Claims
- 1. A method of preparing wires or tapes including Bi-2223 superconductor material comprising, providing oxide and carbonate sources of Bi, Sr, Ca, Cu and Pb, dry milling the sources without grinding media to produce a homogeneous mixture, heat treating by calcining the milled mixture at a temperature of at least about 830° C. for a time not less than about 12 hours, followed by at least one additional milling for a total milling time not to exceed about 30 minutes and one additional heat treatment, to produce an oxide powder having an average diameter in the 4 to 5 micron range, filling a silver or silver alloy tube with the oxide powder, shape forming the tube into a rectangular tape, alternately thermally treating and mechanically working the tape by heating the tape to an elevated temperature of about 835° C. to 840° C. and reducing the thickness of the tape, repeating the thermal treatment and the mechanical working, wherein the tape is held at the elevated temperature for a total time in the range of from about 48 hours to about 350 hours to provide Pb0.4Bi1.8 Sr2.0 Ca2.2 Cu3Ox, where x is between 10 and 11, wherein the material has a Jc value substantially greater than 2500 A/cm2.
- 2. The method of claim 1, wherein calcining is at a temperature in the range of from about 830° C. to about 842° C.
- 3. The method of claim 1, wherein there are no more than 3 millings.
- 4. The method of claim 3, wherein the material is milled not more than a total of about 30 minutes.
- 5. The method of claim 1, wherein there are a total of three millings and a total of at least two calcining treatments.
- 6. The method of claim 1, wherein the total time for calcining does not exceed about 48 hours.
- 7. The method of claim 1, wherein each calcining step is between about 12 and about 24 hours.
- 8. The method of claim 1, wherein the sources of Bi, Sr, Ca, Cu and Pb include Pb doped Bi2Sr2CaCu2O and Ca2CuO3 and CuO.
- 9. The method of claim 8, wherein the Pb is added as PbO.
- 10. The method of claim 1, wherein the filled tube is drawn to produce a wire with a diameter of about 60 mils.
- 11. The method of claim 1, wherein the filled tube is drawn and rolled to produce the rectangular tape and then alternately heat treated and mechanically worked by rolling to produce a tape about 5 mils thick.
- 12. The method of claim 1, wherein each mechanical working step reduces the thickness of the wire or tape not more than about 15%.
- 13. The method of claim 12, wherein the mechanical working step includes pressing the wire or tape at a pressure in the range of from about 20 tons to about 80 tons.
- 14. The method of claim 1, wherein the tape is subjected to four thermal treatments and three mechanical workings, the thermal treatments are at a temperature not greater than 840° C. and the time the tape or wire is held at the elevated temperature is from about 50 hrs. to about 100 hrs. for each thermal treatment.
- 15. A method of preparing wires or tapes including Bi-2223 superconductor material comprising, providing oxide and carbonate sources of Bi, Sr, Ca, Cu and Pb, dry milling the sources without grinding media to produce a homogeneous mixture, heat treating by calcining the milled mixture at a temperature of at least about 830° C. for a time not less than about 12 hours, followed by at least one additional milling, said total milling time being less than about 30 minutes and with any one milling time not greater than about 20 minutes, and one additional heat treatment, to produce an oxide powder having an average diameter in the 4 to 5 micron range, filling a silver or silver alloy tube with the oxide powder, shape forming the tube into a rectangular tape, alternately thermally treating and mechanically working the tape by heating the tape to an elevated temperature of about 835° C. to 840° C. and reducing the thickness of the tape, repeating the thermal treatment and mechanical working, wherein the tape is held at the elevated temperature for a total time in the range of from about 48 hours to about 350 hours to provide Pb0.4Bi1.8 Sr2.0 Ca2.2Cu3Ox, where x is between 10 and 11, where the material has a Jc value substantially treater than 2500 A/cm2.
- 16. The method of claim 15, wherein there are three millings and two calcining treatments.
Parent Case Info
This is a continuation of application Ser. No. 08/323,890, filed Oct. 17, 1994 now abondoned.
CONTRACTUAL ORIGIN OF THE INVENTION
The United States Government has rights in this invention pursuant to Contract No. W-31-109-ENG-38 between the U.S. Department of Energy and The University of Chicago representing Argonne National Laboratory.
US Referenced Citations (6)
Non-Patent Literature Citations (2)
Entry |
Microstructural Study of Bi (2223) /Ag Tapes with Jc (77 K, OT) Values up to 3.3 ×104 A cm -2 Supercond.Sci Tech. 4 (1991) 165-171. |
Reaction Mechanism of High-Tc Phase (Tc=110K) Formation In the Bi-Sr-Ca-Cu-) Superconductive System, Jap. Journal of Applied Physics, No. 11, Nov. 1989, pp. L1918-1921. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
08/323890 |
Oct 1994 |
US |
Child |
08/662515 |
|
US |