Patent Grant
10405593
Provided is a glove formed by latex dipping having one or more textured finger tips wherein: the texture at one or more finger tips results from forming the glove on a former having the following properties at the corresponding finger tip regions:
the glove being non-chlorinated, wherein the glove is a (i) single dip nitrile glove or (ii) a dipped glove with a textured layer formed of polymer latex (e.g., natural rubber latex or another rubber latex, or mixtures), and comprising a multivalent metal ion salt of an organic acid with log P of about 4 to about 15.
Provided is a method of making such a glove comprising: coating a glove former with coagulant; applying a coagulable elastomer formulation to the coagulant coated former so that the former is coated with coagulated elastomer; and curing the elastomer coating, wherein former has the following properties at the corresponding finger tip regions:
Also provided is a former for making a glove (such as a single dip nitrile glove) having one or more textured finger tips wherein the former has the following properties at the corresponding finger tip regions:
So that the manner in which the above recited features of the present invention can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only illustrative embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.
To facilitate understanding, identical reference numerals have been used, where possible, to designate comparable elements that are common to the figures. The figures are not drawn to scale and may be simplified for clarity. It is contemplated that elements and features of one embodiment may be beneficially incorporated in other embodiments without further recitation.
The glove has one or more textured finger tips. texturing can be on one side, since the gripping side of a finger is on one side. However, it will often be convenient to form the grip on both sides. Grip texture can be at a finger tip, such as about 50% of the way down to the first knuckle crease. Or, texture can be found further down the finger. In embodiments, 2, 3, 4 or 5 fingers have texture. Texture can be formed more generally, but is particularly useful at the finger tips.
In embodiments elastomeric layer is primarily acrylonitrile butadiene copolymer (NBR or “nitrile”) by polymer content weight (e.g. 80% or more), thus forming for the purposes of this application a “nitrile glove.’ Other polymers may be natural rubber latex (including Guayule latex), other synthetic rubber latex, or the like, and combinations thereof. The synthetic rubber latex may be selected, for example, from the group comprised of polychloroprene, polyisoprene, polyurethane, styrene-butadiene, butyl, and combinations thereof. The nitrile can include carboxylated acrylonitrile butadiene copolymer. In embodiments, it is highly carboxylated.
The texture at the finger tips results from forming the glove on a former having one or more of the following values (from about value A to about value B):
In embodiments, Ra is about 9, 10, 11 or 12. In embodiments, Rsm is about 500, 630, 650 or 670. In embodiments, Rpc is about 17, 18 or 19.
In embodiments, the former of the invention and used in the invention has one or more of the following roughness properties (from about value A to about value B):
In embodiments, Rz is 34, 38, 40 or 42. In embodiments, Rmax is about 47, 53 or 60. In embodiments, Rp is about 13, 15, 17 or 20. In embodiments, Rv is 20, 21, 24 or 27.
The above parameters are as measured by a Perthometer (Mahr GmbH, Göttingen, Germany), with the stylus running at constant speed across 0.22 in (5.6 mm) length of surface. The Roughness profile R describes the departure from the mean line. The average roughness is calculated as described is the arithmetic average of the absolute values of the roughness profile ordinates.
In embodiments, the former is ceramic.
Gloves formed on the above formers can be tested for falling within the claims by reverse molding. For example, the glove can be treated with a release agent if needed, inverted, and used as a mold for a self-curing polymer mixture that solidifies to sufficient hardness to allow for measurement with the Perthometer device. Perthometer values within the above ranges indicate that the former used falls within the above values.
It is believed that better results are obtained in the manufacturing process if the temperature of the leaching process is about 50° C., such as about 45 to about 55° C. The temperature of the gelling (vulcanization) oven can about 120 to about 160° C., such as 125°, 135°, 145° or 155°.
It is believed that better results are obtained in the manufacturing process if the coagulant used in the dipping step includes a fatty acid salt. For example, the following can be used:
In methods of the invention, the coagulant composition can for example comprise multivalent metal ion salt of an organic acid with log P of about 4 to about 15. In all embodiments with an organic acid salt, the organic acid can a for example C14 to C30 fatty acid (whether or not within the log P parameters). In all embodiments with an organic acid salt, the organic acid can be a for example C16 to C20 fatty acid. In all embodiments with an organic acid salt, the multivalent metal ion can be for example Ca, Mg, Zn or Al. In all embodiments with an organic acid salt, the multivalent metal ion can be Ca. In all embodiments with an organic acid salt, such a salt can for example comprises about 5 to about 50% by wt (e.g., 18%) of coagulant compounds in the coagulant composition.
In embodiments, the gloves of the invention comprise a multivalent metal ion salt of an organic acid consistent with any of the above (e.g., C14-C30, even if not with above log P range). The amount present can be the residue remaining after a post-dipping leaching or washing.
In embodiments of the gloves that contain the fatty acid salt (by any definition herein), the polymer of the outer layer can be natural rubber latex (including Guayule latex), other synthetic rubber latex, or the like, and combinations thereof. In embodiments, such a glove is a single dip glove.
In step 210 (optional), the article on the dipped former is leached. For example, leaching can be conducted at a moderately elevated temperature that effects some cross-linking. In step 212, the article on the former is cured. In step 214 (optional), the article (typically after stripping from the former) is washed and dried.
