Thermally stable polycarbonates, thermoplastic compositions thereof, and articles formed therefrom

Abstract

A polycarbonate such as aliphatic/aromatic polycarbonate comprises repeating structural carbonate units of the formula (H-1): in which Rh is a radical having the formula (H-2): wherein each of R11, R12, R13, R14, R15, R16, R17, R18, R19, R20, R21, R22, R23, R24, R25, R26, R27, and R28 is independently a hydrogen, a C1-C6 alkyl group, or a halogen substituted C1-C6 alkyl group. The polycarbonate, and a thermoplastic composition thereof, have improved thermal stability, cost-effectiveness, and exhibit improved manufacturability such as, for example, minimum cyclic carbonate formation and minimum amine acceptor requirement.

Description

BACKGROUND

This disclosure relates to thermally stable polycarbonates, thermoplastic compositions thereof, and articles and uses thereof.

Aliphatic/aromatic polycarbonates typically have less satisfactory thermal stability due to pyrolytic elimination reactions involving β-hydrogens. EP0922722 A1 has reported that polyesters and polycarbonates with significantly improved thermal stability may be prepared from neoalcohols having no β-hydrogens, such as 2,2,4,4-tetramethylcyclobutane-1,3-diol (TMCBD). However, the high cost of TMCBD makes it impractical for many applications. Although neopentyl glycol (NPG) is a lower cost neodiol than TMCBD, and the bischloroformate of NPG has been prepared and converted into the corresponding BPA copolycarbonates, NPG tends to form cyclic carbonates which are generally undesirable. Moreover, NPG has a lower molecular weight, and requires a large amount of amine acceptor to allow incorporation into polycarbonates and copolycarbonates at effective levels.

There accordingly remains a need in the art for a polycarbonate, and a thermoplastic composition thereof, which is thermally stable, cost-effective, and has improved manufacturability characteristics, such as minimum cyclic carbonate formation and minimum amine acceptor requirement, among others.

SUMMARY

In one aspect, the present disclosure provides a polycarbonate comprising repeating structural carbonate units of the formula (H-1): in which R^h is a radical having the formula (H-2): wherein each of R₁₁, R₁₂, R₁₃, R₁₄, R₁₅, R₁₆, R₁₇, R₁₈, R₁₉, R₂₀, R₂₁, R₂₂, R₂₃, R₂₄, R₂₅, R₂₆, R₂₇, and R₂₈ is independently a hydrogen, a C₁-C₆ alkyl group, or a halogen substituted C₁-C₆ alkyl group. For example, H-1 may be in the form of a formula (H-3) carbonate unit:

In another aspect, the present disclosure provides a thermoplastic composition that includes a polycarbonate comprising, in addition to repeating structural carbonate units of the formula (H-1), repeating structural carbonate units of the formula (A-1): wherein each of A¹ and A² is a monocyclic divalent aryl radical and Y¹ is a bridging radical having one or two atoms that separate A¹ from A²; for example, repeating structural carbonate units of the formula (A-3) or (A-4):

In another aspect, the present disclosure provides a thermoplastic composition including a polycarbonate comprising repeating structural carbonate units of the above formula (H-1).

In yet another aspect, the present disclosure provides a thermally stable article formed from the thermoplastic composition.

The above described and other non-limiting features are exemplified by the following detailed description.

DETAILED DESCRIPTION

The present disclosure relates to a polycarbonate comprising repeating structural carbonate units of the formula (H-1), such as the formula (H-3), and a thermoplastic composition thereof, which have improved thermal stability, cost-effectiveness, and improved manufacturability such as exhibiting minimum cyclic carbonate formation and minimum amine acceptor requirement characteristics, among others.

As used herein, the term “polycarbonate” refers to a polymer comprising the same or different carbonate units, or a copolymer that comprises the same or different carbonate units, as well as one or more units other than carbonate (i.e. copolycarbonate); the term “aliphatic” refers to a hydrocarbon radical having a valence of at least one comprising a linear or branched array of carbon atoms which is not cyclic; “aromatic” refers to a radical having a valence of at least one comprising at least one aromatic group; “cycloaliphatic” refers to a radical having a valence of at least one comprising an array of carbon atoms which is cyclic but not aromatic; “alkyl” refers to a straight or branched chain monovalent hydrocarbon radical; “alkylene” refers to a straight or branched chain divalent hydrocarbon radical; “alkylidene” refers to a straight or branched chain divalent hydrocarbon radical, with both valences on a single common carbon atom; “alkenyl” refers to a straight or branched chain monovalent hydrocarbon radical having at least two carbons joined by a carbon-carbon double bond; “cycloalkyl” refers to a non-aromatic alicyclic monovalent hydrocarbon radical having at least three carbon atoms, with at least one degree of unsaturation; “cycloalkylene” refers to a non-aromatic alicyclic divalent hydrocarbon radical having at least three carbon atoms, with at least one degree of unsaturation; “aryl” refers to a monovalent aromatic benzene ring radical, or to an optionally substituted benzene ring system radical system fused to at least one optionally substituted benzene rings; “aromatic radical” refers to a radical having a valence of at least one comprising at least one aromatic group; Examples of aromatic radicals include phenyl, pyridyl, furanyl, thienyl, naphthyl, and the like; “arylene” refers to a benzene ring diradical or to a benzene ring system diradical fused to at least one optionally substituted benzene rings; “acyl” refers to a monovalent hydrocarbon radical joined to a carbonyl carbon atom, wherein the carbonyl carbon further connects to an adjoining group; “alkylaryl” refers to an alkyl group as defined above substituted onto an aryl as defined above; “arylalkyl” refers to an aryl group as defined above substituted onto an alkyl as defined above; “alkoxy” refers to an alkyl group as defined above connected through an oxygen radical to an adjoining group; “aryloxy” refers to an aryl group as defined above connected through an oxygen radical to an adjoining group; the modifier “about” used in connection with a quantity is inclusive of the stated value and has the meaning dictated by the context (e.g., includes the degree of error associated with measurement of the particular quantity); “optional” or “optionally” means that the subsequently described event or circumstance may or may not occur, and that the description includes instances where the event occurs and instances where it does not; and “direct bond”, where part of a structural variable specification, refers to the direct joining of the substituents preceding and succeeding the variable taken as a “direct bond”.

Compounds are described herein using standard nomenclature. A dash (“-”) that is not between two letters or symbols is used to indicate a point of attachment for a substituent. For example, —CHO is attached through the carbon of the carbonyl (C═O) group. The singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise. The endpoints of all ranges reciting the same characteristic or component are independently combinable and inclusive of the recited endpoint. All references are incorporated herein by reference. The terms “first,” “second,” and the like herein do not denote any order, quantity, or importance, but rather are used to distinguish one element from another.

In one embodiment, the disclosure provides a polycarbonate comprising repeating carbonate units with no β-hydrogen. In another embodiment, the development provides a thermoplastic composition comprising such polycarbonate. Non-limiting β-hydrogen examples include hydrogens that are bonded to carbon atoms which are adjacent to a carbon atom with a hydroxyl group, a chloroformate group, or a carbonate group, as illustrated below:

The polycarbonate comprises repeating structural carbonate units of the formula (H-1): in which R^h is a radical having the formula (H-2): wherein each of R₁₁, R₁₂, R₁₃, R₁₄, R₁₅, R₁₆, R₁₇, R₁₈, R₁₉, R₂₀, R₂₁, R₂₂, R₂₃, R₂₄, R₂₅, R₂₆, R₂₇, and R₂₈ is independently a hydrogen, a C₁-C₆ alkyl group, or a halogen substituted C₁-C₆ alkyl group.

In an embodiment, each of R₁₁, R₁₂, R₁₃, R₁₄, R₁₅, R₁₆, R₁₇, R₁₈, R₁₉, R₂₀, R₂₁, R₂₂, R₂₃, R₂₄, R₂₅, R₂₆, R₂₇, and R₂₈ in formula (H-2) is hydrogen, giving a polycarbonate that comprises repeating structural carbonate units of the formula (H-3):

In addition to formula (H-1) units such as formula (H-3) units, the polycarbonate can further comprise repeating structural carbonate units of the formula (1): in which R¹ group may be selected from any aromatic radicals, alicyclic radicals, and aliphatic radicals other than the radical of formula (H-2). In an embodiment, at least 60 percent of the total number of R^h and R¹ groups is aromatic organic radicals.

In another embodiment, R¹ is an aromatic organic radical, for example a radical of the formula (2):-A¹-Y¹-A²-  (2) wherein each of A¹ and A² is a monocyclic divalent aryl radical and Y¹ is a bridging radical having one or two atoms that separate A¹ from A². In an exemplary embodiment, one atom separates A¹ from A². Illustrative non-limiting examples of radicals of this type are —O—, —S—, —S(O)—, —S(O₂)—, —C(O)—, methylene, cyclohexyl-methylene, 2-[2.2.1]-bicycloheptylidene, ethylidene, isopropylidene, neopentylidene, cyclohexylidene, cyclopentadecylidene, cyclododecylidene, and adamantylidene. The bridging radical Y¹ may be a hydrocarbon group or a saturated hydrocarbon group such as methylene, cyclohexylidene, or isopropylidene.

In a further embodiment, the disclosure provides aliphatic/aromatic polycarbonates based on hydroxypivalyl hydroxypivalate.

In still another embodiment, the polycarbonate can further comprise, in addition to formula (H-1) units such as formula (H-3) units, repeating structural carbonate units of the formula (A-1): wherein Y¹, A¹ and A² are as described above.

Polycarbonates may be produced via the interfacial reaction of dihydroxy compounds having the formula HO—R^h—OH wherein R^h is as described above, which includes: wherein R₁₁, R₁₂, R₁₃, R₁₄, R₁₅, R₁₆, R₁₇, R₁₈, R₁₉, R₂₀, R₂₁, R₂₂, R₂₃, R₂₄, R₂₅, R₂₆, R₂₇, and R₂₈ are as described above.

In one embodiment, polycarbonates may be produced via the interfacial reaction of hydroxypivalyl hydroxypivalate (HPHP), which is a dihydroxy compound having the formula (H-5):

In another embodiment, polycarbonates may be produced via the interfacial reaction of dihydroxy compounds having the formula HO—R^h—OH wherein R^h is as described above, together with dihydroxy compounds having the formula HO—R¹—OH, which includes dihydroxy compounds of formula (3):HO-A¹-Y¹-A²-OH  (3) wherein Y¹, A¹ and A² are as described above.

In still another embodiment, polycarbonates may be produced via the interfacial reaction of dihydroxy compounds having the formula HO—R^h—OH wherein R^h is as described above, together with bisphenol compounds of general formula (4): wherein R^a and R^b each represent a halogen atom or a monovalent hydrocarbon group and may be the same or different; p and q are each independently integers of 0 to 4; and X^a represents one of the groups of formula (5): wherein R^c and R^d each independently represent a hydrogen atom or a monovalent linear or cyclic hydrocarbon group and R^e is a divalent hydrocarbon group.

In yet another embodiment, polycarbonates may be produced via the interfacial reaction of dihydroxy compounds having the formula HO—R^h—OH wherein R^h is as described above, together with one or more bisphenol compounds of general formula (B-1):HOG¹_tE_sG¹_uOH  (B-1) wherein each G¹ is independently at each occurrence a C₆-C₂₀ aromatic radical; E is independently at each occurrence a bond, a C₃-C₂₀ cycloaliphatic radical, a C₃-C₂₀ aromatic radical, a C₁-C₂₀ aliphatic radical, a sulfur-containing linkage, a selenium-containing linkage, a phosphorus-containing linkage, or an oxygen atom; “t” is a number greater than or equal to one; “s” is either zero or one; and “u” is a whole number including zero.

