Patent Application
20220362966
This document describes stone slab products, and systems and processes for surface treatment of stone slab products, for example, stone slabs suitable for use in living or working spaces (e.g., along a countertop, table, floor, or the like) and having multiple regions of different particulate mineral mixes with differing surface characteristics.
Stone slabs are a commonly used building material. Granite, marble, soapstone, and other quarried stones are often selected for use as countertops due to their aesthetic properties. Stone slabs may also be formed from a combination natural and other materials that can provide improved stain-resistant or heat-resistant properties, aesthetic characteristics, reproducibility, etc. Some stone slabs have been made from a combination of particulate mineral material and binder, such as a polymer resin or cement, and have a colored or veined pattern.
Some embodiments described herein include systems and processes for forming stone slabs suitable for use in living or working spaces. In some optional embodiments, slabs can be manufactured by forming a cured and hardened slab, and then abrading one or more faces of the slab to reveal a tactile or visible texture that varies in relation to the composition of particulate mineral mixes of the slab. In some embodiments, a stone slab includes multiple regions of different particulate mineral mixes that have different tactile characteristics, such as different thickness, roughness, gloss, etc.
In an example embodiment, a processed slab is formed from a plurality of particulate mineral mixes, and includes a slab width that is at least 2 feet, a slab length that extends perpendicular to the slab width and that is at least 6 feet, the slab length and the slab width defining a top major surface, a slab thickness that extends perpendicular to the slab width and the slab length, the slab length greater than the slab width, the slab width greater than the slab thickness, and a first pattern defined by a first particulate mineral mix, the first pattern exposed along the top major surface of the slab, and defining a first thickness that extends perpendicular to the slab width and the slab length, and a second pattern defined by a second particulate mineral mix different from the first particulate mineral mix, the second pattern exposed along the top major surface of the slab and defining a second thickness that extends perpendicular to the slab width and the slab length, the first thickness of the first pattern different than the second thickness of the second pattern.
Various embodiments can include some, all, or none of the following features. The first pattern can be exposed along a bottom major surface of the slab. The first pattern exposed along the top major surface of the slab can have a first texture based on the first particulate mineral mix, and the second pattern exposed along the top major surface of the slab can have a second texture, different from the first texture, based on the second particulate mineral mix. The first texture can have a first roughness and the second texture has a second roughness that is different from the first roughness. The first pattern can have a first average gloss value and the second pattern can have a second average gloss value that is different from the first average gloss value. The first pattern can have a first average thickness perpendicular to the slab width and the slab length, and the second pattern can have a second average thickness perpendicular to the slab width and the slab length, and wherein the first average thickness is different from the second average thickness.
In an example implementation, a process of forming a processed slab from a plurality of different particulate mineral mixes includes dispensing a first particulate mineral mix to a first set of regions of a slab mold, dispensing a second particulate mineral mix to a second set of regions of the slab mold, contemporaneously vibrating and compacting the first particulate mineral mix and the second particulate mineral mix arranged in the slab mold so as to form a processed molded slab that is generally rectangular and has a slab thickness and a major surface having a slab width of at least 2 feet and a slab length of at least 6 feet, curing the processed molded slab into a cured slab, and abrading the major surface of the cured slab at locations of the first particulate mineral mix and the second particulate mineral mix with an abrading head to partly remove portions of the major surface such that the first particulate mineral mix in the first set of regions define a first thickness perpendicular to the slab width and the slab length, and the second particulate mineral mix in the second set of regions define a second thickness perpendicular to the slab width and the slab length.
Various implementations can include some, all, or none of the following features. The first particulate mineral mix can have a first hardness in the cured slab and the second particulate mineral mix can have a second hardness different from the first hardness in the cured slab. Abrading a portion of the major surface of the cured slab can include removing an amount of the major surface in the first set of regions to a first average thickness perpendicular to the slab width and the slab length that is different from a second average thickness removed from the second set of regions, wherein a first texture is based on the first average thickness and a second texture is based on the second average thickness. The first particulate mineral mix can include a first percent volume of quartz, and the second particulate mineral mix can include a second percent volume of quartz that is less than the first percent volume of quartz. One of the first set of regions and the second set of regions can define a majority of the major surface, and the other of the first set of regions and the second set of regions can define a vein extending at least partly across the major surface. Abrading the major surface of the cured slab can include abrading substantially an entirety of the major surface. Abrading the major surface of the cured slab can include abrading using an abrasive brush. The first set of regions can have a first texture and the second set of regions can have a second texture different from the first texture. The first texture can have a first roughness and the second texture can have a second roughness that is different from the first roughness. The first set of regions can have a first average gloss value and the second set of regions can have a second average gloss value that is different from the first average gloss value. The first set of regions can have a first average thickness perpendicular to the slab width and the slab length, and the second set of regions can have a second average thickness perpendicular to the slab width and the slab length, and wherein the first average thickness is different from the second average thickness. Abrading the major surface can include passing a sequence of different abrading brushes having different abrasive grits over the entirety of the major surface. Abrading the major surface can include passing the abrading head over the entire major surface with consistent operating parameters. Abrading the major surface can include passing a second abrading head over the entire major surface with consistent operating parameters.
