The present invention relates to the field of textile articles for clothing, in particular it refers to a textile article for motorcyclist protective clothing.
As is known in the accident prevention field, the anti-pierce, anti-cut, high abrasion resistant and anti-burst fabrics that are normally used in the safety footwear and safety clothing field (for example anti-pierce insoles, bulletproof vests, overalls for motorcycle clothing, etc.) are of particular importance, suitable to protect the user in case of accidents.
The EN 13595-1:2002 standard is the main standard in Europe that regulates protective clothing for professional motorcyclists. The norm provides for a division of the garments into 4 zones, wherein zones 1 and 2 correspond to the most exposed and most at risk parts (elbows, arms, shoulders, knees, hips), zones 3 and 4 correspond to parts less at risk, moreover 2 safety levels, wherein level 1 covers the minimum requirements and level 2 the highest requirements for more performing materials, so-called “racing”.
Currently, protective clothing for professional (and not) motorcyclists are made of leather. The Bovine Leather (used for professional and non motorcycling clothing, in fact the bovine leather has a lower quality compared to the kangaroo which is compulsorily used for the professional pilots overalls) normally it has a weight of 1000-1400 g/m2, a thickness of 1.2-1.6 mm and demonstrates an abrasion resistance according to EN 13595 Standard>4 seconds (level 1). The Kangaroo Leather (used for professional motorcycling overalls) normally presents a weight of 800-1000 gr/m2, a thickness of 0.8-1.2 mm and demonstrates an abrasion resistance according to EN 13595 Standard>4 seconds (level 1). It is noted that in all the circuits for speed races it is NOT allowed by the internal regulations clothing DIFFERENT from the leather. The leather, however, has the following disadvantages: non-breathable, not washable, not thermally insulating (during the fall pilots burned for heat that develops), flammable, non-water repellent, little comfortable compared to a fabric, not Eco-friendly.
The research in this field is always aimed to providing fabrics that, while ensuring the essential protective effect, are as soft, elastic and breathable as possible in order to minimize unwanted effects when worn.
Following the aforementioned perspective, it was attempted to increasingly decrease the weight and thickness of the fabrics used, while maintaining the desired protective effect, an example is the motorcyclist clothing fabric described in the Italian patent application n. 102015000051902 in the name of the same Applicant, said fabric wherein the threads constituting the weft have a diameter equal to or different from that of the threads which constituting the warp and wherein the titre of said threads is between 100-700 dtex and possibly colored, coated or resined. In particular, a fabric consisting of a weft wherein the number of superimposed threads is 10 (corresponding to a weft in which the number of overlapping wefts is 5) and a warp whose number of overlapping wefts is 20 (corresponding to a warp in which the number of overlapping threads is 10) is described, wherein the yarns are in high tenacity polyester elasticized for the weft having a titre of 580 dtex(PL HT) and for the warp, in high-tenacity polyester, a titre of 240-280 dtex. Such a fabric had a weight equal to about 1000 g/m2 and a thickness of about 1.8 mm. Such fabric has been certified in class 2 according to the current EN ISO 13595-2002 Standard: —PROTECTIVE CLOTHING FOR PROFESSIONAL MOTORCYCLIST; however, despite wearability and comfort were better than leather; the weight and thickness of the fabric compared to leather garments currently widely used by professional motorcyclist constituted a limit.
The aforementioned Standard provides for 2 security levels, Class 1 and Class 2, where for Class 1 the values of abrasion on the CAMBRIDGE ABRASION MACHINE (the instrument required by the Standard to perform the abrasion resistance test) must be greater than 4 seconds, for Class 2 the values must be greater than 7 seconds. This type of test results to be extremely aggressive towards the tested materials, therefore, to achieve the requisites required by the Standard it has been necessary to create materials with important weight and thickness such that they result in heavy and not very comfortable clothes. The traffic laws does not impose the obligation, in any Community country, to wear protective clothing that respect that Standard during the non-professional driving of motorbikes and motorcycles. Reason why the future Standard pr EN 17092 will see 3 new levels of security less restrictive, to induce habitual motorcyclists to wear garments that provide minimal protection in the event of an accident.
