This invention relates generally to metal halide fill chemistries for discharge lamps. More particularly, this invention relates to thallium-free metal halide fills for discharge lamps.
Metal halide discharge lamps are favored for their high efficacies and high color rendering properties which result from the complex emission spectra generated by their rare-earth chemistries. Particularly desirable are low-wattage ceramic metal halide lamps which offer improved color rendering, color temperature, and efficacy over traditional quartz arc tube types. This is because ceramic arc tubes can operate at higher temperatures than their quartz counterparts and are less prone to react with the various metal halide chemistries. Like most metal halide lamps, ceramic lamps are typically designed to emit white light. This requires that the x,y color coordinates of the target emission lay on or near the blackbody radiator curve. Not only must the fill chemistry of the lamp be adjusted to achieve the targeted emission, but this must also be done while maintaining a high color rendering index (CRI) and high efficacy (lumens/watt, LPW).
Most commercial ceramic metal halide lamps contain a complex combination of metal halides, particularly iodides. In general, iodides are more favored than fluorides because of their lower reactivity and are more favored than chlorides or bromides because they tend to be less stable at higher temperatures. Thallium iodide is a common component which is mainly used to adjust the (x,y) color coordinates so that they lay on the blackbody curve. For example, a commercial 4200 K lamp may contain mercury plus a mixture of TlI, NaI, DyI3, HoI3, TmI3, and CaI2. While lamps that contain thallium operate well at their rated power, their photometric characteristics deteriorate when the lamps are dimmed. This is primarily because the vapor pressure of thallium iodide is much higher than the vapor pressures of the other fill components. As the lamp power is reduced, the operating temperature of the arc tube is lowered and the 535 nm thallium atomic emission line begins to dominate the emission spectrum of the lamp. The disproportionate increase in the thallium emission causes the lamps to attain higher color temperatures and shifts the x,y color coordinates significantly above the blackbody curve. As a result, the dimmed lamps acquire an undesirable greenish hue. Experiments have shown that the higher the percentage of thallium in the fill, the greater the green shift.
Another problem with thallium-containing fills is that small temperature variations (±50° C.) lead to large variations in the correlated color temperature (CCT). This is problematic because the fill chemistry must be re-optimized each time a new outer jacket or reflector is added even though the arc tube and desired color coordinates are identical. Thallium iodide also has been associated with a low power factor (PF) and higher re-ignition (RI) peaks in some metal halide lamps. A low power factor means a less efficient lamp-ballast system and large RI peaks can cause excessive wall blackening. And lastly, thallium has been prohibited from use in U.S. household products since 1975.
It is an object of this invention to obviate the disadvantages of the prior art.
It is another object of this invention to provide a metal halide fill which does not contain thallium.
It is a further object of the invention to provide a thallium-free metal halide fill which can meet the requirements for commercially desirable lamps, particularly when dimmed to less than their rated power.
In one aspect, the thallium-free metal halide fill of this invention is comprised of mercury,
In another aspect, the thallium-free metal halide fill of this invention comprises mercury and a mixture of metal halide salts, the mixture containing about 25 to about 55 mole percent sodium iodide, about 20 to about 50 mole percent of a rare-earth iodide selected from cerium iodide, dysprosium iodide, holmium iodide, thulium iodide, or combinations thereof, and about 5 to about 40 mole percent of an alkaline-earth iodide selected from calcium iodide, strontium iodide, barium iodide, or combinations thereof.
In yet another aspect of this invention, the thallium-free metal halide fill further contains lithium iodide in an amount up to about 30 mole percent of the total iodide content.
For a better understanding of the present invention, together with other and further objects, advantages and capabilities thereof, reference is made to the following disclosure and appended claims taken in conjunction with the above-described drawings.
The thallium-free metal halide fill of this invention contains, in general, mercury and a mixture of metal halide salts comprised of (1) sodium iodide (NaI), (2) an alkaline-earth iodide (AEI2) selected from calcium iodide, strontium iodide, barium iodide, or combinations thereof, and (3) a rare-earth iodide (REI3) selected from thulium iodide, dysprosium iodide, holmium iodide, cerium iodide, or combinations thereof. The relative proportions of the metal halide salts in the mixture are designed to yield commercially desirable lamp characteristics, e.g., color temperature, CRI, high efficacy. Preferably, the correlated color temperature (CCT) is within the range from about 4000 K to about 5000 K, the CRI is greater than about 80, and the efficacy is greater than about 80 LPW. In one embodiment, the molar ratio of sodium iodide to alkaline-earth iodide is from about 0.6 to about 11, the molar ratio of sodium iodide to rare-earth iodide is from about 0.5 to about 2.8, and the molar ratio of alkaline-earth iodide to rare-earth iodide is from about 0.1 to about 2. In a more preferred embodiment, the mixture of metal halide salts comprises about 25 to about 55 mole percent sodium iodide, about 5 to about 40 mole percent alkaline-earth iodide, and about 20 to about 50 mole percent rare-earth iodide. This may be represented by the region encompassed by the polygon shown in
The arc tube has hemispherical end wells 17a, 17b and is commonly referred to as a bulgy shape. The bulgy shape is preferred because it provides a more uniform temperature distribution compared to right-cylinder shapes such as those described in U.S. Pat. Nos. 5,424,609 and 6,525,476. The bulgy-shaped arc tube has an axially symmetric body 6 which encloses a discharge chamber 12. Two opposed capillary tubes 2 extend outwardly from the body 6 along a central axis. In this 2-piece design, the capillary tubes have been integrally molded with the arc tube body. The discharge chamber 12 of the arc tube contains a buffer gas, e.g., 30 to 300 torr Xe or Ar, and a thallium-free metal halide fill 8 as described herein.
