Patent Application
20220274887
Radomes contain and protect electronic installations such as radar from wind, moisture, and visibility. In some cases, radomes are also required to dissipate heat, such when used as nosecones for flight. In all cases, radomes must provide both transparency and low reflectivity for radio frequency signals. Ideally, a radome is constructed of a material that minimally attenuates transmitted or received electromagnetic radiation while filtering or attenuating undesired signals, and yet is mechanically robust and water shedding. Radomes are typically constructed of composite materials designed to perform these functions. As the demand grows for sophisticated electronics used in aviation, defense, space travel, and wireless transmissions, there is a need for materials for constructing radomes and other coverings for electronic components and installations offering superior band-pass tunability, thermal dissipation, and mechanical robustness.
The present technology provides coatings and composite materials containing hexagonal boron nitride for high performance thermal conductivity and use in radomes and other tunable coverings for electronic components and equipment. The composite materials dissipate heat and infrared radiation while providing tunable radio frequency (RF). The materials can include a superhydrophobic coating to limit RF attenuation and distortion caused by rain or other forms of moisture. The technology also provide methods for producing such composites over a range of thickness from less than about 1 micron (as little as a single monolayer of hexagonal boron nitride) up to over a centimeter. Quarter wavelength, twelfth wavelength, or any selected design thicknesses can be integrated within layers to provide bandpass or directional transmission features.
As used herein, the term “platelet” refers to a flat particle having a small dimension on the Z-axis and larger dimensions on the X-axis and Y-axis. The thinnest platelets of hexagonal boron nitride (hBN) are a single atomic layer thick 2D material having a Z-axis of about 0.4-0.5 nm and the size of the larger diameters (X,Y) typically depending upon the method of production. A process of exfoliation can separate multilayers of hBN into fewer or into single layers. Platelets of 2-layer and 3-layer hexagonal boron nitride have thicknesses of about 0.7-0.9 nm and 1.1-1.3 nm, respectively. The smaller platelets of hexagonal boron nitride are known as graphitic or white graphite. The stacked 2D layers in hBN are held together by van der Waals forces. Exfoliation of thicker platelets into thinner platelets can be accomplished by, for example, higher energy sonication (e.g., probe-tip or high amplitude bath), ball milling, chemical, or gas exfoliation. In most methods of exfoliation, the diameter (X,Y) of the platelets is also lowered during exfoliation. Some methods of synthesis for monolayer, 2-layer, and 3-layer hBN can provide larger X,Y dimensions.
Examples of hexagonal boron nitride platelets utilized in the present technology have a mean particle size from about 5 microns to about 100 microns, from about 5 microns to about 50 microns, or from about 5 microns to about 45 microns. As used herein, the term mean particle size can refer to average or median diameter, with the Z-axis from the minimum (discussed above) to about 5 microns, to about 10 microns, to about 20 microns, to about 40 microns, or to about 50 microns.
As used herein, the term mean particle size and average particle size can refer to a mean or median particle size (D50) calculated utilizing particles' number, volume, weight, surface area, or intensity to weight the distribution. Typically, particle sizes measured using laser diffraction generate results based on median or mean volume based distributions. Different particle size instruments can provide different average particle size measurements because of detection methods or calculations of particle size, shape factor, aspect ratio, and varying distributions utilized to calculate the average. Different particle size measurement instruments can use different particle detection and distribution methods; for example, laser diffraction, static or dynamic light scattering, image analysis, gas surface area, mesh, or sieve. The mean or median particle size can be reported as the D50, which refers to the size (in microns) that splits the distribution with half of the distribution above and half below this number. The D10 is the size at which 10% of the distribution is below that size. The D90 is the size at which 90% of the distribution is below that size.
Hexagonal boron nitride particles can be provide increased thermal conductivity to resin systems. Hexagonal boron nitride (hBN) platelets can have very high thermal conductivities with the long-axes (X,Y) of the crystal exhibiting ˜300-600 W/mK and the short-axis (Z) exhibiting ˜20-40 W/mK. Further, hBN is a dielectric material.
As used herein, a superhydrophobic layer, a CFz-E layer, and a CFz layer is a z-aligned fiber outer layer that exhibits super-hydrophobicity and durability. A superhydrophobic layer can be a self-similar material, which is defined as one that wears evenly and its hydrophobic properties do not change as it wears. The fibers can be carbon fibers or other fibers such as hollow polymeric fibers. Superhydrophobic surfaces are highly hydrophobic, (i.e., extremely difficult to wet). The contact angles of a water droplet on a new superhydrophobic material can be greater than about 100-110°, such as greater than 140-150°.
As used herein, a surfactant or detergent can be ionic or non-ionic.
The present technology can be provided as a kit including particles or platelets of hexagonal boron nitride, optionally solvent, and optionally adhesive(s), along with instructions for use to form multilayered composite materials described herein.
As used herein, the term “about” can include values within 10%, 5%, 1%, or 0.5% of the stated value.
The technology can be further summarized in the following list of features.
