The invention relates to pipe systems containing a thermal insulation, in particular thermally insulated medium pipes, and also thermally insulated cover devices or bushings for connecting conduit pipes having improved thermal insulation. Furthermore, the invention relates to methods for producing such devices and also the use of polymer foams which contain hydrofluoroolefins (HFO) in such devices and for producing such devices. Finally, the invention relates to the use of HFO as a cell gas in thermal insulations.
Pipe systems containing a thermal insulation, also called pre-insulated pipe systems or thermally insulated pipe systems, are known and proven per se. Such pipe systems comprise flexible or rigid medium pipes, which are enclosed by a thermal insulation, which is in turn enclosed by a jacket, and also possibly bushings and/or cover devices. Depending on the construction, these pre-insulated pipe systems are also referred to as a plastic medium pipe system (PMP) or plastic jacketed pipe system (PJP). In the first, the medium pipes used have a certain flexibility, so that the entire composite can also be wound onto drums with a certain application of force. These are therefore also referred to as flexible pipe systems. In the latter, the medium pipes used are not flexible, therefore, reference is also made to rigid pipe systems in the case of the overall composite. Accordingly, thermally insulated medium pipes or conduit pipes having one or more thermal insulation layers are known; as is the production thereof. Thus, methods for the continuous production of thermally insulated medium pipes are known from EP0897788 and from EP2213440. A method for producing individual, rigid pipe sections is known from EP2248648.
In such pipe systems, the foam (for example, polyurethane, PU) generally used as an insulation material changes its composition of its cell gases in the course of time. This takes place due to diffusion of nitrogen and oxygen from the surroundings into the foam and due to diffusion of the foam gases and/or cell gases originally contained in the foam, in particular carbon dioxide and other blowing agents, out of the foam. The air gases have a significantly higher thermal conductivity than the originally contained carbon dioxide and the other typically used blowing agents.
Integrating so-called barrier layers into the outer jacket has been proposed to minimize these diffusion processes.
Metallic layers can be used as the barrier layers. If metallic layers are used, not only is the gas exchange completely suppressed, which is desired, but rather water vapor is also completely prevented from diffusing. This is problematic in particular in the case of the use of medium pipes made of plastic, since water typically flows through them as the medium, because of which water vapor, although also only a small quantity, continuously migrates through the walls thereof. This water vapor has to have the possibility of penetrating outward and/or coming into equilibrium with the surroundings, since otherwise water becomes enriched in the thermal insulation of the thermally insulated conduit pipe in the course of time, whereby the thermal conductivity significantly rises and the risk exists that the thermal insulation will become damaged in the long term.
Layers which consist of one or more polymer materials can be used as barrier layers. Thus, EP1355103 describes thermally insulated conduit pipes which contain a barrier layer made of ethylene vinyl alcohol (EVOH), polyamide (PA), or polyvinylidene chloride (PVDC). Furthermore, EP2340929 describes a plastic jacketed pipe, the outer jacket of which is formed as a multilayer pipe and which has a gas permeation barrier layer (“barrier”) in its interior. The pipes described in these documents are difficult to produce and/or have an inadequate insulation capability. Conduit pipes having thermal insulation and a polymer barrier layer are known from CH710709 (post-published) and WO2004/003423; these polymers contain polyketones and/or EVOH.
Molded parts and connecting pieces are used for connecting thermally insulated pipes. In particular, cover shells are used as molded parts, as described in WO2008/019791. Or bushings are used as connecting pieces, in particular in the case of the connection of rigid pipes. The mentioned problems also arise in the case of such molded parts and connecting pieces.
It is an object of the invention to provide a thermally insulated conduit pipe and also molded parts and connecting pieces which do not have the mentioned disadvantages.
The objects outlined above are achieved according to the independent claims. The dependent claims represent advantageous embodiments. Further advantageous embodiments can be inferred from the description and the figures. The general, preferred, and particularly preferred embodiments, ranges, etc. provided in conjunction with the present invention can be combined with one another as desired. Individual definitions, embodiments, etc. can also be omitted and/or can be nonrelevant.
The present invention will be described in detail hereafter. It is apparent that the various embodiments, preferences, and ranges disclosed and described hereafter can be combined with one another as desired. Moreover, individual definitions, preferences, and ranges may not be applied depending on the embodiment. Furthermore, the term “comprising” includes the meanings “containing” and “consisting of”.
