Patent Application
20130164511
The present application claims priority from Korean Patent Application Number 10-2011-0142055 filed on Dec. 26, 2011, the entire contents of which application are incorporated herein for all purposes by this reference.
1. Field of the Invention
The present invention relates to a thermochromic substrate and a method of manufacturing the same, and more particularly, to a thermochromic substrate that has a thermochromic thin film and a method of manufacturing the same.
2. Description of Related Art
Thermochromism refers to the phenomenon in which an oxide or a sulfide of a transition metal undergoes a change in its crystalline structure below and above a specific temperature (i.e. its transition temperature (Tc)), whereby its physical properties (electrical conductivity and infrared (IR) transmittance) suddenly change.
When a glass is coated with a thin film that has such thermochromic capability, a “smart window” can be produced, which transmits visible light but blocks near infrared rays and infrared rays at or above a predetermined temperature in order to prevent the indoor temperature from increasing. The application of smart windows to vehicles or buildings may be very effective in saving energy. Materials that exhibit thermochromism include oxides of several transition metals, of which vanadium dioxide (VO2) is being studied since its transition temperature is 68° C., which is relatively close to a temperature at which practical application becomes possible.
Vanadium oxides, such as VO2, are present in the form of a variety of crystalline phases, such as V2O3, V3O5, V4O7, V6O11, V5O9, V6O13, V4O9, V3O7, V2O5 and VO2. The thermochromic characteristics appear in the crystalline phase of VO2.
Therefore, in order to transform vanadium oxides that are present in a variety of crystalline phases, such as V2O3, V3O5, V4O7, V5O9, V6O11, V6O13, V4O9, V3O7, V2O5 and VO2, into VO2 in the crystalline phase, a method of heating a glass substrate to a high temperature and then coating the glass substrate with a vanadium oxide, a method of coating a glass substrate with a vanadium oxide, followed by post annealing, and the like are used.
The thermochromic glass using the VO2 thin film has a yellowish color due to the unique color of VO2.
However, as a drawback, when the thermochromic glass is applied to the construction industry, the thermochromic glass using the VO2 thin film is not compliant with consumers' demands, since consumers prefer greenish, bluish or grayish colors.
The information disclosed in this Background of the Invention section is only for the enhancement of understanding of the background of the invention, and should not be taken as an acknowledgment or any form of suggestion that this information forms a prior art that would already be known to a person skilled in the art.
Various aspects of the present invention provide a thermochromic substrate, the color of which satisfies consumers' demands, and a method of manufacturing the same.
In an aspect of the present invention, provided is a thermochromic substrate that includes a base substrate; a thermochromic thin film formed on the base substrate; and a photochromic thin film formed on the thermochromic thin film.
In an exemplary embodiment, the photochromic thin film may absorb wavelengths ranging from 380 nm to 780 nm, and be made of at least one substance selected from among silver (Ag), Ag halide, zinc (Zn) halide, spiropyran and diarylethene.
In an exemplary embodiment, the thermochromic thin film may contain at least one selected from among vanadium dioxide (VO2), titanium oxide (III) (Ti2O3) and niobium oxide (NbO2).
In an exemplary embodiment, the thermochromic thin film may be doped with at least one substance selected from among molybdenum (Mo), tungsten (W), chromium (Cr), nickel (Ni) and zirconium (Zr).
In an exemplary embodiment, the thermochromic substrate may further include an oxide or nitride thin film between the base substrate and the thermochromic substrate.
In an exemplary embodiment, the oxide or nitride thin film may be made of at least one selected from among silicon dioxide (SiO2), aluminum oxide (Al2O3), niobium pentoxide (Nb2O5), titanium dioxide (TiO2), and silicon nitride (Si3N4). It is preferred that the thickness of the oxide or nitride thin film range from 30 nm to 80 nm.
In another aspect of the present invention, provided is a method of manufacturing a thermochromic substrate that includes the following steps of: forming an oxide or nitride thin film as a coating on a glass substrate; forming a VO2 thin film as a coating on the oxide or nitride thin film; and forming a photochromic thin film as a coating on the VO2 thin film.
In an exemplary embodiment, the step of forming the VO2 thin film may be carried out using a sputtering target made of VO2 that is doped with at least one substance selected from among Mo, W, Cr, Ni and Zr, or using a sputtering target made of VO2 and a sputtering a sputtering target made of at least one selected from among Mo, W, Cr, Ni and Zr.
In an exemplary embodiment, the step of forming the photochromic thin film may be carried out by direct-current (DC) sputtering deposition or sol-gel processing.
According to embodiments of the invention, the color of the thermochromic substrate can be adjusted such that it satisfies consumers' demands, and can be preferably adjusted such that the thermochromic substrate has a grayish color.
The methods and apparatuses of the present invention have other features and advantages which will be apparent from, or are set forth in greater detail in the accompanying drawings, which are incorporated herein, and in the following Detailed Description of the Invention, which together serve to explain certain principles of the present invention.
