitations, TS is very cumbersome and ineffective (most often not possible) technique to coat ceramics such as a glass surface.
Before the present system and method are described, it is to be understood that this application is not limited to the particular machine or an apparatus, and methodologies described, as there can be multiple possible embodiments that are not expressly illustrated in the present disclosures. It is also to be understood that the terminology used in the description is for the purpose of describing the particular versions or embodiments only, and is not intended to limit the scope of the present application. This summary is provided to introduce aspects related to a technology being implemented in an apparatus for coating a substrate with swarf particles and the aspects are further elaborated below in the detailed description. This summary is not intended to identify essential features of the proposed subject matter nor is it intended for use in determining or limiting the scope of the proposed subject matter.
In one implementation, a technology being implemented in an apparatus for coating a substrate with swarf particles and providing a process for metal coating, named as a grind-coating process is disclosed. It may be noted that the proposed technology and technology deposits a metal coating onto metal surfaces, polymers, and ceramics. In this process, the conventional grinding process is retrofitted to deposit coatings. The apparatus comprises a sample holder, an infeed, and a grinding wheel. The sample holder holds a substrate to be coated with swarf particles. The infeed holds a work piece. The grinding wheel is mounted at a predefined height over the infeed. The apparatus is used to perform metal coating by depositing the swarf materials onto the surface of the substrate. It may be noted that the swarf materials are generated by grinding the work piece with the grinding wheel. In other words, the high speed of the grinding wheel helps to generate and deposit the material removed from the work piece (referred to as swarf material) onto a target surface (referred to as a substrate) as a coating.
It may be noted that the grinding wheel is rotating, on a spindle, at a predefined Rotations Per Minute (RPM) to deposit the swarf particles onto the substrate, when the grinding wheel is interfaced with the work piece. In one aspect, the swarf particles are deposited at a predefined speed and a predefined temperature. It may further be noted that the grinding process is retrofitted to deposit the coating on selected ranges of the substrates including, but not limited to, aluminum and polymer (representative of a soft material) and glass (representative of hard material).
The foregoing summary, as well as the following detailed description of embodiments, is better understood when read in conjunction with the appended drawings. For the purpose of illustrating the disclosure, there is shown in the present document example constructions of the disclosure, however, the disclosure is not limited to the specific methods and apparatus disclosed in the document and the drawings:
The detailed description is described with reference to the accompanying figures. In the figures, the left-most digit(s) of a reference number identifies the figure in which the reference number first appears. The same numbers are used throughout the drawings to refer like features and components.
The figures depict various embodiments of the present disclosure for purposes of illustration only. One skilled in the art will readily recognize from the following discussion that alternative embodiments of the structures and methods illustrated herein may be employed without departing from the principles of the disclosure described herein.
Some embodiments of this disclosure, illustrating all its features, will now be discussed in detail. The words “comprising,” “having,” “containing,” and “including,” and other forms thereof, are intended to be equivalent in meaning and be open ended in that an item or items following any one of these words is not meant to be an exhaustive listing of such item or items, or meant to be limited to only the listed item or items. Although any systems and methods similar or equivalent to those described herein can be used in the practice or testing of embodiments of the present disclosure, the exemplary, systems and methods are now described. The disclosed embodiments are merely exemplary of the disclosure, which may be embodied in various forms.
Various modifications to the embodiment will be readily apparent to those skilled in the art and the generic principles herein may be applied to other embodiments. However, one of ordinary skill in the art will readily recognize that the present disclosure is not intended to be limited to the embodiments illustrated, but is to be accorded the widest scope consistent with the principles and features described herein.
The present invention discloses a technology and process that facilitates coating a substrate with swarf particles. In one embodiment, the technology may be used to deposit the swarf particles onto the substrate for metal coating. The substrate may include metal surfaces and ceramics. In order to deposit the swarf particles, the apparatus is deployed with a sample holder, an infeed, and a grinding wheel. The sample holder holds the substrate to be coated with swarf particles whereas the infeed holds a work piece. In one aspect, the sample holder holds the substrate perpendicularly to the infeed holding the work piece. The grinding wheel, on the other hand, is immovably affixed on top of the infeed under a wheel head. The grinding wheel is configured to rotate, on a spindle, at a predefined Rotations Per Minute (RPM) to deposit the swarf particles onto the substrate upon grinding the work piece, when the grinding wheel is interfaced with the work piece.
It may be noted that the grinding process is retrofitted to deposit the coating. The high speed of the grinding wheel helps to transfer the swarf particles, removed from the workpiece (referred to as swarf particles), towards the substrate. During grinding process, large amounts of the micro-sized particle are removed from the work piece by the grinding wheel subjected to the high rotational speed of the grinding wheel. It may further be noted that the rotational speed of the grinding wheel may be controlled by a controller. Post removal of the swarf particles from the work piece due to the grinding process, the swarf particles are thrown towards the substrate which then adhere on the substrate with a proper splat formation.
Now referring to
In order to coat the substrate 104, the grinding wheel 110 is enabled to rotate at a desired Rotations Per Minute (RPM) speed. Once the grinding wheel 110 is rotated at the desired RPM speed, the work piece 108 is moved transversally or upwardly until the work piece 108 is interfaced with the grinding wheel 110. The work piece 108 is interfaced with the grinding wheel 110 to grind the work piece 108. The grinding of the work piece by the grinding wheel, at high RPM, produces a stream of molten swarf particles 112 (hereinafter may also be referred to as swarf particles 112 or a stream of randomly sized swarf particles 112), that is then thrown towards the substrate 104, as shown in the
It may be noted that the stream of the molten swarf particles 112 may comprise random sized micro particles, as shown in
It may be noted that the swarf particles 112 have a high temperature due to grinding friction and are deposited at a high speed due the rotating speed of the grinding wheel 110. In one aspect, the speed and the temperature of the swarf particles (112) may be changed based on at least one of a grinding time and a set of grinding variables. Examples of the set of grinding variables may include, but not limited to, Cross Feed transverse motion, Longitudinal transverse feed, Rotations Per Minute (RPM) of the grinding wheel, and stand-off distance between the work piece 108 and the substrate 104.
