Patent Application
20100004347
The present invention relates to highly loaded, thermosensitive active ingredient compositions which comprise blowing agents, which lead to density reduction in plastics.
Plastics are usually foamed by using blowing agent masterbatches. The blowing agent masterbatches, produced by the extrusion process, have blowing agent contents in the range from 10 to 75% by weight, and often comprise, alongside a polymeric carrier, a high proportion of polyolefinic waxes, which promote the process of incorporation of the agents into the plastics matrix and maximize uniformity of dispersion of the blowing agents.
Concentrates of this type are subject to stringent industrial requirements: the blowing agents should have ideal distribution, the fineness of the cell structure formed has to be maximized, the carrier has to have ideal compatibility with the polymer, and most importantly premature foaming in the processing machine has to be inhibited.
The following single- or multistage processes are currently known for the production of dust-free blowing agent masterbatches and blowing agent preparations, composed of pellets or of powder.
A cold mix is often used, composed of a suitable polymer carrier, such as polyethylene, polypropylene, or ethylene-vinyl acetate copolymer, or of similar polymers, and which can also comprise dispersing agents, such as waxes, fatty acid derivatives, stearates, etc. The disadvantage of these polymer mixtures is that the polymeric fraction can often cause the critical melt temperature of the blowing agents to be exceeded, the result being that the decomposition temperature of the blowing agent is reached or exceeded. There are great restrictions on compatibility with different polymers.
JP 10212372 describes the production of an expandable masterbatch composed of a tack-free polymer, produced using a catalyst. The catalyst used can be a composite of catalysts from group 4. The proportion used of the expandable microsphere products was 30%.
U.S. Pat. No. 5,611,962 and CA 2135600 describe the production of chemical blowing agent concentrates based on polymers whose melting point is above 149° C.
U.S. Pat. No. 4,632,942 and EP 0 143 545 describe the characteristic of carrier polymers for the production of blowing agent concentrates.
All of the blowing agent preparations used in industry hitherto and having high blowing agent content, more than 40%, have to be produced using relatively complicated processing equipment, e.g. an underwater pelletizer. The high loading actually reduces the extrudate strength of the masterbatches produced. Masterbatch companies currently use strand pelletizers. One possibility for improvement would theoretically be the use of specific free-flowing polymers which are processable at lower temperatures, thus preventing premature triggering of the blowing agent, where these would have good compatibility with different polymers. However, polymers having this property profile are relatively expensive.
The production quantities required for cost-effective production using underwater pelletization and the equipment necessary for this process are generally relatively large. Production of specific active ingredient compositions comprising blowing agents matched to the individual customer requirements is therefore costly and cannot achieve conventional high concentrations.
The object of the present invention was to maximize the loading content of a very wide variety of blowing agents in active ingredient compositions which comprise blowing agents and which are used for polymer processing, thus permitting production of foamed plastomers and elastomers in a manner which is economically and environmentally advantageous, with a unitary active ingredient composition or active ingredient preparation, and thus providing high-quality products.
The intention here is very substantially to avoid use of any polymeric carrier, thus permitting firstly production of preparations with markedly higher active substance content and secondly use of these in significantly more different polymers than hitherto, with varying chemical composition, since the high loading reduces the extent of compatibility problems. The wax carrier is moreover intended to permit easier incorporation and dispersion into the polymers, with the result that cell structure is finer or that molecular or molecular-weight distribution is less polydisperse.
The invention achieves this object by incorporating the blowing agent components into a metallocene wax or a mixture of metallocene wax with Ziegler wax, or a wax-polymer mixture. The main constituent of the wax carrier is a metallocene wax. Metallocene waxes or metallocene-polyolefin waxes are defined as waxes produced in the presence of metallocene as catalyst. The resulting composition is compounded by extrusion to give the active ingredient composition of the invention.
The invention therefore provides an active ingredient composition or active ingredient preparation of the type mentioned above, comprising
It is preferable that the wax fraction comprises at least 50% by weight of polypropylene metallocene wax, based on the weight of the wax fraction.
The active ingredient composition of the invention therefore has particularly high blowing agent content and filler content, and has very good compatibility with the polymers used, and very substantially avoids impairment of mechanical properties in the final product.
The melt viscosity of the metallocene waxes, measured at a temperature of 170° C., is in the range from 40 to 80 000 mPa·s, preferably from 45 to 35 000 mPa·s, in particular from 50 to 10 000 mPa·s.
All of the waxy constituents of the active ingredient composition melt in the temperature range from 80 to 170° C.