1. A layered composite material comprising:
2. The layered composite material of feature 1, comprising said core layer, wherein the core layer comprises air, a foam, a honeycomb, a ferrite material, a magneto-ceramic material, a metal, a polymeric material, a fibrous material, or a combination thereof.
3. The layered composite material of feature 2, wherein the core layer comprises polystyrene, polyethylene, PVC foam, polyurethane foam, polycarbonate honeycomb, honeycomb paper, synthetic fiber, wood, carbon fiber, or a combination thereof.
4. The layered composite material of any of the preceding features, wherein the fiber reinforced layer comprises a synthetic fiber, glass fiber, quartz fiber, carbon fiber, or a combination thereof.
5. The layered composite material of any of the preceding features, wherein the hydrophobic layer comprises a low-loss superhydrophobic material comprising a z-aligned fiber outer layer and/or fibers coated with polytetrafluoroethylene.
6. The layered composite material of any of the preceding features, wherein said hydrophobic layer is disposed at a surface of the composite material.
7. The layered composite material of any of the preceding features, wherein said hexagonal boron nitride layer is disposed at a surface of the composite material.
8. The layered composite material of any of the preceding features, wherein the boron nitride layer comprises or consists of one or more layers of hexagonal boron nitride platelets.
9. The layered composite material of any of the preceding features, wherein the fiber reinforced layer comprises one or more woven glass fiber fabrics embedded in a binder.
10. The layered composite material of feature 9, wherein the binder is an epoxy.
11. The layered composite material of any of the preceding features, comprising a hexaferrite core, fiberglass layers bound to opposite surfaces of the hexaferrite core, a hexagonal boron nitride layer disposed at a first surface of the composite material and bound to one of said fiberglass layers, and a superhydrophobic disposed at a second surface of the composite material opposite the first surface.
12. The layered composite material of any of the preceding features, wherein the material is configured as a radome, a radio frequency filter, a covering for an electronic component or device, or a portion thereof.
13. A product comprising the layered composite material of any of features 1-11.
14. The product of feature 13, wherein the product is selected from the group consisting of a radome, a nosecone, a circuit board shield, a heat shield for an electronic device, a battery package, an aerodynamic heat shield, a satellite heat shield, a cellular network antenna heat shield, an engine heat shield, an exhaust heat shield, a band-pass filter, a CPU or GPU heatsink, a building material, and a thermal soak heat shield.
15. A process for fabricating a thermally conductive coating on a substrate, the process comprising:
16. The process of feature 15, wherein a monolayer or a multilayer of the hexagonal boron nitride platelets is deposited onto the surface of the substrate.
17. The process of feature 15 or 16, wherein the hexagonal boron nitride platelets have an average diameter in the range from about 5 microns to about 50 microns.
18. The process of any of features 15-17, further comprising:
19. The process of any of features 15-18, wherein the surface of the substrate is coated with an adhesive prior to passing the substrate through the liquid-gas interface.
20. The process of feature 19, wherein the adhesive comprises an epoxy resin, a cyanate resin, a polyester resin, a polyimide resin, an organic silicone resin, a polytetrafluoroethylene resin, a cyanoacrylate, a bimaleimide resin, a polyether ether ketone resin, a phenolic resin, a polyethylene resin, or any combination thereof.
21. The process of any of features 15-20, wherein the liquid comprises a surfactant.
22. The process of any of features 15-21, comprising applying heat and spraying the thermally conductive coating with an epoxy binder.
23. A process for fabricating a hydrophobic composite material, the process comprising:
24. The process of feature 23, wherein step (c) comprises vacuum molding, compression curing, shrink wrap molding, autoclaving, heat, or a combination thereof.
25. A process for fabricating a multilayered composite, the process comprising:
26. The process of feature 25, wherein the core layer comprises air, a foam, a honeycomb, a ferrite material, a magneto-ceramic material, a metal, a polymeric material, a fibrous material, or a combination thereof.
27. The process of feature 25 or 26, wherein the hydrophobic layer comprises fibers coated with polytetrafluoroethylene.
28. The process of any of features 25-27, further comprising applying an adhesive or binder to the fiberglass layer and or the hydrophobic layer.
29. The process of feature 28, wherein the adhesive or binder comprises an epoxy resin, a cyanate resin, a polyester resin, a polyimide resin, an organic silicone resin, a polytetrafluoroethylene resin, a cyanoacrylate, a bimaleimide resin, a polyether ether ketone resin, a phenolic resin, a polyethylene resin, or a combination thereof.
30. The process of any of features 25-29, further comprising applying an additional hydrophobic coating over the hydrophobic layer, the additional hydrophobic coating comprising polytetrafluoroethylene, silica, silicone acrylic copolymer, organic or inorganic polysiloxane, manganese oxide polystyrene, zinc oxide polystyrene, calcium carbonate, carbon nanotubes, carbon fibers, fluorinated silane, fluoropolymer, or a combination thereof.
31. The process of any of features 25-30, wherein step (b) comprises forming a Langmuir-Blodgett film comprising said hexagonal boron nitride platelets and dip-coating the product of step (a) with the Langmuir-Blodgett film.