The systems and techniques described here may provide one or more of the following advantages. First, a system can provide stone slab products that have a tactile and/or visible texture. Second, the system can provide stone slab products that have a texture that resembles that of quarried stone. Third, the system can provide stone slab products that have an aesthetic appeal similar to that of quarried stone and with improved performance benefits such as heat and stain resistance and reproducibility, but without the cost and/or environmental impact associated with stone quarrying. Fourth, the system can modify existing stone slab products to provide additional product options from a common base product.
The details of one or more implementations are set forth in the accompanying drawings and the description below. Other features and advantages will be apparent from the description and drawings, and from the claims.
In general, this document describes systems and techniques in which processed stone slabs having textured faces can be manufactured by abrading a cured (e.g., hardened) slab having exposed regions of different component materials that abrade or erode differently (e.g., at different rates when subjected to a common treatment), and/or otherwise reveal different textures due to the abrasion. For example, hardened materials are worn down in different manners to produce one or more different surface characteristics based on the component materials (e.g., and in an example embodiment does not include imparting a pattern into soft, uncured materials and then allowing the pattern to harden). In some embodiments, an example stone slab includes varying texture that caricatures natural erosion and fissuring and/or provides different characteristics that create a predetermined aesthetic and tactile characteristics.
Referring to
In various example embodiments, slab 50 includes any number, combination, pattern, and/or proportion of particulate fills and mixes. For example, the processed slab 50 can include two, three, four, five, ten, or any appropriate number of particulate mineral mixes to provide any appropriate number of regions (e.g., different perceptible patterns/veins). In another example, the primary fill 51 may not occupy a majority of the processed slab 50 (e.g., the processed slab 50 may include a substantially continuous collection of regions without any one of the particulate fill types occupying an identifiably primary or major portion of the volume of the processed slab 50). In some embodiments, processed slab 50 includes one or more regions 51, 52, 53 of different particulate mineral mixes and/or different surface characteristics (e.g., according to a predefined pattern).
The processed slab 50 has a width W and a length L (e.g., at least 2 feet wide by at least 6 feet long, and between about 3 feet and 5 feet wide and between about 6 feet and 14 feet long, preferably about 4.5 feet wide (more particularly, about 140 cm wide) by about 10 feet long (more particularly, about, 310 cm long)). In general, the length L and the width W define a top major surface 60 (e.g., face) and a bottom major surface (e.g., face) 61. The processed slab 50 also has a thickness T between the top major surface 60 and the bottom major surface 61. The periphery of the processed slab 50 includes a collection of edge faces 62.
Each slab 50 can comprise a quartz material and/or other particulate mineral material that, when mixed with pigments and a resin binder and subsequently compressed and cured, provides a hardened slab product suitable for use in living or working spaces (e.g., along a countertop, table, floor, or the like). As shown in
As shown in
The different mixes can be compaction molded and cured in the mold so as to provide the hardened slab 50. One or more of the mixes that are used to form the composite stone material can include organic polymer(s) and inorganic (mineral) particulate component. The inorganic (mineral) particulate component may include such components as silicon, basalt, glass, diamond, rocks, pebbles, shells, a variety of quartz containing materials, such as, for example, but not limited to: crushed quartz, sand, quartz particles, and the like, or any combination thereof. In this embodiment, all four different particulate mineral mixes each comprise a quartz material as a predominant component, which may include sand of various particle sizes and of different combinations. In the hardened, cured form of the slab 50, the organic and inorganic materials can be linked using a binder, which may include for example, mono-functional or multifunctional silane molecules, dendrimeric molecules, and the like, that may have the ability to bind the organic and inorganic components of the composite stone mix. The binders may further include a mixture of various components, such as initiators, hardeners, catalysators, binding molecules and bridges, or any combination thereof. Some or all of the mixes dispensed in the mold may include components that are combined in a mixing apparatus prior to being conveyed to the mold. The mixing apparatus can be used to blend raw material (such as the quartz material, organic polymers, unsaturated polymers, and the like) at various ratios. For example, some or all of the mixes dispensed in the mold 530 may include about 8-95% quartz aggregates to about 5-15% polymer resins. In addition, various additives may be added to the raw materials in the mixing apparatus, such additives may include metallic pieces (e.g., copper flecks or the like), colorants, dyes, pigments, chemical reagents, antimicrobial substances, fungicidal agents, and the like, or any combination thereof. In alternative embodiments, some or all of the quantity of quartz aggregates (mentioned above) can be replaced with or include porcelain and/or ceramic aggregate material.