The terms used in the present invention are used in the generally typical meaning routine to a person skilled in the art. If no other meaning results from the direct context, the following terms in particular have in this case the meaning/definitions indicated here.
The present invention is furthermore illustrated by the figures; in addition to the following description, further embodiments of the invention can be inferred from these figures.
In a first aspect, the invention therefore relates to a pipe system containing a thermal insulation (also called pre-insulated pipe system or thermally insulated pipe system), in which said thermal insulation comprises a foam, the cell gas of which contains hydrofluoroolefins (HFOs). Such pipe systems, but without the mentioned cell gas, are known per se and comprise thermally insulated conduit pipes, bushings, and cover devices for connecting such conduit pipes.
In a first embodiment, the invention relates to a thermally insulated conduit pipe (1), comprising at least one medium pipe (4), at least one thermal insulation (3) arranged around the medium pipe, and at least one outer jacket (2) arranged around the thermal insulation, characterized in that said outer jacket (2) possibly comprises a barrier (9) made of plastic, and said thermal insulation (3) comprises a foam, the cell gas of which contains the components defined hereafter.
In a second embodiment, the invention relates to a cover device made of plastic, in particular for the connection points of at least two pipe pieces, which are connected where the cover device has at least one thermal insulation (3) and at least one outer jacket (2) arranged around the thermal insulation, characterized in that said outer jacket (2) possibly comprises a barrier made of plastic, and said thermal insulation (3) comprises a foam, the cell gas of which contains the components defined hereafter.
In a further embodiment, the invention relates to a bushing made of plastic for connecting thermally insulated conduit pipes, wherein the bushing has at least one thermal insulation (3) and at least one outer jacket (2) arranged around the thermal insulation, characterized in that said outer jacket (2) possibly comprises a barrier made of plastic, and said thermal insulation (3) comprises a foam, the cell gas of which contains the components defined hereafter.
This aspect of the invention is to be explained in greater detail hereafter
Thermal insulation (3): the thermal insulation encloses the medium pipe partially or completely, preferably completely. In particular foamed plastics (“foams”), which contain a cell gas in the cells thereof, are suitable as the thermal insulation. The thermal insulation can be homogeneous along its cross section or can be constructed from multiple layers. The thermal insulation in conduit pipes is typically constructed homogeneously.
Cell gases: The gases present in the thermal insulation are referred to as cell gases. They are a result of the production and are composed of chemical and physical blowing agents, and/or the reaction products thereof. Such cell gases are typically added during the foaming process, or they are formed during the foaming process.
According to the present application, the cell gas in the foam of the thermal insulation is characterized in that it contains hydrofluoroolefins (HFOs). The cell gas can consist of only one or of multiple HFOs and can possibly contain additional further components. The cell gas advantageously contains 10-100 vol % HFOs, preferably 20-100 vol % HFOs, more preferably 30-100 vol % HFOs, particularly preferably 40-100 vol % HFOs, very particularly preferably 50-100 vol % HFOs. The cell gas can accordingly contain further components.
In one embodiment, the cell gas contains 0-50 vol % (cyclo)-alkanes, preferably 0-45 vol % (cyclo)-alkanes, more preferably 0-40 vol % (cyclo)-alkanes, particularly preferably 0-35 vol % (cyclo)-alkanes. The ratio of HFOs to (cyclo)-alkanes is preferably at least 2.5:1, preferably at least 3:1.
In a further embodiment, the cell gas additionally or alternatively contains up to 50 vol % CO2, preferably 0-40 vol % CO2, particularly preferably 0-30% CO2. In a further embodiment, the cell gas additionally or alternatively contains up to 5 vol % nitrogen (N2) and/or oxygen (O2).
These further components can be added to the blowing agent like, for example, the mentioned (cyclo)-alkanes; they can arise during the production of the foam like, for example, CO2; they can enter the foam during the production process like, for example, air, O2, N2.
It has surprisingly been shown that even at such low proportions as, for example, 10 vol % HFO in the cell gas, the properties of pipe systems, in particular of thermally insulated conduit pipes, improve in an array of features.
Specifically, it has been found that the conduit pipes described here have a surprisingly improved insulation behavior. Without feeling bound to a theory, it is presumed that the improved insulation properties are established not only by material properties of the HFOs (thermal conductivity), but rather also by improved foaming, induced by the changed viscosity.