Reference will now be made in detail to a thermochromic substrate that has a thermochromic thin film and a method of manufacturing the same of the present invention, embodiments of which are illustrated in the accompanying drawings and described below.
In the following description of the present invention, detailed descriptions of known functions and components incorporated herein will be omitted when they may make the subject matter of the present invention unclear.
Referring to
The glass substrate 100 is a transparent or color substrate that has a predetermined area or thickness. It is preferred that the glass substrate be a sodalime glass.
The oxide or nitride thin film 200 is formed on the glass substrate 100, and acts as a sodium diffusion barrier to prevent sodium (Na) ions in the glass substrate from diffusing into the VO2 thin film 300, which will be described later, at a temperature of 350° C. or higher in the process of manufacturing the thermochromic substrate. Otherwise, the VO2 thin film would lose the thermochromic characteristics due to the sodium diffusion.
The oxide or nitride thin film 200 may be made of one material selected from among, but not limited to, silicon dioxide (SiO2), niobium pentoxide (Nb2O5), aluminum oxide (Al2O3), titanium dioxide (TiO2), and silicon nitride (Si3N4). Although it is preferred that the thickness of the oxide or nitride thin film 200 range from 30 nm to 80 nm, the thickness may vary depending on the type of materials to be coated, the refractivity of coating materials, and the like.
The VO2 thin film 300 is formed on the oxide or nitride thin film 200, and undergoes phase transition depending on the temperature, thereby adjusting the transmittance of infrared (IR) radiation.
The transition of the VO2 thin film 300 occurs at a predetermined temperature, at which the crystalline structure of VO2 changes due to the thermochromic phenomenon, so that the physical properties (electrical conductivity and infrared radiation transmittance) of the VO2 thin film drastically change. As a result, the VO2 thin film 300 blocks near IR radiation and IR radiation while allowing visible light to pass through.
The VO2 thin film 300 may be doped with a dopant in order to reduce the phase transition of VO2. It is preferred that the VO2 thin film be doped with at least one selected from among molybdenum (Mo), tungsten (W), chromium (Cr), nickel (Ni) and zirconium (Zr).
The photochromic thin film 400 is formed on the VO2 thin film 300 such that it adjusts the color of the photochromic substrate.
When the photochromic thin film 400 is irradiated with light, the joining structure of its chemical substance changes, thereby forming an isomer having a different absorption spectrum. As a result, the color of the thin film reversibly changes.
It is preferred that the photochromic thin film 400 according to an embodiment of the invention absorb wavelengths ranging from 380 nm to 780 nm, so that the thermochromic substrate has a grayish color.
A material that absorbs wavelengths ranging from 380 nm to 780 nm may be implemented as at least one material selected from among silver (Ag), Ag halide, zinc (Zn) halide, spiropyran and diarylethene.
In this way, it is possible to adjust the color of the thermochromic substrate by coating the VO2 thin film having a yellowish color with the photochromic thin film.
In particular, it is possible to manufacture a thermochromic substrate having a grayish color, which will be popular to consumers when applied to the construction industry, by coating a VO2 thin film with a photochromic thin film that absorbs wavelengths ranging from 380 nm to 780 nm.
That is, when a VO2 thin film has a yellowish color, with a being within ±5 and b being 10 or more according to the CIE L*a*b* color system, it is possible to impart the thermochromic substrate with a grayish color, in which a is within ±5 and b is 15 or less, by coating the VO2 thin film with a photochromic thin film that absorbs wavelengths ranging from 380 nm to 780 nm.
Table 1 above is a table that presents a and b values of a VO2 thin film and a photochromic thin film and corrected a and b values of a multilayer film that is formed using the VO2 thin film and the photochromic thin film.
As presented in Table 1 above, it is possible to manufacture the thermochromic substrate having a grayish color by significantly reducing the b value by coating the VO2 thin film that has a yellowish color with the photochromic thin film, in which a is 8.648 and b is −25.31 in the CIE L*a*b* color system.
Referring to
Here, the VO2 thin film may be formed via sputtering deposition using a sputtering target made of VO2 that is doped with at least one substance selected from among Mo, W, Cr, Ni and Zr, or co-sputtering deposition using a sputtering target made of VO2 and a sputtering target made of at least one substance selected from among Mo, W, Cr, Ni and Zr.
In addition, the photochromic thin film may be made via direct current (DC) sputtering deposition or sol-gel processing.
The foregoing descriptions of specific exemplary embodiments of the present invention have been presented with respect to the certain embodiments and drawings. They are not intended to be exhaustive or to limit the invention to the precise forms disclosed, and obviously many modifications and variations are possible for a person having ordinary skill in the art in light of the above teachings.
It is intended therefore that the scope of the invention not be limited to the foregoing embodiments, but be defined by the Claims appended hereto and their equivalents.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2011-0142055 | Dec 2011 | KR | national |