Some illustrative, non-limiting examples of suitable dihydroxy compounds include the following: resorcinol; C₁₃ alkyl-substituted resorcinols; 4-bromoresorcinol, hydroquinone, 4,4′-dihydroxybiphenyl, 1,6-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, 1,l-bis(4-hydroxyphenyl)cyclopentane; 2,2-bis(3-allyl-4-hydroxyphenyl)propane; 2,2-bis(2-t-butyl-4-hydroxy-5-methylphenyl)propane; 2,2-bis(3-t-butyl-4-hydroxy-6-methylphenyl)propane; 2,2-bis(3-t-butyl-4-hydroxy-6-methylphenyl)butane; 1,3-bis[4-hydroxyphenyl-1-(1-methylethylidine)]benzene; 1,4-bis[4-hydroxyphenyl-l-(1-methylethylidine)]benzene; 1,3-bis[3-t-butyl4-hydroxy-6-methylphenyl-1-(1-methylethylidine)]benzene; 1,4-bis[3-t-butyl-4-hydroxy-6-methylphenyl-l-(1-methylethylidine)]benzene; 4,4′-biphenol; 2,2′,6,8-tetramethyl-3,3′,5,5′-tetrabromo-4,4′-biphenol; 2,2′,6,6′-tetramethyl-3,3′,5-tribromo-4,4′-biphenol; 1,l -bis(4-hydroxyphenyl)-2,2,2-trichloroethane; 1,1-bis(4-hydroxyphenyl)-1-cyanoethane; 1,l-bis(4-hydroxyphenyl)dicyanomethane; l,l-bis(4-hydroxyphenyl)-1-cyano-1-phenylmethane; 2,2-bis(3-methyl-4-hydroxyphenyl)propane; 1,1-bis(4-hydroxyphenyl)norbornane; 3,3-bis(4-hydroxyphenyl)phthalide; 1,2-bis(4-hydroxyphenyl)ethane; 1,3-bis(4-hydroxyphenyl)propenone; bis(4-hydroxyphenyl) sulfide; 4,4′-oxydiphenol; 4,4-bis(4-hydroxyphenyl)pentanoic acid; 4,4-bis(3,5-dimethyl-4-hydroxyphenyl)pentanoic acid; 2,2-bis(4-hydroxyphenyl) acetic acid; 2,4′-dihydroxydiphenylmethane; 2-bis(2-hydroxyphenyl)methane; bis(4-hydroxyphenyl)methane; bis(4-hydroxy-5-nitrophenyl)methane; bis(4-hydroxy-2,6-dimethyl-3-methoxyphenyl)methane; 1,1-bis(4-hydroxyphenyl)ethane; 1,1-bis(4-hydroxy-2-chlorophenyl)ethane; 2,2-bis(4-hydroxyphenyl)propane (bisphenol-A); 1,1-bis(4-hydroxyphenyl)propane; 2,2-bis(3-chloro-4-hydroxyphenyl)propane; 2,2-bis(3-bromo-4-hydroxyphenyl)propane; 2,2-bis(4-hydroxy-3-methylphenyl)propane; 2,2-bis(4-hydroxy-3-isopropylphenyl)propane; 2,2-bis(3-t-butyl-4-hydroxyphenyl)propane; 2,2-bis(3-phenyl-4-hydroxyphenyl)propane; 2,2-bis(3,5-dichloro-4-hydroxyphenyl)propane; 2,2-bis(3,5-dibromo-4-hydroxyphenyl)propane; 2,2-bis(3,5-dimethyl-4-hydroxyphenyl)propane; 2,2-bis(3-chloro-4-hydroxy-5-methylphenyl)propane; 2,2-bis(3-bromo-4-hydroxy-5-methylphenyl)propane; 2,2-bis(3-chloro-4-hydroxy-5-isopropylphenyl)propane; 2,2-bis(3-bromo-4-hydroxy-5-isopropylphenyl)propane; 2,2-bis(3-t-butyl-5-chloro-4-hydroxyphenyl)propane; 2,2-bis(3-bromo-5-t-butyl-4-hydroxyphenyl)propane; 2,2-bis(3-chloro-5-phenyl-4-hydroxyphenyl)propane; 2,2-bis(3-bromo-5-phenyl-4-hydroxyphenyl)propane; 2,2-bis(3,5-disopropyl-4-hydroxyphenyl)propane; 2,2-bis(3,5-di-t-butyl-4-hydroxyphenyl)propane; 2,2-bis(3,5-diphenyl-4-hydroxyphenyl)propane; 2,2-bis(4-hydroxy-2,3,5,6-tetrachlorophenyl)propane; 2,2-bis(4-hydroxy-2,3,5,6-tetrabromophenyl)propane; 2,2-bis(4-hydroxy-2,3,5,6-tetramethylphenyl)propane; 2,2-bis(2,6-dichloro-3,5-dimethyl-4-hydroxyphenyl)propane; 2,2-bis(2,6-dibromo-3,5-dimethyl-4-hydroxyphenyl)propane; 2,2-bis(4-hydroxy-3-ethylphenyl)propane; 2,2-bis(4-hydroxy-3,5-dimethylphenyl)propane; 2,2-bis(3,5,3′,5′-tetrachloro-4,4′-dihydroxyphenyl)propane; 1,1-bis(4-hydroxyphenyl)cyclohexylmethane; 2,2-bis(4-hydroxyphenyl)-1-phenylpropane; 1,1-bis(4-hydroxyphenyl)cyclohexane; 1,1-bis(3-chloro-4-hydroxyphenyl)cyclohexane; 1,1-bis(3-bromo-4-hydroxyphenyl)cyclohexane; 1,1-bis(4-hydroxy-3-methylphenyl)cyclohexane; 1,1-bis(4-hydroxy-3-isopropylphenyl)cyclohexane; 1,1-bis(3-t-butyl-4-hydroxyphenyl)cyclohexane; 1,1-bis(3-phenyl-4-hydroxyphenyl)cyclohexane; 1,1-bis(3,5-dichloro-4-hydroxyphenyl)cyclohexane; 1,1-bis(3,5-dibromo-4-hydroxyphenyl)cyclohexane; 1,1-bis(3,5-dimethyl-4-hydroxyphenyl)cyclohexane; 4,4′-[1-methyl-4-(1-methyl-ethyl)-1,3-cyclohexandiyl]bisphenol (1,3 BHPM); 4-[1-[3-(4-hydroxyphenyl)-4-methylcyclohexyl]-1-methyl-ethyl]-phenol (2,8 BHPM); 3,8-dihydroxy-5a,10b-diphenylcoumarano-2′,3′,2,3-coumarane (DCBP); 2-phenyl-3,3-bis(4-hydroxyphenyl)phthalimidine; 1,1-bis(3-chloro-4-hydroxy-5-methylphenyl)cyclohexane; 1,1-bis(3-bromo-4-hydroxy-5-methylphenyl)cyclohexane; 1,1-bis(3-chloro-4-hydroxy-5-isopropylphenyl)cyclohexane; 1,1-bis(3-bromo-4-hydroxy-5-isopropylphenyl)cyclohexane; 1,1-bis(3-t-butyl-5-chloro-4-hydroxyphenyl)cyclohexane; 1,1-bis(3-bromo-5-t-butyl-4-hydroxyphenyl)cyclohexane; 1,1-bis(3-chloro-5-phenyl-4-hydroxyphenyl)cyclohexane; 1,1-bis(3-bromo-5-phenyl-4-hydroxyphenyl)cyclohexane; 1,1-bis(3,5-disopropyl-4-hydroxyphenyl)cyclohexane; 1,1-bis(3,5-di-t-butyl-4-hydroxyphenyl)cyclohexane; 1,1-bis(3,5-diphenyl-4-hydroxyphenyl)cyclohexane; 1,1-bis(4-hydroxy-2,3,5,6-tetrachlorophenyl)cyclohexane; 1,1-bis(4-hydroxy-2,3,5,6-tetrabromophenyl)cyclohexane; 1,1-bis(4-hydroxy-2,3,5,6-tetramethylphenyl)cyclohexane; 1,1-bis(2,6-dichloro-3,5-dimethyl-4-hydroxyphenyl)cyclohexane; 1,1-bis(2,6-dibromo-3,5-dimethyl-4-hydroxyphenyl)cyclohexane; 1,1-bis(4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3-chloro-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3-bromo-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(4-hydroxy-3-methylphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(4-hydroxy-3-isopropylphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3-t-butyl-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3-phenyl-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3,5-dichloro-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3,5-dibromo-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3,5-dimethyl-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3-chloro-4-hydroxy-5-methylphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3-bromo-4-hydroxy-5-methylphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3-chloro-4-hydroxy-5-isopropylphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3-bromo-4-hydroxy-5-isopropylphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3-t-butyl-5-chloro-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3-bromo-5-t-butyl-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; bis(3-chloro-5-phenyl-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3-bromo-5-phenyl-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3,5-disopropyl-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3,5-di-t-butyl-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(3,5-diphenyl-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(4-hydroxy-2,3,5,6-tetrachlorophenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(4-hydroxy-2,3,5,6-tetrabromophenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(4-hydroxy-2,3,5,6-tetramethylphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(2,6-dichloro-3,5-dimethyl-4-hydroxyphenyl)-3,3,5-trimethylcyclohexane; 1,1-bis(2,6-dibromo-3,5-dimethyl-4-hydroxyphenyl)-3,3,5-trimethylcyciohexane; 4,4-bis(4-hydroxyphenyl)heptane; 1,1-bis(4-hydroxyphenyl)decane; 1,1-bis(4-hydroxyphenyl)cyclododecane; 1,1-bis(3,5-dimethyl-4-hydroxyphenyl)cyclododecane; 4,4′dihydroxy-1,1-biphenyl; 4,4′-dihydroxy-3,3′-dimethyl-1,1-biphenyl; 4,4′-dihydroxy-3,3′-dioctyl-1,1-biphenyl; 4,4′-(3,3,5-trimethylcyclohexylidene)diphenol; 4,4′-bis(3,5-dimethyl)diphenol; 4,4′-dihydroxydiphenylether; 4,4′-dihydroxydiphenylthioether; 1,3-bis(2-(4-hydroxyphenyl)-2-propyl)benzene; 1,3-bis(2-(4-hydroxy-3-methylphenyl)-2-propyl)benzene; 1,4-bis(2-(4-hydroxyphenyl)-2-propyl)benzene; 1,4-bis(2-(4-hydroxy-3-methylphenyl)-2-propyl)benzene; 2,4′-dihydroxyphenyl sulfone; 4,4′-dihydroxydiphenylsulfone (BPS); bis(4-hydroxyphenyl)methane; 2,6-dihydroxy naphthalene; hydroquinone; 3-(4-hydroxyphenyl)-1,1,3-trimethylindan-5-ol; 1-(4-hydroxyphenyl)-1,3,3-trimethylindan-5-ol; 4,4-dihydroxydiphenyl ether; 4,4-dihydroxy-3,3-dichlorodiphenylether; 4,4-dihydroxy-2,5-dihydroxydiphenyl ether; 4,4-thiodiphenol; 2,2,2′,2′-tetrahydro-3,3,3′,3′-tetramethyl-1,1′-spirobi[1H-indene]-6,6′-diol; bis(4-hydroxyphenyl)acetonitrile; bis(4-hydroxyphenyl)sulfoxide; bis(4-hydroxyphenyl)sulfone; 9,9-bis(4-hydroxyphenyl)fluorine; 2,7-dihydroxypyrene; 6,6′-dihydroxy-3,3,3′,3′-tetramethylspiro(bis)indane (“spirobiindane bisphenol”); 3,3-bis(4-hydroxyphenyl)phthalide; 2,6-dihydroxydibenzo-p-dioxin; 2,6-dihydroxythianthrene; 2,7-dihydroxyphenoxathin; 2,7-dihydroxy-9,10-dimethylphenazine; 3,6-dihydroxydibenzofuran; 3,6-dihydroxydibenzothiophene; 2,7-dihydroxycarbazole, and the like, as well as combinations comprising at least one of the foregoing dihydroxy compounds.

Specific examples of the types of bisphenol compounds represented by formula (4) include 1,1-bis(4-hydroxyphenyl) methane, 1,1-bis(4-hydroxyphenyl) ethane, 2,2-bis(4-hydroxyphenyl) propane (hereinafter “bisphenol A” or “BPA” ), 2,2-bis(4-hydroxyphenyl) butane, 2,2-bis(4-hydroxyphenyl) octane, 1,1-bis(4-hydroxyphenyl) propane, 1,1-bis(4-hydroxyphenyl) n-butane, 2,2-bis(4-hydroxy-1-methylphenyl) propane, 1,1-bis(4-hydroxy-t-butylphenyl) propane, 3,3-bis(4-hydroxyphenyl)phthalimidine, 2-phenyl-3,3-bis(4-hydroxyphenyl)phthalimidine (PPPBP), 1,1-bis(4-hydroxyphenyl)-3,3,5-trimethylcyclohexane (BPI), and 1,1-bis(4-hydroxy-3-methylphenyl)cyclohexane (DMBPC). Combinations comprising at least one of the foregoing dihydroxy compounds may also be used.

In one embodiment, the polycarbonate can further comprise repeating structural carbonate units of the formula (A-2), in addition to formula (H-1) units such as formula (H-3) units: where p, q, R^a, R^b and X^a are as described above.

In a further embodiment, the polycarbonate can further comprise repeating structural carbonate units of the formula (A-3), in addition to formula (H-1) units such as formula (H-3) units:

In another embodiment, the polycarbonate can further comprise repeating structural carbonate units of the formula (A-4), in addition to formula (H-1) units such as formula (H-3) units:

In a still further embodiment, the polycarbonate of the disclosure comprises from about 0.1 wt % to about 40 wt % of formula (H-1) repeating units such as formula (H-3) repeating units, and fronm about 60 wt % to about 99.9 wt % of formula (A-1) repeating units such as formula (A-3) and/or (A-4) repeating units.

In yet another embodiment, the polycarbonate of the disclosure comprises from about 2 wt % to about 20 wt % of formula (H-1) repeating units such as formula (H-3) repeating units, and from about 80 wt % to about 98 wt % of formula (A-1) repeating units such as formula (A-3) and/or (A4) repeating units.