In the case of PU foams and PIR foams, the addition of HFO to one of the two starting components (isocyanate or polyol, respectively) and/or during the direct mixing in the mixing head results in a marked viscosity reduction. Without feeling bound to a theory, it is presumed that the reduced viscosity improves the mixing of the two components and thus promotes the formation of comparatively smaller cells.
To achieve a viscosity reduction in a similar order of magnitude using cyclopentane as the blowing agent, alternatively its content could also be increased, for example, by 1.86 times. This would be the factor by which the molecular weights of HFO 1233zd (130.5 g/mol) and of cyclopentane (70.2 g/mol) differ, but this would have multiple disadvantageous consequences:
Furthermore, it has been found that the addition of the HFO to one of the starting components and/or the direct addition to the two starting components in the mixing head reduces the combustibility thereof. This effect is very advantageous because the safety-technology requirements on such a production facility are thus reduced and the design of a corresponding production facility can thus be significantly simplified and costs can thus be saved, which otherwise arise when combustible blowing agents are used.
In summary, it can thus be stated that the known problems can be solved in an elegant manner by the partial or complete replacement of cyclopentane (Cp) by HFOs. On the one hand, more blowing agent can be added, which results in a desired viscosity reduction. At the same time, however, the expanding effect remains substantially unchanged and no fundamental adaptations to formula and production facility are required. Finally, the work protection is improved by the replacement of the combustible cyclopentane by the noncombustible HFO and the investment costs for such a production facility are reduced.
It has furthermore been found that high contents of (cyclo)-alkanes, in particular cyclopentane, have a negative influence on the product quality. Experience has shown that an excessively high content of cyclopentane in the polyol results in the formation of large bubbles in the foam, which occur because the blowing agent (in particular cyclopentane) is expelled from the foam by the temperature of the forming PU foam.
In a continuously operating production process, the outer jacket is typically applied by extrusion and is found at this point in time, because of the high temperature of typically 80-250° C., in a state in which it can easily be deformed. The bubbles then become visible on the outer side of the insulated pipe, because the escaping blowing agent inflates the outer jacket. This applies similarly to insulated pipes having a wavy, a smooth, and a corrugated outer jacket. The escape of the blowing agent is promoted by the temperature of the extruded-on outer jacket. Pipes having such defects are to be considered discards and can no longer be supplied to the practical purpose.
The formation of bubbles is prevented if the content of cyclopentane in the cell gas composition of the resulting insulating foam is 0-50 vol %, preferably 0-45 vol %, particularly preferably 0-40 vol %, most preferably 0-35 vol %.
It has surprisingly been established that upon the use of HFO as a blowing agent, the mentioned bubble formation does not occur. This applies in particular if the content of HFO in the cell gas composition of the resulting insulating foam is within the above-mentioned limits. The described behavior is all the more surprising, since the boiling points are 19° C. in the case of the HFO 1233zd and 33° C. in the case of the HFO 1336mzz, respectively. This is in comparison to cyclopentane, the boiling point of which is 49° C. Because of these boiling points, the expectation that the formation of bubbles would be more pronounced upon the use of the lower-boiling-point HFO as a blowing agent than upon the use of higher-boiling-point (cyclo)-alkanes, for example, Cp. The opposite was observed.
Hydrofluoroolefins (HFOs) are known and commercially available and/or producible according to known methods. They are suitable as a blowing agent gas, in particular because of the low global warming potential (GWP) thereof and because of the harmlessness thereof to the ozone layer of the atmosphere (Ozone Depleting Potential, ODP). The term comprises both compounds which only comprise carbon, hydrogen, and fluorine, and also those compounds which additionally contain chlorine (also referred to as HFCO) and in each case at least one unsaturated bond in the molecule. HFOs can be provided as a mixture of various components or as pure components. HFOs can furthermore be provided as isomeric mixtures, in particular E/Z isomers, or as isomer-pure compounds.
In the scope of the present invention, particularly suitable HFOs are selected from the group comprising compounds of the formula (I)
in which R5 denotes H, F, Cl, CF3, preferably Cl, CF3, and R6 denotes H, F, Cl, CF3, preferably H.
Particularly suitable HFOs are R1233zd (for example, solstice LBA, Honeywell) and R1336mzz (for example, Formacel 1100, DuPont).
It has surprisingly been shown that the conduit pipes described here have improved insulation behavior if the cell gases of the insulation contain at least 10 vol %, preferably at least 30 vol %, particularly preferably at least 50 vol % HFO. It has furthermore been shown that adding such HFOs to the starting materials of the foam insulation results in improved producibility.