Electrode assemblies 14 are inserted into each capillary tube 2. One end of the electrode assemblies 14 protrudes out of the arc tube to provide an electrical connection. The tips of the electrode assemblies which extend into the discharge chamber are fitted with a tungsten coil 3 or other similar means for providing a point of attachment for the arc discharge. The electrode assemblies are sealed hermetically to the capillary tubes by a frit material 9 (preferably, a Al2O3—SiO2—Dy2O3 frit). During lamp operation, the electrode assemblies act to conduct an electrical current from an external source of electrical power to the interior of the arc tube in order to form an electrical arc in the discharge chamber.
Several 70-watt ceramic metal halide test lamps were made with bulgy-shaped ceramic arc tubes. The composition of each arc tube fill is given below and the lamp photometry results are provided in Table 1. The points representing the relative mole fractions of NaI, AEI2, and REI3 in the arc tube fills of Examples 2–9 are plotted in
Arc tube fill (thallium-containing):
4.5 mg Hg, 9 mg metal halide mixture (23:38:12:9:9:9 molar ratio of NaI:CaI2:TlI:DyI3:HoI3:TmI3) and 260 torr argon.
NaI:AEI2 molar ratio=0.60;
NaI:REI3 molar ratio=0.85;
AEI2:REI3 molar ratio=1.4;
NaI:TlI molar ratio=1.92.
Arc tube fill:
4 mg Hg, 8.6 mg metal halide mixture (47:16:37 molar ratio of NaI:CaI2:DyI3) and 260 torr Ar.
NaI:AEI2 molar ratio=2.94;
NaI:REI3 molar ratio=1.27;
AEI2:REI3 molar ratio=0.43.
Arc Tube Fill:
4 mg Hg, 9.1 mg metal halide mixture (47.5:15:37.5 molar ratio of NaI:BaI2:DyI3) and 260 torr Ar.
NaI:AEI2 molar ratio=3.17;
NaI:REI3 molar ratio=1.27;
AEI2:REI3 molar ratio=0.40.
Arc tube fill:
4.5 mg Hg, 8.3 mg metal halide mixture (39:8:23:30 molar ratio of NaI:BaI2:LiI:TmI3) and 260 torr Ar.
NaI:AEI2 molar ratio=4.88;
NaI:REI3 molar ratio=1.3;
AEI2:REI3 molar ratio=0.27.
Arc tube fill:
4.0 mg Hg, 8.5 mg metal halide mixture (28:29:43 molar ratio of NaI:CaI2:TmI3) and 260 torr Ar.
NaI:AEI2 molar ratio=0.97;
NaI:REI3 molar ratio=0.65;
AEI2:REI3 molar ratio=0.67.
Arc tube fill:
4 mg Hg, 9.3 mg metal halide mixture (39.7:22.9:7.8:29.6 molar ratio of NaI:LiI:BaI2:TmI3) and 260 torr Ar.
NaI:AEI2 molar ratio=5.1;
NaI:REI3 molar ratio=1.3;
AEI2:REI3 molar ratio=0.26.
Arc tube fill:
4 mg Hg, 9.1 mg metal halide mixture (52:9:39 molar ratio of NaI:BaI2:TmI3) and 260 torr Ar.
NaI:AEI2 molar ratio=5.8;
NaI:REI3 molar ratio=1.3;
AEI2:REI3 molar ratio=0.23.
Arc tube fill:
4 mg Hg, 9.0 mg metal halide mixture (40.4:16.1:18.5:25.1 molar ratio of NaI:BaI2:SrI2:TmI3) and 260 torr Ar.
NaI:AEI2 molar ratio=1.2;
NaI:REI3 molar ratio=1.6;
AEI2:REI3 molar ratio=1.4.
Arc tube fill:
4.15 mg Hg, 9.2 mg metal halide mixture (47.6:9.3:36.0:7.1 molar ratio of NaI:BaI2:TmI3:CeI3) and 260 torr Ar.
NaI:AEI2 molar ratio=5.1;
NaI:REI3 molar ratio=1.1;
AEI2:REI3 molar ratio=0.22.
At rated lamp power, the thallium-free lamps of this invention exhibit photometric characteristics (CCT, CRI, efficacy, and x,y color coordinates) which are similar to their thallium-containing counterparts. However, unlike their thallium-containing counterparts, the thallium-free lamps continue to exhibit desirable photometric characteristics when dimmed to less than their rated power. This behavior can be seen in the chromaticity diagram shown in
While there has been shown and described what are at the present considered the preferred embodiments of the invention, it will be obvious to those skilled in the art that various changes and modifications may be made therein without departing from the scope of the invention as defined by the appended claims.
Number | Name | Date | Kind |
---|---|---|---|
5424609 | Geven et al. | Jun 1995 | A |
6404129 | Hendricx et al. | Jun 2002 | B1 |
6501220 | Lambrechts et al. | Dec 2002 | B1 |
6525476 | Geijtenbeck et al. | Feb 2003 | B1 |
6620272 | Zaslavsky et al. | Sep 2003 | B1 |
6717364 | Zhu et al. | Apr 2004 | B1 |
Number | Date | Country | |
---|---|---|---|
20050212436 A1 | Sep 2005 | US |