Thermochemical gas reduction process using poly-cation oxide

Abstract

A two-step thermochemical gas reduction process based on poly-cation oxides includes repeatedly cycling a thermal reduction step and a gas reduction step. In the thermal reduction the poly-cation oxide is heated to produce a reduced poly-cation oxide and oxygen. In the gas reduction step, the reduced poly-cation oxide is reacted with a gas to reduce the gas, while reoxidizing the poly-cation oxide. The poly-cation oxide has at least two distinct crystal structures at two distinct temperatures and is capable of undergoing a reversible phase transformation between the two distinct crystal structures. For example, the poly-cation oxide may be an entropy tuned mixed metal oxide, such as an entropy stabilized mixed metal oxide, where the entropy-tuning is achieved via change in crystal structure of one of more of the compounds involved. The gas reduction process may be used for water splitting, CO2 splitting, NOx reduction, and other gas reduction processes.

Description

FIELD OF THE INVENTION

The present invention relates generally to gas reduction processes using thermochemical redox reactions. More specifically, it relates to improvements to metal-oxide-based thermochemical redox reactions.

BACKGROUND OF THE INVENTION

Metal-oxide-based thermochemical redox reactions have many applications, including water splitting and carbon dioxide splitting for production of hydrogen fuel and/or carbon monoxide precursors for syngas. For example, a two-step thermochemical splitting of H₂O or CO₂ using metal oxide based redox reactions can be used to produce H₂ or CO, respectively. In a first step, metal oxides are reduced at high temperature, producing oxygen gas. In a second step, H₂O or CO₂ is reduced while the metal oxide is oxidized. The metal oxide then repeats the cycle. The thermodynamic cycle is essentially a redox heat engine.

The most significant barrier for commercialization of current metal-oxide-based thermochemical redox reactions is the requirement of high operation temperatures and high expense that does not allow economies of scale. For example, existing metal oxide-based redox materials such as substituted ceria, two-metal ferrites, and perovskite oxides require temperatures 1300° C. to 1400° C., since they do not produce useful amounts of H₂ at thermal reduction temperatures (T_H) less than 1100° C. This high temperature requirement is a critical limitation for industrial applications because today's chemical infrastructure relies almost exclusively on thermochemical transformations in the regime less than 1100° C. Operating at higher temperatures causes serious material compatibility issues in practice. Thus, it would be an important and valuable advance to overcome these existing problems with the state of the art.

BRIEF SUMMARY OF THE INVENTION

The present invention provides effective and reliable methods for thermochemical redox reactions that can yield desired chemical products using process temperatures below 1300 C. In contrast with existing approaches, the invention has lower operation temperatures and can use powder materials, making the technology practical for industrial applications. It also has economy of scale, i.e., the cost goes down with increasing production scale.

Embodiments of the invention provide thermochemical redox reactions that make use of new poly-cation oxide materials, such as high-entropy mixed metal oxides, that have a large entropy change associated with a phase transformation.

Advantageously, the large entropy change associated with a reversible phase transformation in these new materials allow various thermochemical redox reactions to be performed at operation temperatures below 1300 C, which is significantly lower than that possible with existing metal oxide-based redox materials. Despite the lower operation temperatures, these poly-cation oxide materials show fast oxygen release kinetics, comparable to those of state-of-the-art materials such as ceria at higher temperatures. In fact, below certain temperatures, state-of-the-art materials such as ceria are thermodynamically prohibited to perform gas splitting, whereas the poly-cation oxide materials are not. In addition to maintaining high reaction rates, these poly-cation oxide materials also have high oxygen release capacity even at lowered operation temperatures. Also, conventional industrial thermochemical systems may be used to implement the process at large scales. In addition, the poly-cation oxide materials may be in a powder form, which has an advantage that the process can be easily scaled up volumetrically, so it may benefit from economies of scale.

In one aspect, the invention provides a two-step thermochemical gas reduction process comprising repeatedly cycling a thermal reduction step and a gas reduction step. The thermal reduction step includes heating a poly-cation oxide (MeO_x) under a reduced partial oxygen pressure to produce a reduced poly-cation oxide (MeO_x-1) and oxygen gas (O₂). The gas reduction step includes reacting the reduced poly-cation oxide (MeO_x-1) with a first gas to produce a second gas and reoxidized poly-cation oxide (MeO_x), where the first gas is reduced into the second gas. The poly-cation oxide used in the process has at least two distinct crystal structures at two distinct temperatures corresponding to two distinct average oxidation states of at least one transition metal in a transformation between MeO_x and MeO_x-1, and is capable of undergoing a reversible phase transformation between the two distinct crystal structures. For example, the poly-cation oxide may be an entropy tuned mixed metal oxide, such as an entropy stabilized mixed metal oxide, where the entropy-tuning is achieved via change in crystal structure of one of more of the compounds involved. The mixed metal oxide (MeO_x) may be a mixed metal oxide (Me₁O, . . . , Me_nO)O_x, i.e., a mixture of multiple metal oxides Me₁O, . . . , Me_nO, e.g., an equimolar mixture of MgO, CoO, NiO, FeO and ZnO.