Active ingredient compositions preferred in the invention comprise from 5 to 90% by weight, preferably from 25 to 85% by weight, of an organic or inorganic blowing agent, and from 7 to 80% by weight, preferably from 7.5 to 75% by weight, of the metallocene-polyolefin wax, and from 0 to 30% by weight, preferably from 0.5 to 25% by weight, of one or more non-metallocene waxes and/or homo- and/or copolymers of ethylene and/or of propylene. The preparation of the invention can, if necessary, also comprise an amount of from 0 to 30% by weight of fillers or additives, based on the total weight of the composition.
The waxes produced in the presence of metallocene as catalyst are preferably copolymer waxes composed of propylene and from 0.1 to 50% of ethylene and/or from 0.1 to 50% of at least one branched or unbranched 1-alkene having from 4 to 20 carbon atoms, with drop point (ring and ball) of from 80 to 170° C.
The metallocene waxes produced in the presence of metallocene as catalyst are substantially or completely amorphous and can also, if necessary, be polar-modified waxes. For the purposes of the invention, substantially means at least 80% by weight, preferably at least 90% by weight, particularly preferably at least 95% by weight, specifically at least 99% by weight.
Particular non-metallocene polyolefin waxes are firstly ethylene-vinyl acetate waxes whose drop point is from 90 to 120° C., whose vinyl acetate content is from 1 to 30%, and whose viscosity is from 50 to 3000 mPa·s, preferably from 50 to 1500 mPa·s, measured at a temperature of 140° C., and secondly either nonpolar or polar non-metallocene waxes whose drop point is in the range from 90 to 120° C. and whose viscosity is smaller than 30 000 mPa·s, preferably smaller than 15 000 mPa·s, measured at a temperature of 140° C.
Non-metallocene polyolefin waxes that can be used are homopolymers of ethylene or of higher 1-olefins having from 3 to 10 carbon atoms, or copolymers of these. The weight-average molar mass Mw of the polyolefin waxes is preferably from 1000 to 20 000 g/mol, and their number-average molar mass M, is preferably from 500 to 15 000 g/mol.
The metallocene-polyolefin waxes used in the invention are produced using metallocene compounds of the formula I.
This formula also encompasses compounds of the formula Ia
of the formula Ib
and of the formula Ic
In the formulae I, Ia and Ib, M1 is a metal of group IVb, Vb, or VIb of the Periodic Table, e.g. titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, preferably titanium, zirconium, hafnium.
R1 and R2 are identical or different and are a hydrogen atom, a C0-C10-alkyl group, preferably C1-C3-alkyl group, in particular methyl, a C1-C10-alkoxy group, preferably C1-C3-alkoxy group, a C6-C10-aryl group, preferably C6-C8-aryl group, a C6-C10-aryloxy group, preferably C6-C8-aryloxy group, a C2-C10-alkenyl group, preferably C2-C4-alkenyl group, a C7-C40-arylalkyl group, preferably C7-C10-arylalkyl group, a C7-C40-alkylaryl group, preferably C7-C12-alkylaryl group, a C8-C40-arylalkenyl group, preferably C8-C12-arylalkenyl group, or a halogen atom, preferably a chlorine atom.
R3 and R4 are identical or different and are a mono- or polynuclear hydrocarbon radical which can form a sandwich structure with the central atom M1. R3 and R4 are preferably cyclopentadienyl, indenyl, tetrahydroindenyl, benzoindenyl, or fluorenyl, and the parent structures here may also bear additional substituents or may have bridging to one another. One of the radicals R3 and R4 may moreover be a substituted nitrogen atom, where R24 is as defined for R17 and is preferably methyl, tert-butyl, or cyclohexyl.
R5, R6, R7, R8, R9, and R10 are identical or different and are a hydrogen atom, a halogen atom, preferably a fluorine atom, chlorine atom, or bromine atom, a C1-C10-alkyl group, preferably C1-C4-alkyl group, a C6-C10-aryl group, preferably C6-C8-aryl group, a C1-C10-alkoxy group, preferably C1-C3-alkoxy group, an —NR162—, —SR16—, —OSiR163—, —SiR163—, or —PR162-radical, where R16 is a C1-C10-alkyl group, preferably C1-C3-alkyl group, or C6-C10-aryl group, preferably C6-C8-aryl group, or in the case of Si— or P-containing radicals, a halogen atom, preferably a chlorine atom, or any two adjacent radicals R5, R6, R7, R8, R9, or R10 form a ring with the carbon atoms connecting them. Particularly preferred ligands are the substituted compound structures derived from the parent structures cyclopentadienyl, indenyl, tetrahydroindenyl, benzoindenyl, or fluorenyl.
