This application is a Section 371 submission of international application PCT/FR2005/051098 filed Dec. 16, 2005, and published, in French, as international publication WO 2006/070147 A2 on Jul. 6, 2007, which claims priority of French application 0453145 filed Dec. 22, 2004, which applications are hereby incorporated herein by reference, in their entirety.
The present invention relates to a novel composition based on high molecular weight water-soluble acrylamide copolymers for sizing textile yarns (or fibres). The invention applies particularly well to the sizing of natural fibres, particularly of the cotton type, optionally in the presence of artificial fibres, in particular polyester.
In the textile industry, during weaving operations, the yarns or fibres are subjected to repeated stretching. Yarn stretching can cause breakage. The elongation capacity of the yarn. must therefore be exploited, depending on its type.
In addition to the stretching, other stresses exist. These are essentially:
The use of sizing products is known to protect yarns against these damaging forces and to improve their strength.
To obtain good results, the size must be selected taking account of the following properties:
Moreover, the sizing must not damage the yarn and the liquor must comprise compatible products exclusively. Furthermore, the comb must not be subject to size deposits which, by hardening, could act as abrasives on the yarns.
It should be noted that sizing is an intermediate finish, which is removed after the weaving operation. This operation precedes the finishing of the fabric, after which the size is completely removed. This may prove to be very pollutant because of the releases generated. It is therefore advantageous to have a product which has good solubility for desizing.
Conversely, documents EP-A-262 945 and U.S. Pat. No. 6,736,865 describe products for treating not individualized yarns, but finished woven textiles.
Document EP-A-262 945 thus describes a product combining an acrylamide polymer in the presence of other types of polymers for fastening colour to the previously woven fabric.
Document U.S. Pat. No. 6,736,865 describes a product based on acrylamide in the presence of other components for treating finished textiles to confer crease resistance and dimensional stability, particularly at the time of colour fastening.
In the paper field, document JP 60258244 describes the possibility of making a sheet water-repellent during formation, by treating the paper (and not textile) fibres using a mixture of a cetene and an acrylamide polymer.
The choice of the size mainly depends on the type of chain, and also taking account of the type of weaving:
The main types of basic products usable as sizing agents are natural or synthetic polymers, which are classed as follows:
however, they are also found in combination with starches or cellulose derivatives for natural fibres and mixtures thereof.
Sizing agents of the acrylic type are obtained by homopolYmerization or copolymerization of various derivatives of acrylic acid or methacrylic acid with other monomers such as styrene, vinyl acetate, acrylamide, etc. By an appropriate choice and dosage of the monomers, synthesis produces macromolecular substances, whereof the physical properties can be varied in a very wide interval. This explains the many sizing applications of various yarns: polyamide, polyester, cellulose. The main properties which they provide are:
However, many constraints apply concerning the use of the abovementioned sizing agents. In particular, they are often associated with the quantities required for these sizes to be effective, and with their low activity when used alone on natural fibres.
The problem faced is therefore to find a novel sizing product for sizing natural and/or artificial fibres on dry looms, and which meets the requirements of the industry, that is:
A sizing liquor has now been found for natural and/or artificial textile fibres in the form of an aqueous solution having at least equivalent performance to that of the preexisting compositions, but with significantly lower doses of sizing agent.
A primary subject of the present invention is a temporary sizing agent for natural and/or artificial individualized textile fibres, particularly of the cotton and/or cotton polyester type, characterized in that it comprises a water-soluble homopolymer or copolymer of at least one acrylamide monomer having a molecular weight of at least I million, advantageously above 3 million.
In an advantageous embodiment, the sIzmg agent IS exclusively made of an acrylamide homopolymer or copolymer.
As well known to a person skilled in the art, the larger the quantity of size deposited, the higher the percentage load of the wastewater of the textile plant.
It has been found surprisingly that obtaining an acrylamide based polymer, having a molecular weight above 1 million and having a low ionicity (cationicity and/or anionicity), in practice lower than 10 mol %, preferably lower than 5 mol %, makes it possible, particularly for cotton fabrics and also in the case of mixed polyester/cotton yarns, to obtain considerable savings both in terms of the liquor concentration of the sizing agent and during the de sizing step.
The sizing agent of the invention is obtained in particular by polymerization (or respectively copolymerization, both referred to as “polymerization” throughout the text and the claims) of at least one nonionic monomer of the acrylamide type and optionally other ionic monomers, and advantageously has a UL viscosity above 3.
The polymers of the invention do not require the development of a particular polymerization method. They can be obtained by all polymerization techniques well known to a person skilled in the art (solution polymerization, gel polymerization, precipitation polymerization, emulsion polymerization (aqueous or reverse), followed or not by a spray drying step, suspension polymerization, micellar polymerization, followed or not by a precipitation step).