The present technology provides composite layered material compositions having one or more hexagonal boron nitride (hBN)-containing layers or films, together with layers comprising optional polymeric binders, glass fibers, magneto-ceramic materials, and a superhydrophobic outer coating. The technology also provides methods for making the composite materials and products containing them. The composite materials are useful for making radomes and other coverings for electronic components and equipment, for example. On such method is a Langmuir-Blodgett technique for coating surface of products with layers of boron nitride (BN) in thicknesses ranging from monolayers less than 1 μm to multilayers of up to at least 1 cm for creating a highly efficient thermally conductive coating on any product or device surface.
The thermally conductive hexagonal boron nitride (hBN) films or layers can have a variety of applications and can improve upon existing thermal coatings due to the high in-plane or basal-plane thermal conductivity of hBN. In the specific example of fiberglass-epoxy (FG-epoxy) composites without hBN, poor thermal conductivity leads to localized hot spots in the material when used as a covering for electrical equipment, causing mechanical and electrical degradation. The present inventors have Introduced a thin monolayer of hBN, preferably in the form of hBN platelets, at a surface of a composite, which can allow heat to spread laterally without impacting the material properties and also extending the longevity of the material. The reduction of hot spots in a radome material, for example, can reduce RF distortion and improve signal and special resolution, as well as improve signal to noise ratio, material longevity, and protection of enclosed equipment. The hBN platelets have very high thermal conductivities along the basal-plane axes (X,Y) of the crystal, e.g., ˜300-600 W/mK, and along the through plane or short axis (Z), e.g., ˜20-40 W/mK. The hBN platelets provide RF transparency or translucency in the through plane and can be combined with A-sandwich, C-sandwich, or other band-pass layer structures. The thermal management technologies described herein provide simple, less expensive solutions to thermal management applications that can be active, energy intensive, and complex.
The creation of thermal dispersion layers (thermal spreaders) based on hBN can be achieved in many architectures from single and multiple layers of percolated hBN monolayers to thicker films. The thickness of these thermal spreaders can range from about less than 1 micron in the case of the hBN monolayers and about 50 microns to about 5 millimeters or 1 cm or more for thicker films.
The fabrication techniques can include i) the creation of single and multiple layers of percolated hBN particles on the surface of other materials to serve as a thermal spreading layer to dissipate heat build-up and ii) a sandwich structure that combines, for example, glass-fiber reinforced polymers (GFRP) and hBN filled epoxy or polymer to create thermally conductive hBN-GFRP hybrid materials. In the first process, the single or multiple layers of percolated hBN particles are applied to any component of any material and geometry by using a Langmuir-Blodgett method provided the epoxy or adhesive binder adheres well and the material can withstand short exposure to water, solvent, or mixtures of water and solvent.
The fabrication methods can use a vacuum molding process to laminate the thermal spreading to various substrates, providing excellent flexibility in the desired final product. The effectiveness of thermal spreaders is investigated with hBN particles herein, specifically platelets of varied diameters (diameter referring to the largest linear measure from one end to another in the platelet basal plane). In general, higher thermal conductivities were obtained using larger diameter hBN particles or platelets.
To produce thermal spreading architectures that have single and multiple hBN monolayers, one-step and two-step Langmuir-Blodgett (L-B) film processes can be used. Both the one-step and two-step methods can be used to apply extremely thin (<1 μm) hBN films to components. Additional steps can be used to apply additional functionality to films or layers, to provide additional films or layers, or to provide custom products. The thin layers of hBN can be advantageous in certain applications especially involving electromagnetic or optical transmission.
In a one-step L-B film process, hBN platelets can be self-assembled on the surface (i.e., interface with air or another gas) of water, solvent, or liquid mixture (e.g., water-solvent, such as water-alcohol or water together with a water-miscible organic solvent) using surface tension. Percolation can then be achieved using the Marangoni Effect by adding surfactant to the L-B film, which drives the hBN platelets into a fully percolated state. A component or substrate is then carefully dip coated through the L-B film to directly transfer the percolated monolayer of the hBN platelets onto the surface of the component or to a surface of the substrate. One-step L-B film processes can be implemented to directly coat components with varied topography with a single monolayer of percolated hBN particles. These particles can be fixated in some manner, for example by spray coating of a binder or adhesive. Fixation can allow a second or multiple additional monolayers to be added. Fixation can involve evaporation of residual solvent from the layer on the component or substrate by applying heat or vacuum, or evaporation can be separate from fixation. For example, heat can be applied at about 30° C., about 40° C., about 50° C., about 60° C., about 70° C., about 80° C., about 90° C., or higher depending on the composition of the substrate, while also remaining below the boiling point of the liquid phase.