(Cyclo)-alkanes are known as the cell gas of the insulation in thermally insulated pipes. Said alkane or cycloalkane is advantageously selected from the group comprising propane, butane, pentane, cyclopentane, hexane, and cyclohexane. By the combination of (cyclo)-alkane with HFO, a fine adjustment of the product properties can be performed, and/or the producibility can be improved and/or a cost reduction can occur with acceptable quality losses. The mentioned (cyclo)-alkanes can be provided as a pure compound or as mixtures; the aliphatic alkanes can be provided as isomer-pure compounds or as isomeric mixtures. A particularly suitable (cyclo)-alkane is cyclopentane.
Carbon dioxide: If the foam is formed from PU or polyisocyanurate (PIR), CO2 typically arises in a certain quantity, since the starting material polyol in industrial quality normally contains a small quantity of water. This water then reacts with the isocyanate to form carbamic acid, which splits off CO2 spontaneously. The CO2 content of the cell gas is thus linked to the purity of the starting materials and is typically less than 50 vol %. If the starting materials are anhydrous, for example, if polyolefins are formed, the CO2 content of the cell gas is thus at 0 vol %. The CO2 content of the cell gas can thus be influenced via the selection of the starting materials (and/or the purity thereof).
Further cell gases: Components can enter the cell gas from the atmosphere/ambient air because of production. These are substantially N2 and/or O2, for example, air. The content of the cell gases is typically less than 5 vol. %. If the production facility is specially configured, the contact with the atmosphere/ambient air can thus be avoided and the content of further cell gases is 0 vol %.
Foam: Said thermal insulation (3) comprises (i.e., contains or consists of) a foam. Such foams are known per se, foams which meet the norms DIN EN 253:2015-12 (in particular for PJP) and EN15632-1:2009/A1:2014, EN15632-2:2010/A1:2014 and EN15632-3:2010/A1:2014 (in particular for PMP) are particularly suitable. The term comprises hard foams and soft foams. Foams can be closed-cell or open-cell, preferably closed-cell, in particular as represented in the norm DIN EN 253:2015-12. Such foams are preferably selected from the group of polyurethanes (PU), polyisocyanurates (PIR), thermoplastic polyesters (in particular PET), and thermoplastic polyolefins (in particular PE and PP).
It has been shown that the following combinations of foam and cell gas are particularly advantageous:
In one embodiment, the mentioned cell gases add up to 100 vol %. In a further embodiment, these cell gases add up together with CO2 and air to 100%. In a further embodiment, the ratio of HFO:Cp is at least 2.5:1.
It has furthermore been shown that the following combinations of foam and cell gas are particularly advantageous:
In one embodiment, the mentioned cell gases add up to 100 vol %. In a further embodiment, these cell gases add up together with air to 100%. In a further embodiment, the ratio of HFO:Cp is at least 3:1.
In a further embodiment, the thermal insulation consists of the mentioned foams and the mentioned cell gases.
Barriers (9): Diffusion barriers are known per se in the field of conduit pipes/pipe systems. If a barrier is present, this barrier is formed as a layer. It is preferable that at least one barrier (9) as described hereafter is provided. It is particularly preferable that one barrier (9) as described hereafter is provided.
This layer (9) enables the diffusion of cell gases out of the thermal insulation and of gases outside the conduit pipe (in particular air) into the thermal insulation to be reduced. This property is important to ensure the insulation capability of the conduit pipe/pipe system over a long time.
In one advantageous embodiment, this layer furthermore enables the diffusion of water out of the thermal insulation. This property is important in particular for conduit pipes/pipe systems, the medium pipe (4) of which consists of plastic. If an aqueous medium is transported in such conduit pipes/pipe systems, water can enter the insulation from the medium through the conduit pipe and thus reduce the insulation capability and damage the insulation material.
In one advantageous embodiment, this layer furthermore enables a certain permeability for CO2 to be provided. A particularly suitable value for the CO2 permeability is in the range of 0.5-100 cm3/m2*day*bar.
Therefore, a barrier having selective properties is advantageous, in particular: (i) permeable to water and water steam, (ii) impermeable to the cell gases which have a low thermal conductivity, (iii) permeable to the cell gases which arise because of production but have a relatively high intrinsic thermal conductivity (for example, CO2), (iv) impermeable to the gases from the surroundings, in particular nitrogen and oxygen and air.