The aforementioned patent application on behalf of the same applicant was been an important step forward in terms of both safety and portability and comfort, but the market, in parallel with the new revision project of the EN ISO 13595 Standard proposed to the European Commission, requires materials that are increasingly lighter and thin, but at the same time safe and resistant. The new project pr EN 17092 of the Standard proposed to the European Commission, establish that the levels of protection established by the Standard itself become 5, wherein the first 2 levels “A+A+A and A+A” are the most important and the established requirements remained the same as the two classes of protection of the current Standard, which we will call RACING requirements, while other 3 levels of protection for urban motorcycling have been proposed, which we will call URBAN requirements, with lower parameters than Racing, just to look for to induce who habitually use the motorcycle, to wear protective clothing.
Our research then turned to a structural and targeted improvement of the products made to date, to make available to the market suitable materials and in line with current and future European directives.
Object of the present invention is therefore to provide a textile article which possesses requirements corresponding to ISO 13595:2002 and subsequent modifications but characterized by weights and thicknesses (a weight of less than 1000 g/m2 and a thickness of less than 1.5 mm) such as to guarantee even softness and comfort for the making of protective clothing or (possibly with a weight less than or equal to 1500 g/m2 and a thickness less than or equal to 2.0 mm) for use as reinforcement materials for the further protection of the most exposed areas.
Subject of the present invention is a protective fabric according to claim 1.
Object of the present invention is also a coupled protective fabric according to claim 6.
In fact, it has been surprisingly found that the protective fabric according to the invention is an evolved, light, fine, extremely comfortable, soft and incredibly resistant textile article able to resisting abrasion, cutting and bursting, able to, in fact, satisfying widely all the parameters imposed by the future EN ISO 13595 Standard for the RACING class, further increasing the already exceptional properties of resistance, elasticity, softness and flexibility on the final product, that make it an innovative and extremely safe material for the production of professional motorcyclist clothing with all the advantages of breathability and comfort that only a fabric can give.
As compared to the fabric described in Italian patent n. 102015000051902 on behalf of the same Applicant, the protective fabric coupled or not of the present invention has reduced weight and thickness of 20-25%, the thing is particularly striking in the case of the coupled fabric being a 2-body coupled fabric. Moreover, the mechanical-physical resistances of the finished product were found increased in a considerable manner, so for example, in one coupled embodiment thereof, it has demonstrated an abrasion resistance according to EN 13595 Standard>16 seconds.
The protective fabric coupled or not of the present invention also shows several other advantages because it can be colored in all the desired colors by using the normal staining methods, whether in fiber, in the piece or by printing.
The protective fabric coupled or not according to the invention is machine-washable, breathable, eco-friendly because completely recyclable, if desired it can be elasticized.
If desired, the fabric coupled or not of the invention can be subjected to coating or resin treatment with the known products and used for this purpose, for example to make antacid, waterproof, fireproof a fabric, etc. The aforesaid characteristics allow a great ease of use and a fabric according to the invention can therefore be easily used to manufacture protective clothing (PPE—Personal protective equipment), especially for motorcycling, (such as overalls, trousers, jackets, vests, coats, etc.) or to manufacture sportswear which also requires a considerable ability to protect the user using the normal cutting, sewing and making procedures that are used in the sector. It can also be utilized as a reinforcement material in exposed areas and most at risk.
Object of the present invention is also a method for the preparation of a coupled fabric according to the invention, said method comprising the coupling of the upper layer to the lower layer by means of known traditional coupling techniques or by quilting (seam of the 2 layers).
The protective fabric according to the invention consists of a weft in which the number of superposed wefts is 2-4, even more preferably 2 or 4 and a warp in which the number of overlapped threads is 10-50, preferably 10-16, even more preferably 10.
Any type of weave can be used for the construction of the upper fabric according to the invention (for example, double, double-double-sided, triple, quadruple, six-fold, eight-fold, etc.) and furthermore also the ligation is of the known type which is normally used in this field, for example a ligation in lowered, in raised or a combination of the two or by inversion of the warps or of the wefts may be used. The weft threads are inserted into the warp according to traditional techniques using the looms usually used for the weaving of this type of articles.
The threads constituting the warp preferably have a titre of 200-300 dtex, more preferably 220-280 dtex. The threads constituting the warp are preferably composed of 40-100 filaments, preferably 40-60 or 60-80 filaments. The threads constituting the warp are preferably twisted and optionally elasticized. Preferably according to the present invention the threads constituting the warp of the protective fabric according to the invention are polyester or polyamide filaments (for example nylon), preferably high tenacity, and optionally elasticized with elastomers of known type. The threads constituting the warp are preferably twisted and optionally elasticized polyester (PL) HT or polyamide (PA) HT threads. Even more preferably, the threads constituting the warp have a dtex of 230-275 dtex or 230-270 dtex and a weight composition of 85-95% of PA and 0-15% or 5-15% of elastomer (EA).