In a two-step L-B film process, the desired component or substrate is separately coated with a very thin layer of adhesive and the one-step L-B film process proceeds as above using the smooth intermediate layer of adhesive. The monolayer and component can then be combined using vacuum molding or compression curing with shrink tape methodologies found in traditional composite manufacturing processes. The additional step of coating the component or substrate with a thin layer of adhesive can provide a topographically smooth surface to which the monolayer hBN can be transferred. Additionally, the thin layer of adhesive can act to directly fixate the hBN monolayer making it mechanically robust and allowing subsequent layers to be applied if required. Components with very rough topographies, like glass-fiber reinforced polymers (GFRP), demonstrate enhanced thermal performance with the two-step L-B film. Components with smooth topographies generally would perform similarly thermally; however, the two-step method can provide superior mechanical robustness to ensure the thermal spreading layer is strongly applied. The adhesive can be, for example, an epoxy resin, a cyanate resin, a polyester resin, a polyimide resin, an organic silicone resin, a polytetrafluoroethylene resin, a cyanoacrylate, a bimaleimide resin, a polyether ether ketone resin, a phenolic resin, a polyethylene resin, or any combination thereof.
Thicker hBN films can be produced by plasticizing, for example, about 60 volume percent hBN and epoxy or adhesive slurries with acetone or a solvent followed by traditional mold or tape casting of the slurry to form a thick uncured film on a component such as an uncured fiberglass reinforced polymer prepreg. Additionally, the component can be layered on top of the thick thermal film after casting onto a work substrate. The layered structure including the thermal layer and the component layer can then be consolidated via a vacuum molding process or shrink wrap molding process or autoclaving process or a combination of these to produce strong, fully cured parts with thermal spreading layers that are mechanically connected to the component.
The present methods can use a high volume percent hBN suspension, such as about 60 v %, where the other component is an adhesive or binder. The volume percent hBN t can be in the range from about 1 to about 99 percent, such as about 10 volume percent, about 20 volume percent, about 30 volume percent, about 40 volume percent, about 50 volume percent, about 60 volume percent, about 70 volume percent, about 80 volume percent, or about 90 volume percent, depending on the desired application. A solvent can be optionally added in any amount, for example, to adjust viscosity, penetration, or drying time. For example, the adhesive and solvent can be used along with methods herein to provide durable superhydrophobic functionality, as is discussed in more detail in Example 4.
The technology can provide processing methods to partially or fully coat substrates or components with a single or multiple layers of hBN to improve thermal conductivity in-plane.
A Langmuir-Blodgett (LB) technique can enhance platelet percolation along the basal plane to take advantage of high in-plane conductivity of hBN while maintaining a thin film. The technology can provide any sandwich structure (e.g., A-sandwich, C-sandwich) to combine hBN with GFRP to create thermally conductive and strong dielectric composites. The processing methods can avoid delamination risks involved in combining diverse materials. The processing coatings and methods can be applied flexibly or rigid, and Example 1 provides examples for preparation of hBN coatings and effective hBN-coated FG composites.
The technology can reduce local hotspots that can affect electrical and mechanical behavior. The technology can decouple thermal conduction from electronic conduction via material identity. The technology can provide significant thermal spreading with relatively small electrical interference. The benefits can be achieved with low cost materials.
The technology can be used in a variety of products and commercial applications. Examples are radome materials and coatings, including for aerospace, naval, and terrestrial environments; RF components; printed circuit boards, CPUs (central processing units), or GPUs (graphics processing units), especially in heat spreading layers thereof to reduce thermal loading; circuit boards; transparent or translucent thermal coatings; and thermal management within batteries and in cell packaging.
Multilayered composites and structures described herein, such as a radome structures, exhibit improved mechanical rigidity, thermal management, durable hydrophobicity, and tunable band-pass capability compared to previous materials. The technology addresses previous limitations with low-loss or even no-loss engineered ferrites, which suffer from mechanical brittleness, water adsorption, and non-negligible thermal conductivity. Previous thermal management solutions are often active, energy intensive, and require systems-level infrastructure and design. Water accumulation on RF systems poses a significant performance challenge, as well as typically requiring energy intensive mitigation. Wear resistance and mechanical robustness are essential to longevity and to proper function. With the present technology, thermal and water management can be combined in a customized and robust solution.
Most materials can interact with RF signals. RF signals include electromagnetic energy waves that can radiate from a conductor (antenna) into space with frequencies from about 20 kHz to about 300 GHz. The class of RF materials includes both materials that are good at absorbing RF waves (high-loss materials generally with high electrical permittivity) or are good at transmitting RF waves (low-loss materials generally with very low electrical permittivity). Materials in between high-loss and low-loss (most materials) are less useful for the design and engineering of RF systems. One RF system that represents a low-loss material application is a radome in which an enclosed RF antenna needs to communicate with the outside world. The radome serves as a visual, thermal, and elemental protective shield for the antenna. However, the radome can also work as a shield that can to reduce the transmittance of the RF signal at certain frequencies.
An ideal radome addresses the visual, thermal, elemental and electromagnetic requirements to function well in the application of low-loss RF transmission through a solid object. The ideal radome material should therefore be multi-functional. Several features of a desirable radome material can include optical opacity, extreme low-loss, mechanical robustness, wear-resistance that is super-hydrophobicity, and thermal management.