The regions 51, 52, and 53 each have a different hardness and/or resistivity to abrasion when cured and hardened. In some embodiments, the differences in hardness and/or resistivity to abrasion can be due to differences in the properties and characteristics of the different particulate mineral mixes used in the formation of the slab 50, including particulate composition (e.g., quartz content, other mineral content, particulate size), binder content, pigment content, average particle size, average particle hardness, and/or average particle brittleness. In various example embodiments, one or more of the particulate mineral mixes has relatively higher percent volume of quartz compared to one or more of the other particulate mineral mixes. For example, the first particulate mineral mix (e.g., locations of primary fill 51) has a percent volume of quartz (Q1) between 50% and 95%, 65% and 85%, or about 75%. The second particulate mineral mix (e.g., locations of veins 52 and 53) has a percent volume of quartz (Q2) that is less than the percent volume of quartz of the first particulate mineral mix. In various example embodiments, Q2 is between 40% and 95%, 60% and 90%, or about 80% of Q1. Alternatively or additionally, other components of the particulate mineral mix can be controlled to provide different characteristics of the respective mineral mixes in the hardened slab. For example, in some embodiments, the first particulate mineral mix includes between 70% and 80% volume of quartz, between 0% to 10% volume of pigment, and between 10% and 20% volume resin binder. The second particulate mineral mix includes between 50% and 70% volume of quartz, between 10% and 30% volume pigment, and between 5% and 30% resin binder. In some embodiments, one or more pigmentation layers may be applied over and/or between the particulate mineral mixes. For example, some pigmentation layers may include relatively low volumes of quartz (e.g., between 5% and 30%) and relatively high volumes of pigment (e.g., between 10% and 30%) and/or resin binder (e.g., between 50% and 70%). Such relative compositions of first and second particulate mineral mixes facilitate different response to abrasion operations that facilitates a finished surface having regions of distinct texture, gloss, thickness, and/or other perceptible surface characteristics associated with locations of the respective particulate mineral mixes. In some embodiments, various mineral particulate components are included, such silicon, basalt, glass, diamond, rocks, pebbles, shells, a variety of quartz containing materials, such as, for example, but not limited to: crushed quartz, sand, quartz particles, and the like, or any combination thereof, to facilitate a predetermined response to abrasion operations.
In some embodiments, the regions 51 can define a majority of the major surface 60, and regions 52 and 53 can define one or more veins extending at least partly across the major surface 60. For example, the primary fill can occupy the regions 51 within the slab 50, and other particulate mineral mixes form the regions 52 and 53, which extend partly or entirely across the surfaces and edges of the slab 50.
In some implementations, substantially the entire major surface 60 can be abraded substantially uniformly. For example, the same type and duration of abrasion can be applied across the entire major surface 60 (e.g., causing substantially all of the primary fill exposed at the major surface 60 in the regions 51 to erode to substantially the same average depth, and causing the regions 52 and 53 to each erode to their own respective average depths across the entire major surface 60).
In some implementations, the first set of regions can have a first texture and the second set of regions can have a second texture different from the first texture. For example, the region 51 may have a smooth, glossy texture, while the regions 52 and/or 53 may have a relatively rougher, matte texture.
