Thermally expandable sheet and thermally expandable sheet production method

Abstract

A thermally expandable sheet includes: a first thermally expansive layer that is formed on one side of a base and contains a first thermally expandable material and a first binder, the first thermally expansive layer having a first ratio of the first thermally expandable material with respect to the first binder; and a second thermally expansive layer that is formed on the first thermally expansive layer and contains a second thermally expandable material and a second binder, the second thermally expansive layer having a second ratio of the second thermally expandable material with respect to the second binder, wherein the first ratio is lower than the second ratio.

Description

CROSS-REFERENCE TO RELATED APPLICATION

This application claims the benefit of Japanese Patent Application No. 2017-042815, filed on Mar. 7, 2017, the entire disclosure of which is incorporated by reference herein.

FIELD

This application relates generally to a thermally expandable sheet foaming and expanding according to the amount of heat absorbed and a method of producing the thermally expandable sheet.

BACKGROUND

In the prior art, thermally expandable sheets in which a thermally expansive layer containing a thermally expandable material foaming and expanding according to the amount of heat absorbed is formed on one side of a base sheet are known. The thermally expansive layer can be distended in part or in whole by forming a photothermal conversion layer converting light to heat on the thermally expandable sheet and eradiating the photothermal conversion layer with light. Moreover, methods of forming a shaped object (stereoscopic image) on the thermally expandable sheet by changing the shape of the photothermal conversion layer are also known (for example, see Patent Literature Unexamined Japanese Patent Application Kokai Publication Nos. S64-28660 and 2001-150812).

In thermally expandable sheets, when heat is applied to thermally expansive layer, the thermally expansive layer is distensible in the direction opposite to surface on which the based is provided. In some cases, at this point, the underside of the thermally expansive layer peels-off from the base. Peel-off occurring between the base and the thermally expansive layer is problematic in that the peeled-off portion the thermally expansive layer cannot maintain the shape and height thereof and thus, when force is exerted, the shape and so on deforms.

Therefore, there is a demand for a thermally expandable sheet that can suppress peel-off of the thermally expansive layer from the base when the thermally expansive layer is distended.

The present disclosure is made with the view of the above situation and an objective of the disclosure is to provide a thermally expandable sheet that can suppress peel-off of the thermally expansive layer from the base when the thermally expansive layer is distended and a method of producing the thermally expandable sheet.

SUMMARY

A thermally expandable sheet includes:

a first thermally expansive layer that is formed on one side of a base and contains a first thermally expandable material and a first binder, the first thermally expansive layer having a first ratio of the first thermally expandable material with respect to the first binder; and

a second thermally expansive layer that is formed on the first thermally expansive layer and contains a second thermally expandable material and a second binder, the second thermally expansive layer having a second ratio of the second thermally expandable material with respect to the second binder,

wherein the first ratio is lower than the second ratio.

A thermally expandable sheet production method includes:

a first formation step of forming on one side of a base a first thermally expansive layer that contains a first thermally expandable material and a first binder, the first thermally expansive layer having a first ratio of the first thermally expandable material with respect to the first binder; and

a second formation step of forming on the first thermally expansive layer a second thermally expansive layer that contains a second thermally expandable material and a second binder, the second thermally expansive layer having a second ratio of the second thermally expandable material with respect to the second binder

wherein in the first formation step, the first ratio is lower than the second ratio.

A thermally expandable sheet includes:

a first thermally expansive layer that is formed on one side of a base and in which a first thermally expandable material is dispersed in a first binder at a first ratio; and

a second thermally expansive layer that is formed on the first thermally expansive layer and in which a second thermally expandable material is dispersed in a second binder at a second ratio,

wherein the second ratio is higher than the first ratio.

BRIEF DESCRIPTION OF THE DRAWINGS

A more complete understanding of this application can be obtained when the following detailed description is considered in conjunction with the following drawings, in which:

FIG. 1 is a cross-sectional view schematically showing the thermally expandable sheet according to Embodiment 1;

FIGS. 2A to 2C are cross-sectional views schematically showing the method of producing the thermally expandable sheet according to Embodiment 1;

FIGS. 3A to 3C are illustrations showing the outline of the stereoscopic image formation system according to Embodiment 1;

FIG. 4 is a flowchart showing the stereoscopic image formation process according to Embodiment 1;

FIGS. 5A to 5E are cross-sectional views schematically showing the stereoscopic image formation process according to Embodiment 1;

FIG. 6 is a cross-sectional view schematically showing the thermally expandable sheet according to Embodiment 2;

FIG. 7A and 7B are illustrations showing comparison between a comparative example and the thermally expansive layer of Embodiment 2; and

FIG. 8 is a cross-sectional view schematically showing the thermally expandable sheet according to Embodiment 3.

DETAILED DESCRIPTION

The thermally expandable sheet and the method of producing the thermally expandable sheet according to an embodiment of the present disclosure will be described in detail below using the drawings.

Here, in this embodiment, a “stereoscopic image” means a shaped object and the shaped object includes a wide range of shapes such as simple shapes, geometrical shapes, and characters. Furthermore, the shaped object includes decoration formed as a result of decorating. The decoration means something that invokes a sense of beauty visually and/or tactually. Moreover, “stereoscopic image formation” includes not only forming a shaped object but also decorating (ornamenting).