A radome generally is benefitted by minimizing the lossiness of the selected material. An exception when selective lossiness in certain bands is desired but not in others (e.g., creating bandpass RF filters on the radome). Low-loss materials such as polyethylene and even epoxy have been considered for this application. In addition, epoxy and fiberglass composites can be somewhat lossy but are still widely employed due to their mechanical benefits. Radome composites often layer their epoxy and fiberglass in specific lay-up architectures so as to minimize loss, for example, by creating λ/4 geometries that utilize perfect incoherence to reduce reflected signal and thereby increase transmitted signal.
Engineered ferrites can be used to take advantage of the interaction between RF signals and organized magnetic microstructures. Some systems are essentially no-loss, exhibiting inductive matching with free-space (Z=1). Such no-loss materials have the potential for minimizing their interaction with an RF signal, thereby being “invisible” in a region. In some applications, such a material represents an ideal case. Even with a perfect no-loss radome material, however, a rainstorm can transition it from no-loss to low-loss, and even to high-loss simply by depositing water droplets on the structure. These engineered ferrites exhibit hydrophilicity (contact angles around 45°), meaning that most of the radome would remain wet during and well after a rainstorm. Further, ferrites can be dense polycrystalline ceramics that are inherently brittle and can catastrophically fail under significant or repeated impact (e.g. direct ballistic impact or a few hailstorms). Further, these ceramics tend to have reasonable thermal conductivities which make it difficult to isolate the RF equipment from broad external temperature swings. The thermal strain from these temperature changes can affect device performance significantly over time.
Implementing engineered magneto-ceramics and/or radomes with λ/4 stack-up geometries is known technology which can be implemented herein. The technology described herein can be used to add additional layers to the ferrites or used to construct a hollow core structure (e.g., air core) typical of λ/4 radomes.
Radomes should withstand various types of loading conditions from the environment and the surrounding engineered structure. If no-loss ferrites are to be used, several drawbacks to be addressed include their mechanical integrity. Due to the brittle nature of ferrite ceramics, the structural integrity of the multi-layered ferrite core composite can be improved with the addition of two glass-fiber reinforced polymer (GFRP) layers in an A-sandwich style design. This design provides a tough outer shell that reduces the chance of premature brittle fracture damaging the radome's performance while minimizing the lossiness of the GFRP addition.
The present technology can provide an A-sandwich design, a C-sandwich design, a half-wave design, quarter-wavelength thicknesses, twelfth-wavelength thicknesses, or any thickness designed for band-pass, strength, durability, filtering, resonance, transmission, reflection, or shielding, for example. Band-pass filters can be designed along with the thermal spreading or dissipation technology and super-hydrophobic durability.
For high performance GFRP-based radomes, a suitable material combination is a quartz fabric-reinforced cyanate ester composite due to the excellent electrical, mechanical, and thermal properties. Quartz-reinforced cyanate ester composites are, however, expensive to create. In examples of multi-layered composites described herein, a glass fabric and an epoxy resin (or other suitable binder or adhesive) can be used in place of the cyanate ester matrix. This replacement is less costly and can mimic the high-performance materials from a processing viewpoint and rapidly develop easily transferrable procedures. In addition, epoxy-based glass-fiber reinforced composites can offer suitable electrical, mechanical, and thermal properties for low-cost, mid-performance radomes.
To improve the mechanical integrity of the multilayer composite, the GFRP should (i) provide acceptable mechanical strength especially in the case of direct impact, and (ii) allow good adhesion between the neighboring layers to provide the mechanical reinforcement effects within the multi-layered composite. To provide an example for these sets of experiments, a standard high strength, low viscosity, laminating epoxy resin (System 2000,
The ability for a radome to dissipate heat generated from within the structure or from the external environment is desirable for stable electrical and mechanical properties. Thermal heat spreaders exist for commercial applications; however, existing heat spreaders (e.g., metallic coatings) may not provide the ideal electrical characteristics for radome applications and generally require a thick coating, impeding the RF transmittance. Coating the interior or exterior of the radome with a thin dielectric composite exhibiting high thermal conductivity in the X-Y plane can provide a heat dissipating layer or film. This film can allow hot spots to easily dissipate through the material, reducing the maximum temperature and maintaining a uniform temperature throughout. Exterior coatings by the same methodology are viable, especially for nose-cone radome applications in which localized hot spots from air drag are generated, a condition exacerbated in supersonic flight.
hBN exhibits excellent in-plane thermal conductivity with values reaching as high as 600 W⋅m−1⋅K−1. In addition, hBN has suitable electrical and mechanical properties for radome applications, making it a prime candidate for example thermal heat spreaders. hBN in platelet form is particularly suitable for use in thermal heat spreaders due to the large aspect ratio and excellent thermal conductivity along the basal plane. In addition, platelets with large aspect ratios can be manipulated to create composites with an aligned microstructure, therefore creating a percolated network within the composite and thermal pathways through the basal plane of each platelet. Herein for example, two methods are described to create high volume fraction thin film hBN-epoxy composites with excellent x-y plane alignment. The coatings described are made by either (i) aligning a single monolayer of hBN <1 μm thick on the desired substrate, or (ii) creating thin 50-600 μm films of 60 v % hBN platelets with excellent percolation on the desired substrates. The thermal heat spreading capabilities of both systems are shown using a custom-built infrared thermography set-up. See the hBN description above for additional details.
