The present invention relates generally to disposable plates, bowls, platters and the like and more particularly to plastic articles of this class produced by thermoforming. The articles of the invention are thermoformed from extruded plastic sheet stock which is mineral-filled with a combination of mica and calcium carbonate.
Disposable food containers are well known in the art. Typically, such containers are made from paper or plastic.
Pressed paperboard containers may be made as noted in one or more of U.S. Pat. No. 4,606,496 entitled “Rigid Paperboard Container” of R. P. Marx et al; U.S. Pat. No. 4,609,140 entitled “Rigid Paperboard Container and Method and Apparatus for Producing Same” of G. J. Van Handel et al; U.S. Pat. No. 4,721,499 entitled “Method of Producing a Rigid Paperboard Container” of R. P. Marx et al; U.S. Pat. No. 4,721,500 entitled “Method of Forming a Rigid Paper-Board Container” of G. J. Van Handel et al; and U.S. Pat. No. 5,203,491 entitled “Bake-In Press-Formed Container” of R. P. Marx et al. Equipment and methods for making paperboard containers are also disclosed in U.S. Pat. No. 4,781,566 entitled “Apparatus and Related Method for Aligning Irregular Blanks Relative to a Die Half” of A. F. Rossi et al; U.S. Pat. No. 4,832,676 entitled “Method and Apparatus for Forming Paperboard Containers” of A. D. Johns et al; and U.S. Pat. No. 5,249,946 entitled “Plate Forming Die Set” of R. P. Marx et al.
Thermoformed plastic containers, particularly polypropylene mica-filled containers with a micronodular surface are disclosed in U.S. Pat. No. 6,100,512 to Neculescu et al. Such containers have the advantages that they are durable and may be washed and re-used if so desired and are microwaveable. The disclosure of the foregoing patents is incorporated by reference.
A drawback of plastic thermoformed containers is that they tend to be more costly than their paper counterparts due, in part, to material costs. More rigid materials can be used more sparingly and are thus highly desirable in the field. One way to increase rigidity of polypropylene containers is to use a filler such as mica as disclosed in the '512 patent. However, mica tends to interact with polypropylene to produce undesirable odors, believed to be caused by certain organic ketone compounds generated during melt-processing of the material. The generation of odors is minimized by including a basic inorganic compound, such as calcium carbonate in the composition.
It has been unexpectedly found that fine grades of calcium carbonate can greatly increase the rigidity of polypropylene containers filled with calcium carbonate and mica as described hereinafter.
Disposable polypropylene containers made from extruded polypropylene mica and calcium carbonate filled sheet exhibits enhanced rigidity when fine grades of calcium carbonate are used. An added advantage is that the sheet filled with finer calcium carbonate exhibits less die lip buildup as it is produced. For 11″ plates, normalized rigidity was observed to increase from 11 g/g to 12.8 g/g when the mean particle size of calcium carbonate used was changed from 12 to 6 microns. A further increase to 13.63 g/g of normalized rigidity was achieved when calcium carbonate with a mean particle size of 1 micron was used.
There is thus provided in accordance with the present invention a thermoformed disposable food container having a wall caliper of from about 10 to about 80 mils consisting essentially of from about 30 to about 80 percent by weight of a matrix polymer composition consisting predominantly of a polypropylene polymer and optionally including a polyethylene polymer, from about 10 to about 50 percent mica, from about 2.5 to about 25 percent calcium carbonate, and up to about 5 weight percent titanium dioxide, wherein the calcium carbonate has a mean particle size of less than about 8 microns. More preferably the calcium carbonate has a mean particle size of 6 microns or less; yet more preferably less than about 5 microns, and still more preferably the calcium carbonate has a mean particle size of less than about 3 or 2.5 microns. In some preferred embodiments, the calcium carbonate has a mean particle size of about 1 micron or less.
Particularly preferred embodiments include those wherein the mean particle size of the calcium carbonate is about 6 microns; those in which the mean particle size of the calcium carbonate is about 3 microns; and those wherein the mean particle size of the calcium carbonate is about 1 micron.
In other aspects of the invention, there are provided extrudable and injection moldable compositions having the same components in like proportions as the disposable food containers. These compositions may be in the form of pellets, for example, or extruded into sheet or film form or injection molded into useful articles. Here again, the compositions thus have a calcium carbonate content of from about 2.5 weight percent to about 25 weight percent calcium carbonate and so forth. Particularly preferred compositions include those wherein the calcium carbonate has a mean particle size of 6 microns; those wherein the calcium carbonate has a mean particle size of 3 microns; and those wherein the calcium carbonate has a mean particle size of about 1 micron.