The primary fill 51, the veins 52, and the veins 53 are formed from different mineral particulate mixes having different physical characteristics, such as different cured hardnesses, textures, and/or resistances to abrasion in the processed slab 50. As such, the primary fill 51, and the veins 52 and 53 define different regions of different cured harnesses, textures, or resistances to abrasion across the top major surface 60. When subjected to abrasion by the abrasive brush 200, the primary fill 51, the vein 52, and the vein 53 erode or otherwise react to the abrasion at relatively different rates and/or in different manners.
In an example embodiment, the veins 52 and 53 are relatively susceptible to the abrasion of brush 200 and relatively more material is removed at locations of veins 52 and 53 as compared to region 51 (e.g., during each pass of brush 200 and/or over the course of an entire abrading operation). For example, the vein 52 erodes to an average thickness T2 and the primary fill 51 erodes to an average thickness T1. In some embodiments, the major fill 51 can be relatively less resistant to abrasion than the veins 52, 53, to provide a substantially inverse effect (e.g., with the primary fill having an average thickness T2 and the veins 52, 53 having an average thickness T1). As such, after abrasion, the major top face 60 has a thickness that varies between locations of primary fill 51 and veins 52 and 53 (e.g., relative to an average thickness of the processed slab), and includes peaks, valleys, and plateaus that can be felt and/or seen. In some embodiments, the resulting texture can have a matte finish appearance and/or texture, a gloss finish appearance and/or texture, or combinations of both (e.g., a primarily glossy surface with matte textured veins running across it).
In some implementations, abrading the major surface 60 of the cured slab 50 can include abrading by at least one of an abrasive brush and mechanical application of an abrasive fluid compound. For example, the example abrasion brush 200 can be used to apply a fluid compound containing abrasive material to the major surface 60.
In some implementations, each of the textures can be defined by one or more of roughness, gloss, and average thickness extending perpendicular to the slab width and the slab length. For example, the region 51 and the regions 52, 53 can each be made up of mineral particulate mixes that each have particles that are more rounded or more faceted in shape, or have particulates or binders that have relatively different in terms of light absorption and reflectivity, or exhibit relatively different levels of receptivity to polishing. In another example, as described above, the texture can be defined by some areas having different thicknesses than others (e.g., the example veins 52, 53 have an example thickness of T2 whereas the example primary fill has an example thickness of T1, resulting in boundaries where the transitions between the different thicknesses can be felt or seen).
The slab 300 has a major surface (or face) 310 that is generally defined by an average thickness T1 of a primary fill 351 (e.g., a particulate mix that makes up a majority of the volume of the slab 300). A collection of veins 352 and a collection of veins 353 extend partly and/or entirely across the major surface 310 and/or through the thickness of the slab 300. The veins 352 are recessed below the major surface 310 to an average thickness T2, and the veins 353 are be recessed below the major surface 310 to an average thickness T3 that is different from T1 and/or T2. The difference between the thicknesses T1 and T2 provide the major surface 310 with a three-dimensional texture that can be felt and/or seen. In various example embodiments, the difference between T1 and T2 is in a range between 0.01 mm and 10 mm, 0.1 mm and 2 mm, or about 0.5 mm. In some embodiments, the rear major surface of slab 300 is substantially flat across primary fill 351, and veins 352 and 353, and an average depth of the veins 352, 353 below the major surface 310 is approximately equal to the difference between T1 and T2.
In the illustrated example, the veins 352 and 353 are made of two different particulate mineral mixes in addition to the primary fill 351, such that the slab 300 include first, second, and third particulate mineral mixes that each differ in one or more characteristics. Alternatively or additionally, slab 300 may include two, three, or more than three particulate mineral mixes that each differ in one or more characteristics.
Referring to
Referring now to
The conveyor 510 transports the slab molds 530 to a dispenser 560 (e.g., a mineral aggregate distributor). In the illustrated example, the dispenser 560 is configured to release different particulate mineral mixes (e.g., different cured resistances to abrasion, different textures, different pigments, different mineral compositions, different additives, or a combination thereof). In some embodiments, multiple dispensers 560 may be used (e.g., each dispenser configured to dispense different particulate mineral mix or combination of mixes).
The slab mold 530 receives the different mineral mixes (comprising mostly a quartz material as described above) from the dispenser(s) 560. For example, the dispenser 560 can be configured with a shutter or valve apparatus that is controllable to regulate the flow of particulate mineral mix from the dispenser 560 for input to the slab mold 530. In some embodiments, the dispensing heads (or other inputs for distributing the particulate mineral mixes to the slab mold 530) can be controlled according to a predetermined control algorithm so as to define successive layers or regions of the different particulate mineral mixes for dispensation into the slab mold 530. In the illustrated example, the slab mold 530 is filled with a primary fill 591 and two other different types of particulate mineral mixes to create two different types of patterns such as a vein 592 and a vein 593.
