The present invention relates to a thermo-optical waveguide switch which is formed on a substrate. The waveguide switch furthermore comprises a glass layer arranged on the substrate, a waveguide arranged in the glass layer, a heating strip arranged above the waveguide on the glass layer, and a cavity arranged below the waveguide.
Waveguide components serve for transmitting, modifying, regulating and controlling optical signals. Such elements are used in optical networks for the distribution or changeover of light signals between different light-guiding fiber paths. In a manner similar to that in the case of the light-guiding fiber for optical transmission on long paths, glasses based on silicon dioxide which are modified for example by admixtures of germanium oxide, phosphorus oxide or boron oxide are used in the case of planar-optical waveguide components. In this case, the planar-optical waveguide components are fabricated on a silicon substrate. This fabrication method is described for example in M. Kawachi, “Silica waveguide on silicon and their application to integrated-optic components”, Optical and Quantum Electronics 22 (1990), pp. 391-416 and H. W. Schneider, “Realisation of SiO2—B2O3—TiO2 Waveguides and Reflectors on Si Substrats”, in “Optical Waveguide Materials”, edited by M. M. Broer, R. T. Kersten, G. H. Sigel and H. Kawazoe, Materials Research Society Symposium Proceedings, vol. 244, 1992, pp. 337-342.
It has proved to be advantageous, for the purpose of electromagnetic field matching, to dimension the planar waveguide as similarly as possible to the light-guiding fiber in width, height and refractive index, in order that the coupling losses between light-guiding fiber and planar-optical waveguide are kept as small as possible.
In light-guiding fiber networks, it is necessary not only for light signals to be mixed or separated purely passively but also for said light signals to be changed over actively. The dielectric glass waveguides are initially not switchable owing to their small electro-optical coefficient. Actively controllable planar-optical waveguide components are attained, however, if the dependence of the refractive index on the temperature or on the pressure is utilized. A typical actively controllable optical component is the tunable Mach-Zehnder interferometer which is described in Theodor Tamir (ED.) “Guided-Wave Optoelectronics”, Springer-Verlag, Berlin, 1988, pp. 174-184. In this case, the input signal is split via a beam splitter (directional coupler or else Y hybrid) between the two arms of the interferometer and subsequently recombined. Depending on the phase angle ΔΦ=β·ΔL of the two light signals in the two arms of the interferometer, in the combiner constructive interference arises for ΔΦ=m·2π and destructive interference arises for ΔΦ=m·2π+π (mεZ). For constructive interference, the light signal passes to the output of the Mach-Zehnder interferometer and the output is active, and the output is inactive in the case of destructive interference.
The phase change ΔΦ required for the optical waveguide switch for switching purposes can be effected by a state change of the planar-optical waveguide, e.g. through a temperature change. The temperature change is accompanied both by a length change ΔL and by a change in the propagation constant Δβ, which both contribute to the change in the phase angle: ΔΦ=β·ΔL+L·Δβ or ΔΦ=β(dL/dT)·ΔT+L(dβ/dT)·ΔT.
The thermal length change is produced in accordance with the linear expansion coefficient α according to α=1/L·dL/dT, the change in the propagation constant on account of the thermo-optical effect dn/dT=2/2π·dβ/dT. In acousto-optical components, the phase angle is achieved by a pressure change ΔP.
In planar-optical waveguide components, the glass waveguide is usually situated in a silicon dioxide layer formed on a silicon substrate. In this case, there is an outstanding mechanical contact between the silicon dioxide layer and the silicon substrate, since the silicon dioxide layer is deposited or melted-on at relatively high temperatures. As a result, the waveguide structures acquire not only high optical transparency but also the required mechanical stability. However, the fixed mechanical coupling of the glass structure to the substrate has the effect that thermal implementing of the waveguide, which is intended to bring about a phase change ΔΦ in order that the Mach-Zehnder interferometer can be switched, is attenuated to a very great extent. This is due to the high thermal conductivity of the silicon substrate which dissipates the supplied heat very rapidly, something which leads to high heating powers and adversely affects the heating balance. In practice, particularly in the case of complex circuits, this leads to undesirable problems such as e.g. local overheating and necessitates additional cooling devices.
Therefore, Masayuki Okuno, Nori Takato, Tsutomu Kitoh, Akio Sugita, “Silica-Based Thermo-optic Switches”, NTT Review, vol. 7, no. 5, 1995, pp. 57-63, have already proposed unsupported SiO2 structures which are decoupled from the substrate and have been realized by underetching. These structures require smaller heating powers for the phase tuning, but are difficult to handle on account of their mechanical instability and fragility.
