The invention relates to a thermal analysis apparatus with a sample space, in which a sample carrier and heating devices as well as flow devices with an inert gas supply for an inert gas are contained. The invention also relates to a thermal analysis method wherein a sample carrier and heating devices are surrounded by inert gas in a sample space, and wherein an inert gas flow is generated by an inert gas supply in the sample space.
Investigatory methods for material characterisation are referred to as thermal analysis, wherein the sample is subjected to a controlled temperature program. Dimensional changes, mass changes, calorific effects, the specific thermal capacity and escaping gases, for example, are investigated.
The samples may oxidise due to residual oxygen in an otherwise inert gas atmosphere provided in the sample space, which can falsify the results and is therefore undesirable. The presence of residual oxygen in the inert gas, which is also referred to and/or used as purging gas, in apparatus for measurements under a nominal inert gas atmosphere (e.g. nitrogen, argon or helium) therefore represents a problem.
Residual oxygen in an apparatus is usually minimised by the fact that the typically vacuum-tight apparatus is evacuated and then filled and purged with inert gas of high purity. The residual oxygen concentration thus depends on the vacuum tightness of the apparatus, the vacuum tightness of the gas supply lines and the purity of the inert gas present. Purification of the purging gas before entry into the apparatus is just inadequate due to the finite leakage rate of the apparatus itself and the desorption of residual oxygen from the walls of the apparatus.
Accordingly, although devices and methods for removing residual oxygen from an inert gas according to publications DE 2 340 102 A, DE 698 30 247 T2, DE 36 21 014 C2 and DE 689 10 638 T2 are suitable in principle for reducing the residual oxygen content of an inert gas, the purity of the inert gas in respect of residual oxygen in each case deteriorates again before the use of the inert gas due to its subsequent path into respective apparatuses. In certain production processes and production environments, such as are used for example as applications for inert gas in the aforementioned publications, this may possibly be acceptable, but satisfactory results are not thereby obtained for measurement and analysis apparatuses and methods, such as in particular thermal analysis apparatuses and methods.
It is therefore the aim of the invention to reduce and therefore improve the residual oxygen load in measurements with thermal analysis apparatuses and methods.
This aim is achieved with a thermal analysis apparatus as well as with the thermal analysis method.
The invention thus creates a thermal analysis apparatus with a sample space, in which a sample carrier and heating devices as well as an inert gas are contained, wherein furthermore flow devices for the inert gas for generating an inert gas flow to the sample carrier and getter devices (oxygen trap devices) for removing residual oxygen from the inert gas are contained, said getter devices being disposed in the inert gas flow in the flow direction upstream of the sample carrier in the vicinity thereof.
A considerable in situ reduction in the residual oxygen concentration in the thermal analysis apparatus at the site of the sample is achieved by the getter devices in an advantageous and inventive way.
Provision is also preferably made such that the getter devices are disposed in the inert gas flow in the flow direction upstream of the sample carrier at a distance therefrom.
It is also preferable for the flow devices for the inert gas to comprise an inert gas supply to the sample space.
A further advantageous embodiment consists in the fact that the getter devices comprise a getter carrier and an especially metallic getter material disposed therein or thereon, wherein provision can in particular also be made such that the getter carrier and/or the getter material are/is disposed in the flow direction of the inert gas upstream of the sample carrier and at least approximately axially aligned with the latter. Alternatively or additionally, provision can preferably be made such that
A further preferred embodiment consists in the fact that the heating devices define a heating zone, in which the sample carrier together with a sample placed optionally thereon or therein and at least in part the getter devices, if appropriate at least the getter material, are disposed.
Provision can also preferably be made such that the heating devices are designed and disposed in such a way that they simultaneously heat a sample that can be placed on the sample carrier and at least in part the getter devices, if appropriate at least the getter material.
According to another preferred embodiment, provision is made such that the heating devices for heating a sample that can be placed on the sample carrier comprise at least one heating element which, with respect to the sample on or in the sample carrier, is laterally spaced apart from the latter, wherein provision can in particular also be made such that the heating element or the heating elements surrounds or surround the sample carrier laterally at least in part.
The flow devices are preferably designed and disposed so as to generate an at least essentially vertical inert gas flow, and the sample carrier is disposed at least essentially above the getter devices, so that the inert gas flow flows laterally past the sample carrier and past a sample that can be placed on the sample carrier. Alternatively, provision can also be made such that the flow devices are designed and disposed so as to generate an at least essentially horizontal inert gas flow, and that the sample carrier is disposed at least essentially laterally with respect to the getter devices, so that the inert gas flow flows at least over the sample carrier and a sample that can be placed on the sample carrier.
The inert gas preferably contains argon, in particular of purity 99.996, nitrogen and/or helium.
Furthermore, provision can preferably be made such that the sample carrier is designed to carry a crucible for receiving a sample to be investigated.