Embodiment 1

A thermally expandable sheet 10 according to Embodiment 1 comprises, as shown in FIG. 1, a base 11, a first thermally expansive layer 12, a second thermally expansive layer 13, and an ink reception layer 14. In this embodiment, The first thermally expansive layer 12 and the second thermally expansive layer 13 constitute the thermally expansive layer of the thermally expandable sheet 10. Moreover, as described in detail later, the thermally expandable sheet 10 undergoes printing by a stereoscopic image formation system 50 outlined in FIGS. 3A to 3C and has a shaped object (a stereoscopic image) formed.

The base 11 is a sheet-like member supporting the thermally expansive layer. As the base 11, paper such as high-quality paper, medium-quality paper, and synthetic paper, or a conventionally used plastic film such as polypropylene, polyethylene terephthalate (PET), and polybutylene terephthalate (PBT) can be used. Moreover, the base 11 does not rise on the opposite side of the base 11 (the underside shown in FIG. 1) and furthermore has a strength to the extent of not wrinkling or largely undulating when the first thermally expansive layer 12 and the second thermally expansive layer 13 foam and distend in whole or in part. Additionally, the base 11 has enough heat-resistance to resist heating for foaming the thermally expansive layer.

The first thermally expansive layer 12 is formed on one side (the top surface shown in FIG. 1) of the base 11. The first thermally expansive layer 12 is a layer distensible to the dimension according to the heating temperature and the heating time and comprises multiple thermally expandable materials MC1 (thermally expandable microcapsules or micro powder) dispersed in a binder B1. Moreover, as described in detail later, in this embodiment, a photothermal conversion layer is formed on the ink reception layer 14 provided on the top surface (the front side) of the base 11 and/or on the underside (the back side) of the base 11 and is irradiated with light (electromagnetic waves) to cause the regions where the photothermal conversion layer is provided to generate heat. Absorbing the heat generated in the photothermal conversion layer on the front side and/or on the back side, the first thermally expansive layer 12 foams and distends, whereby it is possible to selectively distend only particular regions.

As the binder B1, a thermoplastic resin selected from vinyl acetate-based polymers, acrylic polymers, and the like is used. Moreover, the thermally expandable microcapsules MC1 comprise propane, butane, or other low-boiling vaporizing substances sealed in a thermoplastic resin shell. The shell is formed by, for example, a thermoplastic resin selected from polystyrene, polyvinyl chloride, polyvinyliden chloride, polyvinyl acetate, polyacrylic acid ester, polyacrylonitrile, polybutadiene, or copolymers thereof. The average particle size of the thermally expandable microcapsules is approximately 5 to 50 μm. As the microcapsules are heated to the thermal expansion start temperature or above, their polymer resin shell softens, the encapsulated low-boiling vaporizing substances vaporize, and the pressure causes the capsules to distend. Although depending on the characteristics of the microcapsules used, the microcapsules distend five or so times the pre-distended particle size. Here, in FIG. 1, the microcapsules MC1 are shown in nearly the same particle size for convenience. In practice, the particle size of the microcapsules MC1 varies and not all microcapsules have the same particle size.

The second thermally expansive layer 13 is formed on the first thermally expansive layer 12. Like the first thermally expansive layer 12, the second thermally expansive layer 13 is also a layer distensible to the dimension according to the heating temperature and the heating time and comprises a thermally expandable material MC2 (thermally expandable microcapsules) dispersed in a binder B2. The binder B2 and the microcapsules MC2 use materials described in the explanation of the binder B1 of the first thermally expansive layer 12 and the thermally expandable microcapsules MC1, respectively. Also, the materials used for the binder B2 and the thermally expandable microcapsules MC2 may be different or may be the same as those used for the binder B1 and the thermally expandable microcapsules MC1, respectively. Use of the same materials for the first thermally expansive layer 12 and the second thermally expansive layer 13 preferably allows the raw materials to share, simplifies the production process, and additionally, contributes to reduction in production cost. Moreover, like the first thermally expansive layer 12, absorbing the heat generated in the photothermal conversion layer formed on the top surface and/or on the underside of the thermally expandable sheet 10, the second thermally expansive layer 13 foams and distends.

In this embodiment, the ratio at which the thermally expandable material MC1 is contained in the binder B1 (also termed the content ratio) in the first thermally expansive layer 12 is lower than the ratio at which the thermally expandable material MC2 is contained in the binder B2 (also termed the content ratio) in the second thermally expansive layer 13. Here, the ratio at which the thermally expandable material is contained in the binder is defined by volume ratio, weight ratio, or the like. For example, in the case of using the weight ratio, the weight ratio of the thermally expandable material MC1 to the binder B1 (the first ratio) is lower than the weight ratio of the thermally expandable material MC2 to the binder B2 (the second ratio) and specifically, is 1/3 to 1/8 or so. In other words, for example, assuming that the thermally expandable material MC1 dispersed in 100 parts by weight of the binder B1 is X1 parts by weight and the thermally expandable material MC2 dispersed in 100 parts by weight of the binder B2 is X2 parts by weight, X1/X2 is less than 1 and 1/3 to 1/8 or so. Here, the ratio at which the thermally expandable material is contained in the binder may be defined by density. In such a case, it can be said that the first thermally expansive layer 12 contains the thermally expandable material at a density lower than the second thermally expansive layer 13.