Typically, the calcium carbonate is present in an amount of from about 5 to about 15 percent by weight of the container, whereas mica is present in an amount of from about 20 to about 40 percent by weight of the container. The matrix polymer composition generally consists of a polypropylene polymer and a polyethylene polymer in preferred cases. The polyethylene polymer may be present in an amount of from about 1 to about 15 percent by weight of the container, typically present in an amount of from 2.5 to about 7.5 percent by weight. A preferred polyethylene polymer is HDPE.
The polypropylene polymer is typically present in an amount of from about 40 to about 60 percent by weight of the container, and may be isotactic polypropylene. Optionally included is titanium dioxide typically in an amount of from about 0.5 to about 4 percent by weight of the container.
The containers may have a wall caliper of from about 10 to about 50 mils, typically from about 15 to about 25 mils.
These and other aspects of the invention will be further appreciated from the following description, drawings and claims.
The invention is described in detail below with reference to the various drawings. In the drawings:
The invention is described in detail below with reference to the figures. Such description is for purposes of illustration only and is not limitative of the invention in any way.
Numerous modifications within the spirit and scope of the present invention, set forth in the appended claims, will be readily apparent to those of skill in the art.
Generally speaking, the present invention is directed to the discovery that using calcium carbonate having a mean particle size of less than 12 microns is beneficial when making polypropylene food containers from polypropylene sheet filled with mica and calcium carbonate. The smaller particle size calcium carbonate has a beneficial effect on container rigidity making it possible to use less material for a given container and also appears to reduce die lip build up during sheet extrusion. A composition with six (6) micron mean size calcium carbonate extruded into sheet extruded well with less die lip build up (about 5/16″ vs. about ⅜″) than a composition with twelve (12) micron mean particle size calcium carbonate. Still less die lip build up (about 3/16″) was observed when a calcium carbonate having a mean particle size of one (1) micron was used in corresponding compositions.
Containers formed from the sheet had the properties summarized in Table 1 below.
As can be seen, product rigidity increases markedly as the particle size of the calcium carbonate is reduced. This discovery makes it possible to make a more rigid product with the same amount of material or maintain a target rigidity while reducing material consumption.
The foregoing is described and illustrated further below.
Test Methods, Definitions and Materials
SSI Rigidity is measured with the Single Service Institute Plate Rigidity Tester of the type originally available through Single Service Institute, 1025 Connecticut Ave., N.W., Washington, D.C. The SSI Rigidity test apparatus has been manufactured and sold through Sherwood Tool, Inc. Kensington, Conn. This test is designed to measure the rigidity (i.e., resistance to buckling and bending) of paper and plastic plates, bowls, dishes, and trays by measuring the force required to deflect the rim of these products a distance of 0.5 inch while the product is supported at its geometric center. Specifically, the plate specimen is restrained by an adjustable bar on one side and is center supported. The rim or flange side opposite to the restrained side is subjected to 0.5 inch deflection by means of a motorized cam assembly equipped with a load cell, and the force (grams) is recorded. The test simulates in many respects the performance of a container as it is held in the hand of a consumer, supporting the weight of the container's contents. SSI Rigidity is expressed as grams per 0.5 inch deflection. A higher SSI value is desirable since this indicates a more rigid product. All measurements were done at standard TAPPI conditions for paperboard testing, 72° F. and 50% relative humidity. Geometric mean averages for the machine direction (MD) and cross machine direction (CD) are reported herein.
The particular apparatus employed for SSI Rigidity measurements was a Model No. ML-4431-2 SSI Rigidity tester as modified by Georgia Pacific Corporation, National Quality Assurance Lab, Lehigh Valley Plant, Easton, Pa. 18040 using a Chatillon gauge available from Chatillon, Force Measurements Division, P.O. Box 35668, Greensboro, N.C. 27425-5668.
Unless otherwise specified, the following terms have the following meanings:
“Rigidity” refers to SSI Rigidity (kilograms or grams/0.5 inches).
“Sheet”, “sheet stock” and the like refers to both a web or roll of material and to material that is cut into sheet form for processing.
