Thermally isolating optical devices

Abstract

A thermo-optic device may be formed with trenches that undercut the substrate beneath the thermo-optic device. Through the removal of the underlying substrate, the heat dissipation of the thermo-optic device may be reduced. This may reduce the thermal budget of the device, reducing the power requirements for operating the device in some embodiments.

Description

BACKGROUND

[0001] This invention relates generally to optical components including those used in optical communication networks.

[0002] In optical communication networks, a waveguide core may extend across a semiconductor substrate. The core may be covered by an upper cladding and may be positioned over a lower cladding. The core may define an optical signal path. The cladding may have a lower refractive index than the core.

[0003] In some cases the optical characteristics of the core may be thermally modified. For example, thermo-optic devices may be operated through the application of heat. The refractive index of an optical device may be changed by heating. Thermo-optic switches may be used in Mach-Zehnder interferometers and directional couplers, as two examples.

[0004] Generally, the more heat that is dissipated by the thermo-optic device, the more the power requirements of the overall component. It is desirable to reduce the heat transfer to only that needed to achieve the thermo-optic effect.

[0005] Thus, there is a need for ways to reduce the amount of heat loss in thermo-optic devices.

BRIEF DESCRIPTION OF THE DRAWINGS

[0006] FIG. 1 is an enlarged cross-sectional view of one embodiment of the present invention at an early stage of manufacture;

[0007] FIG. 2 is an enlarged cross-sectional view of one embodiment of the present invention at a subsequent stage of manufacture;

[0008] FIG. 3 is an enlarged cross-sectional view of one embodiment of the present invention at a subsequent stage of manufacture;

[0009] FIG. 4 is an enlarged cross-sectional view of one embodiment of the present invention at a subsequent stage of manufacture;

[0010] FIG. 5 is an enlarged cross-sectional view of one embodiment of the present invention at a subsequent stage of manufacture; and

[0011] FIG. 6 is an enlarged cross-sectional view of one embodiment of the present invention at a subsequent stage of manufacture.

DETAILED DESCRIPTION

[0012] Referring to FIG. 1, a waveguide core 12 may be defined on a lower cladding 11 over a semiconductor substrate 10. In one embodiment, the core 12 may be part of a planar lightwave circuit. The core 12 and lower cladding 11 may, in turn, be covered by an upper cladding 14 as shown in FIG. 2.

[0013] Referring to FIG. 3, an electric resistance heater 16 may be defined over the upper cladding 14 atop the core 12. The heater 16 may be a more resistive material coupled to a source of power by a less resistive material. The electrical resistance heater 16 is selectively operable to change the optical properties of the core 12 in the vicinity of the heater 16. For example, in one embodiment, a thermo-optic switch may be formed.

[0014] Referring to FIG. 4, a pair of trenches 18 may be formed on either side of the heater 16 and core 12. The trenches 18 may be spaced from the core 12 to leave protective upper cladding 14 around the core 12, in one embodiment. The trenches 18 may extend through the upper cladding 14 and the lower cladding 11 down to the semiconductor substrate 10 in one embodiment of the present invention. A thermo-optic device 26 is defined between the trenches 18, in one embodiment.

[0015] Using the thermo-optic device 26 as a mask, an isotropic etch may be implemented into the substrate 10 through the trenches 18 to form the undercut regions 20, in one embodiment of the present invention, shown in FIG. 5. The etchant is more selective of the substrate 10 material and is less selective of the cladding material 11 and 14. Because of the isotropic nature of the etching, the etching extends under the lower cladding 11 on opposed sides of each trench 18. By the term isotropic, it is intended to refer to an etchant that etches outwardly under a mask that defines an opening for the etchant to etch an underlying material.

[0016] The resulting regions 20 extend under the structure that includes the core 12 and the heater 16. One result of this under-etching is to reduce the amount of substrate 10 material underneath the core 12 and the heater 16.

[0017] Referring to FIG. 6, the trenches 18 may guide the anisotropic etching from the bottoms of the regions 20. The etchant is more selective of the substrate 10 than of the cladding 11 or 14. As a result, an anisotropically etched trench 22 extends below the regions 20 formed by isotropic etching. A substantial portion of the substrate 10 material underneath the core 12 and the heater 16 is removed, leaving a relatively thin pillar 24 of substrate 10.

[0018] The inventors of the present invention have determined that a substantial portion of the heat loss from heater 16 occurs through the semiconductor substrate 10. By reducing the amount of available substrate 10 underneath the heater 16, this heat loss may be reduced. The heat loss may increase the power needs of the device and dispersed heat may adversely affect the optical properties of surrounding components.

[0019] In some embodiments, the regions 20 and the trenches 22 may be filled with a thermally isolating material. Also, in some embodiments, the trenches 18 may also be filled or covered with a thermally isolating material.

[0020] While the present invention has been described with respect to a limited number of embodiments, those skilled in the art will appreciate numerous modifications and variations therefrom. It is intended that the appended claims cover all such modifications and variations as fall within the true spirit and scope of this present invention.

Claims

1. A method comprising: forming a thermo-optic device on a semiconductor substrate; and isotropically removing a first portion of the semiconductor substrate underneath the thermo-optic device and anisotropically removing a second portion of the semiconductor substrate under said first portion.

2-4. (Canceled).

5. The method of claim 1 including forming a waveguide core on the semiconductor substrate and covering said core with an upper cladding.

6. The method of claim 5 including forming an opening through said upper cladding on either side of said core.

7. The method of claim 6 including leaving a portion of said upper cladding surrounding said core.

8. The method of claim 6 including forming a resistance heater over said upper cladding over said core.

9. The method of claim 1 including removing a portion of the semiconductor substrate on two opposed sides of said thermo-optic device.

10-15. (Canceled).

16. An optical circuit comprising: a thermo-optic device including a waveguide core formed over a semiconductor substrate, said core covered by a cladding; and an opening in said semiconductor substrate extending under said thermo-optic device, said opening having a first laterally extending region communicating with a second deeper, vertically extending region, said vertically extending region having a lateral extent less than the lateral extent of said horizontally extending region.

17. The circuit of claim 16 including a pair of openings extending under said thermo-optic device device.

18-19. (Canceled).

20. The circuit of claim 16 wherein said thermo-optic device includes a heater formed over said cladding.