Moreover, since the first thermally expansive layer 12 contains the thermally expandable material at a ratio lower than the second thermally expansive layer 13, the height of the first thermally expansive layer 12 after distension is smaller than the second thermally expansive layer 13 when they are distended under the same condition. Therefore, it is preferable that the first thermally expansive layer 12 is formed thinner than the second thermally expansive layer 13. Additionally, it is preferable that the first thermally expansive layer 12 is formed not thicker than necessary. From these viewpoints, it is preferable that the thickness of the first thermally expansive layer 12 is a thickness corresponding to several, for example one to ten, preferably one to five, of the thermally expandable material MC2. In other words, it is preferable that the second thermally expansive layer 13 is formed to a thickness one to ten times, preferably one to five times, the average particle size of the microcapsules.

The ink reception layer 14 is formed on the second thermally expansive layer 13 formed on one side of the base 11. The ink reception layer 14 is a layer receiving and fixing ink used in the printing step, for example ink of an inkjet printer. The ink reception layer 14 is formed using a general-purpose material according to the ink used in the printing step. For example, in the case of using water-based ink, the ink reception layer 14 is formed using a material selected from porous silica, polyvinyl alcohol (PVA), and the like. Here, in the case of using ultraviolet-curable ink in an inkjet system or the like, the ink reception layer 14 can be omitted. Moreover, when a material that is poor in receiving ink such as plastic film is used for the base 11 and furthermore the photothermal conversion layer is formed on the back side of the base 11, it is preferable to provide an ink reception layer also on another side (underside shown in FIG. 1) of the base 11.

As described in detail later, the thermally expandable sheet 10 of this embodiment comprises the first thermally expansive layer 12 that is between the base 11 and the second thermally expansive layer 13, the first thermally expansive layer 12 containing the thermally distensible material at a ratio lower than the first thermally expansive layer 13, thereby suppressing peel-off of the thermally expansive layer from the base 11 when the thermally expandable sheet 10 is distended.

(Method of Producing the Thermally Expandable Sheet)

The method of producing the thermally expandable sheet 10 will be described next using FIGS. 2A to 2C.

First, a sheet-like material, for example paper, is prepared as the base 11. The base 11 can be in the form of a roll, or precut.

Next, a binder comprising a thermoplastic resin or the like and a thermally expandable material (thermally expandable microcapsules) are mixed to prepare a coating liquid for forming the first thermally expansive layer 12. At this point, the content ratio of the thermally expandable material with respect to binder is lower than the content ratio of the thermally expandable material with respect to binder in the subsequent step of forming the second thermally expansive layer 13 and is, for example, 1/3 to 1/8 or so in weight ratio.

Subsequently, the coating liquid is applied on the base 11 using a known coating device such as a bar coater, a roll coater, or a spray coater. Subsequently, the coating is dried to form the first thermally expansive layer 12 as shown in FIG. 2A. Here, in order to obtain a target thickness of the first thermally expansive layer 12, it is possible to apply and dry the coating liquid multiple times. Also, the first thermally expansive layer 12 is formed thinner than the second thermally expansive layer 13. It is preferable that the thickness of the first thermally expansive layer 12 is a thickness corresponding to several, for example one to ten, preferably one to five, of the thermally expandable material MC1.

Next, a binder and a thermally expandable material are mixed to prepare a coating liquid for forming the second thermally expansive layer 13. The materials used for the binder and the thermally expandable material may be different from the coating liquid for forming the first thermally expansive layer 12 but preferably the same material is used.

Subsequently, the coating liquid for forming the second thermally expansive layer 13 is applied on the first thermally expansive layer 12 using a known coating device of a system such as a bar coater, a roll coater, or a spray coater. Then, the coating is dried to form the second thermally expansive layer 13 as shown in FIG. 2B. Here, in order to obtain a target thickness of the second thermally expansive layer 13, it is possible to apply and dry the coating liquid multiple times.

Next, a material constituting the ink reception layer 14, for example a material selected from porous silica, PVA, and the like, is dispersed in a solvent to prepare a coating liquid for forming the ink reception layer 14. Subsequently, the coating liquid is applied on the second thermally expansive layer 13 using a known coating device of a system such as a bar coater, a roll coater, or a spray coater. Subsequently, the coating is dried to form the ink reception layer 14 as shown in FIG. 2C. Moreover, when the base 11 in the form of a roll is used, the resultant structure is cut into a size suitable for the stereoscopic image formation system (shaping system) 50.

The thermally expandable sheet 10 is produced in the above process.

(Stereoscopic Image Formation System)

The stereoscopic image formation system 50 forming a stereoscopic image (a stereoscopic object or a shaped object) on the thermally expandable sheet 10 of this embodiment will be described next. As shown in FIGS. 3A to 3C, the stereoscopic image formation system 50 comprises a control unit 51, a printing unit 52, an expansion unit 53, a display unit 54, a top plate 55, and a frame 60. FIG. 3A is a front view of the stereoscopic image formation system 50. FIG. 3B is a plane view of the stereoscopic image formation system 50 with the top plate 55 closed. FIG. 3C is a plane view of the stereoscopic image formation system 50 with the top plate 55 opened. In FIGS. 3A to 3C, the direction X coincides with the horizontal direction, the direction Y coincides with the conveyance direction D in which the sheet is conveyed, and the direction Z coincides with the vertical direction. The directions X, Y, and Z are orthogonal to each other.