Particle size refers to mean particle size.
Mean particle size of a particulate material such as calcium carbonate is the particle diameter as to which 50 percent by weight of the particles of the particulate material have a smaller diameter. This quantity may be determined by any suitable technique.
Unless otherwise indicated, “mil”, “mils” and like terminology refers to thousandths of an inch and dimensions appear in inches. Likewise, caliper is the thickness of material and is expressed in mils unless otherwise specified.
The term major component, predominant component and the like refers to a component making up at least about 50% of a composition or that class of compound in the composition by weight as the context indicates; for example, a filler is the predominant filler in a filled plastic composition if it makes up more than about 50% by weight of the filler in the composition based on the combined weight of fillers in the composition, and a resin is the predominant resin in a composition if it makes up more than 50 percent of the resin in the composition.
Basis weights appear in lbs per 3000 square foot ream unless otherwise indicated.
Percents refer to weight percents.
Polypropylene polymers which are suitable are preferably selected from the group consisting of isotactic polypropylene, and copolymers of propylene and ethylene wherein the ethylene moiety is less than about 10% of the units making up the polymer, and mixtures thereof. Generally, such polymers have a melt flow index from about 0.3 to about 4, but most preferably the polymer is isotactic polypropylene with a melt-flow index of about 1.5.
A polyethylene polymer or component may be any suitable polyethylene such as HDPE, LDPE, MDPE, LLDPE or mixtures thereof and may be melt-blended with polypropylene if so desired. The various polyethylene polymers referred to herein are described at length in the Encyclopedia of Polymer Science & Engineering (2d Ed.), Vol. 6; pp: 383-522, Wiley 1986; the disclosure of which is incorporated herein by reference. HDPE refers to high density polyethylene which is substantially linear and has a density of generally greater that 0.94 up to about 0.97 g/cc. LDPE refers to low density polyethylene which is characterized by relatively long chain branching and a density of about 0.912 to about 0.925 g/cc. LLDPE or linear low density polyethylene is characterized by short chain branching and a density of from about 0.92 to about 0.94 g/cc. Finally, intermediate density polyethylene (MDPE) is characterized by relatively low branching and a density of from about 0.925 to about 0.94 g/cc.
“Thermoforming”, “thermoformed” and like terminology is given its ordinary meaning. In the simplest form, thermoforming is the draping of a softened sheet over a shaped mold. In the more advanced form, thermoforming is the automatic high speed positioning of a sheet having an accurately controlled temperature into a pneumatically actuated forming station whereby the article's shape is defined by the mold, followed by trimming and regrind collection as is well known in the art. Still other alternative arrangements include the use of drape, vacuum, pressure, free blowing, matched die, billow drape, vacuum snap-back, billow vacuum, plug assist vacuum, reverse draw with plug assist, pressure bubble immersion, trapped sheet, slip, diaphragm, twin-sheet cut sheet, twin-sheet roll-fed forming or any suitable combinations of the above. Details are provided in J. L. Throne's book, Thermoforming, published in 1987 by Coulthard. Pages 21 through 29 of that book are incorporated herein by reference. Suitable alternate arrangements also include a pillow forming technique which creates a positive air pressure between two heat softened sheets to inflate them against a clamped male/female mold system to produce a hollow product. Metal molds are etched with patterns ranging from fine to coarse in order to simulate a natural or grain like texturized look. Suitable formed articles are trimmed in line with a cutting die and regrind is optionally reused since the material is thermoplastic in nature. Other arrangements for productivity enhancements include the simultaneous forming of multiple articles with multiple dies in order to maximize throughput and minimize scrap. In some preferred embodiments, the melt-compounded composition from which the articles are made may include polypropylene and optionally further includes a polyethylene component and titanium dioxide. Suitable materials and techniques for fabricating the disposable containers of the present invention from thermoplastic materials appear in U.S. Pat. No. 6,211,501 to McCarthy et al. as well as U.S. Pat. No. 6,211,500 to Cochran II et al. the disclosures of which are incorporated herein by reference.