It has been shown that a conduit pipe of the type mentioned at the outset, in which the barrier comprises one or more of the polymers mentioned hereafter, meets the requirements very well. According to the invention, the barrier can be provided in a single layer or in multiple layers separate from one another. Furthermore, the barriers can be attached by means of an additional layer to the insulation or the outer jacket or in the outer jacket (“adhesion promoter layer” (8), (10)).
The barrier (9) can be arranged as a layer in the outer jacket (2); this is preferable, in particular this embodiment preferably has two adhesion promoter layers (8, 10) adjoining the barrier (9) as illustrated in
Furthermore, the barrier can be arranged as a layer on the outer side and/or the inner side of the outer jacket. Furthermore, the barrier can be formed by the outer jacket. Furthermore, the barrier (9) can be arranged as a layer between the thermal insulation (3) and the outer jacket (2). In this embodiment, the adhesion promoter layer is typically omitted.
The barrier layer (9) advantageously has a layer thickness of 0.05-0.5 mm, preferably 0.1-0.3 mm. If the barrier forms the outer jacket, the barrier advantageously has a layer thickness of 0.5-5 mm. If provided, the adhesion promoter layers (8, 10) independently of one another have a layer thickness of 0.02-0.2 mm.
The barrier preferably comprises a copolymer of ethylene with carbon monoxide or with vinyl alcohol.
In one advantageous embodiment, the barrier comprises a polymer, which contains polyketones or consists of polyketones. The polymer layer accordingly comprises polyketones and blends of polyketones and also laminates containing polyketones. Polyketones are materials known per se and are characterized by the keto group (C═O) in the polymer chain. In this embodiment, the polymer advantageously has up to 50-100 wt. %, preferably up to 80-100 wt. %, structural units of formulas (II) or the formula (III).
Polyketones are obtainable by catalytic reaction of carbon monoxide with the corresponding alkenes, such as propene and/or ethene. Such ketones are also referred to as aliphatic ketones. These polymers are commercially available, for example, as polyketone copolymers (formula II) or polyketone terpolymers (formula III) from Hyosung. Such polyketones are furthermore commercially available under the tradename Akrotek® PK. Suitable polymers have a melting temperature of greater than 200° C. (measured using DSC 10 K/min according to ISO11357-1/3) and/or have a low water absorption of less than 3%, measured according to DIN EN ISO 62 (saturation in water at 23° C.).
In one advantageous embodiment, the barrier comprises a polymer, which contains ethyl vinyl alcohol or consists of ethyl vinyl alcohol.
In this embodiment, the polymer has up to 50-100 wt. %, preferably up to 80-100 wt. % structural units of formula (IV).
Suitable ethyl vinyl alcohols are in particular random copolymers in which the ratio m/n is 30/100 to 50/100. These polymers are commercially available, for example, as the EVAL FP series or EP series from Kuraray. They are distinguished by a good processing capability, in particular, they may be processed very well jointly with the normally used jacket material polyethylene (PE) by coextrusion, because the melting viscosities and melting temperatures thereof are in a similar range.
The combination of cell gases from the group of hydrofluoroolefins and barrier layers according to the formulas (II), (III), (IV) described here results in particularly good, superadditive insulation properties of the thermally insulated conduit pipes. Such a positive interaction of these components is surprising. Without feeling bound to one theory, this superadditive effect can be attributed to the barrier properties of the materials according to formulas (II), (III), (IV).
Medium pipe (4): In principle, all medium pipes suitable for thermally insulated pipes can be used. Accordingly, the medium pipe can be formed as a wavy pipe, as a smooth pipe, or as a pipe having a corrugated jacket; it can be a rigid and linear pipe piece, a rigid curved pipe piece, or a flexible pipe piece.
The medium pipe can consist of polymer materials or metallic materials, preferably of polymer materials. Such materials are known per se and are commercially available or produced according to known methods. The materials are selected by a person skilled in the art according to the intended use, possibly after routine experiments.
In one embodiment, said medium pipe (4) is a flexible plastic pipe, the plastic is selected from the group acrylonitrile-butadiene-styrene (ABS), cross-linked polyethylene (PEXa, PEXb, PEXc), PE, polybutene (PB), polyethylene raised temperature (PE-RT), and polyketone (PK).