The control unit 51, the printing unit 52, and the expansion unit 53 are each placed within the frame 60 as shown in FIG. 3A. Specifically, the frame 60 comprises a pair of nearly rectangular sideboards 61 and a coupling beam 62 provided between the sideboards 61. The top plate 55 extends between the sideboards 61 in the upper part. Moreover, the printing unit 52 and the expansion unit 53 are juxtaposed in the direction X on the coupling beam 62 extending between the sideboards 61. The control unit 51 is fixed underneath the coupling beam 62. The display unit 54 is embedded in the top plate 55 to be flush with the top surface of the top plate 55.

The control unit 51 comprises a central processing unit (CPU), a read only memory (ROM), a random access memory (RAM), and the like and controls the printing unit 52, the expansion unit 53, and the display unit 54.

The printing unit 52 is a printing device of an inkjet system. As shown in FIG. 3C, the printing unit 52 comprises an introducer 52a for introducing the thermally expandable sheet 10 and a discharger 52b for discharging the thermally expandable sheet 10. The printing unit 52 prints a specified image on the front side or the back side of the thermally expandable sheet 10 introduced from the introducer 52a and discharges the thermally expandable sheet 10 on which the image is printed from the discharger 52b. Moreover, the printing unit 52 comprises color inks (cyan (C), magenta (M), and yellow (Y)) for forming a color ink layer 42 described later and black ink (containing carbon black) for forming a front side photothermal conversion layer 41 and a back side photothermal conversion layer 43. Here, for forming black or gray color in the color ink layer 42, carbon black-free black color ink may further be provided as a color ink.

The printing unit 52 acquires from the control unit color image data presenting a color image (the color ink layer 42) to print on the front side of the thermally expandable sheet 10 and prints the color image (the color ink layer 42) using the color inks (cyan, magenta, and yellow) based on the color image data. Black or gray color in the color ink layer is formed by mixing the three, CMY, colors or using carbon black-free black color ink.

Moreover, the printing unit 52 prints the front side photothermal conversion layer 41 using black ink based on front side foaming data that are data presenting parts to foam and distend on the front side of the thermally expandable sheet 10. Similarly, the printing unit 52 prints the back side photothermal conversion layer 43 using black ink based on back side foaming data that are data presenting parts to foam and distend on the back side of the thermally expandable sheet 10. Moreover, carbon black-containing black ink is an example of the material converting electromagnetic waves to heat (for example, an electromagnetic-heat conversion material such as carbon), namely the material converting light to heat. The thermally expansive layer distends higher in parts where the black ink density is higher. Therefore, the gradation of the black ink density is determined corresponding to the target heights.

The expansion unit 53 is an expansion device heating and distending the thermally expandable sheet 10. As shown in FIG. 3C, the expansion unit 53 comprises an introducer 53a for introducing the thermally expandable sheet 10 and a discharger 53b for discharging the thermally expandable sheet 10. The expansion unit 53 heats and distends the thermally expandable sheet 10 introduced from the introducer 53a and discharges the distended, thermally expandable sheet 10 from the discharger 53b. The expansion unit 53 comprises an irradiator (not shown) therein. The irradiator is, for example, a halogen lamp and emits light in the near infrared range (wavelengths 750 to 1400 nm), the visible light range (wavelengths 380 to 750 nm), or the mid-infrared range (wavelengths 1400 to 4000 nm). As the thermally expandable sheet 10 on which carbon black-containing black ink is printed is irradiated with light, the light is converted to heat more efficiently in the parts whether the black ink is printed than in the parts where no black ink is printed. Therefore, the thermally expansive layer (the first thermally expansive layer and the second thermally expansive layer) is mainly heated in the regions where the black ink is printed and consequently, the thermally expansive layer distends in the regions where the black ink is printed.

The display unit 54 comprises a touch panel and the like. The display unit 54 displays, for example as shown in FIG. 3B, an image (stars shown in FIG. 3B) to be printed on the thermally expandable sheet 10 by the printing unit 52. Moreover, the display unit 54 displays operation guidance and the like so that the user can operate the stereoscopic image formation system 50 by touching the display unit 54.

(Stereoscopic Image Formation Process)

The process flow of forming a stereoscopic image on the thermally expandable sheet 10 by the stereoscopic image formation system 50 will be described next with reference to the flowchart shown in FIG. 4 and the cross-sectional views of the thermally expandable sheet 10 shown in FIGS. 5A to 5E.

First, the user prepares a thermally expandable sheet 10 before a stereoscopic image is formed, and specifies color image data, front side foaming data, and back side foaming data via the display unit 54. Then, the thermally expandable sheet 10 is inserted into the printing unit 52 with the front side facing up. The printing unit 52 prints a photothermal conversion layer (the front side photothermal conversion layer 41) on the front side of the inserted thermally expandable sheet 10 (Step S1). The front side photothermal conversion layer 41 is a layer formed by a material converting light to heat, specifically carbon black-containing black ink. The printing unit 52 ejects carbon black-containing black ink on the front side of the thermally expandable sheet 10 according to the specified front side foaming data. Consequently, as shown in FIG. 5A, the front side photothermal conversion layer 41 is formed on the ink reception layer 14. Here, for easier understanding, the front side photothermal conversion layer 41 is shown as if it is formed on the ink reception layer 14; however, more precisely, the black ink is received in the ink reception layer 14 and therefore, the photothermal conversion layer is formed in the ink reception layer 14.