In one embodiment, the polycarbonate of the disclosure comprises from about 3 wt % to about 10 wt % of formula (H-1) repeating units such as formula (H-3) repeating units, and from about 90 wt % to about 97 wt % of formula (A-1) repeating units such as formula (A-3) and/or (A-4) repeating units.

Branched polycarbonates are also useful, as well as blend of a linear polycarbonate and a branched polycarbonate. The branched polycarbonates may be prepared by adding a branching agent during polymerization. These branching agents include polyfunctional organic compounds containing at least three functional groups selected from hydroxyl, carboxyl, carboxylic anhydride, haloformyl, and mixtures of the foregoing functional groups. Specific examples include trimellitic acid, trimellitic anhydride, trimellitic trichloride, tris-p-hydroxy phenyl ethane, isatin-bis-phenol, tris-phenol TC (1,3,5-tris((p-hydroxyphenyl)isopropyl)benzene), tris-phenol PA (4(4(1,1-bis(p-hydroxyphenyl)ethyl) alpha, alpha-dimethyl benzyl)phenol), 4-chloroformyl phthalic anhydride, trimesic acid, and benzophenone tetracarboxylic acid. The branching agents may be added at a level of 0.05 to 2.0 wt % of the polycarbonate. All types of polycarbonate end groups are contemplated as being useful in the polycarbonate, provided that such end groups do not significantly affect desired properties of the polycarbonate product.

The polycarbonates may have a weight average molecular weight (Mw) of from about 15,000 to about 100,000, specifically from about 16,000 to about 60,000, and most specifically from about 17,000 to about 40,000, as measured by gel permeation chromatography (GPC) using a crosslinked styrene-divinyl benzene column, at a sample concentration of 1 milligram per milliliter, and as calibrated with polycarbonate standards.

The polycarbonate may have a light transmittance greater than or equal to 55%, specifically greater than or equal to 60% and more specifically greater than or equal to 70%, as measured at 3.18 millimeters thickness according to ASTM D1003-00. The polycarbonate may also have a haze less than or equal to 30%, specifically less than or equal to 20%, and most specifically less than or equal to 10%, as measured at 3.18 millimeters thickness according to ASTM D1003-00.

In an embodiment, the polycarbonate has flow properties suitable for the manufacture of thin articles. Melt volume flow rate (often abbreviated MVR) measures the rate of extrusion of a thermoplastic through an orifice at a prescribed temperature and load. Polycarbonates suitable for the formation of thin articles may have an MVR, measured at 250° C./1.2 kg according to ASTM D1238-04, of 0.1 to 100 cubic centimeters per 10 minutes (cc/10 min). In a specific embodiment, a suitable polycarbonate composition has an MVR measured at 250° C./1.2 kg according to ASTM D1238-04, of 0.1-100 cc/10 min, specifically 0.5 to 50 cc/10 min, and more specifically 1 to 35 cc/10 min. Mixtures of polycarbonates of different flow properties may be used to achieve the overall desired flow property.

Polycarbonates of the disclosure may include copolymers comprising carbonate chain units and other units. A specific suitable copolymer is a polyester-polycarbonate, also known as a copolyester-polycarbonate and polyester-carbonate. Combinations of polycarbonates and polyester-polycarbonates may also be used. As used herein, a “combination” is inclusive of all mixtures, blends, alloys, reaction products, and the like. In one embodiment, polyester-polycarbonates contain, in addition to recurring carbonate chain units of the formula (H-1) and the formula (1), repeating units of formula (6): wherein D is a divalent radical derived from a dihydroxy compound, and may be, for example, a C_2-10 alkylene radical, a C_6-20 alicyclic radical, a C_6-20 aromatic radical or a polyoxyalkylene radical in which the alkylene groups contain 2 to 6 carbon atoms, specifically 2, 3, or 4 carbon atoms; and T is a divalent radical derived from a dicarboxylic acid, and may be, for example, a C_2-10 alkylene radical, a C_6-20 alicyclic radical, a C_6-20 alkyl aromatic radical, or a C_6-20 aromatic radical.

In one embodiment, D is a C_2-6 alkylene radical. In another embodiment, D is derived from an aromatic dihydroxy compound of formula (7): wherein each R^f is independently a halogen atom, a C_1-10 hydrocarbon group, or a C_1-10 halogen substituted hydrocarbon group, and n is 0 to 4. The halogen is usually bromine. Examples of compounds that may be represented by the formula (7) include resorcinol, substituted resorcinol compounds such as 5-methyl resorcinol, 5-ethyl resorcinol, 5-propyl resorcinol, 5-butyl resorcinol, 5-t-butyl resorcinol, 5-phenyl resorcinol, 5-cumyl resorcinol, 2,4,5,6-tetrafluoro resorcinol, 2,4,5,6-tetrabromo resorcinol, or the like; catechol; hydroquinone; substituted hydroquinones such as 2-methyl hydroquinone, 2-ethyl hydroquinone, 2-propyl hydroquinone, 2-butyl hydroquinone, 2-t-butyl hydroquinone, 2-phenyl hydroquinone, 2-cumyl hydroquinone, 2,3,5,6-tetramethyl hydroquinone, 2,3,5,6-tetra-t-butyl hydroquinone, 2,3,5,6-tetrafluoro hydroquinone, 2,3,5,6-tetrabromo hydroquinone, or the like; or combinations comprising at least one of the foregoing compounds.

Examples of aromatic dicarboxylic acids that may be used to prepare the polyesters include isophthalic or terephthalic acid, 1,2-di(p-carboxyphenyl)ethane, 4,4′-dicarboxydiphenyl ether, 4,4′-bisbenzoic acid, and mixtures comprising at least one of the foregoing acids. Acids containing fused rings can also be present, such as in 1,4-, 1,5-, or 2,6-naphthalenedicarboxylic acids. Specific dicarboxylic acids are terephthalic acid, isophthalic acid, naphthalene dicarboxylic acid, cyclohexane dicarboxylic acid, or mixtures thereof. A specific dicarboxylic acid comprises a mixture of isophthalic acid and terephthalic acid wherein the weight ratio of terephthalic acid to isophthalic acid is 91:1 to 2:98. In another specific embodiment, D is a C_2-6 alkylene radical and T is p-phenylene, m-phenylene, naphthalene, a divalent cycloaliphatic radical, or a mixture thereof. This class of polyester includes the poly(alkylene terephthalates).

In another embodiment, carbonate units of formula (1) may also be derived from aromatic dihydroxy compounds of formula (7), wherein specific carbonate units are resorcinol carbonate units.

Specifically, the polyester unit of a polyester-polycarbonate can be derived from the reaction of a combination of isophthalic and terephthalic diacids (or derivatives thereof) with resorcinol, bisphenol A, or a combination comprising one or more of these, wherein the molar ratio of isophthalate units to terephthalate units is 91:9 to 2:98, specifically 85:15 to 3:97, more specifically 80:20 to 5:95, and still more specifically 70:30 to 10:90. In case the polycarbonate comprises units derived from resorcinol and/or bisphenol A, the molar ratio of resorcinol carbonate units to bisphenol A carbonate units of 0:100 to 99:1, and the molar ratio of the mixed isophthalate-terephthalate polyester units to the polycarbonate units in the polyester-polycarbonate can be 1:99 to 99:1, specifically 5:95 to 90:10, more specifically 10:90 to 80:20. Where a blend of polyester-polycarbonate with polycarbonate is used, the ratio of polycarbonate to polyester-polycarbonate in the blend can be, respectively, 1:99 to 99:1, and specifically 10:90 to 90:10.

The polyester-polycarbonates may have a weight-averaged molecular weight (Mw) of 1,500 to 100,000, specifically 1,700 to 50,000, and more specifically 2,000 to 40,000. Molecular weight determinations are performed using gel permeation chromatography (GPC), using a crosslinked styrene-divinylbenzene column and calibrated to polycarbonate references. Samples are prepared at a concentration of about 1 mg/ml, and are eluted at a flow rate of about 1.0 ml/min.

Suitable polycarbonates can be manufactured by processes such as interfacial polymerization and melt polymerization. Although the reaction conditions for interfacial polymerization may vary, an exemplary process generally involves dissolving or dispersing a dihydric phenol reactant in aqueous caustic soda or potash, adding the resulting mixture to a suitable water-immiscible solvent medium, and contacting the reactants with a carbonate precursor in the presence of a suitable catalyst such as triethylamine or a phase transfer catalyst, under controlled pH conditions, e.g., 8 to 11. The most commonly used water immiscible solvents include methylene chloride, 1,2-dichloroethane, chlorobenzene, toluene, and the like. Suitable carbonate precursors include, for example, a carbonyl halide such as carbonyl bromide or carbonyl chloride, or a haloformate such as a bishaloformates of a dihydric phenol (e.g., the bischloroformates of bisphenol A, hydroquinone, or the like) or a glycol (e.g., the bishaloformate of ethylene glycol, neopentyl glycol, polyethylene glycol, or the like). Combinations comprising at least one of the foregoing types of carbonate precursors may also be used.

In a further embodiment, bischloroformate (BCF) of HPHP of the formula (H-6) as shown below is used in the preparation of the polycarbonates. HPHP may be converted into its bischloroformate in high yield and low cost through use of a tube reactor. Without purification or isolation, the resulting HPHP BCF may be fed directly into a standard interfacial polymerization where it is incorporated into an aliphatic/aromatic polycarbonate of the disclosure.

A chain stopper (also referred to as a capping agent) may be included during polymerization. The chain-stopper limits molecular weight growth rate, and so controls molecular weight in the polycarbonate. A chain-stopper may be at least one of mono-phenolic compounds, mono-carboxylic acid chlorides, and/or mono-chloroformates.

For example, mono-phenolic compounds suitable as chain stoppers include monocyclic phenols, such as phenol, C_1-C₂₂ alkyl-substituted phenols, p-cumyl-phenol, p-tertiary-butyl phenol, hydroxy diphenyl; monoethers of diphenols, such as p-methoxyphenol. Alkyl-substituted phenols include those with branched chain alkyl substituents having 8 to 9 carbon atoms. A monb-phenolic UV absorber may be used as capping agent. Such compounds include 4-substituted-2-hydroxybenzophenones and their derivatives, aryl salicylates, monoesters of diphenols such as resorcinol monobenzoate, 2-(2-hydroxyaryl)-benzotriazoles and their derivatives, 2-(2-hydroxyaryl)-1,3,5-triazines and their derivatives, and the like. Specifically, mono-phenolic chain-stoppers include phenol, p-cumylphenol, and/or resorcinol monobenzoate.

Mono-carboxylic acid chlorides may also be suitable as chain stoppers. These include monocyclic, mono-carboxylic acid chlorides such as benzoyl chloride, C_1-C₂₂ alkyl-substituted benzoyl chloride, toluoyl chloride, halogen-substituted benzoyl chloride, bromobenzoyl chloride, cinnamoyl chloride, 4-nadimidobenzoyl chloride, and mixtures thereof; polycyclic, mono-carboxylic acid chlorides such as trimellitic anhydride chloride, and naphthoyl chloride; and mixtures of monocyclic and polycyclic mono-carboxylic acid chlorides. Chlorides of aliphatic monocarboxylic acids with up to 22 carbon atoms are suitable. Functionalized chlorides of aliphatic monocarboxylic acids, such as acryloyl chloride and methacryoyl chloride, are also suitable. Also suitable are mono-chloroformates including monocyclic, mono-chloroformates, such as phenyl chloroformate, alkyl-substituted phenyl chloroformate, p-cumyl phenyl chloroformate, toluene chloroformate, and mixtures thereof.

In still another embodiment, the polyester-polycarbonates may be prepared by interfacial polymerization. Rather than utilizing dicarboxylic acid, it is possible, and sometimes even preferred, to employ the reactive derivatives of the acid, such as the corresponding acid halides, in particular the acid dichlorides and the acid dibromides. Thus, for example instead of using isophthalic acid, terephthalic acid, or mixtures thereof, it is possible to employ isophthaloyl dichloride, terephthaloyl dichloride, and mixtures thereof.

Among the phase transfer catalysts that may be used are catalysts of the formula (R³)₄Q⁺X, wherein each R³ is the same or different, and is a C_1-10 alkyl group; Q is a nitrogen or phosphorus atom; and X is a halogen atom or a C_1-8 alkoxy group or C_6-18 aryloxy group. Suitable phase transfer catalysts include, for example, [CH₃(CH₂)₃]₄NX, [CH₃(CH₂)₃]₄PX, [CH₃(CH₂)₅]₄NX, [CH₃(CH₂)₆]₄NX, [CH₃(CH₂)₄]₄NX, CH₃[CH₃(CH₂)₃]₃NX, and CH₃[CH₃(CH₂)₂]₃NX, wherein X is Cl⁻, Br⁻, a C_1-8 alkoxy group or a C_6-18 aryloxy group. In one embodiment, an effective amount of a phase transfer catalyst may be 0.1 to 10 wt % based on the weight of bisphenol in the phosgenation mixture. In another embodiment, an effective amount of phase transfer catalyst may be 0.5 to 2 wt % based on the weight of bisphenol in the phosgenation mixture.