Hydrophobicity is intimately related to the physiochemical characteristics of a material's surface, which can be influenced by microstructure and surface functionalization.
This property can be used in radome structures to minimize the accumulation of water during rain or dew events and to promote self-cleaning, preserving the functionality of the radome by reducing electrical interference. The structure needs to be tough and consistent over time, so a self-similar structure is desirable for this application. Here, a self-similar material is defined as one that wears evenly and its hydrophobic properties do not change as it wears.
Accordingly, the technology can describe a family of radomes produced by laminating materials of distinct properties together to simultaneously address two or more of the characteristics of a high performance radome including low-loss, mechanical robustness, thermal management, and wear-resistant super-hydrophobicity. Low-loss can be addressed by implementing tunable engineered ferrites described elsewhere. These ferrites are brittle, hydrophilic, and poor thermal conductors (i.e. insulators). To improve the brittleness, very thin sheets of fiberglass composites can be laminated in a sandwich type configuration using the magneto-ceramic in place of structural foam. To preserve the low-loss characteristics of the magneto-ceramic, the thin fiberglass layers can maintain λ/4 spacing to minimize reflections. To provide wear-resistant, super-hydrophobicity, a self-similar, super-hydrophobic layer can be laminated to the outside of the radome capable of shedding water from rain. Durability of superhydrophobic layers can be enhanced by partially penetrating the layer with adhesive as described herein. In some examples, the superhydrophobic layer is completely penetrated (or coated) with adhesive, and some of the outer adhesive is later degraded away. Durability of superhydrophobic layers can be enhanced, for example, as is shown in Example 4. To address thermal management, a combination of insulators and heat spreaders are described herein.
A hexagonal boron nitride (hBN) filled heat spreader as described above can be used for the interior or exterior surface of a sandwich composite to ensure that localized heat is redistributed across the radome chamber. To demonstrate efficacy of this multi-material radome architecture, full sandwich layered structures have been fabricated and found to exhibit excellent mechanical stability, thermal spreading, and hydrophobicity. In Example 2, the multilayered radome composite schematically shown in
In order for the radome to be robust against the elements, such as impending water droplets, sleet, hail, or more significant impacts, an outer laminate was added to the radome stack up that exhibits wear-resistant super-hydrophobicity. An example of such a material that has been successfully tested is Boston Materials' SuperComp products, which exhibit milled fibers in the z-direction in a dense layer on top of a traditional x-y fiber weave (
Such a model for a hydrophobic layer in the described radome system can be described by reference to a lotus leaf. The leaf surface combines physical texturing along with hydrophobic surface chemistry to increase water droplet contact angle and promote non-wetting behavior. Although a lotus leaf exhibits super-hydrophobicity, the surface is highly fragile, comprised of micro pillars and nanoscale wax crystals that fracture under pressure, destroying the hydrophobic properties. This fragile surface structure is also common with synthetic superhydrophobic materials, especially when exposed to short, high impact forces or abrasion. Most commercially available superhydrophobic materials utilize surface coatings which incorporate chemistry and physical texturing to achieve the desired properties. However, these materials are highly vulnerable to delamination and peeling, and the properties will not withstand abrasion such as scratches or dents. In the case of radomes, the surface must be tough, impact resistant, and resistant to surface wear while maintaining the superhydrophobic and electrical properties.
In Example 4 it is shown that SuperComp composites, which are created from a plain-weave fabric with short ˜150 μm long fibers aligned perpendicular to the fabric in the Z-direction (
To bring super-hydrophobicity into the radome, it is shown herein that the wear resistance of these composites following sandblast testing was excellent, showing wear on the surface but free from large defects and deformities. All samples retained their overall shape and structure, with wear occurring only at the surface. Even after extreme sandblasting (Example 4), the contact angle stayed hydrophobic, dropping down to 117.4° as shown in
While the SuperComp composites are provided as examples, any low-loss superhydrophobic coating can be used in the outlayer of the radome composite material.
The present technology provides for high performance radome composites by combining one, two or more of the features described above, including: super-hydrophobic coating, thermal management, mechanical robustness, and low-loss RF magneto-ceramic. Several examples of multilayered composite materials combining these features are in the Examples. Here, interlayer adhesion is of vital importance to creating a useable composite material. A well-joined interface translates to better mechanics, enhancing stress transfer and lowering the chance of layer delamination. Functionally, the strong bond between layers means that heat can transfer more effectively into the thermal spreading layer, the wear resistance of the superhydrophobic layer is improved, and the mechanical strengthening of the GFRP layers can better protect the magneto-ceramic or air core.
The present technology describes designs for and has experimentally delivered a multilayered composite to solve some engineering barriers in radome designs. A high-performance barium hexaferrite core can be coupled with additional thin composite layers to address the mechanical, thermal, and hydrophobic requirements of a high-performance low-loss, ferrite radome. To achieve this, each layer is designed to combat a particular issue, then the layers are laminated together to create a high performance multi-layered radome composite. These type of A-sandwich radome structures can be employed in fiberglass constructions to minimize RF loss. The tuned ferrite may be able to offset the loss of the composite layers, while the composite layers similarly offset the mechanical, thermal, and chemical shortcomings of the ferrite.