The oxygen trap devices preferably comprise getter devices.
The previously described embodiments especially of the getter devices, but also of the thermal analysis apparatus in general, are to be regarded as preferable.
Finally, the invention also creates a thermal analysis method, wherein a sample carrier and heating devices are surrounded by inert gas in a sample space, and wherein the inert gas is caused to flow as an inert gas flow in the sample space first over or past getter devices for the removal of residual oxygen from the inert gas and then to the sample carrier, which is disposed in the vicinity of the getter devices.
A preferred development thereof consists in the fact that the inert gas flow is generated with an inert gas supply to the sample space.
Provision can preferably also be made such that the heating devices define a heating zone, in which the sample carrier together with a sample placed optionally thereon or therein and at least in part the getter devices, if appropriate at least the getter material, are disposed, so that the heating devices simultaneously heat a sample that can be placed on the sample carrier and at least in part the getter devices or a getter material contained in the latter.
Another preferred embodiment of the thermal analysis method consists in the fact that an at least essentially vertical inert gas flow is generated which flows past the getter devices and then flows to the sample carrier disposed at least essentially above the latter, so that the inert gas flow flows laterally past the sample carrier and past a sample that can be placed on the sample carrier. Alternatively, provision can be made such that an at least essentially horizontal inert gas flow is generated which first flows past the getter devices and then flows to the sample carrier disposed at least essentially laterally with respect thereto, so that the inert gas flow flows at least partially over the sample carrier and a sample that can be placed on the sample carrier.
Furthermore, provision can be made such that the thermal analysis apparatus comprises a plurality of heating devices, with which the getter device and the sample can be heated independently of one another.
In an additional embodiment, the thermal analysis apparatus is operated without the latter previously being evacuated. With this embodiment, the sample space is solely exposed to an inert gas flow which washes over the getter device and subsequently the sample.
Further preferred and/or advantageous embodiments of the invention emerge from the claims and their combinations as well as all the present application documents.
The invention is explained in greater detail below, solely by way of example, with the aid of examples of embodiment making reference to the drawing, in which
Identical reference numbers in the individual figures and illustrations of the drawing denote identical or similar components or components acting identically or similarly. With the aid of the representations in the drawing, those features also become clear that are not provided with reference numbers, irrespective of whether such features are described below or not. On the other hand, features which are included in the present description, but are not visible or represented in the drawing, are readily understandable to the person skilled in the art.
A first and a second example of embodiment of a thermal analysis apparatus 1 are shown diagrammatically in
This thermal analysis apparatus 1 comprises a sample space 2, in which a sample carrier 3 and heating devices 4 as well as an inert gas 5 are contained. Flow devices 6 for inert gas 5 for generating an inert gas flow 7 to sample carrier 3 and oxygen trap devices 8 for the removal of residual oxygen from inert gas 5 are also contained. Flow devices 6 comprise an inert gas supply 9 to sample space 2, which further comprises an inert gas outlet 10, so that inert gas 5 flows from inert gas supply 9 to inert gas outlet 10 through sample space 2 and therein, in turn, from oxygen trap devices 8 to sample carrier 3.
Inert gas 5 is for example argon, in particular of purity 99.996, although gases such as for example nitrogen or helium or gas mixtures can also be used.
Oxygen trap devices 8 comprise getter devices 11 for the removal of residual oxygen from inert gas 5 and are disposed in inert gas flow 7 in the flow direction upstream of sample carrier 3 in the vicinity thereof, but spaced apart therefrom. The structure, function and action of getter devices are in principle known from the prior art, such as in particular from the publications mentioned at the outset, and a reference is expressly made here to the latter, so that all previously known embodiments of getter devices 11 and in particular the features disclosed in DE 2 340 102 A, DE 698 30 247 T2, DE 36 21 014 C2 and DE 689 10 638 T2 are included in their entirety by this mere reference in the present documents which is intended to avoid repetition.
Getter devices 11 comprise a getter carrier 12 and a getter material 13 disposed therein or thereon, said getter material containing in particular metals. Getter carrier 12 and/or preferably metallic getter material 13 are/is disposed in the flow direction of inert gas 5 or inert gas flow 7 upstream of sample carrier 3 and aligned approximately axially therewith. Heating devices 4 are designed, in particular constituted, shaped and/or disposed, so as to heat getter material 13 to a sufficiently high temperature (for example, above 400° C.). This temperature value, however, represents only an indication in the context of the example of embodiment; usable getter devices 11 and getter materials 13 are not restricted in the context of the present invention to those which work or act only from temperatures of 400° C. and over, but on the contrary use may also be made of getter devices 11 and getter materials 13 which work or act below 400° C. Getter material 13 is temperature-resistant and contains zirconium. Getter carrier 12 is made of a metallic material, in particular Y2O3, and the material from which getter carrier 12 is made does not react with getter material 13. With regard to the embodiment, getter carrier 12 can be a rod, a wire or a ring.