Secondly, the user inserts the thermally expandable sheet 10 on which the front side photothermal conversion layer 41 is printed into the expansion unit 53 with the front side facing up. The expansion unit 53 heats the inserted thermally expandable sheet 10 from the front side. Specifically speaking, the expansion unit 53 emits light to the front side of the thermally expandable sheet 10 by means of the irradiator (Step S2). The front side photothermal conversion layer 41 printed on the front side of the thermally expandable sheet 10 absorbs the emitted light and generates heat. Consequently, as shown in FIG. 5B, the regions of the thermally expandable sheet 10 where the photothermal conversion layer 41 is printed rise and distend. Moreover, in FIG. 5B, if the black ink density is higher in the photothermal conversion layer 41 on the right than in the photothermal conversion layer 41 on the left, as shown in the figure, it is possible to distend the region where the print is denser higher.

Thirdly, the user inserts the thermally expandable sheet 10 of which the front side is heated and distended into the printing unit 52 with the front side facing up. The printing unit 52 prints a color image (the color ink layer 42) on the front side of the inserted thermally expandable sheet 10 (Step S3). Specifically, the printing unit 52 ejects cyan C, magenta M, and yellow Y inks on the front side of the thermally expandable sheet 10 according to the specified color image data. Consequently, as shown in FIG. 5C, the color ink layer 42 is formed on the ink reception layer 14 and the photothermal conversion layer 41.

Fourthly, the user inserts the thermally expandable sheet 10 on which the color ink layer 42 is printed into the expansion unit 53 with the back side facing up. The expansion unit 53 heats the inserted thermally expandable sheet 10 from the back side and dries the color ink layer 42 formed on the front side of the thermally expandable sheet 10 (Step S4). Specifically speaking, the expansion unit 53 emits light to the back side of the thermally expandable sheet 10 by means of the irradiator to heat the color ink layer 42 and evaporate the solvent contained in the color ink layer 42.

Fifthly, the user inserts the thermally expandable sheet 10 on which the color ink layer 42 is printed into the printing unit 52 with the back side facing up. The printing unit 52 prints a photothermal conversion layer (the back side photothermal conversion layer 43) on the back side of the inserted thermally expandable sheet 10 (Step S5). Like the front side photothermal conversion layer 41 printed on the front side of the thermally expandable sheet 10, the back side photothermal conversion layer 43 is a layer formed by a material converting light to heat, specifically carbon black-containing black ink. The printing unit 52 ejects carbon black-containing black ink on the back side of the thermally expandable sheet 10 according to the specified back side foaming data. Consequently, as shown in FIG. 5D, the photothermal conversion layer 43 is formed on the back side of the base 11. Also with the back side photothermal conversion layer 43, if the black ink density is higher in the photothermal conversion layer 43 on the left than in the photothermal conversion layer 43 on the right, it is possible to distend the region where the print is denser higher as shown in the figure.

Sixthly, the user inserts the thermally expandable sheet 10 on which the back side photothermal conversion layer 43 is printed into the expansion unit 53 with the back side facing up. The expansion unit 53 heats the inserted thermally expandable sheet 10 from the back side. Specifically speaking, the expansion unit 53 emits light to the back side of the thermally expandable sheet 10 by mean of the irradiator (not shown) (Step S6). The photothermal conversion layer 43 printed on the back side of the thermally expandable sheet 10 absorbs the emitted light and generates heat. Consequently, as shown in FIG. 5E, the regions of the thermally expandable sheet 10 where the photothermal conversion layer 43 is printed rise and distend.

A stereoscopic image (a stereoscopic object or a shaped object) is formed on the thermally expandable sheet 10 in the above proceeding.

Generally, in a thermally expandable sheet, the thermally expansive layer provided on the base distends in the direction opposite to the surface on which the base is provided (for example, upward shown in FIG. 1). With this distension, the base and the thermally expansive layer provided immediately above the base may become separated. Moreover, generally, the greater the content ratio of the thermally expandable material, the more likely separation from the base will occur. Conversely, in the thermally expandable sheet 10 of this embodiment, the second thermally expansive layer 13 of which the content ratio of the thermally expandable material is lower than the second thermally expansive layer 13 is interposed between the base 11 and the second thermally expansive layer 13. The first thermally expansive layer 12 is suppressed in degree of foaming and distension compared with the second thermally expansive layer 13, and therefore, peel-off from the base 11 of the thermally expansive layer is also suppressed. The third thermally expansive layer 31 itself distends, whereby the third thermally expansive layer 31 also has an effect of contributing to increase in height of the entire thermally expansive layer. Additionally, the first thermally expansive layer 12 itself distends, whereby the first thermally expansive layer 12 also has an effect of contributing to increase in height of the entire thermally expansive layer.

In this way, the thermally expandable sheet and the thermally expandable sheet production method of this embodiment provide a thermally expandable sheet and thermally expandable sheet production method that suppresses peel-off of the thermally expansive layer from the base when the thermally expansive layer is distended.

Embodiment 2

A thermally expandable sheet 20 according to Embodiment 2 will be described using the drawings. The thermally expandable sheet 20 according to Embodiment 2 is different from the thermally expandable sheet 10 according to Embodiment 1 in that a third thermally expansive layer 26 is further provided on the second thermally expansive layer 13. The parts having the same structure as in Embodiment 1 are referred to by the same reference numbers and their explanation will be omitted.