Alternatively, melt processes may be used to make the polycarbonates. Generally, in the melt polymerization process, polycarbonates may be prepared by co-reacting, in a molten state, the dihydroxy reactant(s) and a diaryl carbonate ester, such as diphenyl carbonate, in the presence of a transesterification catalyst in a Banbury® mixer, twin screw extruder, or the like to form a uniform dispersion. Volatile monohydric phenol is removed from the molten reactants by distillation and the polymer is isolated as a molten residue.

In addition to the polycarbonates, polyester-polycarbonates, and combinations of these as described above, it is also possible to use combinations of the polycarbonates and polyester-polycarbonates with other thermoplastic polymers, for example combinations of polycarbonates and/or polycarbonate copolymers with polyesters.

In one embodiment, the thermoplastic composition of the disclosure comprises (i) polycarbonate comprising formula (H-1) repeating units such as formula (H-3) units; and (ii) a polyester.

In a further embodiment, the thermoplastic composition of the development comprises (i) polycarbonate comprising formula (H-1) repeating units such as formula (H-3) units and formula (A-1) repeating units such as formula (A-2) units, formula (A-3) units and formula (A-4) units; and (ii) a polyester.

Suitable polyesters comprise repeating units of formula (6), and may be, for example, poly(alkylene dicarboxylates), liquid crystalline polyesters, and polyester copolymers. It is also possible to use a branched polyester in which a branching agent, for example, a glycol having three or more hydroxyl groups or a trifunctional or multifunctional carboxylic acid has been incorporated. Furthermore, it is sometime desirable to have various concentrations of acid and hydroxyl end groups on the polyester, depending on the ultimate end use of the composition.

An example of a useful class of polyester is the poly(alkylene terephthalate)s. Specific examples of poly(alkylene terephthalate)s include, but are not limited to, poly(ethylene terephthalate) (PET), poly(1,4-butylene terephthalate) (PBT), poly(ethylene naphthanoate) (PEN), poly(butylene naphthanoate), (PBN), (polypropylene terephthalate) (PPT), polycyclohexanedimethanol terephthalate (PCT), and combinations comprising at least one of the foregoing polyesters. Also useful are poly(cyclohexanedimethanol terephthalate)-co-poly(ethylene terephthalate), abbreviated as PETG wherein the polymer comprises greater than or equal to 50 mole % of poly(ethylene terephthalate), and abbreviated as PCTG, wherein the polymer comprises greater than 50 mole % of poly(cyclohexanedimethanol terephthalate). The above polyesters can include the analogous aliphatic polyesters such as poly(alkylene cyclohexanedicarboxylate), an example of which is poly(1,4-cyclohexylenedimethylene-1,4-cyclohexanedicarboxylate) (PCCD). Also contemplated are the above polyesters with a minor amount, e.g., from 0.5 to 10 percent by weight, of units derived from an aliphatic diacid and/or an aliphatic polyol to make copolyesters.

The polycarbonate may also comprise a polysiloxane-polycarbonate copolymer, also referred to as a polysiloxane-polycarbonate. The polysiloxane (also referred to herein as “polydiorganosiloxane”) blocks of the copolymer comprise repeating siloxane units (also referred to herein as “diorganosiloxane units”) of formula (8): wherein each occurrence of R is same or different, and is a C_1-3 monovalent organic radical. For example, R may independently be a C₁-C₁₃ alkyl group, C₁-C₁₃ alkoxy group, C₂-C₁₃ alkenyl group, C₂-C₁₃ alkenyloxy group, C₃-C₆ cycloalkyl group, C₃-C₆ cycloalkoxy group, C₆-C₁₄ aryl group, C₆-C₁₀ aryloxy group, C₇-C₁₃ arylalkyl group, C₇-C₁₃ arylalkoxy group, C₇-C₁₃ alkylaryl group, or C₇-C₁₃ alkylaryloxy group. The foregoing groups may be fully or partially halogenated with fluorine, chlorine, bromine, or iodine, or a combination thereof. Combinations of the foregoing R groups may be used in the same copolymer.

The value of D in formula (8) may vary widely depending on the type and relative amount of each component in the thermoplastic composition, the desired properties of the composition, and like considerations. Generally, D may have an average value of 2 to 1,000, specifically 2 to 500, and more specifically 5 to 100. In one embodiment, D has an average value of 10 to 75, and in still another embodiment, D has an average value of 40 to 60. Where D is of a lower value, e.g., less than 40, it may be desirable to use a relatively larger amount of the polycarbonate-polysiloxane copolymer. Conversely, where D is of a higher value, e.g., greater than 40, it may be necessary to use a relatively lower amount of the polycarbonate-polysiloxane copolymer.

A combination of a first and a second (or more) polysiloxane-polycarbonate copolymer may be used, wherein the average value of D of the first copolymer is less than the average value of D of the second copolymer.

In one embodiment, the polydiorganosiloxane blocks are provided by repeating structural units of formula (9): wherein D is as defined above; each R may independently be the same or different, and is as defined above; and each Ar may independently be the same or different, and is a substituted or unsubstituted C₆-C₃₀ arylene radical, wherein the bonds are directly connected to an aromatic moiety. Suitable Ar groups in formula (9) may be derived from a C₆-C₃₀ dihydroxyarylene compound, for example a dihydroxyarylene compound of formula (3), (4), or (7) above. Combinations comprising at least one of the foregoing dihydroxyarylene compounds may also be used. Specific examples of suitable dihydroxyarylene compounds are 1,1-bis(4-hydroxyphenyl) methane, 1,1-bis(4-hydroxyphenyl) ethane, 2,2-bis(4-hydroxyphenyl) propane, 2,2-bis(4-hydroxyphenyl) butane, 2,2-bis(4-hydroxyphenyl) octane, 1,1-bis(4-hydroxyphenyl) propane, 1,1-bis(4-hydroxyphenyl) n-butane, 2,2-bis(4-hydroxy-1-methylphenyl) propane, 1,1-bis(4-hydroxyphenyl) cyclohexane, bis(4-hydroxyphenyl sulphide), and 1,1-bis(4-hydroxy-t-butylphenyl) propane. Combinations comprising at least one of the foregoing dihydroxy compounds may also be used.

Units of formula (9) may be derived from the corresponding dihydroxy compound of formula (10): wherein R, Ar, and D are as described above. Compounds of formula (10) may be obtained by the reaction of a dihydroxyarylene compound with, for example, an alpha, omega-bisacetoxypolydiorangonosiloxane under phase transfer conditions.

In another embodiment, polydiorganosiloxane blocks comprise units of formula (11): wherein R and D are as described above, and each occurrence of R¹ is independently a divalent C₁-C₃₀ alkylene, and wherein the polymerized polysiloxane unit is the reaction residue of its corresponding dihydroxy compound. In a specific embodiment, the polydiorganosiloxane blocks are provided by repeating structural units of formula (12): wherein R and D are as defined above. Each R² in formula (12) is independently a divalent C₂-C₈ aliphatic group. Each M in formula (12) may be the same or different, and may be a halogen, cyano, nitro, C₁-C₈ alkylthio, C₁-C₈ alkyl, C₁-C₈ alkoxy, C₂-C₈ alkenyl, C₂-C₈ alkenyloxy group, C₃-C₈ cycloalkyl, C₃-C₈ cycloalkoxy, C₆-C₁₀ aryl, C₆-C₁₀ aryloxy, C₇-C₁₂ arylalkyl, C₇-C₁₂ arylalkoxy, C₇-C₁₂ alkylaryl, or C₇-C₁₂ alkylaryloxy, wherein each n is independently 0, 1, 2, 3, or 4.

In one embodiment, M is bromo or chloro, an alkyl group such as methyl, ethyl, or propyl, an alkoxy group such as methoxy, ethoxy, or propoxy, or an aryl group such as phenyl, chlorophenyl, or tolyl; R² is a dimethylene, trimethylene or tetramethylene group; and R is a C_1-8 alkyl, haloalkyl such as trifluoropropyl, cyanoalkyl, or aryl such as phenyl, chlorophenyl or tolyl. In another embodiment, R is methyl, or a mixture of methyl and trifluoropropyl, or a mixture of methyl and phenyl. In still another embodiment, M is methoxy, n is one, R² is a divalent C₁-C₃ aliphatic group, and R is methyl.

Units of formula (12) may. be derived from the corresponding dihydroxy polydiorganosiloxane (13): wherein R, D, M, R², and n are as described above. Such dihydroxy polysiloxanes can be made by effecting a platinum catalyzed addition between a siloxane hydride of formula (14): wherein R and D are as previously defined, and an aliphatically unsaturated monohydric phenol. Suitable aliphatically unsaturated monohydric phenols included, for example, eugenol, 2-allylphenol, 4-allyl-2-methylphenol, 4-allyl-2-phenylphenol, 4-allyl-2-bromophenol, 4-allyl-2-t-butoxyphenol, 4-phenyl-2-phenylphenol, 2-methyl-4-propylphenol, 2-allyl-4,6-dimethylphenol, 2-allyl-4-bromo-6-methylphenol, 2-allyl-6-methoxy-4-methylphenol and 2-allyl-4,6-dimethylphenol. Mixtures comprising at least one of the foregoing may also be used.

In one embodiment, the polysiloxane-polycarbonate may comprise 50-99.95 wt % of carbonate units and 0.05 to 50 wt % siloxane units. Within this range, the polysiloxane-polycarbonate copolymer may comprise 70 to 99.95 wt %, specifically 95 to 99.95 wt % of carbonate units and 0.05 to 30 wt %, specifically 0.05 to 5 wt % siloxane units.

In an embodiment, the polysiloxane-polycarbonate may have a weight average molecular weight of 2,000 to 100,000, specifically 17,000 to 40,000 as measured by gel permeation chromatography using a crosslinked styrene-divinyl benzene column, at a sample concentration of 1 milligram per milliliter, and as calibrated with polycarbonate standards.

As discussed above, due to pyrolytic elimination reactions involving the β-hydrogens, aliphatic/aromatic polycarbonates typically have less satisfactory thermal stability. Polyesters and polycarbonates with significantly improved thermal stability may be prepared from neoalcohols with no β-hydrogen, such as 2,2,4,4-tetramethylcyclobutane-1,3-diol (TMCBD). However, the high cost of TMCBD makes it impractical for many applications. Although neopentyl glycol (NPG) is a lower cost neodiol than TMCBD, and the bischloroformate of NPG has been prepared and converted into the corresponding BPA copolycarbonates, NPG tends to form cyclic carbonates. Moreover, NPG has a lower molecular weight, and requires a large amount of amine acceptor to allow incorporation into polycarbonates. Hydroxypivalyl hydroxypivalate (HPHP) offers a better combination of material cost/amine requirements. HPHP has almost no tendency to cyclize, and has about 2 times the Mw of NPG, which significantly reduces the amount of amine needed to allow incorporation into polymer at effective levels.

In another embodiment, the thermoplastic composition of the disclosure comprises (i) polycarbonate comprising formula (H-1) repeating units such as formula (H-3) units; and (ii) one or more additives selected from the group consisting of hydrolysis stabilizer, impact modifier, filler/reinforcing agent, visual effect enhancer, antioxidant, heat stabilizer, light stabilizer, ultraviolet light absorber, plasticizer, mold release agent, lubricant, antistatic agent, pigment, dye, flame retardant, processing aid, radiation stabilizer, and anti-drip agent.

In a still further embodiment, the thermoplastic composition of the disclosure comprises (i) polycarbonate comprising formula (H-1) repeating units such as formula (H-3) units; and formula (A-1) repeating units such as formula (A-2) units, formula (A-3) units and formula (A-4) units; and (ii) one or more additives selected from the group consisting of hydrolysis stabilizer, impact modifier, filler/reinforcing agent, visual effect enhancer, antioxidant, heat stabilizer, light stabilizer, ultraviolet light absorber, plasticizer, mold release agent, lubricant, antistatic agent, pigment, dye, flame retardant, processing aid, radiation stabilizer, and anti-drip agent.

In various embodiments, additives ordinarily incorporated in the thermoplastic compositions are selected so as not to adversely affect the desired properties of the thermoplastic composition. Mixtures of additives may be used. Such additives may be mixed at a suitable time during the mixing of the components for forming the thermoplastic composition.