In one implementation, the gas reduction process may be a water splitting process for hydrogen gas production, where the gas reduction step is a water splitting step, where the first gas is water vapor and the second gas is hydrogen gas. In another implementation, the gas reduction process is a CO₂ splitting process for CO gas production, where the gas reduction step is a CO₂ splitting step, where the first gas is CO₂ and the second gas is CO. In another implementation, the gas reduction process is a NO_x reduction process for N₂ gas production, where the gas reduction step is a NO_x reduction step, where the first gas is NO_x and the second gas is N₂.

Applications include syngas production by combining water splitting for hydrogen production and reduction of carbon dioxide to carbon monoxide. Applications also include various chemical looping reactions for hydrocarbon fuel production, and thermal energy storage.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

FIGS. 1A-C are schematic diagrams illustrating a two-step thermochemical gas reduction process according to embodiments of the invention.

FIGS. 2A-F are graphs illustrating experimental results of thermochemical water splitting performance of poly-cation oxides (PCOs) compared with that of ceria and ferrites.

FIGS. 3A-D are graphs illustrating results of experiments on the influence of background gas environment and composition stoichiometry on the performance of poly-cation oxides which may be used in embodiments of the invention.

FIGS. 4A-D are experimental graphs showing results of structural and elemental characterizations of solid-state synthesized samples of a poly-cation oxide which may be used in embodiments of the invention.

DETAILED DESCRIPTION OF THE INVENTION

FIGS. 1A-B are schematic diagrams illustrating a two-step thermochemical gas reduction process according to embodiments of the invention. The process involves repeatedly cycling a thermal reduction step and a gas reduction step. In the first step 100 of this cycle, poly-cation oxide (MeO_x) is reduced by heating it at a high temperature T_H and under reduced oxygen partial pressure (p(O₂)), producing a reduced poly-cation oxide (MeO_x-1) and releasing O₂,

MeO_x→MeO_x-d+δ/2 O₂

where Me represents a poly-cation (i.e., a group of cations). In the second step 102, the reduced poly-cation oxide (MeO_x-d) is reacted at lower temperature T_L with a first gas to reduce the gas, producing a second gas and reoxidized poly-cation oxide (MeO_x).

A key feature of the process is the use of a poly-cation oxide that has two distinct crystal structures at the two distinct temperatures T_H and T_L. These crystal structures correspond to two distinct average oxidation states, MeO_x and MeO_x-d. The poly-cation oxide is capable of undergoing a reversible phase transformation between these two distinct crystal structures. In some embodiments, the poly-cation oxide may be an entropy tuned mixed metal oxide, such as an entropy stabilized mixed metal oxide, where the entropy-tuning is achieved via change in crystal structure of one of more of the compounds involved. In specific implementations, the mixed metal oxide (MeO_x) may be a mixed metal oxide of the form (Me₁O, . . . , Me_nO)O_x, i.e., a mixture of multiple metal oxides Me₁O, . . . , Me_nO. For example, the poly-cation oxide may be an equimolar mixture of MgO, CoO, NiO, FeO and ZnO.

As shown in FIG. 1B, the gas reduction step 102 may be used to reduce various different gasses, for example, the reduction of H₂O to H₂ (i.e., water splitting), the reduction of CO₂ gas to CO (i.e., carbon dioxide splitting), or the reduction of NO_x to N₂:

MeO_x-1+H₂O→MeO_x+H₂

MeO_x-1+CO₂→MeO_x+CO

or

MeO_x-y+NO_y→MeO_x+½N₂.

For purposes of illustration, the process will now be described in detail for the case of water splitting.

Using the new poly-cation oxides (PCOs) the two-step process thermochemically splits water to produce hydrogen and oxygen. For the PCO (FeMgCoNi)O_x, the process produces hydrogen yields of 11.96±0.15 mL-H₂/g and 3.65±0.15 mL-H₂/g at thermal reduction temperatures 1300° C. and 1100° C., respectively, even in the presence of background hydrogen. Remarkably, these capacities are significantly higher than those measured using state-of-the-art materials such as substituted ceria and two-metal ferrites.

In order to be commercially feasible, a thermochemical water splitting process should have large O₂ production at T_H; high H₂O-to-H₂ conversion at T_L; and long-lasting resuse of the reactor and the redox material. To lower T_H while maximizing H₂O-to-H₂ conversion, the partial molar enthalpy and entropy (ΔH_O and ΔS_O, respectively) of the redox oxide should fall within a narrow window of thermodynamic feasibility defined by negative Gibbs free energy changes (ΔG <0) for the reactions at T_H and T_L. For existing metal oxides (such as ceria, substituted ceria, and Co and Ni-substituted ferrites), the ΔH_O and ΔS_O fall in this window and provide useful H₂ production only when T_H ≥1400° C. and p(O₂)=10⁻⁵ atm. However, the use of industrial reactors with cost-effective materials requires lower temperatures of T_H ≤1100° C. and preferably <1000° C. These limitations motivated the present inventors to search for new materials that could evolve O₂ at a lower T_H and split water in the presence of background H₂.