The mechanical reinforcement layers can be achieved through laminating various weights of glass fibers and impregnating them with an epoxy resin (or an adhesive) to create a mechanically tough barrier and protect the ferrite core. In addition, these layers can serve as intermediate layers between the thermal spreading layer, the ferrite, and the superhydrophobic layer to promote adhesion and improve wear resistance.
Thermal gradients are a significant issue in the electrical and mechanical performance of radomes; therefore processes are described to laminate highly aligned hBN films to various substrates to improve the thermal spreading and reduce the overall thermal gradients (e.g., hotspots) of the composite. In this composite, hexagonal boron nitride (hBN) platelets exhibiting a high in-plane thermally conductivity are incorporated into an epoxy matrix using either a monolayer geometry or a high volume fraction hBN composite. These composites show excellent thermal spreading abilities in the X-Y plane and can be used to improve the electrical and mechanical reinforcement of the final radome.
Water accumulation on the surface of radomes is detrimental to RF transmittance. Current superhydrophobic materials do not provide a suitable mechanical strength and self-similar properties in order to survive harsh environmental conditions. To address this, Boston Materials SuperComp Z-aligned composites are modified to exhibit excellent wear resistance and hydrophobic behavior. These composites can be used to achieve superhydrophobic self-similar properties while maintaining excellent impact and surface abrasion properties. Glass fiber SuperComps exhibit compatibility with radome applications.
The technology described herein can be used to prepare customized radome stacks, PCBs, and heat spreading layers for any desired electrical components, circuits, antennas, or used in RF transmission and/or reception. Some example features and advantages of the technology can be a robust aligned hexagonal boron-nitride layer for high-performance dielectric heat spreading, a wearable z-aligned fiber outer layer that exhibits super-hydrophobicity and excellent durability, the ability to tie these layers together along with strengthening glass-fiber reinforced-polymer, and excellent interlayer adhesion between disparate materials. The individual layer components can include relatively inexpensive and common materials. The technology can provide customizable layering architectures.
Monolayer films were created with the L-B (Langmuir-Blodgett) process using water, hBN, ethanol, and detergent. A solution of 25 mg/mL hBN platelets in anhydrous ethanol was dispersed in a bath sonicator and continuously sonicated for even dispersion. 13 mL of the hBN-ethanol solution were slowly pipetted into 700 mL of deionized water to form a monolayer at the air-water interface. 11.7 μL of 10.5% aqueous dishwashing detergent (DAWN ULTRA, Proctor & Gamble) were added to the center of the dish to condense the hBN platelets into a densely packed monolayer (e.g.,
To create cast-molded thin films, hBN platelets were added to epoxy (2120/2000 hardener and resin, FibreGlast) at 60% v/v and thinned with an equal weight of acetone. The acetone was added stepwise to ensure uniform incorporation and mixed in a FlackTek DAC 150.1 FVZ-K Speed Mixer at 2500 RPM for 30 seconds. It was preferable to use acetone, as it only plasticizes the epoxy-hBN slurry without chemically altering it. Speed mixing while the slurry viscosity is high sheared platelet aggregates apart. Adding the bulk acetone reduced slurry viscosity to a castable value. The slurry was poured into a foil mold coated with a mold release agent and left for 1 hour to evaporate all residual solvent. To create various thicknesses, the total slurry volume was increased or reduced depending on the desired final thickness of the heat spreading layer. hBN films ranged in thickness from about 100 μm to about 600 μm depending on the initial volume of the hBN-epoxy slurry. Samples were prepared following the same process for three sizes of hBN platelets (5 μm, 12 μm, and 45 μm). It was found, however, that the smaller platelets compacted more than larger platelets during the solvent evaporation process, ultimately creating cracks within the thermal spreader layer. Therefore, 45 μm platelets were preferred for thicker cast-molded films.
An industry standard vacuum molding process was used for both the two-step monolayer and cast-molded hBN films, with materials provided by FibreGlast. A 3″×3″ piece of woven fiberglass (FG), 2 ounce weight, oriented at 0° to a second coarser-weave piece of FG (10 ounce weight) was pre-impregnated with epoxy by the hand lay-up method. It was found that layering the different FG weights improved uniformity in the BN layers that transfer over. The finer weave of the 2 ounce FG allowed it to fill in the coarser gaps of the 10 ounce weave, leaving the hBN essentially undisturbed, while use of only the 10 ounce weave left sizeable gaps and voids within the composite (
For L-B processing, the concentration of detergent or surfactant can dictate the platelet density at the liquid surface. Higher detergent concentrations push the platelets with enough force to project the platelets out into the space above the liquid surface, allowing them to spread along complex geometries more easily during solvent evaporation (
Direct L-B addition to the FG-epoxy component was investigated using the one-step method, and exhibited platelet sedimentation through the epoxy during curing, which lowered the effective percolation through the monolayer. This technique was superior to the two-step method non-flat substrates, where the standard vacuum molding process could fail to evenly transfer the hBN layer. The L-B technique is also preferred in a situation where a very thin epoxy layer is used, so the sedimentation of the platelets is reduced. One-step L-B without the epoxy binder produces a functional monolayer, but does not have the mechanical stability of the epoxy-bound composite.