Principle of the Test Method
The method uses a 1.0 kg or 1.5 kg weight (e.g., metallic), and measures “Pull Force” needed to grip test bar for lifting the weight, and a “Catch Force” needed to re-grip the test bar after letting it slip.
The test is used to measure the pinch grip performance of glove in grip force (kgf) in a systematic pattern of a pinch grip task. The subject uses only the tips of the first finger and thumb to grip the grip bar. Sufficient grip force between the finger and thumb is required to enable the grip bar to be held in control so that it can then be pulled down in a fixed distance without slipping (“Pull Force”). The pulling down action effectively lifts a specific mass (1.0 kg or/and 1.5 kg) on the other side of a pulley. The grip bar is then released, allowed to slip and then re-gripped (“Catch Force”). Finally the grip bar is returned to the stationary initial position in a controlled manner. The grip bar is wetted with water or covered with oil when performing wet or oil pinch grip test respectively.
With gloves of the invention, the following oil grip values were obtained:
With gloves of the invention, the following dry grip values were obtained:
With gloves of the invention, the following wet grip values were obtained:
With gloves of the invention, the following IPA grip values were obtained:
In embodiments, gloves of the invention achieve grip values of about 1.5× the values listed above (rounded to the nearest 0.01 value) or less, or about 1.4× or less, or about 1.3× or less, or about 1.2× or less, or about 1.1× or less. In embodiments, gloves of the invention achieve grip values of about 0.5× the values listed above (rounded to the nearest 0.01 value) or more, or about 0.7× or more, or about 0.85× or more. These values apply to gloves of any of the embodiments described above.
Formers for use in the invention can be manufactured by casting, selectively sandblasted to form texture, or the like.
All ranges recited herein include ranges therebetween, and can be inclusive or exclusive of the endpoints. Optional included ranges are from integer values therebetween (or inclusive of one original endpoint), at the order of magnitude recited or the next smaller order of magnitude. For example, if the lower range value is 0.2, optional included endpoints can be 0.3, 0.4, . . . 1.1, 1.2, and the like, as well as 1, 2, 3 and the like; if the higher range is 8, optional included endpoints can be 7, 6, and the like, as well as 7.9, 7.8, and the like. One-sided boundaries, such as 3 or more, similarly include consistent boundaries (or ranges) starting at integer values at the recited order of magnitude or one lower. For example, 3 or more includes 4 or more, or 3.1 or more.
This invention described herein is of textured gloves, methods of forming the same, and formers for making the gloves. Although some embodiments have been discussed above, other implementations and applications are also within the scope of the following claims. Although the invention herein has been described with reference to particular embodiments, it is to be understood that these embodiments are merely illustrative of the principles and applications of the present invention. It is therefore to be understood that numerous modifications may be made to the illustrative embodiments and that other arrangements may be devised without departing from the spirit and scope of the present invention as defined by the following claims.
Publications and references, including but not limited to patents and patent applications, cited in this specification are herein incorporated by reference in their entirety in the entire portion cited as if each individual publication or reference were specifically and individually indicated to be incorporated by reference herein as being fully set forth. Any patent application to which this application claims priority is also incorporated by reference herein in the manner described above for publications and references.
This application is a divisional of U.S. patent application Ser. No. 14/880,718, filed on Oct. 12, 2015, which claims priority to U.S. provisional patent application Ser. No. 62/063,531, filed Oct. 14, 2014 and provisional patent application Ser. No. 62/100,610, filed Jan. 7, 2015. Each of the aforementioned patent applications is herein incorporated in its entirety by reference. The present application relates generally to nitrile gloves with molded texture at the finger tips, polymeric gloves with molded texture at the fingertips and containing a multivalent metal ion salt of an organic acid with log P of about 4 to about 15, and a method of making. In seeking to produce texture on the surface of a single dip polymeric glove by a texture structure found at the surface of the dipping former, it is extremely difficult to produce a glove that has good grip while being reliably formed without holes. It has now been unexpectedly found that good grip can be obtained by carefully selecting certain roughness parameters for the former.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5993923 | Lee | Nov 1999 | A |
| 6081928 | Bourne | Jul 2000 | A |
| 6143416 | Brindle et al. | Nov 2000 | A |
| 6732735 | Snell | May 2004 | B1 |
| 7771644 | Flather et al. | Aug 2010 | B2 |
| 20070126149 | Brown, III et al. | Jun 2007 | A1 |
| 20110191936 | Lipinski et al. | Aug 2011 | A1 |
| 20120137404 | Lipinski | Jun 2012 | A1 |
| 20130291283 | Hassan et al. | Nov 2013 | A1 |
| 20160100638 | Aziz et al. | Apr 2016 | A1 |
| Number | Date | Country |
|---|---|---|
| 1310711 | Mar 1973 | GB |
| Entry |
|---|
| International Search Report and Written Opinion dated Dec. 22, 2015 for PCT Application No. PCT/AU2015/000614. |
| Extended European Search Report dated May 3, 2018 for Application No. 15849952.5. |
| Number | Date | Country | |
|---|---|---|---|
| 20180303177 A1 | Oct 2018 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62100610 | Jan 2015 | US | |
| 62063531 | Oct 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14880718 | Oct 2015 | US |
| Child | 16020146 | US |