The thermally expandable sheet 20 according to Embodiment 2 comprises, as shown in FIG. 6, the base 11, the first thermally expansive layer 12, a second thermally expansive layer 13, the ink reception layer 14, and the third thermally expansive layer 26. Also, the first thermally expansive layer 12, the second thermally expansive layer 13, and the third thermally expansive layer 26 constitute the thermally expansive layer of the thermally expandable sheet 20. Also, in this embodiment, the ink reception layer 14 is formed on third thermally expansive layer 26 that is disposed on the second thermally expansive layer 13

The third thermally expansive layer 26 is formed between the second thermally expansive layer 13 and the ink reception layer 14. Like the first thermally expansive layer 12, the third thermally expansive layer 26 comprises a thermally expandable material MC3 (thermally expandable microcapsules) in a binder B3. Like the first thermally expansive layer 12, absorbing heat generated in the photothermal conversion layer that forms on the top surface and/or the underside of the thermally expandable sheet 20, the third thermally expansive layer 26 foams and distends. Moreover, the binder B3 and the microcapsules MC3 use materials described in the explanation of the binder B1 of the first thermally expansive layer 12 and the thermally expandable microcapsules MC1, respectively. The materials used for the thermally expandable microcapsules MC3 may be different from the materials used for the thermally expandable microcapsules MC1 of the first thermally expansive layer 12 and the thermally expandable microcapsules MC2 of the second thermally expansive layer 13 or may be the same as one or both of those used for the thermally expandable microcapsules MC1 of the first thermally expansive layer 12 and the thermally expandable microcapsules MC2 of the second thermally expansive layer 13. When the same materials as the first thermally expansive layer 12 and/or the second thermally expansive layer 13 are used for the third thermally expansive layer 26, the raw materials can be shared and this is preferable. Likewise, the binder B3 may be different from that of binder B2 and binder B3 but it is preferable that the material be the same as one or both of the binders.

Moreover, the ratio at which the thermally expandable material MC3 is contained in the binder B3 in the third thermally expansive layer 26 is lower than the ratio at which the thermally expandable material MC2 is contained in the binder B2 in the second thermally expansive layer 13. As in Embodiment 1, the ratio at which the thermally expandable material MC3 is contained in the binder B3 is defined by volume ratio, weight ratio, or the like. For example, in the case of using the weight ratio, the weight ratio of the thermally expandable material MC3 to the binder B3 is lower than the weight ratio of the thermally expandable material MC2 to the binder B2 and specifically, is 1/3 to 1/8 or so. In other words, assuming that the MC3 dispersed in 100 parts by weight of the binder B3 is X3 parts by weight and the MC2 dispersed in 100 parts by weight of the binder B2 is X2 parts by weight, X3/X2 is less than 1 and 1/3 to 1/8 or so. Here, the ratio at which the thermally expandable material is contained in the binder may be defined by density. In such a case, it can be said that the third thermally expansive layer 26 contains the thermally expandable material at a density lower than the second thermally expansive layer 13

Here, because of a lower content ratio of the thermally expandable material compared with the second thermally expansive layer 13, it is difficult for the third thermally expansive layer 26 to heighten while distending; therefore, it is preferable to form the third thermally expansive layer 26 thinner than the second thermally expansive layer 13. Moreover, it is preferable that the third thermally expansive layer 26 is formed not thicker than necessary. Preferably, the third thermally expansive layer 26 is a thickness corresponding to several, for example one to ten, preferably one to five, of the thermally expandable material MC3. In other words, it is preferable that the third thermally expansive layer 26 is formed to a thickness one to ten times, preferably one to five times, the average particle size of the mircocapsules.

The method of producing the thermally expandable sheet 20 according to Embodiment 2 will be described next.

First, the base 11 is prepared and then the first thermally expansive layer 12 and the second thermally expansive layer 13 are formed on the base 11.

Next, a coating liquid for forming the third thermally expansive layer 26 is prepared. A thermally expandable material is dispersed in a binder using, for example, a known dispersion device to prepare a coating liquid for forming the third thermally expansive layer 26. The same materials as the coating liquid for forming the second thermally expansive layer 13 may be used for the binder and the thermally expandable material. At this point, the content ratio of the thermally expandable material in the binder is lower than the content ratio of thermally expandable material in the binder of the second thermally expansive layer 13. For example, it is 1/3 to 1/8 or so in weight ratio. Subsequently, the coating liquid is applied on the base 11 using a known coating device of a system such as a bar coater, a roll coater, and a spray coater and then a coating forms. Next the coating is dried. The coating liquid may be applied and dried in multiple parts and the third thermally expansive layer 26 of a target thickness is formed on the second thermally expansive layer 13

Subsequently, as in Embodiment 1, the ink reception layer 14 is formed on the third thermally expansive layer 26 and the resultant structure is cut, for example, as needed. As a result, the thermally expandable sheet 20 of Embodiment 2 is produced.

According to the thermally expandable sheet and the thermally expandable sheet production method of this embodiment, the third thermally expansive layer 26 containing a thermally expandable material at a content ratio lower than the second thermally expansive layer 13 is further formed on the second thermally expansive layer 13, whereby it is possible to reduce occurrence of unevenness on the surface of the thermally expandable sheet when the thermally expansive layer is distended, make the thermally expandable sheet surface excellently smooth, and thus impart excellent rub resistance.