Preferably the threads constituting the weft of the protective fabric according to the invention are chosen from the group consisting of:
The threads constituting the weft preferably have a titre of 530-630 dtex, more preferably 550-610 dtex. The threads constituting the weft are preferably composed of 50-150 filaments, preferably 90-110 filaments. The threads constituting the weft are preferably twisted and elasticized polyester (PL) HT threads. Even more preferably, the threads constituting the weft have a dtex of 560-600 dtex and a weight composition of 90-98% PL and 2-10% elastomer (EA).
The fabric according to the invention preferably has 20-200 threads per cm in weft, more preferably 45-85, even more preferably 80, and 20-200 threads per cm in warp, more preferably 45-85, even more preferably 65.
With the particularly preferred specifications described above, it has been possible to prepare a fabric having a weight of about 400-900 g/m2, preferably 600-800 g/m2 and a thickness of about 0.7-1.5 mm, preferably 1-1.4 mm, which it has resulted being extremely comfortable, light and workable, in
Coupled Fabric
The coupled protective fabric according to the present invention is preferably comprised of only two layers; an upper fabric and a lower fabric.
Preferably, the upper layer is different from the lower layer.
The threads constituting the weft of the upper fabric have a different diameter and composition from those of the threads constituting the warp;
Preferably, the threads constituting the lower fabric weft have the same diameter and composition to that of the threads constituting the warp.
Upper Fabric
The upper fabric is constituted by a weft wherein the number of superimposed wefts is 2-20, more preferably 2-6, still more preferably 2, 4 or 5 and a warp wherein the number of overlapping threads is 10-50, preferably 10-16, even more preferably 10.
Any type of weave can be used for the construction of the upper fabric according to the invention (for example, double, double-double-sided, triple, quadruple, six-fold, eight-fold, etc.) and moreover also the ligature is of the known type which is normally used in this sector, for example you can use a ligature in lowered, in raised or a combination of the two or by inversion of the warps or of the wefts. The weft threads are inserted into the warp according to traditional techniques using the looms usually used for weaving of this type of articles.
The threads constituting the warp have a titer of 200-300 dtex, more preferably 220-280 dtex. The wires that constitute the warp are preferably composed of 40-100 filaments, preferably 40-60 or 60-80 filaments. The threads constituting the warp are preferably twisted and optionally elasticized. Preferably, according to the present invention, the threads constituting the warp of the upper fabric are polyester or polyamide filaments (for example nylon), preferably at high-tenacity, and optionally elasticized with known type elastomers. The threads constituting the warp are preferably twisted and optionally elasticized polyester (PL) HT or polyamide (PA) HT threads. Even more preferably, the threads forming the warp have a dtex of 230-275 dtex or 230-270 dtex and a weight composition of 85-95% of PA and 0-15% or 5-15% of elastomer (EA).
Preferably, the threads constituting the weft of the upper fabric are selected in the group consisting of
The threads constituting the weft have a titre of 530-630 dtex, more preferably 550-610 dtex. The threads constituting the weft are preferably composed of 50-150 filaments, preferably 90-110 filaments. The threads constituting the weft are preferably twisted and elasticized polyester (PL) HT threads. Even more preferably, the threads constituting the weft have a dtex of 560-600 dtex and a weight composition 90-98% of PL and 2-10% of elastomer (EA).
The upper fabric according to the invention preferably has 20-200 threads per cm in weft, more preferably 45-85, still more preferably 65, and 20-200 threads per cm in the warp more preferably 45-85, even more preferably 65.
With the particularly preferred specifications described above, it was possible to prepare a upper fabric having a weight of about 400-800 gr/m2, preferably 600 gr/m2 and a thickness of about 0.7-1.3 mm, preferably 1.0 mm, which turned out to be extremely comfortable, light and workable, in
Lower Fabric
Preferably, according to the present invention, the threads constituting the warp and the weft of the lower fabric are preferably the same and selected in the group consisting of
Preferably, the lower fabric consists of a simple canvas wherein the threads forming the warp are the same as the threads constituting the weft and alternate with drawing 1A-1B and wherein both A and B are selected from the listed fibers above.
Clearly, various alterations are possible with the design of threads A and B, the preferred one is 1A-1B, but other possible ones are 2A-2B, 3A-3B, 1A-2B, 2A-1B, etc.
More preferably, the yarn in A is polyester HT and the yarn in B is polyamide/UHMWPE in mixture, both yarns in A and B are elasticized.