The thermoplastic composition may comprise one or more hydrolysis stabilizers for reducing hydrolysis of ester and/or carbonate groups. Typical hydrolysis stabilizers may include carbodiimide-based additives such as aromatic and/or cycloaliphatic monocarbo-diimides substituted in position 2 and 2′, such as 2,2′,6,6′-tetraisopropyidiphenyl-carbodiimide. Polycarbodiimides having a molecular weight of greater than 500 grams per mole are also suitable. Other compounds useful as hydrolysis stabilizers include an epoxy modified acrylic oligomers or polymers, and oligomers based on cycloaliphatic epoxides. Specific examples of suitable epoxy functionalized stabilizers include Cycloaliphatic Epoxide Resin ERL-4221 supplied by Union Carbide Corporation (a subsidiary of Dow Chemical), Danbury, Conn.; and JONCRYL® ADR4300 and JONCRYL® ADR4368, available from Johnson Polymer Inc, Sturtevant, Wis. When present, hydrolysis stabilizers can be used in amounts of 0.05 to 1 percent by weight, specifically 0.1 to 0.5 percent by weight, and more specifically 0.12 to 0.3 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

The thermoplastic composition may comprise a colorant such as a pigment and/or dye additive. Suitable pigments include for example, inorganic pigments such as metal oxides and mixed metal oxides such as zinc oxide, titanium dioxides, iron oxides or the like; sulfides such as zinc sulfides, or the like; aluminates; sodium sulfo-silicates, sulfates, chromates, or the like; carbon blacks; zinc ferrites; ultramarine blue; Pigment Brown 24; Pigment Red 101; Pigment Yellow 119; organic pigments such as azos, di-azos, quinacridones, perylenes, naphthalene tetracarboxylic acids, flavanthrones, isoindolinones, tetrachloroisoindolinones, anthraquinones, anthanthrones, dioxazines, phthalocyanines, and azo lakes; Pigment Blue 60, Pigment Red 122, Pigment Red 149, Pigment Red 177, Pigment Red 179, Pigment Red 202, Pigment Violet 29, Pigment Blue 15, Pigment Green 7, Pigment Yellow 147 and Pigment Yellow 150, or combinations comprising at least one of the foregoing pigments. When present, pigments can be used in amounts of 0.01 to 10 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Suitable dyes can be organic materials and include, for example, coumarin dyes such as coumarin 460 (blue), coumarin 6 (green), nile red or the like; lanthanide complexes; hydrocarbon and substituted hydrocarbon dyes; polycyclic aromatic hydrocarbon dyes; scintillation dyes such as oxazole or oxadiazole dyes; aryl- or heteroaryl-substituted poly (C_2-8) olefin dyes; carbocyanine dyes; indanthrone dyes; phthalocyanine dyes; oxazine dyes; carbostyryl dyes; napthalenetetracarboxylic acid dyes; porphyrin dyes; bis(styryl)biphenyl dyes; acridine dyes; anthraquinone dyes; cyanine dyes; methine dyes; arylmethane dyes; azo dyes; indigoid dyes, thioindigoid dyes, diazonium dyes; nitro dyes; quinone imine dyes; aminoketone dyes; tetrazolium dyes; thiazole dyes; perylene dyes, perinone dyes; bis-benzoxazolylthiophene (BBOT); triarylmethane dyes; xanthene dyes; thioxanthene dyes; naphthalimide dyes; lactone dyes; fluorophores such as anti- stokes shift dyes which absorb in the near infrared wavelength and emit in the visible wavelength, or the like; luminescent dyes such as 7-amino-4-methylcoumarin; 3-(2′-benzothiazolyl)-7-diethylaminocoumarin; 2-(4-biphenylyl)-5-(4-t-butylphenyl)-1,3,4-oxadiazole; 2,5-bis-(4-biphenylyl)-oxazole; 2,2′-dimethyl-p-quaterphenyl; 2,2-dimethyl-p-terphenyl; 3,5,3″″,5″″-tetra-t-butyl-p-quinquephenyl; 2,5-diphenylfuran; 2,5-diphenyloxazole; 4,4′-diphenylstilbene; 4-dicyanomethylene-2-methyl-6-(p-dimethylaminostyryl)-4H-pyran; 1,1′-diethyl-2,2′-carbocyanineiodide; 3,3′-diethyl-4,4′,5,5′-dibenzothiatricarbocyanine iodide; 7-dimethylamino-1-methyl-4-methoxy-8-azaquinolone-2; 7-dimethylamino-4-methylquinolone-2; 2-(4-(4-dimethylaminophenyl)-1,3-butadienyl)-3-ethylbenzothiazolium perchlorate; 3-diethylamino-7-diethyliminophenoxazonium perchlorate; 2-(1-haphthyl)-5-phenyloxazole; 2,2′-p-phenylen-bis(5-phenyloxazole); rhodamine 700; rhodamine 800; pyrene; chrysene; rubrene; coronene, or the like, or combinations comprising at least one of the foregoing dyes. When present, dyes can be used in amounts of 0.01 to 10 percent by weight, based on the total weight of the component (i) polycarbonate used in the thermoplastic composition.

The thermoplastic composition may comprise an impact modifier to increase its impact resistance, where the impact modifier is present in an amount that does not adversely affect the desired properties of the thermoplastic composition. These impact modifiers include elastomer-modified graft copolymers comprising (i) an elastomeric (i.e., rubbery) polymer substrate having a Tg less than 10° C., more specifically less than −10° C., or more specifically −40° to −80° C., and (ii) a rigid polymeric superstrate grafted to the elastomeric polymer substrate. As is known, elastomer-modified graft copolymers may be prepared by first providing the elastomeric polymer, then polymerizing the constituent monomer(s) of the rigid phase in the presence of the elastomer to obtain the graft copolymer. The grafts may be attached as graft branches or as shells to an elastomer core. The shell may merely physically encapsulate the core, or the shell may be partially or essentially completely grafted to the core.

Suitable materials for use as the elastomer phase include, for example, conjugated diene rubbers; copolymers of a conjugated diene with less than 50 wt % of a copolymerizable monomer; olefin rubbers such as ethylene propylene copolymers (EPR) or ethylene-propylene-diene monomer rubbers (EPDM); ethylene-vinyl acetate rubbers; silicone rubbers; elastomeric C_1-8 alkyl (meth)acrylates; elastomeric copolymers of C_1-8 alkyl (meth)acrylates with butadiene and/or styrene; or combinations comprising at least one of the foregoing elastomers.

Suitable conjugated diene monomers for preparing the elastomer phase are of formula (15): wherein each X^b is independently hydrogen, C₁-C₅ alkyl, or the like. Examples of conjugated diene monomers that may be used are butadiene, isoprene, 1,3-heptadiene, methyl-1,3-pentadiene, 2,3-dimethyl-1,3-butadiene, 2-ethyl-1,3-pentadiene; 1,3- and 2,4-hexadienes, and the like, as well as mixtures comprising at least one of the foregoing conjugated diene monomers. Specific conjugated diene homopolymers include polybutadiene and polyisoprene.

Copolymers of a conjugated diene rubber may also be used, for example those produced by aqueous radical emulsion polymerization of a conjugated diene and one or more monomers copolymerizable therewith. Vinyl aromatic compounds may be copolymerized with the ethylenically unsaturated nitrile monomer to form a copolymer, wherein the vinyl aromatic compounds can include monomers of formula (16): wherein each X^c is independently hydrogen, C₁-C₁₂ alkyl, C₃-C₁₂ cycloalkyl, C₆-C₁₂ aryl, C₇-C₁₂ arylalkyl, C₇-C₁₂ alkylaryl, C₁-C₁₂ alkoxy, C₃-C₁₂ cycloalkoxy, C₆-C₁₂ aryloxy, chloro, bromo, or hydroxy, and R is hydrogen, C₁-C₅ alkyl, bromo, or chloro. Examples of suitable monovinylaromatic monomers that may be used include styrene, 3-methylstyrene, 3,5-diethylstyrene, 4-n-propylstyrene, alpha-methylstyrene, alpha-methyl vinyltoluene, alpha-chlorostyrene, alpha-bromostyrene, dichlorostyrene, dibromostyrene, tetra-chlorostyrene, and the like, and combinations comprising at least one of the foregoing compounds. Styrene and/or alpha-methylstyrene may be used as monomers copolymerizable with the conjugated diene monomer.

Other monomers that may be copolymerized with the conjugated diene are monovinylic monomers such as itaconic acid, acrylamide, N-substituted acrylamide or methacrylamide, maleic anhydride, maleimide, N-alkyl-, aryl-, or haloaryl-substituted maleimide, glycidyl (meth)acrylates, and monomers of the generic formula (17): wherein R is hydrogen, C₁-C₅ alkyl, bromo, or chloro, and X^c is C₁-C₁₂ alkoxycarbonyl, C₁-C₁₂ aryloxycarbonyl, hydroxy carbonyl, or the like. Examples of monomers of formula (17) include, acrylic acid, methyl (meth)acrylate, ethyl (meth)acrylate, n-butyl (meth)acrylate, t-butyl (meth)acrylate, n-propyl (meth)acrylate, isopropyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, and the like, and combinations comprising at least one of the foregoing monomers. Monomers such as n-butyl acrylate, ethyl acrylate, and 2-ethylhexyl acrylate are commonly used as monomers copolymerizable with the conjugated diene monomer. Mixtures of the foregoing monovinyl monomers and monovinylaromatic monomers may also be used.

Suitable (meth)acrylate monomers suitable for use as the elastomeric phase may be cross-linked, particulate emulsion homopolymers or copolymers of C₁-₈ alkyl (meth)acrylates, in particular C₄-₆ alkyl acrylates, for example n-butyl acrylate, t-butyl acrylate, n-propyl acrylate, isopropyl acrylate, 2-ethylhexyl acrylate, and the like, and combinations comprising at least one of the foregoing monomers. The C_1-8 alkyl (meth)acrylate monomers may optionally be polymerized in admixture with up to 15 wt % of comonomers of formulas (15), (16), or (17). Exemplary comonomers include but are not limited to butadiene, isoprene, styrene, methyl methacrylate, phenyl methacrylate, penethylmethacrylate, N-cyclohexylacrylamide, vinyl methyl ether, and mixtures comprising at least one of the foregoing comonomers. Optionally, up to 5 wt % of a polyfunctional crosslinking comonomer may be present, for example divinylbenzene, alkylenediol di(meth)acrylates such as glycol bisacrylate, alkylenetriol tri(meth)acrylates, polyester di(meth)acrylates, bisacrylamides, triallyl cyanurate, triallyl isocyanurate, allyl (meth)acrylate, diallyl maleate, diallyl fumarate, diallyl adipate, triallyl esters of citric acid, triallyl esters of phosphoric acid, and the like, as well as combinations comprising at least one of the foregoing crosslinking agents.

The elastomer phase may be polymerized by mass, emulsion, suspension, solution or combined processes such as bulk-suspension, emulsion-bulk, bulk-solution or other techniques, using continuous, semibatch, or batch processes. The particle size of the elastomer substrate is not critical. For example, an average particle size of 0.001 to 25 micrometers, specifically 0.01 to 15 micrometers, or even more specifically 0.1 to 8 micrometers may be used for emulsion based polymerized rubber lattices. A particle size of 0.5 to 10 micrometers, specifically 0.6 to 1.5 micrometers may be used for bulk polymerized rubber substrates. Particle size may be measured by simple light transmittance methods or capillary hydrodynamic chromatography (CHDF). The elastomer phase may be a particulate, moderately cross-linked conjugated butadiene or C_4-6 alkyl acrylate rubber, and preferably has a gel content greater than 70 wt %. Also suitable are mixtures of butadiene with styrene and/or C_4-6 alkyl acrylate rubbers.

The elastomeric phase may provide 5 to 95 wt % of the total graft copolymer, more specifically 20 to 90 wt %, and even more specifically 40 to 85 wt % of the elastomer-modified graft copolymer, the remainder being the rigid graft phase.

The rigid phase of the elastomer-modified graft copolymer may be formed by graft polymerization of a mixture comprising a monovinylaromatic monomer and optionally one or more comonomers in the presence of one or more elastomeric polymer substrates. The above-described monovinylaromatic monomers of formula (16) may be used in the rigid graft phase, including styrene, alpha-methyl styrene, halostyrenes such as dibromostyrene, vinyltoluene, vinylxylene, butylstyrene, para-hydroxystyrene, methoxystyrene, or the like, or combinations comprising at least one of the foregoing monovinylaromatic monomers. Suitable comonomers include, for example, the above-described monovinylic monomers and/or monomers of the general formula (17). In one embodiment, R is hydrogen or C₁-C₂ alkyl, and X^c is cyano or C₁-C₁₂ alkoxycarbonyl. Specific examples of suitable comonomers for use in the rigid phase include, methyl (meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate, isopropyl (meth)acrylate, and the like, and combinations comprising at least one of the foregoing comonomers.

The relative ratio of monovinylaromatic monomer and comonomer in the rigid graft phase may vary widely depending on the type of elastomer substrate, type of monovinylaromatic monomer(s), type of comonomer(s), and the desired properties of the impact modifier. The rigid phase may generally comprise up to 100 wt % of monovinyl aromatic monomer, specifically 30 to 100 wt %, more specifically 50 to 90 wt % monovinylaromatic monomer, with the balance being comonomer(s).

Depending on the amount of elastomer-modified polymer present, a separate matrix or continuous phase of ungrafted rigid polymer or copolymer may be simultaneously obtained along with the elastomer-modified graft copolymer. Typically, such impact modifiers comprise 40 to 95 wt % elastomer-modified graft copolymer and 5 to 65 wt % graft (co)polymer, based on the total weight of the impact modifier. In another embodiment, such impact modifiers comprise 50 to 85 wt %, more specifically 75 to 85 wt % rubber-modified graft copolymer, together with 15 to 50 wt %, more specifically 15 to 25 wt % graft (co)polymer, based on the total weight of the impact modifier.