According to the invention, the water-soluble (co)polymer serving as a sizing agent is obtained from.
A non-limiting list of ionic monomers suitable for use is given below:
A non-limiting list of sizing agents is given below: methylene bisacrylamide (MBA), ethylene glycol di-acrylate, polyethylene glycol dimethacrylate, diacrylamide, cyanomethylacrylate, vinyloxyethylacrylate or methacrylate and formaldehyde, glyoxal, compounds of the glycidylether type such as ethylene glycol diglycidylether, or epoxys or any other means well known to a person skilled in the art and permitting cross-linking.
A non-limiting list of transfer agents is given below: isopropyl alcohol, sodium hypophosphite, mercaptoethanol, etc.
A person skilled in the art will know how to select the best combination according to his own knowledge and the present description, as well as the following examples.
The invention further relates to a sizing liquor comprising the sizing agent as described above at the rate of less than 2% by weight of dry matter, preferably less than 1.5% by weight.
The present invention further relates to a method for sizing/de sizing natural and/or artificial textile fibres, whereby the said fibres are immersed in the liquor described above, and then, after weaving, the fibres are de sized using hot water only.
The concentration of sizing agent in the liquor may vary within the range described above, according to the apparatus employed for the performance of the sizing cycle, particularly the squeezing capacity of the rolls, and the quantity of size to be applied to the yarns. It is known that this depends partly on the strength of the yarns, which itself depends on their texturizing, their degree of twisting, the number of strands per unit yarn, and also on the adhesion of the sizing product to the yarns to be treated.
One of the advantages of the inventive compositions resides in the fact that they provide coatings having good protective power and high adhesive power to the textile yarns of the cotton or polyester/cotton type; accordingly, a concentration equal to 2% by weight or less, preferably less than 1.5%, of the composition is sufficient for all applications, including the most difficult yarns to size.
A deposit representing a larger quantity is perfectly conceivable, but it adds no real advantages and may even be detrimental.
The weft yarns sized in the conditions of the invention have a sufficient strength for subsequent dry weaving operations. The unit strands are correctly bonded and no unravelling or breakage of the yarns, nor fouling of the looms, is observed.
After the weavmg, the desizing stage according to the invention takes place characteristically with hot water. It is completed by drying.
The size compositions according to the invention may be prepared both before their use for sizing and stored, or on contrary, immediately before their use, from their components.
The examples below illustrate the invention without limiting it.
Data of the Polymers used During the Tests as Sizing Agent
The UL viscosity is measured using the Brookfield viscometer (UL type module) at a speed of 60 rpm and at a temperature of 25° C. on a salt solution (1 M NaCl) of polymer containing 0.1% concentration (dry weight).
Data on the Sizing Tests Performed
After having placed the polymer in solution in the water at the desired concentration, the solution is then stirred for a few minutes, the composition is then ready for use to prepare a sizing liquor.
Various chains of yarns are immersed in this liquor, and then drained by passage between two cylinders followed by drying.
The table below gives the test conditions:
Results
The weaving carried out using the yarns described above takes place in satisfactory conditions without unravelling or strand breakage. After weaving, the fabric is treated wide and unwound into a hot water bath at 50° C. and then dried (desizing operation).
Immediately after this treatment, the fabrics are conventionally dyed. The finished, dried fabric was very flexible; it also revealed excellent colour uniformity and good resistance to washing and light.
Comparatively, a sizing was carried out in strictly identical conditions to the above, but using sizing products currently available on the market of the types—sodium acrylate homopolymer (MW: 800 000 and 350 000) and acrylamide homopolymer (MW: 800 000 and 350 000).
It was found that to obtain equivalent sizing quality as obtained with the polymers of the invention (no unravelling nor yarn breakage) on the same natural or mixed fibres, it was necessary to use these polymers in very high concentrations:
Conclusion
According to the present invention, it has been discovered surprisingly that the high molecular weights of the water-soluble acrylamide (co)polymers of the invention confer on the sizing liquor:
| Number | Date | Country | Kind |
|---|---|---|---|
| 04 53145 | Dec 2004 | FR | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/FR2005/051098 | 12/16/2005 | WO | 00 | 2/20/2009 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2006/070147 | 7/6/2006 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4413087 | Bernot | Nov 1983 | A |
| 6736865 | Danner et al. | May 2004 | B1 |
| Number | Date | Country |
|---|---|---|
| 0066078 | Aug 1982 | EP |
| 0262945 | Jun 1988 | EP |
| 0659929 | Jun 1995 | EP |
| 60258244 | Dec 1985 | JP |
| Number | Date | Country | |
|---|---|---|---|
| 20090249596 A1 | Oct 2009 | US |