In a further embodiment, said medium pipe (4) is a flexible plastic pipe having an outer metal layer, the plastic is selected from the group ABS, PEXa, PEXb, PEXc, PE, PB, PE-RT, and PK, the metal is selected from the group aluminum including its alloys. Such inner pipes are also known as composite pipes.
In a further embodiment, said medium pipe (4) is a rigid plastic pipe, the plastic is selected from the group ABS, PEXa, PEXb, PEXc, PE, PB, PE-RT, and PK.
In a further embodiment, said medium pipe (4) is a flexible metal pipe, the metal is selected from the group copper including its alloys, iron including its alloys (for example, rustproof steels), and aluminum including its alloys.
In a further embodiment, said medium pipe (4) is a rigid metal pipe, the metal is selected from the group copper including its alloys, iron including its alloys (for example, rustproof steels), and aluminum including its alloys.
In a further embodiment of the medium pipe (4), the above-mentioned barriers made of plastic can be arranged on the outer side of the inner pipe or they can be formed by the medium pipe itself. A barrier on the medium pipe, or formed by the medium pipe itself, reduces the diffusion of steam from the medium pipe into the thermal insulation. According to the invention, such a (“second”) barrier is combined with a further (“first”) barrier above the thermal insulation.
Outer jacket (2): In principle, all outer jackets suitable for thermally insulated pipes can be used. The outer jacket can accordingly be formed as a corrugated pipe or smooth pipe or as one having a corrugated jacket. It can be a rigid and linear pipe piece, a rigid curved pipe piece, or a flexible pipe piece.
The outer jacket can consist of polymer materials or metallic materials, preferably of polymer materials. Such materials are known per se and are commercially available or produced according to known methods. The materials are selected by a person skilled in the art according to the intended use, possibly after routine experiments. Thermoplastic polymers, such as commercial PE types, are advantageously used. High-density PE (HDPE), low-density PE (LDPE), and linear low-density PE (LLDPE) are suitable. The layer thickness of the outer jacket (2) can vary in broad ranges, but is typically 0.5-20 mm, including the possibly provided barrier and barrier layers.
In one embodiment of the invention, the outer jacket contains the barrier described here, as described above. This embodiment is advantageous, since jacket and barrier can be produced simultaneously and thus cost-effectively by means of coextrusion.
In an alternative embodiment of the invention, the outer jacket does not contain the barrier described here, as described above. In this embodiment, the barrier is provided as a separate layer. This embodiment is advantageous because jacket and barrier can be produced separately and thus flexibly.
In one advantageous embodiment, the invention relates to a conduit pipe as described here, in which said outer jacket (2) is formed as a wavy pipe; and said medium pipe is formed as a flexible pipe piece and in particular has at least one medium pipe based on polyethylene and a thermal insulation based on PU and an outer jacket based on polyethylene.
In a further advantageous embodiment, the invention relates to a conduit pipe as described here, in which said conduit pipe is a rigid linear pipe piece and in particular has at least one medium pipe based on polyethylene or steel and thermal insulation based on PU and an outer jacket based on polyethylene.
In a further advantageous embodiment, the invention relates to a conduit pipe as described here, in which said outer jacket (2) is formed as a corrugated pipe. Such conduit pipes are advantageously combined with a medium pipe, which is formed as a flexible pipe piece and in particular comprises at least one medium pipe based on polyethylene or cross-linked polyethylene. Such conduit pipes are advantageously furthermore provided with a thermal insulation (3), which comprises a foam, the cell gas of which has the above-mentioned composition (wherein the cell gas particularly preferably contains at most 35% (cyclo)-alkane).
In a second aspect, the invention relates to methods for producing thermally insulated conduit pipes, bushings, and cover devices as described here. The invention is accordingly based on the object of providing improved methods for producing a conduit pipe, bushing, or cover device, which can be conducted both continuously and also discontinuously.
This aspect of the invention will be explained in greater detail hereafter.
In principle, the thermally insulated devices described here (cf. first aspect of the invention) can be produced similarly to the known methods. In this case, the known blowing agents (for example, cyclopentane, CO2) are partially or completely replaced by the HFOs described here. Accordingly, facilities known per se can be used for the production, possibly after adaptation to new parameters, as a person skilled in the art can carry out as a routine measure. The methods described in EP0897788 and EP2213440 and EP2248648 and WO2008/019791 and EP1355103 and EP2340929 are hereby incorporated by reference.