Preferred Embodiments
In general, products of the invention are made by first extruding a polypropylene sheet of suitable composition as described in the '500 and '501 patents followed by thermoforming the sheet as is also described in the '500 and '501 patents. A suitable container shape is that described in U.S. Co-Pending application Ser. No. 09/603,579, filed Jun. 26, 2000, entitled “Smooth Profiled Food Service Articles”. These plates have the characteristics seen in
Illustrated in
From the center line 34 a predetermined distance X12 extends toward the outer peripheral surface forming portion 32. A distance Y12 extends a predetermined distance from the base or bottom-forming portion 30 upwardly therefrom. A radius R12 extends from the intersection point of the distance X12 and Y12 to form a first rim portion 36 of the outwardly projecting sidewall 35. The first rim portion 36 is defined by an arc A12 which extends from a substantially vertical line defined at an outer peripheral point 37 to a fixed point 40. The arc A12 may be approximately 60°.
A distance X22 extends from the center line 34 to a predetermined point. A distance Y22 extends from the base or bottom-forming portion 30 of the plate 10 downwardly a predetermined distance. A radius R22 extends from the intersection of the lines X22 and Y22 to define the radius of curvature of a second rim portion 38 of the sidewall 35. The radius R22 extends from the first fixed point 40 to the second fixed point 42 through an arc A22. The arc A22 may be approximately 4°.
A distance X32 extends from the center line 34 to a predetermined distance. A distance Y32 extends from the base or bottom-forming section 30 of the plate 10 to project upwardly a predetermined distance. A radius R32 extends from the intersection of the lines X32 and Y32 which is the radius of the third rim portion 44 of the rim 46. The radius R32 extends from the second fixed point 42 to a third fixed point 48. An arc A32 is formed between the second fixed point 44 and the third fixed point 48 to extend a predetermined distance. The arc A32 may be approximately 55°.
A distance X42 extends a predetermined distance from the center line 34. Similarly, a distance Y42 extends from the base or bottom-forming section 30 of the plate 10 to project upwardly. A radius R42 extends from the intersection of the lines X42 and Y42 to define the radius of curvature of a fourth rim portion 47 of the rim 46. An arc A42 is formed between the third fixed point 48 and a fourth fixed point 50 at diameter D from the center line. The arc A42 may be approximately 60°. A section disposed at 50 forms the outer edge of the plate.
The article made according to the present invention may have any particular size or shape. In various embodiments of the present invention the container may be a 9″ or 11″ plate with profile coordinates as illustrated in
Salient features of the plate illustrated in
The length of the second arc, S2 is generally less the length of the fourth arc S4, which, in turn, is less than the length S1 of the first arc A12. The radius of curvature R42 of the fourth arc is less than the radius of curvature R32 of the third rim portion, which in turn, is less than radius of curvature R22 of the second rim portion. The angle of the first arc, A12 is generally greater that about 55 degrees, while, the angle of the third arc, A32 is generally greater than about 45 degrees as is set forth in the foregoing tables. The angle of the fourth arc A42 is generally less than about 75 degrees and more preferably is about 60 degrees.
Typically, the length S1 of arc A12 is equivalent to the length S3 of arc A32 and R12 of the first rim portion is equivalent in length to the radius of curvature R32 of the third rim portion.
Generally speaking, the height of the center of curvature of the first arc (that is the origin of ray R12) above the central planar portion is substantially less than, perhaps twenty five percent or so less than, the distance that the center of curvature of the second rim portion (the origin of ray R22) is below the central planar portion. In other words, the length Y12 is about 0.75 times or less the length Y22.
So also, the horizontal displacement of the center of curvature of the second rim portion from the center of curvature of the first rim portion is at least about twice the length of the first radius of curvature R12. The height of the center of curvature of the third rim portion above the central planar portion is generally less than the height of the center of curvature of the fourth rim portion above the plane of the central planar portion. The horizontal displacement of the center of curvature of the second rim portion is generally outwardly disposed from the center of curvature of the third and fourth rim portions. A further noteworthy feature of the plate of
Specific Examples
A series of 11″ plates described generally above were thermoformed from extruded sheet having the following composition:
Basis weights of sheet material used were from 255 to 315 lbs/3000 square foot ream and 3 different types of particulate calcium carbonate were used: 12 micron mean particle size material, 1 micron mean particle size material (Lot A) and another 1 micron mean particle size material (Lot B). The one micron material is available from Imerys as supermite calcium carbonate. Six micron material, available from Omya, called Omya 5, has an average particle size of about 6 microns and may likewise be employed. The mica may have a mean particle size of 50 microns or so.