The inventors found that some recently discovered oxides—entropy stabilized oxides (ESOs)—could be used in thermochemical redox reactions. These ESOs exchange oxygen via a reversible solid-solid phase transition. Equimolar quantities of multiple metal oxides (MgO, CoO, NiO, CuO and ZnO) of various crystal structures are mixed and heated them up to 1000° C. in air. The entropy of mixing of the large number of cations stabilizes the complex oxide, denoted as (MgCoNiCuZn)O, within only one rocksalt structure, during which the oxide loses some oxygen to the environment. At lower temperatures, this ESO undergoes phase separation into rocksalt and tenorite structures also by entropic driving force. Meanwhile, oxygen is absorbed from the environment.

In embodiments of the invention, ESO mixed metal oxide materials may be obtained by initially mixing N (2≤N≤6) binary metal oxides (MeO) with the equimolar concentrations and sintering them at a temperature between 1000 C and 1300 C. In the course of the heating process, entropic driving force leads to a reversible phase transformation of the materials from a low entropy multi-phase to high entropy single-phase state. This reversible phase transformation enables designing materials with a large entropy swing between two temperatures, which can give high product yield capacity at moderate temperatures in two-step thermochemical redox reactions. For example, we have demonstrated that a high-entropy mixed metal oxide with the composition (Mg,Ni,Co,Zn,Fe)O gives significant and reversible hydrogen production via two-step thermochemical water splitting reactions between 1200 C and 700 C. Significantly, the oxygen release kinetics at 1200 C is extremely fast, comparable to the state-of-the-art materials such as ceria, suggesting rapid oxygen transport characteristics previously found primarily in non-phase-change materials. This is the first demonstration of water splitting in this new class of material.

Inspired by ESOs, the inventors have expanded the idea of cation mixing to a broader class of materials, poly-cation oxides (PCOs), and shown that these provide unexpected advantages in two-step thermochemical water splitting, and thermochemical redox reactions in general. A PCO has three or more metal cations distributed between two different solid phases (e.g., rocksalt and spinel) whose ratio can swing during oxygen exchange cycles between T_H and T_L. Unlike ESOs, however, PCOs need not undergo a complete transition to a single phase, but instead contain a mixture of phases whose fractions swing between T_H and T_L, and is accompanied by oxygen exchange.

Examples of PCOs that display TWS capabilities include (MgFeCoNi)_0.8Li_0.1Ga_0.1O_x, (LiMgFeCoNi)O_x, (MgAlFeCoNi)O_x, (MgTiMnCoNi)_0.75Fe_0.25O_x, (MgMnCoNi)_0.75Fe_0.25O_x, (MgFeCoNiZn)O_{x, and} (MgFeCoNiCe)O_x (CoNi)_0.65Fe_0.35O_x. Compositions in parenthesis correspond to equimolar concentrations. These materials may be prepared by the solid-state method.

FIG. 1C is a schematic of two-step thermochemical water splitting (TWS) process using poly-cation oxides (PCOs) of the present invention. In two-step TWS, an ESO metal oxide (MeO_x) becomes thermally-reduced at a higher temperature, T_H, and releases O₂ to produce MeO_y (y<x). The reduced oxide is cooled to a lower temperature, T_L, where it is oxidized by water to produce H₂ as it returns to MeO_x. The mixed metal oxide undergoes a reversible phase transformation between two crystal structures corresponding to the two oxidation states. Using PCOs, a reversible phase swing between rocksalt (reduced) 110 and spinel (oxidized) 112 phases occurs during thermochemical cycling. The rocksalt-to-spinel ratio becomes larger in a PCO at T_H compared to that at T_L.

PCOs and ferrites may be synthesized using solid-state (SS) or sol-gel (SG) techniques. As an illustration, following is a method of solid state synthesis of an example PCO, (FeMgCoNi)O_x. All reagents were used without further purification treatment. For the solid-state (SS) synthesis, reagents in powder forms were mixed. To synthesize (FeMgCoNi)O_x, magnesium oxide (99.99%, Sigma-Aldrich), iron (II,III) oxide (99.997%, Alfa Aesar), cobalt (II,III) oxide (99.7%, Alfa Aesar) and nickel (II) oxide (99.99%, Sigma-Aldrich) with equimolar of cations were mixed for 1 min at 2000 rpm in a Vortex Mixer. The mixture was then transferred into an agate mortar and ground in acetone for 2 min. Calcinations were sequentially performed at 1000° C. and 1350° C. for 4 hours each (3° C./min between them), before a final cooling at 6° C./min to 500° C. and a natural cooling thereafter. The sintered sample chunk was then broken and sieved (Fisherbrand stainless steel sieves) into 0.5˜1.0 mm pieces (for TGA) or 1.0˜2.0 mm pieces (for stagnation flow reactor).