R13 is
═BR17, =AIR17, —Ge—, —Sn—, —O—, —S—, ═SO, ═SO2, ═NR17, ═CO, ═PR17 or ═P(O)R17, where R17, R18, and R19 are identical or different and are a hydrogen atom, a halogen atom, preferably a fluorine atom, chlorine atom, or bromine atom, a C1-C30-alkyl group, preferably C1-C4-alkyl group, in particular a methyl group, a C1-C10-fluoroalkyl group, preferably CF3 group, a C6-C10-fluoroaryl group, preferably pentafluorophenyl group, a C6-C10-aryl group, preferably C6-C8-aryl group, a C1-C10-alkoxy group, preferably C1-C4-alkoxy group, in particular a methoxy group, a C2-C10-alkenyl group, preferably C2-C4-alkenyl group, a C7-C40-aralkyl group, preferably C7-C10-aralkyl group, a C8-C40-arylalkenyl group, preferably C8-C12-arylalkenyl group, or a C7-C40-alkylaryl group, preferably C7-C12-alkylaryl group, or R17 and R18, or R17 and R19 form a ring in each case together with the atoms connecting them.
M2 is silicon, germanium, or tin, preferably silicon and germanium. R13 is preferably ═CR7R8, ═SiR17R18, =GeR17R18, —O—, —S—, ═SO, ═PR17 or ═P(O)R
R11 and R12 are identical or different and are as defined for R17. m and n are identical or different and are zero, 1 or 2, preferably zero or 1, where m+n is zero, 1 or 2, preferably zero or 1.
R14 and R15 are as defined for R17 and R18.
Examples of suitable metallocenes are:
Suitable cocatalysts are used to activate the single-center catalyst systems. Suitable cocatalysts for metallocenes of the formula I are organoaluminum compounds, in particular aluminoxanes, or else aluminum-free systems, such as R2 xNH4-xBR214, R20PH4-xBR214, R23CBR214 or BR213. x in these formulae is a number from 1 to 4, and the radicals R20 are identical or different, preferably identical, and are C1-C10-alkyl or C6-C18-aryl, or two radicals R20 form a ring together with the atom connecting them, and the radicals R21 are identical or different, preferably identical, and are C6-C18-aryl, which may have substitution by alkyl, by haloalkyl, or by fluorine. In particular, R20 is ethyl, propyl, butyl, or phenyl, and R21 is phenyl, pentafluorophenyl, 3,5-bistrifluoromethylphenyl, mesityl, xylyl, or tolyl.
A third component is also often required in order to maintain protection from polar catalyst poisons. Organoaluminum compounds are suitable for this purpose, examples being triethylaluminum, tributylaluminum, and others, and also mixtures.
As a function of the process, it is also possible to use supported single-center catalysts. Preference is given to catalyst systems in which the residual contents of support material and cocatalyst do not exceed a concentration of 100 ppm in the product.
Determination methods used here are: melt viscosities to DIN 53019 using a rotary viscometer, drop points to DIN 51801/2, and softening points by ring/ball to DIN EN 1427. Drop point is determined using Ubbelohde drop-point equipment to DIN 51801/2, and softening point using ring/ball equipment to DIN EN 1427.
The compositions of the invention can, as mentioned above, also comprise fillers, such as silicates, silicas, zeolites, e.g. aluminum silicates, sodium silicates, calcium silicates, chalk, talc, or else auxiliaries, e.g. antistatic agents, stearates, antioxidants, slip agents, and/or suspension stabilizers, colorants, flame retardants, antiblocking agents, potash, and alkaline earth metal oxides.
Examples of blowing agents that can be used are azodicarbonamides, nitroso compounds, hydrazides, and citric acid, and also citric acid derivatives, citric salts, and citric esters, sodium hydrogencarbonate, or a mixture thereof. The compounds most often used are those known as modified azodicarbonamides, these being azodicarbonamides in conjunction with kickers, such as ZnO, zinc stearate, or with lead salts. However, it is also possible to use combinations with organic substances, e.g. acids and bases. Other exothermic blowing agents would be 4,4′-oxybis(benzenesulfonyl hydrazide), 5-phenyltetrazole, p-tolylenesulfonyl semicarbazide, or p-tolylenesulfonyl hydrazide, which can be used with advantage. Other possible blowing agents are low-boiling-point liquids, such as isopentane or isooctane, and also microspheres which have a polymeric shell and which have a filling of gases or of low-boiling-point liquids.
The required proportion of metallocene waxes depends on additive-matrix inter-reaction, on the surface structure of the blowing agent, on the surface structure of the finished item, on the desired cell structure, on the triggering temperature (gas-evolution temperature) of the blowing agent used, and also on the desired amount to be used of the end product.