For example, as a comparative embodiment, FIG. 7A schematically shows a sheet surface of a distended thermally expandable sheet not comprising the third thermally expansive layer. In this structure, as shown in FIG. 7A, microcapsules aggregate on the surface of the thermally expansive layer and cause unevenness of a level difference d1 on the surface. As shown in the figure, the microcapsules situated on the surface of the thermally expansive layer easily come off and are poor in rub resistance. Conversely, in the thermally expandable sheet shown in FIG. 7B that adopts the same structure as this embodiment, the level difference d2 that occurs on the surface of the third thermally expansive layer is smaller than the level difference d1. Since the third thermally expansive layer distends not only upward but also downward, unevenness that occurs in the second thermally expansive layer is filled due to distension of the third thermally expansive layer. Moreover, the third thermally expansive layer contains a smaller amount of microcapsules; therefore it is possible to suppress aggregation of microcapsules on the surface of the third thermally expansive layer. Additionally, particularly the third thermally expansive layer 26 of this embodiment contains a thermally expandable material and thus the third thermally expansive layer itself distends, and also has an effect of contributing to increase in height of the entire thermally expansive layer. Moreover, the ink reception layer 14 is a layer to receive and fix ink on the surface of the thermally expandable sheet 20. With this layer provided on the third thermally expansive layer 26, the surface of the thermally expandable sheet 20 is made more excellently smooth and more excellent in rub resistance.

Embodiment 3

A thermally expandable sheet 30 according to Embodiment 3 will be described using the drawings. The thermally expandable sheet 30 according to Embodiment 3 is different from the thermally expandable sheets 10 and 20 of the above Embodiments in that the third thermally expandable sheet 30, as shown in FIG. 8, comprises a third thermally expansive layer 36, and in that the thermally expansive layer 36 contains white pigment W In this embodiment, the first thermally expansive layer 12, the second thermally expansive layer 13, and the third thermally expansive layer 36 constitute the thermally expansive layer. The parts having the same structure as in the other embodiments are referred to by the same reference numbers and their explanation will be omitted.

The thermally expandable sheet 30 according to Embodiment 3, as shown in FIG. 8, comprises a base 11, a the first thermally expansive layer 12, the second thermally expansive layer 13, an ink reception layer 14, and the third thermally expansive layer 36. Moreover, the first thermally expansive layer 12, the second thermally expansive layer 13, and the third thermally expansive layer 36 constitute the thermally expansive layer of the thermally expandable sheet 30. Also, the ink reception layer 14 in this embodiment is formed on the thermally expansive layer 36 formed on the second thermally expansive layer 13.

The third thermally expansive layer 36 is formed on the second thermally expansive layer 13 formed on one side of the base 11. The third thermally expansive layer 36 comprises the thermally expandable material MC3 (thermally expandable microcapsules) in the binder B3 as in Embodiment 2. The third thermally expansive layer 36 characteristically, further contains white pigment W. As the white pigment W, a material selected from titanium oxide, barium sulfate, zinc oxide, and the like can be used and particularly, titanium oxide is preferable. Further, the content ratio of the thermally expandable material MC3 in the binder B3 is set lower than the content ratio of the thermally expandable material MC2 in the binder B2 of the second thermally expansive layer 13 as in Embodiment 2.

Moreover, in this embodiment, using a white material such as porous silica as the ink reception layer 14, the degree of whiteness of the ink reception layer 14 is also improved. Thus, preferably, the degree of whiteness on the surface of the thermally expandable sheet 30 is improved also by the ink reception layer 14.

With the third thermally expansive layer 36 further containing white pigment, the thermally expandable sheet 30 of this embodiment can improve the degree of whiteness of the surface of the thermally expandable sheet 30 and show the color of the color ink provided on the thermally expandable sheet 30 better.

The method of producing the thermally expandable sheet 30 of Embodiment 3 will be described next.

As in Embodiment 1, the base 11 is prepared and the steps up to forming the base 11 and the first thermally expansive layer 12 on the base 11 are the same as in Embodiment 1.

Next, a thermally expandable material and white pigment are dispersed in a binder using a known dispersion device to prepare a coating liquid for forming the third thermally expansive layer. At this point, the weight of the thermally expandable material mixed with respect to the binder in the coating liquid is 1/3 to 1/8 or so compared with the coating liquid for forming the second thermally expansive layer as in Embodiment 2. Subsequently, the coating liquid is applied on the base using a known coating device such as a bar coater, a roll coater, and a spray coater to form a coating. Next, the coating is dried. In order to form the third thermally expansive layer 36 of a target thickness, the coating liquid may be applied and dried in multiple parts.

Subsequently, as in Embodiment 1, the ink reception layer 14 is formed and cut as needed.

As a result, the thermally expandable sheet 30 according to Embodiment 3 is produced.

With the third thermally expansive layer 36 further containing white pigment, the thermally expandable sheet 30 of this embodiment can improve the degree of whiteness of the thermally expansive layer 30, whereby it is possible to show the color of the color ink provided on the thermally expandable sheet 30 better. Furthermore, if the ink reception layer 14 is formed using a white material such as porous silica, preferably, the degree of whiteness of the thermally expandable sheet 30 is improved also by the ink reception layer 14. Additionally, in this embodiment, the white pigment W is contained in the third thermally expansive layer 36, not in the second thermally expansive layer 13 or the ink reception layer 14. Therefore, reduction in the distensible height of the first thermally expansive layer 12 and the second thermally expansive layer 13 can be avoided, without having to mix the white pigment W with the first thermally expansive layer 12 or the second thermally expansive layer 13. Furthermore, since white pigment does not get mixed in with the ink reception layer 14, an excellent effect of preventing the ink reception layer 14 from deteriorating in the ability of receiving ink is also obtained.