In some examples, multiple dispensers 560 can be used to dispense different particulate mixes into different regions of the slab. The slab may be formed from a number of different particulate mineral mixes, such as between 2 and 20 different particulate mineral mixes (e.g., and the system includes a corresponding number of dispensers 560 or a single dispenser 560). In some examples, the number of dispensers 560 can correspond equally to the number of differently pigmented particulate mineral mixes used to create the slab product.
The filled molds 580 are then moved to one or more sequent stations in the system 500 for forming the hardened slab. For example, each of the filled molds 580 can continue to a subsequent station in which a top mold attachment 594 is positioned over the filled mold 580 so as to encase the layers of particulate mineral mixes between the slab mold 530 and a top cover mold piece. From there, the filled mold 580 (e.g., including the top cover mold piece) advances to a subsequent station in which a vibro-compaction press 595 applies compaction pressure, vibration, and/or vacuum to the contents inside the filled mold 580, converting the particulate mixes into a rigid slab. The filled mold is subjected to a curing station 596 in which the material used to form the slab (including any resin binder material) are cured via a heating process or other curing process, strengthening the slab inside the filled mold 580. After the slab is fully cured (and, optionally, after the slab is cooled), the slab mold 530 and the top mold cover piece are removed from the hardened and cured slab at a mold removal station 597. The slab mold 530 is then returned to the conveyor 510. The hardened and cured slab is moved to a surface treatment station 598, in which a major surface of the slab is abraded, to reveal a complex abraded surface having a predetermined texture and pattern. In some embodiments of the system 500, the abraded or otherwise exposed major surface of each of the processed molded slabs can provide an outer appearance that is substantially repeatable for the other slabs (from the other filled molds 580 in
A collection of hardened and cured slabs 630 (e.g., the hardened and cured slabs removed at the example mold removal station 597) are transported on a conveyor 610 to a surface treatment station 640. The hardened and cured slabs 630 include a primary fill 691 (e.g. the primary fill 51 of the example slab 50, the primary fill 591 after it has been cured and hardened, etc.), and/or one or more regions 692 and 693. In an example embodiment, the primary fill 691 is made of a first particulate mineral mix that differs in one or more characteristics as compared to second and third particulate mineral mixes 692, 693. For example, the hardness, brittleness, resistance to abrasion, and/or other characteristics differs between the first particulate mineral mix compared to the second and/or third particulate mineral mix.
The surface treatment station 640 modifies a major surface 632 of the hardened and cured slabs 630. For example, the surface treatment station 640 includes one or more abrasive brushes 642 configured to contact the major surface 632 vertically and rotate about a rotational axis arranged substantially perpendicular to the major surface 632. The one or more abrasive brushes 642 rotate in contact with the major surface 632 as they are drawn across the major surface to provide substantially the same amount (e.g., duration) of abrasion to all areas of the major surface 632. In an example embodiment, the movement of the one or more brushes 642 across the major surface 632 is independent of the region of the slab (e.g., independent of whether the brush is in contact with 691, 692, 693). One or more abrasive fluid compound applicators 644 can be used to apply abrasion promoters and/or water to the areas being treated to modify the action of the abrasive brushes 642, to control the temperature of the process, and/or to reduce the production of dust. The selection of brush type, vertical pressure, rotational speed, lateral direction, lateral pattern, abrasive grit, water flow, and slab advancement speed can all be controlled to further control the abrasion process. In some implementations, the abrasion process may be applied evenly to provide a uniform level of abrasion, or it may be applied unevenly across the major surface 632 to provide an intentionally non-uniform level of abrasion. In various example embodiments, the one or more abrasive brushes include silicon carbine, diamond, or other abrasive brushes such as diamond abrasive brushes available from Tenax USA of Charlotte, NC. In some embodiments, a series of brushes having differing abrasive grit ratings are used in sequence. In some embodiments, abrasive brush application pressures are between 0.5 bar to above 8.0 bar, between 0.8 bar to 4 bar. In some examples, the abrasive brushes 642 can be spun at speeds ranging from 200 RPM to 1500 RPM, 300 RPM to 1200 RPM, or between 400 RPM to 550 RPM. In some implementations, water is applied to the abrasion site at flow rates ranging from zero to 4 gallons per minute or more. In some embodiments, the abrasive brushes 642 are advanced across the major surface 632 at speeds ranging from below 9000 to above 18000.