Preferably, the weight composition of the yarn A is 90-98% of PL and 2-10% of elastomer (EA). Preferably, the weight composition of the yarn B is 40-50% of UHMWPE, 45-55% of PA and 5-10% of elastomer (EA).
The weft threads are inserted into the warp according to traditional techniques using the looms usually used for the weaving of this type of articles.
The weave preferably used is a simple canvas, as illustrated in the warp profile in
Preferably the threads titre constituting the weft and the warp is 100-700 dtex, more preferably 350-650 dtex, preferably 550-600 dtex for the yarn A and 420-480 dtex for the yarn B; the warp threads may be parallel but preferably are twisted and elasticized, while those of the weft may be indifferently twisted or parallel and elasticized.
The threads constituting the weft may have the same diameter as the threads constituting the warp or different diameter.
The lower fabric according to the invention preferably has 10 to 200 threads per cm in weft, more preferably 10-30, still more preferably 18-24, most preferably 22; and 10-200 threads per cm in the warp preferably 10-30, more preferably 18-24, even more preferably 22.
With the particularly preferred specifications described above, it had been possible to prepare a lower fabric having a weight of about 150-500 g/m2, preferably 300 g/m2 and a thickness of about 0.2-0.6 mm, preferably 0.4 mm, which was found to be extremely comfortable, light and workable and surprisingly resistant.
Coupling
In the coupled fabric according to the invention, the two upper and lower fabrics are coupled by means traditional coupling techniques known by the application between the two fabrics of an adhesive means or by quilting, seam between them, of the 2 layers. Among the known coupling techniques, polyurethane (PU) or reactive polyurethane (PUR) coupling, powder coupling, PU film or PL coupling, web coupling, latex coupling are preferred.
The aforesaid adhesive means (also called glue) can be applied by blade, by points or by hot transfer, preferably according to the present invention the selected coupling is reactive polyurethane (PUR) by points, as it allows to maintain exceptional properties of breathability, elasticity, softness without minimally altering the gluing power between the layers, with tightness and resistance to all environmental aging (high temperatures, low temperatures, acid sweat, alkaline sweat, water, etc.) to which the material is subjected.
Preferably, both the upper fabric and the lower fabric, before proceeding to the final phase of PUR by point coupling, preferably in quantities of 30-50 g/m2, take advantage of a good preparation to eliminate all the stiffening agents present on the fibers applied in phase spinning, warping and weaving and possible impurities present in the fibers or collected during the previous workings.
Preferably then, to eliminate all impurities present in the fabric and favor the re-entry and fibers closure, which may also be about 25% in both directions if there is the preferred presence of an elastomer both in the weft and in the warp, both the upper and lower fabrics are purged in width, procedure carried out with water and addition of possible detergent soaps, at a temperature of about 90° C. After washing, the fabric must be dried and thermofixed, preferably with a passage carrying out drying in ramosa at a temperature of 165° C., speed of 25 m/min, then always in ramosa thermofixing at a temperature of 180° C., speed of 25 m/min. The thermofixing serves to give permanent stability for all subsequent procedure (coupling, dyeing, printing, finishing, industrial washing or domestic washing, etc.). After the thermofixing we proceed with the equalization, a rolling operation with application of steam, to homogenize the surface and to make recover softness to the fabric, hardened and strain hardened by the thermofixing.
If the upper fabric and/or the lower fabric contain UHMWPE yarns (for example Dyneema®), the drying and thermofixing phase must be carried out in tumbler, the industrial equivalent of the domestic dryer, which works at temperatures below 100° C., but which performs an important mechanical action given by the centrifugation basket, which determines the maximum re-entry of the fibers, to obtain the same results in terms of dimensional stability of the ramosa. For fabrics in which Dyneema® fiber (UHMWPE) is present tumbler drying is required because above 110° C. said fiber starts to soften and then melts, completely losing the characteristics that make it one of the most resistant fibers to abrasion, cut and tear on the market. This operation in tumbler is more expensive and long compared to the thermofixing in ramosa, reason why, if not forced by technical reasons, it is preferably avoided.
Once the 2 fabrics have been prepared as described above, we can proceed with the reactive polyurethane (PUR) coupling to point.