Alternative, following is a sol-gel synthesis method. This synthesis method gives smaller particle size and bigger surface area than solid-state synthesis. For (FeMgCoNi)O_x, magnesium nitrate hexahydrate (99%, Sigma-Aldrich), iron(III) nitrate nonahydrate (≥98%, Sigma-Aldrich), cobalt(II) nitrate hexahydrate (≥98%, Sigma-Aldrich) and nickel(II) nitrate hexahydrate (crystalline, Sigma-Aldrich) with equimolar cations were dissolved in DI water with precursors:water=1:4 in mass. EDTA (ethylenediamine tetraacetic acid, ACS, MP Biomedicals) and citric acid (≥99.5%, Sigma-Aldrich) were added to the solution with 60% and 75% the total amount of metal ions, respectively. With 300 rpm stirring, ammonium hydroxide solution (28%-30%, Fisher Chemical) was added until pH=11, and a dark solution formed. The resulting solution was stirred and heated on a hot plate at 200° C. for about 5 hrs (gelation). The spin bar was removed and the temperature was increased to 300° C. to dry the gel overnight, during which foaming happened and gel became almost solid. The beaker was then moved to a box furnace and heated at 300° C. for 1 hr. The sample was ground into powder, transferred to an alumina boat and went through the following calcination: 10° C./min until 800° C. and 5° C./min until 1100° C. (1000° C. for T_H=1000° C.), 5° C./min until 800° C. and then natural cooling. For T_H=1000° C. TWS experiments, the maximum calcination temperature was 1000° C. instead of 1100° C. Besides, graphite (<150 μm, powder, 99.99%, Sigma-Aldrich) and 300° C. heated PCO with mass ratio 2:5 was ground with pestle in mortar before treatment at 1000° C.; acetone was used to help mixing.

To test two-step TWS yields with the PCO materials, a custom thermogravimetric analyzer (TGA) setup connected to an oxygen sensor was used. Because the reaction rate in the TGA is limited by the temperature ramp rate and the gas flow rate and dynamics, a stagnation flow reactor with a mass spectrometer was also used as validation and to measure kinetics and directly quantify H₂ production.

FIGS. 2A, 2B, 2C, 2D, 2E, 2F illustrate thermochemical water splitting performance of poly-cation oxides (PCOs) Fe_0.35(MgCoNi)_0.65O_x and (FeMgCoNi)O_x, compared with that of ceria (CeO₂) and ferrites, using a custom-built stagnation flow reactor.

FIG. 2A and FIG. 2B show the measured H₂ yields of the both SS and SG-synthesized PCOs [Fe_0.35(MgCoNi)_0.65O_x and (FeMgCoNi)O_x] as well as nickel ferrite (SS, SG), cobalt ferrite (SS, SG) and CeO₂ (as-received, ‘AR’) at three different TWS conditions, namely: (1) T_H=1300° C. and T_L=800° C.; (2) T_H=1100° C. and T_L=600° C.; (3) T_H=1000° C. and T_L=500° C. These measurements involved 30 mins at T_H for O₂ evolution and 1 hour at T_L for H₂ evolution. During the thermal reduction step at T_H, Ar was flowed to maintain p(O₂)˜10 ppm (5 to 20 ppm), while 91 ppm of background H₂ and 9.5% H₂O (equivalently, p(H₂):p(H₂O)=1:1044) was used for the water splitting step at T_L. This gas composition at T_L emulates the H₂ concentration that would be present in a realistic reactor and sets the equilibrium between the metal oxide and a well-defined H₂:H₂O (abbreviation for p(H₂):p(H₂O)) ratio. FIG. 2A shows that at T_H=1300° C. and T_L=800° C., PCOs yield more than twice H₂ compared to ceria or two-metal ferrites. The performance of sol-gel (SG) synthesized samples is marginally higher than that of solid-state (SS) synthesized ones. The measured value for CeO₂ is close to its thermodynamic limit of 1.41 mL-H₂/g. The measured H₂ yield for CeO₂ in FIG. 2A is close to the thermodynamic H₂ production limit of 1.41 mL/g. FIG. 2B shows that at T_H=1100° C. and T_L=600° C., SG synthesized PCOs yield ˜1.5 mL-H₂/g, whereas ferrites and CeO₂ (as-received, ‘AR’; thermodynamic limit, ‘Limit’) yield almost no H₂; SG synthesis nearly doubles the H₂ production of PCOs compared to that of SS synthesized samples. At T_H=1000° C. and T_L=500° C., only PCOs produce reasonable H₂ yield, whereas ferrites and CeO₂ cannot split water because they are thermodynamically prohibited. The experimental H₂ production for CeO₂ cycled between 1100° C. and 600° C. (FIG. 2B) was below the detection limit, which is also consistent with the thermodynamic limit (0.16 mL/g) considering the TGA detection uncertainty (±0.15 mL/g). At T_H=1300° C. and T_L=800° C., the H₂ yields of the PCOs are above two times higher than that of ferrites and significantly above the thermodynamic limit for CeO₂. Additionally, at T_H=1100° C. and T_L=600° C., when ferrites and CeO₂ almost stop producing H₂, PCOs exhibit an even larger advantage. Remarkably, SG-synthesized (FeMgCoNi)O_x is still able to produce reasonable H₂ yields (˜0.70±0.15 mL/g) at reaction temperatures as low as T_H=1000° C. and T_L=500° C., a regime where ferrites and ceria are either thermodynamically prohibited or do not produce appreciable H₂.