As the abrasive brushes 642 abrade the major surface 632, small amounts of the major surface 632 are removed to provide a processed major surface 652 of a processed stone slab product 650. The particulate mineral mixes in regions 691, 692, 693, abrade at different rates and/or in different manners (e.g., based on different hardness, particle size, resistance to abrasion, etc.).
In some example embodiments, the primary fill 691 is harder and/or more abrasion-resistant than the veins 692, 693 such that the areas of the veins 692, 693 exposed at the major surface 632 (e.g., face areas) recede below a plane generally defined by the primary fill 691. The resulting processed slab has a slab thickness that varies (e.g., between regions 691, 692, 693), with the average thickness of the primary fill 691 (e.g., T1 of
In some example embodiments, the primary fill 691 is softer or less abrasion-resistant than the veins 692, 693, the areas of the major surface 632 exposed at the major surface 632 may recede below bumps and mounds made up of the veins 692, 693. For example, the exposed surface can resemble the appearance of a topographical or relief map of a plain with hills or mountain ranges rising from it.
In some example embodiments, the vein 692 is softer than the primary fill 691, and the vein 693 is harder than the primary fill 691. The resulting texture of the major surface has features that are both raised (e.g., vein 693) and recessed (e.g., vein 693) relative to the average thickness. The processed major surface 652 has a texture that can be seen and/or felt due to the differences in average slab thicknesses in regions of the primary fill 691, the vein 692, and the vein 693.
In some embodiments, the processed stone slab product 650 produced by the example system 600 can be the example processed slabs 50, 300, 400, of
In some example embodiments, the system 600 includes a calibration station arranged before or after the surface treatment station 640. For example, the major surfaces 632 of the cured slabs 630 can polished, planed, smoothed, and/or otherwise provided with a substantially even surface across the entire major surface 632 prior to being abraded. In another example, the processed major surfaces 652 of the cured slabs 630 can be partly polished, planed, smoothed, or otherwise modified to have a collection of plateaus that define a substantially common plane across the processed major surface 652. In some example embodiments, such steps may be omitted (e.g., the abrasion is performed on the major surface 632 in the form that exists after mold removal 597 without subjecting the slab to an intermediate planning or calibration operation).
Referring to
Referring to
In some embodiments, the example systems 600-800 may also use an abrasion promoter, such as an abrasive liquid or paste. In some embodiments, surface treatment stations may use a substantially non-abrasive brush or pad in combination with a paste, powder, or liquid that provides the abrasive properties. In some embodiments, surface treatment stations may use chemical etching, such as an acid or solvent for which the different materials in the slab react differently, to chemically etch the major surfaces of hardened and cured slabs. In some embodiments, surface treatment stations may use any appropriate combinations of the described tools, or any other appropriate tool or substance that can be used to abrade or erode the surface of a hardened and cured processed stone slab.
In some embodiments, the example systems 600-800 may be configured with one or multiple stages of abrasion using one or multiple different types of abrasives, abrasion tools, abrasion patterns (e.g., the abrasion tool can be draw across the surface in predetermined straight lines, curves, circles), application pressures, grits, speeds, directions across the major surfaces, speeds across the major surfaces, any combination of these and/or other appropriate variables that can affect the abrasion of processed stone slabs.
At 910 a first particulate mineral mix is dispensed into a first set of regions of a slab mold. For example, a first particulate mineral mix is deposited into the slab mold to become one or more veins.
At 920, a second particulate mineral mix is dispensed into a second set of regions of the slab mold. For example, the dispenser dispenses primary fill into the slab mold.
At 930, the first particulate mineral mix and the second particulate mineral mix arranged in the slab mold are contemporaneously vibrated and compacted so as to form a molded slab that is generally rectangular and has a slab thickness and a major surface having a width of at least 2 feet and a length of at least 6 feet. For example a vibro-compaction press applies compaction pressure, vibration, and/or vacuum to the contents inside the filled mold, thereby converting the particulate mixes into a rigid slab.
At 940, the compacted first particulate mineral mix and the compacted second particulate mineral mix are cured into a cured slab. For example, the curing station heats or otherwise cures the compacted slabs to further strengthen the slabs inside the filled molds.