The present disclosure is not confined to the above-described embodiments and various modifications and applications are available. For example, the above-described embodiments can be combined as appropriate.

Further, in the above-described embodiments, explanation is made using an exemplary configuration in which the printing is conducted in the process shown in FIG. 4. However, this is not restrictive. For example, the order of processing can be changed as appropriate. For example, it is possible to form a photothermal conversion layer on both sides of the base, form a color ink layer, and then emit light to each of the front side and the back side of the base to cause the thermally expansive layer to distend.

Moreover, in the above-described embodiments, explanation is made using an exemplary configuration in which the photothermal conversion layer is formed on both the front side and the back side. However, this is not restrictive. The photothermal conversion layer may be formed only on the front side or on the back side depending on the intended use and/or the printing method of the print. Here, when the print is made only on the front side, the ink reception layer has only to be formed at least on the front side.

Moreover, adhesive and release paper may be provided on the back side of the base depending on the intended use of the print, for example in the case of using as a sticker. In such a case, a layer comprising adhesive is formed on the back side of the base and release paper is provided thereon. Here, the ink reception layer may be provided on the release paper.

Embodiments of the present disclosure are described above. The present disclosure is included in the scope of claims and its equivalent scope.

The present disclosure is usable for a thermally expandable sheet expanding according to the amount of heat absorbed and a method of producing the thermally expandable sheet.

The foregoing describes some example embodiments for explanatory purposes. Although the foregoing discussion has presented specific embodiments, persons skilled in the art will recognize that changes may be made in form and detail without departing from the broader spirit and scope of the invention. Accordingly, the specification and drawings are to be regarded in an illustrative rather than a restrictive sense. This detailed description, therefore, is not to be taken in a limiting sense, and the scope of the invention is defined only by the included claims, along with the full range of equivalents to which such claims are entitled.

Claims

1. A thermally expandable sheet comprising: a base;a first thermally expansive layer formed on the base, wherein the first thermally expansive layer comprises a first thermally expandable material and a first binder, andwherein the first thermally expansive layer has a first ratio of the first thermally expandable material with respect to the first binder; anda second thermally expansive layer formed on the first thermally expansive layer, wherein the second thermally expansive layer comprises a second thermally expandable material and a second binder, andwherein the second thermally expansive layer has a second ratio of the second thermally expandable material with respect to the second binder,wherein the first ratio is lower than the second ratio.

2. The thermally expandable sheet according to claim 1, wherein a thickness of the first thermally expansive layer is thinner than a thickness of the second thermally expansive layer.

3. The thermally expandable sheet according to claim 1, wherein the first thermally expandable material and the second thermally expandable material are the same material.

4. The thermally expandable sheet according to claim 1, wherein each of the first thermally expandable material and the second thermally expandable material comprises microcapsules,wherein each of the microcapsules comprises a shell and a vaporizing substance in the shell, andwherein a thickness of the first thermally expansive layer corresponds to a combined thickness of one to ten times the average particle size of the microcapsules.

5. The thermally expandable sheet according to claim 1, further comprising: a third thermally expansive layer provided on the second thermally expansive layer and comprises a third thermally expandable material and a third binder,wherein the third thermally expansive layer has a third ratio of the third thermally expandable material with respect to the third binder, andwherein the third ratio is lower than the second ratio.

6. The thermally expandable sheet according to claim 2, further comprising: a third thermally expansive layer provided on the second thermally expansive layer,wherein the third thermally expansive layer comprises a third thermally expandable material and a third binder,wherein the third thermally expansive layer has a third ratio of the third thermally expandable material with respect to the third binder, andwherein the third ratio is lower than the second ratio.

7. The thermally expandable sheet according to claim 5, wherein the third thermally expansive layer further comprises white pigment comprising one of titanium oxide, barium sulfate, and zinc oxide.

8. The thermally expandable sheet according to claim 6, wherein the third thermally expansive layer further comprises white pigment comprising one of titanium oxide, barium sulfate and zinc oxide.

9. The thermally expandable sheet according to claim 7, further comprising: an ink reception layer formed on the third thermally expansive layer,wherein the ink reception layer is configured to receive ink.

10. The thermally expandable sheet according to claim 8, further comprising: an ink reception layer formed on the third thermally expansive layer,wherein the ink reception layer is configured to receive ink.

11. The thermally expandable sheet according to claim 1, wherein the first binder of the first thermally expansive layer and the second binder of the second thermally expansive layer are the same material.

12. A thermally expandable sheet comprising: a base;a first thermally expansive layer formed on the base, wherein the first thermally expansive layer comprises a first binder and a first thermally expandable material dispersed in the first binder at a first ratio; anda second thermally expansive layer formed on the first thermally expansive layer wherein the second thermally expansive layer comprises a second binder and a second thermally expandable material dispersed in the second binder at a second ratio,wherein the second ratio is higher than the first ratio.

13. The thermally expandable sheet according to claim 1, wherein the first ratio is one of a volume ratio of the first thermally expandable material to the first binder, a weight ratio of the first thermally expandable material to the first binder, and a density of the first thermally expandable material contained in the first binder, andwherein the second ratio is one of a volume ratio of the second thermally expandable material to the second binder, a weight ratio of the second thermally expandable material to the second binder, and a density of the second thermally expandable material contained in the second binder.