Claims
- 1. A thermo-shrinkable polyester type film which is obtained from a material selected from the group consisting of a polyester having a glass transition temperature of no less than 35.degree. C., a polyester copolymer having a glass transition temperature of no less than 35.degree. C., and a mixture of both of said polyester and polyester copolymer with at least one other polymer, wherein said film has the following shrinking properties:
- a shrinking ratio in the one axis is not less than 30% of 80.degree. C. and not less than 50% at 100.degree. C., and
- a shrinking ratio in perpendicular axis to the former axis is not more than 15% in the range of 55.degree.-105.degree. C., and the minimum value of the shrinking ratio occurs at a temperature in the range of 55.degree.-105.degree. C.; and
- having an orientation factor of not more than 100.times.10.sup.-3.
- 2. A thermo-shrinkable polyester type film according to claim 1, which is made of a polyester copolymer or the mixture thereof, wherein the polyester copolymer mainly contains an ester group of a dicarboxylic residue and a glycol residue, and contains one kind of an aromatic dicarboxylic residue in an amount of 30-90 mole % based on the total dicarboxylic residue.
- 3. A thermo-shrinkable polyester type film according to claim 1, which has the maximum thermo-shrink stress at 80.degree. C. of 0.95-5 kg/mm.sup.2, and the maximum thermo-shrink stress at 100.degree. C. of 1.0-5 kg/mm.sup.2.
- 4. A tube of a thermo-shrinkable polyester type film which has a jointed surface being jointed by at least one solvent or swelling agent having a solubility or swelling ability to a polyester and a solubility index of 8.0-13.8, and the following shrinking properties:
- a peripheral shrinking ratio is not less than 30% at 80.degree. C. and not less than 50% at 100.degree. C., and
- a longitudinal shrinking ratio is not more than 15% in the range of 55.degree.-105.degree. C., and the minimum value of the shrinking ratio occurs at a temperature in the range of 55.degree. to 105.degree. C.
- 5. . A tube of a thermo-shrinkable polyester type film according to claim 4, which is obtained from a material selected from the group consisting of a polyester having a glass transition temperature of not less than 35.degree. C., a polyester copolymer having a glass transition temperature of not less than 35.degree. C., and the mixture of both of said polyester and polyester copolymer with at least one other polymer, and has an orientation factor of not more than 100.times.10.sup.-3.
- 6. A tube of thermo-shrinkable polyester type film according to claim 4, which is made of a polyester copolymer or the mixture thereof, wherein the polyester copolymer mainly contains an ester group composed of a dicarboxylic residue and a glycol reside, and contains one kind of an aromatic dicarboxylic residue in an amount of 30-90 mole % based on the total dicarboxylic residue, and
- has an orientation factor of not more than 100.times.10.sup.-3.
- 7. A tube of thermo-shrinkable polyester type film according to claim 4, wherein the jointed surface is jointed by means of simply superposing one side of the film onto the another surface, applying a tape onto at least one surface of the film to joint the film, or butt-seam wherein resulting sealed portion is bent and adhered onto either surface of the tube.
- 8. A tube of thermo-shrinkable polyester type film according to claim 4, wherein the tube is jointed by at least one solvent or swelling agent having solubility Parameter of 8.0-13.8 selected from the group consisting of aromatic hydrocarbon, halogenated hydrocarbon, halogenated aromatic hydrocarbon, phenols, alcohols, nitrogen compound, ketones, ethers, esters, organic acids, inorganic acids, sulfur derivative and N',N'-dimethyl formamide.
- 9. A process for production of a tube from polyester type film which comprises:
- disposing a polyester type film having shrinking properties wherein a shrinking ratio in one axis is not less than 30% at 80.degree. C. and not less than 50% at 100.degree. C., and a shrinking ratio in a perpendicular axis to the former axis is not more than 15% in the range of 55.degree.-105.degree. C., and the minimum value of the shrinking ratio in the perpendicular axis occurs at a temperature in the range of 55.degree.-105.degree. C.,
- spreading at least one jointed surface of the film with a solvent or a swelling agent having a solubility or swelling ability to a polyester and a solubility parameter or 8.0-13.8, and
- jointing the surfaces to be jointed to give a tubular film before the solvent or swelling agent is dried.
- 10. A process according to claim 9, wherein the polyester type film is obtained from a material selected from the group consisting of a polyester having a glass transition temperature of not less than 35.degree. C., a polyester copolymer having a glass transition temperature of not less than 35.degree. C., and the mixture of both of said polyester and polyester copolymer with at least one other polymer, and has an orientation factor of not more than 100.times.10.sup.-3.
- 11. A process according to claim 9, wherein the film is jointed by using a solvent or a swelling agent selected from the group consisting of halogenated hydrocarbon and ethers.
- 12. A process according to claim 9, wherein the film is jointed at a temperature of not higher than 70.degree. C.
- 13. A process for production of a tube from polyester type film which comprises:
- disposing a polyester type film having shrinking properties wherein a shrinking ratio in one axis is not less than 30% at 80.degree. C. and not less than 50% at 100.degree. C., and a shrinking ratio in a perpendicular axis to the former axis is not more than 15% in the range of 55.degree.-105.degree.C., and the minimum value of the shrinking ratio in the perpendicular axis occurs at a temperature in the range of 55.degree.-105.degree. C.,
- disposing an adhesive layer on entire or part of at least one surface to be jointed,
- spreading at least one surface with a solvent or a swelling agent having a solubility or swelling ability to a polyester and a solubility parameter of 8.0-13.8, and
- jointing the surfaces to be jointed to give a tubular film before the solvent or swelling agent is dried.
- 14. A process according to claim 13, wherein the polyester type film is obtained from a material selected from the group consisting of a polyester having a glass transition temperature of not less than 35.degree. C., a polyester copolymer having a glass transition temperature of not less than 35.degree. C., and the mixture of both of said polyester and polyester copolymer with at least one other polymer, and has an orientation factor coefficient of surface orientation of not more than 100.times.10.sup.-1.
Priority Claims (4)
Number |
Date |
Country |
Kind |
60-170135 |
Jul 1985 |
JPX |
|
60-171476 |
Aug 1985 |
JPX |
|
60-233958 |
Oct 1985 |
JPX |
|
60-233959 |
Oct 1985 |
JPX |
|
Parent Case Info
This application is a continuation-in-part application Ser. No. 890,368 filed July 29, 1986, now abandoned.
US Referenced Citations (7)
Foreign Referenced Citations (1)
Number |
Date |
Country |
1187742 |
Feb 1965 |
DEX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
890368 |
Jul 1986 |
|