Another specific type of elastomer-modified impact modifier comprises structural units derived from at least one silicone rubber monomer, a branched acrylate rubber monomer having the formula H₂C═C(R^d)C(O)OCH₂CH₂R^e, wherein R^d is hydrogen or a C₁-C₈ linear or branched alkyl group and Re is a branched C₃-C₁₆ alkyl group; a first graft link monomer; a polymerizable alkenyl-containing organic material; and a second graft link monomer. The silicone rubber monomer may comprise, for example, a cyclic siloxane, tetraalkoxysilane, trialkoxysilane, (acryloxy)alkoxysilane, (mercaptoalkyl)alkoxysilane, vinylalkoxysilane, or allylalkoxysilane, alone or in combination, e.g., decamethylcyclopentasiloxane, dodecamethylcyclohexasiloxane, trimethyltriphenylcyclotrisiloxane, tetramethyltetraphenylcyclotetrasiloxane, tetramethyltetravinylcyclotetrasiloxane, octaphenylcyclotetrasiloxane, octamethylcyclotetrasiloxane and/or tetraethoxysilane.

Exemplary branched acrylate rubber monomers include iso-octyl acrylate, 6-methyloctyl acrylate, 7-methyloctyl acrylate, 6-methylheptyl acrylate, and the like, alone or in combination. The polymerizable, alkenyl-containing organic material may be, for example, a monomer of formula (16) or (17), e.g., styrene, alpha-methylstyrene, or an unbranched (meth)acrylate such as methyl methacrylate, 2-ethylhexyl methacrylate, methyl acrylate, ethyl acrylate, n-propyl acrylate, or the like, alone or in combination.

The at least one first graft link monomer may be an (acryloxy)alkoxysilane, a (mercaptoalkyl)alkoxysilane, a vinylalkoxysilane, or an allylalkoxysilane, alone or in combination, e.g., (gamma-methacryloxypropyl) (dimethoxy)methylsilane and/or (3-mercaptopropyl) trimethoxysilane. The at least one second graft link monomer is a polyethylenically unsaturated compound having at least one allyl group, such as allyl methacrylate, triallyl cyanurate, or triallyl isocyanurate, alone or in combination.

The silicone-acrylate impact modifier compositions can be prepared by emulsion polymerization, wherein, for example at least one silicone rubber monomer is reacted with at least one first graft link monomer at a temperature from 30° C. to 110° C. to form a silicone rubber latex, in the presence of a surfactant such as dodecylbenzenesulfonic acid. Alternatively, a cyclic siloxane such as cyclooctamethyltetrasiloxane and tetraethoxyorthosilicate may be reacted with a first graft link monomer such as (gamma-methacryloxypropyl) methyidimethoxysilane, to afford silicone rubber having an average particle size from 100 nanometers to 2 micrometers. At least one branched acrylate rubber monomer is then polymerized with the silicone rubber particles, optionally in the presence of a cross linking monomer, such as allylmethacrylate in the presence of a free radical generating polymerization catalyst such as benzoyl peroxide. This latex is then reacted with a polymerizable alkenyl-containing organic material and a second graft link monomer. The latex particles of the graft silicone-acrylate rubber hybrid may be separated from the aqueous phase through coagulation (by treatment with a coagulant) and dried to a fine powder to produce the silicone-acrylate rubber impact modifier composition. This method can be generally used for producing the silicone-acrylate impact modifier having a particle size from 100 nanometers to 2 micrometers.

Processes known for the. formation of the foregoing elastomer-modified graft copolymers include mass, emulsion, suspension, and solution processes, or combined processes such as bulk-suspension, emulsion-bulk, bulk-solution or other techniques, using continuous, semibatch, or batch processes.

The foregoing types of impact modifiers, including SAN copolymers, can be prepared by an emulsion polymerization process that is free of basic materials such as alkali metal salts of C_6-30 fatty acids, for example sodium stearate, lithium stearate, sodium oleate, potassium oleate, and the like; alkali metal carbonates, amines such as dodecyl dimethyl amine, dodecyl amine, and the like; and ammonium salts of amines. Such materials are commonly used as surfactants in emulsion polymerization, and may catalyze transesterification and/or degradation of polycarbonates. Instead, ionic sulfate, sulfonate or phosphate surfactants may be used in preparing the impact modifiers, particularly the elastomeric substrate portion of the impact modifiers. Suitable surfactants include, for example, C_1-22 alkyl or C_7-25 alkylaryl sulfonates, C_1-22 alkyl or C_7-25 alkylaryl sulfates, C_1-22 alkyl or C_7-25 alkylaryl phosphates, substituted silicates, and mixtures thereof. A specific surfactant is a C_6-16, specifically a C_8-12 alkyl sulfonate. In the practice, any of the above-described impact modifiers may be used providing it is free of the alkali metal salts of fatty acids, alkali metal carbonates and other basic materials.

A specific impact modifier of this type is a methyl methacrylate-butadiene-styrene (MBS) impact modifier wherein the butadiene substrate is prepared using above-described sulfonates, sulfates, or phosphates as surfactants. Other examples of elastomer-modified graft copolymers besides ABS and MBS include but are not limited to acrylonitrile-styrene-butyl acrylate (ASA), methyl methacrylate-acrylonitrile-butadiene-styrene (MABS), and acrylonitrile-ethylene-propylene-diene-styrene (AES).

When present, impact modifiers can be present in amounts of 0.1 to 30 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

The thermoplastic composition may include fillers or reinforcing agents. Where used, suitable fillers or reinforcing agents include, for example, silicates and silica powders such as aluminum silicate (mullite), synthetic calcium silicate, zirconium silicate, fused silica, crystalline silica graphite, natural silica sand, or the like; boron powders such as boron-nitride. powder, boron-silicate powders, or the like; oxides such as TiO₂, aluminum oxide, magnesium oxide, or the like; calcium sulfate (as its anhydride, dihydrate or trihydrate); calcium carbonates such as chalk, limestone, marble, synthetic precipitated calcium carbonates, or the like; talc, including fibrous, modular, needle shaped, lamellar talc, or the like; wollastonite; surface-treated wollastonite; glass spheres such as hollow and solid glass spheres, silicate spheres, cenospheres, aluminosilicate (armospheres), or the like; kaolin, including hard kaolin, soft kaolin, calcined kaolin, kaolin comprising various coatings known in the art to facilitate compatibility with the polymeric matrix resin, or the like; single crystal fibers or “whiskers” such as silicon carbide, alumina, boron carbide, iron, nickel, copper, or the like; fibers (including continuous and chopped fibers) such as asbestos, carbon fibers, glass fibers, such as E, A, C, ECR, R, S, D, or NE glasses, or the like; sulfides such as molybdenum sulfide, zinc sulfide or the like; barium compounds such as barium titanate, barium ferrite, barium sulfate, heavy spar, or the like; metals and metal oxides such as particulate or fibrous aluminum, bronze, zinc, copper and nickel or the like; flaked fillers such as glass flakes, flaked silicon carbide, aluminum diboride, aluminum flakes, steel flakes or the like; fibrous fillers, for example short inorganic fibers such as those derived from blends comprising at least one of aluminum silicates, aluminum oxides, magnesium oxides, and calcium sulfate hemihydrate or the like; natural fillers and reinforcements, such as wood flour obtained by pulverizing wood, fibrous products such as cellulose, cotton, sisal, jute, starch, cork flour, lignin, ground nut shells, corn, rice grain husks or the like; organic fillers such as polytetrafluoroethylene; reinforcing organic fibrous fillers formed from organic polymers capable of forming fibers such as poly(ether ketone), polyimide, polybenzoxazole, poly(phenylene sulfide), polyesters, polyethylene, aromatic polyamides, aromatic polyimides, polyetherimides, polytetrafluoroethylene, acrylic resins, poly(vinyl alcohol) or the like; as well as additional fillers and reinforcing agents such as mica, clay, feldspar, flue dust, fillite, quartz, quartzite, perlite, tripoli, diatomaceous earth, carbon black, or the like, or combinations comprising at least one of the foregoing fillers or reinforcing agents.

The fillers and reinforcing agents may be coated with a layer of metallic material to facilitate conductivity, or surface treated with silanes to improve adhesion and dispersion with the polymeric matrix resin. In addition, the reinforcing fillers may be provided in the form of monofilament or multifilament fibers and may be used either alone or in combination with other types of fiber, through, for example, co-weaving or core/sheath, side-by-side, orange-type or matrix and fibril constructions, or by other methods known to one skilled in the art of fiber manufacture. Suitable cowoven structures include, for example, glass fiber-carbon fiber, carbon fiber-aromatic polyimide (aramid) fiber, and aromatic polyimide fiberglass fiber or the like. Fibrous fillers may be supplied in the form of, for example, rovings, woven fibrous reinforcements, such as 0-90 degree fabrics or the like; non-woven fibrous reinforcements such as continuous strand mat, chopped strand mat, tissues, papers and felts or the like; or three-dimensional reinforcements such as braids. When present, fillers can be used in amounts of 0 to 90 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Visual effect enhancers, sometimes known as visual effects additives or pigments may be present in an encapsulated form, a non-encapsulated form, or laminated to a particle comprising polymeric resin. Some non-limiting examples of visual effects additives are aluminum, gold, silver, copper, nickel, titanium, stainless steel, nickel sulfide, cobalt sulfide, manganese sulfide, metal oxides, white mica, black mica, pearl mica, synthetic mica, mica coated with titanium dioxide, metal-coated glass flakes, and colorants, including but not limited, to Perylene Red. The visual effect additive may have a high or low aspect ratio and may comprise greater than 1 facet. Dyes may be employed such as Solvent Blue 35, Solvent Blue 36, Disperse Violet 26, Solvent Green 3, Anaplast Orange LFP, Perylene Red, and Morplas Red 36. Fluorescent dyes may also be employed including, but not limited to, Permanent Pink R (Color Index Pigment Red 181, from Clariant Corporation), Hostasol Red 5B (Color Index #73300, CAS # 522-75-8, from Clariant Corporation) and Macrolex Fluorescent Yellow 10GN (Color Index Solvent-Yellow 160:1, from Bayer Corporation). Pigments such as titanium dioxide, zinc sulfide, carbon black, cobalt chromate, cobalt titanate, cadmium sulfides, iron oxide, sodium aluminum sulfosilicate, sodium sulfosilicate, chrome antimony titanium rutile, nickel antimony titanium rutile, and zinc oxide may be employed. Visual effect additives in encapsulated form usually comprise a visual effect material such as a high aspect ratio material like aluminum flakes encapsulated by a polymer. The encapsulated visual effect additive has the shape of a bead. When present, visual effect enhancers can be used in amounts of 0.01 to 10 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Suitable antioxidant additives include, for example, organophosphites such as tris(nonyl phenyl)phosphite, tris(2,4-di-t-butylphenyl)phosphite, bis(2,4-di-t-butylphenyl)pentaerythritol diphosphite, distearyl pentaerythritol diphosphite or the like; alkylated monophenols or polyphenols; alkylated reaction products of polyphenols with dienes, such as tetrakis[methylene(3,5-di-tert-butyl-4-hydroxyhydrocinnamate)] methane, or the like; butylated reaction products of para-cresol or dicyclopentadiene; alkylated hydroquinones; hydroxylated thiodiphenyl ethers; alkylidene-bisphenols; benzyl compounds; esters of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid with monohydric or polyhydric alcohols; esters of beta-(5-tert-butyl-4-hydroxy-3-methylphenyl)-propionic acid with monohydric or polyhydric alcohols; esters of thioalkyl or thioaryl compounds such as distearylthiopropionate, dilaurylthiopropionate, ditridecylthiodipropionate, octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, pentaerythrityl-tetrakis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate or the like; amides of beta-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid or the like, or combinations comprising at least one of the foregoing antioxidants. When present, antioxidants can be used in amounts of 0.0001 to 1 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Suitable heat stabilizer additives include, for example, organophosphites such as triphenyl phosphite, tris-(2,6-dimethylphenyl)phosphite, tris-(mixed mono-and di-nonylphenyl)phosphite or the like; phosphonates such as dimethylbenzene phosphonate or the like, phosphates such as trimethyl phosphate, or the like, or combinations comprising at least one of the foregoing heat stabilizers. When present, heat stabilizers can be used in amounts of 0.0001 to 1 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Light stabilizers and/or ultraviolet light (UV) absorbing additives may also be used. Suitable light stabilizer additives include, for example, benzotriazoles such as 2-(2-hydroxy-5-methylphenyl)benzotriazole, 2-(2-hydroxy-5-tert-octylphenyl)-benzotriazole and 2-hydroxy-4-n-octoxy benzophenone, or the like, or combinations comprising at least one of the foregoing light stabilizers. When present, light stabilizers can be used in amounts of 0.0001 to 1 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Suitable UV absorbing additives include for example, hydroxybenzophenones; hydroxybenzotriazoles; hydroxybenzotriazines; cyanoacrylates; oxanilides; benzoxazinones; 2-(2H-benzotriazol-2-yl)-4-(1,1,3,3-tetramethylbutyl)-phenol (CYASORB™ 5411); 2-hydroxy-4-n-octyloxybenzophenone (CYASORBυ 531); 2-[4,6-bis(2,4-dimethylphenyl)-1,3,5-triazin-2-yl]-5-(octyloxy)-phenol (CYASORB™ 1164); 2,2′-(1,4- phenylene)bis(4H-31,-benzoxazin4-one) (CYASORB™ UV-3638);1,3-bis[(2-cyano-3,3-diphenylacryloyl)oxy]-2,2-bis[[(2-cyano-3,3-diphenylacryloyl)oxy]methyl]propane (UVINUL™ 3030); 2,2′-(1,4-phenylene) bis(4H-3,1-benzoxazin-4-one); 1,3-bis[(2-cyano-3,3-diphenylacryloyl)oxy]-2,2-bis[[(2-cyano-3,3-diphenylacryloyl)oxy]methyl]propane; nano-size inorganic materials such as titanium oxide, cerium oxide, and zinc oxide, all with particle size less than 100 nanometers; or the like, or combinations comprising at least one of the foregoing UV absorbers. When present, UV absorbers can be used in amounts of 0.0001 to 1 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Plasticizers, lubricants, and/or mold release agents additives may also be used. There is considerable overlap among these types of materials, which include, for example, phthalic acid esters such as dioctyl-4,5-epoxy-hexahydrophthalate; tris-(octoxycarbonylethyl)isocyanurate; tristearin; di- or polyfunctional aromatic phosphates such as resorcinol tetraphenyl diphosphate (RDP), the bis(diphenyl) phosphate of hydroquinone and the bis(diphenyl) phosphate of bisphenol-A; poly-alpha-olefins; epoxidized soybean oil; silicones, including silicone oils; esters, for example, fatty acid esters such as alkyl stearyl esters, e.g., methyl stearate; stearyl stearate, pentaerythritol tetrastearate, and the like; mixtures of methyl stearate and hydrophilic and hydrophobic nonionic surfactants comprising polyethylene glycol polymers, polypropylene glycol polymers, and copolymers thereof, e.g., methyl stearate and polyethylene-polypropylene glycol copolymers in a suitable solvent; waxes such as beeswax, montan wax, paraffin wax or the like. When present, such materials can be used in amounts of 0.001 to 1 percent by weight, specifically 0.01 to 0.75 percent by weight, more specifically 0.1 to 0.5 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