Cast-molded films were performed using a tape-casting method instead of the slurry-based sedimentation method. While the thermal spreading ability of the tape-casting method was equivalent to the cast-mold process, the viscosity played a more prominent role using this technique and required fine control of the acetone or other solvent concentration. Tape casting requires more labor compared to cast-mold processing, therefore the cast-molding process was preferred. However, tape casting could be useful in construction applications to coat one side of a building material for use as a thermal spreader that reduces convection currents and insulates analogously to double-paned windows.
Different multi-layered composite samples were prepared and scaled up to domino-sized coupons. These samples were a composite of glass-fiber reinforced polymer (GFRP) mechanical reinforcement layers, hBN thermal spreading layers, and superhydrophobic layers and were made using the same materials and methods detailed above. Hexaferrite substrates were purchased from commercial vendors. Several layer permutations were used in the multi-layered composite structures, aimed at characterizing the different interfacial adhesions. The same vacuum molding process detailed above was used, and in some cases multiple iterations were required to achieve the multilayered sample. For example, both thermal spreading hBN layer and the CFz superhydrophobic layer performed the best if they were on the bottom during the vacuum molding process. Therefore, to achieve a superhydrophobic ferrite core composite with a thermal spreading layer, the ferrite went through two separate vacuum molding processes to adhere the desired layers to each side. Different orders of the layers also were investigated, including attaching the hBN thermal spreading layers directly to the ferrite cores.
In general, ferrite cores were prepared by first sanding the surface with 180 grit sandpaper, rinsing with water to remove residual dust, and dried at room temperature. The ferrite was then lightly brushed with epoxy resin to improve adhesion to the neighboring layer. The final multilayer composite was then prepared using the vacuum molding process previously outlined. In the case when a GFRP is immediately neighboring the ferrite core, an additional 2 ounce GF fabric was added between the ferrite and GFRP to improve the adhesion between the two layers. Every relevant layer permutation exhibited excellent adhesion, allowing a considerable degree of customization. Surface roughening was used to achieve good adhesion between layers. In addition, the ordering of the GFRP layers on the ferrite proved significant, in that the 2 ounce weave minimized voids when in direct contact with the flat ferrite surface.
Using basic hexaferrite substrates, the multilayered composite as illustrated schematically in
10B. The examples shown in
The microstructures of the monolayer and cast-molded films were characterized with optical microscopy and scanning electron microscopy (SEM). These imaging techniques allowed full characterization of the hBN alignment within the film and directly correlated with the thermal spreading ability. Thermal spreading was measured with a custom thermal heat stage and an infrared (IR) thermography camera, as shown in
Particle size was also compared in the hBN monolayer films for a single layer, as results for a single layer are shown in
The 45 μm platelets were used to create BN monolayers and an array of cast-molded hBN-fiberglass composite thicknesses, as shown in
Optical microscopy images of cast-molded hBN films showed excellent uniformity and density of the hBN thermal layer that easily contoured to the rough surface of the FG layer. The incorporation of epoxy binder or adhesive allowed good adhesion to the FG as well as adding mechanical stability to the hBN particles. Ideally, the hBN platelets create a percolated network to allow thermal transport through the high conductivity basal plane. The 60 v % hBN-epoxy films show good adhesion to the FG and percolation within the hBN film as shown in
In this example, System 2000 epoxy (
Contact angle measurements showed improvement in the hydrophobicity with SuperComp compared to traditional fiber weaves and bare epoxy. Wear testing results indicated that the epoxy matrix made the system more durable and consistent. Tested SuperComp composites were created from a plain-weave fabric with short ˜150 μm long fibers aligned perpendicular to the fabric in the z-direction, as shown in the SEM image in
The observed microstructure promotes good impact resistance due to loads applied to the long axis of the fibers as well as the desired surface roughness for superhydrophobic properties. The superhydrophobic samples were received as a dry fabric with no binder or filler allowing a high degree of freedom over the processing and impregnation with the epoxy binder. As received sample is shown in
As used herein, “consisting essentially of” allows the inclusion of materials or steps that do not materially affect the basic and novel characteristics of the claim. Any recitation herein of the term “comprising”, particularly in a description of components of a composition or in a description of elements of a device, can be exchanged with the alternative expressions “consisting essentially of” or “consisting of”.
This application claims priority to U.S. Provisional Application No. 62/880,699, filed 31 Jul. 2019, the entirety of which is incorporated herein by reference, and this application claims priority to U.S. Provisional Application No. 62/936,877, filed 18 Nov. 2019, the entirety of which is incorporated herein by reference.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2020/044667 | 7/31/2020 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 62880699 | Jul 2019 | US | |
| 62936877 | Nov 2019 | US |