In some implementation, the first particulate mineral mix can include one or more first component materials having a first hardness, and the first particulate mineral mix can include one or more first component materials having a second hardness different from the first hardness. For example, the primary fill may be made up of a relatively hard particulate mineral mix and a resin binder that cures relatively hard, whereas the veins may be made up of a relatively hard particulate mineral mix and a resin binder that is somewhat softer (e.g., allowing the binder to erode away to expose more hard particulate, possibly resulting in a surface like sandstone or fine sandpaper). In some embodiments, the particulate mineral mix composition results in particulates with rounded facets and a microscopically bumpy surface.
At 950, the major surface of the cured slab is abraded at locations of the first particulate mineral mix and the second particulate mineral mix with an abrading head to partly remove portions of the major surface such that the first particulate mineral mix in the first set of regions define a first thickness perpendicular to the slab width and the slab length, and the second particulate mineral mix in the second set of regions define a second thickness perpendicular to the slab width and the slab length. For example, the surface treatment stations 640, 740, and/or 840 can be used to abrade the major surface, and due to the differences (e.g., hardness, abrasion resistance) among regions of the primary fill and the veins, the various regions abrade or erode to different depths resulting in the primary fill and the veins having different thicknesses across the major surface 632 (e.g., the difference between T1 and T2 in
In some embodiments, abrading a portion of the major surface of the cured slab includes removing an amount of the major surface in the first set of regions to an average first thickness perpendicular to the slab width and the slab length that is at least partly different from a second average thickness removed from the second set of regions, wherein the first texture is based on the first average thickness and the second texture is based on the second average thickness. For example, the primary fill abrades to average thickness T1 while the veins abrade to average thickness T2, less than
In some embodiments, one of the first set of regions and the second set of regions can define a majority of the major surface, and the other of the first set of regions and the second set of regions can define a vein extending at least partly across the major surface. For example, the primary fill 51 occupies a first set of regions within the slab 50, and other particulate mineral mixes form the veins 52 and 53, which extend partly or entirely across the surfaces and edges of the slab 50.
In some implementations, abrading the major surface of the cured slab includes abrading substantially the entire major surface. For example, the system 600 can be configured to apply the same type of abrasion across the entire major surface 632 (e.g., causing substantially all of the primary fill 691 exposed at the major surface 632 to erode to substantially the same average depth, and causing the veins 692 and 693 to each erode to their own respective average depths across the entire major surface 632).
In some implementations, abrading the major surface of the cured slab can include abrading by at least one of an abrasive brush and mechanical application of an abrasive fluid compound. For example, the example abrasive brushes 642 can be used to apply a fluid compound containing abrasive material to the major surface 632.
In some implementations, the first set of regions can have a first texture and the second set of regions can have a second texture different from the first texture. For example, the primary fill 51 may have a smooth, glossy texture, while the vein 52 may have a relatively rougher, matte texture. In some embodiments, the roughness of the vein 52 may be quantified by Ra, Rq, and Rz values.
In some implementations, the first texture can be defined by one or more of a first roughness, a first gloss, and a first average thickness that extends perpendicular to the slab width and the slab length, and the second texture can be defined by one or more of a second roughness, a second gloss, and a second average thickness that extends perpendicular to the slab width and the slab length. For example, the primary fill 51 and the veins 52, 53 can each be made up of mineral particulate mixes that each have particles that are more rounded or more faceted in shape, or have particulates or binders that have relatively different in terms of light absorption and reflectivity, or exhibit relatively different levels of receptivity to polishing. In another example, as described above, the texture can be defined by some areas having different thicknesses than others (e.g., the example veins 52, 53 have an example thickness of T2 whereas the example primary fill has an example thickness of T1, resulting in boundaries where the transitions between the different thicknesses can be felt or seen).
Although a few implementations have been described in detail above, other modifications are possible. For example, the logic flows depicted in the figures do not require the particular order shown, or sequential order, to achieve desirable results. In addition, other steps may be provided, or steps may be eliminated, from the described flows, and other components may be added to, or removed from, the described systems. Accordingly, other implementations are within the scope of the following claims.
This application claims priority to U.S. application Ser. No. 63/188,403, filed on May 13, 2021. The disclosure of the prior application is considered part of the disclosure of this application, and is incorporated in its entirety into this application.