Heating devices 4 define a heating zone 14, in which sample carrier 3 together with sample 15 in a crucible 16 placed thereon (see
Furthermore, heating devices 4 are designed and disposed in such a way that they simultaneously heat sample 15 that can be placed on sample carrier 3 and getter devices 11 or at least their in particular metallic getter material 13. For this purpose, heating devices 4 comprise heating elements 17 which, with respect to sample 15 on or in sample carrier 3, are laterally spaced apart from the latter and which are formed and disposed in such a way that they surround sample carrier 3 laterally at least in part.
In the case of the first example of embodiment according to
As distinct therefrom, and this is the only distinction between the first and second example of embodiment, provision is made with thermal analysis apparatus 1 according to the second example of embodiment represented in
According to the method, therefore, in sample space 2, which contains sample carrier 3 and heating devices 4 which are duly surrounded by inert gas 5, inert gas 5 is caused to flow, as inert gas flow 7 in sample space 2, first over or past getter devices 11 for the removal of residual oxygen from inert gas 5 and then to sample carrier 3, which is disposed spaced apart from getter devices 11, but in the vicinity thereof.
Of great importance in
The mode of operation of thermal analysis apparatus 1 and of the thermal analysis method performed therewith and in particular of oxygen trap devices 8 or getter devices 11 disposed according to the invention in inert gas flow 7 upstream of sample 15 and its sample holder 3 becomes clear, by way of example, with the aid of the TG-DSC measurement curves shown in
TG denotes thermal gravimetry, i.e. the determination of mass changes, and DSC denotes differential scanning calorimetry, wherein calorific effects, such as melting for example, can be investigated. Both measurements were carried out with argon purging gas of purity 99.996. The melting point (Tmelt) of nickel of 1455° C. known from the literature is often used in thermal analysis apparatuses for thermometry at high temperatures. However, nickel is very oxidation-sensitive, as a result of which the melting point falls in an undefined manner and should therefore no longer be used for thermometry.
The measurement with thermal analysis apparatus 1 and the thermal analysis method performed therewith and in particular oxygen trap devices 8 or getter devices 11 disposed according to the invention in inert gas flow 7 upstream of sample 15 and its sample holder 3 delivers in this regard correct results, as the measurement curve represented with a continuous line shows: Sample 15 no longer oxidises significantly, which can be recognised by the horizontally running TG curve; no weight change occurs. The so-called DSC melting peak of nickel occurs at 1454.9° C., i.e. close to the literature value of 1455° C., the detected melting enthalpy delta H amounts to 299.8 J/g, i.e. approx. 300.0 J/g.
During the measurement without oxygen trap devices 8 or getter devices 11 disposed according to the invention in inert gas flow 7 upstream of sample 15 and its sample holder 3, sample 15 oxidises, which can be recognised by the markedly increasing TG curve according to the measurement curve represented by a dashed line (weight increase). The DSC melting peak already occurs at 1443° C. on account of the oxidation, i.e. 12° C. below the literature value. The measured melting enthalpy of 275 J/g also turns out to be less than the literature value of 300 J/g.
Thermal analysis apparatus 1 and the thermal analysis method performed therewith as well as in particular oxygen trap devices 8 or getter devices 11 disposed according to the invention in inert gas flow 7 upstream of sample 15 and its sample holder 3 enables an in situ reduction in the residual oxygen concentration in the thermal analysis measurements (TGA, DSC, STA, DIL etc.), and is constituted such that a particularly temperature-resistant getter material 13 is introduced into measuring or sample space 2 of thermal analysis apparatus 1. In the manner required at the given time, getter material 13 is brought by heating element 17 to a sufficiently high temperature in order to be able to work. The residual oxygen in inert gas 5 in sample space 2 is absorbed by getter material 13, and oxidation of sample 15 is thus effectively prevented. For this purpose, getter material 13 is positioned in thermal analysis apparatus in such a way that inert gas 5 first flows past getter material 13 and then past sample 15. Getter material 13 has no contact with crucible 16 and sample 15. Temperature-resistant getter carrier 12 positions getter material 13 accordingly in sample space 2 of thermal analysis apparatus 1. Getter carrier 12 comprises a material, such as for example a Y2O3 ceramic, which does not react with getter material 13.
In particular, all the individual features and possible embodiments of the invention and its examples of embodiment can be combined.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2009 024 055.1 | Jun 2009 | DE | national |
The present application is a continuation of pending International patent application PCT/DE2010/000623 filed on Sep. 2, 2010 which designates the United States and claims priority from German patent application 10 2009 024 055.1 filed on Jun. 5, 2009, the content of which is incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/DE2010/000623 | Jun 2010 | US |
| Child | 13311329 | US |