Patent Grant
7687150
The present invention relates to a thermal barrier composition for use on a variety of substrates that are exposed to high temperatures. Exemplary substrates include pipelines, engine parts including jet engine components, water conduits including tubes in power plants, reactor vessels and exhaust manifolds.
Substrates, particularly metal substrates, can be subjected to high temperatures causing fatigue, cracking, distortion and the like of the substrate. For example, components of a jet engine or the surrounding parts of the jet can be exposed to temperatures in excess of 1800° F. In such a situation, it is readily apparent that fatiguing or cracking can lead to catastrophic failure. Similarly, piping used in various manufacturing facilities can be subjected to temperatures in excess of 400° F. caused by the liquid or gas passing through the pipe. In such an application, it is preferred that the coating not only provide a thermal barrier but also provide anti-corrosion properties.
The thermal barrier composition of the present invention comprises a glassy matrix comprising an alkoxy-functionalized siloxane and a functionally-terminated silane or siloxane, polymethylsilsesquioxane dissolved in a crosslinking agent, and optionally a filler and/or hollow glass microspheres. The glass matrix provides good adhesion to the surface being coated, as well as, toughness, crack resistance, durability, abrasion resistance, heat resistance and stability in the particular environment.
As briefly discussed above, the present invention relates to a thermal barrier composition. The thermal barrier compositions of the present invention comprise a glassy matrix comprising: an alkoxy-functionalized siloxane and a functionally-terminated silane or siloxane; (b) polymethylsilsesquioxane dissolved in a crosslinking agent; and optionally (c) and (d) a filler and/or hollow glass microspheres. The thermal barrier composition of the present invention can be coated onto a wide variety of substrates including steel, stainless steel, titanium, aluminum, magnesium and zinc. The coating can withstand continuous use temperatures of 1800° F. or higher. Moreover, the composition is resistant to corrosive agents such as nitrogen and sulfur compounds.
Suitable alkoxy-functionalized siloxanes include polydiethoxysiloxane, tetraethoxysilane, tetramethoxysilane, and polydimethoxysiloxane. A preferred alkoxy-functionalized siloxane is polydiethoxysilane. Suitable functionally-terminated silanes or siloxanes include silanol-terminated, vinyl-terminated and amino-terminated silanes or siloxanes such as epoxy-functionalized polydimethylsiloxane, aminopropyltriethoxy silane and silanol-terminated siloxane.
The glassy matrix is crosslinked using a titanium or tin catalyst. Suitable catalysts include titanium alkoxides such as titanium methoxide, titanium ethoxide, titanium isopropoxide, titanium propoxide, titanium butoxide, titanium diisopropoxide (bis 2,4-pentanedionate), titanium diisopropoxide bis(ethylacetoacetao) titanium ethylhexoxide, and organic tin compounds such as dibutyl tin diacetate, dibutyltin laurate, dimethyl tin dineodecanoate, dioctyl dilauryl tin, and dibutyl butoxy chlorotin, as well as mixtures thereof. The glassy matrix can be formed by using a Sol-Gel process such as described in U.S. Pat. No. 6,313,193, the disclosure of which is incorporated herein by reference in its entirety. Other methods of forming the matrix will be within the skill of one in the art.
The thermal barrier composition may also optionally include fillers such as, without limitation, glass fibers, fumed silica, mica, kaolin, bentonite, talc, zinc oxides, iron oxides and pigments or other fillers, as will be readily apparent to those skilled in the art. The composition may also include hollow glass microspheres to provide additional heat resistance. Preferably, thin-walled glass microspheres are used. Typically the volume percent of glass microspheres is from about 30 percent to about 80 percent. If the higher amount is used, it is preferable to include milled glass fibers to improve durability. Anti-corrosion agents such as zinc phosphates and zinc salts can also be added.
In operation, the thermal barrier composition of the present invention can be applied to a substrate by roll-coating, brush, spray coating dipping and the like. It is preferred that the user mix the catalyst with the other components right before or substantially contemporaneously with application to form an interpenetrating polymer network of glass and silicone on the surface of the substrate. Inasmuch as crosslinking occurs via a moisture condensation reaction between ethoxy and hydroxyl groups, the condensation inherently present on the substrate and/or in the atmosphere can be used advantageously.
The following specific examples are provided to afford a better understanding of the present invention to those skilled in the art. It is to be understood that these examples are intended to be illustrative only and is not intended to limit the invention in any way.
The first step is to dissolve the polymethysilsesquioxane (POSS) into the titanium isopropoxide (TIPO). This is accomplished by mixing the POSS into the titanium isopropoxide and heating at 100° C. for 24 hours.
The second step is to mix the silanol terminated polydimethylsiloxane with the titanium diisopropoxide (bis-2,4-pentanedionate) and allowing the mixture to crosslink for 1 hour. If this step is not performed, the silanol groups on the polymer will instantly react with the titanium isopropoxide and the system will gel in a matter of seconds.
The third step is to add the remaining components to the POSS/TIPO prepared in the first step (A component), keeping the titanium diisopropoxide (bis-2,4-pentanedionate)/polydimethylsiloxane mixture prepared in the second step out as the B component in an A/B system.
Formulation
The formulation was manufactured using the same steps as Example 1 except that the POSS did not have to be pre-reacted with the TIPO. The formulation of Example 2 was used in various tests as described below and in Table 1.
Durability Testing
A series of durability tests were performed on the coating composition of Example 2. These tests were designed to simulate real-world events that will test the durability of the coating. The three specific tests performed on the coating composition of Example 2 included: two tool drop tests, a falling sand test, and a 200 lb, 90° pivot test.