Results are summarized in Table 5 below and appear graphically in
The invention has been described in detail hereinabove in connection with numerous embodiments. That discussion is not intended to limit in any way the scope of the present invention which is defined in the appended claims. It will be readily appreciated by one of skill in the art that the particular embodiments illustrated may be scaled up or down in size with the relative proportions shown herein or that product shapes such as square or rectangular with rounded comers, triangular, multi-sided, oval platters, polygonal platters with rounded comers and the like may be formed in accordance with the present invention. Typical products include plates, bowls, trays, deep dish containers, platters and so forth.
This non-provisional application claims the benefit of the filing date of U.S. Provisional Patent Application Ser. No. 60/366,790, of the same title, filed Mar. 22, 2002. This application is a divisional of U.S. patent application Ser. No. 10/387,093 now U.S. Pat. No. 6,881,931 filed on Mar. 12, 2003.
Number | Name | Date | Kind |
---|---|---|---|
1440070 | Fry | Dec 1922 | A |
1813810 | McDonald et al. | Jul 1931 | A |
1848066 | Shepard et al. | Mar 1932 | A |
D88688 | Thompson | Dec 1932 | S |
D169133 | Foster | Mar 1953 | S |
2719413 | Panzer | Oct 1955 | A |
2738915 | St. Clair | Mar 1956 | A |
D179011 | Kimble | Oct 1956 | S |
3030330 | Cines et al. | Apr 1962 | A |
3067922 | Hill | Dec 1962 | A |
3271354 | Weissert et al. | Sep 1966 | A |
3353974 | Trimble et al. | Nov 1967 | A |
3422056 | Carton | Jan 1969 | A |
3507951 | Morecroft et al. | Apr 1970 | A |
3582384 | Belde et al. | Jun 1971 | A |
3672538 | Wiedemann | Jun 1972 | A |
3675811 | Artz | Jul 1972 | A |
3696849 | Davis | Oct 1972 | A |
3702356 | Hall | Nov 1972 | A |
3767444 | Zeisberger | Oct 1973 | A |
3811594 | Paulucci | May 1974 | A |
3844810 | Pollard | Oct 1974 | A |
3865302 | Kane | Feb 1975 | A |
3888679 | Komatsu et al. | Jun 1975 | A |
3893795 | Nauta | Jul 1975 | A |
3923726 | Benz | Dec 1975 | A |
3931890 | Davis | Jan 1976 | A |
3953218 | Pollard | Apr 1976 | A |
3978036 | Pollard | Aug 1976 | A |
4004940 | Cormier | Jan 1977 | A |
4039507 | Paige et al. | Aug 1977 | A |
4113822 | Takiura et al. | Sep 1978 | A |
4116909 | Muller | Sep 1978 | A |
4153659 | Recktenwald et al. | May 1979 | A |
4154622 | Momoi et al. | May 1979 | A |
4165302 | Armenti et al. | Aug 1979 | A |
4165357 | Vetter | Aug 1979 | A |
4197398 | Floyd et al. | Apr 1980 | A |
4209430 | Weber | Jun 1980 | A |
4229504 | Brachman | Oct 1980 | A |
4230501 | Howard et al. | Oct 1980 | A |
4235641 | Engelmann et al. | Nov 1980 | A |
4248651 | Kojimoto et al. | Feb 1981 | A |
4264553 | Loo | Apr 1981 | A |
4282277 | Austen et al. | Aug 1981 | A |
4309323 | Orloff et al. | Jan 1982 | A |
4309374 | Pollard | Jan 1982 | A |
4311658 | Nicoll | Jan 1982 | A |
4338228 | Inoue et al. | Jul 1982 | A |
4338229 | Agarwal et al. | Jul 1982 | A |
4407986 | Nomura et al. | Oct 1983 | A |