In one advantageous embodiment of the method, the thermal insulation (3) is formed by foaming a plastic composition, which contains polymer components for the foam formation and HFO as a blowing agent. According to the invention, the HFO can either be added to one of the components and then processed or the starting components and the HFO are combined simultaneously in a metering device (for example, the mixing head).
In a further advantageous embodiment of the method, the plastic composition comprises two liquid components, wherein the first component contains a polyol and HFO and the second component contains isocyanate. The isocyanate component is preferably one based on methylene diisocyanate. However, other isocyanates, for example, those based on toluene-2,4-diisocyanate or aliphatic isocyanates can also be used.
In a further advantageous embodiment of the method, the plastic composition comprises two liquid components, wherein the first component contains a polyol and the second component contains isocyanate and HFO. In particular, those HFO components are preferred which have a good miscibility with the two liquid components and the boiling point of which is not excessively low (in particular not below 10° C.). The apparatus expenditure in the production is thus low; cooling systems only have to be provided to a small extent.
In a further advantageous embodiment of the method, the plastic composition consists of a melted component and this melt is combined with HFO under pressure.
Variant 1: If the thermally insulated pipe of this invention comprises one or more flexible medium pipe(s) and the outer jacket (13) comprises a barrier made of plastic, a method variant is advantageous in which
In this method variant, furthermore in step a, the inner pipe
Variant 2: If the thermally insulated pipe of this invention comprises one or more rigid medium pipe(s) and the outer jacket (2) with barrier is made of plastic, a method variant is advantageous, in which
Variant 3: If the thermally insulated pipe of this invention contains a thermal insulation made of a thermoplastic foam, i.e., for example, made of PET, PE, or PP, a method variant is advantageous in which the HFO is pressed directly into the molten polymer matrix and subsequently results in the foaming of the thermoplastic used due to expansion. This can take place, for example, in that a polymer mixture is melted in the extruder and HFO under pressure is supplied into this melt. Upon leaving the mold, the provided blowing agent results in the foaming.
In a third aspect, the invention relates to novel uses of HFOs.
This aspect of the invention will be explained in greater detail hereafter.
In a first embodiment, the invention relates to the use of hydrofluoroolefins as a cell gas of the foam insulation in thermally insulated pipe systems, in particular in plastic medium pipe systems (PMP) and in plastic jacketed pipe systems (PJP).
HFOs can advantageously be used as the cell gas in foam insulations of conduit pipes, of cover devices, and of bushings, in particular of conduit pipes, of cover devices, and of bushings as described here (first aspect).
The invention will be explained in greater detail on the basis of the following examples; these are not to limit the invention in any manner.
Medium pipes having an external diameter of 63 mm and a wall thickness of 5.8 mm consisting of PExa were unwound continuously from a supply drum. Shortly before the foaming station, this medium pipe was enclosed by a PE film, which was in turn unwound from a supply and supplied via a forming shoulder. The corresponding quantity of a mixture made of a polymer isocyanate based on diphenyl methylene diisocyanate (MDI) having an NCO content of 31% and a polyol having an OH number of 410 mg KOH/g (determined according to ASTMD4274D) and having a water content of 0.8% was dispensed into the tube film, which was still open on the upper side. The isocyanate component was used slightly superstoichiometrically in relation to the reactive OH groups in this case. The two components were intensively mixed in a high-pressure mixing head at a pressure of 150 bar before the dispensing. The corresponding quantity of HFO/cyclopentane was in turn stirred into the polyol component beforehand. Immediately after the dispensing of the two-component mixture, the tube film was welded at the upper end. The PU foam arising immediately thereafter was forced by molding jaws into a cylindrical geometry and a jacket made of PE was extruded on continuously after the curing.
The obtained pipes were analyzed with respect to the cell gases contained in the foam. For this purpose, small samples of approximately 3 cm3 size were stamped out of the foam and they were mechanically destroyed in a closed system, such that the cell gases could enter the measuring apparatus. The gases present were qualitatively and quantitatively determined in a gas chromatograph.
Moreover, the value of the thermal conductivity was measured at 50° C. on 3 m long pipe pieces according to the norms DIN EN 253:2015-12 and EN ISO 8497:1996 (50 value). Furthermore, the composition of the cell gas was determined (according to the Chalmers method; described in Ramnas et al, J. Cellular Plastics, 31, 375-388, 1995); this method was also used in the following examples. The summary of the results is found in the following table, a graphic representation is apparent in
50value
The data clearly prove the positive influence of HFO on the thermal conductivity.