The term “antistatic agent” refers to monomeric, oligomeric, or polymeric materials that can be processed into polymer resins and/or sprayed onto materials or articles to improve conductive properties and overall physical performance. Examples of monomeric antistatic agents include glycerol monostearate, glycerol distearate, glycerol tristearate, ethoxylated amines, primary, secondary and tertiary amines, ethoxylated alcohols, alkyl sulfates, alkylarylsulfates, alkylphosphates, alkylaminesulfates, alkyl sulfonate salts such as sodium stearyl sulfonate, sodium dodecylbenzenesulfonate or the like, quaternary ammonium salts, quaternary ammonium resins, imidazoline derivatives, sorbitan esters, ethanolamides, betaines, or the like, or combinations comprising at least one of the foregoing monomeric antistatic agents.

Exemplary polymeric antistatic agents include certain polyesteramides polyetherpolyamide (polyetheramide) block copolymers, polyetheresteramide block copolymers, polyetheresters, or polyurethanes, each containing polyalkylene glycol moieties polyalkylene oxide units such as polyethylene glycol, polypropylene glycol, polytetramethylene glycol, and the like. Such polymeric antistatic agents are commercially available, for example Pelestat™ 6321 (Sanyo) or Pebax™ MH1657 (Atofina), Irgastat™ P18 and P22 (Ciba-Geigy). Other polymeric materials that may be used as antistatic agents are inherently conducting polymers such as polyaniline (commercially available as PANIPOL®EB from Panipol), polypyrrole and polythiophene (commercially available from Bayer), which retain some of their intrinsic conductivity after melt processing at elevated temperatures. In one embodiment, carbon fibers, carbon nanofibers, carbon nanotubes, carbon black, or any combination of the foregoing may be used in a polymeric resin containing chemical antistatic agents to render the composition electrostatically dissipative. When present, antistatic agents can be used in amounts of 0.0001 to 5 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Suitable flame retardant that may be added may be organic compounds that include phosphorus, bromine, and/or chlorine. Non-brominated and non-chlorinated phosphorus-containing flame retardants may be preferred in certain applications for regulatory reasons, for example organic phosphates and organic compounds containing phosphorus-nitrogen bonds.

One type of exemplary organic phosphate is an aromatic phosphate of the formula (GO)₃P═O, wherein each G is independently an alkyl, cycloalkyl, aryl, alkylaryl, or arylalkyl group, provided that at least one G is an aromatic group. Two of the G groups may be joined together to provide a cyclic group, for example, diphenyl pentaerythritol diphosphate. Other suitable aromatic phosphates may be, for example, phenyl bis(dodecyl) phosphate, phenyl bis(neopentyl) phosphate, phenyl bis(3,5,5′-trimethylhexyl) phosphate, ethyl diphenyl phosphate, 2-ethylhexyl di(p-tolyl) phosphate, bis(2-ethylhexyl) p-tolyl phosphate, tritolyl phosphate, bis(2-ethylhexyl) phenyl phosphate, tri(nonylphenyl) phosphate, bis(dodecyl) p-tolyl phosphate, dibutyl phenyl phosphate, 2-chloroethyl diphenyl phosphate, p-tolyl bis(2,5,5′-trimethylhexyl) phosphate, 2-ethylhexyl diphenyl phosphate, or the like. A specific aromatic phosphate is one in which each G is aromatic, for example, triphenyl phosphate, tricresyl phosphate, isopropylated trip henyl phosphate, and the like.

Di- or polyfunctional aromatic phosphorus-containing compounds are also useful, for example, compounds of the formulas (18), (19), and (20) below: wherein each G¹ is independently a hydrocarbon having 1 to 30 carbon atoms; each G² is independently a hydrocarbon or hydrocarbonoxy having 1 to 30 carbon atoms; each X^a is independently a hydrocarbon having 1 to 30 carbon atoms; each X is independently a bromine or chlorine; m is 0 to 4, and n is 1 to 30. Examples of suitable di- or polyfunctional aromatic phosphorus-containing compounds include resorcinol tetraphenyl diphosphate (RDP), the bis(diphenyl) phosphate of hydroquinone and the bis(diphenyl) phosphate of bisphenol-A, respectively, their oligomeric and polymeric counterparts, and the like.

Exemplary suitable flame retardant compounds containing phosphorus-nitrogen bonds include phosphonitrilic chloride, phosphorus ester amides, phosphoric acid amides, phosphonic acid amides, phosphinic acid amides, tris(aziridinyl) phosphine oxide. When present, phosphorus-containing flame retardants can be present in amounts of 0.1 to 10 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Halogenated materials may also be used as flame retardants, for example halogenated compounds and resins of formula (21): wherein R is an alkylene, alkylidene or cycloaliphatic linkage, e.g., methylene, ethylene, propylene, isopropylene, isopropylidene, butylene, isobutylene, amylene, cyclohexylene, cyclopentylidene, or the like; or an oxygen ether, carbonyl, amine, or a sulfur containing linkage, e.g., sulfide, sulfoxide, sulfone, or the like. R can also consist of two or more alkylene or alkylidene linkages connected by such groups as aromatic, amino, ether, carbonyl, sulfide, sulfoxide, sulfone, or the like.

Ar and Ar′ in formula (21) are each independently mono- or polycarbocyclic aromatic groups such as phenylene, biphenylene, terphenylene, naphthylene, or the like.

Y is an organic, inorganic, or organometallic radical, for example: halogen, e.g., chlorine, bromine, iodine, fluorine; ether groups of the general formula OE, wherein E is a monovalent hydrocarbon radical similar to X; monovalent hydrocarbon groups of the type represented by R; or other substituents, e.g., nitro, cyano, and the like, said substituents being essentially inert provided that there is at least one and preferably two halogen atoms per aryl nucleus.

When present, each X is independently a monovalent hydrocarbon group, for example an alkyl group such as methyl, ethyl, propyl, isopropyl, butyl, decyl, or the like; an aryl groups such as phenyl, naphthyl, biphenyl, xylyl, tolyl, or the like; and arylalkyl group such as benzyl, ethylphenyl, or the like; a cycloaliphatic group such as cyclopentyl, cyclohexyl, or the like. The monovalent hydrocarbon group may itself contain inert substituents.

Each d is independently 1 to a maximum equivalent to the number of replaceable hydrogens substituted on the aromatic rings comprising Ar or Ar′. Each e is independently 0 to a maximum equivalent to the number of replaceable hydrogens on R. Each a, b, and c is independently a whole number, including 0. When b is not 0, neither a nor c may be 0. Otherwise either a or c, but not both, may be 0. Where b is 0, the aromatic groups are joined by a direct carbon-carbon bond.

The hydroxyl and Y substituents on the aromatic groups, Ar and Ar′, can be varied in the ortho, meta or para positions on the aromatic rings and the groups can be in any possible geometric relationship with respect to one another.

Included within the scope of the above formula are bisphenols of which the following are representative: 2,2-bis-(3,5-dichlorophenyl)-propane; bis-(2-chlorophenyl)-methane; bis(2,6-dibromophenyl)-methane; 1,1-bis-(4-iodophenyl)-ethane; 1,2-bis-(2,6-dichlorophenyl)-ethane; 1,1-bis-(2-chloro-4-iodophenyl)ethane; 1,1-bis-(2-chloro-4-methylphenyl)-ethane; 1,1-bis-(3,5-dichlorophenyl)-ethane; 2,2-bis-(3-phenyl-4-bromophenyl)-ethane; 2,6-bis-(4,6-dichloronaphthyl)-propane; 2,2-bis-(2,6-dichlorophenyl)-pentane; 2,2-bis-(3,5-dibromophenyl)-hexane; bis-(4-chlorophenyl)-phenyl-methane; bis-(3,5-dichlorophenyl)-cyclohexylmethane; bis-(3-nitro-4-bromophenyl)-methane; bis-(4-hydroxy-2,6-dichloro-3-methoxyphenyl)-methane; and 2,2-bis-(3,5-dichloro-4-hydroxyphenyl)-propane 2,2bis-(3-bromo-4-hydroxyphenyl)-propane. Also included within the above structural formula are: 1,3-dichlorobenzene, 1,4-dibromobenzene, 1,3-dichloro-4-hydroxybenzene, and biphenyls such as 2,2′-dichlorobiphenyl, polybrominated 1,4-diphenoxybenzene, 2,4′-dibromobiphenyl, and 2,4′-dichlorobiphenyl as well as decabromo diphenyl oxide, and the like.