As a result of high impact speed and elevated temperature, the swarf particles 112 get deposited onto the substrate 104. It may further be noted that the swarf particles 112 may be deposited in at least one shape comprising spherical, needle and platelet. In one aspect, the shape and size of the swarf particles 112 may be changed by altering a value pertaining to at least one grinding variable of the set of grinding variables.
In order to support the aforementioned description, various experiments have been performed in an open environment. The experimental data of one such experiment is given below. The temperature of the substrate 104 at the start of grinding process is kept at the room temperature. It may be noted that the temperature of the substrate 104 is constantly increased due to continuous striking of the swarf particles 112 onto the substrate 104 i.e. a coating process. This increase in the temperature of the substrate 104 during the coating process is found to be directly proportional to grinding time.
In order to further elucidate the capability of the apparatus 100, both aluminum and glass are used as the substrate 104 on which coating 114 needs to be performed in experimentation. It may be noted that the work piece 108 for this experimentation is used as solid steel material. A plate of the solid steel material is fixed on a vice 116 below the grinding wheel 110. Before starting the grinding process, the infeed 106 is moved so as to bring the work piece 108 in contact with the grinding wheel 110. During the grinding process, friction occurs between the grinding wheel 110 and the workpiece 108. As a result of that, a stream of randomly sized swarf particles 112 is generated and directed towards the substrate 104. Consequently, the solid steel material directly converts into the stream of randomly sized swarf particles 112, which will directly adhere on the substrate 104 as a coating 114.
While using the solid steel material as the work piece 108, low carbon steel swarf particles are directed by the grinding wheel 110 during the grind processing in accordance with the preferred parameters as mentioned below in Table 1. It has been observed that the coating of the low carbon steel swarf particles is 1.8 mm (about 1800 μm) thick and micro-hardness within the range between 162 HV to 536 HV. The proposed technique of coating by using the apparatus 100 may help in achieving a coating thickness in the range between 1.5 mm to 3.5 mm. In one embodiment, coating of low carbon steel swarf on the substrate 104 like aluminum and glass are shown in
Referring to
Referring to
Referring to
To illustrate the capabilities of the apparatus (100), the description has been described with two ranges of the substrates for coatings from soft materials (including Polymer and Aluminum) to hard materials (including Glass) as mentioned in Table 1. Further it may be possible to perform the metal coating using said technology being implemented in the apparatus (100) for a wide range of other substrates which have properties of soft as well as hard material and are not mentioned in this description.
Exemplary embodiments discussed above may provide certain advantages. Though not required to practice aspects of the disclosure, these advantages may include those provided by the following features.
The present apparatus is a sustainable and cost effective coating process as the waste material arising out of the grinding operation is used for many engineering applications.
The present apparatus facilitates coating hard materials like glass which may not be possible with other coating techniques including Thermal Spraying.
The present apparatus processes may be used to achieve a dense metal coating with an excellent bonding.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201811029355 | Aug 2018 | IN | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2354727 | Wulff | Aug 1944 | A |
| 3597881 | Olton | Aug 1971 | A |
| 3922821 | Canterbury | Dec 1975 | A |
| 4040162 | Isogai et al. | Aug 1977 | A |
| 4251903 | Zacharias | Feb 1981 | A |
| 4285324 | Komanduri | Aug 1981 | A |
| 4339896 | Dennis | Jul 1982 | A |
| 4589231 | Roberts | May 1986 | A |
| 4607459 | Rees | Aug 1986 | A |
| 4919824 | Creps | Apr 1990 | A |
| 5645471 | Strecker | Jul 1997 | A |
| 5733178 | Ohishi | Mar 1998 | A |
| 6095897 | Stocker | Aug 2000 | A |
| 6267657 | Tawara | Jul 2001 | B1 |
| 6780368 | Liu et al. | Aug 2004 | B2 |
| 8826938 | Moore | Sep 2014 | B2 |
| 20020061723 | Duescher | May 2002 | A1 |
| 20020090900 | Telischak | Jul 2002 | A1 |
| 20050064799 | Raffaelli | Mar 2005 | A1 |
| 20060172663 | Zhang | Aug 2006 | A1 |
| 20080113594 | Carlson | May 2008 | A1 |
| 20080160883 | Benner | Jul 2008 | A1 |
| 20080216413 | Woo | Sep 2008 | A1 |
| 20090098711 | Sekiya | Apr 2009 | A1 |
| 20120178345 | Wiand | Jul 2012 | A1 |
| 20160009029 | Cohen et al. | Jan 2016 | A1 |
| 20160108302 | Kitai | Apr 2016 | A1 |
| 20180186091 | Wu et al. | Jul 2018 | A1 |
| 20190134782 | Tateishi | May 2019 | A1 |
| 20190291239 | Yoshida | Sep 2019 | A1 |
| Number | Date | Country |
|---|---|---|
| 103639412 | Mar 2014 | CN |
| 10 2010 014 747 | Oct 2011 | DE |
| 10 2015 002 967 | Oct 2016 | DE |
| Number | Date | Country | |
|---|---|---|---|
| 20200038904 A1 | Feb 2020 | US |