In each case a quantity of 380-420 g polyol was provided in a beaker and the quantity of blowing agent indicated in the table was stirred in. The viscosity of the solution was determined in a rotation viscometer of the type viscometer DV I-Prime from Brookfield. The average value of three measurements was recorded.
The results are summarized in the table and shown in a graph in
The data clearly prove the positive influence of HFO on the viscosity.
The average pore size of PU foams, which contained different cell gases, was determined according to DIN EN 253:2015-12. An average was formed from three measurements in each case.
The results are summarized in the table and are shown in a graph in
The data clearly prove the positive influence of HFO on the cell size.
According to the method of Pensky-Martens (DIN EN ISO 2719:2003-9), the flashpoints of specimens number 1 and number 3 were determined. Specimen number 2 was measured according to the method of Abel-Pensky (DIN 51755). The same polyol was used in each case as in Example 1. The results are summarized in the table.
The sample number 3 had a flashpoint which is significantly higher than the comparison sample number 2, which contained an equimolar content of cyclopentane. In particular, the sample number 3 is not to be classified as flammable according to the regulation EG 440/2008.
General: Thermally insulated conduit pipes having various cell gas compositions were produced according to Example 1.
A quantity of cyclopentane (Cp) was added to the polyol component with the aid of a static mixture, such that a content of 7 wt. % resulted in relation to the polyol quantity. On the surface of the pipe thus produced, 12 bubbles were counted on the length of 30 cm, which had a diameter larger than 10 mm and were recognized easily even without further aids.
A quantity of 2 wt. % cyclopentane and 11 wt. % HFO 1233zd was added to the polyol. No bubbles were found on the surface of the pipe thus produced on a produced length of 400 m.
A quantity of 15 wt. % HFO 1233zd was added to the polyol. No bubbles were found on the surface of the pipe thus produced on a produced length of 350 m.
Results of the examples 5.1-5.3: The composition of the cell gases thus obtained was determined by means of GC as in Example 1, the obtained pipe was visually checked.
The data prove that high quantities of Cp result in unusable insulated conduit pipes, while in contrast the partial or complete replacement thereof by HFO results in flawless insulated pipes.
While preferred embodiments of the invention are described in the present description, it is to be noted that the invention is not restricted thereto and can also be executed in another manner within the scope of the following claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 00937/16 | Jul 2016 | CH | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2017/067419 | 7/11/2017 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2018/015216 | 1/25/2018 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6398059 | Hayashi | Jun 2002 | B1 |
| 9862127 | Bronnum | Jan 2018 | B2 |
| 20110124756 | Singh et al. | May 2011 | A1 |
| 20110144216 | Hulse et al. | Jun 2011 | A1 |
| 20130149452 | Bogdan et al. | Jun 2013 | A1 |
| 20160200889 | Parenti | Jul 2016 | A1 |
| Number | Date | Country |
|---|---|---|
| 710 709 | Aug 2016 | CH |
| 0 897 788 | Feb 1999 | EP |
| 1 355 103 | Oct 2003 | EP |
| 2 213 440 | Aug 2010 | EP |
| 2 248 648 | Nov 2010 | EP |
| 2 340 929 | Jul 2011 | EP |
| 3112739 | Jan 2017 | EP |
| 3115389 | Nov 2017 | EP |
| 2953776 | Dec 2017 | EP |
| 2004003423 | Jan 2004 | WO |
| 2007058793 | May 2007 | WO |
| 2008019791 | Feb 2008 | WO |
| 2009043351 | Apr 2009 | WO |
| 2009085857 | Jul 2009 | WO |
| 2010019428 | Feb 2010 | WO |
| 10 2010 015 462 | Oct 2011 | WO |
| 2015042300 | Mar 2015 | WO |
| 2015110404 | Jul 2015 | WO |
| Entry |
|---|
| Australian Search Report dated Aug. 10, 2021. |
| International Search Report for International Application No. PCT/E2017/067419 dated Oct. 5, 2017. |
| “Guide to packaging and barrier materials,” 2002, pp. 1-56, Plastics Design Library. |
| “Specification for Eval Resin with English Abstract,” Dated Nov. 17, 2004. |
| Number | Date | Country | |
|---|---|---|---|
| 20190211962 A1 | Jul 2019 | US |