The first tool drop test consisted of dropping a 106 gram wrench from a height of 48 inches onto a panel coated with the coating composition of Example 2. This test which was repeated multiple times resulted in a dent of about 5 mm×5 mm. The second tool drop test consisted of dropping a 783 gram hammer from the same 48 inch height. The tool drop resulted in a dent of about 15 mm×25 mm.
The indentions from the tool drop tests are consistent with the energy expected form objects of similar size and mass dropped form a height of 48 inches. No cracking or delamination occurred the coating and the divots can be easily repaired with the coating composition of Example 2.
The falling sand test consisted of dropping 1 gallon of sand from a height of 1.5 feet in a concentrated stream onto the surface of a steel panel coasted with the coating composition of Example 2 mounted 45° to the falling sand.
As a results of this test, the impact zone was abraded in a region about 10 mm×16 mm×0.5 mm. The coating composition of Example 2 demonstrated good abrasion resistance.
The third durability test consisted of a 200 lb person standing on a plate coated with the coating composition of Example 2 with all weight on one foot. Then the person pivoted 90°. No damage resulted to the coating composition of Example 2. The test demonstrates the coating composition of Example 2 can be walked on (e.g., a plane wing) with no damage.
Temperature Delta Data
A titanium plate with a 2.5 mm build of the coating composition of Example 2 was prepared. A 3 mm wide channel was cut into the coating from the center of the plate to the edge, and a thermocouple was positioned in the channel such that it would be in contact with the titanium plate. The coating composition of Example 2 was applied over the thermocouple to fill the channel and seal the thermocouple at the interface of the coating composition of Example 2 and the titanium plate, producing a sample with the thermocouple counted at the interface of the coating composition of Example 2 and the titanium. Total coating thickness was approximately 3.0 mm.
After the coating was cured, the plate was placed onto a steel block and was heated to a temperature of 1057° F. by a burner on the turkey fryer. The sample was placed with the coating composition of Example 2 directly in contact with the hot steel block, and allowed to equilibrate for 78 minutes to allow for steady state heat flow.
The temperature measurement at the coating composition of Example 2-titanium interface was found to be 720° F. with the hot steel measuring 1057° F.: a temperature delta of 337° F. across the coating composition of Example 2 for a coating that is 3.0 mm thick.
Measure Thermal Conductivity
Thermal conductivity was measured on a free standing coating composition of Example 2 film using the ASTM E1530 standard test method. Measurements were conducted at 105° F., 334° F., and 561° F. The results are listed in the Table 2.
In the specification and examples, there have been disclosed typical preferred embodiments of the invention and, although specific terms are employed, they are used in a generic and descriptive sense only and not for purposes of limitation of the scope of the invention set forth in the following claims.
The instant application is a continuation application of U.S. patent application Ser. No. 10/814,213 filed Mar. 31, 2004 and claims priority to U.S. Provisional Application Ser. No. 60/461,800 filed Apr. 10, 2003 the disclosures of which are incorporated herein by reference in their entireties.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4405679 | Fujioka et al. | Sep 1983 | A |
| 4510283 | Takeda et al. | Apr 1985 | A |
| 4602959 | Kurita et al. | Jul 1986 | A |
| 4725501 | Rukavina et al. | Feb 1988 | A |
| 4753827 | Yoldas et al. | Jun 1988 | A |
| 4814017 | Yoldas et al. | Mar 1989 | A |
| 4816288 | Rukavina et al. | Mar 1989 | A |
| 4990547 | Stovicek | Feb 1991 | A |
| 5068277 | Vukov et al. | Nov 1991 | A |
| 5096488 | Stovicek | Mar 1992 | A |
| 5173110 | Stovicek | Dec 1992 | A |
| 5218059 | Kishihara et al. | Jun 1993 | A |
| 5232996 | Shah et al. | Aug 1993 | A |
| 5298060 | Harakal et al. | Mar 1994 | A |
| 5331074 | Slater et al. | Jul 1994 | A |
| 5433941 | Patel | Jul 1995 | A |
| 5492730 | Balaba et al. | Feb 1996 | A |
| 5593732 | Griffith | Jan 1997 | A |
| 5663215 | Milligan | Sep 1997 | A |
| 5688851 | Kress | Nov 1997 | A |
| 5939478 | Beck et al. | Aug 1999 | A |
| 5942583 | Azechi | Aug 1999 | A |
| 5958116 | Kishihara et al. | Sep 1999 | A |
| 6013724 | Mizutani et al. | Jan 2000 | A |
| 6045869 | Gesser et al. | Apr 2000 | A |
| 6313193 | Simendinger, lll | Nov 2001 | B1 |
| 6476095 | Simendinger, III | Nov 2002 | B2 |
| 6559201 | Simendinger, III | May 2003 | B2 |
| 20030152785 | Sanders et al. | Aug 2003 | A1 |
| Number | Date | Country |
|---|---|---|
| 0563939 | Oct 1993 | EP |
| 0664322 | Jul 1995 | EP |
| 0851009 | Jul 1998 | EP |
| 60-254034 | Dec 1985 | JP |
| 62-277475 | Dec 1987 | JP |
| 2000319582 | Nov 2000 | JP |
| WO 9516751 | Jun 1995 | WO |
| WO 0102506 | Jan 2001 | WO |
| WO 02059210 | Aug 2002 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20060110612 A1 | May 2006 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60461800 | Apr 2003 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10814213 | Mar 2004 | US |
| Child | 11324687 | US |