4409342 | Ancker et al. | Oct 1983 | A |
4420454 | Kawaguchi et al. | Dec 1983 | A |
4429064 | Marzola et al. | Jan 1984 | A |
4442243 | Woodhams | Apr 1984 | A |
4447479 | Harrison et al. | May 1984 | A |
4455092 | Platts | Jun 1984 | A |
4455344 | Matsuyama et al. | Jun 1984 | A |
4467007 | Elgie | Aug 1984 | A |
4467077 | Meyer et al. | Aug 1984 | A |
4480064 | Chopra et al. | Oct 1984 | A |
4499227 | Bailey | Feb 1985 | A |
4501843 | Needham | Feb 1985 | A |
4504617 | Yui et al. | Mar 1985 | A |
4508859 | Muhle et al. | Apr 1985 | A |
4510271 | Muhle et al. | Apr 1985 | A |
4522982 | Ewen | Jun 1985 | A |
4524160 | Maeda et al. | Jun 1985 | A |
4528155 | Elder | Jul 1985 | A |
4536148 | Murley et al. | Aug 1985 | A |
4550134 | Isogai et al. | Oct 1985 | A |
4555439 | Ueeda et al. | Nov 1985 | A |
4560712 | Chiang | Dec 1985 | A |
4560715 | Ueeda et al. | Dec 1985 | A |
4578296 | Miyazaki et al. | Mar 1986 | A |
4599114 | Atkinson | Jul 1986 | A |
4603153 | Sobajima et al. | Jul 1986 | A |
4604421 | Mitsuno et al. | Aug 1986 | A |
4606496 | Marx et al. | Aug 1986 | A |
4609140 | Van Handel et al. | Sep 1986 | A |
4623586 | Umeya et al. | Nov 1986 | A |
4626456 | Farrell et al. | Dec 1986 | A |
4634735 | Thiersault et al. | Jan 1987 | A |
4636349 | MacLaughlin | Jan 1987 | A |
4643940 | Shaw et al. | Feb 1987 | A |
4650747 | Uno et al. | Mar 1987 | A |
4650818 | Oka et al. | Mar 1987 | A |
4657499 | Lewellen et al. | Apr 1987 | A |
4663103 | McCullough et al. | May 1987 | A |
4668175 | Martin | May 1987 | A |
4668729 | Kataoka | May 1987 | A |
4670499 | Bonnke et al. | Jun 1987 | A |
4684488 | Rudolph | Aug 1987 | A |
4686257 | Mitsuno et al. | Aug 1987 | A |
4690666 | Alexander et al. | Sep 1987 | A |
4696857 | Sibilia et al. | Sep 1987 | A |
4698395 | Inoue et al. | Oct 1987 | A |
4720514 | Needham | Jan 1988 | A |
4721499 | Marx et al. | Jan 1988 | A |
4721500 | Van Handel et al. | Jan 1988 | A |
4728476 | Boring et al. | Mar 1988 | A |
4732926 | Faulkner | Mar 1988 | A |
4734450 | Kawai et al. | Mar 1988 | A |
4735988 | Takada et al. | Apr 1988 | A |
4746057 | Wagner | May 1988 | A |
4758396 | Crass et al. | Jul 1988 | A |
4764546 | Mitsuno et al. | Aug 1988 | A |
4781295 | Gunesin et al. | Nov 1988 | A |
4781566 | Rossi et al. | Nov 1988 | A |
4809876 | Tomaswick et al. | Mar 1989 | A |
4810733 | Sakuma et al. | Mar 1989 | A |
4820760 | Ali et al. | Apr 1989 | A |
4832676 | Johns et al. | May 1989 | A |
4835195 | Rayfield et al. | May 1989 | A |
4866117 | Egashira et al. | Sep 1989 | A |
4879147 | Newman et al. | Nov 1989 | A |
4889885 | Usuki et al. | Dec 1989 | A |
4891392 | Abe et al. | Jan 1990 | A |
4895688 | Shigetani et al. | Jan 1990 | A |
4911978 | Tsubone et al. | Mar 1990 | A |
4916010 | Yamana et al. | Apr 1990 | A |
4929474 | Avni et al. | May 1990 | A |
4933526 | Fisher et al. | Jun 1990 | A |
4933529 | Saville | Jun 1990 | A |
4938604 | Naito et al. | Jul 1990 | A |
4948545 | Bashir et al. | Aug 1990 | A |
4960639 | Oda et al. | Oct 1990 | A |
4981631 | Cheung et al. | Jan 1991 | A |