The present invention also provides a process for the production of the composition of the invention by combining the individual constituents and subsequent homogenization in an extruder or kneader. Preference is given here to the premixing of the individual components during production of the composition, and this can take place in a suitable mixing apparatus. However, it is also possible that the addition of further additives is delayed until later and achieved, in solid or liquid form, by way of a side feed.
The raw materials used can take a very wide variety of forms. The form taken by the waxes, and also the further additives, in the mixture can by way of example be that of pellets, of flake, or of very fine powder or of other types of powder, while the blowing agent can also be present in liquid form.
The following single- or multistage processes are currently known for the production of dust-free active ingredient compositions in the form of pellets or powder with high loadings:
All of the components can be mixed cold, addition taking place by way of the main feed of an extruder, or the waxy/polymeric fractions of the formulation can be introduced by way of the main feed of the extruder, the pulverulent or liquid blowing agents being introduced into the machine by way of appropriate side feeds. Mixing in the melt can then be carried out in a suitable extruder or in kneaders. This is followed by pelletization, milling, or spraying.
A cold mix is composed of suitable polymeric carriers, such as polyethylene, polypropylene, or ethylene-vinyl acetate. The disadvantage of such polymer mixtures is that they often have limited compatibility of individual components, a possible result then being separation of polymer and the additives, such as the blowing agents.
In the case of mixing at an elevated temperature, the thermal energy can be introduced by way of friction, or by way of separate heating of the mixing vessel, or by both methods.
In the case of production of the composition in an extruder, it is preferable to operate with a screw structure matched to the high active ingredient content. The temperature profile is preferably lower than stated in the prior art. Production of the compositions of the invention advantageously uses a strand pelletizer, but it is also possible to use an underwater pelletizer or die-face pelletizer.
The compositions of the invention lead to a reduction of density of semi-synthetic or synthetic polymers, and are therefore used in particular for the production of foamed plastics or plastics articles.
Unlike the compositions described in the prior art and comprising blowing agents, the products of the invention can be used to foam a wide selection of polymers. Examples that may be mentioned are: polyolefins and copolymers of PE, polyvinyl chloride (PVC) in the form of unplasticized PVC or in the form of plasticized PVC, ethylene-vinyl acetate copolymers (EVA), polystyrene (PS), styrene-acrylonitrile copolymers (SAN), acrylonitrile-butadiene-styrene copolymers (ABS), polyethylene glycol terephthalate (PET), polybutylene glycol terephthalate (PBT), and copolyesters of these, and also polycarbonate (PC), butyl rubber and other rubbers, bitumen, and also blends, such as PC/ABS (acrylonitrile-styrene-acrylate terpolymer), PC/PBT, or PC/ASA, and PMMA (polymethyl methacrylate), and also thermoplastic polyurethanes (TPU) and also certain specialty polymers.
After blending with the polymer and achievement of the required concentration intended, the plastics mixtures can then be further processed to give the desired end products.
Each of the examples below uses a metallocene wax or a metallocene wax mixture, produced from metallocene-PE waxes, from polar or nonpolar non-metallocene PE waxes, and from copolymers of ethylene, with the following substance parameters (see below). The products are used in fine-grain form.
The polyolefins a)-d) used in the invention and listed in table 1 were produced by copolymerization of propylene with ethylene using the metallocene catalyst dimethylsilylbisindenylzicronium dichloride by the process stated in EP-A-0 384 264 (general specification of examples 1 to 16). the various softening points and viscosities were set via variation of ethylene usage and of polymerization temperature.
1)Drop point
2)Softening point
The materials are used in fine-grain form (sprayed or ground), but pellet form is also possible (for separate addition of the individual components at the machine).
The active ingredient compositions of the invention were produced as described below:
The materials were then extruded in a corotating twin-screw machine with downstream strand pelletizer.
Energy was introduced exclusively by way of friction. The average grain size of the resultant mixture was smaller than 1 mm.
The following preparations were produced in the examples below by the process described above. In each case, the metallocene wax used comprised the wax described above:
The active ingredient compositions of production examples 1 to 4 were cold-batched and used in a corotating twin-screw machine with a low temperature profile to reduce the density of various polymers. The result was a homogeneous foam structure, and at the same time the use of the preparations was not found to impair the mechanical properties of the polymers.
| Number | Date | Country | Kind |
|---|---|---|---|
| 102006046566.0 | Sep 2006 | DE | national |
| PCT/EP2007/008366 | Sep 2007 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP07/08366 | 9/26/2007 | WO | 00 | 3/27/2009 |