FIG. 2C shows ten cycles of H₂ production using SG-synthesized Fe_0.35(MgCoNi)_0.65O_x. FIG. 2C shows that SG-synthesized Fe_0.35(MgCoNi)_0.65O_x produces less H₂ in the second cycle compared to the first, but shows no noticeable performance degradation during the following 9 cycles. Hence, all data in FIG. 2A and FIG. 2B used the measurements from the second thermochemical cycle. The SG-synthesized samples, with particles sizes around 1-10 μm, generally result in higher H₂ yield than that of the SS-synthesized ones with particle sizes in the 10-100 μm range. This suggests that the larger surface area helps the TWS reaction yield, thus offering the potential to further improve the H₂ yield in the future via morphology control.

FIG. 2D shows Kinetics of a typical two-step TWS cycle in a stagnation flow reactor for Fe_0.35(MgCoNi)_0.65O_x at T_H=1300° C. and T_L=800° C. under H₂:H₂O ratio of 10⁻³. Thermal reduction kinetics (O₂ production) are faster than water splitting (H₂ production). For the measurements in FIGS. 2A-D, the samples were held at T_H for 30 minutes and at T_L for 1 hour. Cycles carried out in the stagnation flow reactor show H₂ productivity (FIG. 2D) of SS-synthesized Fe_0.35(MgCoNi)_0.65O_x and (FeMgCoNi)O_x consistent with the TGA evaluation based on the sample mass change. Thermal reduction at T_H=1300° C. is significantly faster than water splitting at T_L=800° C., with background H₂:H₂O=1:1000. The peak rates of 0.89 mL/min/g O₂ and 0.67 mL/min/g H₂ in FIG. 2D for Fe_0.35(MgCoNi)_0.65O_x are promising, considering that the sample morphology used in these kinetic experiments (solid-state synthesized) was not optimized.

FIG. 2E shows that long cycle (5 hrs thermal reduction at T_H=1300° C.+10 hrs water splitting at T_L=800° C.) results with SG-synthesized samples. Fe_0.35(MgCoNi)_0.65O_x gives the H₂ yield of as high as 15.30±0.15 mL/g, which is higher than the thermodynamic limits of both ferrites and CeO₂. This value is 27.4% of its “redox limit”, defined by assuming all Fe goes through +2/+3 redox swing. Such normalization by Fe redox limit is shown as “Normalized Yield”. FIG. 2F shows that long cycle (5 hrs thermal reduction at T_H=1100° C.+10 hrs water splitting at T_L=600° C.) results with SG synthesized samples. (FeMgCoNi)O_x yields 2.64±0.15 mL-H₂/g. The diamond indicates (FeMgCoNi)O_x yields 3.65±0.15 mL-H₂/g from an even longer cycle of 10 hrs at T_H=1100° C. and 20 hrs at T_L=600° C.

All results in FIGS. 2A-F were obtained using the TGA reactor except for the data in FIG. 2D. In the TGA reactor, thermal reduction at T_H was achieved in ˜10 ppm background O₂ whereas water splitting at T_L was achieved in 91 ppm background H₂ and 9.5% H₂O (balance gas Ar). The uncertainty in the H₂ yield due to thermal mass noise of TGA is ±0.15 mL-H₂/g, and the scatter from repeatability tests in the TGA is ±0.10 mL-H₂/g.

