Terpolymers for use as high temperature fluid loss additive and rheology stabilizer for high pressure, high temperature oil well drilling fluids

Abstract

Novel water-soluble terpolymers comprising:______________________________________Ingredients Mole %______________________________________2-acrylamido-2-methylpropane- 57-61sulfonic acid, sodium salt (AMPS)acrylamide 20-35N,N--diallylacetamide 4-23______________________________________These terpolymers provide high temperature fluid loss additives and rheology stabilizers for high calcium-containing brine clay drilling fluids.

Description

INTRODUCTION

A serious problem is encountered when clay-based oil well drilling fluids are subjected to conditions of high temperature and high pressure in conjunction with utilization of high calcium-containing brines which are used to prepare these drilling fluids. When these conditions exist, conventional drilling fluid polymeric additives such as acrylamide polymers, when used as stabilizers for these fluids, tend to be rendered ineffective.

Recently a partial solution to the problem has been provided by the utilization as a fluid loss additive and rheology stabilizer a terpolymer composed of:

______________________________________Ingredients Mole %______________________________________2-acrylamido-2-methylpropane- 52.0sulfonic acid, sodium salt (AMPS)acrylamide 32.0N--methyl-N--vinyl acetamide 16.0______________________________________

This terpolymer, while proving to be effective as a high temperature fluid loss additive for oil well drilling fluids, has the disadvantage of using in its composition 16.0 mole % of N-methyl-N-vinyl acetamide. This renders the material expensive to use.

If it were possible to use a polymeric high temperature fluid loss additive and rheology stabilizer that was resistant to high calcium-containing brines, an improvement in the art would be afforded.

THE INVENTION

The invention comprises the utilization of terpolymers with the following composition:

______________________________________ Mole %Ingredients Preferred General______________________________________2-acrylamido-2-methylpropane- 58.4 57-61sulfonic acid, sodium salt (AMPS)acrylamide 32.5 20-35N,N--diallylacetamide 09.1 4-23______________________________________

As will be shown hereafter, these terpolymers provide excellent high temperature fluid loss protection to a clay-based brine prepared drilling fluid.

These terpolymers may be prepared in accordance with the following preparative technique, illustrating the preparation of the preferred terpolymer listed above:

A polymerization vessel fitted with a stirrer, thermometer, condenser and addition funnel was charged with 150 g of water and 8.3 g of N,N-diallylacetamide. The solution was purged with nitrogen for 25 minutes while the temperature was raised to 80.degree. C. In a separate vessel, a monomer solution was prepared consisting of 260 g of water, 79.5 g of 2-acrylamido-2-methyl-propanesulfonic acid, 31.5 g of a 50% solution of sodium hydroxide, and 33 g of a 46% solution of acrylamide. This monomer mixture was adjusted to a pH of 8.67 and charged to the addition funnel. The solution of monomers was added continuously over a four-hour period with four portions of 0.05 g of ammonium persulfate added at 45 minute intervals beginning at the first addition of monomers. After the addition of monomers was complete, the reaction temperature was maintained at 85.degree. C. for about 90 minutes. The final polymer solution had a Brookfield viscosity of 325 cps.

The amount of polymer used to stabilize clay-based drilling fluids under conditions of high temperature and pressure may vary between about 10 % up to 60% by weight based on the clay present in the fluid.

The polymers may be further characterized as having a molecular weight below 1,000,000. Preferably, they have a molecular weight within the range of 10,000-500,000.

To illustrate the invention, the preferred composition shown above was tested in a high temperature, high pressure fluid loss additive test which is described in detail in the American Petroleum Institute publication, RP13B.

The particular drilling fluid tested contained 15 pounds/barrel of a pre-hydrated Bentonite drilling fluid clay and a 50% dilution of a brine known as a Williston Basin brine. This brine contained a substantial amount of calcium.

The blank test produced a filtrate of 42 ml/7.5 min.

The preferred composition of the invention was added to provide 6 pounds/barrel of active polymer. This provided an approximate dosage of 40% by weight active polymer based on active clay. At the end of 30 minutes, the fluid loss in the above described test was 15 ml.

Using the same preparative technique and test method for determining fluid loss additive effectiveness, the following additional polymers were prepared and tested;

______________________________________ diallyl acetamide HTHPAMPS Acrylamide acrylamide Fluid Loss______________________________________58.5 32.4 9.1 17 ml.60.7 34.9 4.4 17 ml.57.0 20.4 22.6 18 ml.______________________________________

Claims

1. A method of improving high temperature fluid loss and rheology stabilization of high calcium brine clay-containing oil well drilling fluids which comprises adding thereto a stabilizing amount of a water-soluble terpolymer comprising:

______________________________________Ingredients Mole %______________________________________2-acrylamido-2-methylpropane- 57-61sulfonic acid, sodium saltacrylamide 20-35N,N--diallylacetamide 4-23______________________________________

and said terpolymer being further characterized as having a molecular weight below 1,000,000.

2. A method of improving high temperature fluid loss and rheology stabilization of high calcium brine clay-containing oil well drilling fluids which comprises adding thereto a stabilizing amount of a water-soluble terpolymer comprising:

______________________________________Ingredients Mole %______________________________________2-acrylamido-2-methylpropane- 58.4sulfonic acid, sodium salt (AMPS)acrylamide 32.5N,N--diallylacetamide 09.1______________________________________

and said terpolymer being further characterized as having a molecular weight below 1,000,000.