The object of the present invention is to specify a waveguide switch which has high mechanical stability and in which the required temperature change can be carried out with small heating powers. Furthermore, the object is to specify a corresponding fabrication method.
According to the invention, this object is achieved by means of the waveguide switch specified in claim 1. Claim 1 comprises: a waveguide switch having: a substrate; a glass layer arranged on the substrate; a waveguide arranged in the glass layer; a heating strip arranged above the waveguide on the glass layer; a cavity arranged at least partly below the waveguide, and at least two supports arranged in the cavity below the waveguide.
With regard to the method, the object set is achieved by means of the method specified in claim 3. In this case, a method is specified for fabricating a waveguide switch having the steps of: providing a substrate; covering the substrate with a glass layer; producing a hole arrangement in the glass layer, the substrate being at least partly uncovered; isotropically etching the substrate, so that at least one cavity is produced by at least partial underetching of the glass layer; covering the glass layer with a further glass layer, the cavity not being filled but rather being bridged; applying a first waveguide, so that the waveguide runs at least partly above the cavity.
As an alternative, the object set is achieved by means of the method specified in claim 5. In this case, a method is specified for fabricating a waveguide switch having the steps of: providing a substrate; forming a first glass layer on the substrate, a waveguide being formed in the glass layer; patterning the first glass layer, laterally beside the waveguide, isotropically etching the substrate, the first glass layer and thus the waveguide being partly underetched.
The present invention concerns the partial decoupling of the waveguide from the substrate. Thus, the waveguide can be influenced in its state by small thermal powers. At the same time, the required mechanical stability is preserved. To that end, hollow and solid segments are arranged alternately below the waveguide, so that the waveguide is, section by section, freely suspended and then linked to the substrate again.
In an advantageous design of the method according to the invention, the cavity is arranged not only below the first waveguide but also laterally beside the first waveguide. As a result, the first waveguide is thermally decoupled from the substrate to the greatest possible extent and it is even possible to arrange a heating strip not only above the first waveguide but also laterally beside the first waveguide. This procedure has the advantage that the waveguide can be thermally influenced intensively, from three sides.
Exemplary embodiments of the invention are illustrated and explained below with reference to the drawing.
In the figures:
A first variant of a fabrication method for a waveguide switch according to the invention will now be explained with reference to FIG. 4. Firstly a substrate 1 is provided. The substrate 1 is composed of silicon, for is example. A second glass layer 9 is deposited thereon, said layer being composed of silicon oxide, for example. The second glass layer 9 is typically a thermal oxide having a thickness of about 750 nm. In the region in which the waveguide is later formed, a hole arrangement 10 is produced in the second glass layer 9 by means of photolithography, the substrate 1 being at least partly uncovered. In this case, the distance between two holes of the hole arrangement 10 is expediently chosen to be significantly greater than the hole diameter of a hole. By way of example, a ratio of between 20:1 and 2:1 is chosen, ratio values around 5:1 being preferred.
With reference to
For the subsequent fabrication of the waveguide, a third glass layer 11 is deposited onto the second glass layer 9. The third glass layer 11 may be formed for example with a thickness of 20 μm and is composed of silicon dioxide, for example. For the deposition, use is made for example of flame hydrolysis, which proves to be particularly suitable since, owing to the particular deposition conditions, the hollow segments are not filled but rather bridged. Flame hydrolysis involves a diffusion of relatively large particles from the flame to the plate. The deposition of the third glass layer 11 closes off the cavity 5 in the substrate 1. The first waveguide 3 is then fabricated above the cavity 5 by the methods known from the prior art. Afterward, the resistance heating element required for the state change of the waveguide is formed e.g. as heating strip 4 e.g. made of chromium or gold above the first waveguide 3.
The fabrication of a further exemplary embodiment of a waveguide switch will now be described in connection with FIG. 6. Firstly a structure is produced in accordance with FIG. 2. To that end, a substrate 1 is provided which is usually composed of silicon. Afterward, as is already known from the prior art, a first glass layer 2 is formed with a first waveguide 3 and a second waveguide 8 on the substrate 1. For the control of the waveguide switch, a heating strip 4 is arranged above the first waveguide 3. With reference to
Number | Date | Country | Kind |
---|---|---|---|
199 58 899 | Dec 1999 | DE | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCTDE00/04112 | 11/22/2000 | WO | 00 | 7/15/2002 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO0142848 | 6/14/2001 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
4978188 | Kawachi et al. | Dec 1990 | A |
5467415 | Presby | Nov 1995 | A |
Number | Date | Country |
---|---|---|
0255 270 | Feb 1988 | EP |
0 444 582 | Sep 1991 | EP |
0 653 665 | May 1995 | EP |
1-158 413 | Jun 1989 | JP |