Assuming full redox conversion between Fe²⁺ and Fe³⁺, the H₂ production capacity of Fe-based oxides would correspond to 0.5 mol of H₂ per 1 mol of Fe. We call such capacity the “redox limit”. Nickel ferrite (NiFe₂O₄), for example, has a redox limit of 95.6 mL-H₂/g, an order of magnitude higher than the experimental yields. The redox limits of Fe_0.35(MgCoNi)_0.65O_x (x≈1.25) and (FeMgCoNi)O_x (x≈1.21) are estimated to be 55.8 mL-H₂/g and 40.7 mL-H₂/g, respectively. Values of x were determined assuming Fe is +3, Co is a mixture of +2 and +3 (in the form of Co₃O₄), and Mg and Ni are +2, according to the X-ray absorption near-edge structure (XANES) results. Long two-step TWS cycles with a high purge gas flow rate (200 sccm Ar) were conducted in the TGA in an attempt to approach the thermodynamic limits of PCOs with the help of faster gas phase transport and a longer reaction time. As shown in FIG. 2E, at T_H=1300° C. (5 hrs) and T_L=800° C. (10 hrs) and H₂:H₂O=1:1044, the PCO Fe_0.35(MgCoNi)_0.65O_x yields 15.30±0.15 mL-H₂/g, which is 27.4% (normalized yield) of its redox limit; the PCO (FeMgCoNi)O_x gives 11.96±0.15 mL-H₂/g, 29.5% of its redox limit. In FIG. 2F, T_H=1100° C. (5 hrs) and T_L=600° C. (10 hrs) and H₂:H₂O=1:1044, PCOs show more than twice of the normalized yields from ferrites. With an even longer dwell time (10 hrs thermal reduction and 20 hrs water splitting), (FeMgCoNi)O_x gives 3.65±0.15 mL-H₂/g. For comparison, we also carried out the long cycle tests for the conventional ferrite materials. Extending reaction time increases their H₂ yields, shown in FIG. 2E and FIG. 2F, though still significantly less than PCOs. These results suggest that the redox activity of Fe in PCOs is enhanced presumably due to cation mixing effect.

FIGS. 3A-D illustrate results of experiments on the influence of background gas environment and composition stoichiometry on the performance of poly-cation oxides (PCOs). Specifically, these figures show the influence of background partial pressure ratio of H₂ and H₂O [p(H₂):p(H₂O)] on thermochemical water splitting of sol-gel (SG) synthesized PCOs, compared to ceria, perovskite LSM30 (La_0.7Sr_0.3MnO_3-δ), perovskite LSM40 (La_0.6Sr_0.4MnO_3-δ) (all calculated from thermodynamic data, indicated by *) and SG-synthesized ferrites for T_H=1300° C., T_L=800° C. (FIG. 3A), and for T_H=1100° C., T_L=600° C. (FIG. 3B).

FIG. 3A shows the H₂ yield of Fe_0.35(MgCoNi)_0.65O_x at T_H=1300° C. and T_L=800° C. and at various ratios of background H₂:H₂O values compared to that of ferrites, the thermodynamic limits of ceria, and perovskites such as LSM30 (La_0.7Sr_0.3MnO_3-δ). LSM30, along with LSM40 and LSM50 (not shown), thermodynamically produces less H₂ than PCOs within the H₂:H₂O range considered, and the H₂ production of LSMs decays quickly to zero as H₂:H₂O increases above around 1:300. On the other hand, PCOs display a similar decaying behavior as ferrites when H₂:H₂O increases, and with much higher H₂ yield. CeO₂ is only weakly affected by H₂:H₂O, though the negligible extent of reduction at 1300° C. and even more so at 1100° C. renders the cycle ineffective. We note the prior work on perovskites that reported water splitting did not use a background H₂ and relied on a large flow rate of water vapor to suppress the reverse reaction, which operates in the regime of vanishing H₂:H₂O ratio. FIG. 3B shows the same trend at the cycle condition T_H=1100° C. and T_L=600° C., where the PCOs demonstrate even bigger advantage. LSMs thermodynamically cannot produce H₂ at such condition within the H₂O range considered. Such trends prove that PCOs can split water at substantially higher steam-to-H₂ conversion than ceria, ferrites and Mn-based perovskites, which has practical significance in scale-up.

We found that the active redox partner in the PCOs is Fe. In FIG. 3C and FIG. 3D are shown the influence of Fe and Co stoichiometry on thermochemical water splitting performance of solid-state (SS) synthesized PCOs [T_H=1300° C., T_L=800° C. and p(H₂):p(H₂O)=1:1044]. At y=0.35, Fe_y(MgCoNi)_1-yO_x is shown to have the best performance. At w=0.22, Fe_0.35Co_w(MgNi)_1-wO_x outperforms the other w values. For all the measurements, samples were held at T_H for 30 minutes and at T_L for 1 hour. For SS-synthesized Fe_y(MgCoNi)_1-yO_x, we found the optimal y=0.30˜0.35, which maximizes the H₂ yield. We hypothesize that if the Fe molar ratio is too low, the available amount of redox element per unit mass of oxide is limited; but if the Fe molar ratio is too high, the cation mixing effect is likely to be weakened, as if approaching the ferrite stoichiometry. Starting from Fe_0.35(MgCoNi)_0.65O_x, the influence of Co ratio was further investigated (FIG. 3D). Deviating from the equimolarity of Co, Mg and Ni lowers the H₂ yield.