This procedure is preferably carried out on cold, on a machine where the thermoplastic PUR is dissolved from the pressure plate heated to about 115° C. (accessory external to the machine) and pushed through a pump to the micro-perforated cylinder for application on the fabrics. Immediately after the application of the glue, the 2 coupled fabrics are crushed by a calender which applies a pressure of about 2.5 tons and immediately rolled up to form a large roll, which remains stationary to cross-link in a heated environment where the temperature must never fall below 15° C. (limit temperature which crystallizes the PUR rendering it ineffective). The cross-linking time depends on the external temperature, at 20° C. 24 h of cross-linking are enough (the minimum time below which it can not be lowered), below 20° C. the cross-linking time proportionally extends it with the decrease the temperature itself.
The advantage of this type of coupling is that once the cross-linking is completed, the PUR does not go back any more, neither with high nor with low temperatures, and gives a permanent seal to all the expected environmental aging and to all the domestic and industrial washings.
The present invention can be better understood in the light of the following embodiment examples.
A fabric has been reproduced as described in the Italian patent application n. 102015000051902.
Warp Yarn
Polyester (PL) HT 275 dtex 48 filaments 400 Z twists
Weft Yarn
96 Polyester (PL) HT filaments 550 dtex arranged in a spiral pattern (330 twists per meter, TPM) around a 78 dtex elastomer (EA)
94% Polyester (PL) HT 550 dtex+6% elastomer (EA) 78 dtex Final titre 580 dtex
The fabric has been realized on looms usually used for the weaving of this type of articles, applying a multiple weave (double double-face) of 10 threads superimposed in the warp and 5 wefts superimposed in the weft as shown in
The resulting fabric has a warp reduction of 70 threads/cm±5% and a weft reduction of 96 threads/cm 15%, a weight of 1000 g/m2 and a thickness of 1.80 mm and has shown an abrasion resistance according to EN 13595>8 seconds (level 2).
The fabric is elasticized, machine washable, breathable, completely recyclable, can be dyed and printed in any color, you can make it waterproof, windproof, fireproof etc.
Warp Yarn
Polyester (PL) HT 275 dtex 48 filaments 400 Z twists
Weft Yarn
96 Polyester filaments (PL) HT 550 dtex arranged in a spiral pattern (330 twists per meter, TPM) around a 78 dtex elastomer (EA)
94% Polyester (PL) HT 550 dtex+6% 78 dtex elastomer (EA)
Final titre 580 dtex
The upper fabric has been made on looms usually used for the weaving of this type of articles, applying a multiple weave (double double-sided) of 10 threads superimposed in the warp and 5 wefts superimposed in the weft as shown in
The resulting fabric has a warp reduction of 70 threads/cm±5% and a weft reduction of 80 threads/cm±5%, a weight of 800 g/m2 and a thickness of 1.40 mm and has shown a abrasion resistance according to EN 13595>5 seconds (level 1).
The fabric is elasticized, machine washable, breathable, completely recyclable, can be dyed and printed in any color, you can make it waterproof, windproof, fireproof etc.
Warp Yarn
Polyester (PL) HT 275 dtex 48 filaments 400 Z twists
Weft Yarn
96 Polyester (PL) HT filaments 550 dtex arranged in a spiral pattern (330 twists per meter, TPM) around a 78 dtex elastomer (EA)
94% Polyester (PL) HT 550 dtex+6% 78 dtex elastomer (EA)
Final titre 580 dtex
The fabric has been realized on looms usually used for weaving this type of article, applying a multiple (double) weave of 10 threads superimposed in the warp and 2 wefts superimposed in the weft as shown in
The resulting fabric has a warp reduction of 70 threads/cm±5% and a weft reduction of 62 threads/cm±5%, a weight of 600 g/m2 and a thickness of 1.1 mm and shown an abrasion resistance according to EN 13595>4 seconds (level 1).
The fabric is elasticized, machine washable, breathable, completely recyclable, can be dyed and printed in any color, you can make it waterproof, windproof, fireproof etc.
Warp Yarn
68 filaments of Polyamide (PA) HT 220 dtex arranged in a spiral around an elastomer (EA) of 78 dtex
91% Polyamide (PA) HT 220 dtex+9% elastomer (EA) 78 dtex Final titer 250 dtex
Weft Yarn
96 filaments of Polyester (PL) HT 550 dtex arranged in a spiral (330 twists per meter, TPM) around an elastomer (EA) of 78 dtex
94% Polyester (PL) HT 550 dtex+6% elastomer (EA) 78 dtex Final titer 580 dtex
The fabric has been made on looms usually used for the weaving of this type of articles, applying a multiple weave of 2 superimposed threads in the weft and 10 superimposed threads in the warp as shown in
The resulting fabric has a warp reduction of 65 threads/cm±5% and a weft reduction of 65 threads/cm±5%, a weight of 600 g/m2 and a thickness of 1.00 mm and demonstrated an abrasion resistance in accordance with EN 13595<4 seconds.