4981938 | Hanari et al. | Jan 1991 | A |
4987173 | Namura et al. | Jan 1991 | A |
4987175 | Bunnell, Sr. | Jan 1991 | A |
4994229 | Flecknoe-Brown | Feb 1991 | A |
5001176 | Nakazima | Mar 1991 | A |
5001182 | Maruya et al. | Mar 1991 | A |
D316800 | Wertheim | May 1991 | S |
5015679 | Matumura | May 1991 | A |
5017015 | Schlumpf et al. | May 1991 | A |
5019446 | Bunnell, Sr. | May 1991 | A |
5021463 | Kozma | Jun 1991 | A |
5023286 | Abe et al. | Jun 1991 | A |
5041259 | Fujii et al. | Aug 1991 | A |
5041491 | Turke et al. | Aug 1991 | A |
5045369 | Kobayashi et al. | Sep 1991 | A |
5053444 | Trotoir | Oct 1991 | A |
5082888 | Abe et al. | Jan 1992 | A |
5086109 | Ueno et al. | Feb 1992 | A |
5088640 | Littlejohn | Feb 1992 | A |
5137975 | Kelusky | Aug 1992 | A |
5156790 | Cucchisi et al. | Oct 1992 | A |
5165978 | Lecinski | Nov 1992 | A |
5175051 | Schloegl et al. | Dec 1992 | A |
5184995 | Kuchenbecker | Feb 1993 | A |
5202192 | Hope et al. | Apr 1993 | A |
5203491 | Marx et al. | Apr 1993 | A |
5219627 | Arase et al. | Jun 1993 | A |
5219903 | Fujii et al. | Jun 1993 | A |
5219913 | Tomomatsu et al. | Jun 1993 | A |
5223194 | Rosen | Jun 1993 | A |
5230939 | Baum | Jul 1993 | A |
5232971 | Nomura et al. | Aug 1993 | A |
5249946 | Marx | Oct 1993 | A |
5252384 | Bothe et al. | Oct 1993 | A |
5252659 | Koizumi et al. | Oct 1993 | A |
5254394 | Bothe et al. | Oct 1993 | A |
5266124 | Al-Jumah et al. | Nov 1993 | A |
D342186 | Frere | Dec 1993 | S |
5268220 | Tajima et al. | Dec 1993 | A |
5277970 | Schuhmann et al. | Jan 1994 | A |
5296430 | Funabashi et al. | Mar 1994 | A |
5300747 | Simon | Apr 1994 | A |
5326020 | Cheshire et al. | Jul 1994 | A |
5326625 | Schuhmann et al. | Jul 1994 | A |
5340878 | Sadatoshi et al. | Aug 1994 | A |
D351968 | Zivin | Nov 1994 | S |
5376698 | Sispas et al. | Dec 1994 | A |
5377860 | Littlejohn et al. | Jan 1995 | A |
5423160 | Rosen | Jun 1995 | A |
5424119 | Phillips et al. | Jun 1995 | A |
5427266 | Yun | Jun 1995 | A |
5433983 | Schuhmann et al. | Jul 1995 | A |
5439628 | Huang | Aug 1995 | A |
5453466 | Pellegatti et al. | Sep 1995 | A |
5454394 | Moore et al. | Oct 1995 | A |
5462987 | Shinonaga et al. | Oct 1995 | A |
5468807 | Tsurutani et al. | Nov 1995 | A |
5473016 | Fujii et al. | Dec 1995 | A |
5480931 | Hock et al. | Jan 1996 | A |
5486561 | Hirano et al. | Jan 1996 | A |
5489471 | Inoue et al. | Feb 1996 | A |
5494948 | Nishio et al. | Feb 1996 | A |
5514315 | Watkins et al. | May 1996 | A |
5516035 | Stone | May 1996 | A |
5516563 | Schumann et al. | May 1996 | A |
5539040 | Rohrmann | Jul 1996 | A |
5576374 | Betso et al. | Nov 1996 | A |
5578682 | White | Nov 1996 | A |
5582670 | Andersen et al. | Dec 1996 | A |
5589128 | Lai et al. | Dec 1996 | A |
5622780 | Paleari | Apr 1997 | A |
5640186 | Swanson et al. | Jun 1997 | A |
5641524 | Rush et al. | Jun 1997 | A |
5641828 | Sadatoshi et al. | Jun 1997 | A |
5665442 | Andersen et al. | Sep 1997 | A |
D386048 | Bebawey | Nov 1997 | S |
5686533 | Gahleitner et al. | Nov 1997 | A |