FIGS. 4A-D shows results of structural and elemental characterizations of solid-state synthesized samples of (FeMgCoNi)O_x. FIG. 4A shows Cu Kα X-ray diffraction (XRD) of thermally reduced and water-oxidized (FeMgCoNi)O_x. The change of peak intensity qualitatively illustrates the rocksalt-spinel phase swing in this oxide. FIG. 4B shows Rietveld refinement result of XRD patterns at various quenching conditions. Two sets of (FeMgCoNi)O_x were made by solid-state synthesis and quenched at four different temperature/gas conditions as indicated. Refinement result of each set is shown with one shape/color of data points. Both sets show similar trend of phase ratio change repeatedly. Increased reduction of the PCO leads to higher rocksalt (volumetric) ratio. FIG. 4C shows x-ray absorption near edge structure (XANES) result for the Fe edge of quenched (FeMgCoNi)O_x. The dashed lines indicate reference data of different iron oxides with different oxidation states of Fe. Oxidation state of Fe in the PCO sample is close to +3. The shift of Fe oxidation state is clearly demonstrated between the oxidized and reduced states of (FeMgCoNi)O_x. FIG. 4D shows amount of edge shift (eV) for Fe, Co, and Ni between the reduced and oxidized states of (FeMgCoNi)O_x measured by XANES. Fe is the redox-active cation in this PCO, as Co and Ni have almost no edge shift during the redox cycle. Labels “800° C., Ar+H₂O” indicates the water splitting condition, where there was no H₂ background (different from TGA and stagnation flow reactors); “1300° C., Ar” indicates the thermal reduction condition. This PCO was quenched from these conditions before being characterized.

In order to elucidate the redox reaction mechanism of (FeMgCoNi)O_x during two-step TWS, quenching experiments were performed, assuming sample structure and property are maintained when quenched at the end of thermal reduction or water splitting reaction. The X-ray diffraction (XRD) results in FIG. 4A on the quenched (FeMgCoNi)O_x samples confirm that both rocksalt and spinel phases co-exist during thermal cycling, but their ratio changes as temperatures and gas environments vary, indicating a swing between the two phases. Rietveld refinement was conducted on the obtained XRD patterns. Since Fe, Co and Ni have very similar scattering factors in the XRD conditions, only Fe is needed to account for all three elements in the Rietveld model. The rocksalt phase was assumed to be FeO_tO (t<1) and the spinel phase was assumed to be Fe₃O₄. FIG. 4B shows the phase volumetric percentage of the rocksalt phase obtained from the Rietveld refinement of XRD patterns from two repetitions of (FeMgCoNi)O_x synthesis, quenching (at four different temperature/gas conditions shown in the figure), and XRD measurements. Both sets of data show a consistent trend: the ratio depends mainly on temperature, and higher temperatures generally give more rocksalt phase associated with greater oxygen release. The observed higher H₂ production in the 1300-800° C. cycles could arise from the larger extent of phase swing associated with oxygen exchange compared to the 1100-600° C. cycles.

FIG. 4C shows the XANES data to detect changes in the oxidation states of the transition metals via the shift of the X-ray absorption edge; Mg was assumed not to change valence state. To compare the absorption edge, we compared the energy at the half of the maximum intensity in the normalized absorption spectrum. The experiments showed that Fe has an edge shift of about 0.6 eV (compares to 4.3 eV between Fe 2+ and 3+), which indicates an oxidation state change of 0.14. Interestingly, as FIG. 4D shows, Co and Ni are essentially redox inactive compared to Fe, suggesting that Fe is the only redox-active element in the PCO (FeMgCoNi)O_x. Nevertheless, Mg, Ni and Co contribute to enabling Fe to provide its unprecedented performance at reduced temperatures in these PCO materials. Surprisingly, by adding Mg and Ni to a Fe—Co—O system, the H₂-performance is significantly improved.

In addition to the application to water-splitting, the gas reduction process may also be applied to other gasses.

For CO₂ reduction, the two-step thermochemical CO₂ splitting process for CO production (FIG. 1A and FIG. 1B) includes repeatedly cycling a thermal reduction step and a CO₂ splitting step. The thermal reduction step includes heating a poly-cation oxide under a reduced partial oxygen pressure, producing a reduced poly-cation oxide and oxygen gas. The CO₂ splitting step include reacting the reduced poly-cation oxide with CO₂ to produce CO and reoxidized poly-cation oxide.

The thermodynamic analysis is analogous to that for water splitting since the CO₂/CO has similar thermodynamic properties as H₂O/H₂. Poly-cation oxides containing Fe and has relatively high melting point, such as (Mg,Fe,Co,Ni)O_x, are preferred for such two-step cycle. Thermal reduction happens at around 1000° C., and CO₂ splitting happens at around 600° C., depending on the specific poly-cation oxide that is used and O₂ and on CO background partial pressures used during the thermal reduction and CO₂ splitting steps, respectively. Thermodynamically, it is preferred to have low O₂ partial pressure (˜10⁻⁵ atm) during thermal reduction step and low CO partial pressure (˜10⁻⁴ atm) during CO₂ splitting step.

By this two-step cycle, CO₂ is converted to CO and thermal energy is stored. CO is feedstock for steel and methanol productions, Monsanto process and Fischer-Tropsch process in industry. At the same time, thermal energy is stored and can be used for heat recovery.