The fabric is elasticized, machine washable, breathable, completely recyclable, can be dyed and printed in any color, you can make it waterproof, windproof, fireproof etc.
Upper Fabric
The upper fabric is constituted by a protective fabric according to the invention, in particular coupled protective fabrics have been realized in which the upper fabric is constituted by the fabric according to examples 1 and 4.
Lower Fabric
Yarn A of Warp and Weft
96 filaments of Polyester (PL) HT 550 dtex arranged in a spiral (330 twists per meter, TPM) around an elastomer (EA) of 78 dtex
94% Polyester (PL) HT 550 dtex+6% elastomer (EA) 78 dtex
Final titer 580 dtex
Yarn B of Warp and Weft
130 filaments of UHMWPE (Dyneema®)/Polyamide (PA) arranged in a spiral around an elastomer (EA) of 78 dtex
44% UHMWPE+48% PA+8% EA
Final titer 450 dtex
The lower fabric has been made on looms usually used for weaving this type of articles, applying a simple canvas weave and inserting the yarns A and B to design 1A-1B as shown in
The resulting lower fabric has a warp reduction of 22 threads/cm and a weft reduction of 22 threads/cm, a weight of 300 g/m2 and a thickness of 0.40 mm.
Coupling
The upper fabric is purged in width, operation carried out with water and addition of possible detergent soaps, at a temperature of 90° C., to eliminate all impurities present in the fabric and favor the re-entry and closure of the fibers, that in this case can be very high thanks to the preferred presence of the elastomer both in the weft and in the warp, about 25% in both directions, after washing it is dried with a passageway in ramosa at a temperature of 165° C., speed of 25 m/min, then always in ramosa it is thermofixed at a temperature of 180° C., a speed of 25 m/min, to give permanent stability for all subsequent procedures (coupling, dyeing, printing, finishing, industrial washing or domestic washing, etc.); after thermofixing, proceed with the equalization, a roll-up operation with application of steam, to homogenize the surface and allow the fabric to recover soft, hardened and strain hardened by the thermofixing.
The lower fabric is purged in width exactly as described above for the upper fabric, but the drying and thermofixing phase is carried out in tumbler, the industrial equivalent of the domestic dryer, which works at temperatures below 100° C., but with a important mechanical action given by the centrifuge basket, which determines the maximum re-entry of the fibers, to obtain the same results in terms of dimensional stability of the ramosa. For this fabric tumbler drying is required when the Dyneema® fiber (UHMWPE) is present inside the fabric, because above 110° C. it starts to soften and then melts, completely losing the characteristics that make it one of the fibers more resistant to abrasion, cut and tear on the market. This operation is more expensive and lengthy compared to the thermofixing in ramosa, reason why, if not required for technical reasons, it is preferably avoided. Once the 2 tissues have been prepared as described above, we can proceed with reactive polyurethane (PUR) coupling by point using an amount of PUR equal to 30-50 g/m2.
This operation is carried out on cold, on a machine where the thermoplastic PUR is melted from the pressing plate heated to about 115° C. (accessory external to the machine) and pushed by a pump to the micro-perforated cylinder for application on the fabrics, immediately after the application of the glue, the 2 coupled fabrics are crushed by a calender that applies a pressure of about 2.5 tons and immediately rolled up to form a large roll, which remains stationary to cross-link in a heated environment where the temperature must never fall below 15° C. (limit temperature that crystallizes the PUR making it ineffective), the cross-linking time depends on the external temperature, at 20° C. 24 h of cross-linking is enough (the minimum time below which it cannot be lowered), below the 20° C. the cross-linking time proportionally lengthens with decreasing temperature.
The resulting coupled fabric has, in the case of coupling with upper fabric as ex. 4, a weight of less than 1000 g/m2 and a thickness of less than 1.5 mm and has demonstrated an abrasion resistance according to EN 13595 Standard>16 seconds.
The fabric is elasticized, machine washable, breathable, completely recyclable, can be dyed and printed in any color, you can make it waterproof, windproof, fireproof etc.
| Number | Date | Country | Kind |
|---|---|---|---|
| PCT/IB2018/053519 | May 2018 | IB | international |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2019/054092 | 5/17/2019 | WO | 00 |