5744530 | Skelhorn | Apr 1998 | A |
5750226 | Macauley et al. | May 1998 | A |
5758773 | Clements | Jun 1998 | A |
5766712 | Darr et al. | Jun 1998 | A |
5786427 | Kijima et al. | Jul 1998 | A |
5792807 | Hayashihara et al. | Aug 1998 | A |
5795535 | Giovannone et al. | Aug 1998 | A |
5843260 | Huskey | Dec 1998 | A |
5891946 | Nohara et al. | Apr 1999 | A |
5902848 | Burgin et al. | May 1999 | A |
5968431 | Ang et al. | Oct 1999 | A |
6024907 | Jagunich | Feb 2000 | A |
6025455 | Yoshitake et al. | Feb 2000 | A |
6047845 | Rapaz | Apr 2000 | A |
6100512 | Neculescu et al. | Aug 2000 | A |
6120863 | Neculescu et al. | Sep 2000 | A |
6124370 | Walton et al. | Sep 2000 | A |
D434604 | Littlejohn et al. | Dec 2000 | S |
D434605 | Littlejohn et al. | Dec 2000 | S |
D437527 | Littlejohn et al. | Feb 2001 | S |
6203893 | Nohara et al. | Mar 2001 | B1 |
6211500 | Cochran, II et al. | Apr 2001 | B1 |
6211501 | McCarthy et al. | Apr 2001 | B1 |
6235361 | Jacquemet et al. | May 2001 | B1 |
6241096 | Littlejohn et al. | Jun 2001 | B1 |
D445304 | Littlejohn et al. | Jul 2001 | S |
6325234 | Legaspi | Dec 2001 | B1 |
6340530 | Porter et al. | Jan 2002 | B1 |
6371327 | Swiontek et al. | Apr 2002 | B1 |
6401962 | Littlejohn et al. | Jun 2002 | B1 |
6403936 | Cochran, II et al. | Jun 2002 | B2 |
6420689 | Cochran, II et al. | Jul 2002 | B1 |
6440509 | Littlejohn et al. | Aug 2002 | B1 |
6459075 | McCarthy et al. | Oct 2002 | B1 |
6474497 | Littlejohn et al. | Nov 2002 | B1 |
6571980 | Littlejohn et al. | Jun 2003 | B2 |
6627278 | Sandstrom et al. | Sep 2003 | B1 |
6670592 | McCarthy et al. | Dec 2003 | B2 |
6719943 | Neculescu et al. | Apr 2004 | B1 |
6733852 | Littlejohn et al. | May 2004 | B2 |
6846533 | Wu et al. | Jan 2005 | B2 |
6866905 | Sandstrom et al. | Mar 2005 | B1 |
6881937 | Swiontek | Apr 2005 | B2 |
20020192410 | Wu et al. | Dec 2002 | A1 |
20020197427 | Wu et al. | Dec 2002 | A1 |
Number | Date | Country |
---|---|---|
1 704 405 | Jul 1971 | DE |
2 007 552 | Sep 1971 | DE |
25 51 234 | May 1976 | DE |
296 05 250 | Sep 1997 | DE |
0 122 686 | Oct 1984 | EP |
0 167 660 | Jan 1986 | EP |
0 243 206 | Oct 1987 | EP |
0 311 723 | Apr 1989 | EP |
0 219 198 | Oct 1991 | EP |
0 532 233 | Mar 1993 | EP |
0 544 429 | Jun 1993 | EP |
0 407 198 | Dec 1994 | EP |
0 640 646 | Mar 1995 | EP |
0 837 003 | Apr 1998 | EP |
0 841 150 | May 1998 | EP |
2101307 | Mar 1972 | FR |
53-84044 | Dec 1976 | JP |
56-139927 | Oct 1981 | JP |
59-209520 | May 1983 | JP |
59-64647 | Apr 1984 | JP |
60-4729885 | Apr 1985 | JP |
60-238341 | Nov 1985 | JP |
62265332 | Nov 1987 | JP |
3101864 | Apr 1991 | JP |
03 173626 | Jul 1991 | JP |
4-201234 | Jul 1992 | JP |
5-170985 | Jul 1993 | JP |
6-203893 | Jul 1994 | JP |
6199334 | Jul 1994 | JP |
11-315458 | Nov 1999 | JP |
WO 9948775 | Sep 1999 | WO |
Number | Date | Country | |
---|---|---|---|
20050092742 A1 | May 2005 | US |
Number | Date | Country | |
---|---|---|---|
60366790 | Mar 2002 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 10387093 | Mar 2003 | US |
Child | 10995932 | US |