For NO_x reduction, the two-step thermochemical NO_x reduction process includes repeatedly cycling a thermal reduction step and a NO_x reduction step. The thermal reduction step includes heating a poly-cation oxide under a reduced partial oxygen pressure, producing a reduced poly-cation oxide and oxygen gas. The NO_x reduction step includes reacting the reduced poly-cation oxide with NO_x to produce N₂ and reoxidized poly-cation oxide.

The thermodynamic analysis for NO_x reduction is analogous to water splitting. Poly-cation oxides containing Fe and has relatively high melting point, such as (Mg,Fe,Co,Ni)O_x, are preferred for such two-step cycle. Thermal reduction happens at around 1000° C., and NO_x reduction happens at around 600° C., depending on the specific poly-cation oxide that is used and on the O₂ and N₂ background partial pressures during the thermal reduction and NO_x reduction steps, respectively. Thermodynamically, it is preferred to have low O₂ partial pressure (˜10⁻⁵ atm) during thermal reduction step and low N₂ partial pressure (˜10⁻⁴ atm) during NO_x reduction step.

By this two-step cycle, pollutant NO_x can be converted to N₂ which is the main component in air. This can be used to eliminate NO_x in industrial exhaust.

Variations of the invention are also contemplated. Although the description has specifically discussed examples of water splitting, carbon dioxide splitting, and NO_x reduction, the process may also be applied to reduction of other gasses using the same principles. For example, applications include syngas production by combining water splitting for hydrogen production and reduction of carbon dioxide to carbon monoxide. Applications also include various chemical looping reactions for hydrocarbon fuel production, and thermal energy storage.

From the viewpoint of chemical reactor systems, we note that while most reactor architectures for such reactions so far have used solar concentrators as a heat source, the increasing availability of low-cost carbon-free electricity suggests that localized electrical heating could be used for TWS as well, thus opening more options for system architectures using PCOs as the water splitting materials in various configurations.

Even though this description makes reference to specific PCO compositions, those skilled in the art will understand from the teachings contained herein that the principles and methods apply to other similar materials. For example, many variations in the number of component oxides and the metal species are possible, and may be used to achieve better performance.

In conclusion, the invention provides a two-step thermochemical gas reduction process comprising repeatedly cycling a thermal reduction step and a gas reduction step using a new class of materials, poly-cation oxides (PCOs), which can thermochemically reduce gasses with remarkably high yields that exceed the measured values of state-of-the-art materials. For example, H₂ production with PCOs is demonstrated at thermal reduction temperatures as low as 1000° C. that are not observed for two-metal ferrites and ceria.

Claims

1. A two-step thermochemical gas reduction process comprising repeatedly cycling a thermal reduction step and a gas reduction step; wherein the thermal reduction step comprises heating a poly-cation oxide (MeOx) under a reduced partial oxygen pressure, producing a reduced poly-cation oxide (MeOx-1) and oxygen gas (O2);wherein the gas reduction step comprises reacting the reduced poly-cation oxide (MeOx-1) with a first gas to produce a second gas and reoxidized poly-cation oxide (MeOx), wherein the first gas is reduced into the second gas;wherein the poly-cation oxide has at least two distinct crystal structures at two distinct temperatures corresponding to two distinct average oxidation states of at least one transition metal in a transformation between MeOx and MeOx-1 and is capable of undergoing a reversible phase transformation between the two distinct crystal structures.

2. The two-step thermochemical gas reduction process of claim 1wherein the poly-cation oxide is an entropy tuned mixed metal oxide;

3. The two-step thermochemical gas reduction process of claim 2wherein the entropy tuned mixed metal oxide (MeOx) is an entropy stabilized mixed metal oxide, where the entropy-tuning is achieved via change in crystal structure of one of more of the compounds involved.

4. The two-step thermochemical gas reduction process of claim 1 wherein the mixed metal oxide (MeOx) is a mixture of multiple metal oxides Me1O, . . . , MenO.

5. The two-step thermochemical gas reduction process of claim 4 wherein the mixed metal oxide is (Mg,Ni,Co,Zn,Fe)Ox, i.e., an equimolar mixture of MgO, CoO, NiO, FeO and ZnO.

6. The two-step thermochemical gas reduction process of claim 1wherein the gas reduction process is a water splitting process for hydrogen gas production;wherein the gas reduction step is a water splitting step;wherein the first gas is water vapor and the second gas is hydrogen gas.

7. The two-step thermochemical gas reduction process of claim 1wherein the gas reduction process is a CO2 splitting process for CO gas production;wherein the gas reduction step is a CO2 splitting step;wherein the first gas is CO2 and the second gas is CO.

8. The two-step thermochemical gas reduction process of claim 1wherein the gas reduction process is a NOx reduction process for N2 gas production;wherein the gas reduction step is a NOx reduction step;wherein the first gas is NOx and the second gas is N2.