Also useful are oligomeric and polymeric halogenated aromatic compounds, such as a copolycarbonate of bisphenol A and tetrabromobisphenol A and a carbonate precursor, e.g., phosgene. Metal synergists, e.g., antimony oxide, may also be used with the flame retardant. When present, halogen containing flame retardants can be present in amounts of 0.1 to 10 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Inorganic flame retardants may also be used, for example salts of C_2-16 alkyl sulfonate salts such as potassium perfluorobutane sulfonate (Rimar salt), potassium perfluoroctane sulfonate, tetraethylammonium perfluorohexane sulfonate, and potassium diphenylsulfone sulfonate, and the like; salts formed by reacting for example an alkali metal or alkaline earth metal (for example lithium, sodium, potassium, magnesium, calcium and barium salts) and an inorganic acid complex salt, for example, an oxo-anion, such as alkali metal and alkaline-earth metal salts of carbonic acid, such as Na₂CO₃, K₂CO₃, MgCO₃, CaCO₃, and BaCO₃ or fluoro-anion complexes such as Li₃AlF₆, BaSiF₆, KBF₄, K₃AlF₆, KAlF₄, K₂SiF₆, and/or Na₃AlF₆ or the like. When present, inorganic flame retardant salts can be present in amounts of 0.1 to 5 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Radiation stabilizers may also be present, specifically gamma-radiation stabilizers. Suitable gamma-radiation stabilizers include diols, such as ethylene glycol, propylene glycol, 1,3-propanediol, 1,2-butanediol, 1,4-butanediol, meso-2,3-butanediol, 1,2-pentanediol, 2,3-pentanediol, 1,4-pentanediol, 1,4-hexandiol, and the like; alicyclic alcohols such as 1,2-cyclopentanediol, 1,2-cyclohexanediol, and the like; branched acyclic diols such as 2,3-dimethyl-2,3-butanediol (pinacol), and the like, and polyols, as well as alkoxy-substituted cyclic or acyclic alkanes. Alkenols, with sites of unsaturation, are also a useful class of alcohols, examples of which include 4-methyl-4-penten-2-ol, 3-methyl-pentene-3-ol, 2-methyl-4-penten-2-ol, 2,4-dimethyl-4-pene-2-ol, and 9-decen-1-ol. Another class of suitable alcohols is the tertiary alcohols, which have at least one hydroxy substituted tertiary carbon. Examples of these include 2-methyl-2,4-pentanediol (hexylene glycol), 2-phenyl-2-butanol, 3-hydroxy-3-methyl-2-butanone, 2-phenyl-2-butanol, and the like, and cycoloaliphatic tertiary carbons such as 1-hydroxy-1-methyl-cyclohexane. Another class of suitable alcohols is hydroxymethyl aromatics, which have hydroxy substitution on a saturated carbon attached to an unsaturated carbon in an aromatic ring. The hydroxy substituted saturated carbon may be a methylol group (—CH₂OH) or it may be a member of a more complex hydrocarbon group such as would be the case with (—CR⁴HOH) or (—CR⁴₂OH) wherein R⁴ is a complex or a simple hydrocarbon. Specific hydroxy methyl aromatics may be benzhydrol, 1,3-benzenedimethanol, benzyl alcohol, 4-benzyloxy benzyl alcohol and benzyl benzyl alcohol. Specific alcohols are 2-methyl-2,4-pentanediol (also known as hexylene glycol), polyethylene glycol, and polypropylene glycol. When present, radiation stabilizers are typically used in amounts of 0.001 to 1 wt %, more specifically 0.01 to 0.5 wt %, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Anti-drip agents may also be used, for example a fibril forming or non-fibril forming fluoropolymer such as polytetrafluoroethylene (PTFE). The anti-drip agent may be encapsulated by a rigid copolymer as described above, for example styrene-acrylonitrile copolymer (SAN). PTFE encapsulated in SAN is known as TSAN. Encapsulated fluoropolymers may be made by polymerizing the encapsulating polymer in the presence of the fluoropolymer, for example an aqueous dispersion. TSAN may provide significant advantages over PTFE, in that TSAN may be more readily dispersed in the composition. A suitable TSAN may comprise, for example, 50 wt % PTFE and 50 wt % SAN, based on the total weight of the encapsulated fluoropolymer. The SAN may comprise, for example, 75 wt % styrene and 25 wt % acrylonitrile based on the total weight of the copolymer. Alternatively, the fluoropolymer may be pre-blended in some manner with a second polymer, such as for, example, an aromatic polycarbonate resin or SAN to form an agglomerated material for use as an anti-drip agent. Either method may be used to produce an encapsulated fluoropolymer. When present, antidrip agents can be used in amounts of 0.1 to 5 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

Non-limiting examples of processing aids that can be used include Doverlube® FL-599 (available from Dover Chemical Corporation), Polyoxyter® (available from Polychem Alloy Inc.), Glycolube P (available from Lonza Chemical Company), pentaerythritol tetrastearate, Metablen A-3000 (available from Mitsubishi Rayon), neopentyl glycol dibenzoate, and the like. When present, processing aids can be used in amounts of 0.001 to 1 percent by weight, based on the weight of the component (i) polycarbonate used in the thermoplastic composition.

The thermoplastic composition may be manufactured by methods generally available in the art, for example, in one embodiment, in one manner of proceeding, powdered polycarbonate, and any optional additive(s) are first blended, in a HENSCHEL-Mixer® high speed mixer. Other low shear processes including but not limited to hand mixing may also accomplish this blending. The blend is then fed into the throat of an extruder via a hopper. Alternatively, one or more of the components may be incorporated into the composition by feeding directly into the extruder at the throat and/or downstream through a sidestuffer. Additives may also be compounded into a masterbatch with a desired polymeric resin and fed into the extruder. The extruder is generally operated at a temperature higher than that necessary to cause the composition to flow. The extrudate is immediately quenched in a water batch and pelletized. The pellets, so prepared, when cutting the extrudate may be one-fourth inch long or less as desired. Such pellets may be used for subsequent molding, shaping, or forming.

In a specific embodiment, a method of preparing a thermoplastic article comprises melt combining a polycarbonate, and any optional additive(s), to form a thermoplastic composition. The melt combining can be done by extrusion. In an embodiment, the proportions of polycarbonate, and any optional additive(s) are selected such that the optical properties of the thermoplastic composition are maximized while mechanical performance is at a desirable level.

In a specific embodiment, the extruder is a twin-screw extruder. The extruder is typically operated at a temperature of 180 to 385°0 C., specifically 200 to 330° C., more specifically 220 to 300° C., wherein the die temperature may be different. The extruded thermoplastic composition is quenched in water and pelletized.

Shaped, formed, or molded articles comprising the thermoplastic compositions are also provided. The thermoplastic compositions may be molded into useful shaped articles by a variety of means such as injection molding, extrusion, rotational molding, blow molding and thermoforming. In a specific embodiment, molding is done by injection molding. Desirably, the thermoplastic composition has excellent mold filling capability and is useful to form articles such as, for example, optical media, including holographic storage media, thin-wall parts bottles, tubing, beakers, centrifuge tubes, pipettes, glucose meters, inhalers, syringes, dialysis fittings, sample vials, blood bags, petri dishes, spatulas, connectors, trocars, stopcocks, luer locks, Y-sites, catheters, oxygenator housings, trays, dental instruments, and the like.

The disclosure is further illustrated by the following non-limiting examples.

EXAMPLES

Example 1

BPA/HPHP Copolymer—5 wt % HPHP

A 500 mL Morton flask equipped with a mechanical stirrer, nitrogen bypass, reflux condenser, a tubular reactor, and a pH probe was charged with BPA (22.8 g, 0.1 moles), distilled water (100 mL), methylene chloride (100 mL), triethylamine (200 mL, and p-cumylphenol (0.64 g, ˜3 mol %). The tubular reactor effluent entered the Morton flask via a dip tube. The pH was adjusted to and maintained at 10.5 with 25 wt % aqueous NaOH as phosgene was added through the tube reactor at 0.75 g/min for 8 minutes at which time the phosgene flow rate was lowered to 0.41 g/min and HPHP stock solution was fed to the tube reactor. HPHP chloroformate production was accomplished using 5 tube mixing sections in series (each mixing section comprised a ¼″ o.d.×7″ long Ko-Flo® static mixer) with a flow rate of 20.0 g/min of HPHP stock solution (3.06 g of HPHP and 8.86 mL of triethylamine in 150 g of methylene chloride). The tube was operated under these conditions for 3 minutes in order to deliver 5 wt % HPHP (based on the weight of BPA) to the reaction vessel. After the required amount of HPHP was delivered, the HPHP feed solution was stopped and the phosgene flow rate was raised to 0.75 g/min for an additional 8 minutes. Then the polymer solution was separated from the brine and washed two times with 1N HCl and 3 times with DI water. The polymer solution was hot water crumbed in a blender and the polymer was filtered, washed with water, and dried in a vacuum oven at 110° C. overnight. Proton nmr analysis of the polymer showed complete incorporation of the HPHP. The copolymer Tg was 131.8° C. and the Mw was 45,200 (polystyrene standards). A compression molded film was transparent.

Example 2

BPA/HPHP Copolymer—10 wt % HPHP

A 500 mL Morton flask equipped with a mechanical stirrer, nitrogen bypass, reflux condenser, a tubular reactor, and a pH probe was charged with BPA (22.8 g, 0.1 moles), distilled water (83 mL), methylene chloride (103 mL), and p-cumylphenol (0.64 g, ˜3 mol %). The pH was adjusted to and maintained at 10.5 with 50 wt % aqueous NaOH. HPHP chloroformate production was accomplished using 5 tube mixing sections with a flow rate of 20.0 g/min of HPHP stock solution (6.0 g of HPHP and 11.9 mL of triethylamine in 285.3 g of methylene chloride). The tube was operated under these conditions for 6.3 minutes and accompanied by a phosgene flow of 1.55 g/min in order to deliver 10 wt % HPHP (2.53 g HPHP) to the reaction vessel. After the HPHP was delivered, the phosgene flow rate was lowered to 1.00 g/min for an additional 4.5 minutes. The polymer solution was separated from the brine and washed two times with 1N HCl and 3 times with DI water. The polymer solution was hot water crumbed in a blender and the polymer was filtered, washed with water, and dried in a vacuum oven at 110° C. overnight. Proton nmr analysis of the polymer showed complete incorporation of the HPHP. The copolymer Tg was 119.7° C. and the Mw was 44,478 (polystyrene standards). A compression molded film was transparent.

Example 3

BPI/HPHP Copolymer—5 wt % HPHP

A 500 mL Morton flask equipped with a mechanical stirrer, nitrogen bypass, reflux condenser, a tubular reactor, and a pH probe was charged with BPI (22.8 g, 0.07 moles), distilled water (83 mL), methylene chloride (103 mL), and p-cumylphenol (0.47 g, ˜3 mol %). The pH was adjusted to and maintained at 10.5 with 50 wt % aqueous NaOH. HPHP chloroformate production was accomplished using 5 tube mixing sections with a flow rate of 20.0 g/min of HPHP stock solution (6.0 g of HPHP and 11.9 mL of triethylamine in 285.3 g of methylene chloride). The tube was operated under these conditions for 3.0 minutes and accompanied by a phosgene flow of 1.55 g/min in order to deliver 5 wt % HPHP (1.2 g HPHP) to the reaction vessel. After the HPHP was delivered, the phosgene flow rate was lowered to 1.00 g/min for an additional 5.2 minutes. The polymer solution was separated from the brine and washed two times with 1N HCl and 3 times with DI water. The polymer solution was hot water crumbed in a blender and the polymer was filtered, washed with water, and dried in a vacuum oven at 110° C. overnight. Proton nmr analysis of the polymer showed complete incorporation of the HPHP. The copolymer Tg was 201.8° C. and the Mw was 52,847 (polystyrene standards). A compression molded film was transparent.

While typical embodiments have been set forth for the purpose of illustration, the foregoing descriptions should not be deemed to be a limitation on the scope herein. Accordingly, various modifications, adaptations, and alternatives may occur to one skilled in the art without departing from the spirit and scope herein.

Claims

1. A polycarbonate comprising repeating structural carbonate units of the formula (H-1):

2. The polycarbonate of claim 1, wherein the repeating structural carbonate units have a formula (H-3):

3. The polycarbonate of claim 1, further comprising repeating structural carbonate units of the formula (A-1):

4. The polycarbonate of claim 1, further comprising repeating structural carbonate units of the formula (A-2):

5. The polycarbonate of claim 1, further comprising repeating structural carbonate units of the-formula (A-3):

6. The polycarbonate of claim 1, further comprising repeating structural carbonate units of the formula (A-4):

7. The polycarbonate of claim 1, which has a weight average molecular weight (Mw) of from about 15,000 to about 100,000.

8. The polycarbonate of claim 3, which comprises: from about 0.1 wt % to about 40 wt % of repeating structural carbonate units of the formula (H-1); and from about 60 wt % to about 99.9 wt % of repeating structural carbonate units of the formula (A-1).

9. The polycarbonate of claim 8, which comprises: from about 2 wt % to about 20 wt % of repeating structural carbonate units of the formula (H-1); and from about 80 wt % to about 98 wt % of repeating structural carbonate units of the formula (A-1).

10. The polycarbonate of claim 9, which comprises: from about 3 wt % to about 10 wt % of repeating structural carbonate units of the formula (H-1); and from about 90 wt % to about 97 wt % of repeating structural carbonate units of the formula (A-1).

11. The polycarbonate of claim 8, wherein the repeating structural carbonate units of the formula (H-1) comprise a formula (H-3) unit:

12. The polycarbonate of claim 1, which comprises a copolyester-polycarbonate.

13. The polycarbonate of claim 12, wherein the polyester repeating units have a formula (6):

14. The polycarbonate of claim 1, which comprises a copolymer of polysiloxane-polycarbonate.

15. The polycarbonate of claim 1, in which the formula (H-1) unit is derived from a dihydroxy compound of formula (H-4):

16. The polycarbonate of claim 2, in which the formula (H-3) unit is derived from a dihydroxy compound of formula (H-5):

17. The polycarbonate of claim 2, in which the formula (H-3) unit is derived from a bischloroformate compound of formula (H-6):

18. A thermoplastic composition, which includes a polycarbonate comprising repeating structural carbonate units of the formula (H-1):

19. The thermoplastic composition of claim 18, in which the repeating structural carbonate units of the formula (H-1) comprise a formula (H-3) unit:

20. The thermoplastic composition of claim 18, further comprising one or more additives selected from the group consisting of hydrolysis stabilizer, impact modifier, filler/reinforcing agent, visual effect enhancer, antioxidant, heat stabilizer, light stabilizer, ultraviolet light absorber, plasticizer, mold release agent, lubricant, antistatic agent, pigment, dye, flame retardant, processing aid, radiation stabilizer, and anti-drip agent.

21. A thermally stable article made from the thermoplastic composition of claim 18.